By Partha Patra

Extracellular bacterial protein (EBP) from Paenibacillus polymyxa was isolated. Adsorption of bacterial cells of Paenibacillus polymyxa as well as EBP onto pyrite, galena and sphalerite was studied. Both bacterial cells and EBP was found to have different adsorption density for different minerals. Protein from mineral surfaces were extrated and examined through SDS PAGE electrophoresis. Specific group of protein was found to be adsorbing, specific to respective minerals. EBP was fractionated through FPLC. Adsorption studies were carried out with each fractions. Difference in adsorption density was observed for individual minerals. Flocculation and flotation experiment were carried out with these mineral specific EBP. Pyrite was selectively removed from ternary mixture of galena and spharite through flocculation anf flotation using pyrite specific EBP. Mineral specific EBP was found to selectively separated remove pyrite from the complex sulphide mixture.Zetapotential studies were carried out to examine the surface chemical changes of the minerals on interaction with EBP. Hydrophobicity of the minerals were carried out on interaction with bacterial cells as well as mineral specific EBP.

Jan 1, 2006

By K. Verbeken, E. Wettinck, M. Verhaege

Iron (III) can easily and selectively be removed from acidic sulphate solutions with organo-phosphoric acids like Di-2-Ethyl-Hexyl-Phosphoric Acid [D2EHPA]. Stripping of the iron (III) loaded organic, however, is difficult unless highly concentrated inorganic acid solutions are used. In this paper results are shown for the enhanced stripping of iron from loaded D2EHPA by electro-reduction. The loaded solvent is contacted with a 2 M H2SO4 solution, which is continuously recycled in an electrochemical reactor where iron (III) is reduced to iron(II). As iron (II) is not extracted by D2EHPA, the equilibrium for iron (III)- D2EHPA is shifted towards the aqueous iron (Il)-sulphuric acid solution. The electro-reduction unit is a vessel with separated catholyte and anolyte chambers. The catholyte is the actual stripping solution where iron (III) is reduced to iron (II) on a stainless steel electrode. The anolyte is a 2 M H2SO4 solution where oxygen is evolved on a lead alloy electrode. A sintered glass plug separates the compartments. With this unit, enhanced stripping of iron from the solvent is possible under mild acid conditions [2 M H2SO4], and a concentrated ferrous sulphate solution can be obtained. The results shown have mainly been obtained by studying the parameters affecting the electro-reductive stripping of a D2EHPA loaded organic phase in a batch reactor. From an iron (IH)-saturated 20 vol. % D2EHPA solvent containing ~ 12.5 g/1 Fe (III) over 90% of the iron can be stripped in one stage with a 2 M H2SO4 solution at 50°C. It is shown that in this way it should be possible to obtain a concentrated ferrous sulphate solution which can be processed downstream to recover a pure iron product.

Jan 1, 2000

By Finn Olesen, Melina Garcia, Mark William Kennedy

"Furnace resistance is a function of the complex interrelationship between many factors including: operating practice, slag conductivity, temperature, power intensity, and geometry (electrode shape, diameter, spacing, immersion, slag depth, etc.).Accurate prediction of resistance is critical for success of the overall furnace design. The sizing of electrodes, columns, bus-bars, and transformers are all impacted. Estimation of minimum and maximum resistance or maximum operational current, as well as the maximum operating voltage are of fundamental importance.Various mathematical tools have been developed to assist designers with the selection of furnace dimensions and the prediction of resistance. Elkem found the methods of Downing and Urban 1965 and Westly 1975, to be particularly useful.In the current paper, comparisons are drawn between data from spent aluminum pot lining (SPL) demonstration testing at Elkem Bjolvefossen and predictions based on these classical tools and 3D finite element modeling (FEM) with COMSOL.®"

Jan 1, 2012

By J. H. Meza

La Caridad copper smelter is located in the magnificent but rugged Sierra Madre Mountains. This project presents unusual challenges that require the utmost in detailed analysis and planning. The smelter, owned by Mexicana de Cobre, S.A. de C.V., has an annual production capacity of 225,000 metric tons of copper and 600,000 metric tons of sulfuric acid. It utilizes only the Flash Smelting process. This project will expand the annual production capacity to 270,000 metric tons of copper and 1,000,000 metric tons of sulfuric acid. Offgases from the Flash Furnace and the Teniente Converter will be sent to a mixing chamber, from which it will be led to two sulfuric acid plants. This project will then produce a high quality sulfuric acid.

Jan 1, 1995

By T. V. Jayaraman

Fe-Ga alloys, with compositions around 27.5 at % Ga, can be heat treated to obtain ? (ordered bcc), DO19 (ordered hexagonal), and L12 (ordered fcc) ordered structures. Our earlier work using polycrystalline samples had shown that magnetostriction is strongly influenced by ordering in this alloy. Here more detailed study of the correlation between ordering and magnetostriction using single crystals of Fe 27.5 at. % Ga alloys is reported. Single crystals of Fe 27.5 at % Ga were grown using Bridgman single crystal growth technique. X-ray and electron diffraction were used to study the ordering in this alloy. Magnetostriction measurements were carried out at no load conditions. Elastic constants were measured using Resonant Ultrasound Spectroscopy.

Jan 1, 2006

By P. K. Jha, M. M. Mahapatra, H. K. Mohanty, Pradeep Kumar

"During friction stir welding, the tool geometries affect the weld together with the process parameters like welding speed, vertical pressure and tool rotational speed. The present investigation deals with the three dimensional computational fluid dynamics modeling of friction stir welding process considering material flow around the tool, welding speed with respect to tool geometries. Friction stir welding tools with different tool geometries were used for the experiments to achieve acceptable aluminum welds. The temperatures near the welds for each tool were experimentally observed. A 3-D computational fluid dynamics (CFD) model was developed. Temperature-dependent material properties of the aluminum alloy were used in the CFD model. Thermal analysis was carried out considering rotational speed, vertical pressure and traverse speed for the tool geometries. The numerically predicted stirring patterns and temperature profiles closely matched with the experimental ones. IntroductionThe friction stir welding (FSW) is a solid state welding process where generally the metallic materials are joined by the combined action of frictional heating and weld zone stirring by a rotating tool [1]. The heat generated in the process is much below the requirement of melting the plates; hence the FSW process is devoid of harmful effects those are observed during arc welding. The FSW process utilizes a tool which has a shoulder and a protruding pin known as the probe. The shoulder is responsible for frictional heating while the pin probe facilitates stirring of the joint material. A schematic of FSW process is shown in Fig. 1."

Jan 1, 2012

By Hande Cavus, Ibrahim Yusufoglu, Cem Kahruman

"In this study, ammonium tetramolybdate (ATM) was obtained as the intermediate product of ammonium heptamolybdate tetrahydrate (AHM). The thermal decomposition mechanism of ATM was investigated under nonisothermal and isothermal conditions in air and inert gas atmospheres. Nonisothermal experiments were carried out by TGA/DTA/MS while TG was used for isothermal conditions. Characterization of the decomposition products were carried out by XRD and FT-IR. The thermal decomposition of ATM in air proceeds in a single step and forms M0O3 while [(ÍÇ4)2è]ïïï83Ìïè3 and molybdenum suboxide (Ìïè3.÷, ÷=0.025) were obtained in the first and the second steps of thermal decomposition in He, respectively. Activation energies, frequency factors and kinetic model equations were determined for thermal decomposition reactions. Fractional conversion-time diagrams were compared with diagrams drawn according to kinetic model equation.IntroductionM0O3 is usually used as catalyst in industry [1]. AHM is the basic source to produce molybdenum containing catalysts used in petrochemistry [2]. The oxides of Li, V, W, Te, Bi and Sn are doped in M0O3 to produce catalysts, which find commercial applications in the industry. The properties of M0O3 are affected by dissolution, settling, calcination, drying and thermal decomposition processes [1]. There are several studies in the literature about the thermal decomposition of AHM and the characterization of the decomposition products in different gas atmospheres and at various heating rates [3-19]."

Jan 1, 2012

By Andrew A. Fyfe

The start-up and operating results obtained at Zia Technology Inc.'s first commercial operating facility at Caldwell, Texas are described. The operation which stated in early 1991 is the first to employ the patented Inclined Rotary Reduction System (IRRS') with the associated 'all-metallic retort for the recovery of all metallics contained in EAF dust.

Jan 1, 1992

By S. Aguayo-Salinas, J. L. Valenzuela-García, A. L. Leal-Cruz, M. I. Pech-Canul, M. T. Certucha-Barragán

"The aim of this research was to carry out a comparative and systematic study of the degradation of cyanide by hybrid natural/biodegradation and biodegradation methods using a mixture of Pseudomonas sp and Bacillus megaterium native bacteria. Bioreactors consist of filled columns with contaminated ore containing 100 ppm of total cyanide. In the biodegradation tests a mixture of bacteria was inoculated into the biodegrading solution. Results of cyanide degradation show a similar asymptotic behavior in both the hybrid (opened system) and biodegradation (closed system) methods; however, for the same period of time (72 h) the permissible maximum levels (1-2 ppm of cyanide) are only attained in the closed system. While in the closed system the cyanide levels are reduced from 100 to 1.5 ppm, in the open system, cyanide decreases from 100 to 2.4 ppm.IntroductionOne of the most important tasks of mining industry is the treatment of the wastes generated in mining operations. Accordingly, industrial waste waters and ores represent a complex problem and a great challenge. In addition to ethic and communitarian considerations, there are laws that prohibit or regulate the contamination of water and air. Moreover, they establish that the restoration of wastes must be considered as a necessary operation cost [1]. Currently this important problem is being addressed by the mining and metallurgical industries using different approaches; mainly they are focusing on the treatment of waste waters and ores generated by the leaching process in which cyanide is used as a leaching agent for the recovery of precious metals as gold and silver. Cyanides have toxic characteristics and thus negatively impact the environment when they are discharged to the ground without previous treatment. While there are some processes in current use there are others that have only been proposed and that allow cyanide degradation, transformation to less toxic compounds and/or the complete elimination of cyanide. The second group includes a variety of techniques that use natural, chemical and biological treatments. Natural treatments consist of the passive abandoning of the heap and of its washing with water. Since these processes are slow and generate great volumes of water partially contaminated, then other alternatives should be considered."

Jan 1, 2008

By Larry Southwick

In the early 1940's, the Caron ammonia ? ammonia carbonate leach process was used to produce nickel from Mayari ores at the Nicaro plant in Oriente Province, Cuba. While plant operation was generally successful, it was not broadly economical and was shut down. The plant was later restarted in the 1950's and a number of investigations initiated to resolve the more serious operational and performance issues. Processing steps studied included iron reduction (chemistry ? nickel and iron, reductant, equipment), ore variability (homogeneity and consistency of mineral concentrations, serpentine vs. laterite), leach solution strength, nickel recovery (temperature ? reduction and leaching, reoxidation) and a variety of other topics. These studies and their findings will be discussed. Caron himself obtained good results on these ores in the laboratory. They could not be duplicated in the field, the reasons for which will be reviewed. (Note: the ore looked like garden dirt; charcoal made from palm trees was one of the reductants attempted; and ammonia was the leach solution. Mixing the three, so to speak, was to yield nickel.)

Jan 1, 2006

By N. Kanarin

A thermodynamic study is reported on the chlorination of Fe(1-x.)O, Fe2O3, Cr2O3, MgO, Mg2SiO4 with chlorine in the presence or the absence of reducing atmospheres. The reactivities of these compounds as well as that of Mg3Si2O5(OH)4 using Cl2+N2, Cl2+air, and Cl2+CO gas mixtures were studied by non isothermal thermogravimetric analysis between 20 and 1000 °C. The same solids were chlorinated in a horizontal experimental set, during two hours between 350 and 1000 °C, in reducing and oxidizing atmospheres: The chlorination products were examined by XRD and SEM, and possible reaction paths were examined. Results indicate that the carbochlorination of these solids was better than their chlorination; Furthermore, the carbochlorination was performed at lower temperatures than those of the chlorination. Finally, the reaction extent was higher in the case of carbo-chlorination of these compounds. Based on these results, a process was suggested for the selective recovery of chromium compounds from the chromite concentrate.

Jan 1, 1995

By Xiang Lan

A strain of Thiobacillus ferruuxidans No. 8 was isolated from the acidic mine water of an arsenopyrite deposit, South China. It has been found from the experimental results that the growth of bacteria was inhibited by flotation agents. The order of toxic effect of different flotation agents on the growth of Thiobacillus ferrooxidans is ethyl xanthate > butyat ammonium aerofloat > butyl xanthate ? isobutyt xauthate >? flother No. 2 oil. The bioteaching treatment of arsenic and antimony-bearing gold concentrate in Longshan mine, Hunan province, China, was influenced considerably by the presence of flotation agents. The possible causes of the influence of flotation agents were discussed and an improved method was suggested.

Jan 1, 1991

By Lijuan Li, Xin Xia, Junjun Huang, Qijie Zhai, Xiang Jiang

"Some experiments with different temperatures (1173, 1223, and l273K) and different annealing times (3, 4, 5, 6min) were carried out on cold-rolled plate of Fe-36Ni invar alloy. The microstructure and the mechanical properties were observed and tested respectively, and the fracture morphology was observed by SEM. The results show that with increasing of the temperature and the annealing time, the austenite grains gradually grow up accompanied by a small amount of annealing twin crystals, meanwhile, its plasticity and toughness are improved, and it is typical ductile fracture under the condition of tensile failure. After annealed at l223K, the invar alloy has better comprehensive properties than that at the other annealing temperatures, and the grains size is more uniform. Furthermore, when the annealing time is 4min, the invar alloy has the best comprehensive properties.IntroductionAs we known, most metals and alloys expand with increasing temperature. More than one hundred years ago (in 1897), Guillaume observed that Fe-Ni alloy with face-centered cubic (fcc) crystal structure, consisting of36%Ni, showing a very small thermal expansion coefficient below the ferro-to-paramagnetic transition, the thermal expansion coefficient around room temperature( <2 X 1O-6K-1 compared to most metallic materials which have a thermal expansion coefficient of 10-20 X 1O-6K-1) [1,2]. Since then, the subject has attracted many researchers, and various alloys with low thermal expansion coefficients have been developed. These alloys, generally known as ""invar alloys"", are in demand where dimensional changes due to variation in temperature must be minimized and where high stability is required [3, 4]."

Jan 1, 2012

By Florian Kongoli

Minor components and flux additions can modify the liquidus temperatures of multicomponent slags. In industrial practice, slags with various levels of minor components require various flux additions in order to achieve the lowest possible liquidus temperature The prediction and the optimization of these combinations can decrease the cost of the overall process. In this work the effect of several minor components and flux additions such as Al2O3, MgO, and CaO, on the liquidus temperatures of multicomponent iron-silicate slags has been analyzed in terms of a thermodynamic model Various simple isothermal and non-isothermal diagrams are presented. These diagrams can be used directly by the process operators to define the optimum conditions under which the fluxes can be used to achieve the desired slag liquidus temperatures.

Jan 1, 1999

By Emily Chen, Randolph Kirchain, Gabrielle Gaustad

"As prices and demand for aluminum metal have increased over the past few years, secondary production has begun to outpace primary aluminum production. However, while recycling of packaging and automotive scrap has continued to increase, aerospace secondary materials remain a largely untapped resource. Shredded or co-mingled aerospace scrap has a high degree of compositional uncertainty due to the prevalence of high copper and high zinc alloy series. Although it is clear that upgrading strategies enable increased usage of aerospace scrap, it is not clear that they would be economic or efficient. Previous studies by the authors have shown that modeling techniques, specifically chance-constrained optimization, provide the ability to evaluate upgrading options in terms of potential aerospace scrap utilization and production cost. Three specific cases are analyzed: a dismantled case, a sorted case, and a shredded or co-mingled case; sensitivity analysis of resulting compositional uncertainty is also presented.IntroductionAluminum recycling has a number of key environmental and economic benefits. Secondary recovery forestalls depletion of non-renewable resources and avoids the deleterious effects of extraction and winning (albeit by substituting some effects of its own). For most metals, the latter provides strong motivation for recycling; for light metals, like aluminum, the motivation is compelling[1]. Fortunately, as prices and demand for aluminum have increased greatly over recent years, secondary production has begun to outpace primary production (Figure 1). However, while the recycling rates of many aluminum products such as used beverage cans and cars have increased over this period, aerospace secondary materials remain a comparatively untapped resource.This untapped resource for scrap aluminum is a very large one; aluminum is the primary aircraft material comprising about 80% of a planes unladen weight[2]. It is used extensively for airframes, landing gear, engine components, propellers, and interior trim. A standard Boeing 747 jumbo jet, for example, contains approximately 75,000 kilograms of aluminum[2]. At an approximate rate of 300 per year, more than 6,000 civil aircraft are forecast to arrive at end-of-life in the next 20 years, potentially creating a large aerospace scrap market[3]. Many military aircraft are already available for possible scrap use, however, most are currently in storage at air force bases around the world[4]. The underutilization of these aerospace scrap materials indicates a lack of economic end-of-life options."

Jan 1, 2008

By I. Sofia Fernandez del Rio

This paper describes a process for the treatment of the dusts generated during the operation of blast and reverberatory furnaces in the lead smelter, to remove zinc, cadmium, arsenic and halides from the circuit. The process consists of a Pefloles' developed leaching/purification stage and a solvent extraction process developed by Lurgi. The plant capacity is 5,000 tonnes Zn/year. The feed to solvent extraction contains 8 g/1 Zn. Impurities such as copper, iron, arsenic and cadmium are removed by conventional cementation processes. The cadmium product is 99.99 % pure. The solvent extraction process consists of two extraction stages, one washing stage and two stripping stages. D2EHPA is used as the extraction agent and 25% ammonia as the neutralizer. The rich-zinc solution is sent to the electrolytic zinc plant for zinc recovery. The raffinate produced, which is a mixture of ammonium sulfate and chloride, is used for agricultural applications.

Jan 1, 2000

By Tae-Hyun Kim, Shun Myung Shin, Jin-gu Kang, Jeong-Soo Sohn

We investigated about synthesis of Mn-Zn ferrite with spinel structure using sulfuric acid leaching solution of mixed spent zinc-carbon batteries and spent alkaline batteries. The waste batteries were prepared by physical treatment such as crushing, magnetic separation, and screening. After screening, the crushed batteries were separated to +8 mesh and -8 mesh powder. Among these, under 8 mesh powder was selected for leaching test. The leaching test was investigated at 2 M H2SO4, 4 vol.% H2O2, reaction temperature 60 ?, agitation speed 250 rpm, solid/liquid ratio 50 g/ 500 ml, reaction time 1 h. The leaching efficiency of zinc, manganese and iron were 99.0%, 98.9%, 58.5%, respectively. For co-precipitation of zinc, manganese and iron, 5M NaOH solution was used for pH control. Then in order to synthesize Mn-Zn ferrite powder, it was investigated according to reaction temperature, agitation speed and O2 partial pressure. We could synthesize about 20 nm of Mn-Zn ferrite with spinel structure.

Jan 1, 2008

By Shadia J. Ikhmayies

"Nanocrystalline fluorine doped tin oxide (Sn02:F) thin films were produced by the spray pyrolysis technique (SP) on glass substrates at a substrate temperature T, = 450 ° C. The hydrated stannous chloride (SnClz.2H20) was used as a precursor and ammonium fluoride (NH4F) and hydrofluoric acid (HF) were used as the doping compounds. A comparison between the compositional, morphological and optical properties of the films obtained by using the two doping compounds was performed by using scanning electron microscope (SEM) observations, energy dispersive spectroscopy by X-rays (EDAX) and transmittance measurements. It is found that the films prepared by using HF have larger grain size, and higher fluorine content than the films prepared by using ~- In addition these films have higher transmittance and higher direct optical bandgap energy. These results are interesting for the use of Sn02:F as a forecontact in CdS/CdTe solar cells.IntroductionTin dioxide is an n-type, wide bandgap semiconductor (about 3.5 eV) and in the form of thin films, it is a transparent conducting material, characterized by high optical transmission (80- 90%) [l]. Sn02:F is the most widely used transparent-conducting oxide material. The transparent-conducting thin films of this oxide are used as electrodes in a variety of optoelectronic devices, as heat mirror coatings in 'smart windows' for buildings, in automobile and airplane windshields, in incandescent light bulbs, in flat-plate and concentrating solar collectors. Tin oxide and zinc oxide, in thin film configuration are technologically important materials because of their applications in photovoltaic cells [2].Among various dopants for Sn02, fluorine is often preferred, because fluorine doping results in films with high transparency and good conductivity [3]. By exploring the literatures, it was found that different sources of fluorine were used to produce Sn02:F thin fihns, among which are ammonium fluoride (NH4F) and hydrofluoric acid (HF) are the most used. Some researchers used~ [2, 4-7] and others used HF [3, 6-8] for doping Sn02 films. Gordillo et al.[7] used both of NH4F and HF and showed that the resistivity of thin films obtained by using HF was lower than that of similar films obtained by using NH4F by a factor of 2.2. They also found that the films obtained by using HF have more random orientations."

Jan 1, 2013

By Dachun Liu, Yifu Li, Baoqiang Xu, Yongnian Dai, Bin Yang

"The removal of impurity arsenic from crude tin is one of the major problems in the process of tin refining. Through a thermodynamic analysis on vacuum refining process of crude tin, the vapor pressure of impurity arsenic under different temperatures can be obtained, which demonstrates that it is possible to separate tin and arsenic by the vacuum refining process. This paper attempts to verify the behaviors of impurity arsenic. The experiment result shows that through vacuum distillation, crude tin with 0.16% arsenic can be refined from crude tin with 0.96% arsenic, and about 50% impurity arsenic can be collected in the form of metallic arsenic.PrefaceThe crude tin obtained by the reduction process is insufficiently pure for most applications, even smelting from tin concentrate. Arsenic is a common impurity in crude tin and also one of the predominant elements to affect tin performance. Arsenic is a poisonous metal that has long been linked to an increased risk of cancers, diabetes, thickening of the skin, diseases of the liver and digestive complications, so there is a mandatory limit on the amount of arsenic (<0.015%) in tinfoil wrapper and tin layers for food packaging. Arsenic causes a poor appearance and plasticity, and increases viscosity. The impurities content of crude tin fluctuate over a wide range; a lot depends on composition of tin ore concentrate, treatment method and technological process before reduction smelting. And the content range of arsenic is usually 0.5~4%, but it is higher in some factories."

Jan 1, 2012

By M. Frades, C. Frías, G. Díaz, A. B. Mejías

"In recent years, zinc recovery from flue dusts and other industrial wastes has been increased, offering to the market a large tonnage of secondary zinc oxides, which can not be processed directly to render high quality zinc because of the hazardous impurities and halogens content.The ZINCEXTM Technology has been commercially applied for more than thirty years and represents the most suitable solution to deal with secondary or crude zinc oxides due to its flexibility, simplicity, and cost-efficiency, allowing production of SHG electrolytic zinc and pure zinc sulfate salts thanks to the flexibility and selectivity of the zinc solvent extraction unit regarding to get rid of impurities.A dual plant able to produce electrolytic zinc and crystallized zinc sulfate has been engineered to provide a flexible and profitable solution to zinc market. A description of the study and the relevant achievements is presented in this paper.IntroductionZinc is a valuable commodity in the marketplace and can be recycled again and again and still maintain its physical and chemical properties. Zinc recycling offers both environmental and economic benefits such as reducing volumes of material that end up in landfills, saving energy by reducing the need for mining and smelting, and relieving environmental impact on the land and water, and conserving zinc ore [1].The supply of zinc able to be re-processed will be increasing from year to year according to secondary materials enter the recycling stream, and as a result, more recycled zinc will become available in the market. Thus, some existing zinc refineries are implementing an annexed treatment line to process secondary oxides in conjunction with primary zinc concentrates [2].The galvanized steel scrap is normally recycled in electric arc furnaces or in basic oxygen furnaces, which generates a large tonnage of zinc-bearing flue dusts (EAFD). Around one million ton EAFD is yearly produced at the USA and the EU, respectively. The flue dusts are treated commercially by pyrometallurgical ways such as waelz kilns, electrothermic furnaces, etc, to yield secondary zinc oxides that can not be processed directly to render high quality zinc because of the hazardous impurities and halogens content [3]."

Jan 1, 2008