Search Documents

By A. H. Larson, L. G. Twidwell

The influence which Au, Ag, Sb, Bi, Sn, and Cu have, both individually and collectively, on the activity coefficient of sulfur in liquid lead at 600"C zuas studied by circulating a H2S-Hz gas wlixture over a specific lead alloy until equilibrium was attained. Subsequently, the H2S concentration in the equilibrium gas mixture and sulfur concentration in the condensed phase were deterruined. The elements gold, silver, and antinzony (above 8 at. pct) increased the activity coefficient of sulfur. Bismuth had no apparent effect. Tin (above 3 at. pct) and copper decreased the coefficient. The influence of an individual element, i, on sulfur is best reported as the interaction parameter, riS, which is defined as The values o these first-order interaction zus are: ESzu = —55.0. These interaction parameters are used to predict the activity coefficient of sulfur in six fouv-component alloys and one seven-component alloy. Comparisons are made with direct experimental determinations. INTERACTIONS in dilute solution have been studied by many investigators. Most of the experimental work has been confined to solute-solvent interactions in simple binary systems and solute-solute interactions in ternary systems. Dealy and pehlke"~ have summarized the available literature on activity coefficients at infinite dilution in nonferrous binary alloys and have calculated from published data the values for interaction parameters in dilute nonferrous alloys. Interaction parameters are a convenient means of summarizing the effect of one solute species on another in a given solvent. Only a few investigators have studied interactions of the nonmetallic element sulfur in a metallic solvent. They are as follows: Rosenqvist,~ sulfur in silver; Rosenqvist and Cox,4 sulfur in steel; chipman, sulfur in alloy steels; Alcock and Richardson,% ulfur in copper alloys; Cheng and Alcock,' sulfur in iron, cobalt, and nickel; Cheng and ~lcock,' sulfur in lead and tin. The only reported work on the Pb-S system in the dilute-solution region is that of Cheng and Alcock.' Their investigation involved a study of the solubility of sulfur in liquid lead over the temperature range 500" to 680°C. The results may be summarized by the following relationship: S (dissolved in lead) + Pb(1) = PbS(s) log at. %S = -3388/T + 3.511 Experimentally, it was found that Henry's law was valid up to the solubility limit of sulfur in lead, i.e., at 600°C up to 0.43 pct. Their investigation did not include the study of sulfur in lead alloys. More accurate calculations could be made in smelting and refining systems if activity coefficients of solute species could be accurately predicted in complex solutions. One of the objectives of this study was to compare the experimental data with the values calculated from the equations derived from models for dilute solutions proposed by wagner9 and Alcock and Richardson. A temperature of 600°C was chosen as the experimental temperature to attain reasonable reaction rates and to minimize volatilization of the condensed phase. EXPERIMENTAL Materials. The Pb, Au, Ag, Sb, Bi, Sn, and Cu used for preparation of the alloys were American Smelting and Refining Co. research-grade materials. All were 99.999+ pct purity except the antimony and tin which were 99.99+ pct. The initial alloys prepared for this study consisted of twenty-one binary alloys, eleven ternary alloys, and one six-component alloy. The constituent elements were mixed for each desired alloy and were placed in a crucible machined from spectrographically pure graphite. The crucible was placed in a vycor tube which was evacuated with a vacuum pump and gettered by titanium sponge at 800°C for 8 to 12 hr. After the gettering was completed, the chamber containing the titanium was sealed and removed. The remaining sample chamber was placed in a tube furnace at 800°C for 2 hr and quenched in cold water. The final operation consisted of homogenization of the alloy for 1 to 2 weeks at a temperature just below the solidus for the individual system. The resulting master alloys were sectioned into small pieces and a random choice made for individual equilibrations. Cobalt sulfide (Cogs8) used to control the gas atmosphere in the circulation system was prepared by passing dried HzS for 24 hr over a Co-S mixture heated to 700°C in a tube furnace. This material was then mixed with cobalt metal to give a two-phase mixture which, when heated in hydrogen to a particular temperature, produced a desired H2S/H2 gas atmosphere in the circulation system. A Cu2S-Cu mixture also used in this study was prepared in a comparable manner. Apparatus for Equilibrium Measurements. The experimental technique of this study required apparatus

Jan 1, 1967

By Marius S. Darrow, William B. White, Rustum Roy

The PbS-PbTe systen has been studied by quench-ing and D.T.A. techniques f?om 400' to 1150°C. Runs were made in evacuated silica tubes so that all equilibria are at the vapor pressure of the system. Lattice parameters of the quenched salnples , measured by X-ray diffraction, show a complete crystalline-solution series existing over a narrow temperature range between approximately 805" and 871°C. An exsolution dome extends from a maximum of about 805"C (approximately 30 mole pct PbTe) to 1 and 96.5 pet PbTe at 400°C. A narrow melting region, deternined by D.T.A., extends form 918c (mp PbTe), The shapes of the liquides and solidus curves imply the existence of a minimum at 871°C at approximately 65 pct PbTe. THe exact composition of the minimum could not be established due to the very narrow two-phase region. At compositions containing less than 50 pet PbTe, liquidus temperatures begin to increase, while the solidus remains almost flat to about 15 mole pet PbTe before beginning to vise toward the mp of PbS (1075 C). LEAD sulfide and lead telluride are isostructural (NaC1 type) semiconductors whose electrical and optical properties have been extensively studied and used in recent years. If appreciable crystalline solution exists between these compounds, the variation of physical properties with composition could be of interest. The purpose of this investigation was to determine the extent, if any. of crystalline solution, and to obtain the phase diagram for the system. To the knowledge of the authors, only three studies of the system PbS-PbTe have been reported, and, in chronological order, each investigation found an increasing amount of crystalline solution. In 1956, Yamamoto reported finding no evidence of crystalline solution between the compounds. Sindeyeva and Godov-ikov,' in 1959, found very limited crystalline solution. but only under conditions of excess tellurium concentration. Finally Melevski s3 investigation in 1963 indicated that one solid phase exists in the region from PbS to 7 pct PbTe and from 82 pct PbTe to PbTe at 886'C, with an eutectic at 55 pct PbTe at that temperature. Detailed data on the solvus boundary were not given. EXPERIMENTAL EQUIPMENT AND MATERIALS Commercially produced PbTe and PbS powders were used as starting materials. Batches of specific mole percent composition were accurately weighed and mixed in a plastic bottle, in a shaker mill. An analy- sis of impurity content is given in Table I for pure PbS and PbTe and for two randomly selected batches after the powders were mixed. Individual samples, ranging in weight from 0.2 to 0.5 g, were sealed in evacuated silica tubes which had been thoroughly washed and rinsed with acetone and distilled water. Thus all data taken were at the pressure of the system. Subsolidus relations were studied down to 400°C by heating the samples in a vertical tube furnace for 24 hr. The sealed tubes were quenched in water with quench time from the hot zone not exceeding 1 sec. Temperatures were measured by a chromel-alumel thermocouple and controlled to 53°C for most runs. The number and composition of phases present were determined from powder X-ray diffraction patterns taken at room temperature on a Norelco diffractome-ter, using silicon as an external standard. Above 850°C quenching techniques were, in general, found to be unsatisfactory, and differential thermal analysis (D.T.A.) was used to determine melting relations. The evacuated tubes were recessed about 1 cm at one end to accommodate the differential thermocouple. Al203 was used as the reference material in a similar tube containing the other side of the differential couple. For temperature measurements, a separate thermocouple was placed in the recess of the tube containing the sample to be measured, thus providing an opportunity to obtain thermal, as well as differential, analysis. All thermocouples for these measurements were Pt-Pt 10 pct Rh. Temperature and differential curves were recorded separately on synchronized strip-chart recorders. Thermocouples and recording equipment were calibrated using NaCl and gold standards, using the melting points 801" and 1063 C, respectively, which span most of the temperature range of interest. Heating and cooling rates generally were from 4 to 7°C per min. It was found, in fact. that rates ranging from 1.5 to 25°C per min did not significantly change the data obtained.

Jan 1, 1967

By C. H. Li, R. J. Stokes

This paper compares the fracture behavior of tungsten rods in three conditions: recrystallized. recovered, and wrought. Notched specimens suhjected to a 50 in.-lb impact load showed ductile-brittle transitions at 700, 4.90°, and 440°C, respectinely. The recrystallized material had an equiaxed pain structure and jracbred by simple cleavage from a grain boundary source at all temperatures up to 700°C. The wrought and recovered material had an elongated fibrous structure and at low temperatures fractured by cleavage originating from the notch. As the transition temperature was approached cleavage was preceeded by more and more intergvanular splitting which deflected the crack front into planes parallel to the tensile axis. The enhanced toughness of wrought and recovered tungsten was attributed both to its inability to initiate cleavage because no pain boundaries were suitably oriented perpendicular to the tensile stress and to its inability to maintain cleavage because of intergranular splitting ahead of the crack. It has been appreciated for a long time in a qualitative manner that the room-temperature brittleness of fully recrystallized tungsten may be alleviated by working the material at relatively low temperatures.' More recently this difference in mechanical behavior between wrought and recrystallized tungsten has been examined quantitatively by measurement of the tensile properties as a function of temperature. In these experiments brittleness has been expressed in terms of ductility or reduction in cross-sectional area upon tensile fracture or in terms of the bend radius before fracture under bending.' This work has shown the existence of a fairly sharp transition from brittle to ductile behavior with an increase in temperature. The ductile-brittle transition temperature for recrystallized material is approximately 200°C higher than for wrought material. An increase in strain rate, small additions of impurity,' or an increase in grain size4 shift the respective transition temperatures to higher values, but the difference between them remains approximately the same at 200°C. A number of explanations for this embrittlement by recrystallization have been given. It has been blamed either on the concentration of impurity at the grain boundaries, the increase in grain size, or the change in texture which occurs upon recrystallization. The present paper examines the effect of different heat treatments on the notch-impact behavior of commercial powder-metallurgy tungsten rods. The change in the ductile-brittle transition temperature for this method of loading and the fracture mode has been related to the different mi-crostructures produced by heat treatment. EXPERIMENTAL PROCEDURE Commercial swaged powder-metallurgy tungsten rods 1-3/8 in. in length and 1/8 in. in diameter were machined to introduce a sharp V notch 0.030 in. deep. To change the microstructure from that of the as-received wrought material some of the specimens were subjected to an anneal in nitrogen either at 1300° or 1400°C for 8 hr or at 1600° or 2000°C for 1/2 hr. The notched rods were then placed in a miniature Charpy-type impact machine and struck at their midpoint (opposite the notch) with a hammer designed to deliver 50 in.-lbs of energy. The strain rate at the base of the notch was estimated to be approximately 100 sec-1 at the instant of impact. The specimens were heated in situ to the desired impact temperature. The microstructures produced by the various anneals were studied by both X-ray diffraction and metallographic techniques. Fig. 1 reproduces the microstructures observed metallographically following a 10-sec electroetch in a 10 pct KOH solution. Fig. l(a) shows the elongated fibrous grain structure of the as-received material. Following the anneal at 1300" or 1400°C the grain structure was still elongated as shown in Fig. l(b) but the etch pits delineated dense polygonized dislocation arrays within many of the grains. Occasionally a relatively dislocation-free recrystallized grain was found growing into the matrix. The anneals at 1600° and 2000°C resulted in complete recrystallization and some grain growth. The grains produced at 1600°C were still slightly elongated as shown in Fig. l(c) whereas the anneal at 2000°C produced equiaxed grains. The changes in grain size produced the expected changes in the X-ray back-reflection patterns; there was no indication either in the as-received material or the annealed material of any preferred orientation. RESULTS a) Impact Behavior. Fig. 2 reproduces the ductile-brittle transition curves measured in the manner described in the previous section. It can be seen that under these testing conditions the as-received

Jan 1, 1964

By Mark Malamphy

THE occurrence of outcrops of bituminous schists and sandstones impregnated with heavy asphaltic petroleum first directed attention to the Sao Pedro area as a possible source of commercial production of petroleum. Since 1920, more than 20 wells have been drilled in this area. The discovery of oil shows and small quantities of natural gas in some of the early wells led to the continuation of drilling in the hope that more important findings would result. During the early part of 1934, detailed magnetometer observations were made in this area, and a con-siderable number of torsion balance stations were occupied. The results of these geophysical observations help considerably to clarify the structure of the area and the very considerable amount of geologic information available makes possible a much more exact interpretation of geo-physical anomalies. In presenting the results of these observations, and interpretation of the geophysical data, certain actual case problems are included; i.e., geophysical anomalies due to anomalous masses of which the forms and positions are more or less known. Although anomalies due to igneous intrusions are probably more important to geophysicists in Brazil than in other countries, these data have a certain interest for all geophysicists, particularly because they were obtained in the south magnetic hemisphere, where the lines of magnetic force are directed upward, and in a region of moderately low inclination. This is considered as a geological-geophysical problem, and only passing mention will be given to the petroleum possibilities of the area.

Jan 1, 1936

By K. A. Jackson, G. A. Chadwick, A. Klugert

The diffusion field ahead of a lamellar interfnce is analyzed using an electrical analog. A self-consistent solution is obtained for the shape of the interfnce and the diffusion field by an iterative process. The solutions presented here are for a 50-50 eutectoid or eutectic, The shape of the interface is found to he independent of growth velocity and lamellar spacing, and to depend on the relative values of interfacial free energies at the phase houndaries . The mode of growth of lamellar eutectics and eutectoids has been a subject of much interest for many years.1-4 Mehl and Hagel 1 have shown photomicrographs taken by Tardif when he attempted to determine experimentally the shape of an advancing pearlite interface; the results are completely ambiguous. Brandt' and schei13 have made approximate calculations of the composition ahead of a lamellar growth front. The shape of the advancing front and the composition distribution ahead of the front are difficult to calculate because one depends on the other. It is the purpose of the present paper to describe a method by which this calculation has been done. Lamellar-eutectic growth usually occurs under conditions where the growth is fairly rapid, and the interface temperature is close to the eutectic temperature. The growth rate is usually determined by heat flow. Eutectoid growth, on the other hand, can best be studied by quenching to some temperature, and allowing growth to proceed isother-mally. In both cases the growth is believed to be controlled by diffusion* rather than by the atomic kinetics of the transformation. This being the case, a single treatment of the diffusion equation will apply to both cases, provided the region of the interface in a eutectic may be considered to be isothermal. If a part of the interface could appreciably change its thermodynamic driving force by advancing ahead of or lagging behind the mean interface, then the two cases would not be similar. Eutectics normally grow in temperature gradients of the or-der of a few degrees per centimeter. The normal eutectic spacing is the order of a few microns. Part of the interface would have to extend many lamellar spacings ahead of the mean interface before it experienced sensibly different conditions. The interface temperature is usually a few tenths of a degree below the eutectic temperature so that temperature differences of the order of one-thousandths of a degree (a displacement of one lamellar spacing) would be unimportant. Protrusions large compared to the mean spacing do occur when one phase only grows into a eutectic liquid. This is usually a dendritic type of growth, and easily distinguishable from the lamellar mode of growth. A single treatment of lamellar growth will apply equally well to both eutectic and eutectoid decomposition. At the interface, which as shown above is essentially isothermal, the difference between the equilibrium eutectic temperature Teu and the actual interface temperature Ti, can be divided into two parts: 1) the composition varies across the interface, so that the local equilibrium temperature is not Teu; and 2) the interface is curved, so that the local equilibrium temperature is depressed according to the Gibbs-Thompson relationship. This undercooling can be written as Teu-Ti =?T = mAC(x) + a/r(x) [1] where ?C(X) is the departure of the composition at a point x on the interface from the eutectic composition, see Fig. 1, r(x) is the local radius of curvature at a point x on the interface, m is the slope of the liquidus line on the phase diagram, and a is a constant given by where s is the interfacial free energy, TE is the equilibrium temperature, and L is the latent heat of fusion. The calculations in this paper will be made only for the case where the phase diagram is symmetric, that is, the eutectic occurs at 50 pct, the liquidi have the same magnitude slope m at the eutectic temperature, and C,, the amount of B rejected when unit volume of a freezes, see Fig. 2(a), is the same for both phases. As shown in Fig. 2(b), the composition ahead of the a phase will be rich in B, the composition ahead of the ß phase will be rich in A. The composition at the phase boundary is the eutectic composition. The difference between the local liquidus temperature and the actual tempera-

Jan 1, 1964

By C. L. Sarff

[Automation has become a word that means many things. To management it is the end of the rainbow; you push a button and all your problems are solved. To the working man it is a horrible monster that is taking his livelihood away. To the maintenance man it is a complex that overwhelms him when he thinks of trying to find the trouble when the machine is not operating, properly. Automation has been with us in the coal nines for many years. Long before my time you were using float switches on mine sumps to control the level of the water. That?s automation in the truest sense of the word, but we call it automatic and think nothing of it. If we use the word automatic instead of automation your mine electrician and mechanic will take hold of the problems in stride.]

Jan 1, 1962

By G. Morin, S. Amira, F. Chiesa, B. Duchesne

"The effect of heat treatment on the stress corrosion cracking (SCC) resistance of A206 aluminum alloy was studied using the breaking load test according to ASTM G139 standard. This method uses the residual strength measurement from tensile test specimens previously stressed axially while exposed to the 3.5% NaCl alternate immersion test according to ASTM G44 standard. The residual strength after exposure is used as a measure of SCC degradation. The performed heat treatments were conventional natural aging T4 and artificial over-aging T7 tempers in addition to artificial aging T6 temper added for purpose of comparison. These tests showed that A206-T4 has a good resistance to SCC at pre-loads up to 100 MPa while A206-T7 was prone to SCC for pre-loads of 0 and 50 MPa, and showed total loss of ductility for pre-load of 100 MPa. Both A206-T4 and A206-T7 pre-loaded at 150 MPa showed poor resistance to SCC. A206-T6 showed the worst susceptibility to SCC as it lost all mechanical resistance at the end of the alternate exposure to 3.5% NaCl solution, even without any applied pre-load. Metallographic analyses showed that the resistance of A206 alloy to SCC is mainly affected by the transition from pitting to intergranular corrosion attack. The initiation and the propagation of intergranular corrosion attack might be assisted by high stress concentrations in the pits, particularly for pre-loads higher than 100 MPa. The transition from pitting to intergranular corrosion can also be promoted by hydrogen evolution from growing pits, which supports crack propagation by hydrogen embrittlement.INTRODUCTIONA206 aluminum-copper casting alloy offers ones of the best mechanical properties among the aluminum foundry alloys. This alloy belongs to the 206 alloy family developed in 1970s as an alternative to the highly resistant and ductile but more expensive Ag containing 201 alloy (Tiryakioglu, 2009). A206 showed also good low cycle fatigue strength (Sigworth, 2002). These properties made A206 alloy a strong candidate for some vehicles lightweighting applications. In spite of its interesting properties cited above, A206 alloy was rarely used in critical applications due to its tendency for hot tearing and stress corrosion cracking (SCC). Studies of A206 hot tearing behavior showed that this tendency can be reduced by improving castability and by grain refinement (Sigworth, 2002). The optimisation of the casting design can also prevent the tendency toward hot tearing. The SCC of aluminum-copper alloys arises from their susceptibility to localised corrosion, especially in chloride containing media. The localised corrosion in Al-Cu alloys is caused mainly by their heterogeneous microstructure, where the presence of many phases leads to the formation of micro-galvanic coupling with the matrix. However, most of the studies aimed at investigate the SCC of Al-Cu alloys concerned the wrought ones, especially the AA2024 alloy tempered in the T3 (or derivative) condition and few studies concerned the 206 and cast alloys in general (Alexopoulos, 2009 and 2016; Campestrini, 2000; Vogt, 1998; Talamantes-Silva, 2008; Zhang, 2003). Jean et al. (Jean, 2009) studied the effect of heat treatment on SCC behavior of B206 alloy using alternate immersion technique and grain boundary attack method and did not find direct correlation between the two methods. Another study showed that aging of 206 alloy may make a casting susceptible to SCC (Sigworth, 2002). However, these studies did not provide detailed information about the mechanisms of SCC of 206 alloy, as well as the effect of the stress intensity. The present work investigates the effect heat treatments and the stress intensity on the morphology of the corrosion attack and the SCC behavior A206 aluminum alloy. This study uses the breaking load test according to ASTM G139. This test utilizes direct tensile specimens and was developed to give a more quantitative measure of the SCC performance of resistant aluminum"

Jan 1, 2016

By J. Murray Riddell, Arthur E. Anderson, Grover J. Holt

Out of the depths of each business cycle we emerge with a stimulus for greater efficiency and a realization of progress in industrial technique. The recent years have not been an exception to this rule, and in retrospect we sense that significant advances have been made in mining practices on the Mesabi Range, with emphasis on speed of production and economy of operation. A survey of such changes does not reveal anything that is fundamentally or basically new, but it is apparent that ideas and machines that have found wide application in industry elsewhere, with necessary modifications, are being put to productive use in mining iron ore. Innovations in transporting and conveying ore from the open pits stand out with greatest prominence, so that, in the main, it will be with these features that this paper will treat, in the review of progress made to this date. The late years have witnessed the development of small deposits for open-pit operation, the cleaning up of pits nearing exhaustion, and in two large operations the approach to the limit for haulage by steam locomotives, owing to grades, making it necessary to recover the ore in slopes, track benches and below the power-shovel limit by a milling and scram operation. For several years small standard-type dump trucks have been used in clean-up or scram operations within the pits, but during the season of 1936 the first effort was made to use heavy truck haulage in the transportation of stripping and iron ore. The new units in use today vary from 15 to 20 tons in capacity, and are equipped with powerful gasoline or Diesel engines and supplemented by trailers or wagons on rubber or crawler treads. The Diesel engine finds favor with most operators because of fuel economy. These units develop upward of 125 hp. in the 15-ton trucks. The speed of these trucks varies from 2 miles per hour in Pow gear to 35 in high gear. The transmission affords 12 speeds forward and 3 speeds in reverse.

Jan 1, 1940

By S. G. Cupschalk, F. A. Dahlman, J. J. Wert

Studies have been undertaken to determine the indicidual effects of particle size, degree of long-range ovder, antiphase domain size, and root mean square stran on the microhardness and yield strength of ordered alloys. Dnta have been analyzed for Cu3Pt initzally ordered to a value of 0.82 and after deformations of 1 and 6 pct. It was observed that deformation fleatly reduced the degree of long-range order. Furtherrnore, wztkin this range of relatively small deforntntlons, the average particle size changed very little while the antiphase domain size was greatly reduced. Smultaneosly, the mcrohardness changed by a factor of two durzng the deforrtation process. PREVIOUS studies have reported some of the effects of cold work on the broadening of X-ray diffraction peaks. These investigations were performed on powder and wire samples representing both ordered and disordered states; i.e., the specimens were initially studied in a severly cold-worked condition. By comparing the difference in line shape between the annealed and cold-worked peaks, fundamental information was obtained concerning particle size, strain distribution in different crystallographic directions, degree of long-range order, and change in antiphase domain size. Considerable theoretical work has been done concerning the analysis of diffraction data obtained from cold-worked metals. Stokes' expressed the change in diffraction profiles in terms of Fourier coefficients. Much of the work in this area has been summarized by warren2 in an extensive review article concerning the analysis of plastic deformation by X-ray diffraction. Cohen and Bever3 applied these techniques in studying the effects of cold work on alloy systems exhibiting long-range order. They utilized the Fourier coefficients of fundamental peaks in conjunction with those of the superlattice peaks to determine the change in antiphase domain size. Little work of this nature has been reported for ordered systems that have undergone small degrees of plastic deformation. The purpose of this investiga-tion was to determine the effects of small deformations in such a material with respect to particle size, strain distribution in various crystallographic directions, antiphase domain size, degree of long-range order, and hardness. EXPERIMENTAL PROCEDURE CusPt was used for the initial investigation since the order-disorder transformation takes place with- out a change in crystal structure. The transformation is readily detectable via X-ray diffraction techniques due to the large difference in the scattering factors of copper and platinum. Additionally, the alloy is relatively low melting (approximately 1300°C) and is easily deformable in both the ordered and disordered states. 1) Specimen Preparation and Cold Working. A 100-g, 12-in. diam., cylindrical specimen of Cu3Pt was prepared by melting and casting 99.99 pct pure Cu and Pt i.n vacuo. Prior to any mechanical working, the material was homogenized in a vacuum for 60 hr at 100O0C, and surface defects were removed by machining to a depth of approximately 116 of an in. The material was then cold-rolled, with an intermediate anneal, into a strip approximately 12 in. wide by 14 in. thick. Straightening and flattening removed another 0.025 in. from the thickness. After a recrystallization treatment at 750°C for 30 min, the specimen was slow-cooled from 55OoC, at the rate of 6°C per hr, down to 150°C to induce superlattice formation. This treatment yielded an ASTM grain size of 7 and a degree of long-range order equal to 0.83 0.06. After obtaining X-ray and Knoop hardness data, the sample was cold-rolled approximately 0.75 pct in one pass through a hand-operated jewelers' mill. X-ray and hardness data were again obtained and the specimen was reduced an additional 5.41 pct in a single pass through the mill. 2) X-Ray Measurements. The specimen was examined in the ordered condition and after the two degrees of cold working previously mentioned using a General Electric XRD-5 unit equipped with a spectrometer and scintillation counter. Using Mo-Ka radiation with a zirconium filter, six orders of the 100 reflection were obtained. It was anticipated that point counting would be necessary for an accurate determination of the low-intensity peaks and tails: however, it was demonstrated that, by using a scanning speed of 0.2 deg per min and the appropriate time constant, the recorded data were sufficiently accurate. Thus, for ease of experimental procedure, all peaks were recorded on chart paper. Specimen position in the holder was considered to be insignificant after making a series of measurements of the same peak area in different positions with respect to the beam. Since peak overlapping did occur at high values of 20, it was necessary to separate the peaks graphically prior to analyzing the data in order to minimize this source of error. The peak tails were also carefully drawn to obtain the best possible data. Fourier coefficients of the line profiles were calculated on an IBM 7072 computer, and graphical meth-ods2j3 were employed in analyzing the results. For this type of calculation, in which the line profile is represented by intensities taken at set intervals, the intervals selected must be sufficiently small to give an accurate representation of the line profile. It was decided that for 20 = 0.02 deg the line profiles were

Jan 1, 1967

By Arcy A., J. G. Davis, D&apos Shock

Results of a pilot operation in the Carlsbad Basin are discussed. After hydrafracing between wells, a block of potash was removed by solution techniques. The distance between frac wells was about 200 ft, the thickness of potash mineralization, 5 ft. By proper manipulation, a feed of concentrate brine was obtained. The ex-periment showed that the thin-bedded potash could be removed by the solution techniques. The details of well construction, method of operation, and removal rates are discussed. Continental Oil Co.'s laboratory research on the fundamentals of potash solution mining has been expanded by means of a series of field tests, and subjects such as well completion and hydraulic fracturing were added to the investigation. Both single-well and multi-well systems were studied in the field work. Discussion Background: The current paper discusses one field test in which potash was solution mined by a two-well system from a thin sylvinite zone. The potential economic value of solution mining evolves from (1) the use of drilled holes and solution techniques instead of excavated shafts and caverns and (2) the ability to mine both land and marine deposits through any type of overburden geology and below conventional mining depths. Recent interest has been focused on potash' and other soluble minerals, such as trona. Solution extraction minerals, such as copper and uranium, are also worthy of important consideration. In addition, many of the techniques are directly applicable to the construction of horizontal underground storage carverns in salt. There are two general approaches to potash solution mining. The first is to mine on a single-well basis, in which the same well bore is used for both injection and production. This method is slow, and the areal extent may be quite limited in other than very thick ore zones. The second, and the preferred approach, is to mine on a multi-well basis in which the solvent is circulated between wells. This technique, if applied in a manner which allows the ore zone to be mined from the bottom upward, results in nearly all the solution taking place from the cavern roof. Salt removal rates, therefore, are very much higher than from a single-well system.l Wells can be interconnected into a multi-well pattern by several means. One is to join single-well caverns in the lower part of an ore zone. Another is to use the hydraulic fracturing techniques developed in the oil fields.' We preferred the fracture approach because of its potential for creating the greatest area of salt exposure. Test Site Description: The field tests were conducted in New Mexico's Carlsbad Basin, where the potash deposits are flat and uniform over reasonable distances. Here, 12 potash zones are present in the massive Salado Salt section. The specific target was the Third Ore Zone which is about 4 ft thick at our location and about 1150 ft deep. The test pattern was designed in the shape of an equilateral triangle with a fourth well located in the center, 200 ft from each of the vertex wells. This configuration allowed the ore zone to be hydraulically fractured from the center well with good assurance that the fracture would intersect the bore of at least one outside well. Several multi-well test patterns would be available if the fracture connected all wells. Well Completion: Surface casing was set in the top of the Salado Salt at 600 ft to shut off water flows from the surface sands, and the salt section was drilled and diamond-cored to a point below the Third Ore Zone. A drilling fluid made of diesel oil with a small amount of emulsified water was used to drill and core the salt. This fluid was highly successful in preventing enlargement of the drilled hole and in promoting good core recovery. The three outside wells were completed by setting 51/2-in. casing at the base of a streak of anhydrite about 20 ft above the ore zone. Pipe was set high so that the intersection point of the fracture could be detected even if the fracture migrated above the ore zone as it progressed outward from the center well. The center well itself was completed by cementing 51/2-in. casing through the Third Ore Zone. Cement bond logs run on the center well have shown excellent bonding. Fracturing Practice: A mechanical tool was used to cut a notch through the casing and into the salt at a point about 1 ft below the ore zone in the center well. The purpose of this notch was to fix the point of fracture entry into the salt. The fracturing was done with water at injection rtaes as high as 30 bbl per min. The salt parted at 1450 psi; and it required only 5 min for the fracture to reach the well which was 200 ft to the south. It took about 5 min more to reach the other two wells. Caliper surveys were run to locate the point of fracture entry in the three outside wells. The fracture appears to have drifted downward slightly, entering the outside wells at the top of a streak of carnallite 8 or 9 ft below the ore zone. A cross section of the wells selected for the multi-well test is shown in Fig. 1. The figure includes KC1 values based on core analysis and the trace of the fracture plane between the wells.

Jan 1, 1971

By Jerome F. Kuzmick

Many investigations have been made on the effect of the variables of pressure, sintering temperature and sintering time on the physical and microstructural charactcristics of metal-powder compacts. Severa1 such investigations have indicatcd that pressure is the least important of these three factors in an attempt to secure a dense. strong compact by a simple coltl-pressing and sintering procedure. However, it was felt that a further study of the effect of pressure on pressed and sintered metal powder compacts might prove interesting, for the following reasons: In work done in the past on the effect of pressure, temperature. arid time, the, metal-powder compacts were subjected to long sintering periods, and temperatures right up to the melting point of the metal were applied. It was thought that pressure might exert a more profound effect under short-time simtering and within narrower ranges of temperature. such as normally would be applied in large-scale production of metal-powder parts. 2. It was hoped that something further might be learned of the nature of the bond in pressed and sintered metal-powder compacts. 3. It was thought that interesting infor mation concerning the work-hardening effect of pressure on the crystal structure. of sintered metal-powder compacts would be obtained. Procedure Rectangular bars, 2 by 1/2 by 1/4 in. were molded from the following metal powders: Atomizcd till powder, 325-mesh Atomized aluminum powder, 325-mesh Reduced copper powder, 100-mesh Electrolytic iron powder, 100-mesh Atomized 70-30 brass powder, l00-mesh The, till powder was molded at various pressures up to 40 tolls per sq. in. This was the maximum, because at higher molding pressures there was considerable extrusion of tin into the die wall, jamming the die plungers. The tin specimens were not -in tered, as this phase of the work was- done merely to see how much a very sold metal could be compressed. The aluminum powder was compressed at various pressures up to 50 lons per sq in. Higher pressures could not be used because of extrusion into the die wall The compacts were sintered one hour at 000 in pure dry hydrogen. The copper powder was molded at vari-ous pressures up to 96 tons per sq. in. One set was sintered at 750°C., another at 050 C. for one hour in pure dry hydrogen. The electrolytic iron powder was molded at various pressures up to 00 tons per sq. in. and sintered, one set at Soo°C and one set at 1300°C for one hour in pure dry hydrogen. Extra 325-mesh specimens were also prepared to study the effect of reduced particle size on grain structure. The brass powder was molded at various pressures up to 96 tolls per sq. in. and silltered for one hour. one set at 65o°C. and one set at 800°C, in pure dry hydrogeu.

Jan 1, 1945

By F. E. Pawlek, J. K. Gerlach

The chloridizing roasting of ores is applied when metal sulfides and oxides are to be converted into soluble or volatile compounds. The chlorine required is either obtained from the admixed chlorides of sodium or calcium or added in the gaseous state. In the first part of the investigations the reaction rate of the chlorides of sodium or calcium with gas mixtures of SO,-0, or SO ,-O2 ,-SO , was measured. The rate for reactions with gas mixtures SO2-O2 is ThE chloridizing roasting of ores is applied when metal sulfides and oxides are to be converted into soluble or volatile compounds. At present the process is mainly applied to produce nonferrous metals which occur in pyrite cinders in small concentrations. Thereby the nonferrous metals are converted into water-soluble, acid-soluble, or volatile compounds whereas all the iron remains as insoluble oxide. The chlorine required is either obtained from the admixed chlorides of sodium or calcium or added in the gaseous state. The reactions occurring during the roasting process can be divided into two groups: solid-solid reaction and gas-solid reaction. The reactions between solids proceed by means of solid-state diffusion and are therefore of low velocity. The heterogeneous reactions between solids and gases of the roasting atmosphere5 are high-velocity processes and determine the velocity of the chloridizing roasting. These gas-solid reactions shall be the subject of the paper presented. In order to investigate the still little-known processes which occur during the chloridizing roasting 6-' the complex reaction is split into several partial steps. First the reactions of NaCl and CaCl, with gas mixtures of SO2 and 0, have been investigated at temperatures between 500" and 600°C by measuring the weight increase of the samples. The gas mixtures used in this series of experiments had first variable compositions, then the amount of SO 2 had been increased. Furthermore the influence of Fe 2 O3 admixtures upon these reactions, the behavior of pure Fe 2 O3 with the gaseous reactants, and the chlorination of the sulfides of lead, copper, nickel, and zinc have been investigated. FORMATION OF GASEOUS CHLORINE Pyrite cinders are never completely roasted and therefore contain still a small amount of sulfide sulfur. When heated again in air, this sulfur is converted into SO,. Accordingly the formation of chlorine can first be described by the reactions: dependent on the composition of the gas phase. If more than 1 pct SO 3 is added to the roasting gas, the reaction rate is determined only by the concentrations of the SO,. In the second part the reactions between chlorine and metal sulfides are discussed. The rate of formation of gaseous chlorine is higher by me order of magnitude than is the reaction rate between ZnS and chlorine. The reaction rate of NiS and PbS lies considerably below that of ZnS. The conversion rate of both pure Fe 2 O 3 and Fe 2 O 3 containing NaCl or CaCl2 when reacting with SO2-O2, mixtures with and without SO3 portions was measured at temperatures of 500", 550°, and 600°C. The weight increase of pressings was determined by means of a spiral balanceg and the reaction rate calculated therefrom according to Eqs. [ll to [31 and [5] to [7]. The prepared samples were suspended on a platinum filament in a vertically mounted tube of mullite (ID 4 cm, length 110 cm) which could be heated by a resistance tube furnace. The platinum filament was tied to the lower end of the spiral balance. A supremax glass tube (length 70 cm) was mounted gas-tight on top of the reaction tube. The unit was sealed up at its top by a ground-in stopper which was holding the spiral balance with the sample. The spiral balance therefore hung outside the high-temperature region of the furnace. Fig. 2 shows the experimental arrangement schematically. While lowering the sample into the reaction tube pure nitrogen was flowing through the reaction zone providing a protective atmosphere. After the sample had reached the reaction temperature within approximately 1 min, the protective gas was replaced by the sulfur dioxide-oxygen reaction mixture. It took about 30 sec until the mixture filled the tube homogeneously. A Ni/NiCr thermocouple placed in the center of the furnace where the sample hung during the measure-

Jan 1, 1968

By Alexander May

In its role to provide technology to prevent or limit adverse environmental impacts associated with mining or minerals processing, the Bureau of Mines has conducted research at its Tuscaloosa Research Center to asess the environmental impacts of phosphogypsum produced by the Florida phosphate industry. Over the years, stockpiles containing 335 million tons of phosphogypsun have accumulated and the industry continues to generate an additional 33 million tons a year. Samples from approximately 1,000 feet of drill core, obtained from nine stockpiles were characterized using chemical, X-ray diffraction, emission spectrographic, radiological, and physical means. The data developed indicated that phosphogypsum is not a corrosive or toxic hazardous waste as defined by Environmental Protection Agency criteria. Radium concentration averaged 21 picocuries per gram and its content was inversely related to particle sizes. Thirty-nine elements were detected in phosphogypsum; concentrations of these elements did not vary with depth within the stockpiles.

Jan 1, 1982

By Seung-Kyu Son

This study was investigated about physico-chemical parameter such as water temperature, salinity, inorganic nutrients and total organic carbon (TOC). CTD (Model: Sea-Bird 911 Plus) castings were carried out on two transects in the northeast equatorial Pacific Ocean. As a part of the Korea Deep-sea Environment Study (KODES), inorganic nutrients and TOC were determined at 41 stations located from 131° to 136°W along 10.5°N and from 17° to 5°N along 131.5°W (Fig. 1). We particularly chose KODES Long-term Monitoring Station (St. KOMO) to observe for the annually environmental baseline study in the contract area. [ ]

Jan 1, 2005

By Boland J

Prediction of rock cuttability by various excavation machines such as tunnel boring machines, road headers, rippers, picks, roller disc cutters, excavators, etc is of major concern to both civil and mining engineers and rock mechanics. In principle, the design of a rock cutting tool is based on achieving maximum excavation with minimum input energy, minimum applied force, minimum equipment weight and volume and, more importantly, minimum tool wear. When a rock material is indented by the force of a cutting tool and then unloaded several material zones form underneath and around the tool. As the tool moves into the rock the volume of its associated rock cavity (ie volume of displaced rock) expands and depending on the indenter's shape various phenomena may occur. Immediately beneath the tool a small zone in which the stress state is more or less hydrostatic, is formed which is underlain by an inelastic, or damaged, material zone. Both size and shape of this damaged zone control the magnitude of the indentation force and the chip formation mechanism during unloading. The rock is unable to store the whole strain energy induced by the tool and consequently the extra energy is expended either in forming new fracture surfaces and/or in plastic deformation in the damaged zone. Therefore, it is not surprising to see that both perfect-elastic and rigid-plastic constitutive models are not generally suitable for modelling indentation of rocks. In contrast elastoplastic constitutive models are more appropriate as they can include both elastic and plastic deformations (Kral et al, 1993). Elastic solutions for several half-space indentation problems can be found in most text books on elasticity and in particular in Timoshenko and Goodier (1951), Sneddon, (1951), Poulos and Davis (1974) and Johnson (1985a). If a failure criterion, eg the Mohr-Coulomb failure criterion, is applied to delimit elastic solutions for indentation problems, a lower bound limit of the applied indentation force (for a given indentation depth) can be estimated. It may be noted that elastic analyses, without any delimiting failure criteria, normally overestimate the indentation force. Plastic solutions for a few indentation problems may be found in Hill (1950), Johnson, (1985a) and Alehossein et al (1992). When analysing the behaviour of indented rocks the choice of an appropriate constitutive model describing effectively the behaviour of the rock at various stages and phases during indentation is a challenging issue. Several questions need to be answered before starting an effective analysis. The first question is of course: Which one of these is more appropriate for modelling zones underneath and around a cutter, elasticity or plasticity theory, continuum damage mechanics or fracture mechanics, and what is the bridging link between these various theories? Which mode is more dominant in fracturing rock, tensile or shear mode? What governs the mechanism of chip formation? What is the function, shape and the behaviour of the pulverised zone that forms just underneath a cutter? Is the hydrostatic stress state assumption reasonable for this zone? How does the rock change during the absorption and dissipation of the input energy and how does the indentation energy vary with rock type and depth of penetration? How can we model the damaged zone under the indenter? Furthermore does a plastic material form beneath the pulverised zone? When and how do radial and ring cracks form around and under an indenter?

Jan 1, 1995

By M. J. Marcinkowski, A. Szirmae, R. M. Fisher

Room -temperature hardness measurements obtained from single and polycrystalline samples of a 47.8 at, pet Cr-Fe alloy which were aged for various times al 500°C show a two-fold increase over that of the unaged alloy after annealing for 1000 hr. A detailed examination of the deformation markings in the neighborhood of the hardness imbressions reveals that twinning becomes an increasingly more important mode of deformation as aging proceeds. this observation is shown to be inconsistent with the Proposals that the transformation is eve of order-disorder On the other hand, the results are in agreement with previous observations of Fisher et al. of a coherent chromium-rich precipitate which forms in an iron-rich matrix as a result of a miscibility gap in this alloy system as proposed by Williams . Using the coherent precipitate hypotlzesis as a model, a detailed analysis of the various possible strengthening contributions to both the slip mid twinning stresses is made. In the case of' slip, lattice friction within the chromium-rich phase and the chemical energy associated with the interface between the two phases contribute about 60pet to the total strength. The contributions from coherency strains and modulus differences are thought to contribute the remaining 40 pet of the strength but are difficult to evaluate because of uncertainties regarding the flexibility of the dislocation line. All of the factors have nearly the same or else a smaller effect on the twinning stress in the aged alloy. Twinning is never observed in the unaged alloy because the twinning stress is much higher- than that for slip. With increased aging times, the various contributions to the total stress for both twinning and slip increase, but most of those for slip increase much more rapidly, so that, in the fully aged alloy, it surpasses the stress for twin propagation. When a twin is nucleated by the chance occurrence of an internal stress concentration during a test, the subsequent twin burst results in a low hardness reading. FeRNTIC Fe-Cr alloys from about 15 to 80 at. pet Cr content show considerable change in properties such as hardness, electrical resistivity, saturation magnetization, and so forth, after aging in the vicinity of 500°C.* The most marked change is a large increase in hardness accompanied by a sharp decrease in ductility, so the phenomenon has often been referred to as the 475°C (885°F) em-brittlement problem. Changes in microstructure are rather subtle and most investigators have not been able to observe any X-ray diffraction or metal-lographic changes during aging. There is little doubt that the phenomenon is inherent to the Fe-Cr binary system and is not directly related to the formation of a phase. Two distinct schools of thought have developed during the past decade concerning this problem. Masumoto, Saito, and sugiharal have concluded, from their own specific-heat measurements, that atomic ordering occurs in this temperature range. Pomey and Bastien2 have also attributed the changes in physical properties with aging in the neighborhood of 500°C to atomic ordering. In addition, Takeda and Nagai3 claimed to have found X-ray verification for superlattices corresponding to the compositions FesCr, FeCr, and FeCr3. However, all known attempts to observe superlattices in Fe-Cr alloys using neutron diffraction, which should be much more sensitive, have been unsuccessful. These have been reported by Shull et al.4 for 25 at. pet Cr, williams5 for 75 at. pet Cr, and Tisinai and samans6 for a 28.5 at. pet Cr. steel. The second and more prevalent opinion ascribes the 475°C embrittlement phenomenon to the formation of a coherent precipitate due to the occurrence of a miscibility gap in the Fe-Cr system below about 550°C. This latter concept was first indicated by the results of Fisher, Dulis, and Carroll,7 who were able to extract fine particles about 200Å in diameter from samples of 28.5 at. pet Cr steels aged from 1 to 3 years at 475°C. The extracted material was found to be nonmagnetic, to have a bee structure with a lattice parameter between that of iron and chromium, and to contain about 80 at. pet Cr. Williams and paxton8 and williams5 confirmed these results and first explicitly proposed the existence of a miscibility gap below the a region in the equilibrium diagram. Alloys aged within this gap

Jan 1, 1964

Automation Defined ?Using self-operating equipment to reduce human exposure to the mining environment and routine or repetitive work.?-Atlas Copco Terminology: ?Manual Operation ?A vehicle being operated by a person ?in the cab?. ?Radio Remote Control (RRC) ?A vehicle being physically operated by a person through a Line Of Sight (LOS) or Video-Remote equipment. ?Tele-Remote Control ?A vehicle being physically operated by a person at an operator station which is not necessarily located near the vehicle?s working area. ?Autonomous Operation ?A vehicle under self control with the possibility of human supervision and override.

Oct 1, 2010

By J. C. Swartz

Measurements of the effect of precipitation stresses on the solubility of cementite (Fe3C) precipitates in a iron are reported. Solubilities were determined from measurements of the Snoek relaxation due to interstitial carbon after quenching from various equilibrium treatments. Stress-free precipitates were obtained by a spheroidizing treatment of vacuum-melted Fe 0.06 wt pet C. Subsequent equilibration treatments were designed to suppress nucleation of other precipitates. The results for stress-free cementite give a heat of solution of 14.8 i 0.2 keal per mole and an entropy change of 1.1 i 0.2 eu in the temperature range 400" to 715°C. Comparison with previous data indicates that the heat of solution increases about 6 keal per mole as temperature increases from 700" to 1000°C. Data on self-stressed cementite in quench-aged specimens of Fe 0.013 wt pet C indicate 1) an apparent heat of solution of 12.1 i 0.4 keal per mole in the range 280" to 690°C, 2) a strain energy of- 1.1 keal per mole Fe3C accompanying precipitation at 280°C, and 3') a gradual decrease in the strain energy of precipitation with increasing equilibration temperature. In com-parison with 2 and 3 the strain energy calculated for an isotropic model is 1.7 keal per mole Fe3C. The lower values obtained from the experiment indicated substantial stress velaxation by dislocation motion. WHEN a supersaturated solution of carbon in a iron is aged at temperatures in the range 200o to 700oC, the carbon clusters by interstitial diffusion and forms cementite (Fe3C) precipitate particles. Unstressed cementite has a volume per iron atom 9 pet higher than that of a iron;' hence, cementite precipitate particles are usually under pressure from the iron matrix. The pressure would tend to increase the solubility of cementite in iron.' This report describes anelastic measurements of the solubilities of self-stressed and stress-free cementite in a iron. Previous determinations of the cementite solubility are summarized in Table I. The method of cementite formation for each reference was studied to ascertain the state of stress of the cementite. The results judged to be for stress-free and stressed cementite are distinguished in the table. In the next section an estimate of the stress effect is obtained which is clearly too small to account for the large difference between the previous results in parts A and B of the table. THEORETICAL Let AGO be the standard free-energy change of the reaction Fe3C (eem.) = 3Fe (a) + C (in a) [1] in the absence of stresses. Since cementite precipitates appear to be rather pure10 and the carbon is so dilute in the iron,8 the cementite and iron of Eq. [ I] for the stress-free case have essentially unit activities and the activity of carbon equals its atom fraction xoC Then the stress-free equilibrium is expressed by RT In XoC = -?GO 121 To first approximation the change in the chemical potential of carbon due to the precipitation stresses equals the elastic strain energy W accompanying precipitation of a mole of cementite.2 Hence, in the presence of the precipitation stresses the equilibrium is described by RT In x sq = -?G° + W [3] where xsC is the mole fraction of dissolved carbon in the stressed case. An approximate value of W can be obtained from analysis of the inclusion problem in elasticity theory. The inclusion is a small portion of the matrix phase which has suffered a transformation while still imbedded in the matrix. In the absence of the constraint of the matrix the transformation would be equivalent to a uniform dilational strain eT. Both the matrix (a) phase and inclusion (0) phase are assumed to be homogeneous, isotropic materials. When the a and 0 phases have the same elastic moduli, which is approximately true for iron and cementite,11 the total strain energy per mole ß is12 2µVß(eT)2(3 +4 µx)-I [4]

Jan 1, 1968

This paper reviews the development and operation of a small underground tin mine in NE Tasmania. Tin mineralisation was discovered in the Lottah area in the 1880's with early alluvial and eluvial workings leading to the development of large low grade open pit operations. Apart from short lived activities operations ceased in 1915. Intensive exploration in 1978-81 outlined substantial tonnages of low grade tin mineralisation (0.2% Sn) of open pit material. An underground ore body was also located (800 000 tonnes 0.6% Sn). Spectrum Resources Australia Pty Limited acquired a 98 percent interest in the property in 1988. Mine and mill development began in early 1989 based on an underground mine utilising trackless mining using room and pillar with fill stoping. The milling circuit involves primary jaw crushing, Barmac secondary crushing to lmm, Mogensen and DSM screens with jigs and tables to make a wet concentrate. Final tin concentrates are produced by high tension and magnetic separation. Planned production rates are 500 t/day with a mine life of 6-7 years.

Jan 1, 1990

By Frank F. Aplan

Introduction Heavy media separation (HMS), also called dense media or float¬sink separation, is one of the newer forms of gravity concentration. Though the concept can be traced to the last century, the process has enjoyed its major growth since 1940. Heavy liquid separation is a mutation. The heavy media process is used extensively to clean coal and for the concentration of a wide variety of ores such as those of iron, lead-zinc, chrome, manganese, tin, tungsten, fluorspar, magnesite, sylvite, garnet, diamonds, gravel, etc. It may be used where ever a significant density difference occurs between two minerals, and commercial separations are typically made in the range of 1.3 to 3.8 sp gr. The particle size treated ranges downward from 6-8 in. top size. Particles greater than about 1/16-in. (10 mesh) may be treated in a "static" bath, though for reasons of separation efficiency, + 1/2 -in- feed is usually preferred. For particles less than this size, separation in a heavy media cyclone is generally used. The flowsheet of a typical heavy media process, in this case one using a ferrous medium, is shown in Fig. I. In essence, the process consists of: (1) preparation of the feed usually by wet screening to remove undesired fines, (2) heavy medium separation, and (3) removal and recovery of the medium from the separated products. Many muta¬tions of the basic scheme are possible and numerous options are possi¬ble. HMS offers the following potential advantages:12 1) Ability to make sharp separations. 2) Ability to change the specific gravity of separation quickly to meet changing conditions. 3) Ability to remove products continuously. 4) Ability to treat a broad size range of products. 5) Ease of start-up and shutdown without loss of separating efficiency. 6) Relatively low medium cost and low media losses. 7) Low operating and maintenance costs. 8) High capacity with the use of relatively little floor space. 9) Relatively low capital investment per ton of capacity. The process may be used to produce a finished concentrate, two finished concentrates, or a concentrate and a middling of differing quality, or a preconcentrate by rejection of unwanted gangue. It is an ideal method for the reprocessing of coarse waste dumps. The greatest use for the process lies in coal cleaning and in the preconcentration of ores. The relatively inexpensive heavy media process may be used advantageously to reject large quantities of coarsely crushed gangue. When used in this way, the process will allow: (1) the use of lower cost but less selective mining methods with the "overbreak" material being removed at the front end of the concentrator or preparation plant; (2) a substantial reduction in the quantity of ore that must be finely ground for subsequent mineral liberation and separa¬tion. Since comminution is often the single most expensive step in beneficiation, it is desirable to eliminate as many essentially barren pieces of rock as possible before the grinding step, (3) a decrease in overall plant capital cost per ton of concentrate since the size of the plant from the dense medium step onward will be smaller. Several general references are available,12-18 though much of the technical data on the process is widely scattered in the general litera¬ture. Heavy Liquid Separation Organic Liquids Given sufficient settling time, it is possible to make a perfect separa¬tion between two particles of differing density by placing them in a liquid whose density is intermediate between the two. This means of achieving a perfect separation has proven to be elusive because of problems in feed preparation, particle settling rates, operational considerations, and economic constraints. There are a wide variety of heavy liquids that could be used, most of them halogenated hydrocarbons, and a few typical examples are given in Table 4. These liquids are most commonly used in ore dressing for the laboratory fractionation of ore particles on the basis of specific gravity. Laboratory Separations. Using liquids typified by those given in Table 4, separations are made to develop either the standard washability curves used to estimate the response of a given sample to gravity concentration or to prepare a partition curve to evaluate the effective¬ness of a given gravity separation process or piece of equipment. A typical washability curve is given in Fig. 2.19 Such curves are generated for raw coal, e.g., by treating either the whole or various size fractions of the sample in a series of heavy liquids and analyzing the various specific gravity fractions so produced. The procedure is relatively simple for coal samples because of the ready availability of a wide variety of relatively low cost heavy liquids in the density range 1.2¬-2.0. For ores the problem is much more complicated, because only a few high density liquids, all of rather high cost, are available. Parti¬tion curves are generated in the same manner by treating the separated products in the same liquids. Greater details on the procedures to be used in heavy liquid separa¬tions are to be found in the literature (for coal, Refs. 13, 14 and 19 and for ore, Refs. 20 and 21). For testing coal, calcium and zinc chloride solutions have been used extensively in the past, though today halogenated hydrocarbons (available under the trade name Certigrav) are the preferred media. The liquids shown in Table 4 may

Jan 1, 1985