By O. D. Gonzalez

Existing measurements for the steady-state permeation of hydrogen in a iron above 100°C have been examined for contribution of determinate errors. The analysis leads to a recommended equation for the permeability of hydrogen in a iron: o= (2.9 ±0.5) x 10-3 exp - (8400 ± 400)/RT cu cm (ntp H2) cm-1 sec-1 atm-1/2 THE permeability of a iron to hydrogen has been the subject of numerous investigations over the past 40 years, and at present there are thirteen sets of published results for the rate of steady-state permeation of hydrogen in a iron above 100°C. The numerical values in each set of results are entirely self-consis-tent, but the spread among the sets is too large to be attributed solely to experimental error, i.e., to error other than in the specimen itself. Several reasons have been advanced to explain the disparities, but to date the relative importance of experimental inaccuracy to the spread remains uncertain. The purpose of this report is to examine in detail the sources of determinate errors inherent in the experiments and to assess as far as possible the contribution of the errors to the results. The ultimate goal is the selection of values for the permeability and heat of permeation most nearly representative of hydrogen in a iron. The analysis is limited to those experiments in which the permeation rate was observed at steady state—a condition in which traps for hydrogen within the metal are filled to a fixed level15 so that the trapping mechanism is not reflected in the rate of passage of the gas. Furthermore only data are examined in which surface processes are judged to have little or no influence on the flow. It is hoped with these restrictions to obtain values of the permeability and the heat of permeation which will be as closely related as possible to the mechanism of lattice diffusion. I) DEFINITION OF TERMS; UNITS In this report the data for permeation are given in terms of a coefficient oj permeability, ?, which is defined by the equation: jt=?A/?x{p1/2-po1/2) [1] where jt is the total flow of gas normal to the surface of a membrane of planar geometry, e.g., a disc, of area A and thickness ?x; pi and po are the pressures in the input and output sides, respectively. For flow radial to the walls of a membrane of cylindrical geometry, e.g., a tube, the corresponding equation is: where 1 is the length of the cylinder, and ri and ro are the inner and outer radii, respectively. The flux normal to the surface is given by Fick's law: j= -D(dc/dx) [3] At steady state the concentration gradient will be constant, and integration of Eq. [3] gives for the total flow through a disc of area A and thickness Ax: h =-DA(co - ci) [4] where c, and ci are the concentrations of solute at the output and input surfaces, respectively. When surface control is absent, co and ci are given by Sievert's law c = Kp1/2, and substitution therewith into Eq. [4] gives directly Eq. [I] where ? = DK. Integration of Fick's Eq. [3] in cylindrical coordinates will give Eq. [2] where again ? = DK and is thus shown to be independent of geometry (provided that surface control is negligible). The coefficient of permeability, or simply the permeability,* must be expressed in proper units. In *The term permeability will refer in this report always to the coefficient defined above; permeation will be used to specify the general phenomenon of gas passage through a membrane. this report ? will be expressed in the units of cu cm (ntp H2) cm-1 sec-1 atm-1/2. The variations of D and K with temperature are given by D = Do exp(-Ea/RT) and K = KO exp(-?Hs/RT) where E, is the activation energy for diffusion and AH, the heat of solution, each usually expressed in calories per mole of solute. The variation of permeability with temperature will thus be given (for conditions where surface control is negligible) by ? = ?o exp(-?Hp/RT) where ?0 = DoKo and ?Hp = Ea + ?Hs. The units of ?0 are the same as those of 6, and??Hp will be expressed in calories per mole H. 11) SUMMARY OF PERMEABILITY RESULTS Table I gives the values reported to date for the permeability of H2 in a iron in terms of ?o and ?Hp. Except where noted the parameters listed were taken directly from the numbers reported by the various investigators with only a change in units. The temperature limits within which the listed ?o and ?Hp hold are given in column 7; the limits marked in parentheses in this column indicate the entire temperature range covered in each investigation. The listed values of ?o and ?Hp are those giving a linear plot of ln? against T-1 at the higher temperatures in each set of measurements, and thus presumably represent the case for which surface control was negligible. Column 6 gives values of 9 at a representative tem-

Jan 1, 1970

By C. Feng, W. E. Krul

A study was made of the development of texture and the anisotropy in plastic flow of Ti-8Al-1Mo-1V alloy. Based on Pole figure determinations, the shifting of texture induced by rolling at approximately 400°C was found to be due primarily to slip rotation for the major Portion of the material. Grain boundary shear is believed to be an important factor. The anisotropy of the textured alloy was examined in terms of the variations of yield stress under tension and the ratio of bi -axial strain increments µp, in the temperature range 25" to 290°C. The results were related to Hill&apos;s theory on plastic anisotropy. The Schmid factors of (1100)[1120], (1101)[1120/, and (1101)[1120] slip systems were analyzed and found to be compatible with the observed anisotropy. Cross-slip between these planes was proposed as a possible deformation mode. In a number of published articles, considerable interest has been directed to the possible achievement of texture hardening in hcp metals. Following Backofen, Hosford, and Burke,&apos; this phenomenon was related to the yield criteria of the material and was expressed in terms of the biaxial strain ratio, r = d?w/d?l. The higher the value of r, the greater is the expected potential for texture hardening under certain loading conditions. For a given material, r varies with direction. Such variation can be traced to the anisotropy in plastic flow and can be explained within the framework of the various modes of deformation. Hatch2 found that a high r value coincides with a texture whereby the (0001) pole is closely aligned with the surface normal for sheet materials, Based on the analysis of the slip on the {1010}, {1011}, and (0001) planes, Lee and Backofen3 and Avery, Hosford, and Backofen4 concluded that the resistance to thinning is reduced by the operation of the (0001) <1120> slip system; with this reasoning they were able to explain the low r values (i.e., r « 1) observed in magnesium alloy sheets in the rolling direction and in commercially pure titanium in the transverse direction. The general equation, dealing with plastic flow in a polycrystalline aggregate has been used to correlate the plastic anisotropy and texture. In this expression, T and s are shear and normal stresses, and dri and d? are shear and normal strain increments, respectively. Assuming that five slip systems are operative within each grain and applying the principle of maximum work,5,6 one can determine the m value among the available systems. On this basis, Hosford7 and Chin, Nesbitt, and Williams&apos; were able to correlate m with yield stress under plane-strain compression, and Svensson9 was able to predict the variation of yield stress in textured aluminum. These workers made their analyses from materials in which slip operation is known to be associated with plastic flow. Questions remain regarding the derivation of Hill&apos;s theory on plastic anisotropy,10,11 since it was formulated on von Mises&apos; yield criterion.&apos;&apos; Its ability to deal with other forms of deformation has been in doubt.13 Others have discussed the validity of Hill&apos;s quadratic equation relating strain and yield stress.14&apos;15 For hcp titanium, deformation by various modes of slip and twinning operations has been reported.16-20 If all possible modes of deformation operate and contribute substantially to the plastic flow, it is difficult to imagine how the quadratic expression can suitably describe the anisotropic plastic flow of titanium alloys. Backofen and Hosford15 considered that Hill&apos;s is a macroscopic theory and implied that the major mode of deformation by slip mechanism will adequately describe anisotropy of the material. In the present investigation, slip operation will be shown to play the major role in the development of sheet texture induced by rolling of a commercial titanium alloy. Although twinning and other modes of deformation may also operate, their operation is believed to be secondary. The anisotropic properties of the sheet, which can be expressed in terms of directional variation of r, µp = -d?w/d?l and the yield stress will be shown to be governed primarily by slip operation. MATERIALS AND EXPERIMENTAL TECHNIQUES The titanium alloy chosen for the present investigation had a nominal composition of 8 wt pct Al, 1 wt pct Mo, 1 wt pct V, and 0.1 wt pct interstitial impurities. Sheets varying between 0.1 and 0.15 in. thickness were used. The alloy was received in a condition which was prepared by rolling at 900°C and annealing at 700°C. Subsequently, the sheets were subjected to further reduction in thickness by rolling at 400°C. A total reduction in thickness of 65 to 70 pct was obtained by a series of quick passes in a rolling mill with intermediate reheating. Further reduction in thickness was not possible due to cracking developed at the edges of the sheets. X-ray measurements were conducted in a Siemens and a Norelco unit to determine the texture of the sheets. Reflection techniques were used exclusively with CuK, radiation and a nickel filter. The loss of X-ray intensity due to geometric defocusing was calibrated with a technique described previously." The (0001), (1010), and (1071) pole figures were plotted from 0 to 80 deg, and to present the texture elements quantitatively, inverse pole figures were constructed following the technique described by Jetter, McHargue, and Williams.22 Tensile experiments were carried out at 25", 175",

Jan 1, 1970

By C. J. McHargue, J. C. Ogle

Lightly deformed columbiun single crystals which contained only parallel hoins or purullel and intersecting trains were annealed at 1000&apos; and 1600"C. No re-crystallizntion occurred in specimens hawing only parallel twins. Only noncoherent twin boundaries nzipated at 1000°C but both coherent and noncoherent ones moved al 1600°C. Recrystallization occurred within a few minutes at twin intersections at 1000°C. The orientation 01 the recrystallized grains differed front that of both the matrix and deformation twins, but could he derired by (110) and/or(112) rotations. ALTHOUGH twinning in metals has been extensively studied, there have been no definitive studies of the annealing behavior of crystals containing deformation twins. Some effects observed after annealing deformation twins have been summarized by Cahn1 and Hall2. Any or all of these phenomena are observed: 1) The twins may contract so that the sharp edges of the lens become blunted, and eventually the twin may disappear entirely. 2) The twins may balloon out at an edge, giving rise to a large grain having the same orientation as the twin. 3) The specimen may recrystallize; i.e., new grains are nucleated and grow at the expense of the twins and the crystal immediately adjoining the twin. Such grains have orientations which are not present before. Contraction has been observed in iron,3 titanium,3, 4 beryllium,5 zinc,8, 7 Fe-A1 alloy,&apos; and uranium.9 Long anneals at high temperatures are required to have any appreciable effect in these metals and only thin twins are absorbed. Lens-shaped twins are absorbed from the edges: the thin, almost parallel-sided twins are usually punctured in several places and each piece contracts independently. Absorption is very gradual and no sudden cooperative jumps have been observed. The expansion of a twin into a larger grain of identical orientation is unusual, but such growth has been observed in iron,"&apos;" zinc,6 and uranium." Crystals which have been deformed simultaneously by slip and twinning recrystallize first in the area adjacent to the twin. New grains appear faster where the twins intersect: but isolated twins, especially if thick, can also give rise to new grains. This type of recrystallization occurs in zinc.6, 7, 12, 13 and beryllium.14 Reed-Hill noted, in a single crystal of magnesium, the nucleation of a recrystallized grain at a twin intersection which had the same orientation as the second-order twin and which grew into the highly strained matrix.15 Short-time annealing has been reported to cause no change in the deformation twins in vanadium,16 columbium, 17, 18 tantalum,19 tungsten,&apos;&apos; and zinc.7 The purpose of this investigation was to note the effects of annealing on the coherent and noncoherent boundaries of deformation twins in columbium and to locate the nucleating sites for recrystallization. The orientation relationships, which the new recrystallized grains have with the parent crystal and the deformation twins, were also determined. EXPERIMENTAL PROCEDURE Single crystals of columbium were obtained by cutting large grains from electron-beam-melted buttons which contained 10 to 50 ppm C, 10 to 100 ppm O,, 1 to 10 ppm H2, and 10 to 15 ppm N2. The crystals were hand-ground and chemically polished until all grain boundaries were removed. The specimens were mounted in an epoxy resin and a face of each crystal was mechanically polished on a Syntron polisher using Linde A and then Linde B polishing compounds. After all faces were mechanically polished, the crystal was electrolytically polished to remove all distortion due to cutting and grinding. Laue photographs were taken of all faces of the crystals to determine the quality and orientation of each crystal. The crystals were compressed about 10 pct at -196 C in a specially constructed compression cage with an Instron tensile machine. Each crystal was separated from the top and bottom anvils by teflon films which acted as a lubricant. With the specimen crystal in position, the entire cage was cooled to -196°C by being submerged in a Dewar containing liquid nitrogen. The crystals were compressed at a rate of 0.02 in. per min and the load was recorded on a strip-chart recorder. After deformation the crystals were mechanically polished on 600-grit paper and Pellon cloth with Linde A and Linde B polishing compounds. The crystal faces were chemically polished and then etched. The twin planes were identified metallographically from an analysis of the twin traces on two surfaces. Annealing was carried out by placing each crystal in a columbium bucket made from the same electron-beam-melted material as the crystal itself and suspending the bucket by a tantalum wire in a quartz tube. After a vacuum of 10-7 Torr was attained, a furnace at 1000" or 1600 C was raised into position and the crystals held for various lengths of time. The crystals were repolished and etched after annealing to remove any surface contamination. Approximately 0.010 in. was removed during this process. The resulting surface was examined metallographically for microstructural changes due to annealing. A microbeam Laue camera mounted on a Hilger Micro-focus X-ray unit was used to determine the Orientstions of the recrystallized grains. This X-ray micro-beam camera had a 0.002-in.-diam collimator and incorporated the ideas of both and and chisWik21 and Cahn.22

Jan 1, 1967

By Donald Warren, J. F. Libsch

HIS investigation originated as a result of a pre-vious experimental study&apos; of the magnetic properties of Fe-Co alloys fabricated by the powder metallurgy technique. Densities of powder compacts prepared for the magnetics investigation varied from 7.45 to 7.70 g per cu cm or from 93 to 95 pct of the experimental value of 8.08 g per cu cm for a fused alloy of the same composition.&apos; While this range of density is considered sufficiently high for most applications, the highest possible density is to be desired for maximum magnetic properties. By applying a technique similar to the one described above to a pure electrolytic iron powder, Rostoker³ was able to achieve a density of 7.895 g per cu cm, which is the highest density ever reported for sintered iron. While Rostoker&apos;s work involved the sintering of an elemental powder rather than a mixture, it was believed that higher densities should also have been obtained for alloys using the above technique because of the recoining operation and the high sintering temperature. Consequently, it was decided to investigate the various factors affecting the density of this alloy with the idea that such a study might lead to higher densities and, as a result, powder alloys having magnetic properties identical with those of the fused alloys. It was believed that the principal reason that near-theoretical densities for the powdered alloy were not obtained was the interference of gases with the normal sintering mechanism. When present during the sintering operation, gases can exert several harmful effects: they can remain on the particle surface and interfere with surface diffusion and plastic flow; they can be released and, under certain conditions, expand the void spaces through gas pressure; or they can remain trapped in the pores and exert a hydrostatic pressure that retards elimination of the pores. Jones,4 Rhines,5 Goetzel," and others have given the effect of gases in the sintering of powder compacts an extensive treatment. Among the more important sources of gases in the sintering process are dissolved gases, adsorbed gases, air entrapped during pressing, and gaseous products of chemical reactions. During sintering adsorbed gases are partly released at a relatively low temperature, while those gases entrapped during pressing cannot escape until their pressure is increased sufficiently through increasing temperature to expand the interpartjcle openings. The remaining adsorbed gases, gaseous reduction products, and dissolved gases produce a similar effect at the higher temperatures. If, in the sintering process, gas evolution occurs after the interpore channels have been sealed, an exaggerated expansion of the void spaces results. This is particularly true if the temperature is high enough for extensive plastic flow. In his fabrication of powder bars from tantalum, Balke7 had to consider the effect of adsorbed hydrogen and provide for its escape during sintering by limiting the compacting pressure to a maximum of 50 tons per sq in. The effect of gases entrapped during pressing was first noted by Trzebiatowski8 when he found that gold and silver powders decrease in density with increasing sintering temperature if pressed at 200 tsi, while they exhibit the usual increase when pressed at 40 tsi. Recent investigators9-11 have also noted that entrapped gases have an effect on the expansion of copper compacts during sintering. Proper provision for the escape of gaseous products of reduction must be made in order to avoid deleterious effects. Myers" states that in the sintering of electrolytic tantalum powder, the temperature was gradually raised to 2600°F with a pause at 2000°F to permit reduction of the oxides. Experimental Details For the present study, 50 pct Co-50 pct Fe compacts in the form of circular disks 1½ in. in diam and 0.15 in. thick were fabricated by the pressing and sintering of a mixture of the elemental powders. It was decided to follow the sintering process by means of liquid permeability measurements, because it was thought that such measurements might serve as a measure of relative pore sizes, as well as a possible indication of the point at which most of the interpore channels become sealed. However, since the permeability as measured by the flow of a liquid, such as ethylene glycol, does not give an absolute indication of the point where the pores have become isolated, a method for determining the percentage of pores connected to the surface was set up. As an additional cross check on the permeability measurements, metallographic methods were used to study the relative pore size. Finally, the property of ultimate interest, the density, was measured. Raw Materials: The powders used consisted of an annealed, 99.9 pct pure, —150 mesh grade of electrolytic iron powder, and a 98 pct pure, —200 mesh grade of reduced and comminuted cobalt powder. The cobalt powder was not further processed either by hydrogen reduction or annealing. The screen analyses for the iron and cobalt powders are given in Table I, while the chemical analyses for each type of powder are listed in Table 11. Table 111 gives the hydrogen loss measurements for the powders according to the M.P.A. Standard Method and for a higher temperature as well. Preparation of Compacts: Equal amounts of the elemental powders were mixed by rotation for 1 hr and then pressed into compacts approximately 0.15

Jan 1, 1952

By E. S. Fisher, L. C. R. Alfred

The elastic anisotropy factors, c4,/c6,, c3,/cll, and c12/cl,, for hcp metal crystals vary significantly among the dgferent unalloyed metals. Significant variations with temperature are also found. The effects of elastic anisotropy on the dislocation in an elastic continuum with hexagonal symmetry have been investigated by computing the elasticity factors for the self-energies of dislocations in fourteen different metals at various temperatures where the elastic moduli have been reported. For most of the metals the effects of the orientation of the Burgers vector, dislocation line, and glide plane are small and isotropic conditions can be assumed without significant error. Significant effects of anisotropy are, however, found in Cd, Zn, Co, Tl, Ti, and Zr. The elasticity factors have been applied in the calculations of dislocation line tensions, the repulsive forces between partial dislocations, and the Peierls-Nabarro dislocation widths. It is predicted that the increase in elastic anisotropy with temperature in titanium and zirconium makes edge dislocations with (a), (a + c), and (c) Burgers vectors unstable in basal, pyramidal, and prism planes, respectively. The probability of stacking faults forming by dissociation of Shockley partials in basal planes also decreases with increasing c4,/c6, ratio, when the stacking fault energy is greater than 50 ergs per sq cm. The widths of screw dislocations with b = (a) in titanium and zirconium increase very significantly in prism planes and decrease in basal planes as c4,/c6, increases. The effects of elastic anisotropy on various dislocation properties in cubic crystals have received considerable attention during the past few years. In the case of cubic symmetry the departure from isotropic elasticity depends entirely on the shear modulus ratio, A = 2c4,/(cl, —c12); i.e., the medium is elastically isotropic when A = 1. Foreman1 showed that an increase in the ratio A produces a systematic lowering of the dislocation self-energy for a given orientation and Poisson&apos;s ratio. ~eutonico~, has shown that large anisotropy can have a marked effect on the formation of stacking faults by the splitting of glissile dislocations in (111) planes of fcc and (112) planes of bcc crystals. ~iteK&apos; made similar calculations for (110) planes of bcc metals. Both studies of bcc metals showed that the large A values encountered in the alkali metals tend to reduce the repulsive forces between Shockley partial dislocations. In fcc metals, however, A does not vary over the large range encountered in bcc metals; consequently, the effect of A on the forces between Shockley partials is masked somewhat by the differences in Poisson&apos;s ratio between metals. The effect of A on the line tension of a bowed out pinned dislocation has also been investigated for cubic crystals, first by dewit and Koehler5 and more recent- ly by Head.6 In both cases the line energy model is applied and the core energy is not taken into account, thus making the conclusions somewhat tenuous with regard to the physical interpretation. Nevertheless, the fact that a large A decreases the effective line tension is clearly evident and the tendency for large A to produce conditions that make a straight dislocation unstable (negative line tensions) also seem evident. Head, in fact, shows visual microscopic evidence that stable V-shaped dislocations occur in 0 brasse6 For hcp metals the definition of elastic anisotropy is more complex and, furthermore, significant deviations from an isotropic continuum are found among a number of real hcp metals, especially at higher temperatures. The present work was carried out to survey the effects of elastic anisotropy on the elasticity factors, K, that enter into the calculations of the stress fields around a dislocation core. Some isolated analytical calculations have previously been carried out for several hcp metals but they are restricted in the dislocation orientations and temperature.8&apos;9 The present computations are based on single-crystal elastic moduli that have appeared in the literature and consider various orientations requiring numerical computations. The results are then applied to survey the effects of temperature on the dislocation line tension and dislocation splitting in hcp metals. PROCEDURE Anisotropy Factors. The degree of elastic anisotropy in hcp crystals cannot be described by a single parameter, such as the A ratio in cubic crystals. The following three ratios must be simultaneously equal to unity in order to have an elastically isotropic hexagonal crystal: The magnitudes of these ratios at several temperatures, as computed from the existing data for the elastic moduli of unalloyed hcp metals, are given in Table I. There are no cases of complete elastic isotropy, but the large anisotropy ratios encountered in the cubic alkali metals are also missing. There are, however, several significant differences among the hcp metals, the most notable being the relatively small A and B ratios in zinc and cadmium and the differences in the magnitudes and temperature dependences of A. It has been noted that the temperature dependence of A has a consistent relationship to the occurrence of the hcp — bcc tran~formation. For cadmium, zinc, magnesium, rhenium, and ruthenium, A is less than unity at 4&apos;~ and, with exception for rhenium, decreases with increasing temperature. In the case of rhenium, A has essentially no temperature dependence between 923&apos; and 1123"~, so that it is clear that A does not approach unity at higher temperatures. Cobalt is similar to the above-mentioned group of metals in that it also does

Jan 1, 1969

By Mark J. Klein

The creep of 043 was studied over the temperature range 1650" to 3200°F and over the stress range 3000 to 44,000 psi. The steady-state creep rate over this range of stress and temperature can be expressed by the equation where A is a constant, is the stress, and is -0.8 x 103 psi-&apos;. Over a narrow range of stress variations c0 a and for this proportionality n varies from 3 to 30 in accordance with the relation n = aB. Above about 2400° F, H, the apparent activation energy for creep, is 110,000 cal per mole, a value about equal to that estimated for self-diffusion in this alloy. Below 2400°F, H increases with decreasing temperature reaching a value of -125,000 cal per mole at 1700° F. In this temperature region, H appears to be a function of the interstitial concentration of the alloy. MOST of the detailed creep studies of dispersion strengthened metals have been concerned with metals having fcc structures. However, there are a number of important refractory alloys with bcc structures that derive part of their high temperature strength from an interstitial phase and whose creep behavior has not been well defined. This paper describes the creep behavior of the bcc alloy, D43, over the temperature range 1650" to 3200°F (0.4 to 0.7 Thm) and over the stress range 3000 to 44,000 psi. In addition to colum-bium, this alloy contains 10 pct W. 1 pct Zr, and sufficient carbon (-0.1 pct) to form a carbide dispersion throughout the matrix of the alloy. The effects of variations in temperature and stress on the steady-state creep rate of this alloy are presented in this paper. EXPERIMENTAL PROCEDURES Creep tests were made in a vacuum of 106 torr under constant tensile stress conditions using a Full-man-type lever arm.&apos; Creep specimens were machined from 0.020-in. D43 sheet (grain size -5 x l0-4 in.) processed in a duplex condition (solution annealed -2900°F, 40 pct reduction in area, aged 2600°F). The specimens were tested in this condition without further heat treatment. Specimen extensions over 1-in. gage lengths were continuously recorded using a high temperature strain gage extensometer. Differential temperature and stress measurements were used to determine temperature and stress dependencies of the creep rate. Activation energies were calculated from the changes in strain rate induced by abrupt shifts in the temperature during constant stress creep tests. The 100°F temperature shifts used in most of the activation energy determinations required 15 to 90 sec depending upon the temperature at which the shift was made. The dependence of strain rate on stress was determined by measuring the change in strain rate for incremental stress reductions during constant temperature tests. It has been shown that columbium-base alloys such as D43 are susceptible to contamination by gaseous interstitial elements during vacuum heat treatments.&apos; In this regard, it is unlikely that these alloys can be heat treated without some loss or gain of interstitial elements despite the precautions taken to control the heat treating environment. However, several factors suggest that changes in interstitial concentrations of the specimens during testing did not affect the results presented in this paper. First, the dependence of the creep rate on the stress or temperature determined during the course of a single creep test showed no variations with the duration of the test. A variation would be expected if a loss or gain in interstitial concentration during the course of the test affected results. In addition, precautions taken during this investigation to minimize interstitial contamination by wrapping the gage lengths of the specimens with various foils2 (Mo, Ta, W) did not produce a detectable change in the stress and temperature dependencies relative to the unwrapped specimens. The averages of duplicate analyses for carbon and oxygen in several specimens determined before and after creep testing are listed in Table I. The combined nitrogen and hydrogen concentrations which were ordinarily less than 50 ppm did not change in a detectable way with creep testing. The analyses show that only minor changes in carbon concentration occurred during creep testing except for specimen 4. This specimen which was tested at 3100°F lost a significant amount of its carbon concentration to the vacuum environment. Specimen 1 gained 100 ppm of O, while specimens 2, 3, and 4, which were tested at progressively higher temperatures, lost increasing portions of their initial oxygen concentrations during testing. RESULTS AND DISCUSSION The Temperature Dependence of the Creep Rate. The apparent activation energy for creep, H, was de-rived from creep curves similar to that shown in Fig. 1. Steady-state creep was rapidly attained at the beginning of the test and with each change in temperature. This behavior suggests that the alloy rapidly attains a stable structure with each shift in temperature or that the structure is constant throughout the test. Since the dispersion will tend to stabilize the structure, the latter is probably the case. The activation energy was found to be independent of the direction of the temperature shift and the magnitude of the shift (50" or 100°F). Although H was approximately independent of the strain, there was a tendency for it

Jan 1, 1970

By E. T. Turkdogan, J. H. Swisher

bi the fivst part of the paper results ave given on the rate of decarburization of Fe-C melts ln CO2-CO atmospheres at 1580°C. The rate -controlling step is believed to he that irvlloluing dissociation of curbotz dioxide on the suvfuce of the melt. 4 genevral reaction mechanistm is poslnlated jor gels-t11eta1 veactions oc-curit~g on the surface of iron coutcotamncited with chemi-sovbed osygesL. Oxygen the present work on decavbuvization of liquid iron and previous studies on the kinetics of nitrogen absorption and desorplion are discussed in terms of the postulated mechanism, ManY of the early studies of rate of decarburization of liquid steel were of an exploratory nature and laboratory exppriments carried out pertained to open-hearth or oxygen steelmaking processes. References to previous work on this subject may be found in a literature survey made by Ward. Using more sophisticated experimental techniques, several investigators have recently studied the kinetics of decarburization of molten Fe-C alloys in oxygen-bearing gases. For example, Baker et al2.&apos; reported their findings on the rate of decarburization of liquid iron, levitated by an electromagnetic field, in carbon dioxide-carbon monoxide-helium atmospheres. In these levitation experiments the samples used were small in size, e.g., -0.6-cm-diam spheres weighing -0.7 g, and the rates were measured for decarburization from about 5 to 1 pct C at 1660°C. The rates obtained under their experimental conditions were considered to be controlled primarily by gaseous diffusion through the boundary layer at the surface of the levitated melt. Parlee and coworkers3 measured the rate of absorption of carbon monoxide in liquid iron. The rates were found to follow first-order reaction kinetics, yielding a reaction velocity or a mass transfer coefficient in the range 0.2 to 0.4 cm per min. The coefficient was found to decrease with increasing carbon content of the melt. These investigators attributed the observed rates to the transfer of carbon or oxygen through the diffusion boundary layer adjacent to the surface of the melt. In the work to be reported in this paper, an attempt has been made to study the kinetics of gas-metal surface reactions involved in the decarburization of liquid iron. EXPERIMENTAL The experiments consisted of melting 80-g samples from an Fe-1 pct C master alloy in an induction furnace and decarburizing in controlled CO2-CO mixtures at 1 atm pressure and 1580°C. The master alloy was prepared by adding graphite to electrolytic "Plastiron" melted in racuo. None of the impurities in the master alloy exceeded 0.005 pct. The reacting gases were dried by passage through columns of anhydrone; in addition, CO2 impurity in carbon monoxide was removed by passage through a column of ascarite. A schematic diagram of the apparatus is shown in Fig. 1. A 1.25-in.-diam recrys-tallized alumina crucible containing the sample was placed inside a 3-in.-diam quartz reaction tube, all of which was surrounded by an induction coil. A 450-kcps induction generator was used as the power source. Water-cooled brass flanges, which contained the gas inlet, gas exit, and sight port, were sealed to the top of the reaction tube with epoxy resin. The reacting gases were metered with capillary flowmeters and passed through a platinum wire-wound alumina preheating tube, 0.25 in. ID and 11 in. long. The gases were preheated to about 1300°C. A disappearing-filament optical pyrometer was used to measure the melt temperature. The pyrometer was initially calibrated against a Pt-6 pct Rh/Pt-30 pct Rh thermocouple. The temperature was controlled to within +10°C by manually adjusting the power input to the induction coil. In a typical experiment, an 80-g sample of the master alloy was melted in a CO2-CO atmosphere having pcO2/pco = 0.02 and flowing at 1 liter per min. A negligible amount of carbon was lost and no significant reduction of alumina from the crucible occurred during melting, e.g., 0.005 pct Al in the metal. After reaching the experimental temperature of 1580°C, the gas composition was changed to that desired for a particular series of decarburization experiments. The duration of the transient period for obtaining the desired gas composition at the surface of the melt was about 20 sec . The flow rate of the reacting gas was maintained at 1 liter per min. After a predetermined reaction time, the power to the furnace was turned off. During freezing, which took about 10 sec, the amount of gas evolution was not sufficient to result in a significant loss of carbon. The samples were analyzed for carbon by combustion and in a few cases they were analyzed for oxygen by the vacuum-fusion method. RESULTS A marked increase in the rate of decarburization of iron with increasing pcO2/pco ratio in the gas stream is demonstrated by the experimental results given in Figs. 2 and 3 for pco2/pco ratios from 0.033 to 4.0. In one series of experiments, denoted by filled triangles in Fig. 2, the reacting gas was diluted with argon (48 vol pct) resulting in a slower rate of decarburization. Samples from two series of experiments with pco2/pco = 0.033 and pco2/pco = 0.10 (with argon dilufion) were analyzed for oxygen. In these Samples the oxygen content increased with reaction time

Jan 1, 1968

By Y. C. Liu, G. A. Alers

The effect of rolling reduction on the textures of Cu-A1 alloys has been investigated both by pole figure and by modulus methods. In alloys which exhibit complete copper or brass types of rolling texture, the rolling reduction has little effect on the texture except to increase the degree of preferred orientation. In alloys which exhibit a transition texture, however, increased rolling reduction increases the amount of brass-type texture at the expense of the copper-type texture. The present experimental results show that there is no one-to-one correspondence between the SFE and the rolling texture of fcc metals. Additional data taken from the literature for fcc metals also support this conclusion. On the other hand, the present and previous experimental results are shown to be in good agreement with the suggestion that the texture transition occurs at a critical value for the separation distance between two partial dislocations—a consequence of the "dislocation interaction" hypothesis for texture. formation. This critical separation occurs when the parameter .r/ub is 3.75 x 10&apos;3. From this, a value for the SFE of 39 ergs per sq cm may be deduced for a Cu-2.85 at. pct A1 alloy. ThE correlation between the rolling texture of fcc metals and the stacking fault energy, SFE, was one of the first attempts to relate atomistic properties with the type of rolling texture.&apos; This correlation gives a qualitative explanation for the experimental observation that the addition of alloying elements, which generally lower the SFE, changes the copper-type texture to a brass-type texture. The simplicity of this correlation had led to its general acceptance and even its quantitative use.&apos; However, it is only a correlation and is largely based on descriptive features of pole figures, and on the poorly known SFE values in dilute alloys. Quantitative verification of this phenomenologi-cal correlation is, in fact, completely lacking. One purpose of the present study is to test this correlation. Another atomistic description for the formation of rolling texture is the "dislocation interaction" hypothesis of texture formation.3 In this hypothesis, the factor controlling the type of rolling texture depends on whether or not the separation distance between two partial dislocations exceeds a critical value. Materials having a separation of less than the critical value are supposed to exhibit a copper-type texture while those with a separation above the critical value are supposed to have a brass-type texture. At the critical value, it is expected that the material should show equal amounts of copper- arid brass-type orientations in their textures, i.e., a 50 pct transition texture. The SFE appears in this hypothesis as only one of several factors which determine the separation distance between partial dislocations. It is possible to test the validity of these two concepts by studying the rolling texture as a function of rolling reduction. Since the SFE per se is an intrinsic property of the metal, it should not, by definition, be influenced by local irregularities, such as variable stress conditions. Thus, no change in texture-type is expected to occur with changes in rolling reduction. On the other hand, according to the "dislocation interaction" hypothesis, any factor that effectively influences the separation distance of partial dislocations would be expected to change the rolling texture. Since the separation distance between partial dislocations is known to depend upon local stresses,4-6 it is anticipated that there would be an effect of the degree of reduction on the texture-type. Also, since applied stresses are more likely to increase, rather than to decrease, the separation between partials,4&apos;5 the overall effect would be to increase the amount of material in the brass-type orientations as rolling reduction is increased. Furthermore, this reduction dependence would be most prominent in alloys exhibiting the transition texture since the distance between partials in those alloys is thought to be close to the critical value. Experimental data in the literature is insufficient to distinguish between these two alternatives. Haessner studied the effect of rolling reduction on textures in a series of Ni-Co alloys by means of the X-ray intensity-ratio technique,&apos; and found that while one texture parameter indicated no reduction dependence the other indicated a slight dependence of the rolling texture on reduction in the range of 96 to 99 pct. As has been noticed previously, the intensity-ratio technique is a convenient but controversial method7 because there is no a priori reason to suggest which intensity-ratio would describe the texture most meaningfully. A more quantitative method of describing textures is found in terms of the orientation dependence of Young&apos;s modulus. Here, the type of modulus aniso-tropy associated with the copper-type texture is sufficiently different from that observed for the brass-type texture to allow the two types to be easily distinguishable and a quantitative measure of the amount of each can be deduced from the numerical results. This ability to provide quantitative data is particularly valuable when the two textures occur simultaneously in one alloy as is the case for the transition textures. In this paper the modulus method, supplemented by pole figure data, is used to look for an effect of roll: ing reduction the texture. Also by combining the texture measurements with recent determinations of the SFE in Cu-A1 alloys&apos;0&apos;" it should be possible to test for a relationship between the SFE and textures.

Jan 1, 1970

By G. R. Love, M. L. Picklesimer

Aboue 950°C the Nb-Zr system consists of a completely miscible bcc solid solution, commonly called the phase. Between 950 and 600°C, and between 20 and 85 pct Nb, the phase deconlposes, after sunciently long times, into two bcc solid solutions. The pct Zr alloys are conveniently descibecl with T-T-T (time-temperature-transformation) curves having a nose at about 2 hr at 700°C. The reaction rate varies only slowly with zirconium content and negligibly with oxygen contanzination; it is speeded up by a factor of 10 to 15 by 90 pct cold ulork and slowed dou by n factor oj 10 to 30 by a two-hundrecljold increase in grain size. Nb-r alloys with compositions between 40 and 85 pct Nb have been the basis for the majority of commercially important superconducting materials. In part because of their commercial promise, more is known about these alloys than about most other high-field superconducting materials. At the same time, there is considerable disputed or incomplete metallurgical information. For example, although Rogers and tkins&apos; indicate a monotectoid reaction at approximately 600°C and a two-phase 01 + 0, field extending between 20 and 85 pct Nb and to a maximum of 95OGC, erhout&apos; has reported that this entire region would be a single homogeneous B were it not for oxygen contamination. Again, although it has been shown that relatively short-time heat treatments in the vicinity of 700CZ significantly improve the ability of short wire samples to carry high currents in high magnetic fields at 4.2K, these observations have never been fully correlated with the structural change or changes occurring during the anneal. We intend to investigate in detail the effect of metallurgical variables, including heat treatment, on the superconducting properties of hard superconductors. To verify that our experimental techniques are valid and to establish a relative standard against which other materials may be measured, we feel it advisable to know the behavior of the Nb-Zr alloys under a variety of processing conditions. As an initial step toward this goal, we have determined in detail the kinetics of the transformations in Nb-Zr alloys. EXPERIMENT A number of problems had to be solved before beginning any fruitful work on the reaction kinetics in this system. While solving some of these problems, either by chance or by design, small amounts of information were obtained about alloys containing 40, 50, 60, 65, 67, 70, and 75 pct Nb, bal. Zr. In addition, a large range of grain sizes and a range of temperatures considerably greater than the range indicated by Rogers and Atkins phase diagram were examined. We will, however, report in detail only the results obtained for the Nb + 33 pct Zr and Nb + 25 pct Zr alloys at three grain sizes, two levels of oxygen contamination, and the temperature range 550 to 950°C. These data are most complete, but the other data are sufficiently complete to indicate the kind and magnitude of the variation of the transformation kinetics outside this range. The first and most difficult problem encountered in this inquiry was one of sample homogeneity. When Nb-Zr alloys are arc- or electron-beam-melted on a cooled copper hearth, solidification is sufficiently slow that there is appreciable coring in the cast structure and a large variation of grain size across the button thickness. Both these factors significantly affect the apparent reaction rate in the system. A two-step solution to the problem was attempted; an arc-melting and drop-casting technique has been developed by conald that greatly reduces the as-cast grain size and virtually eliminates coring segregation. Ingots made in this way exhibited no detectable (3 pct maximum) zirconium segregation. Before it was evident just how good this technique was, we attempted to supplement it with rather long-time, high-temperature annealing of the cast ingots. This annealing was carried out in evacuated and sealed (seal-off pressures < 1.0 x 106 torr) quartz capsules lined with tantalum foil at 1400 to 1450 C for 8 to 72 hr. There were two principal effects of this treatment: the grain size increased to a fairly uniform 150 p, and the surface and all grain boundaries near the surface acquired a film of a second phase, tentatively identified as an oxide (possibly additionally contaminated with silicon). There was no evidence that this 1400 C treatment had affected the zirconium segregation. High-temperature annealing was subsequently used only for grain-size control, but anneals of longer than 4 hr at temperatures greater than 1000°C were performed in dynamic vacuums (pressure no greater than 1.0 x lo torr). Any contamination resulting from these treatments was well below the limits of detection of our techniques. All samples, as cast, were cold-swaged to at least 85 pct reduction in area. The samples called cold-worked were tested as swaged. The minimum re-crystallization anneal for these alloys was about 12 hr at 1050 C; this produced an equiaxed grain diameter of about 4 to 8 P. Annealing for 4 hr at 1450°C produced a grain size of about 80 to 150 p; and annealing for 4 hr at 1650aC, close to the melting point of many of these alloys, produced a grain size of 0.5 to 1.0 mm. At all temperatures, the larger grain size was

Jan 1, 1967

By T. K. Redden

Protective coatings based on the formation of a surface coating of nickel aluminide (NiAl) were applied to the nickel-base superalloys IN 100, SEL 15, and U-700. Coated specimens were exposed to an oxidizing environment at temperatures between 1600 and 2200 F for times up to 1000 hr. The oxidation resistance and stability of the coating were evaluated by weight gain measurements, metallographic examination, and X-ray diffraction study of surface oxides and coating. The composition of the coating and diffusion zone was determined by electron microprobe traverse of samples before and after high-temperature exposure. Intermediate phases formed in the coating and diffusion zone were identified by X-ray diffraction in situ and after electrolytic extraction. The outer coating was found to consist of the inter-metallic compound, NiAl, while the diffusion zone contained MC, M23C6 or M6C carbides, and a phase in a matrix of NiAl + Nidl. Oxidation resulted in formation of an A1203 n&apos;ch scale containing some Tz02. Depletion of aluminum during oxidation resulted in degradation of the outer coating to Ni3Al and the nickel alloy matrix. Diffusion of aluminum into the base metal was found to be slight and did not influence coating life significantly. The o formed in the diffusion zone during coating decomposed during elevated-temperature exposure to form stable carbide phases characteristic of the base metal. Diffusion zone phase changes were found to have no effect on the life of the aluminide coating in the oxidizing envzron?nent. THE oxidation resistance of many high-strength nickel-base superalloys is inadequate for extended exposure at temperatures above about 1600°F. In addition, some applications for these materials require that they be exposed to environments containing sulfur compounds and sodium salts which can cause surface attalk known as sulfidation or hot corrosion. In order to provide the necessary corrosion resistance to the high-strength alloys, protective coatings based on an aluminizing process have been developed. These processes, usually based on a pack cementation technique, result in the formation of a NiAl-rich outer coating layer either during the coating process or by a subsequent diffusion treatment. The performance of the aluminide coatings is affected by interactions between the coating layer and the base metal both during the coating process and during subsequent exposure at elevated temperatures. Knowledge of these interactions is required to guide the development of coatings capable of longer life and improved reliability. Goward et al.&apos; recently reported the metallurgical factors which influence coating per- formance on MAR-M200. The present work is concerned with correlating the interactions and performance of coating compositions on several representative materials. EXPERIMENTAL PROCEDURES Materials. Three cast nickel-base superalloys which are used for turbine buckets in air-breathing engines were studied: IN 100, U-700, and SEL 15. Their chemical compositions are given in Table I. The alloys were vacuum-induction-melted and cast to slabs approximately 0.3 in. thick from which rectangular specimens 0.25 by 0.5 by 1 in. were machined. Coating Procedures. The machined specimens were coated by CODEP processes which were developed at the author&apos;s laboratory. These are based on pack cementation in various media to deposit either aluminum or aluminum in combination with titanium. The coating process which deposits only aluminum is designated CODEP-C, while the CODEP-D process deposits titanium in combination with aluminum. The CODEP-D process was applied only to IN 100. Both CODEP processes are applied at 1950" or 2000°F for 4 hr without need for a subsequent diffusion treatment. An outer coating about 1 mil in thickness is produced by these processes. Test Procedures. Coated specimens were exposed to static oxidation for periods ranging from 24 to 1000 hr at temperatures of 1600" to 2200°F. Terminal weight gain measurements and visual examination were used to evaluate oxidation resistance. including oxide spalling and coating failure. Both as-coated and exposed specimens of each alloy were studied by metallographic examination, electron microprobe analysis (EMA), and X-ray diffraction analysis either of the exposed surfaces or of phases extracted from the coating and diffusion zone. RESULTS As-Coated Condition. The microstructures of as-coated conditions were generally similar, irrespective of base materials or the particular coating process. They are typified by IN 100 coated by CODEP-D as shown in Fig. 1. The predominately single-phase outer layer, area A, Fig. 1, was identified by X-ray diffraction as the intermetallic compound NiA1. The NiAl zone extended inward to the original base metal interface. The diffusion zone, area B, Fig. 1, included carbide phases, a lamellar phase oriented perpendicular to the base metal surface, and a matrix phase consisting of a mixture of NiAl and Ni3Al. The phases in the diffusion zone were electrolytically extracted using a 10 pct HCl in methanol solution at approximately 1.3 amp per sq cm. The extracted phases were found to be M6C, MC, or M=C6 carbides and o as shown in Table I1 for each of the alloys. The d spacings from a typical diffraction pattern are

Jan 1, 1969

By R. Silverman, H. Blumenthal

It was found that despite the similarity of chemical analyses of different titanium carbides used as base materials for cermets, the physical properties, especially transverse-rupture strengths, of test bars were different. Hence this metallographic study attempts to link physical properties to micro-structures. It is shown that microstructure, grain shape, and grain growth are functions of three interrelated factors: 1—powder production procedure, 2—surface conditioning of the particles, and 3—impurities either contained in the original powder or acquired during ball milling. An explanation is offered for the "coring effect," long observed, but heretofore of unknown origin. The explanation is based on assumption of an oxide film and on chemical analyses which substantiate these findings. TITANIUM carbide has become in recent years a material of great interest in the high temperature field. Consequently, many manufacturers in the United States and Europe are producing titanium carbide for cermet applications as well as for additions to the well known tungsten carbide tools. All present commercial processes of titanium carbide production utilize the chemical reaction of titanium dioxide and carbon to form as nearly as possible stoichiometric Tic. This reaction is carried out in three ways: 1—in a menstruum of molten metal,&apos; 2—in the solid state, either in a protective atmosphere2 or in vacuum;" or 3—in an are-melting operation. In spite of the fact that the pure carbides obtained in these operations are almost identical chemically, the physical properties vary considerably when they are combined with a binder (Ni, Co) to form cermets. This fact led the authors to examine metal-lographically nickel-bonded titanium carbide in order to find the possible reasons for this behavior. Materials and Methods Five different titanium carbides were used in this investigation. They are identified in Table I. The first four materials were used in the as-received condition. Material E, received in lumps, was crushed to —100 mesh and carried through a flotation process in order to bring its graphite content in line with the other products. A Galagher flotation cell was used with pine oil as frothing agent. The chemical analyses of the investigated materials are given in Table 11. The binder used was carbonyl nickel of 9 to 14 microns particle size, supplied by A. D. Mackay. The materials were ball milled at a ball to charge ratio of 6:1 using procedures described under "Experiments and Results." All particle sizes mentioned are averages determined with a Fisher Sub-sieve Sizer. Test bars (lx0.40x0.16 in.) were prepared by 1—hot pressing to 85 to 95 pct of theoretical density at pressures between 1 and 1½ tsi and temperatures from 1600" to 1800°C, 2-—-cold presssing after 3 pct camphor had been added, or 3—wet pressing, both 2 and 3 at pressures between 5 and 10 tsi. All pressed bars were sintered in a vacuum of 105 to 10-6 mm Hg for 2 hr at 1350 °C. Transverse-rupture strengths were determined by breaking on a Baldwin Universal Testing Machine over a 9/16 in. span. Densities were measured by water displacement. The preparation of the specimens for micrographs was done according to Silverman and Doshna Luscz." All magnifications are at X1000. A sodium picrate electrolytic etch was used. Experiments and Results The influence of ball-milling procedure, ball-milling medium, pressing procedure, and sintering procedure on the microstructure of 80/20 — TiC/Ni were investigated. Ball Milling of Materials A, B, and C in a Steel Mill: Figs. 1 and 2 show microstructures of hot-pressed and vacuum-sintered test bars of materials A and B after the respective materials had been ball milled to 2.1 microns particle size in a steel mill and mixed with 20 pct Ni binder. Material A (Fig. 1) shows considerable grain growth. Also evident is a tendency of the carbide grains to coalesce. The density is 98 pct and the low transverse-rupture strength of 111,000 psi is probably caused by many large grains and an unfavorable packing factor. Almost all grains show a slight indication of "coring." Material B (Fig. 2), although showing grain growth, still has many small particles and a better distribution of binder and carbide due to the relative absence of the coalescing tendency. "Coring" can be observed in almost all grains. The high transverse-rupture strength of 179,000 psi and the density of 100 pct are believed to be due to the many small grains completely surrounded by the binder phase. There is also a preference to form spherical grains with material A, while most grains of material B preserve their angular shapes. Material C, of which no picture is given, stays between A and B in every respect. Rounding of some grains can be observed as well as coring, but the latter to a lesser degree than with material B. Its densification is good and the transverse-rupture strength obtained is 142,000 psi. Ball Milling of Materials A, B, C, and E in a WC Mill: When the Tic powders were ball milled to 2 microns particle size in a we mill, then ball-mill mixed with 20 pct Ni binder, hot pressed, and vacuum

Jan 1, 1956

By F. W. Schremp, V. L. Johnson

This paper discusses the results obtained from high temperature, high pressure filter loss studies in which field samples of clay-water, emulsion, and oil base fluids were used. High temperature, high pressure tests of some premium priced emrilsion and oil base drilling fluids show filter loss peculiarities that are not predicted by standard API tests. It is recommended that high temperature, high pressure filter loss tests be used to evaluate the performance of such fluids. Apparatus is described which proved to be satisfactory for evaluating filter loss behavior over a wide range of temperatures and pressures. INTRODUCTION The petroleum industry spends large sums of money each year on chemical treating agents for lowering filter loss and on premium-priced low filter loss drilling fluids. While it is an accepted fact that low filter loss is advantageous during drilling operations, it is questionable whether the present standard method of determining filter loss gives a reliable indication of the loss to he expected under bottom hole conditions. The purpose of this paper is to show that high temperature. high pressure filter loss tests Should be used to evaluate filter loss behavior of fluids for deep drilling. Concern over possible effects of filter loss on oil well drilling and well productivity dates back to the early 1920&apos;s. During the years 1922 to 1924, filtration studies were reported by Knapp,&apos; Anderson2 and Kirwan." These studies were the first to be reported in the literature on this subject. No further information was published on the subject until 1932 when Rubel&apos; presented a paper in which he discussed the effect of drilling fluids on oil well productivity. In 1935. .Jones and Babson constructed the first laboratory tester designed to study the effects of temperature and pressure on the filter loss behavior of clay-water drilling fluids. In a discussion of their investigations, Jones and Babsons stated, "Performance characteristics of a mud can he evaluated with considerable reliability by a single test at 2,000 psi and 200°F. Exact correlation between the results of performance test5 made under these conditions and the behavior of muds in actual drilling operations is of course impossible." Jones arid Babson apparently were well aware that at best laboratory tests can give only qualitative answers to the question of what is the actual behavior of a drilling fluid when subjected to deep drilling conditions. Jones&apos; presented a paper in 1937 in which he described a static filter loss tester to be used for routine filter loss tests. This instrument subsequently was adopted as the standard APl filter loss tester. In 1938, Larsen7 developed a relationship between filtrate volume and filtrate time that is in general acceptance today. Larsen was cognizant of the danger of estimating bottom hole behavior from filter loss measurements at room temperature. He tried to predict the effect of temperature on filter loss by relating temperature effects through the temperature dependence of filtrate viscosity. This was undoubtedly an over-sirriplification of the temperature dependence of drilling fluid filter loss. In 1940, Byck" published a summary of experimental results of filter loss tests made on six representative California clsy-water drilling fluids. He concluded that "no existing method will permit even an approximate determination of the filtration rate at high temperature from data at room temperature. It is necessary to measure filtration at the temperature actually anticipated in the well, or to make a sufficient number of tests at various lower temperatures so that a small extrapolation of these data to the anticipated well temperature may be applied." Byck&apos;s findings were presuma1)ly well accepted and recognized by drilling Fluid technologists, and yet, they did not lead to wide adoption of high temperature drilling fluid filtration equipment. This is evidenced by the fact that no addition information has appeared in print on the subject since 194). Study of Byck&apos;s data shows that there was a useful consistency in them. The fluids did not show predictable losses at high temperatures, but they did line up at high temperatures in approximately the same order that they lined up at low temperatures. That is, if a fluid appeared to be a good fluid with relatively low loss at low temperatures, it would also be a good fluid with relatively low loss at high temperatures. In the last decade. the above situation has changed. The drilling fluid art is markedly different from what it was. The outstanding change, as far as the present discussion is concerned, has been the adoption of wholly new types of drilling fluids. Oil base and emulsion drilling fluids have come in to wide use. It is, therefore, necessary- to re-examine previously satisfactory generalizations to see if they are still valid. It turns out. as might have been expected. that Byck&apos;s explicit generalization. already quoted, is still true. Filter losses at high temperatures cannot be predicted from filter losses at low temperatures. However, no further generalizations are valid now. Fluids of different chemical types show different general behaviors. No longer do the fluids line up approximately the same at high temperatures as they do at low temperatures. They may line up entirely differently. Special fluids exhibiting very low loss at low temperatures may have losses as high as those of ordinary clay-water fluids at high temperatures. This fact is highly significant, because premium prices are being paid for the special fluids.

Jan 1, 1952

By H. Doi, Y. Fujiwara, K. Miyake

In order to throw light on the mechanism of plastic deformation of WC-Co alloys, compressive tests of WC-(7 to 43) vol pct Co alloys have been carried out at room temperature, and stress-micro strain relation has been investigated in detail. The analysis of the factors affecting the yield stresses reveals that the yield stresses can be predicted by modified Oro-wan&apos;s theory if one properly estimates the planar in-terfiarticle spacings. Conzpressive straining of some of the alloys by 0.066 to 0.17pct increases the decrements by a factor of as much as 3.4 to 14, whereas the corresponding increase in the electrical resistivities is less than 10 pct. The analysis of the decrement data in terms of -Gramto and Lücke theory shows that the marked increase is attributed to increased dislocation darnping itt the binder (cobalt) phase. By cornbilling the decrement data and the conzjwession duta, one obtains the relation between flow stress in shear (?t) and increase in dislocation density (p): At = const . v6 . This is interHeted to mean that the mechanism of strain hardening of CirC-Co alloys is essentially sarne as the one for dispersion strengthened alloys. The possible effect of bridge formations between the carbide particles has also been examined. OWING to the combination of hardness, strength, and other physical and chemical properties, WC-Co alloys have opened the way for unique fields of applications, the recent ones being, for instance, anvils for super-high-pressure generation apparatuses. In such applications, the alloys are frequently subjected to very high compressive stresses: these stresses may cause the alloys to deform plastically and eventually to fail. However, much remains obscure regarding the nature of the plasticity of the alloys. Evidently, the alloys owe their high strength to the hard carbide particles which frequently occupy as much as 80 to 90 pct in volume fraction, whereas the ductility required for practical applications is provided by the small amount of the binder phase between the carbide particles. When the volume fraction of the carbide phase is not very large, deformation behavior of the alloys may be described by some of the current dispersion strengthening theories. However, greatly increasing the carbide phase is thought to lead to some carbide skeleton structure or bridge formations owing to the increased chances for direct contacts between the carbide particles;1,2 this may appreciably affect the plasticity of the alloys. Regarding the effect of formation of the carbide skeleton structure, it is interesting to note the work by Ivensen et al.3 on compression tests of the alloys containing somewhat large carbide particles; they observe extensive generation of slip bands in the carbide particles after application of some preliminary compressive stresses. They interpret the results in terms of plastic deformatiot: of the carbide particles which are supposed to have formed a skeleton structure; the binder phase plays only a passive role, at least in the early stages of the deformation. That carbide crystals exhibit microplasticity at room temperature is apparent from the work of Takahashi and Freise4 and French and Thomas5 on indentation of WC single crystals. On the other hand, Dawihl and coworkers6-10 maintain that even when volume fraction of the carbide phase is very large (for instance, more than 90 pet), a very thin binder layer generally exists between the carbide particles. They interpret the results of the extensive mechanical tests in terms of the plasticity of such a layer. Gurland and Bardzil11 point out that decrease in ductility of the alloys with increase in the carbide phase is caused by the effect of plastic constraint exerted by the dispersed carbide particles. Drucker12 further develops this concept from a continuum-mechanics approach on an assumption that a continuous thin binder layer separates the carbide particles. A common feature of the studies reported so far on the plasticity of the alloys is that the information deduced is invariably qualitative in nature. Thus, very few systematic experiments for obtaining reliable and sufficiently detailed stress-strain curves of the alloys varying widely in the microstructural features have been carried out. In particular, it may be of special interest to investigate in detail the early stages of the plastic deformation of the alloys in order to shed light on the strengthening mechanism. However, such work appears to be extremely rare. Doi et al.13 recently reported a first brief account of the results of some quantitative analysis of the plasticity of the alloys in terms of dislocation theory. Their experiment was rather limited in the composition range covered (volume fraction occupied by the carbide phase: 79 to 83 pct), and thus they could not necessarily elucidate the controlling mechanism of plastic deformation of the alloys of a more general composition range. Consequently, in the present investigation, deformation behavior and some other physical properties of the alloys were investigated and discussed in more detail over a much wider composition range. SPECIMEN PREPARATION WC-Co alloys used in this experiment were prepared in cylindrical or rectangular form by sintering in vacuo compressed mixtures of tungsten carbide and cobalt

Jan 1, 1970

By N. L. Svensson

The model developed by Tuylor for the calculation of Polycrystalline yield strength has been applied to the case of an aggregate hawing a preferred orientation. In general this procedure requires the specification of texture by means of weighting factors applied to specific orientations. The problem to which the model has been applied is that of the yield-strength aniso-tropy of cold-rolled aluminum whose rolling texture was described as a combination of (110)[112] and (311) [112] In this case yield-strength anisotropy is defined by the rutio of yield strength measured at an angle 8 to the rolling direction to that measured along the rolling direction. The method of calculation of yield-strength ratio as a function of ? is described and the results show good agreement with experimental values. The orthotropic yield criterion suggested by Hill has been applied to the results and the strain ratio R also calculated as a function of ?. This has been compared with calculations using the method suggested by Elias, Heyer, and Smith which does not exhibit suck good agreement with observation. one deficietlcy of the method presented is that the strain ratios used by are those applying to iso-Irobic materials. The method should therefore be reg-clrded only as a first abbroximation to the prediction of anisotropy. THE problem of calculating the stress-strain characteristics of polycrystalline aggregates from the properties of single crystals has attracted attention for a number of years. The most important contributions to this study have been those due to: Sachs,&apos; Cox and sopwith,2 Taylor,3 Kochendorfer,4 Batdorf and Budiansky,5 Calnan and Clews,6 Bishop and Hill,7,8 Kocks,9 Budiansky, Hashin, and sanders, 10 Kroner,11 Cyzak, Bow, and payne, 12 Budiansky and Wu,13 and Lin.14 While the earlier work has been largely superseded, recent developments tend to support Taylor&apos;s solution" within the restriction imposed by his assumptions. The essential features of Taylor&apos;s approach were: 1) the material is rigid-plastic; 2) each grain experiences the same strain components as the aggregate as a whole (the problem was that of uniaxial deformation with principal strain components in the ratio 3) all regions of each grain deform uniformly; 4) work hardening occurs equally on all slip systems. While Bishop and Hill7 have generally validated this approach, there has been some criticism offered. Kocks? as pointed out that since multiple slip must occur the single-crystal data must be determined from orientations arranged such that polyslip takes place. Boas and Hargreaves,15 and others, have shown experimentally that the strain distribution within grains is not uniform, the strains in the vicinity of grain boundaries being less than those in the center of the grains. Both of these criticisms can be largely offset by the suitable choice of single-crystal critical shear stress. However, for the problem analyzed below, the critical shear stress is not directly used and, consequently, these criticisms lose their importance. The more recent contributions have attempted to obtain a more complete analysis by considering an elas-toplastic material and considering interactions between grains of differing orientations. Lin14 has considered the early stages of yielding for a polycrystalline aggregate having specific regions of defined slip plane orientations. On the other hand, Budiansky and Wu13 have allowed for these interactions for randomly disposed grain orientations and have calculated the polycrystalline stress-strain curves for crystals exhibiting either elastic-ideally plastic or kinematic hardening characteristics. This work has shown that yielding commences when the macroscopic stress is 2.2 times the critical shear stress for slip in a single crystal (7,). The yield stress-strain curve then rises becoming asymptotic to a value of 3.072 7,. This is close to the value obtained by Bishop and Hill (3.06) in their confirmation of Taylor&apos;s method. This, of course, is to be expected since, at large strain values, the elastic strains are negligible and the rigid-plastic model is satisfactory. The results of Budiansky and Wu indicate that the result obtained by Taylor is 7.7 pct high at a plastic strain which is two times the elastic strain at the initiation of yield. By defining the anisotropy in terms of relative values, the ratio of yield strength at orientation ?, to that measured in the rolling direction, the effect of the discrepancy in Taylor&apos;s solution is considered to be of lesser consequence. Therefore, it is anticipated that an analysis based on Taylor&apos;s solution, which can be quite straightforward, should provide a reasonable estimation of the anisotropy of materials having a preferred orientation texture. OUTLINE OF TAYLOR&apos;S METHOD In fee metals there are four possible slip planes (the octahedral planes) and in each there are three possible slip directions (the edges of the octahedron), that is a total of twelve possible slip systems. von Mises16 has shown that at least five independent slip systems must become operative in each grain of the polycrystalline aggregate in order to preserve continuity of strain. With this geometrical requirement as basis and the assumptions previously listed, Taylor determined the operative slip systems for a number of orientations of the tensile stress axis specified in the unit stereographic triangle. For the ith slip system, the critical shear stress

Jan 1, 1967

By A. Raman, P. P. Singh

The constitution of the La-Rh system was studied by powder X-ray diffraction, metallopaphic, and differential thermal analysis techniques and an equilibrium diagram is presented. Eleven intermediate phases occur in the system and the crystal structural data for nine of them were determined. La3Rh crystallizes in an orthorhombic structure of undetermined type, whose unit cell is obtained by doubling the &apos;a; and &apos;c,,&apos; edges of an FesC type unit cell. The other intermediate phases of the system are LarRh-3( undetermined structures also occur in the system. LaRh, undergoes a polymorphic phase transformation at 1240°C. LaRh3 and La2Rh7 also exhibit polymorphisnz. The phases Laah and LazRh7 melt congruently. The latter undergoes a eutectoid transformation into LaRh, and Rh at 1205°C. Laah3 is formed by a peritectoid reaction between Laah and La,Rh,,. The other Phases result from peritectic reactions between the liquid and the adjacent rhodium-rich phases. The intermediate Phases of the La-Rh system are compared with those of the La-Co and La-Ni systems. DURING the course of a detailed investigation to study the occurrence of CrB, FeB, A1B2, and related structures in the rare earth alloys it was found that much information is lacking for the rare earth noble metal systems. Although the structures of several rare earth alloys containing the noble metals at the AB and AB2 stoichiometries have been reported, the occurrence of related structures at other stoichiometries has not been studied. We have initiated a project to study the crystal structural features of selected rare earth-rhodium alloys and to map the equilibrium diagrams of representative systems with conventional methods. The results of our investigation in the La-Rh system are presented in this paper. Two phases were known in the La-Rh system. LaRh has the CrB-type structure.&apos; LaRhz is a MgCu2-type Laves phase.z EXPERIMENTAL PROCEDURE Alloys weighing less than 1 g were prepared from commercially pure lanthanum (99.9 pct +), supplied by Lunex Company, Pleasant Valley, Iowa, and rhodium (99.92 pct +), supplied by Engelhardt Industries, Newark, N.J., in a conventional arc melting furnace under argon atmosphere. The buttons were turned upside down and remelted three times to insure homogeneity in the samples. Since negligible loss of material was encountered during melting, a chemical analysis of the alloy buttons was not undertaken. Powder specimens for X-ray diffraction studies in the as cast state were then prepared. The buttons were wrapped in thin molybdenum foils and homogenized by heating in vacuum at suitable high temperatures for more than 1 week. They were then broken into three or four pieces for annealing experiments. The pieces were wrapped in molybdenum foils and annealed at various temperatures in evacuated quartz capsules. The annealing was carried out for 2 hr at or above 1200°C, 1 day at temperatures close to llOO°C, 2 days at 1000°C, and for 1 week at temperatures below 1000°C. After annealing the alloy pieces were again broken and powder specimens for X-ray diffraction were prepared. The powders of the lanthanum rich alloys with more than 80 at. pct La were prepared by filing. The filings were sealed in molybdenum tubings and stress-relieved at 600°C in vacuum. It was not deemed necessary to stress-relieve the powders of the other alloys, since the alloys were very brittle and were ground easily. POWDER X-RAY DIFFRACTION X-ray diffraction photographs of powders (-325 mesh size) of the alloys in the as cast and annealed states were prepared in a Guinier-de Wolff focussing camera with copper K, X radiations. These patterns were studied to identify the stoichiometries and the crystal structures of the intermediate phases. The lattice parameters of the phases were calculated after minimizing the differences between the observed sin2 6 values, calculated from the diffraction angles 8, and the sin2 8 values, calculated using approximate lattice constants obtained from a few lines. These differences were minimized manually to less than 0.0005. The latLice constants are judged to be accurate to *0.005A for values less thp about 10A and to k0.01~ for values greater than 10A. The relative intensities of the lines were calculated using a computer program written by Jeitschko and Parthk.~ No attempt was made to refine the atomic positional parameters in the phases. METALLOGRAPHY The phase equilibria in the investigated alloys in the as cast and annealed states were also studied by metallographic examination. The polished specimen surfaces were etched with 10 pct picric acid in alcohol (alloys up to 25 pct Rh), concentrated picric acid (from 25 to 37.5 pct Rh), 2 pct nital (40 to 50 pct Rh), 10 pct nital (from 50 to 66.7 pct Rh) and with concentrated 48 pct HF for the other rhodium-rich alloys. Selected microstruture~ were then photographed using a Po-laroid Land camera. THERMAL ANALYSIS Differential thermal analysis of the alloys was carried out in DTA-668 Stone differential thermal ana-

Jan 1, 1970

By D. T. Peters, S. Floreen

The age hardening behavior of an Fe-8Ni-13Mo alloy was studied after the matrix had been varied to produce either ferrite, cold u~orked ferrite, or nzassive nzartensite. The aging behavior of the cold worked ferrite and murtensite structures were very similar. The martensite aging kinetics were much different from those observed in earlier studies of aging of maraging steels, even though the martensite wzatri.r had the same dislocation structure as those found in maraging steels. The results suggest that the previously observed precipitation kinetics of maraging steels ?nay have been controlled by the nucleation be-haviov, which in turn were dictated by the alloy compositions and the resultant identities of the precipitating phases. IT is well known that the rate of precipitation from solid solution depends not only on the degree of super-saturation, but also on the density and distribution of dislocations in the matrix structure. These imperfections often act as nucleation sites, and may also enhance atomic mobility. &apos;Thus, the presence of dislocations is important since the type and distribution of precipitates may be determined by them. The precipitate density and morphology in turn affects the mechanical properties of the alloy. A number of studies have been devoted to the precipitation characteristics in various types of maraging steels.&apos;-" These are iron-base alloys containing 10 to 25 pct Ni along with other substitutional elements such as Mo, Ti, Al, and so forth, that are used to produce age hardening. The carbon contents of these steels are quite low, and carbide precipitation is not believed to play any significant role in the aging reactions. After solution annealing and cooling these alloys generally transfclrm to a bcc lath or massive martensite structure characterized by elongated martensite platelets that are separated from each other by low angle boundaries, and that contain a very high dislocation den~it~.~~~~~~~~-~~ Age hardening is then conducted at temperatures on the order of 800" to 1000°F to produce substitutional element precipitation within the massive martensite matrix. Most of the aging studies to date have revealed several common traits in these alloys, regardless of the particular identity of the precipitation elements. Generally hardening has been found to be extremely rapid, with incubation times that approach zero. The agng kinetics, at least up to the time when reversion of the martensite matrix to austenite begins to predominate, frequently follow a AX/~~ = ktn type law, where x is hardness or electrical resistivity, t is the time, and k and n are constants. The values of n are frequently on the order of 0.2 to 0.5, which are well below the idealized values of n based on diffusion controlled precipitate growth models. Finally, the observed activation energy values are typically on the order of 30 kcal per mole, and thus are well below the nominal value of about 60 kcal per mole found for substitutional element diffusion in ferrite. The common explanation of these observations is that the precipitation kinetics are controlled by the massive martensite matrix structure. Thus, the absence of any noticeable incubation time has been attributed, after ~ahn," to the fact that the precipitate nucleation on dislocations may occur without a finite activation energy barrier. The low values of the activation energy are generally assumed to be due to enhanced diffusivity in the highly faulted structure. If this explanation that the precipitation kinetics are dominated by the matrix structure is correct then one should observe a distinct difference in lunetics between aging in a martensitic matrix and aging the same alloy when it has a ferritic matrix. Such a comparison cannot be made with conventional maraging compositions, but could be made with the alloy used in the present study. In addition, the ferritic structure of the present alloy could be cold worked to produce a high dislocation density so that one could determine whether ferrite in this condition would age similarly to martensite. EXPERIMENTAL PROCEDURE The composition of the alloy used in this study was 8.1 pct Ni, 13.0 pct Mo, 0.10 pct Al, 0.13 pct Ti, 0.012 pct C, bal Fe. The alloy was prepared as a 40 lb vacuum induction melt. The heat was homogenized and hot forged at 2100°F to 2 by 2 in. bar, and then hot rolled at 1900°F to $ in. bar stock. The aging lunetics were followed by Rockwell C hardness and electrical resistivity measurements. Samples for hardness testing were prepared as small strips approximately 2 by $ by 4 in. thick. Electrical resistivity was studied on cylindrical samples approximately 2 in. long by 0.1 in. diam. The method for making the alloy either martensitic or ferritic was based on the fact that the alloy showed a closed y loop type of phase diagram. At high temperatures, above approximately 24003F, the alloy was entirely ferritic. Small samples on the order of the dimensions described above remained entirely ferritic after iced-brine quenching from this temperature. In practice, a heat treatment of 1 hr in an inert atmosphere at 2500°F followed by water quenching was used to produce the ferritic microstructure. These samples were quite coarse grained and usually en-

Jan 1, 1970

By T. R. A. Davey

IN 1947 the author became interested in the fundamental aspects of the desilverizing of lead by zinc, conducted some experimental work, and searched the technical literature for all available fundamental data. Since then a revival of interest in the subject in Europe resulted in the appearance of quite a number of papers. It became evident that it would be more profitable to collect together and examine thoroughly the results of various workers, than to attempt to duplicate the experimental determinations. There are many inconsistencies in the various publications, and it is opportune to review at this time the present status of knowledge on the Ag-Pb-Zn system. There is also a need for a clear description, in fundamental terms, of the various desilverizing procedures. This paper is presented in four sections: 1—There is an historical review of the origins of the Parkes process, of the results of many attempts to find a satisfactory fundamental explanation for the phenomena, and of the modifications proposed to date. 2—A diagram of the Ag-Pb-Zn system is presented. This is believed to be free of obvious inconsistencies or theoretical impossibilities, although thermodynamic analysis subsequently may reveal errors. 3—The fundamental bases of the various desilverizing procedures, which have been used up to the present day, are described; and a new method is suggested for desilverizing a continuous flow of softened bullion in which the bullion is stirred at a low temperature in two stages producing desilverized lead at least as low in silver as that from the Williams continuous process and a crust which, on liquation, yields a very high-silver Ag-Zn alloy. 4—A suggestion is made for the revival of de-golding practice, following a recently published account which does not seem to have attracted the attention it deserves. The terms "eutectic trough" and "peritectic fold" as used in this paper are synonymous with "line of binary eutectic crystallization" and "line of binary peritectic crystallization" as used by Masing.&apos; The German literature on ternary and higher systems is rather extensive and a fairly general system of nomenclature has arisen, whereas in English usage the corresponding terms are not as well established. For this reason the meanings of terms used in this paper, together with the equivalent German terms, are given as follows: 1—Eutectic trough—eutektische rinne: line at which a liquid precipitates two solids S1 and S2 simultaneously. If the composition of a liquid which is cooling reaches this line, it then follows the course of this line until a eutectic point is reached, or until all the liquid is exhausted. The tangent to the eutec-tic trough cuts the line joining S1S2. 2—Peritectic fold—peritektische rinne: line at which a solid S1 and a liquid L transform into another solid S2. If the composition of a liquid which is precipitating S1 reaches the line, on further cooling only S2 is precipitated. The liquid composition moves from one phase region (L + S1) into the other (L + S2), and does not follow the course of the boundary. The tangent to the peritectic fold cuts the line S1S2 produced nearer S,. 3—Liquid miscibility gap, or conjugate solution region—mischungslucke: the region within which two liquid phases coexist in equilibrium over a certain range of temperature. A system whose composition is represented by a point in this region comprises one liquid at high temperature; then as the temperature is progressively reduced, two liquids, one liquid and one solid, one liquid and two solids, and finally three solids. 4—Liquid miscibility gap boundary—begrenzung der flussigen mischungsliicke: the line along which the surface of the miscibility gap dome, considered as a solid model, intersects the surrounding liquidus surfaces. 5—Tie lines—konoden: lines joining points representing the compositions of two liquids, a liquid and a solid, or two solids, in equilibrium. In binary systems the only tie lines customarily drawn are those through invariant points, e.g., through the eutectics of the Pb-Zn and Ag-Pb systems, or the various peritectics of the Ag-Zn system, as in Figs. 1 to 3. In ternary systems it is desirable to draw sufficient tie lines to indicate the slopes of all possible tie lines. 6—Ternary eutectic point—ternares eutektikum: point at which liquid transforms isothermally to three solids, S1, S2, and S Such a point can lie only within the triangle 7—Invariant peritectic (transformation) point— nonvariante peritektische umsetzungspunkt: (a) — On the miscibility gap boundary, the point at which two liquids and two solids react isothermally so that L, + S, + L, + S2. (b)—On the eutectic trough, the point at which a liquid and three solids react iso-thermally so that L + S, + S2 + S3. Such a point must lie on that side of the line joining S,S which is further from S,. (c)—A further possibility, not found in this ternary system, is that the point is at the intersection of two peritectic folds when the reaction concerned is L + S, + S, + S Historical Introduction Karsten discovered in 1842 that silver and gold may be separated from lead by the addition of zinc.2 Ten years later Parkes used this fact to develop the well known desilverizing process which bears his

Jan 1, 1955

By J. R. Szedon, T. L. Chu, G. A. Gruber

Amorphous adherent filnzs of silicon dioxide have been deposited on silicon substrates by the oxidation of silane at temperatures ranging from 650 to 1050C. Various diluents (argon, nitrogen, hydrogen) were used to suppress the formation of SiO2 in the gas phase. Deposition rates of the oxide were determined over the temperature range in question as functions of&apos; re-actant flow rates. Etch rate studies were used for a cursory comparison of structural properties of deposited and thermally grown oxides. From electrical evaluation of metal-insulator-silicon capacitors it was determined that the interface charge density of deposited films is similar go that of dry-oxygen-grown films in the 850° to 1050 C temperature range. Deposited films exhibit several ionic instability effects which differ in detail from those reported for thermal oxides. Stable passivating films of silicon nitride over deposited oxides appear to be practical for use in silicon planar device fabrication. Such films can be prepared under temperature conditions which have less effect on substrate impurity distributions than in the case of grown oxides. AMORPHOUS silicon dioxide (silica) is compatible with silicon in electrical properties and is the most widely used dielectric in silicon devices at present. Silica films can be prepared by the oxidation of silicon or deposited on silicon or other substrate surfaces by chemical reactions or vacuum techniques. The ability of thermally grown silicon dioxide films to passivate silicon surfaces forms one of the practical bases of the planar device technology. Properly produced and treated films of grown SiO 2 can have low densities of interface charge (-1 X 10" charges per sq cm) and can be stable as regards fast migrating ionic sgecies. 1 To maintain these properties, even with an otherwise hermetically sealed ambient, the Sia layers must be at least l000 A thick. Such thicknesses require oxidation in dry oxygen for periods of 7.8 hr at 900°C or 2 hr at 1000°C. Although oxidation in steam or wet oxygen can reduce these times to 17 and 5 min, the resulting oxides must be annealed to produce acceptable levels of interface charge., Oxidation or annealing involving moderate to high temperatures for extended periods of time can be undesirable. Under some conditions, there can be changes in the distribution of impurities within the underlying substrate. A chemical deposition technique using gaseous am-bients is particularly attractive and flexible for preparing oxide films. With a wide range of deposition rates available, films can be produced under condi- tions of time and temperature less detrimental to impurity distributions in the silicon than in the case of thermal oxidation. The pyrolysis of alkoxysilanes, the hydrolysis of silicon halides, and various modifications of these reactions are most commonly used for the deposition of silica films.3 Silica films obtained in this manner are likely to be contaminated by the by-products of the reaction, organic impurities, or hydrogen halides. The use of the oxidation of silane for the deposition process has been reported recently.4 The deposition of silica films on single-crystal silicon substrates by the oxidation of silane in a gas flow system has been studied in this work. The deposition variables studied were the crystallographic orientation of the substrate surface, the substrate temperature, and the nature of the diluent gas. The electrical charge behavior of Si-SiO2-A1 structures prepared under various conditions was investigated by capacitance-voltage (C-V) measurements of metal-insulator-semiconductor (MIS) capacitors. The experimental approaches and results are discussed in this paper. 1) DEPOSITION OF SILICA FILMS The overall reaction for the oxidation of silane is: The equilibrium constants of this reaction in the temperature range 500° to 1500°K, calculated from the JANAF thermochemical data,= are shown in Fig. 1. In addition to the large equilibrium constants, the oxidation of silane is also kinetically feasible at room temperature and above. However, the strong reactivity of silane toward oxygen tends to promote the nucleation of silica in the gas phase through homogeneous reactions, and the deposition of this silica on the substrate would yield nonadherent material. The formation of silica in the gas phase can be reduced by using low partial pressures of the reactants. Argon, hydrogen, and nitrogen were used as diluents in this work. 1.1) Experimental. The deposition of silica films by the oxidation of silane was carried out in a gas flow system using an apparatus shown schematically in Fig. 2. Appropriate flow meters and valves were used to control the flow of various reactants, i.e., argon, hydrogen, nitrogen, oxygen, and silane. Semiconductor-grade silane, argon of 99.999 pct minimum purity, oxygen of 99.95 pct minimum purity, and nitrogen of 99.997 pct minimum purity, all purchased from the Matheson Co., were used without further purification. In several instances, a silicon nitride film was deposited over the silica film. This was achieved by the nitridation of silane with ammonia using anhydrous ammonia of better than 99.99 pct purity supplied by the Matheson CO.&apos; The reactant mixture of the desired composition was passed through a Millipore filter into a horizontal water-cooled fused silica tube of 55 mm

Jan 1, 1969

By J. Leja, J. H. Schulman

FROTH flotation is usually effected by the addition of a collector agent and a frothing agent to an aqueous suspension of suitably comminuted mineral ores. The action of collectors is to adsorb onto the surfaces of minerals to be separated, sensitizing them to bubble adherence. The action of frothers has, in the past, been accepted as that of froth formation only, brought about by a lowering of the air/water interfacial tension. Substances capable of producing froth are classed1a,b according to their relative capacities for production of froth-volume and froth stability in the simple frother-water system. The purpose of this paper is to show that the surface active agents acting as frothers become effective only when there is a suitable degree of molecular interaction taking place between collector molecules and frother molecules at the air/water and solid/ water interfaces. Further, the discussion will demonstrate that the actual mechanism of adherence of an air bubble to a suitably collector-coated particle is due to the molecular interaction collector-frother. This leads to the formation of a continuous interfacial film of associated molecules, anchored to the mineral by polar groups of the collector, and enveloping the whole bubble. The tenacity of adhesion mineral-to-bubble results from the strength and the visco-elasticity of this mixed film. Some 20 years ago Christman2 postulated mutual dependence of collector and frother in effecting flotation. This view was, however, strongly opposed by Wark,3 who pointed out that an addition of frother had no effect on the value of contact angle once this was established in the solution of collector. More recent work by Taggart and Hassialis&apos; indicated that the presence of frother, namely, cresol, leads to the immediate establishment of a contact angle on sphalerite, partially coated with xanthate, whereas an air bubble fails to make contact in potassium ethyl xanthate solution alone, even after 60 min induction time. Wrobel5 raws attention to the selectivity of frothers in flotation. Many instances of antagonistic effects of certain mixtures of frothers (or collectors and frothers) on flotation froth have been known to flotation operators and have been reported in literature. Taggart6 and Cooke7 give several examples of incompatibility of certain ratios of frothers and collectors, e.g., oleate and long-chain sulphates, pine oil and soaps. Monolayer Penetration. Properties of insoluble films produced by molecules of surface active agents orientated at the air/liquid interface are conveniently studied by the Langmuir trough technique, described fully by Adam.&apos; Using the trough technique Schulman and Hughes" and Schulman et al.10a. b, c, d,e established the existence of molecular interactions occur- ring between certain types of surface active agents. Their experiments revealed the phenomenon of penetration of an insoluble monolayer (e.g., a film of a long-chain alcohol) by a soluble agent (e.g., sodium alkyl sulphate) injected into the substrate (water or salt solution). The degree of molecular interaction taking place on penetration is determined by changes in the surface pressure of the resulting film, changes of its surface potential and its mechanical properties (viscosity and rigidity). When the interaction takes place between both polar groups and both hydrophobic groups of the two participating amphipathic molecules a molecular complex is formed. Complexes formed on penetration of the monolayer at interfaces are not necessarily true chemical compounds: they are labile in solution, the activity and reactivity of individual components are greatly different from those of the molecularly associated complex, and on crystallization they usually separate out into components. However, when formed in the orientated state at interfaces they are found to be very stable, although some mixed films spread as monolayers of stoichiometric complexes can show further penetration by subsequent additions of the soluble component injected into the substrate.&apos;" The degree of association between two or more types of surface active agents is very sensitive even to small changes in electric (dipole) moment of the polar groups of the amphipathic molecules as influenced by magnitude and position of neighboring ions or dipoles, their size, concentration, and stereochemistry. In addition, the molecular association is greatly influenced by concentration and type of inorganic salts in the substrate, by its pH, and by temperature. The nonpolar groups of interacting molecules greatly affect the stability of molecular complexes. Progressive shortening of the aliphatic chain of one of the reacting molecules weakens (at an increasing rate) its tendency to form stable complexes. Similarly, introduction of a double bond of cis-form into one of the reacting chains, which changes the straight hydrocarbon chain into a kinked one, or introduction of a branched chain, reduces the stability of the associated complex. Monolayer Adsorption. Using the trough technique and injecting metal ions into the substrate (water or salt solution) underlying insoluble films of fatty acids, alkyl amines, and sulphates, Wolsten-holme and Schulman11a,b,e. &apos; and Thomas and Schulman" have established conditions, namely, pH, concentration. and steric factors, under which molecular interactions take place between the polar groups of the surface active agents and the metal ions. These interactions are marked by great changes in the solubility and mechanical properties of the monolayer of the agent; no surface pressure increases are observed as in monolayer penetration experiments. The results of these adsorption studies, correlated with flotation experiments, indicated that in the case of fatty acids and alkyl sulphates their adsorption onto minerals of base-metals takes place by a similar

Jan 1, 1955

By J. Sibakin, R. D. Hindson

In order to devise a practicable soaking pit schedule for use at The Steel Co. of Canada Ltd.&apos;s Hamilton Works, soaking pit heating temperatures, sooking times, pit capacity, and safe maximum mill drafts were correlated with fluctuations in the current or load of the bloom mill driving motor. Other variables such as total delays in the pit, rolling schedules, mill delays, and track times were also investigated. IN order to show an easily applied and accurate means of establishing soaking pit heating temperatures, soaking times, pit capacity, and safe maximum mill drafts, these various factors are correlated herein with fluctuations in the current or load of the bloom mill driving motor. Rolling practices have a considerable influence on the production capacity of a blooming mill. The maximum values of the torque, in particular, are of importance, since even instantaneous current peaks lead to the tripping of the motor by the overload relay and result in loss of mill time. The establishment of safe maximum drafts and accelerations for ingots of different sizes and of a soaking pit practice which would ensure a consistent and satisfactory plasticity of the metal is of considerable importance for increasing the efficiency of both the blooming mill and the soaking pits. The Bloom Mill Dept. of the Hamilton Works, The Steel Co. of Canada Ltd., is equipped with one 44 in. mill driven by a 7000 hp motor with the setting of the overload relay at 22.0 ka. The speed of rotation of the motor is regulated after the Ward-Leonard system. There are three basic speeds of 9.5, 28, and 47 rpm and a further possibility of increasing the speed by weakening the field. This last possibility is hardly ever used during practical operations. The rolling program of the blooming mill is varied, both in the size of the ingots to be handled and in the steel grades. The total tonnage handled by the mill is about 2,000,000 ingot tons per year. At the time of the investigation, the Bloom Mill Dept. was equipped with 22 soaking pits (6 regenerative, 14 bottom-fired, and 2 one-way top-fired pits) with a total bottom area of 2770 sq ft. The pits are fired with a blast furnace-coke oven gas mixture having a calorific value of 155 Btu per cu ft. The foregoing figures show that the production program was such as to impose the necessity of a most efficient usage of the available equipment. For this purpose, the operations of the 44 in. mill and of the soaking pits were investigated, and the results of the investigation were used as a basis for a revised soaking pit schedule and drafting practice. The plasticity of an ingot of a certain chemical composition when being rolled is determined mainly by the following factors: I—the ingot size, both thickness and width; 2—the length of the gas soak; and 3—the surface temperature. The first two factors determine the uniformity of the temperature distribution over the cross-section of an ingot. The third factor introduces the level of the heating of an ingot. The torque produced by an ingot being rolled is determined by the area of the metal displaced, its plasticity, and acceleration values. On the other hand, with shunt motors the torque is determined by the current. This can be assumed to be correct with only a small degree of error for compound motors with a relatively small effect of the series windings as long as the velocity is not regulated by weakening the field. Since the spread is relatively unimportant when compared to the width of an ingot and since it is also reduced several times during rolling by edging passes, the draft alone and not the area of the metal displaced may be taken into consideration with ingots of a similar size. It is therefore possible to determine the main features of the heating and drafting of an ingot by measuring the current and acceleration of the mill motor. After the acceleration has been taken into account, the amount of current will be an indication of how the motor responds to a heating and/or drafting practice and these practices can be adjusted in order to get the desired result. As peak currents are more likely when heavier ingots are rolled, the rolling of plate and slab ingots was investigated. Conditions prevailing when smaller ingots are rolled can be deduced from the results obtained on heavier ingots. All measurements were made when plain carbon grades under 0.15 pct C were rolled. The motor current, the voltage across the armature, and the rpm were recorded simultaneously on synchronized charts, Fig. 1, which moved with the speed of 6 in. per min. Each draft was recorded by a special observer. The rpm curve made it possible to establish the acceleration at any given moment. For purposes of correlation, the maximum current during a pass and the corresponding acceleration were used. The charts made it possible to establish the position of the roller&apos;s lever at any given moment as well as the total time of a pass. The slab ingots were divided into three groups (28x35, 28x45, and 27Mx53 in. ingots) and each group was investigated separately. Since they account for most of the current peaks, only flat passes were used for purposes of correlation, a total of 1373 having been investigated.

Jan 1, 1956