A Liquidus Temperature Model of High Alumina Blast Furnace Slags

"High alumina slag, with alumina normally more than 15 pct, is encountered with blast furnaces in China because of high alumina/silica ratio in iron ore as well as sinter and high ash content in coke for cost reason. High alumina slag with high viscosity and high liquidus temperature would lead to higher slag volume and thereby, furnace productivity. In the present work, liquidus temperature of high alumina slag, based on Meishan factory, Baosteel China, were investigated. A liquidus temperature model was introduced in the present work based on basic physical chemistry theory and focused on the chemical composition area used in Meishan factory(pct): Al2O3 from 14 to 17.5 and MgO from 8 to 12, so that the blast furnace slag could be designed for optimum blast furnace performance.IntroductionBlast furnace slag composition[1] has very important bearing on its physicochemical characteristics which affects smoothness of operation, slag handling, coke consumption, the degree of desulphurization, hot metal productivity and its quality etc. The slag properties which affect most are liquidus temperature, viscosity, sulphide capacity and alkali capacity. Variation of these slag characteristics with composition and temperature has been a field of active researches as these its great influence on the blast furnace operation. In the early years, most of these studies were carried out over low alumina blast furnace slags with alumina normally less than 15 pct. High alumina slag was first introduced in India because of its high alumina/silica ratio iron ore as well as sinter and high ash content in coke[2]. And then this problem becomes common as higher alumina/silica ratio iron ore imported and used [2-5]. The most important problem caused by high alumina content is liquidus temperature and then viscosity of the slag.Generally speaking those reported works [2-5] investigated a pretty wide range of chemical compositions and then obtained complex model, respectively. In fact, every factory has its own interest because of different resources. For example, the Al2O3 content from 20% to 30% pct was studied in Tata Steel India [2], but it is too high for Baosteel Meishan. A very lower percentage of alumina content, 14-18 % pct, was mainly used."