The Viscosity of the Molten FeO-Fe 03-SiO2 System

The viscosity of the molten FeO-Fe2O3-Si0z system in the composition range of interest to copper smelting has been investigated using a rotating cylinder technique. The silica content of the slag was varied from 20 to 35 wt percent while the oxygen pressure of the system was varied from 10-7 10-11 atm. The temperature range investigated was from 1200 to 1350°C. It was found that the viscosity of the slag generally decreased with increasing temperature and increasing oxygen pressure. As the silica content was increased, the viscosity was found to increase.