Synthesis of Mn-Zn-Fe Soft ferrite from mixed batteries with spent zinc-carbon batteries and spent alkaline batteries

We investigated about synthesis of Mn-Zn ferrite with spinel structure using sulfuric acid leaching solution of mixed spent zinc-carbon batteries and spent alkaline batteries. The waste batteries were prepared by physical treatment such as crushing, magnetic separation, and screening. After screening, the crushed batteries were separated to +8 mesh and -8 mesh powder. Among these, under 8 mesh powder was selected for leaching test. The leaching test was investigated at 2 M H2SO4, 4 vol.% H2O2, reaction temperature 60 ?, agitation speed 250 rpm, solid/liquid ratio 50 g/ 500 ml, reaction time 1 h. The leaching efficiency of zinc, manganese and iron were 99.0%, 98.9%, 58.5%, respectively. For co-precipitation of zinc, manganese and iron, 5M NaOH solution was used for pH control. Then in order to synthesize Mn-Zn ferrite powder, it was investigated according to reaction temperature, agitation speed and O2 partial pressure. We could synthesize about 20 nm of Mn-Zn ferrite with spinel structure.