Search Documents

By John Hall

(New York Meeting, October, 1913.) THE Fremont test for measuring the energy consumed in breaking a notched bar of steel is not so well known in this country as it deserves to be. The test specimen used in this test is about 3/8 by 1/4 by about 11/4 in., notched with a hack saw on the lower side to cause the piece to break at a fixed point. A weight of 10 kg. falling 4 m., and provided with a knife or. chisel which strikes the specimen, breaks the test piece by impact. The residual force in the falling weight after it has broken the specimen is recorded by a suitable device, and the difference between the total energy and the residual energy of the weight (in kilogrammeters) is the force consumed in breaking the specimen. An experience of several years with the Fremont testing machine has shown its great value in readily detecting brittleness not revealed by tensile testing or slow bending testing. In this paper it is proposed to discuss (1) the supersensitiveness of the test as applied to cast steel and (2) its value in revealing the effect of heat treatment under certain conditions.

Jan 7, 1913

By T. S. Lundy, J. Askill

J. Askill and T. S. Lundy (Oak Ridge National Laboratory)—Moore has proposed a simple correlation between the activation energy for solute diffusion in fee metals and the atomic volume of the diffusing species using both tracer and chemical-diffusion data. The first point we wish to make is that it is wrong to attempt such correlations without separating the two types of data. Activation energies obtained using tracer techniques cannot, in general, be directly compared with those obtained from chemical-diffusion experiments. A knowledge of the variations of chemical potentials with composition is necessary and chemical-diffusion data must be corrected for such variations, even for dilute alloys, before a comparison is possible. Secondly, for nickel, iron, aluminum, and lead, Moore neglected a number of recently published works, e.g., Al26 and Mn54 in aluminum,46 cr51 in nickel,47 and Fe55 in iron.48 These and others should have been used. If one considers only the tracer diffusion data, there is left no simple correlation of the type proposed by Moore. For example, in the case of solute diffusion in aluminum the only reliable tracer data listed by Moore are for zinc and aluminum. The nickel, cobalt, and iron data of Agarwala49 are representative of near-surface diffusion-not bulk diffusion. In conclusion we suggest that for tracer diffusion data in these fee metals there is no justification for proposing any simple correlation of activation energy with atomic volume using the limited data that are presently available. R. H. Moore (author's reply)—The writer has proposed a simple correlation which is useful in estimating the internal consistency of diffusion data. The accuracy of the correlation is, of course, a function of the number of data available. Lundy and Askill take issue with the writer's decision to include data for the systems: nickel, iron, aluminum, and lead, taking the view that the data are insufficient to establish the correlation. The writer agrees that the data are insufficient and has cau- tioned the reader that the correlation is tentative in these instances. Inclusion of these systems is justified by the interesting trends the correlation reveals. For example, the distinction between interstitial and substitutional diffusion may be clearly established, Figs. 4 and 6, and the behavior of transition elements and nontransition elements is indicated to parallel the behavior illustrated by the silver and copper systems. Lundy and Askill have singled out the aluminum system for special criticism. The writer chose to discuss the data for diffusion of iron, nickel, and cobalt in aluminum in the terms used by the original authors9 and has included the comments of Balluffi.l0 The writer did not intend the reader to conclude that data for these elements should correlate with data for the nontransition elements as Lundy and Askill have evidently assumed. Iron, nickel, and cobalt form intermetallic compounds with aluminum, so the activity coefficients of these elements may be expected to deviate markedly from unity. This may account for the low frequency factors observed by Hirano.9 The nontransition elements, on the other hand, yield relatively simple phase diagrams with no evidence for intermetallic compound formation as in the case of iron, nickel, and cobalt. In dilute solution, Henry's law should be closely obeyed, the activity coefficients should not deviate markedly from unity, and the effect on the activation energy should not be large. The accuracy of the correlation applied to these systems will improve as the data is extended. It does not seem unreasonable to conclude that its extension should be encouraged.

Jan 1, 1965

By Kenneth Seaver

(San Francisco Meeting, September, 1915) INTRODUCTION IT is rather gratifying that in the field of the manufacture 'of refractories, in which, as a whole, foreign practice has surpassed us, the United States stands pre-eminent in the making of silica brick. In some instances European manufacturers have refused point-blank to credit the possibility of making to such specifications as are common with us, until the actual 'completed shapes were shipped for inspection. But both the manufacturer and consumer in foreign lands are now frankly learning from us, and benefiting by our advanced practice in this field, as is evidenced by the orders placed here and the efforts put forth abroad to come up to the standard of American-made material. In no metallurgical operation has the employment of silica brick spread with. such leaps and bounds as in the building of plants for the carbonization of coal, particularly in the byproduct coke oven. Today, in practically all types of oven, the structure above the floor level (except the facings) is of silica, while in the recuperative and in some regenerative types, its use is extended to that portion of the oven below the floor as well. By reason of the fact that there are a number of classes of refractories of higher silica content than the usual so-called fire-clay brick, there is sometimes a misunderstanding as to the class of material referred to as "silica" brick. We here refer only to a brick having a silica content of 94 per cent. or more and made usually from quartzite rock with a small percentage of lime as a binder. The term "silica" brick is sometimes rather loosely applied to brick front highly siliceous clays, or to a quartzite refractory of mingled fire-clay and quartz rock; but such products are not considered in this discussion.

Jan 9, 1915

By B. C. Allen

The interface energies of chronzium, molybdenunz. hugsten, and their solid-solution alloys Cv-35Re, MO-33Re, and UJ-25Re were studied at 0.6 to 1.0 of the absolllte liquidus ter)zpe,vature using fiz&apos;e )izethods. Liquid surface tension, yv , was deter mined clsing the pendant-drop and drop-weight methods. Results are, respectizlely, 1700, 2370, and 2480 +100 dynes per ct for the rhernium -containing alloys and essentially the same as tlwse reported for liquid chro)riln, trolybdenum, and tungsten. Average solid slrjace energy, rsv< xias ))zeasured using tlre fiber-extetlsion method. The ratio of ysS, the acerage high-angle grain-boundary energy, to ySV cclas jolnd fronz grain-bolzdary grooue angles fort)zed at the surface in an inert atrfizosphere. Absolllte iute?:face energies were deterawined using ?nultip/rase equilibria involzing suitable liquids of known surface tension (tin, silver). Interpretation of the experimented results in view of pvobable tenzperatzcre, orientation, and purity effects giz,e the follouling approximations in ergs per sq ctn: ysv (i2lo. Mo-33Re) - 2100, ySS (Mo, Mo-33Re) - 800, rr (defornzation twins in MO-33Re at 1200"C) - 800. ysV (Cr. Cr-35Re) - 2400. YSS (CY, Cr-35Re) - 1000. Probably Ylv- YSV- 2500 for tungsten and W-25Re, giving yss (It&apos;, W-25Re) - 900. The interface energies of solid and liqid ch?&apos;omiu?.z, nolybdenu?rr, and tungsten are not geatly aff&apos;ected by rhenium and therefore are not a ttlajor factor in the ductili zing rhenium effect in Croup VI-A metals. THE interface energies of the refractory Group VI-A metals, chromium, molybdenum, and tungsten, are not well-established. The objective of this investigation was to study the liquid surface tension, solid surface energy, and grain-boundary energy of these metals and compare them to those found for the bcc solid-solution alloys, Cr-35e,&apos; 0-33e,&apos; and -25e. Five techniques were used to measure interface energies in high-purity polycrystal rod, wire, and sheet at 0.6 to 1.0 of the absolute liquidus temperature. The alloys were chosen to see if there was any connection between interface-energy behavior and the ductilizing rhenium effecL4j5 EXPERIMENTAL WORK Materials. A description of the materials used is presented in Table I. Chromium rod was prepared by arc melting iodide process crystals supplied by Chromallo Cor., hot extruding, and warm swaging to 0.63-cm-diam rod.6 The sheet was prepared by rolling as-extruded rod to 95 pct reduction in area from a hydrogen furnace at 800" to 900°C and surface grinding off 0.02 cm from each face. Cr-35Re rod was prepared by arc melting sintered rhenium powder and iodide chromium crystals, warm rod rolling to 50 pct reduction in area in cans, and swaging to 60 pct reduction in area at 1100" to 1200°C. Some of the rod was warm-rolled to sheet and then surface-ground. Portions of swaged chromium and Cr-35Re were further reduced by swaging and drawing to 0.013-cm-diam wire by the General Electric Co. Mo-33Re and W-25Re rod, sheet, and wire were provided by Chase Brass and Copper Co. The molybdenum sheet consisted of two lots, both essentially the same except for the carbon content. Liquid Surface Tension. The liquid surface tension of Cr-35Re, Mo-33Re, and W-25Re was measured by a combination of pendant-drop and drop-weight methods using techniques already decribed." Following out-gassing, molten drops were formed on the ends of centerless-ground Mo-33Re and W-25Re rods by electron bombardment at 5 x 106 mm. Similar drops were formed on outgassed Cr-35Re rods by induction heating under 1 atm of 99.995 pct Ar. Solid Surface Energy. Solid surface energy was measured by conducting microcreep experiments on molybdenum, Mo-33Re, chromium, and Cr-35Re wires at 2350°, 2306, 1550°, and 180O°C, respectively. In preparation, gage marks -2.5 cm apart and -0.001 cm deep were circumferentially scribed on the wire with a razor blade. Weights of the wire material were then attached. Five to seven reasonably straight wires were hung in a container made out of the wire material. The free end was placed through a small hole in the removable top and secured by bending a small portion 90 deg. The containers not only tended to provide vapor-solid equilibrium for the wires but also protected them from gaseous impurities. They were nominally 2.5 cm in diam by 5 cm high and were made from extruded chromium rod, Cr-35Re arc casting, molybdenum bar stock, or welded Mo-33Re sheet. After deg re as ing, the assembly was outgassed at a relatively low temperature to 2 x 10"5 mm and then recrystallized 2 to 8 hr at the creep temperature in a rhenium-element resistance furnace. The static argon atmosphere was gettered by tantalum radiation shielding. Specimen temperature was measured optically to 25"C using calibration with known melting points and blackbody conditions. The wires generally developed a stable bamboo-type structure according to Fig, l(b), (c), and (d) and retained their gage marks [upper portion of Fig. l(d)]. One or two of the weights were clipped off to provide a low load for the creep anneal. To minimize the possibility of bending or breakage, the wires remained attached to the top of the annealing container which was held to keep the wires vertical. The distance between gage marks was

Jan 1, 1967

By William Ian Wark, Alwyn Birchmore Cox

DIFFERENT parts of the world in which mineral separation by flotation is practiced experience vastly different natural temperatures, and in some districts there is a big difference between summer and winter temperatures. It will be shown in this paper that the temperature is of considerable importance where it is desired to separate pyrite or arsenopyrite from other minerals. It is probable that some of the differences obtained in the flotation of these minerals at plants working under otherwise similar conditions are due to temperature variations. The influence of temperature on the flotation of galena, chalcopyrite and sphalerite by xanthates is less marked than its influence on pyrite flotation. EXPERIMENTAL METHOD The methods used have been described previously.1-4 In each test the clean mineral specimen was immersed in a solution prepared by adding the reagents in the following order: (1) sodium carbonate and hydrochloric acid as necessary to buffer the solution and to give approximately the pH value desired, (2) sodium cyanide, (3) copper sulphate, (4) ethyl xanthate, followed by (5) a final adjustment of pH value. After ½ hr. the mineral was tested for a xanthate film by bringing a bubble of air into apparent contact with the submerged polished surface. If true contact (spreading) was not obtained within ½ min. and after cleaning the surface by wiping with a small linen pad, it was concluded that the adsorption of a xanthate film had been prevented. Following the method already described (ref. 2), curves have been constructed such that for a solution &apos; composition corresponding to any point below the curve, contact between mineral and air is possible, whereas for a solution composition corresponding to any point above the curve, contact is impossible.

Jan 1, 1938

By Y. C. Kim, S. L. Barua

M. Armstrong&apos;s paper is very interesting and can be regarded as a pioneering work of applying geostatistics on washed coal. The density levels used in her study are uniformly spaced, which facilitated curve fitting through a proper experimental design. Most of the existing coal washing plants in the US, however, gather washability data at non-uniform intervals which, in turn, affects the goodness of curve fitting. We would like to emphasize the importance of having a proper experimental design, if a similar geostatistical application is to be conducted on washed coal. We, at the University of Arizona, tried the variogram on recovery (Kim, Barua, and Baafi, 1982, SME preprint 82-143) which showed a similar pattern as Fig. 4 of Armstrong&apos;s paper. In both cases, the first experimental variogram value is invariably and inexplicably higher than the second variogram value. Although Armstrong ignores the first point because of "small number of sample points," we did not do so because there were 17 sample pairs. As a consequence, we concluded that the obtained experimental variogram was unsatisfactory and that further research is warranted. In other words, this disagreement in variogram interpretation between M. Armstrong and the University of Arizona begs the question whether the experimental variogram of Fig. 4 truly reflects the spatial correlation in washed coal, assuming there is such a correlation. Finally, we wish that Armstrong could have done a similar study on clean sulfur, which is a vital interest to the coal mines in the US. Her implied remark on sulfur in the concluding section of the paper may turn out to be incorrect because our experimental variograms on clean sulfur at different density levels were even less satisfactory than those on recovery. ?

Jan 1, 1986

By ALFRED T. BARR

In certain areas of the New Cornelia pit, considerable secondary blasting is necessary to reduce oversized boulders, formed from primary blasting, to pieces which will pass the 41/2-cu yd dippers on the shovels. Some of the boulders are &apos;dobied, but when time permits they are blockholed and blasted. In most instances one hole drilled to a depth of 2 to 3 ft and blasted with 1/3 to 1/2 of a stick of powder will break a boulder satisfactorily. Blockholing is normally done by using a jackhammer of the 55-lb class, 1-in. round drill steel, and detachable steel bits, 2-in. gauge when new. A bit change is usually made after the completion of each hole. The use of light drilling equipment in blockholing is desirable, both from the standpoint of safety and ease of doing the work, and when it was seen there was a possibility of using a lighter jackhammer through the use of tungsten-carbide bits and at the same time get at least the same drilling efficiency as with the standard equipment, it was decided to test tungsten-carbide bits. The claims for long life of the bits and footage drilled before resharpening gave hopes of eliminating much of the delay time in changing bits which is unavoidable with the use of steel bits. and thus gain in actual drilling time.

Jan 1, 1949

By Cyril Smith

FOR several years an investigation has been in progress in the research laboratory of The American Brass Co. to determine the thermal and electrical conductivities of most copper alloys of commercial importance and several of scientific interest. This paper contains such data on the binary alloys of copper with silicon, aluminum, manganese and nickel, and on a large number of ternary or more complex alloys. Some inter-esting general relationships between the thermal and electrical conductivi-ties for all copper alloys at all temperatures are pointed out. The data for the copper-zinc, copper-phosphorus and copper-tin binary systems have already been published1,2 ? except for the electrical conductivity at 200° C., which is given in the appendix of this paper.

Jan 1, 1935

UNIVERSITY OF ALABAMA University, Ala Mining and Metalliaigical Society* G L Roberts, President T G Patterson, Vice-President B B Copeland, Treasurer K F Stark, Secretary G T Bator, Faculty Sponsor F H Crockard, Counselor

Jan 1, 1949

By Olav Idelgeland

FROM indirect evidence point defects have been believed to influence the fatigue behavior of metals and alloys.1,2 Measurements of changes in resistivity made after cyclicstressing at low temperatures indicate that a very high density of defects is present, part of which may be removed by room-temperature annealing.3&apos;4 These results are consistent with the generation of a high number of point defects at low temperatures. Corresponding measurements made after room-temperature stressing did not show any recovery effects.3 This was attributed to a stabilization of the dislocation network after a few thousand cycles without generation of vacancies. In this laboratory resistance measurements of copper single crystals, shaped as normal fatigue specimens ,5 have been made with a Kelvin double bridge at room temperature during and after cyclic stressing at 80 cps by comparing with a dummy at a close and constant temperature. Temperature differences were measured to ±0.025°C with fine thermocouples taped onto the gage lengths. Potential leads were tin-soldered into small holes in the gage length to give stable values. Corrections for differences in temperature and changes in mean length of the specimen were made according to the formula:

Jan 1, 1968

By E. S. Machlin, W. R. Yankee

IN a previous study1 of the effect of heating com-mercial titanium in air on its subsequent friction coefficient against other metals, as well as itself, it was found that the friction coefficient markedly decreased from a value of about 0.7 to about 0.3. A tentative explanation was given that surfaces normally produced at room temperature are not contaminated sufficiently to prevent seizing or welding of the titanium to the softer mating metals. The latter tend to cleanse themselves during rubbing over the harder titanium. It was thought that the lack of a contaminant protective film on the titanium was due to the high solubility of titanium for oxygen and nitrogen and hence an inability to form a contaminant oxide or nitride. This explanation requires the ratio of the surface absorption rate to the diffusion rate to become much lower at room temperature than it is at high temperatures. In order to check the phenomenon further, commercial titanium specimens were nitrided or oxidized at 800°C for 20 hr in flows of prepurified N2 and 01, respectively, at about 1/2 in. H2O above atmospheric pressure. Friction runs were made in argon using a freshly cut copper hemisphere (cut in argon) on surfaces cut successively into the diffusion layers in the titanium (cut in argon) using the techniques described in a previous publication.&apos; DPH values (100 gram load) were made as a function of depth into the diffusion layer using a Tukon tester. Also, micrographs were taken at separate cross sections to indicate the diffusion layers. The results obtained are presented in Figs. 1 and 2, which show the "static" friction coefficient vs hardness for the nitrided and oxidized specimens, respectively. A separate measurement of the friction coefficient of clean copper vs iodide titanium also was made. From results reported in the literature&apos; giving the oxygen and nitrogen contents as functions of the hardness, cross plots were made showing the friction coefficients as functions of the amount of interstitial solute. These plots are given in Figs. 3 and 4. From micrographs of the diffusion layers and the phase diagrams, it was deduced that the data in Figs. l through 4 correspond to the single phase a region. The points observed on the compound regions have been excluded from the figures. It is apparent that nitrogen or oxygen in solution in the a titanium markedly affects the friction coefficient against a softer mating metal. Discussion of Results These results are extremely interesting from both a practical and theoretical viewpoint. The theoretical implications will be discussed first. According to Bowden, the friction coefficient should be given to a good approximation by the relation where a is the fraction of contact area that has welded, a is the shear strength of weaker component, and H is the hardness of softer component. Using this relation alone, it is difficult to understand the results because none of the terms should be affected by a variation in the oxygen or nitrogen content of the harder and stronger metal, titanium. Even if the ratio of S/H for titanium is used in Eq. 1, the ratio has been shown to be independent of oxy-gen or nitrogen content.&apos; If a more rigorous equa-tion is used combining Eq. 1 and a result given pre-viously" for the case where welding is absent, then the relation obtained is µ = a S/H + (1-a) a W aß/H where a is constant and Waß is the work of adhesion between the two metals comprising the friction couple. This relation states that if a is less than 1/2 or so, variation in the work of adhesion Waß between copper and the titanium should affect the friction coefficient markedly. It is reasonable to expect that the work of adhesion will depend on the oxygen or nitrogen content of the titanium. Available data4 show that clean metals and oxides have much lower works of adhesion than the same metals against the

Jan 1, 1955

By George S. Ramsay

The Appalachian system contains the largest area of all known Carboniferous coal-fields. Beginning near the north line dividing Pennsylvania and New York, it extends southwest through West Virginia, southeastern Ohio, Kentucky and Tennessee and terminates in Alabama—a distance of about 950 miles. The northeastern part of this field will be considered in this paper. The general dips of the measures are toward a trough about parallel to the Ohio river, from the Allegheny mountains and ridges on the west. The Potonlac field is an exception; the dip in this case being northeast, the folding to the east of the Allegheny mountains in Pennsylvania being of a greater degree and diminishing southwestward. The cause of the general dip to the west of the mountains seems to be the westward movement of the thrust east of the mountains, with the large Nittany fold including other folds to the east of the escarpment, raising the mountains high above the coal-fields to the west, making a general slope toward the Ohio river southwest, and crossing waves of anticlinals west ward. The synclinals contain the coals, while in many cases on the top of the folds or anticlinals some of the veins (or, in some cases, all) are eroded. The Coal-Measures of this field are generally divided into three principal divisions, known as the Upper, the Barren, and the Lower Coal-Measures, but there is a tendency to divide them into five groups, which is more convenient. Beginning at the bottom, the first would be the Conglomerate ; second, the Lower Coal-Measures; third, the Barren; fourth, the Upper Coal-Measures, and fifth, the Upper Barren or Permian Measures.

Jan 1, 1896

By Edward H. Robie

SEPTEMBER usually being a fine month for motoring, we set out with our better half at the end of August in our Studebaker for points West. A combined business trip and vacation. The first night found us 392 miles away, at the Statler Hotel in Buffalo, and the next morning we revisited Niagara Falls for the first time in some forty years. The cataracts were as impressive as ever and certainly worth a day of any vacationist&apos;s time, instead of the half hour we could spare before going on to Chicago. The Centennial of Engineering, the hundredth anniversary of the founding of the ASCE, no doubt attracted the greatest gathering of engineers in history but still the attendance was disappointing to most of the forty or fifty societies that participated. Perhaps the time-the two weeks following Labor Day-was unfavorable. Few could afford to spend ten days away from home and business at that time of the year. Fall meetings of the AIME normally attract far more than the 300 that registered in Chicago. The technical program, however, was excellent, especially that arranged by the Minerals Beneficiation and Industrial Minerals Divs. The mineral industry papers of a more general nature that were presented as a part of the Centennial program on Monday and Tuesday of the following week were of high quality and offered by top names but had a meager audience. Undoubtedly the celebration brought engineers and engineering to the attention of millions of people. The pageant at the Museum of Science and Industry proved continuously interesting, showing the progress of engineering following the first use of fire. The show continued for many weeks. A special stamp was issued by the Government, which engineers might well use on their Christmas cards or other mail this year. After six days in Chicago we set out north, first visiting Fairbanks Morse in Beloit and Allis-Chalmers in Milwaukee. Will Mitchell&apos;s Basic Industries Research Laboratory is doing interesting work and being installed in more comfortable quarters. The next day at Ishpeming, C. W. Allen arranged for luncheon with a local group of AIME members and we then looked over the new surface plant of the Mather B mine, a model of modern functional design. Then on to a small dinner meeting at Calumet following cocktails at Endicott Lovell&apos;s attractive summer home on the lake at Point Mills. The new Memorial Union Bldg. at Houghton, where we were domiciled for the night through the courtesy of Roy Drier, is a beautiful modern addition to the college, a model of its kind.

Jan 1, 1952

By Andrew Hyslop

In our never ending search for new and better ways of underground mining, we find that transportation has had its share of new ideas in the past few years. The old and still effective method of track haulage has had some competition from rubber-tired cars and belt conveyors, each of which has its own safety hazards which demand close scrutiny in any safety study. The use of shuttle cars, in particular, has introduced clearance hazards caused by the absence of the more or less positive guides formed by the rails of a track sys- tem; likewise the requirement of greater clearance tends to increase roof hazards which we all know to be great enough with the best of methods. However, the subject of transportation hazards is too broad to be covered entirely in one paper, so I will confine myself to track methods which carry the preponderance of underground tonnage. I am quite sure that to this group it is an evident fact that haulage accidents are of major importance. However, to stress the point, it may be well to look at a few figures. Safety statistics can be quite boring and often are subject to question as to mathematical accuracy because of different

Jan 1, 1949

At a large meeting of the members of the American Fund for French Wounded it which Mr. Franklin D. Roosevelt presided and at which Mrs. B. Girault Lathrop, President of the Paris Administration A. F.F. W., gave a most interesting address, special rows of seats were reserved for the members of the W. A. A. I. M. E. Those who were unable to be present will be glad to hear that Mrs. Lathrop complimented our organization on having supplied the largest dispensary operated by the A. F. F. W. and the Red Cross in northern France. The A. F. F. W. is going to erect an American Memorial Hospital at Rheims and it is hoped that the one hundred beds in the hospital will be endowed in memory of the men who gave their lives for the liberty of the world. It will be possible not only to endow beds, for which sums of $6000 each are needed, but also to give, as. memorials, sun- parlors at a cost of $10,000 each, two roof gardens at $5000 each, a laundry at $10,000 and a garage at $10,000. The New York Section has undertaken to endow a heel in memory of members of the A. I. M. E. who gave their lives in the Great War. Perhaps other Sections or groups of Sections may wish to do the same thing, or if no other Section cares to assume so much responsibility possibly individuals may like to join the fund already growing in New York, in which case they should send their contributions to Mrs. W. Y. Westervelt, 1 Lexington Ave., New York, N. Y.

Jan 6, 1919

By Alwyn Birchmore Cox, Ian William Wark

Different parts of the world in which mineral separation by flotation is practiced experience vastly different natural temperatures, and in some districts there is a big difference between summer and winter temperatures. It will be shown in this paper that the temperature is of considerable importance where it is desired to separate pyrite or arsenopyrite from other minerals. It is probable that some of the differences obtained in the flotation of these minerals at plants working under otherwise similar conditions are due to temperature variations. The influence of temperature on the flotation of galena, chalcopyrite and sphalerite by xanthates is less marked than its influence on pyrite flotation. Experimental Method The methods used have been described previously.l-4 In each test the clean mineral specimen was immersed in a solution prepared by adding the reagents in the following order: (1) sodium carbonate and hydrochloric acid as necessary to buffer the solution and to give approximately the pH value desired, (2) sodium cyanide, (3) copper sulphate, (4) ethyl xanthate, followed by (5) a final adjustment of pH value. After ½ hr. the mineral was tested for a xanthate film by bringing a bubble of air into apparent contact with the submerged polished surface. If true contact (spreading) was not obtained within ½ min. and after cleaning the surface by wiping with a small linen pad, it was concluded that the adsorption of a xanthate film had been prevented. Following the method already described (ref. 2), curves have been constructed such that for a solution composition corresponding to any point below the curve, contact between mineral and air is possible, whereas for a solution composition corresponding to any point above the curve, contact is impossible.

Jan 1, 1939

By Ian William Wark, Alwyn Birchmore Cox

Different parts of the world in which mineral separation by flotation is practiced experience vastly different natural temperatures, and in some districts there is a big difference between summer and winter temperatures. It will be shown in this paper that the temperature is of considerable importance where it is desired to separate pyrite or arsenopyrite from other minerals. It is probable that some of the differences obtained in the flotation of these minerals at plants working under otherwise similar conditions are due to temperature variations. The influence of temperature on the flotation of galena, chalcopyrite and sphalerite by xanthates is less marked than its influence on pyrite flotation. Experimental Method The methods used have been described previously.l-4 In each test the clean mineral specimen was immersed in a solution prepared by adding the reagents in the following order: (1) sodium carbonate and hydrochloric acid as necessary to buffer the solution and to give approximately the pH value desired, (2) sodium cyanide, (3) copper sulphate, (4) ethyl xanthate, followed by (5) a final adjustment of pH value. After ½ hr. the mineral was tested for a xanthate film by bringing a bubble of air into apparent contact with the submerged polished surface. If true contact (spreading) was not obtained within ½ min. and after cleaning the surface by wiping with a small linen pad, it was concluded that the adsorption of a xanthate film had been prevented. Following the method already described (ref. 2), curves have been constructed such that for a solution composition corresponding to any point below the curve, contact between mineral and air is possible, whereas for a solution composition corresponding to any point above the curve, contact is impossible.

Jan 1, 1939

By T. J. Koppenaal, M. E. Fine

The critical resolved shear stress of aCu-A1 single crystals has been investigated as a function of composition, testing temperature, and strain rate. The strength, and its temperature and strain rate dependency increase markedly with aluminum content. The solid solution strengthening at 4.2°K is much larger than at room temperature. The activation energy for the low temperature dislocation cutting process increases from about 0.17 ev for a 0.5 at. pct A1 alloy to about 0.50 ev for a 14 at. pct A1 alloy. This result is attributed to an increase in the width of extended dislocations due to the known decrease in the stacking fault energy. In addition, the activation volumes at 4.2 and 77°K decrease with aluminum additions. Concerning the solid solution strengthening in the 296° to 373°K range, no definite conclusions are reached, but it is suggested that subgrains and cutting of subgrains are important. In a previous paper,&apos; the authors reported that adding aluminum to copper produces two types of strengthening: a yield point effect and an increase in the lower yield stress. This behavior is illustrated in Fig. 1 by shear stress-shear strain curves of furnace-cooled single crystals of pure copper and Cu-14 at. pct A1. The yield point effect, At, was thoroughly studied previously1 and shown to be associated with short-range order. The present paper reports an investigation of the lower-yield stress in aCu-A1 single crystals as a function of composition, testing temperature, and strain rate. EXPERIMENTAL PROCEDURE Single cryski1 tensile specimens were prepared in the same manner as previously described.l Briefly,

Jan 1, 1962

By Gilbert E. Doan

IN a technical civilization, that is. one whose major difference from past civilizations is its enormous development of technology, in transportation, communication, labor saving, centralized control, and mass production, it is natural that the most critical problems should be those that arise out of technologic advances; it is natural also that a. man who understands these advances should be chosen as the leader to meet these problems. This was done in the selection of Herbert Hoover as President of the United States. Mr. Hoover was a good, and perhaps a great President. But he was not a great politician and that ensured his defeat when a crisis came.

Jan 1, 1939

By I. R. Kramer

The stress associated with the surface layer was deter-minedfor iron and molybdcnum. These measurements show that the surface layer plays a very important role in the plastic deformation of bcc metals. From the relationship between strain arui the surface layer stress and the back stress imposed by the internal obstacles, it is Proposed that the term of of the Hall-Petch equation is related only THE large number of studies on plastic flow of bcc metals have failed to delineate clearly the nature of the obstacles influencing dislocation movement. Since there have been numerous articles which have reviewed the mechanisms proposed to explain various aspects of plastic flow of bcc metals (for example, conrad1 and Keh and weissmann2), no attempt will be made here to discuss their conclusions. However, it should be to the surface stress while the term Kfd is the stress required to move dislocations through internal obstacles. Further, it was possible to derive the well-known empirical equation C = , and it is shown that the terprz a is comprised of two terms: a term Cs associated with the surface layer stress and Ci related to internal dislocation obstacles. pointed out that in all of these publications it has been tacitly assumed that plastic flow occurred uniformly throughout the cross section of the specimen (except, of course, for the Luders band region), It has generally been further assumed that the nature and distribution of the obstacles opposing the motion of dislocations are of the same type throughout. The role of the surface layer in bcc metals has not, as yet, been considered even though its role in fcc metals has been shown clearly to be of primary importance.3-5 Investigations on fcc metals have shown that at the onset of plastic deformation a surface layer acts to

Jan 1, 1968