Search Documents

By J. A. Roberson, Robert A. Rapp

From the observation of platinum wire marker movement in the oxidation of columbium at high lemperatures and low oxygen pressures, predonzinant cation diffusion in CbO, has been demonstrated. The Cu,0 molecule was used as an oxidizing species to study the nature of the porous scale and the location of the reduction site in the oxidation of colum-bium. The Cb205 scale contains microporosity and forms by alternate ionic diffusional growth and fracture. The oxidation of columbium at high temperatures and very low po, results in a relatively compact and protective Cb205 layer. THE observation of marker movements during oxidation is one means for the identification of the mobile ionic species in an oxide lattice. Previous marker experiments in the oxidation of columbium have all resulted in the markers being found on the outside surface of the Cbz05 scale. The Cr203 powder markers of Klopp et a1.,' the gold film marker of Kofstad and ~jijllesdal,' and the platinum wire marker of Cathcart et a1 .3 were found at the oxide/gas interface for oxidation temperatures ranging from 450" to 120O0C. However, in all experiments relatively high oxygen pressures were used. As discussed by Mrowec, even the interpretation of marker experiments in simple scales containing only one compound is not without ambiguities. In brief, it can be said that a marker may be found almost anywhere in the scale layer if the metal oxidizes by cation diffusion through the scale; the position of the marker depends upon morphological happenings in the scale. When considering marker movement in a polyphase scale one must proceed with extreme caution. For example, in the past (and present) work markers have never been found at the columbium-scale interface, and one might infer that the oxygen ion is mobile in CbO and CbO,. However, only trace quantities of CbO and CbOz have been present on any of the specimens, so no firm statement is justified on this basis. Despite previous experimental work, considerable doubt still exists concerning the role of the oxides CbO and CbOz in the oxidation of columbium. The identification of the mobile ionic species in CbO and CbOz from the observation of platinum wire markers was one goal of the present investigation . The linear kinetics of columbium oxidation at high temperatures (T - 1000°C) suggests that the Cbz05 scales which form on columbium are porous. From mercury absorption measurements on a Cbz05 scale formed at 500"C, Aylmore et al.' reported a minimum volume fraction of connected voids equal to 0.15. While these scales often appear to be quite porous when viewed in metallographic cross section, they are so brittle that metallographic preparation is likely to exaggerate any porosity originally present. In this investigation, porosity developed during the oxidation of pure columbium and present at the high temperature was detected by oxidizing specimens in sealed evacuated capsules containing large compacts of mixed copper and CuzO powders. wooda has demonstrated that the CuzO, or (CuzO),, molecule is volatile and that oxygen is transferred by the CuzO molecule from a Cu/CuzO mixture to materials having a greater affinity for oxygen. For each molecule of CuzO that is reduced at a sink for oxygen, two atoms of copper are deposited. Quantitatively, essentially all of the oxidation carried out by a Cu-Cu20 compact results from a displacement reaction involving the CuzO molecule. When a metal which oxidizes to form a porous scale is exposed to the CuzO vapor, the CUZO molecules are reduced in the pores leaving a deposit of metallic copper to mark the site of the reduction. This technique has the rather unique advantage that any copper-coated pores found in the scale are unambiguously related to the reduction site in the growth of the scale under consideration. Pores or cracks which form in a msition*- external to the reduction site or which occur as a result of cooling or handling of the specimen will not exhibit the copper deposit. EXPERIMENTAL PROCEDURE Marker experiments were made on columbium metal, and on pellets of CbO which had been pressed and sintered. Platinum wire markers (0.001 and

Jan 1, 1968

By Robert D. Pehlke, Kazuhisa Okajima

The activity of zinc in dilute liquid lead alloys containing small additions of silver and gold has been measured using a multielectrode galvanic cell with a fused chloride salt electrolyte. The range of temperatures studied in the Pb-Zn-Ag system was 550" to 670°C and in the Pb-Zn-Au system was 680" to 800°C. The interaction parameters between zinc and the precious metals in the respective temperature ranges are ThE lead-rich corners of the Pb-Zn-Ag and Pb-Zn-Au ternary systems are of considerable industrial importance. The use of zinc additions for the desilvering The results of this investigation have Provided a senzi-quantitative determination of the liquidus phase boundaries in the lead-rich corner of these ternary diagrams. of liquid lead either by the Parkes process or by the more recent Williams continuous process is an important refining phase of lead production.1 Several in-ve~ti~ations~-~ have been carried out on the Pb-Zn-Ag system with the hope of improving the efficiency of refining lead in this manner. The addition of zinc also provides a means for separating gold from lead. Since gold is eliminated more easily than silver, a two-stage removal of gold and silver is possible.8'7 The thermodynamic interactions between zinc and these precious metals in dilute solution in liquid lead

Jan 1, 1968

By Emerson F. Heald

A systematic study was made of new and old data on chemical activities in Fe-Pt alloys at elevated ternperatuves. Experimental results may be expressed in terms of the excess free energy using Least-squares analysis of the data gave the following values for the constants: for the temperature range 1130° to 1350°C, and tentatively to 155O°C, B = -3.326564 and C = 0.221051; for the temperature range 650" to 850°C, B = -2.555690, C = 1.762735, and D =0.097196. In the study of iron-containing silicate systems, it is sometimes desirable to have a direct experimental measure of the activity of iron in the system. The well-known solubility of iron in platinum, often a headache in experimental work on iron compounds under reducing conditions, can be used to advantage in this respect. If the activity of iron in an Fe-Pt alloy in equilibrium with the silicate is known as a function of the composition of the alloy, chemical analysis of the alloy will give a knowledge of the activity of iron in all of the phases in the system. The present study was undertaken in order to elucidate the characteristics of Fe-Pt alloys as iron activity indicators. This work is intended to tie together some previous work, which may be summarized as follows. Larson and Chipman1 determined the activity of iron in Fe-Pt alloys at 1550°C by equilibrating platinum metal with calcium oxide-iron oxide-silica melts of known iron activity. Compositions of the resulting alloys were determined by chemical analysis. A similar study was carried out by Taylor and ~uan,' who worked at 1300°C. They brought the Fe-Pt alloys into equilibrium with iron oxide under conditions of known partial pressure of oxygen, and thus, from the work of Darken and ~urr~,~ conditions of known iron activity. Compositions were determined indirectly, by following the change in weight of the sample. Sundaresen et el* used the electromotive force of cells in which the alloy formed one electrode in order to measure the activity of iron in the alloy at 650" and 850°C. These temperatures were chosen to be above and below the first-order phase transition which takes place upon the ordering of Fe3Pt and the second-order transition which occurs upon the ordering of FePt3. EXPERIMENTAL 1) High Temperatures. The starting materials used were thin platinum foil, about 0.002 mm thick, and Fisher Certified reagent ferric oxide, Fez03, which had been heated for 24 hr at 1000°C. An intimate mixture of 80-mesh Fez03 and platinum platelets was placed in a thin platinum foil envelope. The latter was suspended from thin platinum wires in the hot zone of a vertical-tube, platinum-wound furnace of the type described by Muan and ~sborn.~ A capillary gas mixer similar to that used by Darken and Gurry3 was used to prepare a precisely known mixture of carbon dioxide and hydrogen, which was allowed to flow upward through the furnace tube. The partial pressure of oxygen in contact with the sample was thereby fixed at a value which was calculated from the charts prepared by porter? Temperatures were measured with a Pt-10 pct Rh-in-platinum thermocouple, which was calibrated using the melting points of gold (1062 .@C) and diopside, CaMgSizOB (1391.5"C). Temperature control was maintained to within i3"C with a Geophysical Laboratory proportional controller, using the furnace resistance as the sensing element. Samples were quenched by passing a small current through the platinum suspension wires, allowing the sample to drop into a bath of dibutyl phthalate at the bottom of the furnace tube. Prior to chemical analysis the samples were washed with acetone and dried. 2) Chemical Analysis. It proved possible, in almost all cases, to separate the Pt-Fe platelets physically from particles of iron oxide. The platelets were dissolved in a small volume of aqua regia, evaporated to dryness, and redissolved to 0.1 M HC1. In order to determine iron in the platinum alloy potentiometrically, it is necessary first to remove the platinum. A 10-cm column of Amberlite IR-120 cation exchange resin in the hydrogen form provided separation quickly and quantitatively: The mixture of iron and platinum in 0.1 M HC1 was added to the top of the column, and washed with about 100 ml of 0.1 M HC1. Under these conditions, the iron, principally in the form of cations such as FeC1" and FeCl;, is held quantitatively in the uppermost centimeter of the column. The platinum, in the form of anions such as PtC&- , is washed through without being adsorbed. After a qualitative test with stannous chloride indicated all of the platinum was removed, the iron was

Jan 1, 1968

By E. T. Turkdogan, M. T. Hepworth, R. P. Smith

The permeability of oxygen in 0 iron in the tempera-ture range 700" to 900 C and in 6 iron at 1450°C was determined by the rate of internal oxidation of iron, containing -0.1 pct Al. The solubility of oxygen in zone-refined iron was determined by equilibration with hydrogen-water vapor gas mixtures at 1450" and 1510°C; oxygen solubilities , for iron in equi1ibriu.rn with molten oxide, are found to be 66 and 83 ppm for these two temperatures, respectively. The diffusivity of oxygen in iron at 14500C3 as calculated from the permeability and solubility data, is (4.1 * 0.6) x 10 "B sq cm per sec. OXYGEN is one of the most common impurities present in iron or steel, mainly in the form of oxide inclusions. In the study of many metallurgical problems concerning solid iron, it is often desirable to know with a reasonable accuracy the solubility and diffusivity of oxygen over a wide temperature range. The solubility of oxygen in solid iron has been the subject of numerous studies yielding highly discordant results as seen for example from the literature surveys made by Meijering &apos; and Schenck et a1.&apos; As shown by Kitchener et aL3 and by Sifferlen, the high oxygen solubilities reported by many investigators are the result of oxidizable impurities which are often present in iron. In addition, there have been experimental problems associated with icaccuracy of oxygen analysis of iron containing less than 100 ppm 0. A number of studies have been made on the permeability of oxygen in a and y iron using Fe-Si, Fe-Mn, and Fe-A1 alloys in the internal-oxidation experiments.1&apos;2&apos;5&apos;6 However, no direct measurements have been made of the diffusivity of oxygen in iron. In the present work two sets of experimental measurements were made: permeability and solubility studies at 1450" and 1510°C and permeability studies only in the range 700 to 900°C. In both sets of permeability measurements slab-shaped specimens containing small predetermined amounts of aluminum in solution were exposed at constant temperature to gas mixtures of hydrogen, water vapor, and argon for varying times. These specimens were quenched, sectioned, and examined for oxygen penetration by metallographic observation of aluminum oxide particles which formed. From these data, it is possible to calculate the ratio of the diffusivity of oxygen in iron, D, to the equilibrium constant K for the reaction Hz(g) * O (dissolved in iron) = H,O(g). EXPERIMENTAL Permeability Measurements at 1450°C. An ingot of vacuum-carbon deoxidized iron containing 0.086 pct A1 was prepared, using commercial "Type lO4A Plas-tiron"; after hot rolling, specimens were machined into slabs a by 2 by 2 in. The impurity contents were: S, P < 0.002 pct; C, Mn < 0.01 pct; each of all other Usual impurities < 0.004 pet. The amount of oxide inclusions in this material, determined by a bromine-methyl acetate extraction, corresponded to about 20 ppm 0 in the iron which agreed well with the results of vacuum-fusion analysis. Each specimen was annealed at 1450°C for 1 hr in purified hydrogen, polished to a smooth surface, and then introduced into a controlled oxidizing atmosphere in a recrystallized alumina tube at 1450°C. The constant temperature zone (*3"C) was about 3 in. in length. The gas composition was controlled by mixing argon with hydrogen (using calibrated constant-head flow meters) and passing the mixture through a column of a mixture of oxalic acid dihydrate and 10 pct anhydrous oxalic acid, to establish a required water-vapor content in the gas mixture. The temperature of the oxalic acid dihydrate column was controlled by a thermostat. The total gas flow was in the range 800 to 1000 cu cm per min. The exit gas from the reaction tube was passed through a weighing bottle containing a desiccant, to cross-check the degree of water-vapor saturation, which for all experiments was about 97 pct of those derived from the data of Baxter and Lansing.1 For a typical experiment, a specimen was introduced into the furnace in a stream of dry argon and hydrogen. The specimen was then rapidly raised by a Pt-Rh alloy wire into the hot zone and allowed to reach the reaction temperature, at which time the oxidizing gas mixture was introduced. The oxygen potentials employed were sufficient to oxidize aluminum but not to cause liquid iron oxide to form. After a specified time, the experiment was ended by dropping the specimen onto a water-cooled copper block at the bottom of the reaction tube. The depth of the internally oxidized zone, hereafter called the "case", was determined by sectioning the specimen at right angles to the long direction. The section was then examined under a microscope equipped with a micrometer stage. In general, the oxide particles were fairly uniform in size and distribution, forming a reasonably well-defined interface between the oxidized and unoxidized region. A typical cross section as observed at X30 is shown in Fig. 1. A thermal macroetch was used in one selected specimen to delineate the case. A cross section of a previously oxidized slab was polished and reheated at 1450°C in a hydrogen atmosphere for about 10 min. Upon quenching, the surface relief shown in Fig. 2 was produced; causes of this effect are unknown. Permeability Measurements Below 900°C. A slightly

Jan 1, 1967

By K. Mukherjee

A quasi-thermodynamic calculation is presented for estirt~ating vacancy Parameters in fcc metals. For fcc metals the equilibrium vacancy concentration at the melting point can be approximated by a constant mole fraction. The Gibbs free energy of formation of the vacancies can then be expressed as a simple function of the absolute melting temperature alone. From this description the formation energy Ef, the vibrational entropy Sv, and the formation volume of a vacancy can be calculated in terms of known thermodynamic parameters. The calculated values are in good agree-rnent with available experimental results. IT appears that many of the physical parameters associated with lattice defects can be empirically related to thermodynamic melting parameters.&apos;-7 Besides the implicit correlations between melting phenomenon and point defects, the melting temperature itself at atmospheric pressure can be used as a reference temperature for the purpose of comparison of vacancy concentrations in a given crystal class. The concentration at the melting point then corresponds to the maximum vacancy super saturation in the crystalline state at a fixed pressure. For pure fcc metals such as Au, Cu, Al, Ag, Pb, and Pt the mole fraction of vacancies at the melting point8 is of the order of 10*"3 to 10"1. The equation expressing the equilibrium vacancy concentration at the melting point contains three parameters: the formation energy, the vibrational entropy, and the absolute melting temperature, see Eq. [2]. Since these three parameters cover a wide range of values8 in the above-mentioned metals, it can be assumed that in other fcc metals, for which no reliable data are available, the mole fraction of vacancies at the melting point most likely lies in the range 10~3 to lO"4. This is then the basis of the calculations described in this article. Within this range the mixing entropy can be linearized and the vibrational entropy, the formation energy, and the vacancy formation volume can be calculated in terms of known thermodynamic constants. 1} LINEARIZATION OF MIXING ENTROPY The Helmholtz free energy of a crystal containing n vacancies at the melting point can be writteng as where Ef, T,, k, and S, are the formation energy of a vacancy, the absolute melting temperature, Boltz-mann&apos;s constant, and the vacancy formation entropy, respectively. After applying Stirling&apos;s approximation in Eq. [l] and minimizing with respect to n where (n/N), is the equilibrium vacancy concentration in mole fraction at the melting temperature at 1 atm pressure. If instead of setting (6~/6n) = 0 immediately after Stirling&apos;s approximation in Eq. [I], the configurational partition function is simplified, then some useful and significant results can be obtained by utilizing the experimental inforrnation After applying Stirling&apos;s approximation and rearranging is plotted as a function of (n/N) in Fig. 1. The points, not all of which are shown, are fitted by a straight line substituting from Eq. [5] into Eq. [I] and minimizing with respect to n combining Eqs. [6] and [2] It must be emphasized that Eq. [7] is only a crude approximation based on an oversimplified model of

Jan 1, 1967

By C. A. Stickels

A heat of electrolytic iron, to whzch alunzinutn and nitrogen had been added, was hot-rolled, cold-rolled 90 pct, and recrystallized at temperatures from 500" to 700°C. Primary recrystallization textures appear to arise from competitive growth of two types of nuclei: 1) those having orientations belonging to the "usual" primary recrystallization texture found in riming steel, and 2) those with the {111} (110) ovientation. Development of a (111}(1 10) component in the primary recrystallization texture occurs only over a certain interval of isothermal recrystallizatzon temperatures when the material is supersaturated with respect to the precipitation of AlN. Lowering the degree of supersaturation depresses the temperature interval in which a (111)(110) component occurs. An elongated, &apos;pancake-shaped" recrystallized pain structure and a marked delay in the start of recrystallization were found in all specimens which were supersaturated with respect to A1N precipitation after cold work, regardless of their recrystallization texture. ONE of the consequences of killing low-carbon steel with aluminum is a significant change in recrystallization behavior. About 15 years ago, Solter and eatttiel showed that this behavior was largely controlled by aluminum and nitrogen in the steel. If complete precipitation of A1N was prevented before cold rolling, an increased "recrystallization temperature" was observed in subsequent. annealing, and the recrystal-lized grains were not equiaxed. Leslie et a1.2 studied this phenomenon in some detail and clearly demonstrated the relationship between A1N precipitation, recrystallization kinetics, and the development of "pancake-shaped" grains. It has also been known for some time that aluminum-killed steels, processed to produce elongated "pancake" grains, develop a (11 I}( 110) primary recrystallization texture. This texture has not been found in iron or low-carbon rimming steel as a primary texture4j5 but has been observed following grain growth in electrolytic iron.5 The present work was undertaken to study in more detail the effect of A1N supersaturation on recrystallization textures in iron. LITERATURE REVIEW The deformation texture in heavily rolled iron has been studied in detail by Bennewitz.~ The texture consists primarily of a partial fiber texture about a (110) axis in the rolling direction, designated here as fiber texture A. It includes the range of orienta- tions (111)[110] - (001)[ 110] - (11l)[110]. A weak secondary texture also is present.6 This is a duplex partial fiber texture about two (110) fiber axes located 60 deg from the rolling direction and 30 deg from the sheet normal. The range of this texture, designated here as fiber texture B, about the [101} fiber axis is (112)[110] - near (545)[252] - (211:1[011] *The range given here follows Bennewit~.~ A few pole figures from re-crystallized material indicate a broader range than this.&apos; However, the components which are strongest in the recrystallization texture are in this range.&apos;________________________________________________________ Primary recrystallization textures in unkilled steels can be accounted for by growth of members of fiber texture B present in the deformed metal.5 However, while members of fiber texture B dominate the primary texture, other orientations survive primary recrystallization as well. In particular, some {111}(110) members of fiber texture A must also grow during primary recrystallization, because a well-defined {1ll)( 110) texture develops during subsequent grain growth at 700°C.5 The unusual recrystallization behavior of deformed supersaturated solid solutions has been attributed to: 1) retention of the solute in solution,&apos; 2) formation of coherent, preprecipitation solute clusters prior to and during re~r~stallization,~ and 3) formation of a precipitate prior to and concurrent with recrystallization.&apos;~-&apos;~ When aluminum is supersaturated with iron, the difference in grain boundary mobility between general high-angle boundaries and certain special coincidence site boundaries is apparently eliminated.&apos; In aluminum-killed steels, precipitation of A1N can take place at ordinary subcritical recrystallization temperatures. The rate of precipitation increases with increasing aluminum or nitrogen contents.2&apos;13 There is some doubt, however, as to whether true precipitates form during the time at temperature needed to complete recrystallization. Leslie ef a1.2 found that precipitation in one steel was complete after about 100 min at 700GC, or after about 1000 min at 650GC, as measured by chemical analysis for AlN. Aoki et a1.,13 using internal friction for dissolved nitrogen, showed that a large fraction of the dissolved nitrogen was removed from solution within a few minutes annealing time at temperatures from 400" to 800°C. However , the rate of formation of AlN, as detected bv chemical analvsis. was much slower than the apparent rate of nitrogen removal. Hasebe,&apos;~~ using carbon extraction replicas, has identified A1N precipitates by electron diffraction in a 0.2 C steel, solution-treated at 1300°C and annealed 2 hr at 700°C. Borchers and kim,I6 also using a replication technique, observed precipitates after annealing treatments as short as 2 min at 640°C. However, Leslie et a1.&apos; state that no A1N precipitate can be seen while recrystallization is being inhibited in aluminum-killed steel.

Jan 1, 1967

Jan 1, 1967

Jan 1, 1968

By D. Cox, M. J. Duggin, L. Zwell

The carbides of approximate composition and Mn have been studied using X-ray diffraction techniques. Those carbides of the type (Fe,Aln)zC ave isostructural with cementite. The cell pararmeters a and c have minimum values at approximately 10 at. pd substitution of manganese for iron; no satisfactory explanation has yet been found for this phenomenon. The carbide fFeMn4)C has a monoclinic unit cell whose dimensions are close to those of ,11,15Cz A neu-troip-dij~ractiot~ study of (F&apos;eAlrz4)C~ reveals that, like MnsCZ, it is isostructural with Pd5Bz. The iron and manganese atoms occupy the palladium atom sites, while the carbon atoms were found to have the same atomic coordinates as the hovon atoms. A neutrorr-diffraction study of indicates that the carbon-atom positions are very close to those occupied in (Fez.,ll/lr~,.3)C. In both carbides studied, tlre iron and manganese atomzs were found to be essentially randomly distributed, although, in the case of (Fe,.811fn1.2)C, it is possible that there may be a slight preference of manganese atoms for- the general (d) positions and a corresponding slight preference of iron atoms for the special (c) positions. It has been found that a complete range of solid solution exists between Fe3C and Mn3C at 1050°C,I although Mn3C becomes unstable when the temperature is reduced to 95O0C,&apos; and can only be retained by rapid quenching. It is also known that a complete range of solid solution exists from Fe5Cz to M~SC~,~ although the stability range of carbides of the type (Fe,Mn)sCz as a function of the relative proportions of iron and manganese is not known. X-ray examinations of Oh-man&apos;s carbide3 and Spiegeleisenkristall,~ which have the approximate compositions (Fe3.67Mnl.33)C2 and (Fe3-,Mn,)C, where x lies between 0.4 and 1, respectively, have been made. The following carbides have also been studied: ] The lattice parameters determined during these investigations are listed in Table I. It is seen that carbides of the type (Fe,Mn)sCz have a monoclinic unit cell while carbides of the type (Fe,Mn)3C have an orthorhombic unit cell. It is evident that the variation of lattice parameters with manganese content is not linear for carbides of the type (Fe,Mn)3C. The coordinates of the atoms in (Fe2.7Mno.3)C have recently been determined by single-crystal analysis., The fractional atomic coordinates have been shown by Fasiska and jeffrey to be in good agreement withj those deduced from an earlier analysis of Fe3C by Lipson and etch.&apos; However, it was impossible to determine whether iron and manganese atoms occupied ordered positions because of the small difference between the atomic scattering factors of iron and manganese. The atomic positions in Mn5Cz (Refs. 8 and 9) and Fe5C2 (Refs. 7 and 8) have been obtained only by comparisons made with the isostructural compounds P~SB~.&apos; Since X-ray diffraction techniques were used in these investigations, accurate positioning of the carbon atoms, which have a low atomic scattering factor, was difficult. No attempt has been made to determine the atomic positions in the other carbides previously studied. It was felt that an investigation of the lattice parameters of a number of intermediate carbides of the types (Fe,Mn)sCZ and (Fe,Mn)& would be of interest. It seemed likely that a neutron-diffract ion study of such carbides would indicate whether ordering occurred between the iron and manganese atoms because of the large difference between the neutron-scattering cross sections of iron and manganese. It also seemed probable that such an investigation would provide a determination of the atomic coordinates of the carbon atoms. I) EXPERIMENTAL DETAILS Specimens, each weighing approximately 20 g, were carefully prepared according to the following proportions: The components were 500-mesh powders of 99.995 pct purity iron and spectroscopically pure carbon and a 200-mesh powder of 99.995 pct purity manganese. The component powders were intimately mixed by prolonged shaking, then each specimen was inserted into a spot-welded cylindrical container of tantalum foil, whose end was closed but not sealed. Each specimen in its envelope was then sintered at 1050° C for 24 hr in a thin-walled evacuated quartz capsule, such a time having been previously found sufficient for equilibrium to be attained.&apos; Each specimen was then quenched in order to attempt to retain the high-temperature phase, as the literature indicates that transformations may occur on cooling. Debye-Scherrer X-ray photographs were taken of each specimen using a 114.6-mm-diam camera, Fig. 1, patterns 2 to 6. The exposure time was 6 hr using filtered iron radiation at a tube voltage of 40 kv and a tube current of 12 ma.

Jan 1, 1967

By J. D. Embury, R. M. Fisher, A. S. Keh

An investigation of the defect structure and properties following large strain deformation has been carried out using transmission electron microscopy and mechanical testing for a range of ferrous materials and for copper. It is shown that, for a variety of ferrous materials, a cellular substructure is developed during the initial stages of working and on further deformation the dimensions of this substructure are reduced. Quantitative measurements of the flow stress and the scale of the substructure indicate that the strength of heavily worked materials is largely determined by the spacing of cell walls. These cell walls act as dislocation barriers in a manner analogous to grain boundaries. FCC materials do not harden as extensively as bcc after cold working and the present observations on copper indicate that the dimensions of the substructure in fcc materials are not markedly reduced on deformation. The differences between the fcc and bcc structures produced by large plastic strains are ascribed to differences in the extent of dynamic recovery. It is tentatively proposed that the greater stability of substructural barriers in bcc structures results from strong interstitial Pinning effects. It is proposed that for large plastic strains the work-hardening process may be considered in terms of the reduction of substructural-barrier spacing during the working process. This pvovides a simplified hut useful analysis of the strain hardening occurring during mechanical processes. THE mechanisms of strain-hardening processes have occupied the attention of numerous investigators over the past three decades and a multitude of theories have emerged in this field. The majority of previous work has been concerned with the development of a description of the plastic behavior of single crystals in terms of dislocation theory.&apos;" In contrast, scant attention has been given to the strengthening mechanisms operative during mechanical working processes such as rolling and drawing. The large plastic strains involved in these processes make it difficult to correlate the observations with any elementary dislocation theory. Further, as Bullen and coworkers3 have opined, for large plastic strains both hardening and recovery occur simultaneously and thus it is extremely difficult to estimate the effect of plastic strain on the ambient internal stress field. It is probable that for large plas- tic strains any theoretical estimate of the internal stress field must be made in terms of complex dislocation groups. Although some valuable theoretical work has been done toward calculating the elastic properties of dislocation groups4 any detailed self-consistent model for large plastic strain is as yet impossible. With these limitations in view it is still of value to examine the mechanical properties of highly strained materials as a function of their substructure. This relationship is explored in the present communication for a variety of materials subjected to rolling, drawing, or swaging. The primary object of this investigation has been to establish the validity and the limitations of the substructural strengthening mechanism proposed by Embury and eisher&apos; for drawn pearlitic wire and by Meieran and Thomas for drawn tungsten wire. No attempt has been made to delineate the basic interaction mechanism which occurs between a slip dislocation and the substructure and the authors believe that a great deal more experimental evidence must be compiled before these fundamental aspects can be explored. Also, no specific attention has been given to the detailed formation of substructure during working. Experimental Details. A variety of materials were used in this investigation, the compositions and heat treatment of which are tabulated in Table I. The commercially pure iron is referred to throughout this report as Ferrovac E. The mechanical working processes were all performed at room temperature. The wire drawing was performed on a manual drawing bench. Reductions of between 10 and 20 pct in area per pass were used in both swaging and drawing. The experimental parameter used to evaluate the mechanical properties of the materials was the 0.2 pct proof stress. This was determined for wire samples using an Instron tensile machine at a crosshead speed of 0.02 in. per min. The techniques for preparation of samples for transmission electron microscopy have been described previo~sl~.~ Specimens from wire samples were prepared from longitudinal sections and in some cases from transverse sections. To evaluate the substructural characteristics of rolled materials, thin foil samples were prepared of both the face and edge sections. Results. One of the more familiar ways of expressing work hardening in mechanical working is by the flow stress as a function of reduction in cross-sectional area. Fig. 1 shows such a plot for Ferrovac E eutectoid carbon steel and for copper. The curve for Ferrovac E is characterized by an initial stage of rapid work hardening and a final stage of rapid work hardening separated by an intermediate stage with a low rate of work hardening. This behavior is typical of many ferrous materials and the drawn pearlite wire previously investigated by Embury and Fisher is a more pronounced example. Copper shows an initial

Jan 1, 1967

By Harry C. Gatos, Frank J. Bachner

It was shown through high-pressure experiments that tin loss by volatilizatim is necessary for the degrada-tion of the superconducting transition temperature of Nb,Sn associated with high-temperature annealing. Crystallochemical analysis of the degraded Nb3Sn showed that it constitutes a new phase with ordered niobium-site vacancies, created by the migration of niobium atoms to vaccnt tin sites. This new phase was found to form when 4 pct Nb-site vacancies were present. It has a transition temperature of 6&apos;K and a lattice parameter of 5.283A. A similar degradation effect was observed in Nb,Al. Its superconducting transition temperature dropped from 16.5" to 8" K following a high-temperature annealing. The superconducting temperature degradation in these 0-tungsten structure compounds is attributed to the disruption of the interchain d bonding by the periodic interruption of the niobium atom chains. By annealing the degraded Nb, Sn at 1000 C in nitrogen its normal superconducting behavior is restored most likely due to the incorporation of nitrogen atoms causing the elimination of the ordered vacancies. HANAK et al.&apos; have observed low superconducting transition-temperature values (T, - 9"K) in some NbsSn samples deposited from the vapor phase. They attributed such low T, values to disorder in the 0-tung-sten structure. Much lower T values (down to 5.6"K) were reported by Reed et al.zC for NbsSn samples annealed at high temperatures. These authors also attributed this degradation effect to disorder (random occupation of the A and B sites by niobium and tin) but pointed out that such disorder could be brought about (by high-temperature treatment) only in samples containing niobium in excess of the stoichiometric composition NbsSn. Both groups reported that the normal superconductivity behavior could be rever-sibly restored by appropriate heat treatment. Courtney et al., also found that degradation in NbsSn requires excess niobium brought about by the loss of tin during the treatment. However, these investigators proposed that the degradation is due to niobium-site vacancies resulting from the migration of the niobium atoms to the vacated tin atom sites. They did not consider the reversibility of the effect. The present study attempts to establish the nature of the above degradation phenomenon. EXPERIMENTAL PROCEDURES All compounds prepared for this investigation were made from the powders or filings of the elements which were intimately mixed, cold-pressed into a cylindrical pellet at approximately 50,000 lb per sq in., and then submitted to the desired heat treatment. The samples annealed under high pressure were placed in a MgO sample container which was mounted in a pyrophyllite tetrahedron designed for a tetra-hedral-anvil press. Details of the experimental arrangement are given elsewhere. This setup allowed heating at 1800°C or above under pressures in excess of 30kbars for 3 hr. The samples annealed in a vacuum were prepared in a high-temperature vacuum furnace which could reach temperatures up to 2400°C under a pressure of 2 x lo-&apos; Torr. For annealing in a reactive atmosphere, a quartz tube was placed in a clamshell furnace and the desired gas ambient passed through the tube. Lattice parameters were determined using a Debye-Scherer 114.6-mm camera. Cohen&apos;s method, programmed for the IBM 7094 computer, was used to calculate the lattice parameter from the measured d spacings. X-ray integrated intensity measurements were made on several samples. These samples were ground to -400 mesh and the powder mixed with a solution of collodion in amyl acetate. The mixture was poured into a depression milled in a bakelite disc. When the mixture dried, the surface of the disc was ground flat leaving a diffraction surface defined by the face of the disc. The disc was mounted in a Philips rotating specimen holder which allowed the rotation of the sample in the plane of the diffraction surface and the integrated intensity measured using a scintillation counter and a pulse-height analysis sys-tem. The superconducting transition temperatures were determined by means of self-inductance techniques.&apos; EXPERIMENTAL RESULTS AND DISCUSSION The Role of Tin Loss in the Degradation of Super-conductivity. The loss of tin during high-temperature annealing can be effectively suppressed by annealing under high hydrostatic pressures. Accordingly, a series of experiments were performed under pressures of approximately 30kbars. This pressure was the minimum under which high-temperature experiments could be safely performed in the particular pressure apparatus employed. Experiments were also designed to test high-pressure effects on the superconductivity behavior of NbJSn. The results of the high-pressure annealing experi-ments are summarized in Table I. All samples were prepared as described earlier. They were reacted and homogenized at 1000°C for 24 hr under argon at-

Jan 1, 1967

By N. A. Gjostein

The formal descnption of the decay of an isolated scratch can be written in terms of an appropriate Fourier integral. With the application of certain approximations, this description leads to the second-moment analysis developed by King and Mullins. It is shown that the second-moment analysis does not adequately describe the behavior of a decaying, isolated scratch, and that it is difficult to obtain internally consistent values of the surface self-diffusion coefficient, D,,from this analysis. This inconsistency arises from contributions of higher-order moments to the decay process. Two new analytical methods, based on the Fourier integval representation of a scratch profile, have been developed for determining values of D, from the decay kinetics of isolated scratches. In the profile-matching method, a given initial profile is resolved into its Fourier components, the components are allowed to decay exponentially over an annealing time interval, At, and finally they are synthesized to form a decayed profile. The predicted profile is adjusted to fit the experimental profile by varying only the parameter, D,At; the contribution from volume diffusion is directly taken into account and the integrals involved in the Fourier analysis are evaluated by numerical integration on an electronic computer. In the kinetic method, the widths, W, of a series of predicted profiles are determined for various volume-diffusion contributions, and the results are plotted in the form W vs DSAt. For a fixed ratio of surface to volume diffusivities, R, these plots are linear; the slope of the lines increases as R decreases. A simi-lar analysis can be performed on the depths of the predicted profiles. In this case, plots of (l/df3 vs D,At are found to be nonlinear. The proper value of Ds is found by superimposing the data for the experimental widths and depths on Plots of this kind and adjusting Ds until a fit is obtained with the line having the appropriate value oj R. An analysis of the slopes of these plots for R —= (surface diffusion only) reveals that they do not give the correct value, 2276, for width tf second-moment standard profile. This finding allows one to modify the second-moment analysis in such a way as to obtain internally consistent values of Ds. ThERE are several processes, involving a flow of matter along a surface, due to gradients in curvature of the surface, that may be used to determine the surface self-diffusion coefficient, Ds. These processes are commonly known as 1) thermal grooving, 2) single and 3) multiple scratch decay, 4) blunting of field-emitter tips, and 5) sintering. In this series of papers, the first three of these processes are examined in detail in an attempt to subject the phenomenological theories governing these processes to a critical test and, furthermore, to make a critical comparison of the values of D, obtained from these techniques. Although the thermal grooving technique has been established&apos;&apos; as a reliable method for determining D, , this has not been the case for the process of scratch flattening. Mullins and coworkers374 have proposed phenomenological laws governing the growth of the width and the decay of the amplitude of an isolated scratch, but only in one study5 has the width-growth law been supported by experimental evidence. In paper I of this series detailed experimental evidence is presented that points up the deficiencies of the second-moment analysis; the origins of these deficiencies are also discussed. Following this development, some new analytical procedures, based on representing the scratch profile by Fourier integrals, are presented as a means of obtaining reliable values of D, from the kinetics of the scratch-flattening process. Further applications of the Fourier integral approach are reported in papers 11&apos; and 111,~ where the method has been useful in interpreting the anisotropy of flattening rates of isolated scratches (paper 11) and in describing the multiple scratch decay process (paper 111). THEORY OF SCRATCH DECAY Following ~ullins" approach we consider an arbitrarily shaped scratch profile, Fig. 6, at some time, t. The profile is designated by a function z(x,t) which can be expressed in terms of a Fourier integral as follows:

Jan 1, 1967

By P. G. Shewmon, H. E. Collins

A study has been made to determine the sites at which sulfur adsorption occurs on copper surfaces. measurements were made of the relative torques, Ys, at the intersection of twin boundaries with surfaces near the three low-index orientations, i.e., (100), @lo), and 011), over a range of H2S/H2 ratios. HZS concerztvations j&apos;ro~n 3 to 1500pp)n between 830" and 1050°C were used. It is concluded that sulfur adsorption occurved preferentially though not exclusively at edge sites near the (100) and (110) surfaces in the HzS range — 700 Ppm giving rise to negative torques near these orientations. Beyond this HzS range, adsorption occurred at all sites. Near the (111) surface, 7/y little with HzS concentration up to approxiwzately 75pptn. Above this range, the results indicate adsorption is occurring OH both terrace and edge sites. SCIENTIFIC interest in surfaces and their interactions with a gaseous environment dates back to the beginning of the 19th century. The scientific luminaries of that period—Faraday, Maxwell, Rayleigh, Dewar, and Gibbs—were already concerned about such processes. However, it has only been within the past several decades that adsorption on metal surfaces has been actively studied. This increased interest in adsorption has been brought about by the advent of new and improved experimental techniques and apparatus, e.g., ultrahigh vacuum, and field-emission and ion microscopes. However, most of the work done using these techniques has been carried out at low temperatures. When adsorption studies have been made at either low or high temperatures, they usually gave no indication of the particular surface orientations or type of sites on which adsorption was occurring. In the last few years, there have been a series of studies in which the surface tension, y,, and/or its derivative with respect to orientation, 7, have been studied as a function of orientation and atmosphere.&apos;-7 Nearly all of the work on the relative torque,* ~/y, silver annealed in hydrogen and air.6 Recently Winterbottom and Gjostein" have used a modified and more accurate Mykurian method to determine the y plot of gold in hydrogen The only work in which T/~, has been measured over a range of chemical potentials for a given solute, p2, is that of Robertson and shewmon7 on the Cu-0 system. They measured T/Y, vs Po, (10"" to 10- l3 atm) at 1000°C in various mixtures of Hz0 and HZ. From this work they estimated the value of p2 at which one half of the surface sites are occupied with oxygen, pg, as being in the range 10- l6 to 10- l5 atm of oxygen. They also found that increasing Pa increased the magnitude of ~/y, near the (111) and (100) orientations. This indicates that oxygen is not adsorbed preferentially at step edges, but uniformly over all surface sites. In addition, they did one experiment on sulfur adsorption on copper surfaces, which indicated that sulfur adsorption decreases ~/y, near the (100) orientation, while not affecting ~/y, near the (111). This could be interpreted as indicating that sulfur adsorbs preferentially at step edges near the (100). In this paper the primary objective of the work has been to carry out a study of sulfur adsorption on copper surfaces over a range of temperatures and p,. In conjunction with this work, thermal grooving at grain boundaries has been examined as a method of determining the effect of sulfur adsorption on y,. METHODS Ideally, one would like to have information on the quantity of solute adsorbed on a surface and the types of sites at which it is absorbed as a function of p2. The total quantity adsorbed or the surface excess is given by the thermodynamic equation Thus data on the variation of y, with pz indicates the value of p2 at which adsorption becomes appreciable and the quantity adsorbed. The type of adsorption site is more difficult to deduce but information on this can be obtained from the variation of rz with 8, the angular deviation of the surface orientation. This is obtained from the thermodynamic equationlg Data on t and ys as functions of p2 have been obtained by the following methods. 1) Twin Boundary Grooving—By determining the effect of adsorption on the torque, 7, where T is the variation of surface energy, y,, with orientation, it is possible to obtain some indication as to the preferred sites of adsorption. Experimentally, the torque value measured is the relative torque, 7/ys The twin boundary grooving technique suggested by Mykura&apos;&apos; was used in this study to determine near the three low-index orientations— (loo), (110), and (111). Mykura&apos;s equation relates 7 /yS to measurements of the di-

Jan 1, 1967

By Robert Maes, Robert de Strycker

The solidifzcation reactions in the Cu-Sn-As system were determined by microscopic examination, thermal analysis, and X-ray diffraction. The system presents no ternary compound. There is a quasi-binary section, of a simple eutectic type, between the compounds Cu5As2 and SnAs; the system presents, in addition, one ternary eutectic reaction, one ternary peritectic reaction, and seven transitional reactions. The temp-peratures corresponding to each of these reactions were determined, most of them with an accuracy of *lLC. The isothermal lines of the liquidus surface were also established for almost the entire diagram. NO reference was found in the literature relative to the Cu-Sn-As phase diagram and this is believed to be the first study on this subject. The Cu-Sn diagram was taken from Hansen and Anderko;&apos; it is represented by Fig. 1, with the phase designation which will be used in the remainder of this work. For the Cu-As diagram, the solution proposed by Hansen and ~nderko&apos; must be modified to take account of recent data, principally from Heyding and Despault~ and from Hume-Rothery and Burns; this yields the diagram represented by Fig. 2. As for the Sn-As diagram, it is not established with certainty, particularly so far as concerns the solid solubility of tin in arsenic and the solidification reactions near the compound SnsAsz. For this last point, Hansen and Anderko propose two solutions: congruent melting of Sn3Asz with a eutectic SnsAsZ + SnAs or incongruent melting implying a peri-tectic reaction L + SnAs = Sn3As2. Microscopic examination of the few binary alloys prepared in this composition range made us prefer the second of these solutions, which gives the diagram shown by Fig. 3. EXPERIMENTAL METHODS The experimental techniques used in this work were microscopic observation and thermal analysis; a few X-ray diffraction patterns were taken to verify the

Jan 1, 1967

By Robert Maes, Robert de Strycker

The Cu-Sn-As systeM was studied in the region near the Cu-42 and (214-As binary diagrams, where reactions in the solid state appear, resulting from the decomposition of the y(Cu-Sn) phase and from the formation of the 7 phase (Cu,As). The techniques used were microscopic observation, thermal analysis by dilatometry, and X-vay diffraction. The formation of the 7 phase gives rise to a ternavy pevitectoid veaction; the decomposition of the y phase gives rise to five transitional reactions. The temperatures of almost all these reactions could be determined; in the most favorable cases , the accuracy of this determination was of 11.5-C. The 7 phase is stabilized by tin additions, the arsenic atoms being replaced by tin atoms up to 35 pct; this has allowed the preparation of pure j) phase and the confirmation, by extrapolation, of the conrposition of this compound in the Cu-As diagram. In the first part of this work, the solidification reactions in the Cu-Sn-As phase diagram were studied. In the copper corner, the structure of the alloys presented the evidence of reactions in the solid state: on the one hand, all the alloys containing the y phase of the Cu-Sn diagram showed, under the microscope, that this phase had formed different decomposition products after complete solidification; on the other hand, the appearance of the 7 phase of the Cu-As diagram necessitated the introduction of a peritectoid formation reaction. The study of the decomposition of the y phase has been done by preparing about forty alloys that were homogeneous y at high temperature. The formation of the 7 phase has been studied by means of a few alloys with a composition near the homogeneity field of this phase at room temperature. The part of the Cu-Sn phase diagram of interest for this study is represented by Fig. 1, with the phase designation which will be used in the remainder of this paper; it is drawn after Hansen and Anderko.&apos; The Cu-As diagram has already been presented in Part I of this work; the significant features of this study are the existence of the arsenides CusAs and Cu5Asz, and the formation of a compound CUEAS, designated as the 7 phase, by a peritectoid reaction at about 325°C. EXPERIMENTAL METHODS The fundamental technique for the investigation of this part of the Cu-Sn-As constitution diagram was microscopic observation; the greatest part of the observed alloys has also been subjected to thermal analysis by dilatometry; a few selected alloys have then undergone an X-ray analysis by powder diffraction. Alloy Preparation. The alloys were prepared from the same products as in Part I of this study: cathode copper, arsenic with a purity better than 99.5, and tin with a purity of 99.98. The fusion of the ternary alloys was realized from

Jan 1, 1967

By P. G. Shewmon, H. E. Collins

We have studied the effect of adsorbed sulfur on the surface self-diffusion of copper using eight diflerent surface orientations and the grain boundary grooving method. The eight orientations studied were the four lying near the low-index surfaces—(loo), (Ill), and two directions in the (110)-plus four higher-index surfaces. Surface-diffusion measurements were made over a range of HZS concentrations (in Hz) from 3 to 1500 ppm between 830°and 1050°C. The results can be divided into two groups—Group 1 contains the two (110) surfaces while Group 2 contains the remaining six surfaces. In Group 1, increasing the temperature increases the effect of Hz S on DS for the Hz S range 5700 ppvn. Qs and Do increase with increasing H2S concentration in this Hz S range. Beyond this range, increasing the temperature decreases this effect on D,; also Q, and Do decrease. In Group 2, increasing the telnperature decreases the effect of H2 S on D, for the H2S range studied, and Qs and Do decrease with increasing Hz S concentration. In any study of surface phenomena, there invariably arises the question of the possible presence of and effect of adsorbed impurities. Such questions are well-founded since the presence of adsorbed atoms can sometimes produce marked changes in the kinetics of surface-energy-driven processes. In the last few years, values of the surface self-diffusion coefficient, D,, have been determined on a variety of metals by studying the decay of scratches or the growth of grain boundary grooves.L~3-L0~L3 Yet there has been relatively little work done in which the concentration of an adsorbed impurity was systematically varied and the effects observed. Work of this sort would provide some basis in fact for the assertions often made about the ro1.e of adsorbed impurities in the differences between the results of different workers in different atmospheres and on different metals. It also is relevant to those cases in which surface monolayers produce profound effects in commercially important processes. The most marked example of such effects is the ability of nickel or palladium to increase the sintering rate of tungsten by many orders of magnitude.&apos; The aim of this work was to study the effect of sulfur partial pressures on the surface self-diffusion of copper. It was felt that this in conjunction with a study of the degree of adsorption and type of active sites involvedL8 would provide a wide range of data for one system and hopefully lead to some insight into the mechanism by which sulfur adsorption influences copper diffusion. The main reasons for choosing the Cu-S system were, first, faceting was reported not to accompany the adsorption of sulfur. This is required if our experimental technique is to work. Second, Oudar has determined a high temperature adsorption isotherm for this system, an event which puts the Cu-S system almost in a class by itself.I4 EXPERIMENTAL PROCEDURE Initially, we considered studying the effect of an adsorbed impurity on surface self-diffusion of copper using isolated (or single) scratch smoothing as the technique and oxygen as the impurity. Copper was chosen as the material because the effects of orientation and anisotropy of the surface self-diffusion coefficient, D,, of copper in a dry hydrogen atmosphere had been studied extensively by Gjostein&apos; and by Shewmon and ~hoi.~,~ The isolated scratch technique was chosen because both the effects of surface orientation and anisotropy of D, in a given surface could be easily studied with this method.~ Oxygen was tried as the impurity because Robertson and Shewmon""~ had studied its adsorption on copper at 1000°C over the range of oxygen partial pressures of 10"22 to 10-l3 atm. After several preliminary runs, it became evident that neither the scratch technique nor the impurity oxygen would be satisfactory for this work. Scratching deforms an annealed surface so that the region near the scratches recrystallizes, thereby disrupting the scratch profiles. One can avoid this by deforming the specimen sufficiently before scratching to give complete recrystallization on subsequent heating.4 However, as a result of Gjostein&apos;s success in scratching and annealing undeformed gold single crystals without local recrystallization,13 we attempted something similar with copper single crystals using a 0.7-mil diamond phonograph needle mounted in a Tukon hardness tester. All specimens recrystallized upon being annealed. Also, some copper specimens were sent to Gjostein to be scratched using his technique. The results were the same. As a result, the scratch technique was dropped in favor of the grooving of symmetric grain boundaries. Preliminary work using oxygen showed that faceting began to occur before oxygen adsorption had any measurable effect on D, at 938°C (at Pbo/P, = 0.12). Since heavy faceting would interfere with the measurement, we decided to use a sulfur-containing atmosphere (H2S/H2). Work by Oudar and Benard&apos; and Robertson" showed that sulfur absorbed on copper and that faceting was not observed.

Jan 1, 1967

By Richard R. Zupp, David A. Stevenson

An experimental method to determine the carbon activity in various solid solutions was developed. Samples of the solid solutions and an Fe-C reference sample were equilibrated with respect to carbon content by annealing them in a Hz-CHI gas mixture in a closed cell. The carbon content of each sample was determined, and the carbon activity was obtained from the carbon content of&apos; the reference sample and well-established data for the dependence of the carbon activity on the carbon content in Fe-C alloys. The influence of vanadium on the activity of carbon in austenitic Fe-C-V alloys at 1000°C was determined by this technique. A general semiempirical correlation was developed to describe the dependence of the activity coefficient of- carbon on the composition of ternary austenitic iron-base alloys containing interstitial carbon and a substitutional solute. The correlation is particularly useful in predicting the partitioning of- carbon between various alloys. THE influence of substitutional solutes on the activity of interstitial solutes in metallic solid solutions is important in the theory of alloy phases. Solid solutions of particular interest are the fcc austenite phases of ternary Fe-C-Z systems, in which carbon is the interstitial solute and Z represents any substitutional solute. Carbon-activity data are also needed in these solid solutions to solve practical problems; the quantitative treatment of diffusion-controlled transformations&apos; is an examvle. Experimental information is available for ternary austenitic solid solutions containing Mn,2 Si,2 and A16 as the substitutional solute. Because qualitative preliminary studies indicated that vanadium appreciably decreases the carbon activity,14 the present investigation was undertaken to determine the influence of vanadium on the activity of carbon in austenite. Although Flender and ever" measured carbon activity over a range of compositions in the Fe-C-V system, they were primarily interested in determining phase boundaries in the ternary system, so most of their measurements were outside the composition range for stability of single-phase austenite. Petrova and Shvartsman&apos; also made limited measurements of the carbon activity in Fe-C-V alloys. The dependence of the carbon activity on the carbon content of an alloy may be determined by passing COCOz or H2-CH4 gas mixtures of carefully measured composition over the alloys, determining their equilibrium carbon content, and utilizing the relevant equilibrium relationships. smith16 used this technique with both CO-COZ and HZ-CH4 gas mixtures to determine the dependence of carbon activity on carbon content in pure Fe-C alloys. His data, which are in good agreement with those of some previous and subsequent investigators,6&apos;17 but not with those of others,lfl&apos;ao are usually considered to be the most reliable. Although the same method can be applied to Fe-C-Z alloys, it is difficult experimentally, because the appropriate gas mixtures are almost pure CO or Hz. A simpler technique is to simultaneously equilibrate the Fe-C-Z alloys and pure Fe-C alloys with the gas mixtures, and then use Smith&apos;s data to determine the carbon activity in the pure Fe-C alloy. A number of investigators have employed this technique. others Have used the partitioning of carbon at the interface of a diffusion couple prepared from an Fe-C alloy and a Fe-C-Z alloy. In the present study, a closed-cell method was developed by which carbon was selectively transferred via a gas medium between pure Fe-C alloys and Fe-C-V alloys which were not in physical contact. A similar method was developed independently by Heckler and winchel14 and used to study the Fe-C-Ni system. EXPERIMENTAL METHOD A schematic diagram of the experimental arrangement is shown in Fig. 1. In a typical experiment, a 5-g Fe-C sample was placed in one compartment of a quartz cell, and a 5-g Fe-V sample was placed in each of the other compartments. The cell was evacuated, outgassed, backfilled with approximately 125 Torr of hydrogen, and sealed. After being placed in a fur-

Jan 1, 1967

By Robert K. Steunenberg, Irving Johnson, James B. Knighton

The activity coefficient of plutonium in liquid magnesium, over the temperature range 650° to 800°C, was obtained from measurements of the distribution of plutoninm between a 50 mole pct MgC12-30 mole pct NaCl-20 mole pct KC1 molten-salt mixture and liquid Zn-Mg alloys. For dilute solutions (0.08 at. pct Pu) the activity coefficient of plutonium was found to vary from 10.1 at 650°C to 12.2 at 800°C. The activity coefficients of plutonium in dilute liquid solutions of plutonium in uranium, silver, lanthanum. cerium, and calcium were estimated to be. The distribution data indicate a value of about 0.1 at 800°C for the activity coefficient of PuCl3 dissolved in the above ternary salt mixture. LIQUID magnesium and several liquid alloys of magnesium with metals such as zinc and cadmium have been shown to be useful solvents in pyrochemical processes for the recovery of uranium and plutonium from discharged nuclear fuels,&apos; and for the separation of transuranium elements.&apos; The present study was undertaken to determine the activity coefficient of plutonium in liquid Pu-Mg alloys in support of process-development work. The activity coefficient of plutonium in liquid magnesium was determined from experimental data on the distribution of plutonium between a liquid ternary MgC12-NaC1-KC1 salt mixture and various liquid Zn-Mg alloys. The distribution data were used to calculate the ratio of the activity coefficients of plutonium in liquid zinc and in liquid magnesium. The activity coefficient of plutonium in liquid magnesium was then computed from the known activity coefficient of plutonium in liquid zinc. It was not necessary to know the thermodynamic properties of the molten-salt system explicitly. The major features of the Pu-Mg system have been reported by Schonfeld.3 At the temperatures of interest in the present study, i.e., above about 600°C, the phase diagram indicates the existence of a wide liquid-miscibility gap, with the plutonium-rich liquid containing about 8 at. pct Mg and the magnesium-rich liquid containing about 10 at. pct Pu at the intersection with the solidus regions. Additional data on the compositions of the two equilibrium liquid phases obtained in this laboratory4 have defined the miscibility gap up to the consolute temperature (at about 1040°C). EXPERIMENTAL PROCEDURE AND RESULTS Materials. The 50 mole pct MgC12-30 mole pct NaC1-20 mole pct KC1 salt mixture was prepared by melting the required proportions of reagent-grade NaCl and KC1 with anhydrous MgC12. The molten salt was then purified by contacting it with liquid Cd-30 wt pct Mg alloy (at 450°C) to reduce oxidizing impurities, followed by filtration through a stainless-steel frit (pore size, 65 µ) to remove solid MgO formed during the reduction. The purity specifications of the zinc, magnesium, and plutonium were 99.999, 99.8, and 99.85 pct, respectively. Apparatus. The liquid salt and metal were contained in a tantalum crucible inside a graphite secondary vessel. The crucible assembly was located inside a resistance-heated stainless-steel furnace tube. The furnace tube was closed by means of a stainless-steel cover, which was attached by bolts, with a neoprene O-ring serving as a gas-tight seal. The top of the furnace tube was water-cooled to protect the O-ring. The furnace-tube cover was provided with a tantalum thermowell, a tantalum stirrer, and a port through which sampling tubes could be inserted and materials could be added to the melt without admitting air to the furnace tube. Vacuum and an argon atmosphere were available through a side-arm on the furnace tube. The furnace temperature was regulated by a proportional controller that was actuated by a chromel-alumel thermocouple between the furnace tube and the heating elements of the furnace. The melt temperature was measured by means of a chromel-alumel thermocouple in the tantalum thermowell. The accuracy of temperature measurement was ±3°C. The salt and metal phases were intermixed by a motor-driven tantalum paddle positioned at the liquid interface. The tantalum crucible was provided with four baffles to increase the turbulence. The sampling tubes consisted of 1/4-in.-OD tantalum tubing that terminated in a tantalum frit (Kawecki Chemical Co.; average pore size, 30 µ). Procedure. The zinc, magnesium, plutonium, and salt were charged to the tantalum crucible; then the system was evacuated and filled with argon. The melt was brought to the desired temperature, and agitated for 1 to 2 hr. After allowing the salt and metal to separate, both phases were sampled. Filtered samples were obtained by immersing the end of the sampling tube in the liquid and increasing the argon pressure sufficiently to force the liquid salt or metal through the frit into the tantalum tube. The sample was then partially withdrawn into the cooler portion of the furnace tube and permitted to solidify before being removed. The temperature sequence for sampling at each magnesium concentration was 800°, 700°, 600°, 650°, and 750°C. The composition of the liquid-metal phase was varied by incremental additions of magnesium in a series of experiments at low magnesium

Jan 1, 1967

By P. Rama Rao, D. H. Sastry, T. R. Anantharaman

Deformation (a) and twin (a&apos;) stacking-fault densities in cold - wor ked filings of fcc silver alloys containing 2, 4, and 6 wt pct Sb have been estimated from Debye-Scherrer peak shifts and asymmetries, respectively. Evidence has been obtained for a possible strain-induced transformation in a two-phase alloy containing 9.0 zut pct Sb. Using Fourier analysis of X-ray line profiles, the effective particle sizes and root mean square strains have been determined for the three fcc alloys in the cold-worked condition. The values of the compound fault probability 0.5a + a&apos;) evaluated from peak shifts and asymmetries are in reasonable apeement with those derived from peak broadening. COLD work of fcc metals may produce both deformation and twin (also called growth) stacking faults, which can be detected and quantitatively estimated by X-ray diffraction techniques.&apos; In addition to peak broadening, deformation faults produce a shift in peak positions and twin faults an asymmetry of the Debye-Scherrer reflections. Besides stacking faults, a reduction in the size of coherently diffracting domains and distortion within these also broaden the powder reflections of deformed fcc metals and alloys. Fourier analysis&apos; of peak shapes provides quantitative infor- mation about the effective domain sizes, lattice strains, and also the compound fault probability (1.5a + a&apos;), where a and a&apos; represent deformation-and growth-fault density, respectively. The Paterson method2 for determination of a from peak shifts, the warren3 or wagner4 method for evaluation of a&apos; from peak asymmetries, and the Fourier analysis for quantitative estimates of all the contributory causes of peak broadening have, in the course of the last decade, been extensively applied to obtain data for a number of deformed fcc metals and alloys. One of the useful results of earlier measurements of a in several solid solutions is a correlation between a and the solute valence as well as electron concentration per atom (p) in alloy systems based on a particular solvent. The work of Smallman and westmacott5 on Cu-Zn, Cu-A1, and Cu-Sn, of Foley, Cahn, and ~aynor&apos; on Cu-Si and Cu-Ge, and of Rama Rao and Anantharaman7 on Cu-Si and Cu-Sb has revealed a common trend in the increase of a with p and also a with valency of the solute. Cahn and Davies&apos; and Ad-ler and wagnerg have observed similar trends for silver alloys containing cadmium, indium, and tin. Data on a for silver alloys with a pentavalent solute element are not, however, available. It is primarily to fill this need that the present investigation on Ag-Sb alloys was undertaken. Utilizing the Patersonand Warren methods, values of a and a&apos;, respectively, have been determined in three silver alloys containing 2, 4, and 6 wt pct Sb. By Fourier analysis of the broadening of Debye-Scherrer peaks, effective particle sizes, lattice strains, and the compound fault probability (1.5a +a&apos;) have also been evaluated.

Jan 1, 1967

By K. R. Waugh, Barbara S. Brown, D. W. James

AN electronic data-processing system is described which permits rapid, accurate, low-cost processing of strain-dependent damping data utilizing equipment normally available within the service facilities of most large laboratories. On analyzing the record of a stress-dependent damping test, the operator usually measures the double amplitudes at several points on the decay curve. The logarithmic decrement is then calculated for decay between consecutive amplitudes. These values of 6 are plotted against the corresponding maximum surface shear stress, T, which is proportional to the average of the two amplitudes between which is calculated: where d is the specimen diameter. The period of the vibration is not necessarily constant during decay; thus, each cycle must be counted. A decay curve may extend to, perhaps, 1000 cycles, and at least two curves are always obtained for each specimen or set of conditions. It can, therefore, be seen that manual analysis of decay curves is both tedious and costly in terms of man-hours. Furthermore, the resolution of the record is often such that accurate measurement of amplitude is extremely dif-

Jan 1, 1969