By C. N. J. Wagner, E. N. Aqua

The bee alloys of the terminal solid solution of rhenium in niobium were investigated by X-ray diffraclion methods. The analysis of the broadening of the powder pattern peaks from the niobium-rich alloys, cold-worked by filing, showed evidence for faulting on (211) planes. The alloys with larger rhenium concentrations were brittle, and fractured when filed. The analysis of the shapes of the diffraction profiles from powders produced by hammering with steel plates) of these brittle alloys indicated that the broadening was due predominantly to platelets bounded by clibe planes. This result was consistent with the Laue patterns from single-cleazlage facets which showed evidence for clearage fracture on {100} planes. The influence of faulting on the mechanical properties of face-centered cubic (fcc) metals and alloys, i.e., how faulting affects the various dislocation configurations in fcc metals, is well-known.' The important question is whether or not faulting occurs in body-centered cubic (bcc) metals and alloys, and, furthermore, if faulting does occur, to what extent it affects the mechanical properties. Theoretical calculations indicate that the stacking-fault energy is rather high in most bcc metals.2 The results of sev-eral studies using transmission electron microscopy have indicated that faults are present in well-annealed and lightly deformed bcc metals and alloys, such as tungsten,3 vanadium,4 and Mo-Re alloys.5,6 These faults, as have been observed, may be stabilized by the presence of interstitial (C,N,O) atom segregation to the extended dislocations. In addition, there is considerable X-ray diffraction evidence for faulting in bee metals,7-8 using the same techniques that were successful for the study of faulting in fee metals and alloys.7 This X-ray diffraction method is currently the only technique applicable for the investigation of faulting in metals with high stacking fault energies, i.e., when severe amounts of deformation are required to produce sufficient amounts of faulting to be detectable by X-rays. The thinned films of heavily deformed metals will become opaque in the electron microscope due to the high dislocation densities present. In a previous investigation of faulting8 in bee metals of group Vb and VIb, the authors observed that niobium was ductile when filed at room temperature, and showed the highest density of faults on the (112) family of planes. A niobium-base alloy system was therefore chosen to study the effect of alloying on the occurrence of faults in a bcc alloy. There is a large range of terminal solid solubility of rhenium in the alloys of the bee refractory metals. All of the Group VIb-rhenium alloys, i.e., Cr-Re, Mo-Re, and W-Re, exhibit solid solution hardening without loss of ductility.9 In fact, the ductility reaches a maximum for alloys with compositions near to the limits of solubility. This enhanced ductility has been attributed to the lowering of the stacking-fault energy in the alloy; i.e., the increased amounts of twinning provide an additional mode of deformation, resulting in the observed high ductility.' Because of this demonstrated effect of rhenium in bee alloys, it was decided to study a series of alloys of Nb-Re. Using the same X-ray diffraction methods as described in the previous investigation,' one is able to identify the possible causes of broadening of the powder pattern peaks, e.q., particle size, microstrains, stacking faults, and/or twin faults. The separation of these various contributions to the measured peak shape is accomplished by the Warren-Averbach analysis.7 I) EXPERIMENTAL PROCEDURE A series of seven bee solid solution alloys containing from 2.5 to 21.5 at. pct Re (remainder niobium) were prepared at the General Electric Research Laboratory. Buttons, weighing 25 g, were alloyed from electron-beam-melted niobium chips and random rhenium sheet by arc melting in a water-cooled copper crucible, under an argon atmosphere. The buttons were inverted and completely remelted to promote homogenization. The nominal alloy compositions are listed in Table I. Samples of the cold-worked alloys were obtained by filing to produce a powder for the X-ray study. Alloys too brittle to be filed were hammered with steel plates. The resultant filings or brittle impactings were screened through 150-mesh classifiers and compacted to the required shape for the diffractometer holder. The X-ray diffraction peaks were automatically recorded by fixed time counting at uniform 28 intervals, or by continuous registration with a ratemeter. In all cases, the (110)-(220) and (200)-(400) pairs of peaks and the (211), (310), (222), and (321) reflections were measured on a GE-XRD5 diffractometer using CuKa radiation with nickel filter or MoKct radiation and a LiF monochromator in the diffracted beam. The first part of the data reduction, completed with the aid of a series of programmed computations,10 was the analytical resolution of the Kol component of the diffraction profile. Subsequent computations were then made with reference only to the resolved Kol peak shape. These included the measurement of the

Jan 1, 1967

THE increased demand for titanium alloys with improved high-temperature creep strengths has stimulated interest in silicon as an alloying addition to titanium. Silicon is a potent solid-solution strength-ener and, if added in sufficient concentration and properly heat-treated, can also dispersion-strengthen titanium by eutectoid decomposition.' However, better understanding of the nature and distribution of the resulting silicide dispersion in more highly alloyed titanium matrices is necessary for the development of useful titanium alloys which utilize the latter strengthening mechanism. This note describes the chemical and crystallographic characteristics of the silicide phase as it occurs in a typical high-temperature near-a titanium alloy matrix. Several Ti-6A1-3Sn-3Zr a11oys containing various amounts of silicon ranging from 0.1 to 1.0 pct were melted as 10- to 20-lb ingots and processed into 1/2-in.-diam bar stock. The microstructures of specimens annealed at various temperatures were conveniently summarized by the (Ti-6Al-3Sn-3Zr)-Si pseudobinary phase diagram illustrated in Fig. 1. Comparison with the Ti-Si equilibrium diagram indicates the substitutional solutes (Al-Sn-Zr) increase the eutectoid temperature and decrease the a terminal solubility. Annealing at temperatures sufficiently high to dissolve the silicon in a ß solid solution and cooling rapidly enough to preclude coarsening generally produced a uniform dispersion of fine silicide particles, whereas annealing at temperatures near but below the ß transus produced relatively coarse silicide particles. Annealing in the limited a, plus 3 region produced a duplex coarse and fine silicide array. Several a-annealed specimens were examined by X-ray diffraction to determine the crystallographic identity of the precipitate phase. Copper Ka X-ray diffraction patterns of bulk specimens which contained 0.5 and 0.8 pct Si were virtually identical to that of the silicon-free Ti-6Al-3Sn-3Zr base alloy except for a slight shift in some of the high-angle diffraction lines. Apparently the silicide volume fraction was too low to be detected in bulk specimens. X-

Jan 1, 1969

By M. B. Bever, A. K. Jena

In the investigation reported here, calorimetric measurements have been made to determine the heat of formation of the compound AuSb2 and the partial gram-atomic enthalpies of antimony and gold in dilute solution in liquid tin and their enthalpy interaction coefficients. In order to interpret the behavior of antimony and gold in dilute solution in tin, nonzero values are assigned to the energies of bonds between like solute atoms relative to the pure solute state. Sa.mples of the compound AuSb2 were prepared by melting stoichiometric amounts of antimony and gold (99.999 pct pure) in evacuated and sealed Vycor tubes, which were shaken vigorously and quenched in water. The ingots were annealed in evacuated and sealed tubes at approximately 700°K for 2 weeks. Metallo-graphic and X-ray examinations gave no indication of second phases or microsegregation. The samples were added from 273°K to tin-rich solutions in a solution calorimeter1 maintained at 623°K. The calorimeter was calibrated with tin; the heat content of tin, H623°K- H273°K, was taken as 4.08 kcal per g-atom.2 In each calorimetric run at least four additions were made. The total concentration of solutes in the bath at the end of any run did not exceed 1 at. pct. The measured heat effect of an addition was plotted against the average of the atom fractions x of Sb + Au in solution before and after that addition. From this plot the heat effect at infinite dilution h,,, and the composition dependence of the heat effect dh/dx in the composition range 0 < x < 0.01 were obtained. The results for the additions of antimony, mixtures of antimony and gold, and the compound AuSb2 are listed in Table I. The heat effect h on addition of a sample of the compound AuSb2 or a mechanical mixture of antimony and gold at 273°K to a tin-rich solution at 623°K can be expressed as:

Jan 1, 1969

By D. McLean

For many pu@oses uniform strength is desired over a long temperature range, coupled to a band of softness at the hot end for easy shaping. Various types of material fulfill such a requirement to different degrees, depending on the regularity of their atomic structure. In long-chain polymers and vitreous glasses the irregular structure leads to a steep temperature dependence of deformation resistance and the temperature band between the hard and brittle condition and the soft condition is only about 100 C. In crystals and especially metals the atomically regular structure leads to a much smaller sensitivity over a wide temperature band, thus approaching the ideal behavim. The reason for this insensitivity is that the regular crystalline structure deforms by the movement of dislocations and the elastic interactions of dislocations in- PLASTICS, GLASSES, AND CRYSTALS The ease or otherwise of deformation varies with temperature much more in some substances than in others. This is an important matter when service over a wide temperature range is needed, especially volve energies of several hundred electron volts compared with which the energy of thermal agitation is insignificant. However, temperature affects a metal&apos;s defmmation resistance through its influence on the annealing, m coarsening, of the three-dimensional dislocation network. This coarsening is a phenomenon very similar to grain growth and ideas about grain growth can be applied to it. Taking into account also the temperature dependence of the glide resistance from alloying additions, a reasonable account can be given of the overall effect of temperature on deformation strength and of stress and grain size on deformation rake. Special structures me described. some arising from these ideas and as yet untried, which may benefit metals and polymers but not ni-treous glasses. when in addition a degree of softness suitable for shaping is required at some stage. It would be nice if one could write on this subject in as much detail about plastics, glasses, and so forth, as about metals, but there has been far more study of this matter in metals than in other substances, which is one reason why most of this paper concerns metals. However, in Fig. 1 there are shown the deformation strengths of several nonmetallic substances as a function of temperature. In many tests the attempt at deformation caused breakage and the graph lines are then drawn dashed. Long-chain plastics, a glass, and a crystalline substance are included in Fig. 1. The notable feature of all of them is the sensitivity of the

Jan 1, 1969

By R. H. Tien

The accuracy of the method of steady-state approximation applied to the problems of heat transfer involving phase change (London and Seban&apos;s solution) is improved by defining a "modified heat of fusion" which accounts for the effect of specific heat. An analytical expression for this modified heat of fusion is derived in terms of the actual heat of fusion, specific heat, and surface temperature. Numerical solution for the freezing of iron indicates that the ratio of the modified heat of fusion to the actual heat of fusion increases from 1.04 to 1.4 as the surface temperature decreases from 2700° to 1600°F. The heat transfer process accompanying solidification is complicated owing to the moving solid-liquid interface where the latent heat of fusion is released. Exact analytical solution is available only for a few special cases of freezing problems such as Stefan&apos;s1 problem. In a commonly used steady-state approximation method, London and seban&apos;s2 solution, the effect of specific heat is neglected. This approximation, however, may introduce some degree of error in mathematical analysis when the temperature of the solid surface is much lower than the freezing temperature, as in the case of freezing metals. In a recent work by Robertson and Schenck,3 the problem of freezing a semi-infinite region with finite surface conductance was programed in a digital computer through the finite difference method. A family of curves for the correction of the London-Seban solution was given in a dimensionless plot for different ratios of heat of fusion and specific heat effect; it was shown that the London-Seban solution when applied to the freezing of a mild steel slab under some particular conditions gave results in error by about 10 pct in the solidification rate. Although the Robertson-Schenck computer result has improved the London-Seban solution to a great extent, lack of generality and the tedious computing procedure have restricted its application. In this paper a "modified heat of fusion" which accounts for the effect of specific heat is defined, and is used instead of the actual heat of fusion in the London-Seban solution. An analytical expression of this modified heat of fusion in terms of the specific heat, surface temperature, and actual heat of fusion is derived by comparing the solutions of Stefan and London-Seban for the case of freezing of a semi-infinite region with constant surface temperature. It can also be extended to the case with finite surface conductance, and the results show good agreement with the Robertson-Schenck computer solution. The expression of the modified heat of fusion, the accuracy of the London-Seban solution, and the temperature distribution within the solid are presented graphically in dimensionless form. Numerical solution for the freezing of iron indicates that the ratio of the modified heat of fusion to the actual heat of fusion increases from 1.04 to 1.40 as the surface temperature decreases from 2700° to 1600°F.

Jan 1, 1969

By O. F. Walker, W. C. Hahn, V. A. Johnson, J. D. Wood

The diffusion coefficients of zinc in single-crystal zinc and carbon in single-crystal and poly crystalline nickel were measured by means of radioactive tracer techniques both with and without the application of ultrasonic vibrations under conditions such that the temperature of the sample was closely controlled. The results of this investigation indicate no enhancement of diffusion in any of the samples. It is suggested that previously reported enhancement may have been due either solely to temperature increases caused by ultrasonic vibrations or in combination with changes in the boundary conditions. A number of observations have been reported in the literature in which it has been implied or inferred that the application of ultrasonics enhances diffusion (see, for example, Refs. 1-5). The present study was undertaken in an attempt to observe this effect under carefully controlled conditions, particularly with regard to measurement and control of the temperature of the sample. Two different types of systems were studied; these were the self-diffusion of zinc and the diffusion of carbon in nickel. EXPERIMENTAL For diffusion with ultrasonic energy applied, the samples were included as part of a resonant ultrasonic system operating at 58.5 kcps. The ultrasonic generators used were rated at 100 and 250 w and could be tuned over a frequency from 10 to 100 kc. A PZT (lead titanate/lead zirconate) ceramic transducer provided the driving vibration. This system requires no metallurgical joining of the specimen to the acoustical transmission line since the ultrasonic driver and the follow-up section clamp the specimen in position by means of a constant pressure of 50 lb developed by an air cylinder. The ultrasonic driver and follow-up section, both made of titanium, were 4 in. in length from clamping point to the end in contact with the specimen. Using the relationship given by Mason,6 A = V/f, the resonant wavelength, A, in titanium is calculated to be 3.3 in. at a frequency, f, of 58.5 kc, taking the velocity of sound in titanium, V, as 1.95 X 105 in. per sec. The 4-in. driver and follow-up section, therefore, are each 4.0/3.3 =1.21 times the resonant wavelength. Clamping pressure must be applied at stress nodes of the transmission line in order to preserve resonance. Therefore, a specimen length of 0.58 times the wavelength in the specimen was required to place the clamping pressure application points at stress nodes exactly three wavelengths apart. A stress antinode was contained in the center 3 in. of the specimen. A small PZT ceramic disc attached to the follow-up section provided an output voltage proportional to the intensity of the standing wave. This output voltage was monitored on an oscilloscope and the ultrasonic system was tuned to resonance by varying the frequency until the output signal was a maximum amplitude. The amplitude of the output signal was maintained constant throughout the diffusion anneal. A split cylindrical stainless-steel chamber, which was purged with argon prior to and during the runs, was placed around the specimen. The chamber in turn was surrounded by a movable furnace whose temperature could be controlled to 7C. Heat exchangers were used to cool the driver, follow-up section, and ultrasonic transducer. Great care was taken to obtain the true specimen temperature in all cases. Several different methods were tried; the most successful was that in which the thermocouple was held in contact with the midlength of the specimen by means of an asbestos insulating pad and wire straps. In the case of zinc, single-crystal specimens of 99.999 pct purity were used. The samples were 0.25 by 0.25 in. square and of the proper length for resonance, that is 1.1 in. long with the c axis parallel to the long dimension of the specimen for the case of diffusion perpendicular to the c axis and ultrasonic motion parallel to the c axis, and 1.9 in. long with the c axis perpendicular to the long dimension of the specimen for the case of diffusion parallel to the c axis and ultrasonic motion perpendicular to the c axis. In each case, one of the rectangular faces was electroplated with a thin film of zinc containing Zn The constant pressure used to clamp the specimen in place in the ultrasonic system caused some deformation in some of the samples. For these samples the deformation was concentrated in either end of the specimen; thus, for all samples (both zinc and nickel) the center in. was cut from the specimen after the diffusion anneal to be used for sectioning and counting. The nickel single-crystal samples, of 99.999 pct purity, were used in the form of rods 0.25 by 0.187 by 2.07 in. long with the (100) direction parallel to the rod axis. The polycrystalline nickel samples of 99.97 pct purity had an average grain diameter of 0.007 in. and were used in the form of rods 0.25 by 0.125 by 1.87 in. long. The direction of ultrasonic motion was parallel to (100) direction (bar axis) for the single-cqstal samples and parallel to the bar axis for the polycrystalline specimens. A thin film of c14 suspended in methanol was applied to the diffusing face of the specimen. Two specimens were butted together lengthwise for each diffusion anneal to minimize oxidation. After diffusion, a precision lapping device similar to the one described by Goldstein7 and a radiation detector were used to obtain a plot of specific activity vs penetration distance for each specimen. (A scintil-

Jan 1, 1969

By M. A. Dayananda

Based on the Kirkendall frame of reference, a method is proposed for the determination of atomic mobilities of all the diffusing species in a multicorn-ponent system with a single diffusion couple. The method is based on an atomic mobility model developed on the concept of negligible interactions among the intrinsic fluxes. It is shown in the model that mobilities can be obtained directly from the cumulative intrinsic fluxes past the Kirkendall interface. The proposed method replaces the need for a prior determination of interdiffusion coefficients far the calculation of mobilities. Relations between intrinsic diffusion coefficients and mobilities are derived and the mobility calculations are illustrated with diffusion data in Cu-Zn-Mn alloys at 850°C. ThE concept of "intrinsic flux" with respect to a fixed lattice was introduced "i Darken1 to explain toa Kirkendall effect2 demonstrated by the motion of inert markers during isothermal diffusion in single-phase binary solid solutions. Based on this concept, intrinsic diffusion studies have been made in various binary metallic systems3,4 employing such a lattice frame of reference, commonly referred to as the Kirkendall interface. Similar approaches, both theoretical and experimental, have been presented5"10 to study intrinsic diffusion in multicomponent systems. Based on the direct integration of Fick&apos;s law extended to multicomponent diffusion, Philibert and Guy8 proposed a method for the determination of intrinsic diffusion coefficients. For an n-component system, this procedure requires an experimental study with (n — 1) diffusion couples, all having their Kirkendall interfaces at the same compositio;, where n(n — 1) intrinsic diffusion coefficients are defined. This technique has been employed for ternary diffusion studies by Dayananda and Grace" and Guy and Leroy.11 A different approach is recommended by Ziebold and Cooper,12 who have derived relations between interdiffusion coefficients and atomic mobilities employing fluxes referred to the local center of volume. Their analysis is based on the simplifying assumption of negligible interactions among intrinsic fluxes. This assumption has been considered satisfactory for dilute solutions.5"7 The use of this analysis for the calculation of mobilities requires an initial determination of interdiffusion coefficients with a set of diffusion couples having intersecting diffusion paths. It is the purpose of this paper to propose a method that would permit a direct determination of mobilities of all components of a multicomponent system from a single diffusion couple. This method is based on a mo- bility model developed with diffusion fluxes referred directly to the Kirkendall interface, generally identified by inert markers. gen erall, like that of Ziebold and Cooper,12 employs the simplifying assumption that the flux of each component relative to a fixed lattice is caused only by the driving force of its own chemical potential gradient. THE KIRKENDALL INTERFACE Inert markers are employed in diffusion couples to locate experimentally the position of the Kirkendall interface. They are initially placed at the weld interface for "sandwich" couples, or at the original vapor-solid interface for vapor-solid couples. Studies of marker motion in binary systems3&apos;4 with both types of couples indicate that markers remain in a plane of constant composition and move with this plane para-bolically with time. Parabolic marker movements were also observed in ternary Cu-Zn-Mn couples by Dayananda and Grace.10 It is reasonable to expect a similar marker behavior even for diffusion couples with a higher number of components.

Jan 1, 1969

By G. R. Speich

The interlarnmelm spacing, growth rate, and degree of segregation that accompany cellular precipitation in four Fe-Zn alloys containing 9.7, 15.2, 23.5, and 30.5 at. pct Zn have been determined in the temperature range 400" to 600°C. The chemical free-energy change for the reaction was calculated from the available thermodynamic data and the known compositions of the phases. The fraction of the chemical free-energy change for equilibrium segregation that is converted into interfacial free energy decreases from 0.43 to 0.08 as the magnitude of this free-energy change increases from 35 to 270 cal per mole. At constant temperature the cellular growth rate is proportional to the cube of the dissipated free energy. At 600°C newly 100 pct of the equilibrium segregation is achieved during cellulm precipitation whereas at 400°C only 85 pct of the equilibrium segregation is attained. During cellular growth, mass transport of zinc occurs by grain boundary diffusion; excess zinc remaining in the a! phase after the completion of growth is removed slowly by volume diffusion. A modified Cahn theory of cellular precipitation predicts the observed interlamellar spacing within a factor of two. In cellular precipitation reactions such as pearlite formation or discontinuous precipitation, the basic problem is to predict the variation of growth rate G, interlamellar spacing S, and degree of segregation P with composition and temperature. To accomplish this we need three independent equations relating these quantities. One of these equations comes from the diffusion solution. To obtain two additional independent equations, some assumptions must be made. cahnl has suggested recently that two plausible assumptions are 1) that growth rate is proportional to the dissipated free energy and 2) that the spacing which occurs is that which maximizes the dissipated free energy. According to the first assumption, this spacing also maximizes the growth rate and the rate of decrease of free energy per unit area of cell boundary. The present work was undertaken to test these assumptions. To test the first assumption it is necessary to study a cellular reaction over a wide range of supersatura-tions to establish a relationship between G and the dissipated free energy at constant temperature. This is possible only in discontinuous precipitation reactions since in pearlite reactions constituents other than pearlite form if the composition of the parent phase deviates even slightly from the eutectoid composition. The Fe-Zn system was chosen for study because 1) discontinuous precipitation proceeds to completion over a wide temperature and concentration range, 2) the degree of segregation within the cell can be measured by lattice parameter measurements,2 and 3) the thermodynamics of this system have recently been determined by Wriedt.3 In this system the cells consisting d alternate lamellae of a and r phases form from supercooled iron-rich a phase. The a phase within the cells is bcc as is the original a phase, cia, but has a different orientation and a slightly lower zinc content than the original a phase. The r phase has a zinc content of about 70 at. pct and a crystal structure isomor-phous with T brass. EXPERIMENTAL PROCEDURE Four Fe-Zn alloys with 9.7, 15.2, 23.5, and 30.5 at. pct Zn were prepared from carbonyl-iron powder (400 mesh, 99.8 wt pct Fe) and zinc powder (200 mesh, 99.99 wt pct Zn). The powders were ball-milled together and cold-pressed under 60,000 psi to discs $ in. thick by $ in. diam. The cold-pressed discs of the alloys with 9.7 and 15.2 at. pct Zn were sealed in evacuated silica capsules and heated slowly to 1100°C over a period of 1 week (3 days at 600°C, then 3 days at 80O°C, then 1 day at 1100°C). The alloys with 23.5 and 30.5 at. pct Zn were treated similarly except that the final homogenization temperatures were 1000" and 85O°C, respectively, to prevent melting. The alloys were quenched in iced brine from the final homogenization temperature. Specimens of each alloy were subsequently aged in salt pots at temperatures of 400°, 450°, 500°, 550°, 600°, and 650°C for times that varied from a few minutes to several hundred hours. At a late stage of this work, an alloy containing 11.2 at. pct Zn was prepared by vapor-impregnation of iron foil with zinc vapor at 890°C. This alloy proved useful for electron microscope studies because it was free of porosity. The homogenization and aging conditions were based on the recent Fe-Zn phase diagram of Stadelmaier and Bridgers4 rather than the earlier diagram of ansen.5 They consist of a homogenization heat treatment in the homogeneous a field followed by an aging treatment in the two-phase a + r field. The aged specimens were metallographically polished and etched in 2 pct nital and the radius of the largest cell in the microstructure determined. This radius plotted vs time gave a straight line whose slope is the boundary migration rate or growth rate G of the cell. To determine the interlamellar spacing, specimens were examined by surface-replica and thin-section electron microscope techniques. Because of the irregular nature of the lamellae within the cell, the average interlamellar spacing S .of the cell was measured by the method of Cahn and Hagel,6 where S is defined by:

Jan 1, 1969

By R. A. Meussner, C. T. Fujii

Chromium solution in wustite depresses the oxygen activity in a nonideal manner and expands the lattice slightly. Gravimetric measurements of the equilibrium compositions of wustite containing 0.00 to 1.38 wt pct Cr define the oxygen potential (CO2-CO atm) and the limits of the phase field at 1000°C. These data extrapolate to a maximum solubility of 2 wt pct Cr. The lattice parameter data, room-temperature measurements of quenched samples, differ significantly from those in the literature. Both pure and chromium wus-tites contract at uniform and equal rates as the oxygen content (metal deficit) increases. The a. US metal deficit relationships are straight lines showing none of the curvature previously reported. At constant metal deficit, the a. expands by 0.002? on alloying with 0.4 to 0.5 wt pct Cr but is insensitive to further chromium additions: a small expansion rather than a marked contraction. These results require a modification of the accepted alloying mechanism. IN the high-temperature oxidation of Fe-Cr alloys in Ha-H,and CO2-CO atmospheres the vapor transfer of oxygen from the continuous wustite outer scale to the porous inner scale/alloy interface sustains the high oxidation rates.1"3 The driving force for this transport is the difference in the oxygen activity of the outer wustite and that at the inner scale/alloy interface. In pure CO2, as well as in CO2-CO atmospheres, carburization of the alloy accompanies this oxidation. Current efforts to evaluate the parameters controlling this carburization have shown that the process is not simple; i.e., the carbon concentration in the alloy initially increases rapidly, reaches a maximum, and then decreases slowly as the oxidation time is extended. This is the same pattern reported by McCoy for the more complex oxidation-carburization of stainless steels and an Fe-Cr alloy in CO2 at lower temperatures.4 These changes in the carburization process occur while the overall oxidation rate and the lattice parameters of the scale layers remain constant. If this invariance of the lattice parameter is assumed to indicate a constant scale composition and thus a constant oxygen potential, the carburization results are not easily explained. Electron microprobe traces across the thickness of these outer scales, however, have revealed distinct chromium gradients penetrating 10 to 50 µ from the inner surface where the chromium concentrations were estimated at a few tenths percent. The variation of the chromium cmcentration on the inner surface of the scale, and the resulting change of the oxygen activity, during the oxidation process is considered to be important in defining the carburization process. Thus, to gain an understanding of the complex oxidation-carburization proc- ess, it was necessary to measure the properties of wustite containing known amounts of chromium (chromium wustite). Although the general features of the Fe-Cr-0 equilibrium diagram between 900° and 1300°C have been fairly well established by Richards and white: Wood-house and White,6 Seybolt,7 and Katsura and Muan,8 there have been no detailed studies of the limits of the chromium wustite phase field or the properties of these alloyed wustites. The recent results of a limited study of chromium wustite by Levin and wagner9 indicate that more than 0.67 wt pct Cr is soluble in wustite above 850°C and that this alloying is accompanied by a substantial lattice contraction. This change in the lattice parameter was not evident in the X-ray diffraction patterns of wustite layers from the oxidation experiments;1,3 the lines were sharp even though a chromium gradient existed in the scale. The present paper describes gravimetric equilibrium experiments which delineate the boundaries of the chromium wustite single-phase field at 1000°C and define the changes in the oxygen activity and the lattice parameter of wustite as functions of chromium and oxygen contents. The lattice parameter data of chromium wustite obtained from these equilibrium and special quenching experiments differ considerably from those reported.9 Those for pure wustite show significant differences from the widely accepted data of Jette and Foote.10 Since the causes of these differences are not easily assignable, and since the literature contains many sets of data on wustite which if not in conflict are at best not in harmony, the experimental procedures are discussed in the present paper. EXPERIMENTAL Oxide Preparation. The specimens used in these studies were porous pellets compacted from high-purity (Fe,Cr)2O3 or Fe2O3 powders. These powders were prepared from electrolytic chromium (99.8 pct purity) and electrolytic iron purified by consumable-electrode, vacuum arc-melting processing (299.9 pct purity).11 The oxides were produced by standard analytical procedures: solution of the metals in acids (HC1, then HNO3 added), coprecipitation of the hydroxides (NHaOH), and filtering and washing these precipitates. Initial dehydration of the coprecipitated hydroxides was done in a porcelain evaporating dish heated by a Meker-type burner, final dehydration by firing in a recrystallized alumina crucible at 1000" to 1050°C for 20 hr in an electrically heated furnace. Spectrographic analysis detected the following impurities: silicon, 0.01 pct or less; aluminum, 0.001 pct to trace; manganese and copper, 0.0001 pct to none. Each of these levels is at least one order of magnitude lower than in commercially available CP grade ferric and chromic oxides. Fluorescence analy-

Jan 1, 1969

By W. D. Forgeng, R. E. Grace

The rate of copper corrosion in liquid lead was studied as a function of flow rate and temperature in a closed isothermal loop system between 350" and 500°C. Kinetic data were interpreted with the Nernst-Brunner equation and the Chilton-Colbum mass transfer analogy to heat transfer. Over the range of temperatures and flow rates employed the solution rate constant varied from 2 x 10-3 to 20 x 10-3 cm per sec. The rate constant was found to vary with the 0.76 power of the Reynolds number in the range 7500 < Re < 40,000. The results of this investigation indicate that the Cu-Pb corrosion process is controlled largely by diffusion across a boundary layer. particularly at the higher temperatures. The effective boundary layer for diffusion is found to be approximately three to four times smaller than the momentum boundary layer. CORROSION by liquid metals has long been a problem during melting, static containment, and casting. Recently, considerable emphasis has been placed on the understanding of liquid metal corrosion mechanisms in an effort to prevent mass transfer and eventual failure in liquid metal heat exchangers and in liquid-metal-fueled nuclear reactors. The present investigation was conducted to determine the relationships which exist between corrosion kinetics and hydrodynamic conditions in an isothermal loop containing a simple liquid metal-solid metal corrosion system. The Cu-Pb system was chosen for its simplicity and ease in handling. Previous isothermal Cu-Pb corrosion studies1-3 have been conducted in both static and dynamic systems but not under conditions which allow easy "scale-up" to engineering systems, such as liquid metal heat exchangers. On the other hand, most liquid metal loops which have been used to evaluate mass transfer rates4 have been driven with temperature gradients under conditions of natural convection and unknown flow rates. The primary contributions of this research are twofold: 1) to evaluate the design of a simple isothermal loop corrosion system and 2) to investigate liquid metal corrosion behavior under well-defined hydrodynamic conditions. MATERIALS AND EXPERIMENTAL WORK The apparatus used to measure the Cu-Pb corrosion rates is shown schematically in Fig. 1. The loop system consisted of 1) a reservoir made of Type 316 stainless steel containing a centrifugal pump and 2) stainless-steel tubing containing a removable copper test section. The copper test section was OFHC hard-drawn tubing, 11.0 0.05 cm in length and 0.775 ±0.005 cm ID. A Type 316 stainless-steel venturi meter* was inserted in place of the copper test sec- tion in order to determine the lead velocity as a function of pump speed at each temperature. The Cu-Pb system was chosen for this study because the solubility of copper in liquid lead is large enough to measure accurately but small enough that the diameter of the copper tubing was not changed significantly by corrosion. There are no intermediate phases formed in the system, and the solid solubility of lead in copper is vanishingly small so that back-diffusion cannot occur. Molten lead (corroding grade; 99.94+ pct Pb, 0.0015 max pct Cu) was charged from an auxiliary melting furnace into the system under an argon cover to minimize oxidation. The lead was then maintained at constant temperature by a stirred molten salt bath in which the loop was immersed to a depth just above the lead level in the reservoir, Fig. 1. The total volume of lead in the system was 320 2 cu cm.

Jan 1, 1969

By J. E. Hilliard

A procedure is described for determining, from measurements on a section, the moments of any degree n (i.e., the mean value of Dn, where D is a linear dimension) of the size distribution of particles (or grains) in an opaque sarnple. The analysis is applicable to particles of alnzost any shape and to any mixture of shapes. However, if absolute values of the wloments are required, it is necessary to know what shapes are present and the relative frequency of their occurrence. In addition, certain shape-dependent parameters have to be evaluated before the formulas can be used. The measurement required is the distribution of intercept lengths. This can be determined either visually or with an automatic scanning instrument. Corrections me derived for the bias due to instrumental end effects. The proposed analysis has the following advantages over existing ones: 1) Confidence limits are easily estimated for the measured properties or, conversely, the number of counts required to achieve a given accuracy can be determined. 2) The analysis is not restricted to particles of a special shape. 3) The error resulting from any known degree of departure of the actual from the assumed particle shape can be estimated. 4) The computations are simple and, apart from a change in constants, are independent of particle shape. 5) The number of particles per unit volume can be determined by a simple counting procedure. MANY procedures have been described for determining the size distribution of particles from measurements on a section (or plane of polish). They differ from one another in the property measured on the section (radius, intercept length, profile area) and in the method used for the numerical solution of the integral equation relating the property to the particle size distribution. However, all existing analyses share at least two of the following disadvantages. 1) They are limited to a particular shape of particle (usually spherical). 2) It is very difficult to determine how the statistical sampling error is propagated into the computed size distribution. The investigator thus has no means of knowing the reliability of his result and, what is of equal concern, he is unable to estimate how many measurements are required to obtain a result of the required accuracy. 3) It is also difficult to assess the error resulting from any deviation between the actual and assumed particle shape. The foregoing limitations stem from the complex relationship between the particle size distribution and the distribution of the property measured on the section. As will be shown, they can be avoided by defining the size distribution in terms of discrete parameters

Jan 1, 1969

By K. R. Carson, J. Weertman

An attempt is made to ascertain the mechanism of tangle and cell formation and its dependence upon dislocation-interstitial carbon interactions. The strain-hardening behavior of single crystals of 3.25 pct Si-Fe was determined at 300° and 425°K and under conditions of both continuous and interrupted tensile strain. Significantly enhanced hardening was observed in crystals deformed at the elevated temperature, and it was further accentuated by interrupted straining. Transmission electron microscopy was used to study the resultant dislocation structures. Strain aging was found to aid tangle and cell formation at 425°K, but at both temperatures embryo tangles formed solely from primary glide dislocations, presumably by a process involving cross slip and "mushrooming". IN the course of plastic deformation all bcc metals and alloys develop a dislocation structure characterized by loose-knit groups of tangled dislocations. With increasing strain the tangles become more tightly knit and grow larger; finally a three-dimensional cellular substructure is formed:1 This process has been observed with the transmission electron microscope.&apos;-l7 However, most investigations were confined to the study of nearly pure polycrystalline metals at relatively low temperatures. At intermediate temperatures, 0.17 to 0.14 Tm where T, is the melting temperature in degrees absolute, the mobility of interstitial impurities such as carbon is high enough to permit migration to nearby glide dislocations but is still low enough so that a significant drag force is exerted.18,19 it is also in this temperature range that a hump occurs in the curve of work-hardening rate vs temperature for iron. Analogous plots for tantalum" and columbiumzo show a definite upward trend in the work-hardening rate. Keh and Weissman1 have pointed out that this behavior may be explained solely on the basis of changes in the dislocation configuration: at low temperatures the dislocations tend to be relatively straight and uniformly distributed, but at intermediate temperatures tightly knit tangles and cellular substructure appear. The interference of these tangles with glide dislocations causes the observed increase in the work-hardening rate. This explanation appears reasonable, yet one might ask what factors cause tangle formation to be so favorable at intermediate temperatures. It seens likely that the strong dislocation-interstitial interactions which are known to occur in this temperature range are at least partly responsible," with the magnitude of the effect being proportional to the interstitial concentration. The purpose of the present work is to study the relationship between tangle formation and strain hardening in a bcc metal in the temperature range 0.17 to 0.4 Tm. Particular emphasis was placed upon a study of the effects of interstitial-dislocation interactions. Single crystals of 3.25 pct Si-Fe containing about 200 ppm of C in solid solution were used in the investigation for the following reasons: 1) The mobility of interstitial carbon in 3.25 pct Si-Fe is negligible at 300°K but increases rapidly at slightly elevated temperature22. Hence, differences between the flow curves and dislocation structures of crystals deformed at 300°K, 0.17 T,, and crystals deformed, say, at 425°K, 0.24 Tm, should be appreciable because of the enhanced dislocation-carbon interactions at the elevated temperature. This effect was accentuated in some samples by interrupted straining, thereby introducing a certain amount of aging. 2) Near room temperature, slip in suitably oriented 3.25 pct Si-Fe single crystals is largely confined to the (110) planes.23&apos;24 Dislocation structures formed under conditions of single glide are the least complicated and their method of formation is the most easily discernable. 3) Dislocations in Si-Fe can be tightly locked with carbon atmospheres by a low-temperature aging treatment. The subsequent thinning of samples to foil thicbess causes little or no rearrangement in the dislocation structure.25 EXPERIMENTAL PROCEDURE Large single-crystal sheets of 3.25 pct Si-Fe were donated by Dr. C. G. Dunn of the General Electric Research Laboratory, Schenectady, N. Y. The orientations of the sheets were determined and slabs 1.0 by 0.25 by 0.05 in. were cut such that the desired tensile axis corresponded to the long dimension. The slabs were mechanically polished and subsequently decar-burized by heating at 1000°C for 3 days in a flowing wet-hydrogen atmosphere. A carbon content of about 200 ppm was introduced by heating at 805°C for 25 min in a flowing atmosphere of dry hydrogen containing heptane vapor. Shaped copper tools were then used to spark-machine at 0.125 by 0.50 in. gage length onto each slab. Vacuum annealing at 1225°C for 2 days followed by a quench into the cold end of the furnace to retain carbon in solid solution concluded the soecimen preparation. Continuous tensile flow curves for crystals of severa1 orientations Were obtained both at 300&apos; and 425°K. A strain rate of 6.67 x 10-4 Per set was used in these and all other tests. Crystals oriented for single glide, B and D in Fig. 1, were subjected to a 3.5 pct plastic elongation to insure uniform slip along the gage length; they were then immediately subjected to interrupted strain cycling as indicated in Fig. 2(a). Each cycle consisted of unloading to 1.5 kg per sq mm, holding

Jan 1, 1969

By D. R. Packard, J. D. Verhoeven

The resistivity us atom fraction relationships for dilute solutions of cadmium, mercury, and tin in molten sodium have been determined. With these data and the resistivity capillary-reservoir technique, the electro-transport mobilities, effective valences, and the diflusion coefficients of the three solutes have been determined. The mobilities are found to be higher than in other molten alloys by a factor of around 20. The results are compared to the Mmgelsdorf model for electrotrmtsport. The high values found for the mobility to diffusion coefficient ratio indicate that small quantities of the alkali metals should be susceptible to purification from many solutes by means of electrotransport. PASSAGE of a direct electric current through a liquid metal containing a solute will usually cause a relative motion between the solute and solvent atoms of the alloy. This electrotransport phenomenon may be described experimentally in terms of the mobility of the solute atoms, i.e., the drift velocity of the solute relative to the solvent per unit electric field. In dilute solutions of liquid alloys this relative mobility becomes a measure of the velocity of the solute with respect to the observer since the motion of the solvent is negligible. The mobility is a significant parameter in evaluating the potential usefulness of electrotransport for such things as purification or solute control upon solidification. Prior to around 1958, quantitative data for the mobility of solutes in liquid metals were restricted to some solutes in liquid mercury. Since that time ad- ditional data have been reported for the mobility of solutes in liquid mercury, bismuth, tin, and lead, as shown in Table I. In 1963 Drakin et al.11 reported some values of a transport number for mercury and thallium in molten sodium and potassium. When these values were converted to mobilities, it was found that the mobilities were higher than any of the previously reported values by a factor of around 20, as shown in Table I. Drakin&apos;s experimental technique did not eliminate the presence of back-diffusion and consequently his data were expected to be lower than the true values. The purpose of the present investigation was to determine the mobility of a number of solutes in molten sodium with an experimental technique which eliminates back-diffusion errors. EXPERIMENTAL The technique used to determine the mobility was a resistivity capillary-reservoir technique which had previously been used with a high degree of precision on Sn-Bi alloys.4 This technique consists of dipping the vertical Pyrex capillary cell shown in Fig. 1 into a molten bath of alloy while the bath and capillary are under vacuum. The capillary is then filled by intro-

Jan 1, 1969

By C. Laird, C. E. Feltner

May different kinds of dislocation structures have been observed in strain-cycled metals and alloys. In order to understand their pattern and causes, an experimental program has been carried out to determine the influence on the dislocation structures of the three variables: 1) slip character of the material, 2) test temperature, and 3) strain amplitude. The results show that at high strain amplitudes cell structures me formed when the slip character is wavy, and that these are progressively replaced by uniform distributions of dislocations as the stacking fault energy is decreased. At lower strains, dislocation debris is formed which consists primarily of dipoles in wavy slip mode materials and multipoles in planar slip mode materials. Temperature merely acts to change the scale of the structure, smaller cells, and clumps of dislocation debris being associated with lower temperatures. It is shown that the results for many metals fit this pattern, which Parallels that occurring in unidirectional deformation. DISLOCATION structures produced by cyclic strain (fatigue) have been examined in a number of metals by transmission electron microscopy. These studies have produced a variety of interesting and often seemingly conflicting results. For example, different investigators have reported such structural features as cells.le4 bands of tangled dislocations,4&apos;5 dense patches or clusters of prismatic dislocation loops, planar arrays,4&apos;10 and various combinations or mixtures of these different structures. Most of these observations have been made on materials which were initially annealed and cyclically strained at low amplitudes resulting in long lives. Recently we have reported observations of the dislocation structures produced in copper and Cu-7.5 pct Al cycled at large amplitudes, resulting in lives of less than 104 cycles.4 These results, examined in combination with those in the literature, have suggested that a common or consistent structural pattern exists. Variations in this pattern appear to be determined chiefly by the three variables, namely, the slip character of the material,4,11 test temperature. and the strain amplitude. To verify this interpretation, we have studied [he influence of the above three variables (in different combinations) on the resultant structures in cyclically strained metals. Copper, fatigued at room temperature, was chosen as a reference state to which all other observations can be compared. The effect of slip character has been investigated by employing fcc metals of different stacking fault energy. Thus aluminum which has a more wavy slip character than copper, and Cu-2.5 pct A1 having a more planar slip char- acter, have been examined. The aluminum samples were fatigued at 210°K thus making their homologous temperature equal to that of copper at room temperature. The influence of temperature has been evaluated by examining the structures in copper at room temperature and 78°K. Finally the effect of strain amplitude was studied by looking at the structures at amplitudes giving lives ranging from 104 to 107 cycles. All of the specimens were examined at the 50 pct life level at which stage the structures have reached a stable configuration.12 I) EXPERIMENTAL PROCEDURE Strip specimens, 0.006 in. in thickness, were prepared from base elements of 99.99 pct purity or greater. Specimens were fatigued by cementing the strips to a lucite substrate which was subjected to reverse plane bending. This method of testing has been described e1sewhere.7 After fatiguing, specimens were thinned and examined in a Philips EM 200 which was equipped with a goniometer stage capable of ±30-deg tilt and 330-deg rotation of the specimen. On the basis of separate calibrations,13 allowances were made for the relative rotation and inversions between the bright-field images and the diffraction patterns. II) RESULTS AND DISCUSSION The life behavior of the materials under different test conditions is shown in Fig. 1 in the form of plots of total strain range vs cycles to failure. Comparisons of structures produced in the different materials were made at amplitudes which produced equal numbers of cycles to failure. The influence of strain amplitude on the structures produced in the reference state material (copper tested at room temperature) is shown in Fig. 2. At the 104 life level the structure produced comprises cells similar to those previously observed.3,4 They are approximately 0.5 p in diam and the cell walls are generally more regular or sharper than those produced by unidirectional deformation.14 At the 10&apos; life level the

Jan 1, 1969

By W. T. Roberts, N. G. Turner

A study of the fatigue properties of several grades of commercially pure titanium has established that the strain-aging process is of minor importance in the development of a fatigue limit and a relatively high fatigue strength ratio. Metallographic observations and damping measurements at room temperature indicate that striations are able to spread from grain to grain only at stress levels above the fatigue limit. This suggests that the fatigue limit represents the stress above which large-scale dislocation unlocking takes place. Fatigue tests on annealed material at - 60" and - 196" c showed that under conditions when a thermally activated diffusion process would be suppressed the fatigue limit is not eliminated. Prestraining at room temperature did not have a detrimental effect on fatigue strength at room temperature but a decrease was recorded at — 60°C. This is further evidence that initial dislocation locking is a important strengthening mechanism. TITANIUM and titanium alloys have S-N curves with a definite fatigue limit, and a high ratio of fatigue limit to UTS can be attained. Other materials which show similar fatigue characteristics are mild steel and some Al-Mg alloys. The fatigue limit of these materials has been associated with their strain-aging capacity. It is well-known that commercial-purity titanium contains interstitial impurities which can give rise to a sharp yield point, and a small strain-aging effect following static strain has been demonstrated.7 This type of aging reaction is differentiated from the dynamic aging process when aging occurs during plastic deformation, and which is generally observed at elevated temperatures. In a titanium at room temperature, dislocation locking is associated with the interaction of interstitial oxygen, nitrogen, and carbon atoms with dislocations. Ehr-lich has shown that the distortion produced by introduction of these atoms into the hcp lattice has no shear stress component and hence there is no interaction between the stress field and the screw component of a dislocation. Thus the dislocations as a whole are only weakly locked. It is clear that strain-aging effects in hcp a titanium will be much less pronounced than those observed in bcc iron and steel. In recent years, the attribution of the fatigue limit solely to strain aging has been questioned. It has been pointed out that a definite fatigue limit is observed at temperatures as low as -196°C in some titanium alloys,&apos; and strain aging is not expected to be effective at this temperature. The role of initial locking of dislocations in determining fatigue behavior has been examined in low-carbon steel by Oates and Wilson. They showed that under conditions in which the aging potential is low the factors which control the buildup of local stresses and hence affect dislocation unlocking, e.g., grain size, are important. There are indications that other metals can have a definite fatigue limit with no established strain-aging capacity, an example being magnesium12 which has the same crystal structure as a titanium. The spread of plasticity from grain to grain in hexagonal metals may be more difficult than in cubic metals because of the limited number of slip systems in the former, and this may account in part for their fatigue behavior. The present work was undertaken to elucidate the relative importance of crystal structure, strain aging, and initial dislocation locking in determining the properties of commercially pure titanium when subjected to cyclic stressing. 1) EXPERIMENTAL METHODS Three grades of commercial-purity titanium were used and a material of lower interstitial content was prepared by melting high-purity Japanese sponge titanium (referred to as H.P. Ti). The compositions and typical mechanical properties of the materials are shown in Table I. Fatigue tests were made in push-pull (zero mean stress) using an Amsler Vibraphore machine at a frequency of about 160 cps. Two types of fatigue specimen were used—one with a waisted gage length for determination of S-N curves and the other with a parallel gage length for metallographic studies and damping measurements. After careful machining and mechanical polishing, all specimens were electropolished prior to fatigue testing. The electrolyte consisted of 10 parts methyl alcohol, 6 parts 2-butoxyethanol, and 1 part perchloric acid (SG 1.54) and it was maintained at a temperature of -10" to -20°C during polishing. Tests at room temperature were normally carried out with the specimen immersed in a silicone oil bath which could be heated for elevated-temperature tests.

Jan 1, 1969

By J. C. Bierlein, R. A. Dodd

Endurance strengths at 10&apos; cycles, fatigue-hardening rates, and endurance strength/0.2 pct proof stress ratios have been determined jbr a range of Cu(Ni), Cu(Si), and S.R.0. Cu(Au) solid solutions. Some douht is cast on simple cross slip models of fatigue hardening in view of opposite composition dependencies of hardening displayed by Cu(Si) and Cu(Au). The temperature dependencies of hardening also are the opposite of predictions made on the basis of a cross slip model. A correlation apparently exists between the fatigue strength/0.2 Pc~ proof s1.re.s~ ratios and rates of fatigue hardening. An increase in PS/PS due to alloying or temperature change is accompanied by a decrease in hardening rate, and vice versa. In recent years there has been much interest in the determination of the dislocation structure of fatigued metals and alloys. The accumulated evidence, e.g., Refs. 1 to 5, suggests that the structure may be dependent on the stacking fault energy, 7, of the fatigued metal in the same way that fatigue hardening rates have also been shown to apparently depend on u .6&apos; 7 The above research followed the various earlier theories relating crack nucleation to ease of cross slip, e.g., Refs. 8 to 131 so "ggesting that y may indeed be the parameter of principal significance in all facets of the fatigue process. However, comparatively little attention has been paid to correlating engineering fatigue data with observations of the above type. Certainly, it would be useful if potential engineering fatigue performance could be assessed from a knowledge of easily determined alloy properties, and the present research originated from this standpoint. TO investigate the widest Possible range of 7 would require the use of two solvent bases, e.g., aluminum and copper, but a reasonable coverage can be provided by copper-based solutions alone. Therefore, it was decided to work with Cu(Ni) and Cu(Si) solid solutions, the approximate stackillg fault energies of which are given in Table I. The y range extends from low, Cu(7.5 at- Pet Si), to moderately high in Cu(2-5 at. ~ct ~i) and two of the Cu(Ni) alloys. The values listed in Table I should be regarded as qualitative only, being derived as follows. Dillamore and smallman14 quote a value of 85 i 30 erg.cm-2 for the stacking fault energy of pure copper, based on an earlier value due to Howie and swannl5 corrected by Brown&apos;s formula.&apos;&apos; Since the ratios (alloy)h(pure copper) have been reported17,18 for Cu(Ni) alloys containing up to 30 pct Ni, approximate ) values for these alloys can be computed, and a rough estimate of 7 for Cu(50 at. pct Ni) obtained by extrapolation. The relatively low y value obtained in this way for Cu(50 at. pct Ni) coincides with the observation of Nakajima19 that the stacking fault probability is a maximum at this composition. Likewise, the y values for the three ~u(~i) alloys are estimates based on values given by Swann and Nuttingo corrected on the basis Of Brown&apos;s estimate that the true 7 values are probably 2.3 times greater than those originally computed. In addition to the above alloys it was decided to investigate short-range ordered (s.R.O.) CU(AU) alloys containing up to 25 at. pct Au. This last alloy has been shown to have a well-defined planar arrangement of dislocations when deformed,21,22 probably due to cross slip being restricted by the S.R.O. Engineering fatigue data was to be represented by the determination of endurance strengths, and these were to be correlated with fatigue hardening and mechanical property data. EXPERIMENTAL I, order to study the desired properties and property changes, the following alloys were prepared: Cu(2.5 at. pct Si), Cu(5.0 at. pct Si), Cu(7.5 at. pct Si), Cu(5.0 at. pct Ni), Cu(25.0 at. pct Nil, Cu(50.0 at. pct Ni), Cu(5.0 at. pct AU), Cu(15.0 at. pct AU), Cu(25.0 at. pct AU). The copper and gold were zone-refined, while the silicon was semiconductor grade. The nickel was of 99.95 p,t. purity.* All alloys were induction-melted in a *Kindly supplied by the International Nickel co. helium atmosphere, appropriate precautions being taken to avoid segregation in the Cu-Au series. Rod stock was obtained by rolling and swag,ng. A few Bridgman single crystals were grown for fatigue-hardening studies, but most material was machined into polycrystalline fatigue speciments of the design shown in Fig. 1, and into polycrystalline tensile and fatigue-hardening specimens of simple cylindrical design. All specimens except Cu(Au) were annealed; the latter were quenched from above T, to produce short-range order. A few of the quenched alloys were examined for long-range order by step-scanning over

Jan 1, 1969

By G. H. Bishop

The kinetics of the inter granular penetration and embrittlement of [100] tilt boundaries in 99.998 pct pure nickel upon exposure to bismuth-rich Ni-Bi liquids have been determined in the temperature range from 700° to 900°C. The kinetics of penetration are parabolic in time at constant temperature over most of the temperature range. In a series of 43-deg bicrystals the rate of penetration is anisotropic with respect to the direction of penetration into the grain boundaries. In lower-angle bicrystals the penetration rate is isotropic. The rate of penetration decreases with tilt angle at 700°C. The activation energy for penetration in the 43-deg bicrystals is 42 kcal per g-atom independent of direction. It is concluded that the intergranular penetration and embrittlement in the presence of the liquid proceeds by a grain boundary diffusion process and not by the intrusion of a liquid film. This was confirmed by a determination that the kinetics of penetration and embrittlement were the same in the 43-deg bicrystals upon exposure to bismuth vapor under conditions such that no bulk liquid phase would be thermodynamically stable. WhEN solid metals are exposed to a corrosive liquid-metal environment, the grain boundaries are sites of preferential attack. Depending on the temperature, the composition of the liquid, and the composition, structure, and state of stress of the solid, a number of modes of attack are possible. This paper reports a study of the kinetics of intergranular penetration and embrittlement of high-purity nickel bicrystals upon exposure to bismuth which, together with an earlier study by Cheney, Hochgraf, and Spencer,&apos; demonstrates that there are at least two modes of intergranular attack possible in the Ni-Bi system. In the study by Cheney et al., columnar-grain specimens of 99.5 pct pure nickel were exposed to liquid bismuth presaturated with nickel in the temperature range 670" to 1050°C. They found that the majority of the boundaries, which were predominantely high-angle boundaries, were penetrated by capillary liquid films, the attack proceeding by a process which will be termed grain boundary wetting. This process occurs in a stress-free solid when twice the liquid-solid surface tension is less than the surface tension of the grain boundary,* i.e., when 2yLs < YGB In this case the penetration of the grain boundary by the liquid occurs at a relatively rapid rate, resulting in the severe embrittlement of a polycrystalline solid. Grain boundary wetting is a common mode of intergranular attack in systems in which the lower melting component is relatively insoluble in the solid, but the solid has an appreciable solubility in the liquid, for example, the Ni-Bi system, Fig. 1. In systems of this type at temperatures above the range of stability of any intermetallic phases, once the liquid is saturated with respect to the solid so that no gross solution occurs, chemical gradients are small, and surface tensions become major driving forces for attack, provided the solid is stress-free. The results of Cheney et al. appear to be typical of those encountered when grain boundary wetting occurs.&apos; Capillary films were observed in the boundaries after quenching from the exposure temperature. The mean depth of penetration increased linearly with time, and the activation energy for the process was found to be 22 kcal per g-atom. In a study of the Cu-Bi system Yukawa and sinott4 found that the depth of penetration of bismuth into high-purity copper bicrystals of orientations from 22 to 63 deg of tilt about (100) at 649°C ranged from 0.05 to 0.25 in. after a 12-hr anneal. This corresponds to a linear rate of 6 to 15 X 10~6 cm per sec. At the same reduced temperature of 0.68 the rate for the Ni-Bi system&apos; was 7 x lo-&apos; cm per sec. In another study of the Cu-Bi system, Scheil and schess15 determined the kinetics of grain boundary wetting in hot-worked commercial rod. While there were several complicating factors present in this study, there is general agreement with the above results. The kinetics of penetration were linear, the activation energy was 20 kcal per g-atom, and at 650°C the rate of wetting was 2 to 5 x 10-6 cm per sec. The rate of wetting in the A1-Ga system6 is somewhat

Jan 1, 1969

By Che-Yu Li, J. L. Gregg, W. F. Brehm

Oriented, oxygen-doped niobium bicrystals were tested in liquid lithium. The grain boundaries were attacked preferentially. The depth of the penetrated zone varies as (time)2. The penetration was aniso-tropic, had a high activation energy, and increased with the increased oxygen doping level. A possible model was proposed to account for the experimental observations. 1 HE grain boundary penetration of a metallic system by liquid metal has been studied by several investigators. Their results are summarized by Bishop.&apos; Most of these works show that the penetration by liquid metal corresponds to the phenomenon of liquid metal wetting. In the case of a grain boundary, wetting will occur when twice the solid-liquid interfacial tension is smaller than the grain boundary tension resulting in the replacement of the grain boundary by two new solid-liquid interfaces. Other possibilities exist; for example, the atoms of the liquid metal may diffuse into the grain boundary region due to chemical potential gradient. The gradient can be produced by impurity segregation or simply be due to the increase in solubility in the grain boundary region. The penetrated grain boundary in these cases may remain solid at the test temperature. The Nb-Li system has been of considerable interest because of its possible technological applications. For fundamental interest it provides a possibility of studying the grain boundary penetration process which is not controlled by the wetting mechanism. The pure niobium is not attacked by the liquid lithium, but if niobium containing more than 300 to 500 ppm oxygen by weight is exposed to liquid lithium, corrosion occurs at the solid-liquid interface and preferentially at grain boundaries. Previous investigators2-&apos; have proposed that this preferential corrosion at grain boundaries is caused by oxygen segregation there, with subsequent inward diffusion of lithium to form a Li-Nb-0 compound. These investigators also found that the corrosion could be retarded by adding 1 pct Zr to the niobium to precipitate the oxygen as ZrO2 upon proper heat treatment. However, there are no quantitative data on the kinetics of the grain boundary penetration process to test the validity of the proposed corrosion mechanism. In this work an investigation of this penetration process in oriented bicrystals was made as a function of the oxygen doping level in the bulk niobium and the grain boundary orientation. A possible model for the penetration process based on the experimental results was proposed. EXPERIMENTS Oriented niobium bicrystals were grown by arc-zone melting oriented single-crystal seeds.7 These bicrystals contained simple tilt boundary. The [001] directions in the two grains were tilted about a common [110]. The bicrystals were 31/2 in. long and 5 by 4 in. in cross section with the straight, symmetric, planar grain boundary longitudinally bisecting the crystal rod. The bicrystals were doped with oxygen by anodically depositing a layer of Nb2O on the surface in a 70 pct HNO solution at 100 v, using a stainless-steel cathode. The specimens were homogenized by annealing in evacuated quartz tubes at 127 5°C. Oxygen content of the niobium was measured from microhardness values, after DiStefano and Litmman.&apos; Supplementary checks were made with vacuum-fusion analysis.7 Individual test specimens cut from the doped bi-crystal rods, about by by % in. in size, were tested inside double jacket sealed capsules. The inner jacket was niobium, the outer was stainless steel. The niobium inner jacket eliminated the problem of dissimilar-metal mass transfer.&apos; The lithium (99.8 pct pure, obtained from Lithium Corp. of America) was handled only in a purified argon atmosphere in a Blickman stainless-steel glove box. After introduction of lithium, the capsules were sealed by welding. Further detailed experimental procedures are given in Ref. 7. The capsules were heat-treated in vertical Marshall resistance furnaces. Temperatures were controlled to When heating above 1100°C, it was necessary to seal the furnace work tube and flow argon through to prevent failure of the stainless-steel outer jacket of the capsule. Tests were made on 6" 2", 16" 2, and 33" i2" bicrystals at oxygen levels up to 2600 ppm by weight in the 6&apos; and 16" crystals and with 1300 ppm oxygen in the 33&apos; crystals. The oxygen levels were controlled to 100 ppm. Most of the quantitative data were obtained from 16" bicrystals between 800" and 1050°C. The capsules were quenched into water after the test and cut open with a water-cooled abrasive wheel. The capsules were then submerged in water, which dissolved the lithium and freed the specimen. Measurement of the depth of the penetrated zone in the grain boundary was done either on metallographically prepared surfaces or directly on the grain boundary plane after the specimen was fractured in tension in the grain boundary plane. The depth of penetration measured by both methods agreed well. Further details describing these techniques have been reported elsewhere.&apos;p7

Jan 1, 1969

By C. Wert, G. Mah

A relaxation peak thought to be due to the presence of C-C pairs in cobalt has been observed. It exists both above 420"C, where cobalt has the fcc structure, and below 420"C, where cobalt has the hcp structure at equilibrium. The effect is thought, however, to be caused by motion of C-C pairs in the fcc phase in both instances; enough retained fcc phase was deduced to be present at temperatures below 420°C to make the phenomenon possible. Measurements of the aniso-tropy of the effect in single crystals of various orientations of fcc phase showed the effect to have a maximum value in longitudinal strain for a [loo] crystal and a minimum value for a [Ill] crystal. This observation seems to rule out the possibility of (110) nn pairs being responsible for the effect. From measurements of the strength of the relaxation in the alloys, we reach the conclusion that both the binding energy of the pairs and the specific relaxation per pair are smaller than corresponding quantities for interstitial pairs in bcc metals. DETERMINATION of the details of atom placement of small atoms such as carbon, nitrogen, oxygen, and hydrogen in metals has been a difficult problem. In certain alloys such as martensite extensive departure from random placement of the interstitials can be deduced from X-ray diffraction off the atoms of the host metal, but such diffraction techniques are of small help for small departures from randomness. A technique which does offer promise in the latter instance is the anelasticity of these interstitial alloys. Most previous investigations using this property have utilized alloys in which the solvent is one of the bcc metals, alloys such as These studies have been interpreted to show that an interaction exists between interstitials which causes them to form clusters in more than random numbers; the binding energy of interstitials in such clusters has been deduced to be about 0.1 ev per atom (for small clusters of size two to four atoms). Similar investigations have been carried out on close-packed solvent metals, Ni-C by and Diamond and Ag-O by Papazian.8- In both of these svstems. no relaxation of the singly dissolved interstitial is expected, so an-elastic behavior of the interstitials must be caused by their association in some cluster or complex of non-cubic symmetry. Since relaxations in these alloys were observed to have a strength which varied about as the square of the interstitial concentration, the effect was deduced to be caused predominately by motion of i-i pairs in the crystal. A striking difference is observed in relaxation strength of interstitial alloys between the bcc and fcc systems. The specific effect per interstitial atom is much larger for the alloys in the bcc crystals than for those in fcc crystals. Comparing clusters of size two in the Nb-O system4 and the Ni-C system,7 one finds the magnitude of the anelastic effect per interstitial atom in the former to be some 100 times greater than that in the latter. Such a difference in relaxation strength might be caused by a difference in concentration of the pairs (this means a higher binding energy in the bcc crystals). It might also be caused by a large difference in shape factor of the elastic strain field about the pairs between the two cases (a much more noncubic shape factor would be required for the bcc crystals). This investigation was undertaken to examine the possibility of C-C pair formation in alloys of cobalt and carbon using anelastic effects. Since cobalt has both fcc and hep phases, it seemed to offer the chance that measurements over a range of frequency might permit comparison of properties of pairs in the two crystal types. Although this goal was not reached, several significant facts were deduced from the observations. 1) An anelastic phenomenon believed to be associated with the presence of C-C pairs in cobalt exists. It has many features in common with that observed in nickel. 2) The effect is thought to be caused by pair motion in the fcc phase. 3) Calculations of the relaxation strength A, which includes as a parameter the product of the pair concentration, C, and the square of the shape factor &apos;, show that this parameter is much smaller in the CO-C alloy system than in the interstitial alloys in the bcc systems. 4) From this finding, we reach the conclusion that both the binding energy of C-C pairs in cobalt and the specific relaxation strength per pair are small compared to corresponding values for such pairs in the bcc systems. 5) The crystalline anisotropy of the effect permits the identification of reasonable geometrical models of close C-C pairs. I) EXPERIMENTAL PROCEDURE A) Method of Measurement. The anelastic measurements-—all of which were constant frequency measurements of internal friction—were designed to study the expected phenomenon in both the hcp and fcc structures in cobalt. Knowledge of similar measurements in Ni-C alloys led us to believe that the damping peak should occur below the transformation temperature for frequencies near 1 cps and above for frequencies near 100 kcps. This surmise was correct. The low-frequency measurements were made on wire specimens using a vacuum torsion pendulum; the damping peak was found at about 2&apos;70°C at a frequency of 1 cps. Because of large superimposed damping of magnetic origin at this temperature, a longitudinal magnetic field of about 1500 oe was applied to the

Jan 1, 1969

By H. T. Shore, J. M. Schultz

A number of experimental rnethods—X-ray powder diffractometry, Laue photography, X-ray small-angle scattering, and transmission electron microscopy and dijfraction—have been utilized to examine the morphology associated with precipitation from the terminal, g, solid solution of a Zn-1 pct Cu alloy. A significant age hardening was observed in a 1 pct Cu alloy. X-ray and electron diffraction results showed that the structural inhomogeneities associated with the hardening were isotructural with the matrix. The average size and shape of the inhomogeneities were deduced from the electron microscopy and X-ray small-angle scattering. The preprecipitates are hexagonal platelets some 300? in diam. and some twelve unit cells thick. The orientation of the platelets was deduced from Laue photographs and electron diffraction. The platelet plane is (0001). When a large amount of pre-precipitation is present in a localized volume the new lattice is often disoriented by a rotation about (0001) of of the matrix. WhILE dilute Zn-Cu alloys have been commercially important for some 50 years, relatively very little is known metallographically about this material. The "Zilloys", zinc with about 1 wt pct Cu and sometimes a small addition of magnesium, are used to produce rolled zinc which is harder and stronger than that produced by other rollable zinc alloys.&apos; According to the phase diagrams of the zinc-rich side of the Cu-Zn system, such dilute Zn-Cu alloys should age-harden;2-5 the solubility of copper in zinc, g-phase, at 424°C is 2.68 pct, while at 0°C it is only to 0.3 pct. However, the published literature on the aging of this system appears to be limited to a documentation of the contraction of 1, 2, and 3 pct Cu alloys aging at 95°c,6 and an attempt to measure changes in lattice parameters during aging.&apos; In the latter work, no lattice parameter changes were detected, although a broadening of the highest-angle lines was detected and considerable diffuse scattering was observed. Micro-structural investigations have been limited to the latest stage of aging, wherein Widmanstatten precipitates are formed.3,47 These alloys are of interest for still another reason. The two most zinc-rich phases in the Cu-Zn system, 77 and E, are both hcp. Moreover, the change in a, between 17 and t for a 1 wt pct Cu alloy is onlv 3.64 -,~ct: the change in Co is 12.0 ict. It would be anticipated that precipitation in such a material might occur through metastable phases or G.P. zones with epitaxy along mutual 0001 planes. The goals of the present work are aimed at partially filling the void of knowledge concerning the early stages of precipitation from the g phase. In particular, we have attempted to document the magnitude of the age hardening of this system and to determine the size, shape, and orientation within the matrix of the elements of precipitation in an early stage of condensation. EXPERIMENTAL A) Specimen Preparation. Specimens were prepared In two somewhat different ways, one method being used for X-ray Laue and diffractometer measurements, optical microscopy, and Rockwell hardness measurements and the other used for electron microscopy and X-ray small-angle scattering. In the first case zinc and copper in the proper proportions to yield a 1 wt pct Cu alloy were melted together in a closed graphite crucible. Castings so made were free of apparent segregation or oxidation. The castings were then solution-annealed at 400°C for several days and then quenched in water to room temperature. Filings of portions of the specimens were made for use as X-ray powder diffractometry specimens. The electron microscope material was made as follows. Castings were made under vacuum with copper powder placed inside a hollow zinc cylinder to insure good contact of the materials. These 1 wt pct Cu pieces were then rolled to 0.1 mm with an intermediate anneal in vacuo. The rolled sheets so formed were then annealed for about 6 hr at 225°C. Finally the specimens were electropolished slowly until thin enough for transmission electron microscopy. The polishing is discussed in greater detail in the Results section. B) Measurements. X-ray measurements of three types were performed. A G.E. XRD-5 diffractometer was used to examine powders of the alloy for identification of second-phase material. A Kratky small-angle camera, also operating from a G.E. tube, was used to investigate the sizes of small precipitate particles. In both cases, nickel-filtered copper radiation was utilized. Finally, individual grains of the large-grained castings were examined in the back-reflection Laue geometry. Electron microscope studies were carried out with a J.E.O.L. Model 6A instrument. RESULTS A) Hardness Measurements. Hardness measurements performed at room temperature on the large-grained polycrystalline specimens showed a hardening which was essentially complete in 3 hr. Fig. 1 shows a typical plot of hardness vs aging time. The relative magnitude of the ultimate hardening varied from run to run between 150 and 200 pct of the value for the material immediately after quenching from the solution anneal. Most probably the variations reflect small changes in the time taken to remove the specimen from the vacuum furnace after the solution anneal.

Jan 1, 1969