By S. Jana, C. M. Wayman

The reverse transformation of bcc martensite to the fcc phase was studied in an Fe-33.95 wl pct Ni alloy by nzeans oj dilatometry, melallography, and electron microscopy. Upon "slozc" heating (-1°C per min) length cJmnge us temperature plots showed u gradual contracLion over the temperature range 200" to 280"C ,followed by a more abrupt contraction beginning a1 -280°C. Howet,ev, zchen the heating rate was increased -4°C per tnin, no gradual contraction was observed and only the abrupt contraction starting at -2BO"C was found. Thus on slower heating- the AS "temperature" for the subject alloy, unlike the MS temperature, is better defined as a range of temperatures. Both optical and transmissiorl electron microscope observations showed that some of the martensite plates exizibited a partial loss of transformation twins during reversal. The midvib region of the martensite plates disappeaved relatively early duirng the reversal. Metallographic observations slowed that the earliest detectable stage of the rezlerse tvansforrvration begins (axd Moues inulardly) at The Martensens i te - parent interface. At higher temperatirres, the. formation of martensitically reversed jcc plates within the bcc martensite plales was observed. It is concluded that the reverse transformation consists of a diffusion less process (martensitic); but this is ps-obably aided by a prior or simultaneous dijjusiorz-comltvolled process, at leasl in the case of slower heat-ing' experiments. ALTHOUGH numerous investigations have dealt with the parent-to-martensite ("forward") transformation (fcc — bcc) in Fe-Ni alloys, comparatively little is reported on the ("reverse7') martensite-to-parent transformation.'-4 Even though such reverse transformations have been studied in detail in some nonferrous systems, one of the difficulties of studying the reverse transformation in most ferrous mar-tensites is that the martensite decomposes by tempering during heating. However, carbonless Fe-Ni alloys do not exhibit this difficulty since the transformation in these alloys is completely reversible. The present investigation represents an attempt to shed more light on the nature and mechanism of the martensite-to-parent transformation. 1) EXPERIMENTAL PROCEDURE 1.1) Alloy Prepatation. Fe-Ni alloys of compositions near 34 wt pct Ni were prepared from zone-refined iron (99.994 wt pct Fe) and high-purity nickel (99.999 wt pct Ni) by induction melting in recrystallized alumina crucibles in an argon atmosphere, with prior vacuum evacuation to 10"3 mm Hg. The alloys were homogenized by induction stirring in the molten state for 5 min. After solidification, the alloys were further homogenized in evacuated quartz capsules for 96 hr at 1230°C. 1.2) Dilatometry. Slices of the ingot were hot-forged (750°C in air) into approximate rod form and these specimens were then hot-swaged (750°C in air) into long cylindrical rods 0.55 mm diam. From the rods, specimens about 1 in. long were cut. These were then vacuum-annealed for 24 hr at 1200°C, cooled to room temperature, and subsequently transformed to martensite in liquid nitrogen (whereby about 40 pct transformation was obtained). Dilatation measurements were made by observing length changes in a vacuum dilatometer with an externally mounted LVDT sensing element. 1. 3) Preparation of Electron Microscope Specimens. Slices of the ingots were cold-rolled (with intermediate vacuum anneals) to -0.020 in. Out of these rolled sheets, specimens (about 1 by 1 in.) were cut. These were then vacuum-annealed, transformed to martensite by cooling in liquid nitrogen, and subsequently heated from room temperature to various temperatures to effect either partial or complete reverse transformation. These specimens were then chemically polished to 0.002 in. in l:l HsOz (30 pct) and &PO4 (85 pct) solution, and thinned to electron transparency in an electrolyte consisting of 150 g CraOs, 750 ml glacial acetic acid, and 30 ml ~~0.~ Observations were made with a 100-kv Hitachi HU-11 electron microscope equipped with an HK-2A tilting device. 1.4) Optical Microscopy. Metallographic observations were made with a Leitz MM5 metallograph on the same 0.020-in. sheet specimens as were used for electron microscopy and on bulk specimens which were 0.2 in. or more on a side. The chemical thinning solution when cooled below 20°C also served as an etchant for this alloy. Observations of surface relief were made with a Zeiss interference microscope employing a Thallium light source of wavelength 0.54 p. Specimens for interference studies were prepared by two-stage polishing on Buehler vibromet polishers using 0.3 and 0.05 p alumina abrasives. 2) EXPERIMENTAL RESULTS 2.1) Comparison of the MS,AS, and Af Tempera-tures wTth Previous Re sults. The AS aLd Af tempera -tures of several Fe-Ni alloys were determined dila-tometrically. The MS temperatures of the same alloys were determined by continuously lowering the temperature using a mixture of isopentane and liquid nitrogen and observing the highest temperature at which a prepolished specimen showed surface upheavals. For the present the As temperature is defined as the temperature at which an abrupt decrease in length occurs in the dilatation plot. The Ms,As7 and A determinations in the present investigation and those of Kaufman

Jan 1, 1968

By Klaus-Peter M. Hanke

INTRODUCTION In early 1979 Jim Walter Resources, Inc. (JWR) of Brookwood, Alabama approached TMCI Construction, Inc (TMCI) to make a proposal on a program that involved the sinking of up to 10 ventilation shafts of approximately 6.7 m (22 ft) diameter and ranging in depth from 500 to 700 m (1650 to 2300 ft) for the JWR coal mines in Alabama. At this time TMCI was already constructing the first spiral underground bunker (capacity 2000 tons) in North America for the JWR organization at their No. 4 mine in Alabama. The TMCI proposal was based on the use of the mos modern large diameter shaft boring machine rather than sinking the shafts using the conventional drill blast-muck technique. The proposal was made based o: the experiences by the parent company, Thyssen Schachtbau, which has been using this type of machin in Germany for shaft boring since 1971. As a result of the TMCI proposal JWR issued a purchase order to TMCI for the construction of four 6.7 m (22 ft) diameter, concrete lined, unfurnished ventilation shafts ranging in depth from 500 to 700 (1650 to 2300 ft). An order was thus placed with WIRTH Machinen- and Bohrgeraete Fabrik GmbH, in Germany for the manufacture of a model 650/850 E/Sch "Schachtbohrmaschine" (Vertical Shaft Borer = V-mole which arrived on site in Alabama in early 1981. The first V-mole GSB 450/500 was introduced in Germany in 1971 and was capable of enlarging in one step a pre-drilled 1.2 m (4 ft) pilot hole to 4.5 - 5.0 m (14.7 - 16.4 ft). This machine has sunk 9 staple shafts and deepened one surface shaft for a total of 2360 m (7740 ft) of shafts. On the last shaft boring operation in 1978 the machine was converted as an experiment to drill without a pilot hol using a hydraulic pumping system to remove the cutting debris. A second generation machine, the SB VI 500/650, was introduced in 1977 for enlarging the pilot hole to a range of 5.0 - 6.5 m (16.4 - 21.3 ft) diameter. This machine is still in operation and has already drilled well over 2000 m (6500 ft) of shaft. The third generation of V-mole, the SB VII 650/85( for diameters from 6.5 to 8.5 m (21.3 to 27.9 ft) was: commissioned in May 1980 and has been used for two surface shaft deepenings totalling 606 m (1990 ft) with another scheduled for 1982. The main advantages favouring the use of such V-moles were identified as: 1) A reduction in manpower to the crew required in a conventional shaft sinking operation. 2) A considerable reduction in time to complete a shaft compared to conventional techniques. 3) The use of the V-mole eliminates many of the hazards encountered in conventional sinking. Based on the successful performance of the first three V-moles in Germany, Thyssen Schachtbau decided to employ this principle abroad. In 1980 a second machine of the third generation was built and is now operated by TMCI Construction, Inc. in Alabama. The first shaft was completed at the end of 1981 and this paper describes the method of operation including some unique aspects not attempted on prior V-mole operations and some of the statistics arising out of the experiences during the first shaft boring operation. THE NO. 7 MINE FAN SHAFT SITE Jim Walter Resources, Inc. was formed in 1970 to exploit the coal field in Alabama on the southern tip of the Appalachian coal field. The coal reserves amount to around 650 million tons of mainly good quality coking coal of which about 350 million tons are to be extracted over the next 30 years. Shaft sinking and preparatory work began in 1972, and at present 6 mines are producing around 5.4 million t.p.a. Annual production is to expand to 10 million t.p.a. as soon as possible, and the ventilation shafts to be sunk by TMCI play a vital role towards attaining this goal. The first shaft site is located at the No.7 mine, near Brookwood, Alabama. The actual location of the shaft relative to the production shafts is shown on the mine plan (Fig. 1), which also shows the room-and-pillar extraction system used at present. The mine plan further shows the conveyor route used for the muck removal. The geological survey showed that the strata consisted of horizontal layers of mainly sandstone, sandy shale and shale interspersed with several coal seams. The seam being extracted at the No. 7 mine is a combined seam made up of the Blue Creek and Mary Lee seams at a depth of 513 m (1682 ft) and having an average seam thickness of about 2 m (6 ft). At the beginning of September 1980 the surface site preparation and pre-grouting work was completed by JWR, and TMCI was able to commence with Stage I of the shaft sinking program - the drilling of the pilot hole.

Jan 1, 1982

By T. H. Alden

Using alternating tension-compression straining, the hardening of magnesium oxide single crystals was studied up to large stresses and strains. At 0.25 pct plastic strain amplitude, the hardening curve is approximately linear with slope 25,000 psi from the shear yield stress, 7 to 8000 psi, to 35,000psi. Above this stress, the slope decreases. The strain hardening behavior of MgO is considered qualitatively similar to that of metal single crystals. The relatively high stress attainable by strain hardening is associated apparently with the high yield stress on the cross-slip system, (001) <110>. Cleavage fracture during testing is uncommon. It is argued that the centers of high internal stress at glide band intersections, at which cracks tend to nucleate, are dispersed by cyclic strain. Special features of the glide band structure produced by cyclic strain and revealed by dislocation etch pits, support this view. Strain hardened MgO has mechanical properties greatly superior to the as-received material: yield stress, greater than 100,000 psi; elongation to fracture about 1 pct. A material is said to strain harden if the yield stress increases with an increment of plastic strain. This definition is usually applied for straining done in one direction, but is also applicable when the strain direction is periodically reversed, Fig. 1. For certain metal single crystals, data are available which permit a comparison of the hardening behavior for cyclic straining and for tension straining.&apos;-4 With certain qualifications, these data show that the same processes of hardening are operative in each type of test.5 Despite this fact, the importance of the technique is not immediately evident, although tension-compression studies of the common metals appear to suggest some deficiencies in theories of strain hardening developed exclusively on the basis of tensile tests. However, a recent observation suggests that the cyclic straining method may be very useful for studying semibrittle crystals in which large plastic strains are not accessible in unidirectional testing. The observation is that zinc crystals, when strained in tension-compression at -52°C, do not fail by cleavage at low stress (-500 psi)6 as they do in tension, but harden to a limiting stress of more than 5000 psi over a total plastic strain of about 600 pct.2 An important characteristic of the behavior of zinc crystals is the high stress, relative to the yield stress, attainable by strain hardening. By comparison, the hardening of aluminum single crystals tested by an identical technique saturates at 1100 psi. This difference is best explained by the cross-slip hypothesis of dynamic recovery.7,8 In zinc, cross slip is difficult because of the high yield stress for glide on planes other than the basal plane in the < 1120 > zone. The present work was undertaken in order to test whether these methods and ideas are applicable to other materials. Magnesium oxide single crystals, in common with most crystals of the rock-salt structure, deform plastically but fail by cleavage after a small strain when tested in tension. It was hoped that larger strains would be attained using tension-compression. There is, in addition, evidence 8a which shows that slip on the probable cross system, (001) < 110>, is difficult in magnesium oxide; it may therefore be possible to attain high stresses by strain hardening. 1) EXPERIMENTAL PROCEDURE Experimental methods used in this study were based in part on techniques reported in papers of Stokes, Johnston, and Li.&apos; MgO blocks, purchased from Norton Co., were used without further annealing. Specimens were cleaved to dimensions approximately 0.125 in. sq and 1 in. in length. The gage section, formed by chemical polishing, was sprinkled with 280 mesh silicon carbide particles in order to introduce fresh dislocations. The crystals were then cemented into cylindrical aluminum adapters and clamped in an Instron testing machine. One of two alternating straining programs was used. In the first, total cross-head travel was established and increased in steps after various numbers of cycles. In the second, a capacitance gage was used to directly measure the elongation of the specimen and the crosshead was controlled so as to keep the plastic strain amplitude constant. The straining was always symmetrical with respect to the initial, zero strain condition. While both procedures produce strain hardening, only the latter permits a measure of the total plastic strain so that hardening curves may be drawn. Constant plastic strain amplitude tests were done

Jan 1, 1963

By Nicholas J. Grant, John S. Benjamin

A series of composite alloys containing a high volume of NiAl, Ni3Ah or CoAl, bonded with 0 to 40 vol pct of a ductile metal phase, were prepared by powder blending and hot extrusion. The binder metals were of four types: pure nickel or cobalt, near saturated solid solutions of aluminum in nickel and cobalt, type 316 stainless steel, and niobium. Sound extrusions were obtained in almost all instances. Studied or measured were the following: interaction between the alunzinides and the binders, room-temperature modulus of rupture values, 1500° and 1800°F stress rupture properties, hardness, structure, and oxidation resistance. Stable structures can be produced for 1800°F exposure, with interesting high-temperature strength and good high-temperature ductility. Oxidation resistance was excellent. A large number of experimental investigations have been made of the role of structure on the properties of cermets and composite materials. Gurland,1 Kreimer et al.,2 and Gurland and Bardzil3 have indicated the preferred particle size in carbide base cermets to be about 1 µ, with a hard phase content of 60 to 80 vol pct. The optimum ductile binder thickness was noted to be 0.3 to 0.6 µ.1 Complete separation of the hard phase particles by the binder is important in reducing the severity of brittle fracture.&apos; The purpose of the present study was to produce structures comparable to the conventional cermets, using a series of relatively close-packed intermetal-lic compounds rather than carbides as the refractory hard phase, and to study the effects of binder content and composition on both high- and low-temperature properties. The selected intermetallic compounds were particularly of interest because of the potential they offered in yielding room-temperature ductility. The highly symmetrical structures are known to possess high-temperature ductility and room-temperature toughness. Based on a ductile binder, the alloys were prepared by the powder-metallurgy route to avoid melting and subsequent alloying of the matrix, and were extruded at relatively low temperatures. It was expected that the composite alloy would retain useful ductility. In contrast, infiltration and high-temperature sintering led to alloying of the matrix and to decreased ductility. The systems Ni-A1 and Co-A1 were selected for this study. In the Ni-A1 system the compounds NiA1, having an ordered bcc B2 structure, and Ni3Al(?1), having an ordered fcc L12 structure, were chosen. In the system Co-A1 the intermetallic compound CoAl with an ordered bcc B2 structure was used. ALLOY PREPARATION The intermetallic compounds, see Table I, were prepared by using master alloys of Ni-A1 and CO-A1, with additions of either cobalt or nickel to achieve the desired compositions. The master alloy in crushed, homogenized form, was melted with pure nickel or cobalt in an inert atmosphere, cold copper crucible, nonconsumable tungsten arc furnace. The resultant intermetallic compounds were homogenized at 2192°C in argon, crushed, and dry ball-milled in a stainless mill to -100 and -325 mesh for the Ni-A1 compounds and to -325 mesh for the CoAl compound. Finer fractions were separated for some of the composite alloys. Several ductile binders were utilized. These included Inco B nickel, 5µ ; pure cobalt, 5 µ, from Sher-ritt Gordon Mines, Ltd.; fine (-325 mesh) niobium hydride powder; fine (15 µ) type 316 stainless-steel powder; and near-saturated Ni-A1 and Co-A1 solid-solution alloys, also in fine powder form. The niobium hydride was decomposed above about 700°C in processing of the compacts in vacuum to produce niobium powder. The Ni-7.1 pct A1 and the Co-5.3 pct A1 solid-solution alloys were prepared from pure nickel or cobalt and pure aluminum by nonconsumable tungsten arc melting under an inert atmosphere. The ingots were homogenized, lathe-turned to fine chips, and dry ball-milled in air to -325 mesh powder. These solid-solution alloys are designated NiSS and CoSS; see Table I. Subsequently the hard and ductile phases were dry ball-milled as a blend. Experiments clearly established the need to coat the hard particles with the ductile binder to optimize subsequent hot compaction by extrusion. Ordinary dry mixing usually resulted in nonhomogeneous alloys which were quite brittle. Conventional cermets are consolidated by liquid phase sinteiing or infiltration, which resulis in undesirable and uncontrolled alloying of the binder phase. For this study, a loose (unsintered) powder-extrusion process was emploved, minimizing reactions between binder and hard particle, thereby permitting much greater control of composition and structure. The constituent powders were first mixed in the desired

Jan 1, 1967

By D. R. Uhlmann, T. P. Seward, K. A. Jackson, J. D. Hunt

microscopic ohservations on alloys of organic trzaterials show that dendrite arms can melt off under normal conditiorzs of growth. This occurs because of the interactiorz of&apos; heat and matter fluxes during dendritic growth. The re melting occurs where the den-drite arms are joined onto the main deizclrite sterrz. Many detached crystals can be produced in this fashion. It is postulated that this remelting phenornenon occurs in metal alloys, giving rise to the equi-axed region in castings. Experiments peyformed orr castings of transparent materials support remelting as a primary source of detached crystals. Ob~ervations an equiaxed tones in metal castings are discussed in terms of this and other mechanisms. It is concluded that the partial remelting of dendrites is on important mechanisnl for producing the equiaxed regions in castings. THE freezing of a casting can be divided into three regions: a chill zone formed near the mold wall, a columnar region, and a third region, at the center of the casting, which is called the equiaxed zone. The origin of the grains that comprise the equiaxed region is the subject of this paper. We will first outline the mechanisms which have been proposed to account for the origin of the equiaxed region and discuss some recent experiments which cannot be explained by these theories. We will then present some microscopic observations of dendritic growth which have led us to conclude that the equiaxed zone in castings can arise from partial remelting of dendrites. This proposal is supported by observations on transparent castings. Finally, we will discuss several observations on metal castings which could not be explained previously, and which can be accounted for by the present proposal. Previous Mechanisms. Winegard and Chalmers3 pointed out that the molten central region of an ingot could be constitutionally supercooled, because of the solute layer at the growing interface. In this supercooled region, nucleation on particles could occur, giving rise to the equiaxed crystals. Another mechanism has also been suggested,4y5 that the nuclei originate in the chill zone then float or are carried by convection to the center of the casting, where they grow to produce equiaxed crystals. In this case, all the crystals nucleate immediately on casting, so this mechanism will be termed "big-bang" nucleation. Walker&apos;s Experiments. J. L. Walker has made observations on the solidification of nickel and Ni-Cu alloys which cannot be accounted for by either of the above mechanisms. In studying the grain size resulting from freezing of nickel at various undercoolings, walker6 found that at large undercoolings the grain size was small, due to mechanical nucleation, as discussed by walker7 and Horvay.&apos; At small undercoolings, the grain size was large, and the growth dendritic. In Ni-Cu alloys, however, for initial undercoolings starting from just below the melting point and extending for a hundred or so degrees of undercooling, fine grains were also observed. Samples were undercooled 200 Centigrade degrees without nucleating, and were then heated 130 Centigrade degrees so that the undercooling was 70 Centigrade degrees, and nucleated. The samples had a small grain size, indicating multiple nucleation. There were no heterogeneous nuclei in the liquid which could operate at the temperature of growth. Constitutional supercooling could not have been greater than the supercooling of the initial melt, since the temperature rose as the freezing continued. walker -as also shown that a Ni-Cu alloy which can be undercooled to below its solidus will produce typical columnar and equiaxed regions when cast into a cold mold. This alloy could not reach a temperature below its solidus by constitutional supercooling. It could not, therefore, have nucleated heterogeneously. Neither the big-bang mechanism nor the Winegard-Chalmers mechanism can account for the fine grain

Jan 1, 1967

By J. L. Lehman, J. D. Sudbury, J. E. Landers, W. D. Greathouse

A full scale field experiment on cathodic protection of casing answers questions concerning (1) the proper criteria for determining current requirments, (2) the amount of protection provided by different currents, and (3) the transfer of current at the base of the surface pipe. Three dry holes in the Trico pool in Rooks County, Kans., were selected for cathodic protection tests. The three holes were in an area where casing failures opposite the Dakota water sand often accur in less than a year. Examination of the electric togs showed the wells to be similar to other wells in the field where casing in four of seven producing wells has failed. The three holes were cleaned out and cased with 75 joints of new 51/2-in. 14-tb J-55. Each joint was visually inspected and marked before it as run. The casing was bull plugged and floated in the hole 50 that the inside might remain dry and free of excessive attack. Also, if a leak occurred, a pressure increase could be observed on gawge at the surface. Extensive testing was done, including potential profiles, log current-potentid curves and electrode measurements from both surface and downhole connections. Based on these data, a current of 12 amps was applied to one well and 4 amps to mother. The third well was left to corrode. During the two-year period when the casing was in the ground, [he applied current was checked weekly, and reference electrode measurements were made about every two months. Three sets of casing potential profi1e.c were run. When the three strings were pulled, each joint was examined for type of scale formed, presence of sulfate-reducing bacteria, extent of corrosion nttnck and pit depth. Since the pipe was new when run, quantitative determination of the protection provided by current was possible. This is the first concrete field evidence to help resolve the many arguments about the proper method for selecting adequate current for cathodic protection of oilwell (-using. INTRODUCTION A casing string is run when a well is drilled. This pipe is supposed to protect this valuable "hole in the ground" for the life of the well. Often the casing does not last the life of the well; it is with these casing failures that this work is concerned. The cost of repairing a casing failure varies from field to field—from as much as a $30,000 per leak average in California to $5,000 per leak in Kansas. Additional costs other than actual repairs are also important. These include formation damage, lost production, etc. Casing damage caused by internal corrosion is important in some areas. Treatment normally consists of flushing inhibitor down the annulus, but further research is being done on control measures. The test described in this paper is concerned only with external corrosion. The problem of casing failure from external attack has appeared in several areas including western Kansas, California, Montana, Wyoming, Texas, Arkansas and Mississippi. Cathodic protection is currently being used in an attempt to control external corrosion. From reports in the NACE there are thousands of wells currently under cathodic protection. The quantity of current being applied ranges from 27 amps on some deep California wells to a few tenths of an amp being supplied from magnesium anodes on wells in Texas and Kansas. Considerable field and laboratory effort1,9,5,6 was exented on the problem of cathodic prctection of casing, and it became fairly obvious that this method could be used to protect wells. Early workers showed that current applied to a well distributed itself over the length of the casing and was not concentrated on the upper few hundred feet. Basic cathodic protection theory had shown that corrosion attack could be stopped by applying sufficient current. The problem resolved itself, then, into one of trying to decide just how much current was necessary. Various criteria were utilized in installing the many existing cathodic protection installations. These methods included the following. 1. Applying sufficient current to remove the anodic slope as shown by the potential profile." 7. Applying enough current to maintain all areas of the casing at a pipe-to-soil potential of .85 v.&apos; 3. Applying the current indicated by a log current-potential (or E log I) curve." 4. Supplying the current necessary to shift the pipe to-soil potential .3 v." 5. Applying 2 or 3 milliamps of current per sq ft of casing."

By C. E. Tsoutrelis

A new method for determining rock drillability in diamond drilling is discussed; the method takes into consideration both penetration rate and bit wear. The method is based on drilling a rock specimen under controlled laboratory conditions using a model bit. The technique used for determining the experimental variables is extremely simple, quick, and reliable. Drillability is then determined by the mathematics of drilling. In considering the different factors that affect diamond drilling performance, the nature of the rock to be drilled is of outmost importance since it affects significantly the drilling costs and such other variables as bit type and design, drilling thrust, and bit rotary speed. Many attempts have been made to study this effect by correlating actual drilling performances either to certain physical properties of the rock being drilled1-? or to test drilling data obtained under laboratory conditions.7-13 These attempts were aimed at providing a reliable method of predicting by simple means the expected rock behavior in actual drilling, thus giving the engineer a tool to use in estimating drilling performances and costs in different types of rock. The purpose of this paper is to describe such a method by which rock drillability (a term used in the technical literature to describe rock behavior in drilling) could be determined in diamond drilling. It is believed that the proposed simple and reliable method will cover the need of the mining industry for a workable method of measuring the drillability of rocks. It should be emphasized, however, that since drill-ability depends on the physical properties of rock and each drilling process (diamond, percussive, rotary) is affected by different or partly different rock properties,14-l6 the proposed method of determining rock drillability cannot be extended to the other drilling processes. The results presented in this paper form part of an extensive three-year research program carried out by the author in the laboratories of the Greek Institute of Geology and Subsurface Research. During this period the effects of the physical properties of rocks and of such operational variables as drilling thrust and bit rotary speed in diamond drilling were investigated in detail. DRILLABILITY CONCEPT The literature is not devoid of drillability studies. While there are a number of investigators1,3,5-7,9-0,12-13,17 who have attempted to establish by direct methods (i.e., drilling tests under laboratory conditions) or indirect (i.e., through a physical property of rock) an index from which the drilling performance in a given rock may be estimated, very few6-7,9,12, of the proposed methods seem to be of much practical value to the diamond drilling engineer and none to date has been universally accepted. Commenting on the proposed methods for assessing rock drillability, Fish14 remarks that "for a measure of drillability to be accepted it is essential that penetration rate at a given thrust and bit life are elucidated as otherwise the method is of little value." This statement should be examined in more detail by making use of the penetration rate-drilling time diagram obtained in drilling a rock under constant operational conditions. Furthermore, the merits of using this diagram to describe rock drillability will be pointed out. At the same time reference will be made to this diagram when discussing some previously proposed methods. Fig. 1 illustrates such a diagram for three rocks,A, B, and C, which have been diamond drilled under identical conditions. It is assumed here that rocks A and B have the same initial penetration rate, i.e., VOA = Vog, but since rock B is more abrasive than A, rapid bit wear occurs and as a result the fall of its penetration rate with respect to time is more vigorous than in rock A. This is shown graphically by a steeper V = f(t) (0 curve in this rock than in rock A. Rock C has a lower initial penetration rate, due to higher strength properties16 but since it is not very abrasive, only a slight fall of its penetration rate occurs during drilling (in this category are some limestone and marbles with compressive strength above 1000 kg per sq cm). It follows from the foregoing considerations that the characteristic for each rock curve (I) is a function of (i), the penetration rate of the rock Vo recorded at the instant of commencing drilling, which determines the starting point of the curve (1) on the y-axis and (ii), the abrasive rock properties which determine the rate of fall of Vo with respect to time. Thus, curve (I) provides an actual picture of the rock behavior in drilling for given operational conditions, and it can be used with complete satisfaction to assess rock drillability. It can be seen clearly from Fig. I that proposed methods for assessing rock drillability by measuring the

Jan 1, 1970

By R. D. Burlingame, T. L. Joseph, Gust Bitsianes

DESPITE almost fifty years of commercial practice, the sintering of iron ore has received little fundamental study. Much of the theoretical work1-&apos;has dealt with the constitution of sinter produced under widely varying conditions. While these studies have broadened our knowledge of the changes that occur in the sintering zone and in the freshly formed sinter during the early stages of cooling, they provide little insight into the changes that precede the formation of sinter. These preliminary changes merit study as a part of the overall process. Hessle. working with beds of Swedish magnetite concentrates, was one of the first investigators to study the sintering process in its entirety. On the basis of temperatures observed at various levels of the bed during sintering, he postulated a number of distinct reaction zones to account for the chemical changes leading to the formation of sinter. A more direct method of attack is that of arresting the sintering zone after it has progressed part way through the bed. A study of a vertical cross section through such a quenched bed provides direct information on the changes taking place at various levels. This method was used by McBriar et al.&apos; to show that several well-defined zones of chemical change existed within beds that were typical of British sintering practice. The same general method of attack was developed independently in the present investigation to study partially sintered beds typical of American practice. Experimental Sintering Equipment The sintering operation was carried out on an experimental scale with the equipment shown in Fig. 1. The refractory-walled sintering chamber A was 11 in. deep and averaged 9 in. in diameter. Air was introduced through a tapered flow section B, which contained the orifice C for accurate metering of the incoming air. This section was located directly above the square ignition housing D, which in turn rested upon the sintering chamber A. The bed was ignited with burner E. The required suction for the operation was furnished by a fan F, which had an air capacity of 500 cfm (stp). Hot exhaust gases from the sintering chamber were cleaned in the dustcatcher G before entering the exhaust fan. In the study of partially sintered beds, it was essential to find some technique for removing the entire charge from the sintering pot without disarranging the unsintered bottom portion. This problem was finally solved by sintering the charge in a removable basket, which snugly fitted the sintering chamber. This basket was constructed of two thicknesses of window screen and was lined with a 3/16-in. layer of asbestos paper. The bottom of the basket consisted of two thicknesses of wire screen, which were fastened to the basket wall. For high fuel mixtures, additional insulation was provided by a somewhat thicker layer of asbestos cement. Preparation of Partially Sintered Mixtures The moist feed was carefully placed in the sintering basket, to prevent segregation of the particles, which varied widely in size and composition. A thermocouple was placed in the center of the basket with the hot junction halfway down, and the mixture was evenly distributed around it. During ignition and throughout the sintering of the upper half of the bed, the hot junction temperature increased very little. When the sintering zone reached the halfway point, as indicated by the sudden increase in the hot junction temperature, the charge was quenched. During quenching the suction was turned off and the orifice was tightly stoppered to prevent further influx of air. At the same time, nitrogen was admitted to the sintering chamber through the orifice tap. As soon as the nitrogen had displaced the air and products of combustion, the charge was removed from the sintering pot for immediate dissection. It is impossible to preserve the exact zone structure of the bed at the instant that combustion is arrested unless the downward transmission of heat is also immediately stopped. Fortunately, heat transfer is very slow in beds containing a stationary fluid, especially if the particle size is small. It follows that the minimum quantity of nitrogen should be used to displace the air and that static conditions be established as soon as possible. A very steep temperature gradient across the combustion zone for some time after the quench was evidence of in-

Jan 1, 1957

By N. N. Breyer

A specially built "hard" tensile machine with characteristics permitting the precise detertnination of the drop of the load at the yield point has been used to study the magnitude of the yield-point phenotnenon in prestrained martensitic 4340 steel. A new phenonzenon, the appearance of a secondary yield point, has been observed by holding the specimen at constant strain in the plastic region. Furthermore, it has been found that a series of yield-point drops could be introduced by successive constant strain holds in the plastic region. The isothermal kinetics of the development of the secondary yielding point lave been studied at four temperatures: 24° 0° -18°, and -79°C. From the results of the kinetic investigation, equations for the In a previous investigation1 it was shown that, contrary to generally held opinion, steels of medium carbon content, such as 4340, 4140, and 86B30, in the as-quenched martensitic condition, can be cold-drawn through a die with reductions in area of up to 10 pct without cracking. Tensile specimens of 4340 machined from bars quenched and prestrained in this manner exhibited tensile strengths of about 400,000 psi coupled with 30 pct reductions in area. In addition, it was found that each sample of such steels exhibited a yield point in the quenched, cold-drawn condition. Since these studies were conducted on a commercial hydraulic testing machine of a type which is not well-suited to detailed study of yield-point behavior, it was decided to study this phenomenon more thoroughly on a rigid straining machine. In this new investigation, use of such a "hard" machine not only allowed study of the magnitude of the yield-point drop but also revealed a new phenomenon—secondary yielding of the martensite introduced by stopping crosshead motion after plastic deformation of the sample had begun. The present paper is a report of these findings. MATERIALS AND PROCESSING The material used was a commercial 4340 steel of the composition shown below: 0.41 0.80 0.013 0.019 0.31 0.85 1.76 0.28 1 0.42 0.77 0.015 0.024 0.30 0.84 1.69 0.28 0.08 2 1 = Ladle analysis. 2 = Laboratory analysis. Bars of this steel were processed in the following way: 1) machined to predetermined diameters; 2) austenitized at 870°C for 1 1/2 hr; 3) oil-quenched; 4) cooled to -115°C for 1/2 hr; onset and increase in magnitude of the secondary yielding in this temperature region have been found to fit the relationship ?Ys = Atn where ?Ys is the magnitude of the secondary yield Point in psi, t is the time in seconds, and A and n are parameter characteris-tics of the material. Although the occurrence of the primary and secondary yield points could be rationalized qualitatively on the basis of stress-induced ordering of carbon atoms in the stress fields of dislocations, as postulated in an earlier paper, the kinetics of the secondary-yield-point development were interpreted to indicate that the ordering involves more than just single jumps of carbon atoms from high-energy to neighboring low-energy sites. 5) pickled and lime-coated; 6) drawn through a carbide die. The predetermined diameters were chosen so that drawing through the same die gave the various reductions desired. Tensile specimens of 0.252 in. diam with a 1 1/4 in. gage length were then prepared from the drawn bars and tested. In order to study the stress-strain behavior at the yield point in detail, a rigid tensile machine with a high spring constant was constructed. Columns of large cross section (relative to the specimen cross section) constituted the machine frame. A dc motor was used to drive a screw via a gear reducing train and a "crane" thrust bearing. In this relatively simple device small deformations could be observed un-blurred by the slow response and lower spring constant inherent in hydraulic machines.&apos; A strain-gage dynamometer permitted load changes as small as 8 lb to be read. RESULTS Tensile test samples machined from bars in the as-quenched condition with no subsequent drawing and samples from bars with 3.8 pct reduction after quenching gave stress-strain curves typified by those shown in Figs. I and 2. The time lapse between predrawing and tensile testing varied but usually ranged between 3 to 6 days at room temperature. The strain rate during testing was 0.003 in. per in. per min. The as-quenched curve is seen to have a broad serrated maximum whereas the stress on the specimen prestrained 3.8 pct rose linearly to point A, Fig. 2, fell abruptly to B, and then gradually to C. The abrupt drop to B was accompanied by evidence of incipient necking. The drop of the stress at the yield point in the prestrained samples (A to B in Fig. 2) changed with the percent prestrain, as illustrated on Fig. 3. Although the tensile strength increased continuously with the amount of previous cold drawing, the magnitude of the yield point drop first increased—up to about 6 pct prior reduction—and then decreased. Specimens from bars predrawn more than 8 pct broke in a brittle fashion in the elastic portion of the stress-strain curve.

Jan 1, 1967

By R. E. Ogilvie, A. R. Kaufmann, S. H. Gelles

The solid-solubility limits of iron in beryllium were determined between 850o and 1200oC by analysis of differential type multiphase diffusion couples, using an X-ray absorption technique. The maximum value of the solubility limit was found to be 0.92 ± 0.02 at. pct (5.46 wt pet) at the eutectic temperature 1225°C. The solubilities of nickel and beryllium were determined between 900°and 1200°C by the same technique and the maximum solubility was found to be 4.93 + 0.01 at. pct (25.2 wt pet) at the eutectoid temperature, 1065°C. A previously unreported high-temperature phase which decomposes eutectoidally at 1065 °C was found to exist in the beryllium-nickel system at a composition of approximately 8 at. pct Ni (36 wt pet) by diffision-couple analysis. The presence of this phase was confirmed by thermal analysis and metallo-graphic analysis of the structure resulting from the eutectoid decomposition. G. V. Raynor1 has treated the solid solubilities of some of the elements in beryllium on the basis of the "Hume-Rothery" rules2 which have been modified to include ionic size and ionic distortion effects. It was predicted that the solubility of iron and nickel in beryllium should be slightly less than that of copper. The lowering of the solubility, according to Raynor, is due to a more unfavorable relative valency effect and an ionic size effect. Kaufmann and corzine3 have compiled data on the solubilities of elements in beryllium and have discussed them in the light of the Raynor paper. These authors feel that, because the elements having the greatest solubility in beryllium systematically fall in the Group VIII and IB Columns of the periodic table, the electronic structure greatly influences the maximum solid solubility of elements in beryllium. The solubility of iron in beryllium was determined by Teitel and cohen4 as part of the study of the beryllium-iron phase diagram. The determination was carried out by X-ray and thermal analysis and according to the phase diagram presented, the maximum solubility of iron in beryllium is 0.41 at. pct (2.5 wt pct) at 1225oC. However, it is estimated that the uncertainty in the position of the a-beryllium primary solid-solution boundary is about 0.5 at. pct (3wtpct). Losana and Goria3 in studying the beryllium-nickel phase diagram, determined the solid solubility of nickel in beryllium by thermal analysis. They found the maximum solubility to be between 1.65 and 2.65 at. pct (10 to 15 wt pct) at 1240°C. This value decreased rapidly with decreasing temperature. In determining approximate ranges of solubilities for different elements in beryllium, Kaufmann, et al,8 reported a value of between 1.3 and 1.7 at. pct (7.9 to 10.1 wt pct) for the solubility of nickel in beryllium. The value was obtained by metallographic examination of quenched alloys and lattice-parameter measurements. However, the authors also noted a single-phase structure for a 1.7 at. pct Ni alloy (10 wt pct) on cooling from the liquid. This would indicate a higher solubility range than was reported. ~isch,&apos; in his X-ray studies of beryllium-copper, beryllium-nickel, and beryllium-iron intermetallic compounds, reports the disappearance of a second phase (Ni,Be2) in the beryllium primary solid solution at approximately 4 at. pct (20 wt pct). THEORY The analysis of concentration gradients in diffusion couples has proven to be a useful tool in determining phase equilibria.8-14 In this particular study the diffusion couples were chosen to straddle the expected composition range of the phase boundary, then heat treated at a given temperature and the concentration gradient evaluated. The composition of the phase boundary for a given temperature appears at a point of discontinuity of the composition gradient. Examples of typical phase diagrams and the concentration gradients which should be found in such systems are shown in Fig. 1. In the present work, gradients of the form of Fig. l(c) were obtained in diffusion couples made of pure beryllium and two-phase alloys of beryllium with either iron or nickel. The composition at the point where the gradient becomes discontinuous, Cs, corresponds to the solubility limit of either iron or nickel in beryllium. The analysis of the concentration gradients was carried out by an X-ra absorption method developed and applied by Ogilvie and later used by Moll13 and Hilliard.l4 It depends on the fact that the absorption of X-rays by matter is determined by the concentration and type of the various atomic species present. The relationship for the intensity, I, of a monochro-

Jan 1, 1960

By R. W. Carpenter, J. C. Ogle

It is possible, by using pack-rolling instead of conventional rolling, to reduce a number of metals to thicknesses of 2µm or less. Such thinfoils are generally made at room temperature without intermediate annealing. In addition, pack-rolled foils fail by developing pinholes at thicknesses near 2µm instead of developing the shear cracks usually observed in cold-rolled ductile metals. This paper presents the results of a general investigation of the deformation substructure and texture developed in copper and iron pack -rolled from 130 to about 2µm thickness. Electron microscopy showed that in both metals a fine (0.2 to 0.5?µ m) deformation subgrain structure formed during pack-rolling; in neither case was this substructure grossly different from substructures formed during conventional rolling. The deformation texture formed in pack-rolled iron was quite similar to usual bcc textures; however, in the case of copper, the cube texture was stable during pack-rolling and the normal copper deformation texture was unstable. It is shown analytically that the constraining pack induced a large hydrostatic pressure in the foils during pack-rolling. The pinhole failure mechanism is attributed to the presence of the large hydrostatic pressure during pack-rolling; this strongly suppressed the growth of shear cracks. The stability of the cube texture in copper is also probably due to the unusuul stress distribution developed during pack-rolling. EXPERIMENTS at several laboratories have shown that very thin foils of the common structural metals and many of the rare earths can be made by "pack-rolling". 1-3 The technique was originally developed to make specimens for nuclear scattering experiments and foils for X-ray filters. It is also useful for making experimental laminar metallic composite bodies and foils thin enough for direct examination by ultra-high voltage electron microscopy without the need for special thinning techniques. Pack-rolling in the present context means a three-layer pack, with the material to be rolled into foil comprising the center layer. The outer two layers, which constrain the foil during reduction, are ordinarily austenitic stainless steel. Typically, a 130 µm (0.005 in.) metal strip can be reduced to a final thickness of 2 µm or less by this process. This is accomplished at room temperature, without intermediate annealing. It has been observed that foils produced by this process do not exhibit at any stage of their reduction the severe work-hardening found in strip rolled by conventional cold-rolling methods. Neither is the failure characteristic the same."&apos; Conventionally cold-rolled ductile metal strip fails by developing shear cracks on planes whose normals nearly bisect the angle between the rolling direction and normal to the rolling plane; these are planes of maximum shear stress. In pack-rolling this mechanism has not been observed; failure occurs by the formation of pinholes on the foil surface (penetrating the foil). If pack-rolling is continued the hole density increases. These differences in behavior imply the existence of appreciably different substructure in pack-rolled foils compared to substructure in conventionally rolled material, or perhaps that the geometry of pack-rolling has an effect on the foil behavior. This paper describes an investigation of deformation substructure and texture in some specimens of pack-rolled copper and iron, and some considerations of the stress distribution in the foils during rolling that result from the geometry of pack-rolling. EXPERIMENTAL DETAILS Three different materials were used for pack-rolling in the present work: soft copper sheet (99.8 pct Cu, 0.03 pct 0, electrolytic tough pitch) and two types of iron, Ferrovac E* and Armco iron. Each was "Crucible Stccl Co. initially in the form of 130 µm annealed strip with grain size ranges of approximately 10 to 40 µm. The initial texture of the copper (determined as noted below) was the normally observed cube type (001)[100]; there was evidence of a small amount of material in the cube-twin orientation reported by Beck and Hu.4 The initial texture of the Ferrovac E was similar to that reported for recrystallized iron by Kurdjumov and sachs,5 who list the principal orientations as {111}<112>, {001}<110> 15degfrom RD and a weak component {112}(110) 15 deg from RD. The starting texture of the Armco iron was not determined. Pack-Rolling Procedure. A four-high mill was used for all specimens. The work roll and backing roll diameters were 1.625 and 5.25 in., respectively. The peripheral roll speed of the work rolls was about 2.5 in. per sec. All foils were initially reduced from 130 to 100 µm by conventional straight rolling and then inserted into a pack, without any intermediate annealing, for further reduction. The pack consisted of an 0.033 in. (838 µm) thick 3 by 6 in. polished sheet of austenitic stainless steel, folded to make a 3 by 3 in. jacket. After folding, the jacket was given a small reduction to close the fold tightly before insertion of the foil. During pack-rolling a constant change in roll spacing was made every third pass. The roll-spacing change corresponded to a 5 pct reduction in thickness for a new pack. This approached a 10 pct reduction when the pack had decreased to about half its original thickness. At this point the deformed pack was discarded and a new one

Jan 1, 1970

By Paul F. Kerr, Raymond F. Robinson

Uranium mineralization occurs in the footwall of the Sunshine vein from the 2900 to the 3700 level. Veinlets of uraninite associated with pyrite and jasper have been so extensively divided and recemented that units more than a few feet in length are seldom observed. The wall rock is St. Regis quartzite of the Belt series. The age of the uraninite, on the basis of isotopic analyses, is 750 * 50, which agrees with geological data suggesting that phases of the Sunshine mineralization are pre Cambrian. THE Sunshine mine in the Coeur d&apos;Alene district, Idaho, is well known for its silver-bearing veins but prior to the summer of 1949 had not been recognized as a possible source of uranium. At that time, during a geiger counter reconnaissance by T. E. Gillingham, R. F. Robinson, and E. E. Thurlow, high radioactivity was noted and radioactive specimens were collected from the footwall of the Sunshine vein.&apos; The detection led to the identification of uraninite-bearing veins, since explored jointly by the Atomic Energy Commission and the Sunshine Mining Co. After the occurrence was noted, the geology of the uranium deposit was studied by the Sunshine staff, and a laboratory examination of the ores was conducted at Columbia University. Several types of laboratory work were undertaken. Differential thermal curves were made of selected siderite samples and results from many more were secured through the work of Mitcham.2 X-ray diffraction and X-ray fluorescence analyses were employed on uraninite, jasper, and siderite. Chemical analyses were made through the cooperation of the Division of Raw Materials of the Atomic Energy Commission. General Geological Features Several silver-bearing veins cut the overturned north limb of the Big Creek anticline as mapped by Shenon and McConne1,³ while the Osburn fault, a long-recognized regional feature about a mile away, marks the north boundary of the Silver Belt. The Sunshine vein, Fig. 1, has a south dip more or less parallel to the 60" axial plane of the fold and cuts rocks of the Belt. Series, starting with the Wallace formation near the surface, continuing downward through the St. Regis formation, and probably extending into the Revett quartzite which lies below the bottom or 3700-ft level. The limb of the anticline is locally modified by secondary folds, one being prominently exposed in the uranian area along the Jewel1 crosscut near the Sunshine vein. Crumpling of the limb resulted from compression which formed the anticline and probably preceded the faults in which the vein deposits accumulated. Evidence of drag along these faults points to reverse movement in the uranium-bearing area and elsewhere. This is true of major faults in the mine workings, and the majority of faults which can be mapped, as pointed out by Robinson.&apos; The St. Regis formation, as measured in the mine, appears to have an initial thickness of some 2000 ft, but the apparent thickness due to thickening during folding is some 3400 ft. Along the Sunshine vein the purple and green rocks characteristic of the Wallace formation in the nearby Military Gulch section p. 37 of ref. 5) have been completely bleached because of introduced sericite. Hydrothermal solutions acting on the wall rock have substituted for the original color a pale greenish cast, although no pronounced mineralogical change has resulted, as Mitcham has observed.&apos; The silver and the uranium depositions appear to belong to distinct epochs resulting from several periods of emplacement. Likewise, multiple periods of deformation account for the faulting. Uraninite is generally associated with silicification, while silver . mineralization accompanies carbonate veins. Rarely, uraninite may be found in a matrix of siderite. Ordinarily uraninite formed prior to ar-gentian tetrahedrite. Where clusters of veins form a stockwork, uraninite-jasper veins often favor one trend while tetrahedrite-siderite veins favor another. During deformation, brecciation of the St. Regis quartzite provided openings between broken rock fragments for precipitation from vein-forming solutions. Fractures due to major breaks were filled during the first stages of vein formation, while later deformation displaced the first veins and provided new channels along which further mineralizing solutions proceeded. The uraninite veins, as the first formed, have suffered fracturing, displacement, and segmentation. Uranian vein segments uncut by faults and more than a few feet in length are rare or nonexistent. Siderite veins are more massive and often extend without a break for tens and even hundreds of feet. In general they show much less segmentation. While the siderite is usually later, there is an overlap in the periods of deposition, some earlier siderite veins being extensively segmented in much the same way uraninite veins have been broken. Vein silica is more extensively distributed than the uranium and iron mineralization it carries. Along the vein course concentrations of uraninite frequently fade away and barren white quartz continues, the transition often occurring within a few feet along strike or down dip. An example appears on the 3700-ft level where a uraninite vein, see Fig. 2a,

Jan 1, 1954

By G. Townsend Harley

STOPING methods in which shoveling plays an important part are gradually being replaced by other and cheaper methods. But there will always be considerable shoveling done underground in stopes as well as in drifts, tunnels, urinzes, and shafts. At the mines of the PhelpsDodge Corporation at Tyrone, N. M., the cost of shoveling in all stopes in 1917 amounted to 24c. per T. In the top-slice stopes for the same period, it cost 27 c. per T. or 16 per cent, of the total cost of these stopes. The tonnage for shovelers from all stoping was 9.3 T. per man, and for topslicing 8.2 T. per man. These stopes were not unduly hot, and there was not more than the usual amount of timber to interfere with the work of the men. The tonnages obtained per shoveler were considered low; first, because of a poor grade of Mexican labor, many of the men having come in from railroad grading camps; and second, because of a poor spacing of raises, especially in the top-slice stopes, where, in general, they were spaced 25 ft. by 66 ft. (7.6 by 20.1 m.) centers. The average wage per laborer shift was $2.67 during the year. It was thought, however, that even under these conditions the men were not producing the tonnage that they should, so, with the consent of the management, the writer undertook to determine how the general efficiency of the underground shoveling could be improved. No predetermined plan for conducting these experiments was arranged because we had no definite ideas as to the scope of the work or the number of elements into which the investigation would resolve itself, before all of its phases could be determined. We were sure, however, that any work that would thoroughly cover the ground would have to be in the nature of a systematic time study, combined with a course of instruction in correct shoveling methods and adequate and intelligent supervision of the work. Two or three companies in the Southwest have done some work to determine the proper shovel to be used undcrground, but so far as is known the work has been limited to equipping certain parts of their mines with a particular type and size of shovel and thereafter watching the cost and efficiency records. In each case it seems to have been the shovel that held the 21-lb. (9.5-kg.) load that gave the bcst results. Excepting personal communications from these companies, the only data available on scientific shoveling are contained in F. W. Taylor's book, "The Principles of Scientific Management," and D. J. Haucr's article, in The Contractor for March 29, 1918, "A Hundred Hints for Shovelers." This paper discusses and draws conclusions from several thousand time-study readings, taken both on the surface and in the mines for nearly a year. A sufficient number of readings were taken on each factor in the problem for the plotting of curves of the performances and to obtain accurate indices of the work to be expected from this class of labor. The work is not as complete in all of its details as we would like to havc it, because we were forced to stop the work temporarily, owing to the numbcr of men going into the National service and our inability to get others who could make time studies. The results obtained so far, however, have been of such a startling nature that we have decided to submit them at this time, subject to future modification. It is hoped, also, that a free discussion of this paper will lead to a disclosure of any errors that may have becn embodied and offer some valuable suggestions for the conduct of future work.

Jan 1, 1920

By B. A. Wilcox, A. H. Clauer

The steady-state creep of TD Nickel NL + 2 001 pct TltOz) has been studied orer the telirperatve range 325&apos; to 1100O and the stress range 15,000 to 36,000 psi. At high temperatures (aboue 0.5 T& gran-boundary slzding is the )nost znportant )node of creep deformation, and the steady-state creep rate, is, can be related to stress and temperature by: where Q = 190 kcal pev mole and n has an unusually high value of 40. A creep mechanism based on cross slip of dislocations around The O2 particles can satisfactovily explain the low-temperature (T < 0.5 T,) cveep behavior, and the follo wing relation is applicable: Q, (a) is found to decrease from 57 to 46 kcal per mole as the stress is increased from 32,000 to 36,000 psi. THERE have been a variety of theories proposed to explain the influence of dispersed second-phase particles on the yield strength and flow stress of metals, and these have been reviewed recently by Kelly and icholson.&apos; However, only several attempts2"4 have been made to develop mechanistic treatments which characterize the creep behavior of dispersion-strengthened metals, and to date these have not been fully evaluated experimentally. weertman2 and Ansell and weertman3 proposed a quantitative creep theory for coarse-grairzed dispersion-strengthened metals, based on the concept that the rate-controlling process for steady-state creep was the climb of dislocations over second-phase particles, as suggested by choeck. The theory predicted that the steady-state creep rate, <,, was proportional to the applied stress, a, for low stresses and that is a4 o for high stresses. The activation energy for creep, Q,, was equivalent to that for self-diffusion, Qs.d., in the matrix. Some limited experimental evidence in support of this theory was obtained on a recrystallized Al-Alz03 S.A.P.-type alloy by Ansell and Lenel.6 Ansell and weertman3 also developed a semiquanti-tative theory for high-temperature creep of lineg-rained dispersion-strengthened metals in order to explain their results on an extruded S:A.P.-type alloy, which had a fine-grained fibrous structure. They suggested that the rate of dislocation generation from grain boundaries was the rate-controlling process, and fitted their results to the equation: where Q, was found to be 150 kcal per mole, i.e., QC- 4Q,.d. in aluminum. Similar high activation energies for creep7-&apos;&apos; and tensile deformation" of dispersion-strengthened alloys have been observed by other investigators for S.A.P.,&apos;" indium-glass bead omosites, and Ni + A1203 alls.&apos; There is no general agreement regarding the mechanisms involved in the creep of dispersion-strengthened metals, and this is due in part to the lack of detailed studies relating the structures of crept specimens to the mechanical behavior. The present investigation on thoriated nickel was undertaken with the aim of studying the structural changes which occur during creep of a dispersion-strengthened alloy and rationalizing the observed mechanical behavior in terms of the creep structures. EXPERIMENTAL METHODS The material used in this investigation was 1/2-in.-diam TD Nickel bar, which contained 2.3 vol pct Tho,. Obtained from E. I. duPont de Nemours & Co., Inc. The final fabrication treatment by DuPont consisted of -95 pct reduction by swaging followed by a 1-hr anneal at 1000°C. Transmission and replica electron microscopy revealed that the material had a fine-grained fibered structure with an average transverse grain size of -1 p and a longitudinal grain size of 10 to 15 p. Selected-area diffraction indicated that the fiber axis was parallel to (OOl), in agreement with the results of Inman eta1." All creep specimens were vacuum-annealed at 1300°C for 3 hr prior to testing. Transmission electron microscopy showed that the only structural change due to annealing was a slight decrease in dislocation density, confirming the reported high degree of structural stability.13 Furthermore, recrys-tallization or grain growth during creep was never observed. The structure typical of uncrept material (after the 1300 C, 3-hr anneal) is shown in Fig. 1. The grain boundaries are predominantly high angle and. although some areas show a tangled cell structure, the grain interiors are relatively dislocation-free. Individual dislocations are strongly pinned by the Tho2 particles; i.e., very rarely did dislocations move within a thin foil. The grey "halos" around some of the larger particles which protrude out of the foil surface arise from contamination in the electron microscoge. The Tho, particle size ranged from -100 to IOOOA, and the distribution is shown in Fig. 2. The technique used to obtain the data in Fig. 2 consisted of dissolving the nickel matrix in acid, collecting the Tho2 particles on cellulose acetate, and measuring about 1000 particle diameters in the electron microscope. Similar results were obtained by measuring about 600 particles in thin foils, an; the average particle size was found to be 2r, = 370A. Using the data in Fig. 2 (annealed structure), the mean planar center-to-center particle

Jan 1, 1967

By Lucien F. Trueb

The microstructure of explosion-bonded pairs of similar and dissimilar metals has been investigated by electron microscopy. A review of the specific problems encountered and the methods used for obtaining surface replicas and thin-film transmission specimens of the bond interface is given. The bond area is mainly characterized by continuous and practically diffusionless metallurgical bonding. The very large shear stresses induced along the collision front of the plates being joined causes extreme grain elongation and a symmetrical pattern of subgrains in the bonding direction. The bond zone is also characterized by a very high density of dislocations and pressure-induced twins. Localized heating occurring during the cladding process can result in partial re-crystallization or the formation of thin layers of molten material. The force of precisely controlled explosions causing a high-velocity impact between metal plates has been used for several years to achieve metallurgical bonding between an extremely wide variety of metals. This method essentially consists of accelerating a plate to high velocity toward a stationary plate by a detonating explosive. Since the restrictions to bonding are not those encountered with conventional nethods, it becomes possible to bond pairs of metals having widely different mechanical properties that are immiscible or form brittle intermetallic compounds. Many applications of such composite metals are found in the field of corrosion protection as well as numerous other fields; for example, explosion bonding is being applied for fabricating the materials used by the United States Mint in the new sandwich-type coins. The primary condition for establishing a metallurgical bond is that absolutely clean metal surfaces be brought together. Any metal exposed to the atmosphere is covered with oxides, adsorbed gases, and other contaminants; even a very forceful impact of two such surfaces is not sufficient for bonding. Cowan and Holtz-man,"&apos; who reviewed the dynamics of colliding plates in detail, showed that in order to achieve a good bond the explosion conditions must be chosen in such a way that the plate collision velocity is less than the sonic velocity, in which case no oblique shock waves are attached to the collision front. A pressure wave is then generated ahead of the collision line, and the material forming the colliding surface of each of the plates flows forward and is ejected in the form of a spray, the so-called jet. The dynamic elastic limit of the metals must be exceeded so that there is sufficient plastic deformation. At the point where the jet formed by the junction of the inner surface layers of both plates separates from the combined plates, the material experi- ences a very high shearing strain and the pressure can reach several hundred kilobars. This process strongly influences the microstructure of the bond zone as will be seen later. Behind the collision front, uncontami-nated layers of internal material are brought together under high pressure and are thus metallurgically bonded. I) STRUCTURE OF EXPLOSION BONDS The different types of explosion bonds that can be obtained depend on the explosion conditions, and have been investigated by Cowan and Holtzman,1&apos;2 Holtzman,3 Klein; Bahrani and crossland,&apos; and Buck and Horn-bogen. The preferred kind for practical applications is the so-called wavy bond, typical examples of which are given in Fig. 1 showing light micrographs of various metal-to-metal interfaces. In forming this type-- of bond the collision energy is mainly expended in jetting, the formation of waves, and localized melting. Beyond the crest of the waves, eddy-shaped areas are observed in which the two metals are mixed in a complex pattern of streaks. Cowan and Holtzmanl first proposed that this wavy pattern is analogous to periodic eddy shedding in the flow of a viscous fluid around an obstacle (Von Karman&apos;s eddy street). The mass of metal ahead of the stagnation point, which is associated with the jet and has forward momentum, plays the role of an obstacle and the eddies created in the flow of solid metal around the stagnation point are preserved in the final clad specimen. This idea has been reviewed more recently by Klein4 and the variables involved in the wave formation have been discussed in some detail by Bahrani and crosslands and Buck and Hornbogen.6 Several studies of the structure of explosion bonds by light metallography have already been published.1-6 Aside from the waviness and the eddies which were mentioned above, the most striking characteristic of the area in the vicinity of the bond interface is a very considerable longitudinal grain deformation which appears to be strongest at the metal-to-metal boundary and dies out as one moves away from it. Large twins are often observed within the deformed grains, and molten areas are found in the center of the eddy-shaped structures situated beyond the crest of the waves. The large hydrostatic pressures and shear stresses occurring at the interface modify the mechanical and chemical properties of the bond zone. Increases in hardness in this area have been reported by various authors.396 The defects along the interface can also cause a local increase of the chemical reactivity and thus might be expected to boost the etching rate. However, the effects of this preferential etching cannot be observed by light microscopy due to its inherently limited resolution power. The same limitation precludes the observation of morphological features directly along the bond interface as well as the interface itself. Furthermore, no information can be gained by light-

Jan 1, 1969

By H. K. Birnbaum

The termination of a twin lamella in the interior of a crystal requires accommodation of the strains at the tip of the twin which result from coherency of the twin and matrix. In zinc and magnesium crystals,

Jan 1, 1960

By J. C. Kerkering, P. M. Daling

This paper discusses a study performed to evaluate the feasibility of transferring formal system safety assessment technology to the mining industry. A representative listing of formal techniques was evaluated to select the most useful methods for the mining industry to implement. Criteria for selecting methods included the interests, needs, and requirements of mine safety officials. This paper describes one of the selected methods, preliminary hazards analysis (PHA), and illustrates the analysis procedure for a mining example. This study also includes an assessment of the adaptability of selected methods to a user-interactive computer system for use by mine safety personnel. This paper includes a description of a conceptual computerized PHA-type safety program that facilitates performance of the safety analysis and can accommodate updates and revisions as necessary.

Jan 1, 1983

By Ma Guang, Huang Jinshou

In this paper we briefly describe measuring techniques and their practical use in the mining industry of China. A strain coefficient matrix of triaxial strain cell for a flat ended borehole is also introduced.

Jan 1, 1983

By C. W. Davis

THE name fuller&apos;s earth, which was derived from its early use in "fulling" or removing grease from woolen goods, is a term that is generally considered to designate mineral matter, containing hydrous aluminum silicates of the clay group, which has a high capacity for removing colors from oils, whether of animal, vegetable, or mineral origin. Fuller&apos;s earths are usually dried and may be "tempered" by heating or may be treated with water or reagents to improve their efficiency. For our purpose the term "acid-treated earths" will include those products from the partial decomposition of mineral water by acid which are equal to or more efficient than an untreated fuller&apos;s earth from Quincy, Fla., when used in bleaching mineral oil by the "contact" process. In general, the contact process for treating oils consists of heating and agitating a mixture of oil and finely divided adsorbent, the latter being subsequently removed by filtration. The term "adsorbent" is used because, although there has been a great deal of controversy over the mechanism of removal of impurities from oils by mineral matter, there is no doubt that adsorption, which involves the surface of the solid, plays a major part.1 The properties that make fuller&apos;s earth useful in the treatment of petroleum products by "percolation" and in the purification of edible oils by the contact process have long been studied, but the comparatively recent adaptation of the contact process to the bleaching of petroleum products has made desirable the further investigation of fuller&apos;s earth and other adsorbent earths.

Jan 1, 1929

By H. Vincent Wallace

ALTHOUGH it is universally accepted that free oxygen is A necessary in a cyanide solution for the dissolution of gold and silver-in accordance with Elsner&apos;s equation that 2Au + 4KCN + 0 + H20 = 2KAu (CN), + 2KOH- little has been written and insufficient attention paid to the drop in extraction due apparently to loss of dissolved oxygen in mill solutions. Aeration or oxygenation of cyanide solutions has been more or less successfully accomplished by various types of agitators such as the Dorr (with or without air lifts), Pachuca tanks and more recently "Turbo-mixers" and Denver "Super- agitators"; also by the introduction of chemical oxidizing agents such as Solozone (Na,O,) . At the Wright-Hargreaves and other mines in the Kirkland Lake camp, the introduction of this reagent at the rate of about 1.25 oz. per ton of ore applied to the feed of the ball mills has certainly been beneficial.

Jan 1, 1932