By A. H. Larson, R. J. McClincy

Laboratory-scale decopperizing experiments with multiple sulfur addifions were conducted at 330°C on ternary Pb-Cu alloys containing, as the third elenlent, Sn, Ag, As, Sb, Bi, Zn, and Au, common impurities in lead blast-furnace bullion. For silver and tin, an increased rate and extent of 'cofifier removal was obsert3ed. The elements As, Sb, Zn, Au, and Bi had no effect or less effect as compared to sulfur additions with no i)npurily additions. THE production of primary lead in the blast furnace yields an impure lead frequently containing such impurities as copper. antimony. arsenic. tin, gold, silver iron, oxygen. and sulfur. By cooling this lead to a temperature near its melting point. most of the iron, sulfur, and oxygen and part of the other impurities are removed in the form of a dross. With incipient solidification of the lead, the copper concentration wil have been reduced to 0.02 to 0.05 pct. depending upon the concentration of the other impurities. according to Davey.' Since copper interferes with the treatment of silver after the desilverizing process, it is desirable to decrease the copper content of the lead still fur-ther before the lead is desilvered. The decopperizing of the lead is accomplished by stirring a small quantity. approximately 0.1 pct. of elemental sulfur into the lead at a temperature near its melting point, 330" to 360°C. The copper is removed as a copper sulfide which constitutes a small fraction of a voluminous dross consisting mostly of lead sulfide and entrained metallic lead. The residual copper concentration following the decopperizing operation is frequently as low as 0.001 to 0.005 pct. Thi fact has aroused considerable interest because the equilibrium copper concentration of lead in contact with solid PbS and solid Cu2S is at least an order of magnitude greater, 0.05 pct Cu at 330C. 1, 2 Most investigators have suggested that various impurities in the lead bullion are responsible for the very low copper concentrations frequently encountered in practice. There is little agreement, however? as to which of the impurities are helpful and which are not.3"11 Also. few investigators have sought to explain the mechanisms responsible for the removal of copper to very low concentrations. Willis and Blanks9 have proposed that a nonstoichiometric copper-deficient cuprous sulfide forms in place of the supposed Cu2S. Being copper-deficient, this sulfide phase would possess a low copper activity, and the diffusion of copper dissolved in the liquid lead into this phase would be greatly facilitated. Pin and wagner2 have investigated the removal of copper from liquid lead by studying the effect of impurity-doped lead sulfide on the decopperizing of pure Pb-Cu alloys. Samples of the doped PbS were held in contact with copper-saturated lead for 1 week at 33'7°C. They reported a beneficial effect on decopperizing with bismuth and antimony and no effect with tin or silver. which is directly opposite to the results observed in practice and those reported by Davey 3 and this studv. The purpose of this paper is to describe the effects of certain additive elements on the extent to which copper can be removed fro111 liquid lead by successive additions of sulfur. The impurity elements were added individually to prepared Pb-Cu alloys. The resulting ternary alloys as well as a binary Pb-Cu alloy were then decopperized with repeated additions of sulfur. EXPERIMENTAL Materials. Granulated test lead with a purity of 99.999 pct and the additive elements Cu. Ag. Sb. Bi. Zn. Sn. and Au with purities of 99.99 pct were American Smelting and Refining Co. research-grade materials. The major impurities in the lead were 1 ppm each of iron and copper. all others being less than 1 ppm. The arsenic used was a technical-grade arsenic of 98+ pct purity. Reagent-grade flowers of sulfur were melted under argon to provide small pieces free of fines. Apparatus. The decopperizing experiments were carried out in a 25-mm-OD by 375-mm-long Pyrex tube sealed at one end. The tube was mounted vertically in a resistance-heated. hinge-type tube furnace controlled to within ±lcC. Temperature measurement was accomplished by means of a standardized chromel-alumel thermocouple sealed into the base of a silica. paddle-type stirring rod. All decopperizing experiments were carried out under an argon atmosphere. Procedure. A Pb-Cu starting alloy containing 0.05 pet Cu was prepared under carbon and poured into cold tap water to produce shot. The ternary alloys were prepared by melting together 100 g of the starting alloy and a sufficient amount of the impurity element to yield the desired concentration. The resulting alloy was then homogenized in a Pyrex tube at 450C with continuous stirring. The furnace temperature was then lowered to the operating temperature of 330°C. When thermal equilibrium had been obtained at the operating temperature, individual additions of 0.2 pct (0.2 g) of solid sulfur were added to the melt and stirred in. Stirring was continued for a period of 3 min. discontinued for 5 min. and resumed for the remaining 2 min of a 10-min cycle. This cycle was repeated for as many sulfur additions as desired. When the decopperizing experiment had been completed the lead bullion was quenched and samples of the bullion and dross phases were taken for analysis. Results. The results obtained in the decopperizing

Jan 1, 1970

By G. R. Love, M. L. Picklesimer

Aboue 950°C the Nb-Zr system consists of a completely miscible bcc solid solution, commonly called the phase. Between 950 and 600°C, and between 20 and 85 pct Nb, the phase deconlposes, after sunciently long times, into two bcc solid solutions. The pct Zr alloys are conveniently descibecl with T-T-T (time-temperature-transformation) curves having a nose at about 2 hr at 700°C. The reaction rate varies only slowly with zirconium content and negligibly with oxygen contanzination; it is speeded up by a factor of 10 to 15 by 90 pct cold ulork and slowed dou by n factor oj 10 to 30 by a two-hundrecljold increase in grain size. Nb-r alloys with compositions between 40 and 85 pct Nb have been the basis for the majority of commercially important superconducting materials. In part because of their commercial promise, more is known about these alloys than about most other high-field superconducting materials. At the same time, there is considerable disputed or incomplete metallurgical information. For example, although Rogers and tkins&apos; indicate a monotectoid reaction at approximately 600°C and a two-phase 01 + 0, field extending between 20 and 85 pct Nb and to a maximum of 95OGC, erhout&apos; has reported that this entire region would be a single homogeneous B were it not for oxygen contamination. Again, although it has been shown that relatively short-time heat treatments in the vicinity of 700CZ significantly improve the ability of short wire samples to carry high currents in high magnetic fields at 4.2K, these observations have never been fully correlated with the structural change or changes occurring during the anneal. We intend to investigate in detail the effect of metallurgical variables, including heat treatment, on the superconducting properties of hard superconductors. To verify that our experimental techniques are valid and to establish a relative standard against which other materials may be measured, we feel it advisable to know the behavior of the Nb-Zr alloys under a variety of processing conditions. As an initial step toward this goal, we have determined in detail the kinetics of the transformations in Nb-Zr alloys. EXPERIMENT A number of problems had to be solved before beginning any fruitful work on the reaction kinetics in this system. While solving some of these problems, either by chance or by design, small amounts of information were obtained about alloys containing 40, 50, 60, 65, 67, 70, and 75 pct Nb, bal. Zr. In addition, a large range of grain sizes and a range of temperatures considerably greater than the range indicated by Rogers and Atkins phase diagram were examined. We will, however, report in detail only the results obtained for the Nb + 33 pct Zr and Nb + 25 pct Zr alloys at three grain sizes, two levels of oxygen contamination, and the temperature range 550 to 950°C. These data are most complete, but the other data are sufficiently complete to indicate the kind and magnitude of the variation of the transformation kinetics outside this range. The first and most difficult problem encountered in this inquiry was one of sample homogeneity. When Nb-Zr alloys are arc- or electron-beam-melted on a cooled copper hearth, solidification is sufficiently slow that there is appreciable coring in the cast structure and a large variation of grain size across the button thickness. Both these factors significantly affect the apparent reaction rate in the system. A two-step solution to the problem was attempted; an arc-melting and drop-casting technique has been developed by conald that greatly reduces the as-cast grain size and virtually eliminates coring segregation. Ingots made in this way exhibited no detectable (3 pct maximum) zirconium segregation. Before it was evident just how good this technique was, we attempted to supplement it with rather long-time, high-temperature annealing of the cast ingots. This annealing was carried out in evacuated and sealed (seal-off pressures < 1.0 x 106 torr) quartz capsules lined with tantalum foil at 1400 to 1450 C for 8 to 72 hr. There were two principal effects of this treatment: the grain size increased to a fairly uniform 150 p, and the surface and all grain boundaries near the surface acquired a film of a second phase, tentatively identified as an oxide (possibly additionally contaminated with silicon). There was no evidence that this 1400 C treatment had affected the zirconium segregation. High-temperature annealing was subsequently used only for grain-size control, but anneals of longer than 4 hr at temperatures greater than 1000°C were performed in dynamic vacuums (pressure no greater than 1.0 x lo torr). Any contamination resulting from these treatments was well below the limits of detection of our techniques. All samples, as cast, were cold-swaged to at least 85 pct reduction in area. The samples called cold-worked were tested as swaged. The minimum re-crystallization anneal for these alloys was about 12 hr at 1050 C; this produced an equiaxed grain diameter of about 4 to 8 P. Annealing for 4 hr at 1450°C produced a grain size of about 80 to 150 p; and annealing for 4 hr at 1650aC, close to the melting point of many of these alloys, produced a grain size of 0.5 to 1.0 mm. At all temperatures, the larger grain size was

Jan 1, 1967

By Oren C. Baptist, Carlon S. Land

Laboratory research has been conducted to evaluute the effect of clay hydration on the permeability to gas of water-sensitive reservoir sands. Samples of a .sandstone containing trace amounts of montmorillonite and a sample of montmorillonite were .studied in the laboratory to detertnine whether swelling or dispersion was the cause of permeability reduction in these samples. Heliuin, containing various amounts of water vapor, was used to hydrate the clay minerals and to determine the gas permeability at various stages of clay hydration. The amount of water adsorbed by the samples using this method is small. The nonwetting-phase permeability at higher water saturations war investigated by saturating the with water and measuring the permeability to humid helium while decreasing the water saturation, Relative-permeability curves obtained from results of these procedures were used to estimate the effect of the swelling of trace amounts of mont/tlorillonite on the permeability of the .samples. Most of the damage to the permeability when reservoir sands containing trace amounts of montmorillonite are exposed to fresh water is due to dispersion and movement of clays. Blockage of pores by the increased volume of expanded montmorillonite is believed to result in permeability damage that is small in comparison to the observed damage to the samples tested. INTRODUCTION Studies have shown that permeability is severely damaged when sands containing only small amounts of montmorillonite are contacted by fresh water.15 When samples of sands containing large amounts of montmorillonite are placed in fresh water in the laboratory, these samples may completely disintegrate, forming an unconsolidated mass of larger volume than that occupied by the dry sample." In this case, it is apparent that the swelling of montmoril-lonite has destroyed the pore structure of the sand. If only a trace of montmorillonite is present in a sand. samples may remain intact when saturated with water, although the permeability to water is a small fraction of the gas permeability of the dry sample. Many workers in the field of water sensitivity have attributed this reduction in permeability to the blocking of pores and reduction of pore size by the increased volume occupied by expanded mont- niorillonite. if the sand contains a detectable amount of montmorill&apos;onite or mixed-layer clay containing rnontmorillonite. Logically3 the smaller amount of montmorillonite present in a sand, the smaller should he the effect of montnlorillonite swelling on permeability; however, the quantity of montmorillonite sufficient to cause severe damage by swelling is not known. Although hundreds of samples have been tested in our laboratory, no correlation has been established between the amount of montmorillonite in samples and the permeability reduction caused by fresh water. To many petroleum engineers, the phrase "clay swelling" is synonymous with "water sensitivity", or "permeability reduction" implying that any formation damage due to the hydration of clays is caused by swelling. Although all clays adsorb water on their surfaces, montmorillonite is the only clay mineral commonly found in reservoir rocks which adsorbs water between intercrystalline layers, resulting in expansion of the clay particle. As montmoril-lonite swells, the first few layers of water adsorbed between platelets are strongly held and well oriented, and the montmorillonite retains its crystalline structure, although expanded. As swelling of sodium montmorillonite continues, the platelets become farther apart and the forces orienting the platelets in the crystalline structure become weaker, resulting in a less orderly orientation of platelets. In an abundance of water, small groups of platelets may become detached from the original monl-rnorillonite particle and may be dispersed throughout the water phase. Because of its swelling properties, sodium montmorillonite is very easily dispersed in water. Particles of other clay minerals. such as illite and kaolinite may also be dispersed in water. causing water sensitivity of sands not containing montmorillonite. The presence of an immobile layer of water adsorbed on the surface of clays has been considered a possible cause of the low permeability to water of dirty sands. Grim states that the thickness of the layer of immobile water held by sodium montrnorillonite is three nlolecular layers or 7.5 A (angstroms), with some orientation of water extending to 100 A. Assuming a very thick, immobile water layer adsorbed on the surface of a pore represented by a capillary tube, the maximum effect of the water layer on permeability can be calculated. Using a pore radius of 10 &apos; cm and an immobile water layer of 50 A. the calculation shows the permeability to be reduced only 2 per cent. Similar calculations can be used to show that the effect of electro-osmotic counterflow is of the same order of magnitude as that of bound water. The reduction of the permeability to water by either an immobile water layer

Jan 1, 1966

By H. O. Jahns

This paper describes the application of regression analysis for obtaining a two-dimensional areal description of heterogeneous reservoirs from short-term pressure-time data such as that obtained in interference tests. The method replaces the time-consuming trial-and-error procedure commonly used to match field data on an electric analyzer or digital computer with a systematic search which is programmed for a computer. The computer program adjusts the properties of a reservoir model automatically until a least-squares fit is obtained between observed and calculated pressure data. The reservoir is simulated by a single-phase, compressible, two-dimensional model. It is divided into a number of homogeneous blocks whose transmissibility (kh/F) and storage (Fch) values are varied to obtain the least-squares fit. The reliability of these values is determined from their standard deviations and correlation coefficients. Although the method is rigorously applicable to single-phase flow only, multiphase flow can be handled provided saturation changes are small during the test. Possibly the method can also be used to obtain a reservoir description from pressure-production history, but this application is outside the scope of this work. The paper includes, in addition to a description of the numerical procedure, a discussion of some of the problems associated with the method. Rules are given to help in selecting the number of homogeneous blocks and deciding upon their arrangement. The uniqueness of a reservoir description is considered. Finally, the use of the method is illustrated by the interpretation of field data from two interference tests. INTRODUCTION Pressure data from short-term transient tests, such as single-well and interference tests, are widely used to obtain reservoir properties. These tests are usually analyzed by assuming a simple reservoir model; very often, a homogeneous one is used. As a result, analysis of the transient data from each well frequently gives different values for reservoir properties. The problem then arises to combine all these differing results into a more detailed picture of the reservoir. One technique is to simulate the reservoir with a digital computer or with an electrical analyzer and to adjust the reservoir parameters by trial and error until the simulated pressure data are in reasonable agreement with the observed pressure data for all wells. Although this method has been used for both transient tests and pressure-history data, it is time-consuming and subjective. A second technique uses regression analysis to replace the trial-and-error procedure with a systematic search that can be programmed for a digital computer. Use of regression analysis in reservoir description was proposed recently by Jacquard and Jain.1 They divided the reservoir into a number of homogeneous blocks whose properties are varied until a least-squares fit is obtained between observed and calculated pressures. However, they did not consider their technique to be operational, mainly because of ".. .(I) the lack of experience in using the method .. . notably for the improvement of convergence; and (2) limitations imposed by the insufficiency of available computers". 1 While the analysis presented in this paper applies the same general principle used by Jacquard and Jain, the specific method is significantly different. Some differences are (1) the regression problem is solved in a different way which requires less computer time in most cases; (2) a stepwise solution, in which the detail in the reservoir description is increased from step to step, is used to improve convergence; and (3) the reliability of the estimated reservoir .properties.. as measured by their standard deviation and correlation coefficient, is estimated&apos;

Jan 1, 1967

By Marius S. Darrow, William B. White, Rustum Roy

The PbS-PbTe systen has been studied by quench-ing and D.T.A. techniques f?om 400&apos; to 1150°C. Runs were made in evacuated silica tubes so that all equilibria are at the vapor pressure of the system. Lattice parameters of the quenched salnples , measured by X-ray diffraction, show a complete crystalline-solution series existing over a narrow temperature range between approximately 805" and 871°C. An exsolution dome extends from a maximum of about 805"C (approximately 30 mole pct PbTe) to 1 and 96.5 pet PbTe at 400°C. A narrow melting region, deternined by D.T.A., extends form 918c (mp PbTe), The shapes of the liquides and solidus curves imply the existence of a minimum at 871°C at approximately 65 pct PbTe. THe exact composition of the minimum could not be established due to the very narrow two-phase region. At compositions containing less than 50 pet PbTe, liquidus temperatures begin to increase, while the solidus remains almost flat to about 15 mole pet PbTe before beginning to vise toward the mp of PbS (1075 C). LEAD sulfide and lead telluride are isostructural (NaC1 type) semiconductors whose electrical and optical properties have been extensively studied and used in recent years. If appreciable crystalline solution exists between these compounds, the variation of physical properties with composition could be of interest. The purpose of this investigation was to determine the extent, if any. of crystalline solution, and to obtain the phase diagram for the system. To the knowledge of the authors, only three studies of the system PbS-PbTe have been reported, and, in chronological order, each investigation found an increasing amount of crystalline solution. In 1956, Yamamoto reported finding no evidence of crystalline solution between the compounds. Sindeyeva and Godov-ikov,&apos; in 1959, found very limited crystalline solution. but only under conditions of excess tellurium concentration. Finally Melevski s3 investigation in 1963 indicated that one solid phase exists in the region from PbS to 7 pct PbTe and from 82 pct PbTe to PbTe at 886&apos;C, with an eutectic at 55 pct PbTe at that temperature. Detailed data on the solvus boundary were not given. EXPERIMENTAL EQUIPMENT AND MATERIALS Commercially produced PbTe and PbS powders were used as starting materials. Batches of specific mole percent composition were accurately weighed and mixed in a plastic bottle, in a shaker mill. An analy- sis of impurity content is given in Table I for pure PbS and PbTe and for two randomly selected batches after the powders were mixed. Individual samples, ranging in weight from 0.2 to 0.5 g, were sealed in evacuated silica tubes which had been thoroughly washed and rinsed with acetone and distilled water. Thus all data taken were at the pressure of the system. Subsolidus relations were studied down to 400°C by heating the samples in a vertical tube furnace for 24 hr. The sealed tubes were quenched in water with quench time from the hot zone not exceeding 1 sec. Temperatures were measured by a chromel-alumel thermocouple and controlled to 53°C for most runs. The number and composition of phases present were determined from powder X-ray diffraction patterns taken at room temperature on a Norelco diffractome-ter, using silicon as an external standard. Above 850°C quenching techniques were, in general, found to be unsatisfactory, and differential thermal analysis (D.T.A.) was used to determine melting relations. The evacuated tubes were recessed about 1 cm at one end to accommodate the differential thermocouple. Al203 was used as the reference material in a similar tube containing the other side of the differential couple. For temperature measurements, a separate thermocouple was placed in the recess of the tube containing the sample to be measured, thus providing an opportunity to obtain thermal, as well as differential, analysis. All thermocouples for these measurements were Pt-Pt 10 pct Rh. Temperature and differential curves were recorded separately on synchronized strip-chart recorders. Thermocouples and recording equipment were calibrated using NaCl and gold standards, using the melting points 801" and 1063 C, respectively, which span most of the temperature range of interest. Heating and cooling rates generally were from 4 to 7°C per min. It was found, in fact. that rates ranging from 1.5 to 25°C per min did not significantly change the data obtained.

Jan 1, 1967

By Ottar Dragge, C. Danielsson, Bo Kalling

THE desulphurizing of pig iron has been accomplished with a number of different additions. The oldest and still most commonly used agent is soda, the extensive use of which commenced about 1925, when it was used principally for cupola furnace iron. More recent experience&apos; seems to show that better results can be obtained with sodium hydroxide. The well-known desulphurizing properties of lime have also been exploited in different technical processes. Another material with even more powerful effect is calcium carbide.&apos; The desulphurizing ability of manganese, when added to the ladle in sufficient quantity, should also be mentioned in this connection. During recent years increasing attention has been paid to the desulphurizing properties of metallic magnesium." An addition of a suitable alloy of magnesium is now in use purely for the purpose of sulphur elimination. Of the desulphurizing agents mentioned, lime is by far the cheapest, provided that the reaction can be brought about rapidly and completely. Therefore, a method that makes full use of the desulphurizing ability of lime may be able to compete with other processes. A method developed at the Dom-narfvet Iron and Steel Works (Sweden) will be described, which enables pig iron to be rapidly desulphurized to very low sulphur contents by using a burnt lime powder. as the desulphurizing agent. Lime in Older Processes In cases where lime has been used for the desul-phurization of pig iron, it has generally not been used alone, but mixed with other substances such as fluorspar, to obtain the formation of a molten slag during the process. This method has been tried by Tigerschiold,&apos; who treated the iron with a lime-fluorspar mixture, the stirring of the iron being brought about inductively with low frequency alternating current. Very good results were obtained. A process of this type has also been suggested by R. P. Heuer, U. S. A. The principles of this method, which has been tested in Great Britain by Newell. Lanener. and Parsons." re that a mixture of lime and fluoispar is added to the hot metal in the ladle, while a powerful stream of nitrogen gas is blown into the bath to produce the required intermixing. The results of the tests were unsatisfactory, however. A similar process has been developed at The Steel Co. of Canada, according to a statement by H. M. Griffith.&apos; Here the tests were carried out in a carbon-lined ladle provided with carbon tuyeres in the side wall for blowing nitrogen into the bath. The addition consisted of about 20 lb of a mixture of burnt lime and fluorspar per ton of pig iron. Good results appear to have been achieved. The sulphur content of the pig iron is stated to have been reduced from 0.025 to 0.050 pct down to 0.006 pct. Various methods of desulphurizing pig iron have been tried using lime powder without fluxing material for fusing. Eichholz and Behrendt7 have experimented with blowing a powdered limeicoke mixture with air into the ladle. Their results were, however, not conclusive and the experiments do not appear to have been continued. Similar experiments have been carried out at Domnarfvet, using nitrogen instead of air in order to avoid oxidation. But these attempts were not particularly successful. It appears to be difficult to achieve the required agitation by this means. The strong cooling effect of the gas on the iron is also a serious drawback. A method in many respects similar to that tried at Domnarfvet was tried by Eulenberg and Krus at the end of the 1930&apos;s. Here again desulphurization was carried out with lime alone, brought into contact with the molten iron in a rotary furnace. The temperature was kept at the required level, 1400" to 1500°C, by the introduction of a pulverized coal burner in one end of the furnace. The speed of rotating was not given. A paper by Bading and Krus states that, in one of the first experiments, the sulphur content in 56 tons of pig iron was brought down from 0.186 to 0.035 pct in 117 min, but that a considerable shortening of the time would be possible. According to later reports by Eichholz and Behrendt,&apos; it should be possible by this process to achieve a desulphurization speed of 0.35 pct S per hr for a consumption of 6 to 10 pct limestone and 2 to 3 pct coke, as fuel exclusively. The final sulphur content is, however, not stated. Domnarfvet Method After a number of different procedures had been investigated, the tests at Domnarfvet were directed to desulphurization with lime in a rotary furnace. Before going into the practical details of the method, the theoretical aspects will be discussed briefly. If the pig iron does not contain alloying elements other than carbon, the reaction can be expressed most simply by the usual equation: FeS + CaO + C = Fe + CaS + CO [I] 4H,. ~ 34,000 cal That this reaction can be carried through to a very complete desulphurization of pig iron has been shown by OelsenD in a discussion in connection with the Eulenberg and Krus&apos; method. He mentions two laboratory tests, in one of which the sulphur content in the pig iron at 1400°C was reduced from 0.540 to 0.006 pct after treating with 3.35 pct lime. The pig iron had a low manganese content, but other analysis is th. given. Mention also should be made of the recently published investigations by Fischer and Cohnen&apos;" dealing with the influence of the carbon content of the iron on desulphurization with lime, although in this case fluorspar was added also. The tests show that efficient desulphurization is possible with lime in the steel bath, provided that the carbon content is sufficiently high. The temperature employed in these tests was considerably higher (1620") than that normal for treatment of pig iron. The author concludes that the product S% X C% - 0.011 at the temperature in question.

Jan 1, 1952

By L. F. Mondolfo, B. E. Sundquist

The crystallographic orientation relationships resulting when lead is nucleated from the liquid by Ni, Cu, Ag, and Ge were determined. For each nucleating agent several definite orientatioz relationships were found. These relationships seemed to be controlled by good symmetry relations and low crystallographic disregistry between mating planes. For any given nucleating agent the under colling for nucleation was found fairly constant and independent of the orientation relationship and consequent disregistry. It was also found that, upon re melting and refreezing the Pb, the orientation relationship was changed. These findings prove that crystallographic disregistry is not the controlling factor in heterogeneous nucleation from the liquid. The results of this investigation tend to confirm the theory presented in a preceding paper that heterogeneous nucleation starts with the formation of an adsorbed layer of nucleated metal on the nucleat-ing impurity. Evidence is given that cavities in the nucleating agent act as centers of nucleation. IT has long been known&apos; that solid extraneous particles are active in catalyzing phase transformations that occur in a system, particularly condensation and crystallization. It is well established that these heterogeneities act as catalysts by providing surfaces upon which nuclei of the precipitating phase can form with activation energies smaller than those required for homogeneous nucleation. Numerous investigations have shown that in this process of heterogeneous nucleation: a) the nucleus forms with one, or several, definite crystallographic orientation relationships with the nucleating phase2-4 and b) that there is a small range of undercoolings or super saturations characteristic of the nucleation of a given solid on a given Substrate.5-10 Turnbull and vonnegut11 have developed a theory based on theories developed by Volmer12 and Turn-bull and Fisher1= for heterogeneous nucleation from gases and liquids, that relates the super saturation or undercooling required for nucleation to the dis-registry between the lattices of the nucleus and the nucleating agent. This theory predicts that nucleation should occur with the orientation relationship between the nucleus and nucleating agent that minimizes the disregistry. Further, it predicts that the undercooling or super saturation necessary for nucleation should be a function of the disregistry. Numerous investigations have dealt with the orientation relationships resulting from the condensation of vapors onto crystalline solid substrates2,3 and a few with the nucleation of one phase by a second phase in solidification4,14. Others have dealt with the supersaturation8-10 and undercooling5-7 associated with nucleation in condensation and solidification respectively. However, there is virtually no report that gives both of these factors for the same system. In this investigation a study was made of the undercoolings and orientation relationships resulting when Pb is nucleated from the liquid by Ni, Cu, Ag, and Ge. It was the purpose of this investigation to check the Turnbull-Vonnegut theory, i.e., the importance of crystallographic disregistry between nucleating catalyst and nucleated metal. The results indicate that disregistry is not an important factor in nucleation and that the nucleation process is probably somewhat more complex than current theories suggest. EXPERMENTAL PROCEDURE Small single crystals of nickel, copper, silver, and germanium were prepared from materials of four to five nines purity, and the Pb used was also 99.999+ pet pure. Cu and Ag single crystals were prepared by sealing small chips of Cu or Ag in an evacuated quartz capsule and heating the capsule at 2000°F for 1 hr before cooling. Nickel crystals of 200 diam were also prepared in evacuated quartz capsules, but melting was done by heating the capsules in an oxy-acetylene flame for a few minutes. These spheres were invariably polycrystalline so

Jan 1, 1962

By G. W. Nabor, A. S. Odeh

The effect of production history of a well on the results of two-rate flow tests, and conventional build-up analyses was investigated. The effect was examined by means of digital computers and an R-C network model, respectively, for wells with infinite and finite radii of drainage. For systems which behave as infinite, it was found that production history and the duration of production at constant rate prior to the initiation of the test have important effects on the results. During build-up time equal to about one-fourth of the stabilized time, correct permeability-thickness product calculations can be made. For wells with finite radii of drainage, the time was determined during which the straight line can be satisfactorily used for permeability-thickness product calculations in case of drawdowns and build-ups. On build-ups, the dimensionless time (based on the external radius) during which the straight line gives reliable results was detertriined to be about 1/12. This is one-fourth as long as that of the drawdown. The investigation was done theoretically, and subsequently was verified by R-C network model runs. General interpretive rules were formulated which, if not followed, could lead to serious errors. Moreover, a recommended testing procedure is reported. INTRODUCTION The method used by most reservoir engineers for estimating formation characteristics in a producing well is the analysis of pressure build-up data. The method originally devised by Horner&apos; makes use of the point source solution to the diffusion equation. This solution is approximated by a logarithmic function and the superposition principle is employed to arrive at the well known pressure build-up equation:where q, the flow rate, is in reservoir B/D; ft is in cp; kh is in md-ft; At is the shut-in time; and t is the producing time. At and t are in any consistent time units. Ey. 1 is applicable to a well of unlimited drainage radius which produces at a constant rate q from zero to time t and is then shut in. Such a constant production rate seldom obtains in practice. Therefore. a correction term must be applied to Eq. I to account for the varying rate. Two theoretically accurate methods are available for treating the variable rate case. The first, originally derived by Horner,&apos; is based on the application of the superposition theorem. It requires knowlege of production history of the well as a function of time and results in lengthy and laborious calculations. The second t*q* niethod is suited for short production tests and requires that the shut-in time be at least one and one-half times the production time. A third method which is not based on any theoretical justification and which was suggested by Horner as a "good working approximation" is the one used by the majority of reservoir analysts. especially when the well has been producing for a long time and the t*q* method is not practicable. The key to this method is in choosing or determining the t that appears in Eq. 1. Horner suggested using a corrected time t, in place of t. t, is calculated by dividing the total cumulative production by the last established rate. Therefore, a normal procedure of pressure build-up testing is to stabilize the well at a constant rate for at least 24 hours before shut in and to use the stabilized rate to calculate t,. The analysis is then made by plotting either or P. and examining the resulting plot for the expected straight line to calculate kh and the original reservoir pressure. Recently, Russell" proposed a method for determining formation characteristics from two-rate flow tests. His method reduces to pressure build-up if the second flow rate is zero. Russell uses the Horner simplified procedure for calculating a corrected t,. His method also requires the stabilization of the well at a constant rate q which is used to calculate t,. Theoretically, the above procedure is valid for a well with an unlimited radius of drainage or with a limited radius as long as the boundary effect has not been felt by the well. Several authors&apos;&apos; derived formulas which allow the estimation of time during which limited reservoirs behave as infinite ones and, thus, can be treated by unsteady-state mechanics. One equation derived by Swift and Kiel&apos; terminates the application of unsteady-state theory when the drainage radius reaches one-half the reservoir radius. Thereafter, steady-state behavior obtains. Another equation derived by Jones&apos;" initiates steady-state

Jan 1, 1967

By M. Nicholas, D. M. Poole

The diameters of sessile drops have been found to increase linearly with time in five reacting binary metal systems. The spreading rates of the drops are markedly dependent on temperature and on prior alloying of the solid with the lower melting point metal, hut are independent of the drop volume, wetting atruosphere , solid-surface roughness, and prior alloying of the drop with the substrate metal. A mechanism has been suggested that relates the linear-spreading rate to lateral diffusion of the liquid-metal atoms into the solid at the drop edge. An Arrhenius- type equation has been derived that describes the temperature dependence 0) the spreading rate, and although the agreement between the actual and the predicted pre-exponen-tial terms is poor that between the activation energies is excellent and the variation in the spreading rate of copper on Ni-Cu alloys produced by different extents of alloying can be predicted with considerable accuracy. CHEMICAL interactions frequently change the wetting behavior of solid-liquid systems causing, for example, "secondary spreading1 of sessile drops beyond the size defined by the surface and interfacial tensions of the unreacted components. The kinetics of the contact-angle decreases associated with this spreading are similar for many systems, but few studies have been made with the objective of determining whether the similarities are a reflection of a common mechanism. Some workers2,3 have assumed the secondary spreading is controlled by changes in the liquid surface and liquid-solid interfacial tensions and hence by the composition of the liquid, and contact-angle changes measured by the vertical-plate technique have been used to follow the course of liquid-solid chemical reactions.4 Other processes that have been invoked to explain these time-dependent changes in specific systems include the removal of adsorbed gas from the liquid-solid interface.5 penetration of containment layers on the solid Surface,6 interdiffusion,1,7 reori-entation of the solid surface into a wettable configuration: vapor-phase transport of the liquid onto the solid in advance of the drop,9 and, from vertical-plate studies. capillary flow between oxide layers and the solid surface.10 One of the reasons for the profuseness of these suggestions may be the complexity of the contact-angle change kinetics. However, in an analysis of secondary spreading gold and copper on UC,11 it was found that the diameter of the contact area between the sessile drop and the solid surface showed a simple linear increase with time although contact-angle changes were more complex. To check whether the linearity was merely fortuitous! additional exploratory work was conducted with four reacting metal-metal systems: Au on Ni. Cu on Ni, Cu on Fe, and Ag on Au. Linear spreading was observed in every case even though the kinetics of the contact-angle changes were complex. A further detailed study of the kinetics of linear spreading of five reacting metal-metal systems has been made with the object of determining the mechanism involved. The influence of variables such as temperature, drop volume. and the initial composition of the drop on the linear-spreading rate has been measured and compared with those predicted by a number of possible mechanisms. The systems employed in this study (Cu and Au on Ni and Pt, and Ag on Au) were selected because of the availability of potentially relevant chemical and physical property data. the simplicity of their phase diagrams at the wetting temperatures, and the ease of experimentation. EXPERIMENTAL TECHNIQUES The purities of the metals used in the study were: copper, 99.9 pct; gold. 99.96 pct; nickel, 99.2 pct; platinum 99.99 pct; and silver, 99.999 pct. The wetting tests were performed in a split tantalum tube vacuum resistance furnace of a conventional design. The furnace element was held vertically and was 1 $ in. in diam and 6 in, long. Viewing ports were provided in the water-cooled chamber to enable the specimens to be observed in both the horizontal and vertical planes. The temperature in the hot zone of the furnace could be held at 1500" i 5°C for an indefinite time. The surfaces of the solid-plaque metals were ground flat on Microcut paper and both the sessile drop and substrate metals were ultrasonically cleaned in methyl alcohol prior to their insertion in the furnace. After loading, the furnace was pumped down to a pressure of 2 x 10-5 mm of mercury and degassed for 30 min at 900° to 950°C. The temperature was then increased at more than 100°C per min to that used in the wetting test. The vacuum at the wetting temperature was better than 5 x 10-5 mm of mercury. Dewetting and retraction of the drop on cooling did not occur and the contact-area diameters, therefore, were measured after solidification with a vernier traveling microscope. The diameters quoted later are arithmetic means of ten measurements. The standard error of the mean never exceeded 3 pct and was often less than 1 pct.

Jan 1, 1967

By C. N. J. Wagner, E. N. Aqua

The bee alloys of the terminal solid solution of rhenium in niobium were investigated by X-ray diffraclion methods. The analysis of the broadening of the powder pattern peaks from the niobium-rich alloys, cold-worked by filing, showed evidence for faulting on (211) planes. The alloys with larger rhenium concentrations were brittle, and fractured when filed. The analysis of the shapes of the diffraction profiles from powders produced by hammering with steel plates) of these brittle alloys indicated that the broadening was due predominantly to platelets bounded by clibe planes. This result was consistent with the Laue patterns from single-cleazlage facets which showed evidence for clearage fracture on {100} planes. The influence of faulting on the mechanical properties of face-centered cubic (fcc) metals and alloys, i.e., how faulting affects the various dislocation configurations in fcc metals, is well-known.&apos; The important question is whether or not faulting occurs in body-centered cubic (bcc) metals and alloys, and, furthermore, if faulting does occur, to what extent it affects the mechanical properties. Theoretical calculations indicate that the stacking-fault energy is rather high in most bcc metals.2 The results of sev-eral studies using transmission electron microscopy have indicated that faults are present in well-annealed and lightly deformed bcc metals and alloys, such as tungsten,3 vanadium,4 and Mo-Re alloys.5,6 These faults, as have been observed, may be stabilized by the presence of interstitial (C,N,O) atom segregation to the extended dislocations. In addition, there is considerable X-ray diffraction evidence for faulting in bee metals,7-8 using the same techniques that were successful for the study of faulting in fee metals and alloys.7 This X-ray diffraction method is currently the only technique applicable for the investigation of faulting in metals with high stacking fault energies, i.e., when severe amounts of deformation are required to produce sufficient amounts of faulting to be detectable by X-rays. The thinned films of heavily deformed metals will become opaque in the electron microscope due to the high dislocation densities present. In a previous investigation of faulting8 in bee metals of group Vb and VIb, the authors observed that niobium was ductile when filed at room temperature, and showed the highest density of faults on the (112) family of planes. A niobium-base alloy system was therefore chosen to study the effect of alloying on the occurrence of faults in a bcc alloy. There is a large range of terminal solid solubility of rhenium in the alloys of the bee refractory metals. All of the Group VIb-rhenium alloys, i.e., Cr-Re, Mo-Re, and W-Re, exhibit solid solution hardening without loss of ductility.9 In fact, the ductility reaches a maximum for alloys with compositions near to the limits of solubility. This enhanced ductility has been attributed to the lowering of the stacking-fault energy in the alloy; i.e., the increased amounts of twinning provide an additional mode of deformation, resulting in the observed high ductility.&apos; Because of this demonstrated effect of rhenium in bee alloys, it was decided to study a series of alloys of Nb-Re. Using the same X-ray diffraction methods as described in the previous investigation,&apos; one is able to identify the possible causes of broadening of the powder pattern peaks, e.q., particle size, microstrains, stacking faults, and/or twin faults. The separation of these various contributions to the measured peak shape is accomplished by the Warren-Averbach analysis.7 I) EXPERIMENTAL PROCEDURE A series of seven bee solid solution alloys containing from 2.5 to 21.5 at. pct Re (remainder niobium) were prepared at the General Electric Research Laboratory. Buttons, weighing 25 g, were alloyed from electron-beam-melted niobium chips and random rhenium sheet by arc melting in a water-cooled copper crucible, under an argon atmosphere. The buttons were inverted and completely remelted to promote homogenization. The nominal alloy compositions are listed in Table I. Samples of the cold-worked alloys were obtained by filing to produce a powder for the X-ray study. Alloys too brittle to be filed were hammered with steel plates. The resultant filings or brittle impactings were screened through 150-mesh classifiers and compacted to the required shape for the diffractometer holder. The X-ray diffraction peaks were automatically recorded by fixed time counting at uniform 28 intervals, or by continuous registration with a ratemeter. In all cases, the (110)-(220) and (200)-(400) pairs of peaks and the (211), (310), (222), and (321) reflections were measured on a GE-XRD5 diffractometer using CuKa radiation with nickel filter or MoKct radiation and a LiF monochromator in the diffracted beam. The first part of the data reduction, completed with the aid of a series of programmed computations,10 was the analytical resolution of the Kol component of the diffraction profile. Subsequent computations were then made with reference only to the resolved Kol peak shape. These included the measurement of the

Jan 1, 1967

By B. C. Allen

Grain-boundary gvoocing was studied irz chronziu?n. molybdenum, tungsten, and the solid-solution alloys, Cr-35Re. Mo-33Re, and W-25Re at 0.6 to 0.9 of the absolute liquidus temperature under an inevt atmosphere , foveign nzetal zlapor, and liquid metal. The controlling mechanism of matter transport was deduced frolr groove size and shape. kinetics of growth, and cotnparisoz with theoretical relatiotzships derived by Mullins. Grooves in chowzizon formed prittzarily by volume diffusion tkrongk kelium or argon at 1 atm pressure and by e1)apovation-condensatiotz in a static vacuum. Groozles in the other nzetals and alloys forrned priniarily by sirface diffusion, the coefficients of which were calculated. Carbon was found to decrease the acti7:ation energy for surface diffusion on molybdenun. Sitrface diffusizities weve sinzilav for iWo-0.0ZC and Mo-33Re. The presence of about 1 -?nm pressure of silver or tin vapor did not affect the neckanis)n of grooz;e formation. In liquid titz or silz:er, pain bolindary gvooves formed by zolume diffusion in the liquid. BASED on theories of ullins," the mechanisms of grain-boundary grooving have been determined for low-melting metals such as copper in an inert atmospheres or in liquid lead.4 The purpose of this investigation was to study grain-boundary grooving in the refractory Group VI-A metals, chromium, molybdenum, and tungsten, and the bcc solid-solution alloys, r-35e, 0-33e,= and -25e,&apos; at 0.6 to 0.9 of included to see whether Mullins&apos; theories were applicable to them as well. EXPERIMENTAL WORK The materials chromium, molybdenum, tungsten, Cr-35Re, Mo-33Re, and W-25Re were in the form of 0.050-cm-thick sheet assaying 99.98 pct or better. The nominal carbon level was generally 30 ppm. The oxygen + nitrogen + hydrogen content was -50 ppm. Mo-33Re and W-25Re were prepared by powder-metallurgy methods and supplied by Chase Brass and Copper Co. The remaining materials were arc-cast. Chromium and Cr-35Re were prepared at Battelle by arc melting, extruding, swaging, and rolling. Mo-0.003C was supplied by Climax Molybdenum Co., and Mo-0.02C and tungsten by Universal Cyclops Corp. As a source of liquid metals, tin and silver granules assaying 99.98 pct were used. Spectrographic analyses indicated the presence of -100 ppm each of iron and silicon. Vacuum melting reduced the combined gas content to c5 ppm (2.60,, 0.9N2, 0.4H2 in tin and l.602, 0.7N2, and c0.04H2 in silver). Specimens were prepared for grain-boundary grooving. Coupons 0.5 by 1.5 cm with a small hole in one end, or substrates 1.5 by 1.5 cm, were cut from sheet. The specimens were annealed in containers of the same material to provide a vapor-solid equilibrium as well as to protect them from gaseous impurities. Outgassing was done at 2 x 10"5 mm for 15 to 30 min at 1150°C for chromium and Cr-35Re, 1750°C for molybdenum and Mo-33Re, and 2600°C for tungsten and W-25Re. Then recrystallization to a stable grain size of about 0.5 mm was accomplished by annealing at least 1 hr at 1600°C for chromium, 1800°C for Cr-35Re, 2350°C for molybdenum, and 2300°C for Mo-33Re in a rhenium-element resistance furnace under 1 atm of static argon or helium. The atmosphere was gettered by tantalum radiation shielding. Tungsten and

Jan 1, 1967

By C. L. Shapiro, R. Schempp

DuRing the past few years, general interest in the steel-producing and steel-consuming industries has been centered on the so-called "inherent characteristics" of steels. While often vaguely described, these characteristics are known to influence the response to heat-treatment and the hardening characteristics of the material. Although most of the recent papers and discussions have associated the "inherent characteristics" with the austenitic grain size and emphasized the importance of it, comparatively little is known of the variables that may affect the size of the austenite grain. The work to be described in this paper was carried out during the course of a study on the inherent characteristics of tool steel containing one per cent carbon. The discrepancies encountered in the determination and classification of the austenitic grain size led to an investigation of some of the variants influencing the austenitic grain size as determined by standard methods. Methods of Determining Austenitic Grain Size The present methods used for the determination of the austenitic grain size may briefly be classified in two groups: 1. Etching at room temperature to reveal the austenite grain size prior to cooling. 2. Etching at elevated temperatures, cooling to room temperature, and observing the structural conditions that existed at the temperature from which cooling occurred. The outstanding methods of the first group are: (1) the McQuaid-Ehn test, (2) optimum rate of cooling, (3) quenching and etching. McQuaid-Ehn Test.—This established and accepted test does not need much elaboration. It consists of pack carburizing at a definite temperature for a standard period of time and slowly cooling in the furnace. The temperature is 1700" F. (925&apos; C.) and the time is 8 hr. The interpretation and evaluation of this test are fairly well defined in the A.S.T.M.

Jan 1, 1937

By A. M. Sarem, J. M. Campbell

Molecular refraction is introduced as a new and improved third parameter for prediction of the PVT behavior of hydrocarbon systems. This parameter, characterizing the complex as well as the pure hydrocarbon systems (1) is a direct measure of London dispersion forces which affect the PVT behavior; (2) can be measured directly, accurately and easily for complex as well as pure hydrocarbon systems; (3) varies significantly between the reference substances thus allowing accurate interpolation of PVT properties; and (4) has a fundamentally sound basis. Molal average molecular refraction was used with the pseudocritical mixing rule proposed by Leland and Mueller to predict the molal volume of liquid and vapor for 84 published data points on nC4-nCI0, Cl-nC5, Cl-nC4-nC10 systems in the region of coexisting vapor-liquid and at the critical point. The same technique was applied to predict the densities of liquid hydrocarbon mixtures in the two-phase and single-phase regions near the critical point for seven different systems each having different properties of the heptanes-plus fraction, but all simulating the fluids of either gas-condensate or volatile oil reservoirs. A modification of the Leland-Mueller mixing rule for the determination of pseudocritical properties is also presented which yields more accurate liquid density predictions than the original form when used with the proposed third parameter. INTRODUCTION The PVT behavior of multicomponent systems has received widespread attention in the literature in recent years. A large portion of the reported work has stemmed from attempts to overcome the inherent difficulties encountered when using the standard compressibility-factor chart which shows 2 as a function of reduced temperature T, and and reduced pressure p,. This chart assumes that z, is constant for all systems. The error in this assumption is not pronounced for pipeline-type gases high in methane and low in heavy ends, particularly when contained at moderate pressures. For such gases the error in the calculated z is usually less than 2 to 3 per cent. However, the reliability of this approach becomes somewhat nebulous for gas condensate and volatile oil systems at high pressure. One logical approach has been to recognize the variation of 2,. This idea was first suggested by Meissner and Seferianl and used by Lyderson, Greenkorn and Hougen2 to prepare extensive tables of thermodynamic properties. Other third parameters have been proposed by Stockmeyer, Kihara, Riedel, Lightfoot, Bloomer and Pitzer. These were tested by Satter and Campbel13 for many gas mixtures and it was shown that they were inter-related. All of these third parameters have a common fault — they cannot be directly evaluated for the heptanes-plus fraction. Consequently, one necessary requisite of an improved method for predicting the density of multicomponent hydrocarbon systems, was development of a third parameter that could be evaluated for that fraction. PREVIOUS MULTICOMPONENT DENSITY PREDICTION METHODS Sage and Lacey4 suggested a method of using partial molal volumes for computing the density of hydrocarbon gas mixture for pressures to 3,000 psi. In this technique, they approximate the complex multicomponent gaseous mixtures by a quarternary system of methane, ethane, propane and butane. Sage, Hicks and Lacey5 suggest a method of using partial molal volumes for computing the density of hydrocarbon liquids. The results agree within 3 per cent of the experimental values. However, the composition range is limited to about 10 per cent by weight of methane. Consequently, this correlation does not cover the low-molecular-weight liquid similar to natural gasoline and high-pressure gas condensates.

Jan 1, 1966

By P. K. Strangway, H. U. Ross

Briquets consisting of pure artificial magnetite, pure artificial hematite, and mixtures of the two were reduced by hydrogen in a loss-in-weight furnace at temperatures in the range 500° to 1000° . The rate of reduction of the pure hematite briquets increased continuously with increased temperature. In contrast, the pure nmgnetite briquets exhibited a pronounced rate ninimutn at about 700°C. Metallographic studies of partially reduced briquets rerlealed that, at this temperature, the he.matite samples reduced in a topo-chemical manner while the magnetite ones reduced uniformly throughout, and after partial reduction their cross sections contained a mixture of iron and unreacted wustite grains. No iron shells could be detected on the surfices of any of these uwstite grains. X-ray diffraction investigations indicated that these grains had a rzinimum lattice parameter when they had been formed at the rate rninimum temperature. Also, it was found that an activation energy of 41,000 cal per mole zoas required for reduction when only these wustite grains were present. Thus, it is suggested that the overall reduction rate of the rnagnetile su?nples at temperatures in the range influenced by the rate nzinirnum phenomenon was limited by the rate qf iron ion diffusion in the unreacted wustite grains. THE rate minimum phenomenon, which has often been observed when reducing iron oxides at a temperature of about 700°C, is one of the most interesting, yet unresolved, problems in the field of reduction kinetics. Basic principles of chemical kinetics and &apos;In some instance, a second rate minimum has been observed at about 900°C. Since most investigators are in agreement that this minimum is directly related to the transformation from a to y iron (which takes place at 911°C) and since it was not encountered during the present reduction tests, it will not be referred to in this vaver. fundamental laws of diffusion all agree that, as the temperature is increased, the rate of reduction should also increase. However, with certain ores, it has been found that their reduction rate actually decreases with an increase in temperature up to some value X where a minimum reduction rate is reached. With further temperature increases beyond X the rate becomes more rapid again. Temperature X is usually referred to as the "rate minimum temperature", while the overall type of behavior constitutes the "rate minimum phenomenon". This phenomenon has been reported by numerous investigators. They have found rate minima during the reduction of both artifiial&apos; and natural374 magnetites and artificia15j6 and natural5" hematites. Rate minima have been observed when reducing high-purity material2 or low-grade ores,3&apos;4 when studying particles in the micronsize range5 or relatively large agglomerates,g10 and during reduction with either hydrogen7 or carbon monoxide.11"2 Previously, this phenomenon has been attributed to many factors; these include sintering and recrystallization of the iron formed during reduction374 changes in microporosity of the ore upon redction,"" formation of dense iron shells around retained wustite grains,11716 and chem-isorption,17 to name only a few. However, most investigators who have reported a rate minimum merely speculated as to what seemed to influence it and they did not examine the fundamental causes. Consequently, the present experimental study was initiated in order to evaluate the basic factors which could be associated with this phenomenon. MATERIALS AND METHODS The experimental techniques, followed during this investigation, are similar to those which have been described previously.18 The chemically pure magnetic powder was prepared by partially reducing Fisher reagent-grade hematite with a gaseous mixture of carbon monoxide and carbon dioxide in a rotating-drum furnace. Three-quarter-inch diam cylindrical briquets which weighed about 12 g were formed from this magnetite powder and pure hematite powder. All of the briquets were sintered while they were slowly raised through the 1200°C hot zone of a vertical tube furnace. An argon stream was continually flushed through this furnace in order to prevent oxidation of the magnetite briquets, while in the case of the pure hematite briquets sintering was carried out in air. The sintered hematite briquets had a density of 5.06 g per cu cm while the density of the sintered magnetite briquets was 4.27 g per cu cm. The sintered briquets were reduced by purified hydrogen in a loss-in-weight furnace at temperatures in the range 500" to 1000°C. In all instances, the critical reducing gas velocity was exceeded and, in order to ensure that the results were reproducible, duplicate briquets of each type were reduced under each set of experimental conditions. A continuous record of the weight loss during reduction was obtained with the aid of a Statham transducer. The present experimental setup was capable of detecting a change in weight as small as 10 mg. Since a weight loss of over 2 g usually occurred during each reduction test, an accuracy of better than 0.5 pct of the total weight loss could be achieved. RESULTS AND DISCUSSION Reducibility Tests. In the first set of experiments, pure hematite and pure magnetite briquets were used.

Jan 1, 1969

By Hertha Freche

THE diffusion of magnesium and silicon from the core into the high-purity coating of Alclad sheet is important commercially, and led to the use of a duplex product for the study of diffusion by means of spectro-graphic analysis of successive layers. It has been found that in the duplex materials the diffusion of magne-sium from an undersaturated aluminum-magnesium alloy into its high-purity aluminum coating is approximately of the same order of magnitude as the diffusion of silicon from a saturated aluminum-silicon alloy into its high-purity aluminum coating. However, if magnesium and silicon are both present in the alloy in the ratio of Mg2Si they appear to diffuse in the approximate ratio of this compound. Finally, if the alloy contains silicon in excess of the amount required by magnesium silicide, the amount of diffused silicon in the high-purity aluminum coating will also be in excess. The interdiffusion of metals in the solid state is of both scientific and technical interest, because it is helpful in the study of the alloy structure and in the solution of problems pertaining to the strength and surface condition of the fabricated product. W. C. Roberts-Austen1 carried out the first quantitative determination of the coefficient of diffusion of gold into lead. This classical experiment was followed by a series of investigations on the diffusion of metals and nonmetals in iron and steel and in nonferrous metals and alloys. Recently the diffusion of copper in coated strong aluminum alloys was investigated by A. Burkhardt2. This appeared to be the first published investigation on the diffusion of metals into aluminum.

Jan 1, 1936

By R. F. Hehemann, R. H. Goodenow

Thermal arrest, hot-stage microscopy, and transtnission electron microscopy techniques have been employed to study the transformations in low-carbon iron and Fe-9 pct Ni alloys. In continuous cooling experiments, each alloy transforms at an essentially constant temperature for cooling rates below the critical rate required for martensite formation. However, high-tenzperature transformation in pure iron takes place by a different mechanism than that in the 9 pct Ni alloys. Pure iron exhibits an equi-a a structure with a low and random dislocation density while the 9 pct Ni alloy exhibits a cell or lathlike substructure analogous to that of low-carbon martensite. This same substructure characterizes upper bainite in higher-carbon inaterials. UNTIL relatively recently, diffusionless transformations have been considered to take place by the same mechanism and have been termed mar-tensitic transformations.l-3 The most characteristic feature2 of this mode of transformation is the shape change produced by a shear deformation and growth of the product phase frequently occurs at an extremely high velocity approaching that of an elastic wave.4&apos;5 A different mechanism of diffusionless transformation was recognized first in Cu-Ga and other copper-base alloys.6,7 From the absence of surface tilting in these alloys, it has been concluded that transformation is not accomplished by the cooperative shear displacements that occur in mar-tensitic reactions. Transformation presumably takes place by the rapid movement of an incoherent interface which is capable of propagating across parent grain boundaries. Although the transformation is diffusionless in the macroscopic sense, advancement of these interfaces is accomplished by an atom by atom rearrangement. Transformations of this type therefore require thermal activation and are generally operative only at high temperature. Although requiring short-range diffusion at the interface, propagation still occurs so rapidly that the reaction cannot be suppressed with normal cooling rates.7 The resulting microstructures exhibit large, irregular-shaped regions of the product phase, which are essentially free of crystallographic features. Consequently, these reactions have been termed massive transformations. Transformation by the massive mechanism has been reported to occur in ferrous systems involving pure iron and binary alloys of iron with nickel, chromium, and silicon by Gilbert and owen.&apos; The Fe-Ni system is of special interest in that the massive transformation was observed in alloys with less than 15 pct Ni while alloys having more than about 28 pct Ni transformed by the conventional mar-tensitic mechanism. By employing cooling rates substantially higher than those used by Gilbert and Owen, Swanson and Parr have been able to suppress the massive transformation in alloys with 0 to 10 pct Ni9 and produce martensite as revealed by surface relief. The massive transformation in the alloys having less than 15 pct Ni was identified by the lack of surface relief and an irregular rather than clearly acicular microstructure.&apos; Speich and Swann, using thin-foil electron microscopy, identified three distinctly different structures10 in quenched binary Fe-Ni alloys. From 0 to 4 pct Ni the structure consisted of blocky grains of a with a low and random dislocation density. Alloys with 4 to 25 pct Ni exhibited a cell structure with a high dislocation density; and at greater than 25 pct Ni the structure consisted of internally twinned plates. The structural change at approximately 4 pct Ni suggests that alloys with low nickel content transform by a different mechanism than those with intermediate nickel contents and the transition from the cellular to the internally twinned structures at approximately 25 pct Ni is analogous to the transition from needles to internally twinned plates that occurs over a narrow range of carbon contents in Fe-C martensites.11,12 Conventional bainitic and martensitic modes of austenite decomposition operate in ternary Fe-C-Ni alloys having less than 10 pct Ni. This investigation was conducted in order to explore the conditions under which the massive, bainitic, and martensitic transformations occur and the relationships between these modes of decomposition.

Jan 1, 1965

By S. Pearson, L. Rotherham

Measurements have been made of the variation of internal friction with temperature for spectroscopically pure silver, and for o series of solid solutions of silver with cadmium, indium, and tin, using a Ke-type torsion pendulum apparatus. Some experiments have also been made to investigate the effect of nonmetallic impurity on grain boundary relaxation in silver. The effect of the alloying elements is to increase the grain boundary viscosity, and to raise the activation energy for grain boundary relaxation from 22,000 cal per mol for pure silver to 43,000 cal per mol for the solid solutions; the same value being obtained, within the limits of experimental error, for all the alloying elements and solute concentrations investigated. Results of the experiments show exactly the same trend as those obtained previously for a similar series of copper solid solutions. They are in agreement with the general theory of grain boundary relaxation developed by Zener and Ke, but do not seem to be in agreement with either of the mechanisms so far put forward to explain grain boundary slip. EXPERIMENTS described in this paper were made as part of an investigation into the effect of alloying elements in substitutional solid solution on grain boundary viscosity, measured by the internal friction method developed by Ke.&apos; The apparatus and experimental procedure have already been described.&apos; Preliminary work was done with spectro-scopically pure silver. Experimental Work Materials Used—All the materials were supplied in the form of % mm diam wire by Messrs. Johnson Matthey and Co. Ltd. The silver and all the alloying elements used were spectroscopically pure. Composition of the alloys is given in Table I. They were all melted and chill cast under the same conditions as the copper alloys. The ingots were rolled to 1/4 in. sq rod with intermediate annealing at 600°C in an atmosphere of cracked ammonia when necessary. These rods were then drawn to wire by standard procedure with intermediate bright anneals at suitable steps in the drawing operations. Specimens from the annealed wires were sectioned longitudinally. mechanically polished, and examined under the microscope. They were then etched and reexamined. Grain sizes were reasonably uniform for all wires, and no traces of a second constituent were observed. The wires were weighed before and after testing so as to measure any loss of the alloying element due to evaporation. The loss was less than the accuracy of measurement—< 0.1 pct of the total weight— for the Ag-In and Ag-Sn alloys, but appreciable loss of weight occurred in the case of the Ag-Cd alloys. The percentage loss is given in Table 11. X-ray diffraction photographs were taken of all thc wires after test to determine whether there was any marked preferred orientation. Results of the examination are given in Table 111. Experiments on Spectroscopically Pure Silver-— Experiments were made on specimens in which the grain diameter was small relative to that of the wire, and on one specimen in which the grains were grown by the usual strain-anneal method to extend across the full diameter of the wire. These large grained specimens will be referred to as single crystal specimens. The wires were annealed for 11/2 hr at 700°C, and experiments were made at two frequencies of vibration, 1.5 and 0.4 vibrations per sec. The variation of internal friction with temperature is shown in Fig. 1. Experiments on a second small grain specimen gave approximately the same results as for the first wire. It will be seen from Fig. 1 that the peak in the curve for the small grained wire, which is presum-

Jan 1, 1957

By F. Keller, A. H. Geisler

Some of the important changes that take lace in the structure of aluminum alloys are largely submicroscopic in character. This is especially true of the changes that accompany age-hardening and recrys-tallization. Although improved metal-lographic practices have been helpful in indicating some of these changes indirectly, results are limited by the resolving power of optical microscope lenses. The electron microscope, however, provides a new and important means for investigating the fine structure of metals in a range not possible heretofore. It is anticipated that this microscope will yield new and useful information to metallurgists when suitable techniques are developed to utilize its very high resolving power. Several unique methods have been devised to permit the examination of the structure of opaque samples by the electron microscope. These are all based 011 the principle of producing a very thin film that represents the prepared surface of the opaque metal sample, which can be examined in the transmission microscope; however, the available methods fall into three categories, depending on the manner in which the film is obtained. With the oxide-film method developed by Mah13-l7 a very thin surface layer of the metallographic sample is converted into oxide by a thermal, chcmical or anodic treatment. .After removal from the metal sample by one of the special techniques described by Evans,l9 this oxide film is examined in the electron microscope, and is found to portray the structure of the original metal surface. Films formed on aluminum,8,l7 nicke1,7 iron3,8,9 and a nickel-beryllium alloyl1 by heating; films formed on iron8,9 by chemical action; and films formed on aluminum3-&apos;" by anodic oxidation, have been examined. The other two are more recent methods developed principally in this country; they consist in making the thin film in the form of a mold or replica of the surface contour of an etched sample. With the negative replica method the thin film is made directly on the sample; with the positive replica method it is made on a negative reproduction of the sample. With both methods, variations in the contour of the metal sample, caused mainly by etching, produce variations in the thickness of the surface replica. Because of the direct dependence of the amount of scattering of the illuminating electrons upon the thickness of the film penetrated, only the variations in thickness of the replica are responsible for tones in the electron image. Negative replicas are made by forming a thin film of some suitable material directly on the polished and etched metal sample, and derive their name from the fact that after removal from the sample they have the high and low points in the sample reversed, as shown in Fig. I. Nega-

Jan 1, 1944

By John E. Hockett

The need for basic information about the relationship between resistance to dejormatim (flow stress), temperature, strain, and strain rate, for the solution of metal-fovming problems, is pointed out. Some early attempts to satisfy the need are mentioned. A brief description of a machine called a Cam Plastome-ter is given, including the processing of results of testing in the machine. Next, a program of testing aluminum in compression over a wide range of constant true-strain rates (0.1 to > 200 sec-1) and a modevately broad range of temperatures (223° to 673°K) is described. The results of this program are presented in the form of true-stress us true-strain cuvves. The data in these curves are presented in the form of relationships between true stress and true-strain rate in sermilogarithmic and log-log form, as functions of temperatures—for several true strains. Finally, true stress, for a given true strain, is displayed as a function of log true-strain rate and absolute temperature, i.e., a surface. SINCE the publication of Hill&apos;s book1 on plasticity theory, increasingly rapid advances have been made in analytical solutions to forming problems. Methods in common use are the slab method, the uniform deformation energy method, the limit analysis method, the slipline field method, and the semiexperimental method called "visioplasticity". These approaches, and examples of their use, are covered in detail by Johnson and Melloor2 and by Thornsen, Yang, and Kobayashi.3 unfortunately, practically all of the above work has had to rely upon a number of basic assumptions, e.g., homogeneous deformation and Coulomb (sliding) friction; and virtually no dependence of the mechanical behavior of the deforming metal, upon temperature, strain, and strain rate, has been included. It is with this dependency that this paper is concerned. Loizou and sims4 looked at the above relationship for lead using both a constant compression-speed Cam Plastometer and a constant true-strain-rate Cam Plastometer designed by Orowan.5 Alder and Phillips8 investigated the relationships for aluminum, copper, and steel in the same constant true-strain-rate Plastometer. cook7 tested twelve steels at temperatures ranging from 1170° to 1473°K in the same Plastometer over a range of true-strain rates of 1.5 to 100 sec-&apos;. The writer tested commercially pure aluminum at room temperature and depleted uranium at temperatures from 573" to 873°K at strain rates from 10-3 to 1.0 sec-1 in a Cam Plastometer designed and built at Los Alamos Scientific Laboratory.8 During the past few years the Cam Plastometer at Los Alamos has been used for a number of relatively minor experiments on brass, mild steel, duralumin, Armco iron, and depleted uranium. In this time the machine has been continually modified and improved. It was decided to utilize fully the wide range of strain rates now available with the machine by testing a material about which some information was already in the literature. Prior work on commercially pure aluminum6 appeared to deserve confirmation and expansion. So it was decided to explore the resistance to compression of this material over the currently available range of constant true-strain rates and a convenient range of temperatures. This paper is a report of that exploration. I) EQUIPMENT AND PROCEDURE The principal item of equipment is, of course, the Cam Plastometer, the working part of which is shown in Fig. 1. In this figure, an aluminum specimen may be seen between two tungsten carbide platens, in position for a room-temperature test. Above the upper carbide platen is a load cell. Output from the load cell is amplified and applied to a galvanometer in a recording oscillograph. Auxiliary equipment includes the oscillograph, the control console, a counter, and a time-mark generator. The counter is first used in adjusting the time base. Then it registers the count, of sixty pips per revolution generated by the rotating cam, in each second. These pips and the time base are also applied to galvanometers in the oscillograph. Thus, load, time, and cam position are recorded simultaneously. Heating of a specimen prior to compression is done

Jan 1, 1968

By S. B. Twiss, P. R. Basford

The relationship between areas of iron powders, briquettes, and sintered compacts and tensile strength has been determined. It has been found necessary to distinguish between two types of areas which exist in such powders—a macroscopic area due to the shape and size of particles and a microscopic area due to pores and cracks in the surface. Only the macroscopic area, specifically the area due to particle irregularity, contributes to tensile strength; the microscopic area cannot be forced into contact with adjacent particles ond does not participate in bond formation. Of the two methods of area measurement employed in this study—permeability to liquids and gas-phase adsorption—only the former is useful for determining the roughness factor. A measure of this roughness, (area measured by permeability to liquid) -f- (orea of powder with the same size distribution, but made up of spherical particles), is shown to be uniquely related to tensile strength at constant density. The other important factors in determining the strength of sintered-metal compacts are the density and presence or absence of surface oxide. THE manufacture of metal parts by the process of powder metallurgy is an important and rapidly growing industry. Progress has been rapid and continuous, largely because of the excellent research in the field. Nevertheless, the process remains inherently complex and empirical. Several investigators have shown that the properties of the final compact must depend on many variables; namely, shape,&apos; size distribution,"-" nd compositiona of the original particles, the pressure necessary to compress to the desired density, the density of the compact, the time and temperature of sintering, and so on. Through the application of some new techniques to the study of powders and compacts, and the correlation of a number of observations of known variables, the present paper attempts to clarify and simplify the underlying theory of the powder-metallurgy process. Any theory must start with the obvious fact that the strength of a compact, its most useful property, is due to the formation of welded areas between adjacent particles, and attempt to deduce what effect other variables will have on (a) the area and (b) the intrinsic strength of these welds. Such welded areas can be demonstrated by electron micrographs, as in Fig. 1. It was believed that (a) could be most directly studied by means of surface-area measurements on the original powders and on the compacts made from them; the area decrease should be related closely to the welded area. A representative group of eleven iron powders from commercial sources, and made by a variety of processes, was chosen for this study. In addition to the surface-area measurements, correlations were established between the tensile strength and all the known variables which might possibly affect it. The results are quite unexpected. They indicate that the situation is much simpler than the authors had anticipated. The strength of the sintered compact is determined, indeed, by no more than three variables; viz., the irregularity of the original particles, the density of the compact and, in exceptional cases, the amount of surface oxide. All three had been recognized previously as having some effect on the tensile strength, but in the absence of the special techniques and interpretations to be developed here, there could be no suspicion that they were the only relevant variables. Materials and Methods Material—All the iron powders were commercial products obtained from the Amplex Division of Chrysler Corporation. Powders A, B, C, and J were very pure electrolytic iron. Powder D was made from oxidized scrap reduced by heating with an excess of cast iron. Powder E was a high-grade iron ore reduced by hydrogen. Powder I was prepared by atomizing molten cast iron in an air blast, quenching the droplets in cold water, and crushing the coarse powder. Mill scale (oxide) is added and the mixture heated to reduce the high carbon content. The other powders were all prepared by reduction of iron oxides, such as mill scale. They

Jan 1, 1959