By Lary L. Speakman

Typical heavy metal removal system generate a great deal of waste that must then be discharged somewhere. Using Bio-Fix Beads developed by the Bureau of Mines in combination with other waste stream minimization processes, Harrison Western Environmental Services has developed a "zero" discharge operation. Data from current on-site operations will demonstrate the effectiveness of the Harrison Western approach. For 1992 Annual TMS meeting,: "Future Trends and Innovations" Material category Key words: Residues and Effluents Technical category Key words: Extraction and Processing.

Jan 1, 1992

By Masaaki Naito

The Japanese steel industry has a long history of introducing new and innovative technologies in the field of ironmaking. The new technologies introduced during the past ten years include technologies to use cheaper and lower-grade raw materials and fuels, measures to prolong the service life of blast furnaces and coke ovens, promotion of energy saving, use of wastes and solutions to environmental problems. This report outlines the condition of production and technological trends and technical development themes in ironmaking technologies.

Jan 1, 2006

By R. L. Nyirenda

One of the problems with ammoniacal-ammonium carbonate leaching of EAF carbon steelmaking flue dust is that zinc present in spinel phases is not leached. This paper presents results of test work in which prior to leaching, EAF dust was reduced with CO containing gas to decompose the spinels into zinc oxide and iron bearing phases, mainly metallic iron and wustite. From such reduction products, the amount of zinc leached increases but the iron co-leached becomes extensive. The effect of various leaching parameters such as liquor concentration and redox potential on zinc and iron dissolution has been investigated. Supplementary experiments utilizing pure zinc oxide and pure iron phases were also carried out. Results show that the co-dissolution of iron from severely reduced EAF dust cannot be prevented. This is because the wustite phase contains zinc which can only be leached when iron also dissolves. Further, the zinc bearing wustite phase is not totally soluble so that the residue cannot be made zinc free. In the absence of air, dissolution of metallic iron hardly occurred, though in leaching experiments of a long duration its transformation to a spinel structure was observed.

Jan 1, 1992

By C. S. Ek

Tests have been performed to recover silver and lead from residues produced after a super-hot leaching in a zinc hydrometallurgical plant operating with jarosite precipitation. When this residue is leached in ammoniaammonium sulfate or in diethylenetriamine solutions, lead dissolution is not complete and its recovery from the aqueous solutions is either difficult, due to the operating conditions, either expensive due to the amount of added reagents. In both cases, silver is partly dissolved, partly left in a new residue still containing lead and baryum sulfates. The best treatment seems to include a selective flotation producing first a silver concentrate assaying about I % Ag, then a 50 % lead concentrate collecting the baryum salts, and a final quartz-gypsum tailing. Metal recoveries can reach 50 % and 80 %, respectively.

Jan 1, 1989

By W. K. Connor, O&apos

The Bureau of Mines has conducted beneficiation, carbothermic reduction, and leaching tests of Mn oxide ores as part of its evaluation of the Mn and Co resources of the West- Central Arkansas District. The major Mn oxides in the ore include cryptomelane, psilomelane, pyrolusite, and lithiophorite. Cobalt is contained within the Mn oxides. Nonbeneficiated ore was reduced at 800' C with coal and leached in ammonium sulfate and ammonium carbonate leach liquors. Ore concentrates were calcined at 600" C prior to reduction under the same conditions as the raw ore. Head analyses reported up to 21 ptt Mn and 0.11 pct Co. Extractions of 70 to 90 pct Mn and 40 to 60 pct Co were achieved.

Jan 1, 1992

By Zhitong Sui

Based on several case studies on the precipitating behavior of valuable nonferrous metal compounds (VNMC) in molten slags a green technology for the recovery of VNMC from molten slags was proposed. This technology involves three steps: (I) The selective enrichment of the dispersed VNMC into the designed mineral phase in the molten slag; (2) The selective coarsening of the designed mineral phase to a critical grain size in the molten slag; (3) The selective separation from tailing of the grown mineral phase in the solidified slag by dressing or hydrometallurgy processes. This is a clean and low cost technique and has a great capacity to deal with a large quantity of slags. The utilization of the recovered VNMC such as Titanium, Boron, Vanadium compounds was summarized as examples of application. It was confirmed by experiments that the precipitating behavior of the designed mineral phases like Perovskite(CaTiO3), Suanite(2MgO*B2O3) and Sincosite(CaOoV2O5*P2O5) in molten slags is obviously affected by operation factors such as temperature, chemical composition, heat-treatment, additives and so on. The precipitating kinetics and mechanism of the VNMC from molten slags during solidification processes were also investigated.

Jan 1, 2003

By M. L. Apel

A conceptual approach to the bioremediation of uranium mill tailings (UMT) is presented., This approach focuses on, biosorption to remediate the. effluent solution and bioleaching remediate the. solid fraction. Comparative biosorption studies were performed with synthetic single metal solutions using a commercially available biopolymer. The maximum rate of metal sorption by calcium alginate was found to be 5.43, 6,39, 6.48, and 9.74 mg dm-3 min-1 for U022*, Ba2+, Cd2+ and Zn2+, respectively. Activation energy (AEa) for barium uptake by calcium alginate beads was determined to be 11.5 kJ, indicating a diffusion controlled reaction mechanism. Thermodynamic values (AG+ AH+ and ASt) of the metal-alginate activated complex, as reported in the literature, were found to be in agreement with those calculated from this research. Results show that this biopolymer can be effectively applied in the removal of select metals prevalent in uranium mill tailing effluents and associated waste streams.

Jan 1, 1991

By Boxun Lu, Juan Wei, Kun Chen, Wanlin Wang, Lejun Zhou

"Slag system is an indispensable part during the continuous casting process, and playing various important roles like absorbing inclusions, modifying heat transfer rate, preventing oxidation of molten steel, etc. to ensure the smooth process and excellent slab quality. However most slags contains more than 8% fluorides which tend to introduce a series of environmental and health problems. This study involves the research of the removal of fluorine through the chemical composition optimization. Through the studies of CCT, DHTT, XRD and SEM, it has been successfully founded that the crystalline phase of Ca11Si4B2O22 discovered in this study shows very similar crystallization property as Cuspidine (Ca4Si2O7F2), which is the most important crystalline phase in the current fluorine bearing slags. Moreover, the optimized free/low fluorine slag shows the opportunity to replace conventional high-fluorine mold slag for casting medium carbon steels that is regarded as the bottleneck of green slag development for continuous casting.IntroductionMold flux has been widely used in continuous casting to control heat transfer, lubricate the strand, absorb inclusions, provide insulation and prevent oxidation of the molten steel[1-3]. It usually contains fluorides, like CaF2, NaF etc., which are used to control the viscosity and solidification temperature of mold fluxes [4-5]. However, the presence of fluoride leads to corrosion of equipment, serious environmental pollution (toxic volatiles and water pollution), and high processing cost of cooling water[6-7]. Therefore, the study of low or free fluorine mold flux is of interest and attracts worldwide attention.S. Y. Choi et al. [4] used B2O3 as a substitute for cuspidine in steel B2PB2) however, B2O3 content was extremely high (up to 30 w%). Other studies have investigated F-free mold flux by adding or optimizing components as MgO, Li2O, B2O3 et al[8-11]. However, most of these focused on the melting and viscosity issues or for low or ultra-low carbon steels, where crystallization tendency is not significantly strong. Very few studies regarding to the development of low/free Fluorine mold flux for casting medium carbon (MC) steels have been conducted, due to the difficulty of the crystallization and heat transfer control without the formation of cuspidine."

Jan 1, 2014

By LuisW. Pommier

The industrial wastes generated by the plating industry, the circuit board manufacturing industries and other related industries normally contain high concentrations of metals, which make them hazardous. The extraction of the contained metals and their separation may be achieved by both pyro and hydro metallurgical processes. Some of the industrial wastes, those rich in some metals like nickel for instance, are being treated like mine ore concentrates and are being fed to smelting furnaces. The slags from these smelter operations are hazardous. They have, however, special environmental dispensations issued by the regulatory authorities. Hydro-metallurflcal processes have been reported. They also generate a residue which is hazardous because not all the valuable metals are leached out and also, because "non valuable" components, like chromium, are less readily leached. Residues from the plating industry, containing nickel, copper. zinc, iron and chromium as the major constituents and also sodium and calcium, together with cadmium, cobalt, lead. manganese, magnesium, molybdenum, and potassium, have been processed for the extraction of the valuable components. The generation of electrolytic nickel, copper and zinc and also of ferric chloride and chromium oxide is reported. The operation is achieved by a caustic leach for the extraction of zinc, followed by a sulfuric acid leach for the extraction of nickel and copper. This acid leach also extracts the iron and some chromium. The nickel copper and zinc are rendered pure by electrolysis, the iron is oxidized for the production of ferric chloride and the chromium is recovered as an oxide. The leaching operation is performed in two stages, first at a pH of 2.5 to generate an electrolyte for the partial recovery of the metals and then at a pH of 0.5 for the complete extraction of the metals. This leaching operation generates a residue, which although small in volume compared to the initial feed, still contains traces of the valuable metals and a portion of the chromium which makes it hazardous. Additional leaching with hydrochloric acid or nitric acid is required for its complete dissolution. The other minor constituents mentioned are present in concentrations each of less than 0.1% and are handled as impurities in the process. The metals which are soluble at a pH 0.5 and precipitate between 0.5 and 2.0 are bled off. Other impurities will concentrate on the raffinate from the solvent extraction operations from whence they are bled off. These bleeding streams are hazardous and the "impurity metals" are now present in concentrations which would make them valuable, however, the size of these streams is so small that they do not warrant their processing, however they could be marketed to specialized smelters. The extraction of the valuable metals, of the hazardous constituents, the generation of a marketable mixture of minor constituents and the production of a non-hazardous residue for declassification is profitably achieved.

Jan 1, 1998

By Takeo Fujino, Nobuaki Sato, Junichi Hasegawa, Masato Nakazawa, Kohta Yamada

"Tantalum oxide thin films were deposited on quartz substrates by laser ablation of Ta2O5 target using Nd:YAG pulse laser. Deposition-was observed when a laser light energy higher than 200 mJ and its repetition rate higher than 3 Hz. A thin film of 0.1 µm thickness was obtained by the ablation using a laser light of 300 mJ and 6 Hz for 2 sec. The thickness of the film increased with increasing energy, repetition rate and irradiation time of laser. By the SEM observation, it was found that many island-like particles were deposited on quartz substrate forming a thin film. The obtained thin film, which was identified as ? Ta-O by X-ray diffraction, was oxidized to Ta2O5 by the heat treatment in air at I273 K for 3 h.IntroductionTransition metal oxides have a potential to show special characteristics in electrical, magnetic and/or optical properties. When such compounds are fabricated in the form of thin film, the special properties would be improved or new characters would appear in comparison with bulk materials. Tantalum penta-oxide is widely used as a capacitor since Ta2O5 shows high dielectric constants up to high temperatures. The tantalum solid capacitor has been fabricated by the electrical oxidation of sintered Ta metal cylinder followed by MnO2 film coating. However, further improvements, reduction and layered structure formation, are required for compacting the devices. The layered structure of thin films would be applicable for the above requirements. The formation ofTa2O5 film by low pressure CVD1), photo CVD2) and magnetron sputtering3l were reported. The laser ablation -method is one of the most convenient techniques for the deposition of thin films from their compounds, such as oxides. Formation of Ta2O5 film by pulse laser deposition (PLD) method using ArF excimer4), Nd:YAG (533nm)5) and TEA CO2 6 lasers was reported. In these PLD studies, ablation was carried out in relatively high oxygen pressures resulting in formation of Ta2O 5 film. In this paper, the deposition of tantalum oxide thin film by the laser ablation of Ta2O 5 using Nd:YAG pulse laser was examined at a viliety oxygen pressures ranging from 10-8 to 10 Torr. The morphology of the films was also investigated in relation with substrate temperature and oxygen pressure."

Jan 1, 2000

By Erich Hovestädt, Hans-Jürgen Odenthal, Christian Wuppermann, Herbert Pfeifer, Antje Rückert

"During the argon oxygen decarburization (AOD) process high-chromium steel melts are decarburized by oxygen and inert gas injection through sidewall nozzles and a top-lance. Due to the large amount of the injected processing gas, low frequency oscillations of the vessel can be observed. It is suspected that these oscillations can influence the converter's structure. The exchange of forces between fluid and the surrounding vessel is the focus of this study. An oscillation model was developed and tested, one objective being to limit the computational effort which is necessary for fully coupled and time resolved CFD and FEM simulations. Experimental results obtained from water-model studies as well as from on-sight measurements are available and were used in order to validate the numerical results. The authors' intention is a contribution towards a more in depth understanding of the factors influencing vessel vibration during the AOD process.IntroductionDuring the last four decades the AOD process has been established as a reliable and efficient refining process in stainless steel making. The injection of process gases (O2, N2, Ar) through sidewall nozzles shows advantages in mixing effectiveness compared to other injection geometries e.g. bottom blowing [1]. Stainless steel grades contain usually more than 10% chromium. With decreasing carbon content during the decarburization periods the tendency of chromium oxidation increases according to the varying chemical equilibrium which depends on the partial pressure of carbon-monoxide (CO) in the gas phase. That's why oxygen is gradually replaced by inert gases, usually argon or nitrogen, in order to lower the CO partial pressure and thus to minimize chromium oxidation. Despite the high injection velocity of approximately Ma = 1, the kinetic energy of the gas jets is consumed within a short distance from the nozzle exits due to the large density ratio between gas and melt of approximately 1:8000. With increasing distance to the nozzle exit, the initial horizontal velocity of the gas jet decreases and due to buoyancy force motion of the detached bubbles turns into a vertical direction. Subsequently a gas plume develops with its typical conical shape described by various authors [1-4]. Due to the drag force between gas bubbles and melt also the liquid phase is forced into a vertical motion. Near the free surface and the wall regions the melt flow is deflected in different directions. Subsequently, the typical flow pattern in the AOD vessel arises, as sketched in Figure 1 and described in literature [5-9]."

Jan 1, 2012

By Hojat Naderi

In this research assisted leaching of chalcopyrite using sodium peroxodisulfate was studied. Electrochemical techniques such as Tafel analysis and electrochemical impedance spectroscopy (EIS) were used to investigate the surface reactions of a chalcopyrite electrode in the presence and absence of Na2S2O8. According to the results, addition of sodium peroxodisulfate increases the current exchange of the corrosion process and prevents the formation of a passive layer on the surface of the electrode. EIS tests show the trans-passive dissolution of the passive layer on the chalcopyrite electrode in presence of Na2S2O8. Equivalent electrochemical circuits were modeled for Na2S2O8-free and -containing solutions and the model parameters were compared to determine the effect of S2O8 2− on chalcopyrite dissolution. Copper dissolution from pure chalcopyrite mineral and chalcopyrite concentrate was carried out using 15 g/L sulfuric acid solution with and without Na2S2O8. Simultaneous presence of 10 g/L ferric ion and 40 g/L peroxodisulfate salt results in about 40 and 18% of Cu extraction from chalcopyrite concentrate and pure chalcopyrite mineral, after 96 h, respectively.

By Magnus Ek, Peter Olsson

The Rönnskär Smelter has been faithful to Peirce Smith Converting during its 79 years of existence. Though a visitor to our smelter museum will easily find out that a lot has happened since the beginning – and development continues. In this paper an up-date on Converting and Casting at the Rönnskär Smelter is presented. Recent developments include an investment into converter process gas handling, but also day-to-day operational aspects such as converter aisle productivity and flexibility, but also minimal EH&S impact. 127

Jan 1, 2009

By Daoxin Wu

Originated from(C4H9O)4Ti, nano--rutile TiO2 was synthesized by low temperature hydrolysis process in this paper. After being prepared by decomposing ammonium tungstate and covering on the surface of TiO2, TiO2/WO3 were characterized by means of X-ray diffraction(XRD), UV--vis difuse reflectance(DRS), fluorescence spectrum (FS). Results showed that with the increase of the supported concentration of WO3, the reflectance of DRS and the fluorescence spectrum intensity of TiO2/WO3 decreased accordingly, which indicated the powder?s increase in light absorbance and the decrease in luminescence respectively; with the increase of calcined temperature, the reflectance of DRS increased.

Jan 1, 2009

By Daoxin Wu

In this paper, the rutile TiO2 were prepared under air, Ar and H2 calcination atmosphere by low temperature hydrolysis using Tetrabutyl titanate (C16H36O4Ti) as raw material. Powers were characterized by X-ray diffraction, UV-vis diffuse reflectance and X-ray photoelectron spectroscopy. The influence of the calcination atmosphere on the photocatalytic reactivity of rutile TiO2 for oxygen production was investigated. The photocatalytic reactivity of rutile TiO2 prepared under air, Ar and H2 atmosphere was compared under ultraviolet and visible light radiation with Fe3+ (c=8.0mmol.L-1) as electron acceptor. The results showed that rutile TiO2 prepared under Ar and H2 atmosphere had higher photocatalytic activity for oxygen production than that prepared under air atmosphere. The oxygen production rates under ultraviolet irradiation were 427.5, 378.2 and 357.0µmol.l-1h-1 respectively when rutile TiO2 was prepared under Ar, H2 and air atmosphere. The oxygen production rates under visible light irradiation were 78.2, 52.2 and 13.5µmol.l-1h-1 respectively when rutile TiO2 was prepared under Ar, H2 and air atmosphere.

Jan 1, 2008

By Jhon Cuya

Titanium dioxide is the well-known catalyst for the photodecomposition of water in UV region and its nanoparticles show better performance than its bulk materials. Furthermore, partially sulfurized TiO2 is expected to be chemically stable and have an enhanced photocatalytic activity compared with TiO2. For this purpose, the sulfurization behavior of TiO2 nanoparticles was thermogravimetically (TG) studied by a thermo-balance with a quartz spring using CS2. From the TG curve of TiO2 nanoparticles, first, the weight decrease appeared down to around 8 wt% and then sulfurization reaction started at around 500 °C at heating rate of 1O 'Cumin. The weight increase curve showed a maximum of ca 30 wt% at around 750 T and then gradually decreased to ca 12w% at 1000OC. This would be caused by the formation of TiS2 followed by the decomposition of TiS2 to lower sulfides, such as Til.08S2 and Ti3S4. From the comparison of the sulfurization of TiO2 nanpparticles with that of anatase, rutile and Ti(OH)4, it was found that TiO2 nanoparticles showed a similar behavior to that of Ti(OH)4.

Jan 1, 2003

By W. G. Davenport

H20 is present in many flash furnace inputs. Examples are: (a) moisture in concentrate and flux (b) humidity in blast (c) moisture in hydrocarbon fuel, particularly coal, Appendix IV. H20 may also leak into the furnace from damaged water-cooling jackets. H2O, especially that it be included H2O, exerts a strong cooling effect on the flash furnace. It is important our calculations. As will be seen from the calculations, gaseous and liquid H2O both increase flash furnace industrial oxygen and oil requirements. This is because gaseous H2O (humidity in blast) must be heated from its input temperature to the flash furnace off gas temperature. Liquid H2O must be evaporated and heated.

Jan 1, 2001

By Uday Pal

In direct reduction processes for iron and steel making, significant amounts of Fe-C alloy droplets are generated and these remain suspended in relatively low FeO (around 5%) containing slags. Earlier workers have found that when the FeO content in the slag is <5%, the decarburization reaction becomes extremely slow (virtually ceases to occur) even though the alloy droplet contains a significant amount of carbons (2-3%). Understanding this rate controlling kinetic phenomena is crucial to designing an&apos; optimum direct steel making process. We studied decarburization of Fe-C particles by low FeO (<5%) containing CaO-SiO2A12O3 slags and found that by putting both the droplet and the slag in direct contact with an inert electronically conductive member that extends deep inside the slag bulk were able to quickly and completely decarburize the droplets. A detailed description and an explanation of the process will be presented.

Jan 1, 1995

By Yotamu Stephen Rainford Hara, Animesh Jha

The investigation focuses on a low temperature recovery of Cu and Co from a 40 wt% SiO2-(30 wt%Fe,6 wt%Al)2O3-10wt% CaO-7wt%CuO-7wt%CoO slag over a temperature range of 1173K to 1323K. The alloy phases containing Cu-Co and Fe-Co alloy formed via the carbothermic reduction of oxides: MO + C = M + CO(g), where M represents metallic copper, cobalt or iron. In the direct reduction of oxides, the recovery of metallic phase was well below 90% at 1323K, due to the kinetic barrier which was analysed and attributed to oxygen and metal-ion transport in the slag. This barrier was overcome by adding CaSO4 and carbon, which yields a matte (MS) phase via MO + CaSO4 + 4C = MS + CaO + 4CO reaction. Lime thus produced in situ participates in metal oxide/metal sulphide reduction reactions, which are analysed with the help of X-ray powder diffraction, scanning electron microscopy, and thermogravimetric analysis.

Jan 1, 2014

By Linlin Wu, Marlen Bertram, Chris Bayliss, Bernard de Gelas, Samantha Jones, Kurt Buxmann

"Environmental management is one of the industry cornerstones of sustainable development. In order to understand fully the environmental aspects associated with the raw material acquisition, production, use, and end-of-life operations of aluminium products, the Aluminium Industry has developed an approach based on Life Cycle Analysis (LCA) methodology.Within this framework, the Primary Aluminium Industry has established a global Life Cycle Inventory (LCI) data set. Inventory flows include inputs of raw materials, energy and water, emissions to air and water, and solid waste.This paper presents the latest LCI data update by the International Aluminium Institute for the year 2010, based on a survey of aluminium plants globally, including bauxite mining, alumina refining, anode production, electrolysis and casting. This update also includes some performance tracking based on the last LCI data collection in 2005, reflecting progress in efficiency and technology, as well as changes in the geographical location of the industry [2010 data pending]. IntroductionIn 2010 the Primary Aluminium Industry produced a total of 41 Mt of aluminium. The International Aluminium Institute (IAI) membership represents approximately 70% of total global production. The industry recognises the importance of co=itting to reducing the environmental impacts of producing primary aluminium, and the significance of working towards a more sustainable future. As part of this co=itment the IAI has developed an in depth Life Cycle Inventory programme, in which data is collected every five years, with supplementary key metrics collected annually.In 2003 the IAI released its first Report ""Life Cycle Assessment of Aluminium: Inventory Data for the Worldwide Primary Aluminium Industry"" based on the year 2000 with an update Report released in 2007, based on 2005 data.This paper presents the latest update for the year 2010 [2010 data pending]. It has been prepared with the same view of collecting all significant Life Cycle Inventory data (raw materials and energy use, air and water emissions and solid waste generated) associated with producing primary aluminium ingot from bauxite ore, with worldwide coverage. The intended purpose of the Inventory Report is to accurately characterize resource consumption and significant environmental aspects associated with the worldwide production of primary aluminium. It reflects the fuct that primary aluminium is a globally traded co=odity."

Jan 1, 2012