By Harvey T. Kennedy, Charles R. Olson

In many investigations of the performance of petroleum reservoirs the assumption is made that the liquid, if below its bubble-point pressure, is at all times in equilibrium with gas. On the other hand, observations by numerous investigators have indicated that gas-liquid systems including hydrocarbon systems, may exhibit supersaturation to the extent of many hundred psi in the laboratory. Up to the present, there has been no reliable data on which ti judge the actual extent of supersaturation under conditions approaching those existing in petroleum reservoirs. The work reported here deals with observations and measurements on mixtures of methane and kerosene in the presence of silica and calcite crystals. Bubbles were observed to form on crystal-hydrocarbon surfaces in preference to the glass-hydrocarbon interface or to the body of the liquid. Statistically, it was found that the number of bubbles formed per second per square centimeter of crystal surface was a function of the supersaturation only. and the function was evaluated graphically. Supersaturations were observed up to 770 psi, under which condition bubbles formed quickly and with considerable violence. With decreasing degrees of supersaturation, the frequency of bubble formation became less, until at 30 psi supersaturation and lower, no bubbles were observed to form, even though the observation at 30 psi was continued for 138 hours. It was found that silica and calcite crystals had identical effects, within experimental error, in accelerating the formation of bubbles, and that small amounts of water and crude oil had no effect on the results. It is shown that the maximum supersaturation that can exist in a reservoir may be calculated from the data presented and from the area of the rock surface. It is also shown that the number of bubbles formed in the reservoir, in order of magni- tude, may be calculated for any rate of pressure decline imposed on the reservoir by production. The bearing of the number and distribution of bubbles on reservoir performance is discussed. INTRODUCTION A liquid system is supersaturated with gas when the amount of gas dissolved exceeds that corresponding to equilibrium at the existing pressure and temperature. The degree of super-saturation may be conveniently expressed as the difference between the bubble-point of the mixture and the prevailing pressure. Thus, if a mixture having a bubble-point of 1,000 psi at a given temperature exists in single liquid phase at 700 psi at the same temperature. it is supersaturated to the extent of 300 psi. There are many examples of high supersaturations, mostly in aqueous solutions, reported in the literature. Thus, Kenrick, Wismer and Wyatt1 showed that water may be saturated with oxygen, nitrogen or carbon dioxide at 100 atmospheres, and the pressure reduced to one atmosphere without producing bubbles immediately. When liquids are in a state of tension, they may be considered as supersaturated at least to the extent of the tension. The tensile strength of water has been reported as 30 atmospheres by Meyer,1 60 atmospheres bv Budgett. 30 to 50 atmospheres by Temperley and Chambers,4,5 200 atmospheres by Dixon6. and 223 atmospheres by Briggs.7 Vincent8,9 determined the tensile strength of a mineral oil as 45 psi. Gardescu1 maintained pressures for short times in a model reservoir at 115 psi below the bubble-point. It should be noted that the high supersaturations observed were obtained on systems carefully purified to remove particles or surfaces which might promote the formation of bubble; These "nuclei" were considered as contaminants which interfered with the determination of a property of the liquid. In

Jan 1, 1952

By Paul C. Merritt

For more than 100 years, British Columbia has been considered a mountainous mining province, rich with potential but relatively poor in actual production. Times have changed. Today, Japanese interests and money have altered the difficult, if not once impossible, economic conditions and market factors which until recently precluded any great growth of the British Columbia mineral industry. The mining boom now underway in British Columbia has carried the total value of mineral production in the Province to a record height in 1962 as it rang up a 27% increase over that of 1961. Breaking the $200 million barrier for the first time, total value of British Columbia's mineral output reached $229- 276,385. Of this amount, metals accounted for 70%; industrial minerals, 6 %; structural materials, 9 %; and fuels, 15%. The substantial increase is attributed to the record production of copper, iron, asbestos, natural gas and petroleum, in addition to the continuing high production rate and favorable prices of other mineral commodities.

Jan 12, 1963

By B. Hyatt, E. Klokholm

The reesistivity of Cu-Pd alloys of 9.6 to 29 pct Pd alloys was measured after plastic deformzation in tension. For all compositions a continzting decrease in resistivity with increasing plastic strain was observed. By comparison with the results of Damask on a brass ad Cu3Au, it was deduced that these anonzalous decreases in resistivity are due to the decrease in short-vunge order caused by cold work. An anomalous decrease in the resistivity of cold-worked CU-Pd alloys was first reported by Jaumot and Sawatzky.' They observed decreases in the electrical resistivity when disordered Cu-Pd alloys drawing at room temperature. Recently, a similar anomaly was reported by Aarts and Houston-Mac-Mi1lan2 in Ag-Pd alloys containing 10 to 45 pct Pd. The plastic deformation in this case was produced by tensile strain at liquid-nitrogen temperatures. For AE-Pd alloys the relative resistivity change becomes positive for tensile strains of about 20 pct.

Jan 1, 1960

By Charles W. Frey

COMPRESSED air is one of the most useful tools that the mine operator has at his disposal. It is clean, nontoxic, easily handled, and can be distributed anywhere that a man can drag a length of rubber hose. Without it a great deal of drilling would still be a laborious hand process, and although the John Henry of legendary fame could beat a mechanical drill, John Henrys are few and far between, and in the long run the air drill is the victor. As a general rule, horizontal compressors are lubricated by mechanical lubricators, which furnish oil to the cylinder walls, whereas vertical units are splash lubricated. In most horizontal machines oil is introduced at the top center of the piston, from which point it can run down and lubricate the rest of the piston. Some large units introduce oil at more than one point on the cylinder wall, the necessity for this and the number of points of introduction depending upon the size of the cylinder.

Jan 1, 1938

By Dan White

Stress measurements taken at Climax, El Teniente, Henderson, Lakeshore and Urad mines indicate that the deposits cited are generally subject to an inclined stress field that can be highly anisotropic. The horizontal stresses vary significantly between deposits and exceed the measured vertical stresses at Henderson and El Teniente mines. Experience at Henderson, Lakeshore and Urad mines is used to suggest a relationship between cavability and the premining stress. In poorly fractured, high strength rock masses, high stresses can assist the caving process. In well fractured, low strength rock masses, caving is ensured by breakage along fracture planes. The relationship between ground weight and the premining stress is also investigated. Ground weight problems appear to be most related to the competence of the ground rather than the magnitude of the premining stress as supported by experience at Climax and El Teniente mines. Recent developments in block caving favor the extraction of poorly fractured, high stressed rock. Accompanying the development of these deposits are new problems such as rock bursts. These pose particular problems to mine designers in that no experience currently exists in combatting rock burst problems at block caving mines.

Jan 1, 1984

By F. P. Dewey

At the Wilkes-Barre Meeting of the Institute, Dr. J. Lawrence Smith, in the course of his remarks on some peculiarities in the composition of irons, alluded to the so-called " bucltshot" iron, and exhibited a specimen of this material. He said that when the small granules, or shot, were separatetl from the mass, they could be flattencd under the hammer, and inferred that these particles had been decarburized by the blast before sinking into the hearth of the furnace, and thus we had the exceptional production of wrought iron in the blast furnace. I have recently obtained a characteristic specimen of this variety of iron from one of the furnaces at Orbisona, Pa. Considerable uncertainty existed as to its true nature and the conditions of its production. Its weight seemed to preclude the idea that it containetl much or any slag, yet its lack of strength indicated that it was not homogeneous cast iron. At times considerable quantities had been produced, which could only be utilized by charging in the furnace and remelting. The specimen, on the freshly fractured surfacc, appeared to consist of flattened globules of iron cemented together by a bluish material which one would naturally suppose to be slag, and qualitative examination for lime strengthened this supposition. It was quite difficult to obtain drillings, as there was a tendency to split in several directions as soon as pressure mas applied; but enough was obtained to undertaltc quantitative determinations. They were found to consist of two portions—one attracted by the magnet, and the other not. By repeated separation the magnetic portion was found to be 94.44 per cent., and the non-magnetic 5.56 per cent. Analyses of these gave the following results: Magnetic Portion. Non-magnetic Portion. Percent, Percent. Graphite,.....3.480 Lime,. . 71.41 0 = 24.028 Combined carbon,. .. 0.260 Magnesia,. trace. Silicon,..... 2.790 Protox. of Phosphorus,.... 0.412 iron,. trace. Sulphur,.....0.292 Sulphide of Copper,.....0.110 caleium, 3.67 S= 1.72 0 = 3.440 Manganese,.... 0.500 -Iron (by dif.).,. .. . 91.206 27.468 --Silica,. 24 62 0 = 13.131 100.000 99.90

Jan 1, 1879

By Francis Collins, E. R. Brownscombe

A study has been made of the material balance-fluid flow method of estimating reserves and degree of water drive from pressure and production history data. By considering the effect of random pressure errors it is shown that in a particular example a standard deviation of three and one-half pounds in each of ten pressure survey? permits the determination of the reserves with a standard deviation of 8 per cent and the water drive with a standard deviation of 15 per cent, assuming that certain basic geologic data are correct. It is believed that this method of estimating reserves and water drive is useful and reliable in a number of cases. The method is particularly valuable when reservoir pressure data are accurate within a very few pounds, but may also be applied with less accurate pressure data if a relatively large reservoir pressure decline occurs early in the life of the field, as for example in an under-saturated oil field. INTRODUCTION A knowledge of the magnitude of reserves and degree of water drive present in any newly discovered petroleum reservoir is necessary to early application of proper production practices. A number of investigators have contributed to methods of relating reserves, degree of water drive, and production and pressure history. 1-8 Three types of problems of increasing complexity may be mentioned. If a reservoir is known to have no water drive. and if the ratio of the volume of the reservoir occupied by gas to the volume of the reservoir occupied by oil (which ratio permits fixing the overall compressibility of the reservoir) is known, then only one further extensive reservoir property remains to be determined, namely the magnitude of the reserves. A straightforward application of material balance considerations will permit this determination. The problem becomes very much more difficult if we wish to determine not only the magnitude of the reserves but also the magnitude of water drive, if any, which is present. In principle, a combination of material balance and fluid flow considerations will permit this evaluation. Finally, if neither the magnitude of reserves, the degree of water drive, nor the ratio of oil to gas present in the reservoir is known and it is desired to determine all three of these variables, the problem could in principle be solved by a fluid flow-material balance analysis which determines the overall compressibility of the reservoir at various points in its history. The change in compressibility with pressure would provide a means of determining the ratio of gas to liquid present, since the compressibilities of gas and liquid vary differently with pressure variation. However, in practice this problem is probably so difficult as to defy solution in terms of basic data precision apt to be available.' It is the purpose of this discussion to illustrate the second case, which involves the determination of two unknown variables, single phase reserves and degree of water drive, from pressure and production history and fluid property data, and to study the precision with which these unknowns can be determined in this manner in a particular case. Although an electric analyzer developed by Bruce as used in making the calculations to be described, numerical methods necessary in carrying out the process have been devised and have been applied for this purpose. Schilthuis,' for example, developed a comprehensive equation for the material balance in a reservoir. He combined this with a simplified water drive equation, assuming that the ratio of free gas to oil was fixed by geological data and that a period of constant pressure operation at constant rate of production was available to determine the constant for his water drive equation. On this basis he was able to compute the reserves and predict the future pressure history of the reservoir. Hurst developed a generalized equation permitting the calculation of the water drive by unsteady state expansion from a finite aquifer. He showed in a specific case how the water influx calculated by his equation, using basic geologic and reservoir data to fix the constants, matched the water influx required by material balance considerations. Old3 illustrated the simultaneous use of Schilthuis' material balance equation and Hurst's fluid flow equation for the determination of the magnitude of reserves and a water drive parameter from pressure and production history. He used this method to calculate the future pressure history of the reservoir under assumed operating conditions. As a basis for determining reserves, Old assumed a value for his water drive parameter and calculated a set of values for the reserves, using the initial reservoir pressure and each successive measured pressure. The sum of the absolute values of the deviations of the resulting reserve numbers from their mean value was taken as a criterion of the closeness of fit to the experimental data possible with the water drive parameter assumed. New values of the water drive parameter were then assumed and new sets of the reserves calculated until a set of reserves numbers having a minimum deviation from the average was established. The average value of- the re-

Jan 1, 1949

By E. R. Brownscombe, Francis Collins

A study has been made of the material balance-fluid flow method of estimating reserves and degree of water drive from pressure and production history data. By considering the effect of random pressure errors it is shown that in a particular example a standard deviation of three and one-half pounds in each of ten pressure survey? permits the determination of the reserves with a standard deviation of 8 per cent and the water drive with a standard deviation of 15 per cent, assuming that certain basic geologic data are correct. It is believed that this method of estimating reserves and water drive is useful and reliable in a number of cases. The method is particularly valuable when reservoir pressure data are accurate within a very few pounds, but may also be applied with less accurate pressure data if a relatively large reservoir pressure decline occurs early in the life of the field, as for example in an under-saturated oil field. INTRODUCTION A knowledge of the magnitude of reserves and degree of water drive present in any newly discovered petroleum reservoir is necessary to early application of proper production practices. A number of investigators have contributed to methods of relating reserves, degree of water drive, and production and pressure history. 1-8 Three types of problems of increasing complexity may be mentioned. If a reservoir is known to have no water drive. and if the ratio of the volume of the reservoir occupied by gas to the volume of the reservoir occupied by oil (which ratio permits fixing the overall compressibility of the reservoir) is known, then only one further extensive reservoir property remains to be determined, namely the magnitude of the reserves. A straightforward application of material balance considerations will permit this determination. The problem becomes very much more difficult if we wish to determine not only the magnitude of the reserves but also the magnitude of water drive, if any, which is present. In principle, a combination of material balance and fluid flow considerations will permit this evaluation. Finally, if neither the magnitude of reserves, the degree of water drive, nor the ratio of oil to gas present in the reservoir is known and it is desired to determine all three of these variables, the problem could in principle be solved by a fluid flow-material balance analysis which determines the overall compressibility of the reservoir at various points in its history. The change in compressibility with pressure would provide a means of determining the ratio of gas to liquid present, since the compressibilities of gas and liquid vary differently with pressure variation. However, in practice this problem is probably so difficult as to defy solution in terms of basic data precision apt to be available.' It is the purpose of this discussion to illustrate the second case, which involves the determination of two unknown variables, single phase reserves and degree of water drive, from pressure and production history and fluid property data, and to study the precision with which these unknowns can be determined in this manner in a particular case. Although an electric analyzer developed by Bruce as used in making the calculations to be described, numerical methods necessary in carrying out the process have been devised and have been applied for this purpose. Schilthuis,' for example, developed a comprehensive equation for the material balance in a reservoir. He combined this with a simplified water drive equation, assuming that the ratio of free gas to oil was fixed by geological data and that a period of constant pressure operation at constant rate of production was available to determine the constant for his water drive equation. On this basis he was able to compute the reserves and predict the future pressure history of the reservoir. Hurst developed a generalized equation permitting the calculation of the water drive by unsteady state expansion from a finite aquifer. He showed in a specific case how the water influx calculated by his equation, using basic geologic and reservoir data to fix the constants, matched the water influx required by material balance considerations. Old3 illustrated the simultaneous use of Schilthuis' material balance equation and Hurst's fluid flow equation for the determination of the magnitude of reserves and a water drive parameter from pressure and production history. He used this method to calculate the future pressure history of the reservoir under assumed operating conditions. As a basis for determining reserves, Old assumed a value for his water drive parameter and calculated a set of values for the reserves, using the initial reservoir pressure and each successive measured pressure. The sum of the absolute values of the deviations of the resulting reserve numbers from their mean value was taken as a criterion of the closeness of fit to the experimental data possible with the water drive parameter assumed. New values of the water drive parameter were then assumed and new sets of the reserves calculated until a set of reserves numbers having a minimum deviation from the average was established. The average value of- the re-

Jan 1, 1949

By J. R. Long, C. E. Armantrout, A. H. Roberson, T. R. Graham, R. S. Dean

THE general program of the Federal Bureau of Mines on the study of alloys made with electrolytic manganese has been extended to copper-manganese-aluminum alloys. The initial results of the work are presented in this report and concern a determination of the mutual solubilities of these three metals to form the alpha solid solution. The principal studies of this system, reported in the literature, have been focused on the Heusler alloys containing 10 to 30 per cent Mn with 9 to 15 per cent Al. These investigations concern the ferromagnetic properties and the determination of the crystallization contours, with little emphasis on the phases present in the solid state outside of this area. Heusler1 recognized a breakdown of the beta solid solution of the magnetic alloy, which he says decomposes into the alpha, beta, and gamma phases of the copper-aluminum system, somewhat modified by the presence of manganese. Rosenhain and Lantsberry2 examined alloys ranging up to 10 per cent Mn and io per cent Al but were unable to reach definite conclusions concerning the phase boundaries in that area. Krings and Ostmann3 made magnetic studies and examined the system by thermal analysis. They present contours of the liquidus surface but do not place any of the phase boundaries. Corson4 [ ] has drawn a hypothetical boundary for the alpha field with few data to support such construction. The binary systems involved have received considerable attention by numerous investigators, and their general features are well established. The hopper-aluminum system (Fig, I) has been thoroughly examined by Stockdale,5 who places the limit of solubility of aluminum in copper at 7.4 per cent at the liquidus and 9.5 per cent at room temperature. Smiths established the eutectoid temperature at 570°C. by a study of isothermal decomposition of the beta phase. The copper-manganese system (Fig. 2) has been recently reviewed by Dean and co-workers.7 Using high-purity alloys, they place the solubility of alpha man-

Jan 1, 1946

By R. S. Dean. J. R. Long T. R. Graham, Roberson A. H., Armantrout C. E.

The general program of the Federal Bureau of Mines on the study of alloys made with electrolytic manganese has been extended to copper-manganese-aluminum alloys. The initial results of the work are presented in this report and concern a determination of the mutual solubilities of these three metals to form the alpha solid solution. The principal studies of this system, reported in the literature, have been focused on the Heusler alloys containing ro to 30 per cent Mn with 9 to 15 per cent Al. These investigations concern the ferromagnetic properties and the determination of the crystallization contours, with little emphasis on the phases present in the solid state outside of this area. Heuslerl recognized a breakdown of the beta solid solution of the magnetic alloy, which he says decomposes into the alpha, beta, and gamma phases of the copper-aluminum system, somewhat modified by the presence of manganese. Rosenhain and Lantsberry2 examined alloys ranging up to 10 per cent Mn and 10 per cent A1 but were unable to reach definite conclusions concerning the phase boundaries in that area. Krings and Ostmann3 made magnetic studies and examined the system by thermal analysis. They present contours of the liquidus surface but do not place any of the phase boundaries. Corson4 has drawn a hypothetical boundary for the alpha field with few, data to support such construction. The binary systems involved have rcceived considerable attention by numerous investigators, and their general features are well established. The copper-ahminum system (Fig. I) has been thoroughly examined by Stockdale,5 who places the limit of solubility of aluminum in copper at 7.4 per cent at the liquidus and 9.5 per cent at room temperature. Smith6 established the eutectoid temperature at 570°C. by a study of isothermal decomposition of the beta phase. The copper-manganese system (Fig' ') has been recently reviewed by Dean and CO-WorkersS.7 Using high-purity alloys,

Jan 1, 1947

By Armantrout C. E., R. S. Dean. J. R. Long T. R. Graham, Roberson A. H.

The general program of the Federal Bureau of Mines on the study of alloys made with electrolytic manganese has been extended to copper-manganese-aluminum alloys. The initial results of the work are presented in this report and concern a determination of the mutual solubilities of these three metals to form the alpha solid solution. The principal studies of this system, reported in the literature, have been focused on the Heusler alloys containing ro to 30 per cent Mn with 9 to 15 per cent Al. These investigations concern the ferromagnetic properties and the determination of the crystallization contours, with little emphasis on the phases present in the solid state outside of this area. Heuslerl recognized a breakdown of the beta solid solution of the magnetic alloy, which he says decomposes into the alpha, beta, and gamma phases of the copper-aluminum system, somewhat modified by the presence of manganese. Rosenhain and Lantsberry2 examined alloys ranging up to 10 per cent Mn and 10 per cent A1 but were unable to reach definite conclusions concerning the phase boundaries in that area. Krings and Ostmann3 made magnetic studies and examined the system by thermal analysis. They present contours of the liquidus surface but do not place any of the phase boundaries. Corson4 has drawn a hypothetical boundary for the alpha field with few, data to support such construction. The binary systems involved have rcceived considerable attention by numerous investigators, and their general features are well established. The copper-ahminum system (Fig. I) has been thoroughly examined by Stockdale,5 who places the limit of solubility of aluminum in copper at 7.4 per cent at the liquidus and 9.5 per cent at room temperature. Smith6 established the eutectoid temperature at 570°C. by a study of isothermal decomposition of the beta phase. The copper-manganese system (Fig' ') has been recently reviewed by Dean and CO-WorkersS.7 Using high-purity alloys,

Jan 1, 1947

By H. W. Camp

In attempting to summarize and pick out the outstanding development,s in refinery engineering during the past 12 or 13 months, one is immediately impressed by the great strides that have taken place. It is, of course, difficult to obtain the proper perspective with the old year so fresh in our minds, and if relatively minor improvements seem to be given equal recognition with those of magnitude, it will be because the nature of the human mind causes us to place the trivial incidents of today with the important things of yesterday. For instance, the Twenly-Second Semiannual Motor Gasoline Survey (December, 1930) of the U. S. Bureau of Mines shows that the total gasoline yield per barrel of crude increased from 39.6 per cent.. in 1929 to 41.99 per cent. in 1930. This latter fact may appear rather confusing since the production of high-gravity crudes has been steadily increasing. However, during the past yew there has been a reduction in gasoline end point of approximately 8" F. which roughly corresponds to about 1.0 per cent. yield from the crude oil. It appears, therefore, that, if the gasoline mere based on a corresponding distillation basis 1930 would show better yields from the crude than 1929. Cracked gasoline increased from 14.83 per cent. in 1929 to 17.46 per cent. in 1930. Percentage of total gasoline from cracking stills has doubled since 192.5, thus indicating the extent to which this phase of refining has advanced over past years. Replacement of the old shell still batteries by a pipe still and single flash system, with an efficient fractionating tower, has proved advantageous both in fuel consumption and in decreasing space required for the installation. Considerable activity has been shown in the field of vapor-phase cracking, with the development of several new types of units. The production of a product with a high antiknock value makes the vapor-phase processes particularly attractive. Cracking equipment has shown a marked advance with the development of corrosion-resisting alloys. Nickel, chromium and vanadium have shown interesting possibilities, but as yet are fairly expensive. Ceramic material for lining reaction

Jan 1, 1931

By AIME AIME

ON March 14, the University of Tulsa was accepted as a member of the North Central Association of Colleges, which ranks Tulsa among the leading universities of the country. A. G. OIiphant recently donated to the new school of petroleum engineering a splendid collection of books on geology, valued at $25,000. Waite Phillips, an oil producer and chairman of directors of The Independent Oil & Gas Co., donated $150,000 for a petroleum engineering building

Jan 1, 1929

By A. H. Geisler

INTRODUCTION THE correlation of property changes during precipitation with structure has progressed, sometimes rapidly but other times more slowly, since the fundamental discovery of Merica, Waltenberg and Scott.1 The predominent factor that hampered the progress has been limitations imposed by the various detection methods. Refinements in X ray diffraction techniques and in metallographic methods, which have been extended by the electron microscope, have contributed new information within the last few years. These permit an extension of the theory as proposed by Mehl and fetter in 1940.2 Now that a suffcient number of alloys has been investigated to establish a general mechanism of the precipitation process, a correlation of the facts into a generally applicable theory of age-hardening is both warranted and desirable. 'I he purpose of the paper is to provide an orderly correlation of the phenomenological facts of precipitation hardening. Speculation on mechanism of hardening will be confined to that consistent with existing theories of hardening. Age-hardening accompanies the formation of a new structure, the precipitate, as provided by an alloy system in which solid solubility decreases with decreasing temperature. Upon this premise alone all such systems would be expected to include age-hardenable alloys. Alas, this is not always the case. Few attempts have been made to explain the variable degree of age-hardening among different alloys or to explain the influence of small alloying additions upon the hardening. Dispersion hardening as originally postulated3 is not adequate.* Coherency hardening-the term that will be used to distinguish the properties of a two-phase mixture in the unique and unstable transition state at which the phases are strained into precise atomic registry (continuity or coherency) in planes

Jan 1, 1948

By AIME AIME

A METALLURGICAL research building is to be erected for the Armour Research Foundation at the Illinois Institute of Technology. It will be located at the corner of Federal and 34th Sts., Chicago, and fully equipped will cost $250,000. It will provide the Middle West with the largest and most complete of facilities for the conduct of developmental and industrial research in this field. The new building will be constructed around an existing foundry and metallurgical research building which has become too small to carry on and service the many research projects contracted for by the Foundation, having to do with steel, alloys, and nonferrous metals. After two bays of the new unit have been completed, the old unit will be torn down and the new one completed.

Jan 1, 1942

By G. C. Mudd, E. J. Myers

Within the last 15 years David Brown Gear Industries has manufactured approximately 200 large mill gears over 6m diam., 58 of them over 9 m and up to 12 m diam. The experience has not been without problems, due to a lack of clear understanding of the loads and stresses imposed on large gear wheels. American Gear Manufacturers Association (AGMA) practices suggest that a service factor be used for mill gears. But what is meant by "service factor"? The layman might be forgiven for believing that the term is synonymous with "safety factor," but this is certainly not true. The service factor is an aggregate of the following in some proportion: -An application factor, i.e., an allowance for the fact that systems do not run smoothly with uniform torque. -An ignorance factor covering the imperfections in the basic gear calculation. -Possibly a safety factor. In the following sections some of the ways in which the limits of applicability can be overstepped are discussed.

Jan 1, 1983

By Philip D. Wilson

IT has been my privilege to read the article prepared by R. S. Dean entitled "Production of Alumina from Low-Grade Domestic Materials" which appears on another page of this issue. Dr. Dean should be congratulated on the preparation of such an erudite and scholarly dissertation on bauxite and on the work which the Bureau of Mines has been doing in connection with the development of processes to use low-grade domestic materials.

Jan 1, 1943

By J. McD. Porter

IN many of the old placer-mining districts are still to be found large tracts of gold-bearing gravel not suitable to be worked with a dredge, because the bed is too shallow- or the gulch too narrow. Frequently there is not enough grade to handle the gravel successfully by ground-sluicing or a bedrock flume, or it contains too many boulders to be worked successfully with the ordinary pipe or tube hydraulic elevator. In southwestern Oregon, two practical placer-miners named Ruble, after working for years trying to make money out of placer-ground containing many large boulders, invented and patented a hydraulic elevator of an entirely new type, and one . that has been found to work very successfully in flat' ground and in gravel containing many large boulders. It is a very simple contrivance. A few years ago I acquired the property near Pierce City, Idaho, known as the American placer-mine. Various attempts .bad been made to work this ground. A bed-rock flume had been installed by one company, an Evans elevator by another, and still other methods were tried on a smaller scale. All were unsuccessful. I installed a Ruble elevator, and it has proved very satisfactory. Working under 100-ft. (pipe) head, the 'ground has been handled at a cost of a little less than 8 cents per cubic yard. The conditions at the American mine are exceptionally hard, the boulders being large, heavy, and numerous. Basalt-boulders, up to a size of 16 by 18 by 32 in., have been elevated to a height of 16 or 17 ft., with a 4-in. nozzle-stream, under 100-ft. head. Boulders larger than this size are blasted. At the American mine, a foreman, two pipemen, and two laborers are-required per day of 24 hr. to operate the elevator. Several sizes of this elevator are in use, the one at the American mine being the 25-ft. size, having 25 ft. of grizzly

Oct 1, 1909

By K. P. Mukherjee, K. P. Gupta, J. Bandyopadhyaya

Even though a lot of work has been done in the past to establish phase equilibrium in the Cu-Si system a re cent investigation casts some doubt about the existence and crystal structure of some of the phases that form in the composition range of 15 to 25 at. pct Si in Cu. The present investigation was carried out using high temperature X-ray diffraction technique along with other standard techniques to study the phases in this composition range. The high temperature 6 phase appears to be tetragonal with parameters a,, = 8.815A, c, = 7.903A, and co/ao = 0.896. The reported bcc E phase exists at room temperature and at least up to 780°C and appears to undergo a transformation near 600°C. The phase appears to be cubic but not of the bcc type. The ? phase appears to undergo a transformation, as has been indicated by earlier investigators, and the low temperature form of .? phase is tetragonal with parameters a, = 7.267A, co = 7.8924, and co/ao = 1.086. THE Cu-Si binary system has been investigated by several investigators1" and several intermediate phases,?,e,?' at lower temperatures and ?,ß,0,e, and ? at higher temperatures, were observed between terminal solid solutions of copper and silicon. Even though the existence of the e phase and the transformation in the ? phase were reported in many early works, in a recent study of this system Nowotny and Bittner6 doubted the existence of the e phase and phase at 550°C. Among the high temperature phases, the 6 phase was reported to have a complex cubic structure with parameter a, = 8.805A.7 Nowotny and Bittner, however, suggested that the structure of the 6 phase might be of CsCl type. In order to check these contradictory reports the present study was taken up to investigate the Cu-Si binary system in the composition range of 17 to 25 at. pct Si. EXPERIMENTAL PROCEDURE Weighed amounts of copper (99.99 pct) and silicon (99.9 pct) were induction melted in recrystallized alumina crucibles under argon gas atmosphere. The alloys containing 17, 18, 20, 21, 21.2, 22, and 24 at. pct Si were annealed in evacuated and sealed quartz capsules at 700°C for 3 days and subsequently water quenched. Other than this annealing, the 21.2 at. pct Si and 24 at. pct Si alloys were annealed at 550°C for 10 days, the 17 at. pct Si alloy was annealed at 750°C for 3 days, and the 22 and 24 at. pct Si alloys were annealed at 780°C for 2 days. All annealing temperatures were controlled to within *l°C. Alloys after quenching were subjected to metallographic and X-ray diffraction investigation. A solution containing 5 g FeC13 + 10 cc HCl + 120 cc H2O diluted with six times its volume with water was used as etching reagent. A 114.6 mm diam Debye Scherrer camera was used for obtaining diffraction patterns. The 17, 21.2, and 24 at. pct Si alloys were subjected to high temperature diffractometry using a Tempress Research High temperature attachment and a GEXRD VI diffractometer. For the 6 phase (17 at. pct Si alloy) powder specimen from a 750°C annealed alloy was reheated to 750°C in the high temperature attachment for 1½ hr before taking a diffraction trace. A 550°C annealed and slowly cooled phase (24 at. pct Si) alloy was first reheated to 550°C. a diffraction trace was made after annealing it for 2 hr, and subsequently it was heated to 716OC and kept at this temperature for 2 hr before taking a diffraction trace. For the e phase (21.2 at. pct Si alloy) a 550°C annealed and slowly cooled specimen was heated first to 425°C and annealed at this temperature for 2 hr before taking a diffraction trace. Subsequently, the specimen temperature was raised to 495", 540°, 603", 635", 682", 720°, and 748°C and homogenized at each temperature for 1 hr before taking diffraction traces. The powder specimen temperature was controlled to within +2oC at each temperature and argon gas, purified by passing it at slow rate through a fused CaC12 column, hot (800°C) copper and titanium chips and finally through a P2O5 column, was used to prevent oxidation of the powder. For all X-ray work copper-radiations at 25 kv, 15 ma (for Debye Scherrer technique), and 40 kv, 20 ma (for diffractometer tech-nique) were used. RESULTS AND DISCUSSION At 700°C the alloys containing 17 to 21 at. pct Si showed two phases while the 21.2 at. pct Si alloy was found to be single phase. The X-ray diffraction patterns of the two-phase alloys were consistent with the phase (ßP-Mn type structure) and the phase (21.2 at. pct Si) patterns. The diffraction patterns of the 17 at. pct Si alloy quenched from 750" and 700°C were identical. According to the accepted Cu-Si phase dia-gram4,5,10 the 17 at. pct Si alloy at 750°C should be in the (k + 6) two-phase region and very close to the -phase boundary. The identical patterns possibly resulted from the decomposition of the 6 phase on

Jan 1, 1970

By W. M. Corse

I bring this investigation to your attention to emphasize the needless waste attendent upon the use of tin plate with an unnecessarily heavy tin coating. With our present knowledge, we are unable commercially to produce coatings as light as the lower weights used in this test. If, however, future research should develop means to this end, the resultant product would meet all practical requirements, and a very considerable saving in pig tin would result. DISCUSSION G. H. Clamer.-—The National Canners' Association is studying the action of fruit juices, etc., on solders. Of course these tests will take quite a long time, and we hope by that time the war will be over and there will be no need for conserving tin for war purposes. Germany for a great many years has prohibited the use of more than 37 per cent. of lead in alloys used in contact with food products. The eutectic composition is 37 per cent. of lead and 63 per cent. of tin; alloys containing more than that percentage of lead have some free lead. J. W. Richards,' South Bethlehem, Pa.—A great deal of conservation can result from the packing of dry foods in cartons and in fiber packages instead of using sheet tin. Many of the boxes used for packing things other than food are frequently made of sheet tin because it prints and lithographs well; these could be made of sheet iron coated with copper or some other substitute metal which prints equally well. The Aluminum Bronze Industry W. M. CORSE,† Mansfield, Ohio.—The conservation of tin, in view of the shipping situation, is one of great importance. Several methods of conservation can be employed: 1. Reduction of the amount of tin in an alloy or compound. 2. Substitution of an entirely different metal or compound for tin. 3. A combination of the first and second methods. The second method is the one that I wish to discuss. Metallic aluminum, has been known for a long time, and its use in copper alloys was discovered about 1855 by Lord Percy. The high cost of production of metallic aluminum retarded its commercial development, and it was not until the discovery of the electrochemical processes for its production that it came to be known as a common metal. I have been particularly interested, for the past few years, in working with the alloy known as aluminum bronze, which is usually composed of approximately 90 parts of copper and 10 parts of aluminum, by weight.

Jan 1, 1919