By Shenghui Guo, Dongbo Li, Lijun Liu, Chengdong He, Jinhui Peng, Libo Zhang

In present study, partially stabilized zirconia (PSZ) was prepared by CaO doped fused zirconia heated by microwave furnace at the temperature of 1450 oC and holding time of 120 min. The XRD results showed that untreated fused zirconia mainly consists of crystalline compounds of cubic ZrO2 phase; while the roasted one mainly is composed of crystalline compounds of cubic ZrO2 phase and monoclinic ZrO2 phase. It is shown through the optimization of structures of two phases that structure of cubic ZrO2 and monoclinic ZrO2 reject each other, revealing its difficulty in forming coinciding interface and linkage of two phases being of Ca atom. Introduction Due to advantages of zirconia, such as high melting point, chemistry inertia, low heat transmission and so on. Zirconia is always taken as megathermal refractory material[1]. However, in the heating and cooling processes of pure zirconium oxide, martensitic transformation will take place associated with greater shear force and volume change, which severely limits the industrial application of pure zirconia in some areas. Such as: Refractory materials, grinding materials and high temperature insulation materials[2]. Through adding a certain amount of MgO, CaO, or Y2O3 stabilizer, etc.[3,4], the zirconia can change into fully stabilized zirconia, which exists in cubic phase. But this high purity fully stabilized zirconia cracks easily because of thermal stress. Therefore, the thermal shock resistance variation is one of the most important quality indicators of zirconia-based materials. According to the heat treatment, the fully stabilized zirconia can be changed into the partially stabilized zirconia (PSZ)[5], which exists in cubic phase and monoclinic phase and has superior mechanical properties, such as anti-heat, low thermal conductivity, large coefficient of thermal expansion and stability, as well as good wear resistance[6].

Jan 1, 2011

By Ning Wang, Bing Xie, Hong-Yi Li

"Compared to traditional sodium roasting, calcified roast inhibits chlorine pollution. A vanadium extraction technique based on a calcified roast is especially suitable for vanadium slag with high calcium content. In this report, V205was extracted from vanadium slag by calcified roast followed by acid leaching and hydrolysis precipitation. In optimized conditions, the high silicon low vanadium slag was roasted at 850'C for 2 hours without CaO addition. The roasted materials were leached with 35 % H2SO4 in liquid/solid ratio of 5:1 (mL/g) at 95OC for 4 hours. The extraction of vanadium was as high as 97.66 %. These results are instructive to V2O5 production in industry.IntroductionVanadium slag is produced in converter, sodium salt roasting is the commonly used technique to extract vanadium. In sodium salt roasting, vanadium slag is roasted with sodium salts including sodium chloride and soda as additives, followed by leaching with acidic or basic solution [1]. However, in this process chloride reacts to produce corrosive gases including HC1 andCl2- SO2 and SO3 can also corrode equipment severely and are also an environmental contaminant. The low melting point of sodium salts leads to fusion agglomeration, which blocks vanadium oxidation and thus decreases the extraction rate of vanadium. A large amount of sodium salts consumed as roasting additives increases the production cost. Moreover, sodium salt roasting requires low CaO content in vanadium slag. When the CaO content increases to 1%, V2O5 extraction can amount to 4.7%-9% [2]. For vanadium slag with high CaO content, the sodium salt roasting technique leads to low vanadium extraction rate."

Jan 1, 2012

By M. A. Halim, V. I. Lakshmanan, T. Sheikhzeinoddin, R. Roy

"Chloride metallurgy is emerging as an alternative process for the production of base metals. Process Research ORTECH Inc. (PRO) has been at the forefront of technological development of chloride metallurgy. PRO has developed an innovative technology for the production of high purity titanium dioxide, iron oxide and vanadium pentoxide from ilmenite ores and concentrates. PRO is also developing its proprietary mixed chloride technology for the extraction of vanadium from other sources such as oil shales. In this paper, results from the test work conducted at PRO for the extraction of Ti and V using a mixed chloride lixiviant are presented.IntroductionTitanium and vanadium alloys and compounds have numerous industrial applications. Titanium dioxide is used in paints, plastics, rubber, paper, inks, textiles and a number of other miscellaneous applications. Currently nanosize T1O2 is being investigated for application in the cosmetics industry. Inorganic sunscreens mainly use T1O2 or ZnO particles, which reflect and scatter ultra-violet light. T1O2 nanomaterial is also finding application in smart construction materials and coatings, as a photo-catalytic converter. Nano TiO2 can catalyze the dissociation of NOX gases and other automotive emissions, thereby reducing the smog in urban centers. After the construction material is exposed to sunlight or ultra-violet light, the T1O2 is photo-activated and degrades the pollutants.Titanium metal and titanium dioxide are produced from ilmenite (FeTiOs) or rutile (naturally occurring T1O2) ore. Only about 6% of the titanium resources are used to produce titanium metal and the rest is used to produce T1O2. Many of the titanium ore deposits currently have unacceptable levels of transition metals which limits their processing by conventional routes."

Jan 1, 2012

By M. Brian Maple

A rich variety of phenomena are produced by superconducting-magnetic interactions in rare earth and actinide compounds. These phenomena, and the materials in. which they have been observed, are described in this talk, with an emphasis on the new high superconducting transition temperature (Tc) copper oxides. The Materials The-materials in which these phenomena occur can' be divided into two classes. In the first group, there are two distinct interpenetrating systems of electrons, a set of localized 4f or 5f electrons and a set of itinerant electrons. The localized f electrons carry magnetic moments and interact with the spins and momenta of the the itinerant electrons, which are involved in the superconductivity, via exchange and electromagnetic interactions; respectively. This category includes materials containing rare earth (R) and actinide elements with partially-filled f electron shells which have been inroduced as substitutional impurities [e.g., La1-xCexA12, Th1-xUx] or form a sublattice in compounds [e.g., RRh4B4, RMo6S8, RMo6Se8, the high Tc. superconductors RBa2Cu3O7-d(d - 0.05)]. Materials of the second type are characterized by a single band of electrons that is responsible for both superconductivity and magnetic order. This group includes heavy electron rare earth and actinide compounds [e.g., CeCu2Si2, UBe13, UPt3, URu2Si2], and the high Tc copper oxide superconductors such as the hole-doped systems Lag- MxCuO4 (M = Ca, Sr, Ba, Na) and RBa2Cu3O7-d(0 =d= 1) and the electron-dope system Ln2-xMxCuO4-y (Ln = Pr, Nd, Sm, Eu; M = Ce, Th; x = 0.15; y - 0.02).

Jan 1, 1992

By Qingcai Liu

The effect of the TiC addition on corrosion resistance of the Al2O3-C refractories in smelting reduction melts has been studied by quasi-station immersion and rotary immersion. The corrosion rate of Al2O3-C refractories is decreased with the TiC addition. The corrosion mechanism of Al2O3-C refractories is oxidization of graphite carbon by the oxides of the melts and the formation of deteriorate layer.

Jan 1, 2006

By KNona C. Liddell

The time and spatial dependence of component and species concentrations during in situ uraninite leaching have been modeled using a reactive transport model based on partial equilibrium between reactive minerals and the solution. The flow field is represented by mixing cells in series. The effects of the H2O2, (NH4)2CO3, and NH4HCO3 component concentrations have been simulated, and results are presented for a one-dimensional flow field.

Jan 1, 1995

By S. H. Amini

The effects of CaF2 and ilmenite on dissolution rate and diffusivity of CaO in calcium alumino-silicate based slag in a temperature range of 1500 ? 1600 ºC were studied by using the rotating disk/cylinder technique. The effect of rotation speed on the rate of dissolution in the base slag indicated that mass transfer in liquid slag played a significant role in controlling the dissolution. At a constant rotation speed, the effect of 5 wt% addition of fluxes tothe slag on the dissolution rate was investigated at various temperatures. While CaF2 had the highest effect, addition of ilmenite increased the rate of dissolution significantly. The diffusivity of lime in these slags was quantified using the dimensionless mass transfer correlations for rotating disk/cylinder in the melt. The diffusivity values were deduced using the data on dissolution rate and solubility of lime in the slags. The measured diffusivity in base slag at 1500 C was found to be about 1.32 10-5 cm2/s and increased to 3.07 10-5 cm2/s at 1600 °C. Addition of 5wt% CaF2 increased the diffusivity by a factor of 3 to 5, while 5wt% ilmenite increased the diffusivity by a factor of 2 to 3 in the temperature range of 1500 to 1600 ºC. The two examined fluxes reduced the activation energy of diffusion.

Jan 1, 2006

By M. Jahazi, P. P. Bhattacharjee, K. Chadha

The present work investigated the effect of strain reversal during high pressure torsion on the evolution of microstructure, texture and hardness properties of two different materials with different dynamic recovery behavior, namely, high purity (99%) Aluminum (2N-Al) and Aluminum-Magnesium (Al-2.5%Mg) alloy. In the two aluminum alloys subjected to different routes, the evolution of the ultrafine structure followed same trend. At lower strain level, sub grains with prominent LAGBs network were observed and at higher strains, ultrafine equiaxed grains separated by HAGBs were observed throughout the disk. The texture evolution in monotonically and strain reversal processed 2N-Al and Al-2.5%Mg showed presence of typical torsion texture components at different strain levels. The strength of the components was observed to follow different trends depending on the processing routes.

Jan 1, 2015

By Kalyani Das Sarkar

"Steel Authority of India Limited, a Public Sector Undertaking with a production capacity of 14 million tones of crude steel, is India's largest steel maker and ranks among the leading steel producers in the world. SAIL owns and operates eight manufacturing plant – five integrated steel plants at Bhilai, Durgapur, Rourkela, Bokaro and Burnpur producing carbon steel, and three speciality steel plants. All integrated steel plants have hospitals of 650 – 750 bed capacity with modern facilities to serve it's employees and adjoining localities in a clean and sustainable environment.According to the Bio-Medical Waste(Management and Handling) Rules, 1998 and as amended to date, all Bio-Medical waste which is generated during the diagnosis, treatment or immunization of human beings or in research activities pertaining thereto or in the production or testing of biologicals are to be categorized and taken to any facility wherein treatment, disposal of this waste or processes incidental to such treatment or disposal is carried out.The hospital management has created adequate treatment facility for Sharp and Infectious Waste, Pathological Waste and Anatomical Waste through Autoclave, Shredding Machine and developing deep burial pits. Some of these hospitals is ISO 9000-14000 certified. Use of above said treatment facilities in these hospitals are discussed in this paper.INTRODUCTIONBio-Medical waste means any waste, which is generated during diagnosis, treatment or immunization of human beings or animals or in research activities pertaining to these or in the production or testing of biologicals.Steel Authority of India Limited, a Public Sector Undertaking with a production capacity of 14 million tones of crude steel, is India's largest steel maker and ranks among the leading steel producers in the world. SAIL owns and operates eight manufacturing plant – five integrated steel plants at Bhilai, Durgapur, Rourkela, Bokaro and Burnpur producing carbon steel, and three speciality steel plants. All integrated steel plants have hospitals of 650 – 750 bed capacity with modern facilities to serve it's employees and adjoining localities in a clean and sustainable environment."

Jan 1, 2008

By Toshiaki Nakai, Kunihiko Takeda, Kimio Imaizumi, Hiroaki Shirasaka

"The new type of nano-porous silica particle was considered to be constructed by the spinodal decomposition-type process which was found to have narrower pores than those of conventional porous silica prepared from boron silicate or ""Shirasu"" balloon. Nano-porous silica particles were fabricated by the calcination of silica gel mixed with well-dispersed complex salts composed of phosphorous and molybdenum compounds. Both silica and inorganic salts were not perfectly dissolved in the suspension solution. After removing of the water, the silica-inorganic salts complex was volatized and successively calcinated at a temperature ranging from 650 °C to 800 °C. Then, the inorganic salts were removed by dissolving in hot water. Other inorganic salts such as potassium halides were also found to be effective as a pore-size controller.IntroductionControl of structure has an important role in the field of industry as well as in the separation and purification technology for metals and organic syntheses. Many studies on the control of material structures have been reported regarding porous materials with pores ranging from nanometer to micrometer scale. 1 ) One example is zeolite as a naturally yielded porous inorganic material. Various types of synthetic zeolites have been studied as ""molecular sieve"" materials with ordinary pore-size of less than one nanometer. In 1992, crystalline meso-porous material with a large surface area named MCM-41 was synthesized through the use of template synthesis. 2) In direct relation to our study, amorphous borate glass having 4 to 100 nm of fine pores known as Corning glass 3l or SiO2-Al2OrB2O 3-CaO porous glass having large pore dispersity ranging from 4 to 10,000 nm have been reported. 4 ) S) 6 ) Some examples of several reported studies are as follows: phase-separated porous glass consisting of B2OrAl2O3-ZrO2-RO-R2O complex oxide 7 ) glass with finer pore induced from hydrolysis of silane alkoxide, porous material attained by condensation polymerization through the use of sol-gel process 8), alumina meso-porous material 9 ) 10), silica-zirconia material 11), carbon porous material 12), etc.."

Jan 1, 2000

By Laurence G. Dyer, David G. Dixon, John Rumball, Maziar Eghbalnia, Edouard Asselin

"Linear scan voltarnmetry was used to determine the reactions that occur during the cyanidation of petzite (Ag3AuTe2). Gold oxidation in petzite requires more oxidising conditions than are required for pure gold, it also does not achieve the same current (related to reaction rate). Tellurium oxidation occurs at a similar potential in water and cyanide, but as a component of petzite is impeded somewhat in water, likely due to the stability of the precious metals. Pre-treatment of petzite to oxidise tellurium in the absence of cyanide prior to gold recovery appears to be at least moderately successful.IntroductionWhile gold occurs most prevalently in its native form, many other gold bearing phases appear throughout natural systems [I]. Tellurides are a common group of such minerals, many of which also contain silver, often existing in association with native gold deposits. The six major gold-bearing tellurides are calaverite (AuTe2), sylvanite [(Au, Ag)2Te4], montbrayite [(AuSb)zTe3], krennerite [(Au1-x, Ag,)Te2], petzite (Ag3AuTe2) and muthmannite (AuAgTe2) [2]. While several other phases exist they are much more complex (i .e. buckhornite), which dilutes and confuses the influence of each specific component. Studies of gold tellurides have predominantly focussed on calaverite as it is the simplest and most common phase, however petzite, commonly found in Australia and North America, is the focus of this investigation.Gold processing via cyanidation has been operated for more than a century and is a highly effective hydrometallurgical treatment of native gold deposits. However, some gold alloys such as tellurides have proven to be somewhat less responsive under the same conditions. Several groups have shown that gold/silver tellurides are amenable to cyanidation, but are significantly more refractory than native gold [3]. Pre-oxidation steps have been tested to remove constituents that would consume cyanide such as sulfides. Such species are also linked to the precipitation of oxidised telluriwn, forming a passive layer, further inhibiting gold recovery [2]. It is uncertain to the definite reasons underpinning the refractory nature of precious metal tellurides in conventional cyanidation."

Jan 1, 2012

By Patrick R. Taylor

The synthesis of high-purity ultra-fine barium strontium titanate powders (BST: BaO6Sro.4TiO3) has been performed in a non-transferred are D.C. thermal plasma reactor. Slurries of aqueous solutions of dissolved barium and strontium nitrates and solid titanium dioxide powders were used as precursors. Oxygen and argon were used as carrier gases, and pure argon and combinations of argon and nitrogen were used as plasma gases. The plasma torch power was varied, as well as the oxygen flow rate and the total molar concentration of the precursors. A graphite plate was designed to protect the torch electrode and lower the level of impurities in the product. A thermochemical analysis of the Ba(NO3)2-Sr(NO3)2-TiO2-H2O-O2 system was performed to predict the conditions for the formation of BST and the feasibility of the reaction, The powders collected from the different sections of the reactor were characterized using Transmission and Scanning Electron Microscopy, X-Ray Diffraction, and ICP chemical analysis. The powders produced showed high conversion to BST, ultra-fine particle size (< 30 rim) and high purity, which makes this a potential process to produce ceramic materials for electronic devices.

Jan 1, 2003

Rapidly solidified TiAl-Cr-xNb-Y(x=2,4,6, at.%) alloys have been produced using a single roller melt spinning method. The microstructure of alloy ribbon was refined and component became more homogeneously by rapid solidification technology. There were two phases in alloy ribbons, including -TiAl and 2-Ti3Al phases, yet the amount of 2-Ti3Al phase in matrix obviously increased by rapid solidification than cast alloys. The micro-hardness testing also carried out. Compared to the cast alloys, the alloy ribbons have much higher hardness.

Jan 1, 2009

By Gi-Chun Han

This study focused on stabilization of heavy metals and removal of chlorine in MSWI bottom ash by artificial carbonation with washing. Artificial carbonation was carried out by applying CO2(g) injection in washing for fractions above and below 4mesh for reuse as construction materials like aggregate, As a result, carbonation with washing could satisfy Korean environmental regulation and remove chlorine in bottom ash more effectively by resolving residual friedel?s salt(3CaOAl2O3CaCl210H2O).

Jan 1, 2006

By W. B. Carter, A. T. Hunt, G. W. Book

"Combustion Chemical Vapor Deposition (CCVDSM ), an open air, flame assisted CVD process, is under development. The CCVD process produces non-line-of-sight, epitaxial deposition. Materials deposited include YBa2Cu3Ox' Y2BaCuOx, BaTiO3, Y2FesOI2, ZrO2, yttria stabilized ZrO2 (YSZ), partially (yttria) stabilized ZrO2 (PSZ), and amorphous silica. Two modifications of the CCVD process are being studied. Liquid fuel CCVD deposition, involves the combustion of an organic solvent that contains dissolved reagents carrying the desired coating cations. Gaseous fuel CCVD deposition uses a flammable gas as fuel. A non-flammable solution containing dissolved reagents is either aspirated into the flame or mixed with the fuel gas as an aerosol prior to its combustion. Substrates to be coated are held near the flames' ends.IntroductionThin films and coatings can be deposited using a wide variety of techniques including chemical vapor deposition (CVD). CVD is ""a materials synthesis process whereby constituents of the vapor phase react chemically near or on a substrate surface to form a solid product.""lIn conventional CVD processing, gases carrying coating constituents flow into a reaction vessel where deposition occurs onto a heated substrate. The deposition process is often conducted at reduced pressure. Both cold and hot wall reaction chambers are used. Heat can be provided by a resistance furnace, rf induction, or high-intensity radiation lamps. Plasma, microwave, photo, laser, RF, and electron-enhanced CVD processes have been developed. The necessity of using a reaction vessel limits the substrate size and affects coating economics. Although most CVD depositions are performed as batch processes, continuous deposition can be accomplished with the use of appropriate hardware.The chemical vapor deposition of thin, dense oxide films has been accomplished in the open atmosphere with a flame assisted process. The process is called combustion chemical vapor deposition (CCVDSM).2 Two modifications of the CCVD process have been developed. The liquid fuel CCVD process involves the combustion of an organic solvent in which reagents (containing the coating cations) are dissolved. The gaseous fuel CCVD process uses a flammable gas as fuel. In this modification, a non-flammable solution containing dissolved reagents is either aspirated into the flame or mixed with the fuel gas as an aerosol of small droplets prior to its combustion. Substrates to be coated are held near the flames' ends."

Jan 1, 1994

"Mineral flotation processes are often characterized by long dead times and slow process dynamics. The process dynamics change due to different ore types, feed grades and circulating loads. These are some of the factors that can make control of flotation processes difficult. Implementation of adaptive control algorithms at Brunswick Mining has made controlling these processes feasible. The role of adaptive controllers in plant optimization and the overall control philosophy is discussed.IntroductionBrunswick Mining is located just outside of Bathurst, New Brunswick, Canada. The concentrator processes approximately 10,250 tonnes per day of ore that assays at approximately 8.9 %Zn, 3.6 %Pb, 0.3 %Cu and 100 gram/tonne of Ag. The four products produced are zinc concentrate assaying 51 %Zn, lead concentrate assaying 36 %Pb, copper concentrate assaying 21 %Cu, and a bulk concentrate assaying 32 %Zn and 18 %Pb.The original flotation process control system, supplied by Outokompu Oy of Finland, was replaced in the summer of 1988 by a Provox system supplied by Fisher Controls Inc. The Provox system consists of two redundant integrated function controllers (IFC's), two operator console stations with two screens each and a Digital Equipment Co. microVax II computer running Fisher's Computer Highway Interface Package (CHIP).In January 1989 a boiler management package, which includes the boiler control hardware and another operator's console, will be added to the Provox system. In late spring of 1989, a Vax 3200 computer running G2 artificial intelligence software from Gensym Corporation will be installed. These devices are all connected using a redundant data highway that runs around the plant.The primary measurement devices in the flotation circuit are two Courier on-stream X-ray analyzers. The Courier systems each have 14 sample cells with two streams multiplexed into each cell. Each pass of the on-stream head takes approximately 6 minutes yielding a nominal sampling interval of 12 minutes. The Courier passes its assays to its respective IFC. The IFC handles the digital and analog I/O, DDC and cascade loop control, some low level calculations and sequencing. The CHIP microVax has 9MB of memory and 220MB of mass storage running under the VMS operating system. The CHIP microVax is a central database for the Provox system. It is used for data trending, metallurgical modelling and balancing, instrumentation database, long term storage, and on-line adaptive assay control."

Jan 1, 1989

By Lucas Nana Wiredu Damoah, Lifeng Zhang

"The use of electromagnetic field to remove suspended particles from metals such as aluminum by pushing to the boundary has been well studied. However, the potential of this method is yet to be exploited for the removal of inclusions from silicon. Considering the increasing amount of Top-cut SoG-Si scraps year upon year, there is the need to harness all the potentials of technologies to recycle this materials to ensure sustainability. This study investigates, and discusses new results on the effect of processing parameters such as composition, coil current, and frequency on the removal of inclusions from silicon under high frequency AC electromagnetic field.IntroductionThe solar cell silicon making industry requires pure and clean silicon in order to maximize the conversion potential of the solar cell material. The conversion efficiency of solar cells is limited by minority carrier recombination at dislocations and those intra-granular defects such as impurities, small clusters of atoms, or precipitates [1]. Recent global developments in the energy sector with a drive for the production of clean, reliable, and affordable energy have stirred a rapid growth in the production of photovoltaic (PV) cells.[2] Thus over the years, silicon based PV cells has seen a lot of growth as it has a PV market share of over 90 % [3] either as single-crystalline silicon, or multi-crystalline Si (MC-Si), or amorphous Si [4]. MC-Si produced by directional solidification of solar grade silicon melt dominates the silicon PV market. During the directional solidification process, SiC and Si3N4 particles within the melt are pushed by the solidification front to the top of the ingot which is the last to solidify. Therefore the top of the ingot is cut generating what is known as top-cut solar silicon scraps. The Si3N4 particles are mainly from the coating material at the inside surface of the silica crucible and from the air absorption during solidification process. The SiC particles mainly stem from the carbon reduction process of the primary production of silicon [5]. For sustainability the silicon in the top-cut silicon scraps must be recovered. Therefore methods for removing non-metallic particles, such as SiC and Si3N4, from the silicon are important in order to recycle the top-cut scraps to a useful feedstock for the silicon solar cells manufacturing."

Jan 1, 2012

By Donald L. Stewart, Ken Overfield, Edward M. Williams

"Recent increases in energy cost have lead to a renewed focus on energy efficiency during aluminum melting operations to reduce fuel usage. The goals of a batch melting operation are to melt the charge using the minimum required energy, to melt the metal to the required temperature within the required timeframe, and to avoid generating unwanted contaminants by overheating the charge.The heat transfer efficiency of a conventional hydrocarbon fired aluminum melting furnace varies over the course of the melt cycle, depending on the conditions in the furnace. The purpose of this work was to develop a method of determining the transient heat transfer efficiency throughout the furnace cycle and to take advantage of this knowledge to optimize the melting process through furnace controls and proper production operations. This furnace survey methodology has been developed and used to evaluate a number of furnaces.Description of a Typical Batch Melting Furnace CycleA typical batch melting furnace cycle will consist of three stages:1. Charging – Solid metal charged through an open roof, solid or molten charged through an open door, and/or molten poured through a furnace blister2. Melting – From the time the door or roof is closed and the burners are turned to high fire until the charge is all liquid and has reached a temperature suitable for alloying (typically ~1350 °F / 730 °C)3. Holding – From the end of the melting stage until transfer or casting is completeIn some cases, further charging can take place after the melting cycle has started. This can happen when the entire solid charge will not fit in the furnace in one load, or if additional molten metal is added while the charge is melting. The bulk of the energy used in the melter is consumed during the melting cycle. The thermodynamic minimum energy requirements for melting pure aluminum are:• Energy required to heat pure aluminum from room temperature to the melting point at 1220°F (660°C) is 288 BTU/lb (670 kJ/kg)• Energy required to change state of pure aluminum from solid to liquid (heat of fusion) is 171 BTU/lb (397 kJ/kg)• Energy required to heat molten from melting point at 1220°F (660°C) to 1350°F (730°C) is 36 BTU/lb (83 kJ/kg)• Total energy required to melt a solid charge from room temperature to 1350°F (730°C ) is 495 BTU/lb (1151 kJ/kg)"

Jan 1, 2009

By Tetsuya Uda, Sakae Shirayama

"With the aim of producing nickel (Ni) metal directly from acidic aqueous solution containing cobalt (Co) and other impurities, selective reduction of Ni was examined. As a preliminary experiment, sodium hypophosphite monohydrate (NaH2PO2·H2O) was selected as a reductant, and reacted with aqueous solution containing 0.1 mol L-1 nickel sulfate (NiSO4·6H2O) and 0 ~ 0.05 mol L-1 cobalt sulfate (CoSO4·7H2O) for 3 hours at 90 °C. As a result, it was revealed that Ni was selectively reduced and separated from Co in the acidic region (pH= 4.8). In this study, differences of reduction behavior between Ni and Co were investigated, and the feasibility of Ni I Co separation by the selective reduction of Ni was discussed.IntroductionEfficient Ni condensation and separation from Co are essential in nickel hydrometallurgical processes. Currently, the hydrometallurgical production of Ni from oxide ore is mainly carried out by acid leaching at elevated temperature, followed by the removal of impurities using neutralization, and condensation of Ni and Co into intermediate products such as hydroxides and sulfides. Then, the intermediate product is dissolved in acid aqueous solutions, and Ni I Co separation is conducted by solvent extraction. Finally, Ni and Co are recovered by electro-winning. This complicated process consumes large amounts of alkali, hydrogen sulfide (H2S), and organic solution in a multiple-staged process'. To reduce the consumption of these chemicals, it is important to recover Ni more efficiently from acidic aqueous solution containing impurities."

Jan 1, 2014

By Suguru Kohno, Yoshihiro Momose, Masakazu Honma, Tokirou Kamosawa

Copper metal surfaces have been examined by an extremely sensitive surface analysis technique called temperature programmed photoelectron emission (TPPE). The surfaces were ultrasonically cleaned and subsequently abraded by a screw in organic solvents and water. The TPPE apparatus is composed of a Geiger counter with Q gas (He+ iso-C4H10). The curve of photoelectron emission (PE) intensity vs. wavelength from 300 to 170 nm, termed PE spectrum, was repeatedly measured at different temperatures in the temperature- increase process from 25 to 350°C. The number of emitted electrons in a PE spectrum (PE total count) increased, reached a maximum at-250°C, and decreased with increasing temperature. With the surfaces cleaned alone in the liquids the maximum PE total count decreased in the order C3H70H > (CH3) 2CHOH > C2HpH > CHPH > H2O. With the mechanically abraded surfaces in the liquids the maximum PE total count changed as a function of the abrasion period and the maximum tended to appear at higher temperature with increasing abrasion period; the maximum value at 10-min abrasion decreased in the order H2O > CHpH > C2HPH > (CH3) 2CHOH > n-C3HpH. It was suggested that the TPPE behavior can be related to the acid-base interaction between the alcohols and the abraded metal surfaces and the presence of a contaminant over layer on the surface. From the XPS analysis of the 01 s spectra it was suggested that the chemical change of the adsorbed oxygen to oxide oxygen with temperature plays a substantial role in the appearance of the maximum PE total count.

Jan 1, 2000