By Ningchuan Feng

A biosorbent, the chemically modified orange peel, was prepared from hydrolysis of the grafted copolymer, which was synthesized by interacting methyl acrylate with cross-linking orange peel, and FT-IR spectroscopy was used for determining the structure of the biosorbent. Adsorption characteristics and effects of various factors of the biosorbent on Cu (II) were investigated including pH, adsorption time and initial concentration of Cu (II). Experiment results show that when pH was 6.0 and the initial concentration of Cu (II) was 50mg·L-1, the removal rate was 91.7% after 3 h adsorption. After four cycles being reused, 85.3% removal rate could be obtained by the biosorbent.

Jan 1, 2008

By Andrew Shabalin, Vladimir Skorohodov, Svetlana Babaeva, ?lga Makovskaya

"At processing of some kinds of wastes (electronic scrap, secondary materials, spent nuclear fuel) in nitric acid solutions, and also in technology of silver refining, the significant amounts of palladium and platinum passes into a solution. The ion-exchange concentration of palladium and platinum in nitric acid solutions (5-500/dm3) are investigated. More than 30 various classes of ionites are tested. The most chemically resistance resins at the given conditions are identified. It is shown, that the maximum sorptive capacity to studied metals at high acidity the complexing, synthetic and inorganic sorbents possess. To definition of platinum metals sorption optimum conditions the kinetics is studied, isotherms of a sorption at various parameters from nitrate solutions are obtained. The conditions of the platinum and a palladium desorption from the pregnant sorbents and its regeneration with the subsequent reuse of materials were defined. The raw materials containing precious metals have very diverse composition and physical properties. Commonly the materials are processed by hydrometallurgical way. If gold or PGMs there are in raw materials to its opening hydrochloric acid solutions are applied. As an oxidizer nitric acid, hydrogen peroxide, gaseous chlorine, etc are used. Nevertheless, at processing of argentiferous materials and preliminary treatment of a waste including the spent nuclear fuel, nitric acid solutions are often used and the specified metals in some extent pass into solution [1]. Therefore selective extraction of PGMs from nitrate solutions is an actual problem. In the present work the ion-exchange concentrations of palladium and platinum in nitric acid solutions (5-500 g/dm3) are investigated. At the testing more than 30 various classes of ionites the most chemically resistance resins at the given conditions are identified. These resins are synthesized on the base of polyacrylate, styrene-divinylbenzene and vinylpyridine. For a selection of the most effective resin among what are made in Russia and overseas, a number of ionites with various functional groups were studied. Influence of functional groups type on a PGM sorption is shown for extraction of a palladium as an example (table 1). The presented data shows, that palladium concentration in a phase of ionites depends on sorbent type. If the increasing of solution acidity essentially reduces palladium sorption by sulfonic cation-exchange resins (KU-2×8) than its sorption by strongly basic anionites is approximately equal. Intermediate position is occupied by complexing sorbents. The latter (AN-31, SN-3, ANKB-35, Lewatit TP 207, Purolite S 930) are the most effective for extraction of PGMs from nitrate solutions from the point of view of capacity value. According to [2], solution behavior of Pt (II) and Pd (II) are similar. As is known from coordination chemistry, ligand environment of the metal ions substantially impacts to character of electronic spectra. The figure 1 shows the results of measurements of optical density of platinum bearing solutions with various concentration of nitric acid at ?=400 nanometers"

Jan 1, 2008

By Wenjie Zhu

Chromite ore processing residue (COPR) is a hazardous waste containing high concentration of chromium. We describe here a pioneer trial of detoxification of COPR in column reactor with an indigenous chromate reducing bacterium Leucobacter sp. Ch1, which showed high chromate reducing ability at high pH. Under the optimum conditions, at 30°C and pH 10.0, pH of leachate decreased from 10.3 to 8.3, and Cr(VI) concentration in solution decreased to zero mg L-1, and 76.4% of Cr(VI) was removed from COPR samples. The leaching toxicity of detoxified residue was 1.1 mg L-1 that was lower than national standard of China.

Jan 1, 2008

By E. Saez, M. Bellet, T. Coupez, O. Jaouen

"The paper presents a 3D finite element solver for non-steady state fluid flow. The thermomechanical simulation package REM3D® has been initially developed to model Stokes' flow for polymer injection. The mechanical module is based on a Eulerian velocitypressure formulation. The spatial discretization uses P 1+IP1 tetrahedral elements. The front tracking module consists of the resolution of a transport equation, thanks to a space-time discontinuous Galerkin formulation. It includes mesh adaptation, which permits a dynamic refinement at the front, thus controling the numerical diffusion. The same approach is used to solve heat transfer. In this paper, we focus on the specific adaptations done to treat Navier Stokes flow. The treatment of inertia is detailed, as well as the implementation of sliding conditions at mould surface, using conservative normals. Industrial applications are presented.IntroductionThe study of the mould filling stage in casting processes requires the ability to simulate complex non steady-state three-dimensional flows. Most commercial software use the volume of fluid (VOF) method, associated with a Eulerian formulation, see for instance the series of conferences ""Modelling of Casting, Welding and Advanced Solidification Processes"" [1-3]. The VOF method [4] consists in solving the conservation equation dF / dt = 0 for a variable F - the volumic fraction of fluid - whose value is 1 in filled regions and 0 elsewhere. Two fluids are actually considered: the molten alloy and a gas in the empty regions. This method suffers generally from numerical diffusion in the resolution of the free surface tracking equation, which is of pure advective type. The precision of the computation is then strongly dependent on the mesh density. Since the mesh is fixed (Eulerian formulation) this implies that in case of complex flow the user must have a priori a fairly good idea of the flow characteristics in order to capture properly the critical features of the flow. In addition, the method can hardly handle the discontinuity of the material viscosity at the interface. To prevent this difficulty, the viscosity value is smoothed around the interfuce, adding once again some inaccuracy. Since the value F = ½ is supposed to represent the free surface, it results in a smeared fluid surface. An alternative to the fixed mesh methods are the methods in which the mesh covers the fluid domain only, as proposed by Navti and Lewis [5-6], or Gaston and Bellet [7]. Based on updated Lagrangian schemes, they must be associated with an ALE formulation (arbitrary LagrangianEulerian) in order to reduce the number of full remeshing operations."

Jan 1, 2004

By J. M. Toguri

The viscosity of the molten FeO-Fe2O3-Si0z system in the composition range of interest to copper smelting has been investigated using a rotating cylinder technique. The silica content of the slag was varied from 20 to 35 wt percent while the oxygen pressure of the system was varied from 10-7 10-11 atm. The temperature range investigated was from 1200 to 1350°C. It was found that the viscosity of the slag generally decreased with increasing temperature and increasing oxygen pressure. As the silica content was increased, the viscosity was found to increase.

Jan 1, 1976

By W. G. Davenport

The Cu content of industrial flash furnace concentrates varies considerably. It is usually around 30% Cu (Tables 2.1, 3.1) but it may be as high as 55% Cu and as low as 20% Cu. The mineralogy of flash furnace concentrates also varies. The most common Cu mineral is chalcopyrite (CuFeSz), but many concentrates contain bornite (CuSFeS4), chalcocite (CU2S), covellite (CuS) and even native copper (CUO). Pyrite (FeSz) :is also present in many concentrates. This chapter examines how concentrate composition affects flash smelting -with specific reference to 'low-Cu-grade' FeS2-CuFeSz concentrates. Chapter 14 does the same with 'high-Cu-grade' CuzS-CuFeSz?concentrates.

Jan 1, 2001

By Jordan Mayorga, Joseph Kopp, Robert Boehm, Daniel P. Cook

"Solar generated power has long been considered a useful energy source only for low-energy density and non-mission critical use, such as providing electricity for residential applications. The success of Concentrating Solar Power (CSP) facilities, such as the 64 MW Nevada Solar- 1 near Las Vegas, have demonstrated that solar does have application to high energy density industries such as materials and chemical production. This paper will discuss the current operating con_guration of the Solar-1 facility and show how proposed modi_cations, such as addition of thermal storage and use of liquid salts as the working uid, can further improve the e_ciency and energy production of the plant.IntroductionThe United States as a nation is the largest consumer of energy in the world at an estimated 29 trillion kWh per year[1], which is roughly 15% of total global energy consumption[2]. On a per capita basis, the United States also leads most of the world, using an average of 96,000 kWh per person[3]. Roughly 40% of the energy consumed in the United States was produced from petroleum, 23% from coal, 23% from natural gas, 9% from nuclear and the remaining 5% from renewable sources such as solar, geothermal, wind, and hydroelectric[1].Energy demands associated with the industrial-scale production of chemicals and materials is a signicant portion of the United States total energy consumption. Roughly 33% of the energy consumed in the United States is used by the industrial sector, with 22% of this amount used in chemical production, 16% used in petroleum rening, and 14% used in the smelting and rening of metals[1]. Energy costs are also a signicant, if not the most signicant, portion of the total production costs for many materials. For example, roughly 30% of the cost of producing aluminum is the electricity used in the Hall-Heroult process [4], while the cost of energy is roughly 15% of the total cost of producing steel products [5].The primary sources of power for the industrial sector have been coal, petroleum, hydro- electric and nuclear. The use of alternative energy sources, e.g. solar, wind, geothermal, for industrial materials production has been slow in coming because they are intermittent and low-energy density sources, i.e. no solar power at night, no wind power when the air is still, etc. The success of Concentrating Solar Power (CSP) facilities, such as the 64 MW Nevada Solar-1 (NS-1) near Las Vegas, have demonstrated that solar can have application to high energy density industries such as materials and chemical production.This paper will discuss the current conguration of the NS-1 facility, and potential modications to the facility that will increase both its power e_ciency and power density."

Jan 1, 2010

By Xiang-ning Meng, Miao-yong Zhu

"A three-dimensional finite-element heat-transfer model is conducted to predict temperature of hot copper plate in a slab continuous casting mold and the effect of casting speed on temperature difference between copper plate and solidifying shell is simulated in combination with process data. The results show that centre temperature of hot copper surface at casting speed 1.8 m·min-1 and 2.0 m·min-1 are higher than that of 1.6 m·min-1 casting speed 4.7-5.2 °C and 11.2-12.2 °C respectively and temperature is not increased linearly with casting speed. Temperature difference in meniscus between mold and shell is influenced obviously by casting speed and increased 4.0- 6.0 °C with increment of casting speed 0.2 m·min-1• Fluctuation of temperature difference in meniscus is a main reason to deteriorate casting quality as increasing casting speed.IntroductionIn conventional continuous casting of steel, a large amount of sensible and latent heat of molten steel dissipates in primary cooling zone and mold becomes a critical component of caster to govern steel quality, meanwhile, thermal load on mold is increased constantly and environment is also more abominable since high productivity and quality are required and high-effective technologies are applied. So, an in-depth understanding of thermal behavior of mold at high casting speed is essential to design cooling structure and maintain casting stability. Many studies have been carried out to shed light on thermal behavior in mold. Chow et al. [l] applied a mathematical model to heat transfer in billet mold at a high casting speed to give a new taper in order to minimize mold-strand interaction. Thomas et al. [2] researched relation between mold geometry and temperature distribution based on a finite-element heat-transfer model. Lu et al. [3] indicated that slab mold temperature are mainly affected by thickness of copper plate and nickel layer by a heat transfer model. Samarasekera et al. [4, 5] researched temperature of copper plates for both billet and slab molds and effect of a large number of factors ranging from water quality to casting speed. Park and Thomas et al. [6, 7] developed a finite-element thermal-stress model to determine temperature and thermal distortion and stress in both thin and slab molds and O'Connor et al. [8] applied an elastic-plastic-creep finite-element model in a funnel shaped mold to achieve same goals. Cicutti et al. [9] evaluated heat transfer and temperature fluctuation in a slab mold and proposed an expression to predict global heat flux as a function of process parameters and an index to quantify thermal instability. All mentioned above shown that thermal behavior is not only important to casting stability, it is also premise to further understand mechanical behavior in mold."

Jan 1, 2011

By Upali Siriwardane, Tushar V. Kudale, Naidu V. Seetala

"Cellulose acetate (CA) membranes with 25% triethyl citrate (TEC) as plasticizer were prepared with varying thickness for CO2 gas separation from water-gas-shift (WGS) reaction products. The AFM analysis of the CA membrane showed that the uniform coating had fewer and smaller pores as the film thickness increased, and corroborated by gas permeability studies. The CO2 permeability has decreased faster than CO permeability with the CA/TEC membrane thickness, and findings support that the CA membrane could be used to entrap CO2. Several CA/TEC membranes were also staked to increase the separation efficiency. Positron Annihilation Lifetime Spectroscopy (PALS) was used to estimate the nano-porosity (pore size and concentration) changes of CA/TEC films. PALS results show a decrease in pore size with increasing CA-TEC concentration in acetone, while the pore concentration increases. The PALS results are correlated with the CO2/CO permeability variations as the CA-TEC concentration change.IntroductionHydrogen is one of the main energy sources available for the future advancement of clean fuel technologies especially for fuel cells. Generation of hydrogen and CO2 from Water Gas Shift (WGS) reaction mixtures of CO and H2O is of interest to many researchers since it allows a large scale production of hydrogen [1, 2]. Once hydrogen is produced using the WGS reaction, the output products contain mixture of CO, CO2, H2, and water vapor. Metallic membranes have been used as hydrogen separation membranes [3-6]. As H2 is separated from the mixture using the metal membranes, we need to separate CO2, and find ways of sequestration of CO2 to avoid environmental problems by greenhouse gasses. Polymeric Membranes have been used for CO2 separation [7]. Plasticizer can control the micro-structural properties such as pore size and concentration of polymer membranes [8], which influence the size/molecular weight dependent diffusion rates of the gas molecules. We have used cellulose acetate with triethyl citrate as plasticizer to separate CO2 from the WGS reaction products. Positron annihilation lifetime spectroscopy (PALS) is very sensitive and able to identify different kinds of defects and their agglomerates such as vacancies, vacancy loops, and voids [9, 10]. PALS has been successful in determining the free volume in polymers that influence the properties of the polymers [11, 12]. Microscopic properties of the free volume obtained from PALS have been correlated to macroscopic properties [13, 14]. We used PALS to study the nanoporosity (pore size and concentration) and fractional free volume changes of CA/TEC films, and used to understand the variations observed in the CO2/CO permeability as the CA-TEC concentration in the membranes change."

Jan 1, 2014

By Yanhui Liu, Xuewei Lv, Chenguang Bai

A thermodynamic model for determining the surface tension of molten slag by considering the surface tension and molar volume of the pure oxide component, and their ionic radii was extended to the slag bearing high TiO2 (varying from 80 to 67%) at 1973 K. The iso-surface tension curves for the FeO-TiO2-Ti2O3 ternary system at 1973 K are almost parallel to the FeOTi2O3 line. TiO2 plays a role of surface-active solute, and its surface-active effect is attenuating with increasing the TiO2 content. The iso-surface tension curve shifts away from the TiO2 corner, indicating that the surface tension of the ternary slag decreases along with the addition of SiO2. The reasons include the addition of SiO2 with lower surface tension and the decrease of the total ion moment at the surface. Both CaO and MgO can bring about that the iso-surface tension curve shifts towards the TiO2 corner, indicating that the surface tension of the ternary slag increases along with the addition of CaO or MgO. CaO has a more pronounced effect on increasing the surface tension of the ternary slag than MgO at an equimolar amount addition. The increase of the surface tension results from both the compositional change and the variation of the slag structure.

Jan 1, 2015

By Muhlis Nezihi Saridede, Burak Birol

"The scraps of high quality steels generally contain expensive alloying elements such as chromium, vanadium, nickel, etc. These scraps are melted in an induction or an electric arc furnace and refined in ESR (Electroslag Remelting) purification process. A significant amount of alloying elements are lost during these processes. In order to avoid these losses, scraps can be utilized directly in ESR by skipping the melting step. In this study, 316L stainless steel scraps were refined in ESR with selected synthetic slags. The products were analyzed by optic emission spectrometry and the effects of slag compositions on the alloying element losses were examined. According to the analysis of the scrap and the products, generally chromium, nickel and manganese losses were encountered. It was determined that the alloying element losses has no connection with electrical conductivity. The slag containing CaF2, Al2O3, and FeO gives the optimum Cr and Ni losses.IntroductionElectroslag remelting (ESR), which is the consumable electrode refining process, finds a wide range of utilization for the production of high quality, low inclusion alloys. This process is based on melting a consumable electrode under a molten synthetic slag containing CaF2, Al2O3, CaO etc. The synthetic slag provides the chemical refining and insulation of molten metal from air which leads to a higher purity and an inclusion-free product. [ 1,2] A schematic diagram of ESR system is shown in Figure 1."

Jan 1, 2011

By Flavio Begazo, William A. Enrico

"Southern Peru Copper Corporation's Ilo Refinery, the largest in Peru, began operations in 1975 with a production capacity of 165,000 stpy. Southern Peru bought the Refinery from the state owned Minero Peru SA on June 1, 1994.The Refinery processes blister from Southern Peru's I/o Smelter. Blister copper is processed in an anode plant equipped with two 365 st tilting reverberatory furnaces, a 26 mold casting wheel and an anode press machine. Copper is electrorefined in a tank house equipped with 768 commercial cells, 44 stripper cells, and 40 liberator cells, utilizing two electrolyte circuits and a 21,000 Ampere rectifier.During 1989 through 1994 a program for improving productivity was carried out by increasing the number of cells and increasing current density to the total rectifier capacity. As a result, a capacity 215,000 stpy of refined copper, 2 million tr. oz silver and 6,000 tr. oz gold per year was achieved. In 1994 Southern Peru announced plans to increase capacity to 250,000 stpy of cathode with a US$ 18 million investment and a US$ 2 million investment in environmental improvement projects, as part of the purchase agreement with the Peruvian government.This paper outlines the scope of the SPCC lio Refinery modernization and environmental program. It describes the implementation of the Electrolytic Plant expansion based on instaliation of polymer concrete cells, a new rectifier, a new selenium roaster and a Precious Metal Plant upgrades."

Jan 1, 1997

By Cong Wang, Kexin Jiao, Yongan Zhao, Haibin Zuo, Jianliang Zhang

The carbon composite brick is a new refractory used in blast furnace hearth and bottom. It caused wide attention due to its high thermal conductivity and low erosion by molten iron. In this paper, chemical constituents, SEM-EDS and X-ray diffraction were carried out in order to understand reaction mechanisms. A series of experiments of oxidation resistance characteristics were made. The oxidation mechanisms of carbon composite bricks in the presence of air were analyzed. According to the analysis on many experimental results, the oxidation process of carbon composite bricks under different temperatures were controlled by different mechanisms. In the condition of high temperature, SiO2 as oxidation product hindered the diffusion of O2, and reduced the oxidation loss of graphite in the internal.

Jan 1, 2015

By Hua Hou, Xiaofeng Niu, Wei Liang

"The explicit finite difference (EFD) method is used for calculating the casting temperature field during solidification. Because the time step is limited, the computational efficiency of the EFD method is lower. In order to improve the computational efficiency, a fourth-order in space and second-order in time model based on the equivalent specific heat method and the alternating direction implicit (ADI) method is established. The degree of similarity between the simulation results and the experimental results is analyzed. The results show that the simulation results of this high order mathematical model are close to the experimental results.IntroductionThe 3D heat transfer equation of temperature field during solidification process is as the following: [1-3]."

Jan 1, 2013

By M. A. Rabah, F. E. Farghaly, M. A. Motaleb

"Wastewater from industrial galvanization industry was reclaimed under current flow stream conditions. Results showed that the raw water contains 0.7 % by weight total suspended solids (TSS) causing turbidity amounting to 30. Measurements of Zeta potential as a function of pH revealed that solid separation takes place at pH 9. Addition of H2O2 to the polmer solution helps to oxdize ions of iron and zinc metals toinsoluble ferric oxide and zinc hydroxide to a higher state of oxidation. Addition of 5 mg/L of cationic magna flocculants polymeric solution helps the rapid separation of the turbidity. Separation of floccules so formed takes place by filtration. Addition of peroxide ions to the turbid wastewater confirms the physical stability of the flocs so formed. Impurity flocculation takes place in few seconds. Maximum temperature for safe solid removal was <30°C. The treated water was pure and safe for recycling or use in domestic purposes.IntroductionStocks and et. al. [1] show that the galvanizing process introduces spent pickling acid waste production, but its major constituent, could be used. Survey of the operational procedures adopted and the acid wastes produced by UK Galvanizers are reported. Various methods to recovery spent acid of suitable composition and to eliminate zinc contamination was considered. Application of the Kleingarn acid management system reduces waste volume, saves hydrochloric acid (HCl) and increases component throughput whilst, in conjunction with zinc elimination, could allow recycling of the majority of galvanizer’s acid wastes.Dahab [2]; Kerney [3] reported recycling of galvanizing products, including pickleliquor. Kerney suggested a mobile treatment plant for recycling pickling acids. Dahab found that pollution reduction could be achieved by relatively simple operational changes to the process that gave fairly short payback times.Rozenblat and et. al.[4] studied the extraction of zinc (II), iron(III) and iron(II) with Tributyl phosphate (TBP) from hydrochloric acid solutions containing high zinc(II) concentration. Two technological approaches for the separation are considered. Firstly, the selective extraction of iron(III) (iron(II) is oxidized to iron(III)) over zinc(II) with TBP deficiency. Secondly, iron(III) reduction to iron(II) followed by zinc(II) selective extraction with an excess of TBP. Prior stripping, the organic phase was washed with small amounts of water. Scrubbing of TBP solutions containing iron(III) contaminated with zinc(II) gives always a mixture of zinc(II) and iron(III) which must be recycled to the extraction step in continuous process. The following technological concept is proposed: reduction of iron(III) to iron(II), extraction of zinc(II) with 5-10 volume excess of TBP, washing of TBP phase contaminated with iron(II) with small volumes of water and recycling of the scrubbings and stripping of zinc with water."

Jan 1, 2008

By H. Hahn, B. H. Kear, K. Kan, S. C. Danforth, G. Skandan, W. Chang

"A new chemical synthetic process for the production of non-agglomeratednano structured ceramic (n-ceramic) powders, starting from metalorganic precursors, is described. The process combines rapid thermal decomposition of a precursor/carrier gas stream in a hot tubular reactor with rapid condensation of the product particle species on a cold substrate. Critical to the success of this Chemical Vapor Condensation (CVC) process are (1) a low concentration of precursor compound in the carrier gas, (2) rapid expansion of the gas stream through an uniformly heated tubular reactor under a reduced inert gas pressure of 1-35 mbar, and (3) rapid quenching of the gas phase nucleated clusters or nanoparticles as they exit from the reactor tube. A wide variety of metal organic precursors is available commercially, all of which can be utilized in the CVC process to produce n-ceramic powders, including single phase, multiphase and multicomponent systems.The CVC process has been used to synthesize non-agglomerated n-SiCxNy and n-ZrOxCy powders, with controlled particle size in the range 2-20 nm. Heat treatment of the assynthesized n-powders in various high purity gas streams causes compositional and structural modifications, including particle purification and crystallization, as well as transformation to a whisker-like morphology. Thus, as-synthesized amorphous n-SiCxNy particles transform to (1) cubic n-SiC particles, when heated in flowing argon at temperatures> 1350 °C, (2) hexagonal n-Si3N4 whiskers, when heated in flowing NH3IH2 at 1400 °C, and (3) cubic nSiC whiskers, when heated in flowing H2 at 1400 °C.Non-agglomerated n-ceramic powders form uniformly dense powder compacts by cold pressing, which can be sintered to theoretical density at temperatures as low as 0.5 Tm' For example, full densification ofn-Zr02 powder compacts under free sintering conditions can be achieved at 1125 °C."

Jan 1, 1994

By Liang Yu, Yuhua Li, Yuanchi Dong

"High alumina slag, with alumina normally more than 15 pct, is encountered with blast furnaces in China because of high alumina/silica ratio in iron ore as well as sinter and high ash content in coke for cost reason. High alumina slag with high viscosity and high liquidus temperature would lead to higher slag volume and thereby, furnace productivity. In the present work, liquidus temperature of high alumina slag, based on Meishan factory, Baosteel China, were investigated. A liquidus temperature model was introduced in the present work based on basic physical chemistry theory and focused on the chemical composition area used in Meishan factory(pct): Al2O3 from 14 to 17.5 and MgO from 8 to 12, so that the blast furnace slag could be designed for optimum blast furnace performance.IntroductionBlast furnace slag composition[1] has very important bearing on its physicochemical characteristics which affects smoothness of operation, slag handling, coke consumption, the degree of desulphurization, hot metal productivity and its quality etc. The slag properties which affect most are liquidus temperature, viscosity, sulphide capacity and alkali capacity. Variation of these slag characteristics with composition and temperature has been a field of active researches as these its great influence on the blast furnace operation. In the early years, most of these studies were carried out over low alumina blast furnace slags with alumina normally less than 15 pct. High alumina slag was first introduced in India because of its high alumina/silica ratio iron ore as well as sinter and high ash content in coke[2]. And then this problem becomes common as higher alumina/silica ratio iron ore imported and used [2-5]. The most important problem caused by high alumina content is liquidus temperature and then viscosity of the slag.Generally speaking those reported works [2-5] investigated a pretty wide range of chemical compositions and then obtained complex model, respectively. In fact, every factory has its own interest because of different resources. For example, the Al2O3 content from 20% to 30% pct was studied in Tata Steel India [2], but it is too high for Baosteel Meishan. A very lower percentage of alumina content, 14-18 % pct, was mainly used."

Jan 1, 2008

By Metehan Erdogan, Ishak Karakaya, Fuat Erden

"Mg-Ni system draws attention due to the promising hydrogen storage properties of Mg2Ni. The proposed method involves the use of NiO and MgCl2 in an electrochemical cell to from Mg-Ni intermetallics directly. The electrodeoxidation of NiO was followed by combination of Mg and Ni in molten salt electrolytes. The products were characterized by XRD analysis and SEM examinations. The quantitative results from Rigaku supported by Rietveld Refinement method conducted by Maud showed that more than 50 percent of the input Ni was converted to Mg-Ni intermetallics.INTRODUCTIONIt is well known that fossil fuels are the most common energy producing materials throughout the last century although, they are not renewable and their usage cause critical environmental problems [1, 2]. Hydrogen, on the other hand, is known as a clean, renewable energy carrier and instead of fossil fuels; usage of hydrogen for energy production will be the benefit of mankind. However, there are problems that hinder more common usage of hydrogen such as hydrogen storage [3]. Mg2Ni is known as Mg based hydrogen storage material with high hydrogen storage capacity [3-6]. Common Mg2Ni production methods are; mechanical alloying [8-11], vacuum induction melting [12, 13], vacuum arc melting [14], combustion synthesis [15], melt spinning [16], repetitive rolling [17] and isothermal evaporation casting [18] were also used. However, in all of these, pure Mg and Ni are required to be produced previously. Therefore, difficulties arise during handling, preparation and combination of Mg and Ni due to highly reactive nature of especially magnesium (i.e. oxidation of Mg) [11, 17, 19, 20]. Although hydrogen desorption dynamics can be significantly improved with usage of nanostructured Mg2Ni [7], it is difficult and it requires very long processing durations to produce nanostructured Mg2Ni by above processes."

Jan 1, 2014

By Renxing Li, Yongyong Gong, Yufeng Cheng, Zhenxing Yin, Xin Cao, Qijie Zhai

"The influence of electric current pulse (ECP) on the solidification structure of SUS430 ferritic stainless steel (FSS) was investigated in the current study. The technology of ECP has been widely used to improve the properties of metals with relatively low cost. The parallel electrodes were inserted into the free melt surface to constitute a current loop. The different influences of three parameters on solidification structure were studied by changing the peak current value, frequency and treating time respectively. The results indicated that the ECP significantly increased the number of equiaxed grains of SUS430 FSS. The as-cast structure without ECP treating was almost wholly columnar, while the number of equiaxed grains of the specimen, which was treated 3min with a peak current of 400kIA, increased to 2698 in the observed surface. To get the best refinement, an optimum range of these three parameters is required and the peak current value plays the most important role.IntroductionFor the lack of nickel resource and the pressure of environment protection, ferritic stainless steel is increasingly adopted to replace the austenite stainless steel because of its low nickel content and good mechanical properties. SUS430 steel is a typical example with excellent performance and relatively low price to replace the application of austenitic stainless steel[1-3]. This type of steel with high thermal conductivity coefficient, low expansion coefficient, good oxidation resistance, excellent stress corrosion resistance and other fantastic characteristics is often used to make components which need to have resistances for atmosphere, water, steam and oxidizing acid corrosion[4]. Since the developing of columnar grains and low toughness at high temperature, its products are easily crinkled and cracked during the subsequent rolling process[5]. The application of ferritic stainless steel is limited by these defects[6-8]."

Jan 1, 2012

By Magnus Ek

After the installation of three new converters as part of the recent expansion of the Rönnskär smelter completed in 2000 work continues to further improve the converter operation. The converter upgrade led to an increase in blister copper taps from 150 tons per batch to more than 300 tons. The total cathode copper production increased from 130,000 tons in 1999 to 230,000 tons in 2001, the first year in full production. In recent years focus has been to improve operating practise, maximize the blowing time, extend the converter campaigns hence to reduce the specific brick consumption and improve the converter slag composition.

Jan 1, 2005