By Jack L. Taylor

Single crystals of tungsten grown from powder -metallurgy swaged rod by high-temperative annealing were deformed in tetzsion at temperatures from 2500 to 5000 OF. Orientation of specittzen tensile axis, strained ratrix, and defortnation bands was determined optically by reflections from {110} etch pits. Slip traces meve analyzed and slip directiorz determined. Results indicate that {110}(111) , {112){111}. and {123}{111} type slip occur in tungsten over the terpe,atuve rutge investigated. Slip is orientation-dependent occuvring on tCuzt cowzbitzation oj slip plane and direction which has the highest critical resolved shear stvess. Overshooting appears to be a general occurrence between 2500' and 5000°F. Dejornatiotz bands show rotation in a directiorz opposite to the yotation of tire tensile axis. DEFORMATION in bcc metals has been reviewed by Maddin and Chen,' Keh and eissman,' and most recently by Nabarro, Basinski, and olt. From these reviews it is apparent that some disagreement exists concerning the crystallography of plastic deformation in bcc metals. There is evidence of noncrystallo-graphic slip, the crystal slipping on or near a noncrys-tallographic plane in the (111) zone for which the resolved shear stress is greatest. There is also evidence to indicate that crystallographic slip occurs in the planes of the same zone. On the other hand, there is agreement that the close-packed direction ( 111) is the slip direction in bcc metals. Further, in pure bcc metals4 and alloys the operative crystallographic slip systems are strongly dependent on temperature. Both crystallographic and noncrystallographic slip have been reportede8 in tungsten, a group VIA bcc metal. The number of slip families which operate in the case of crystallographic slip, however, has been in question. The earliest study by oucher' of single-crystal tungsten tested at temperatures of 1800 to 5000°F led to the conclusion that only {112)( 111) type slip operated. Raymond and eumann recently reached the same conclusion studying deformation by rolling of plasma-flame single crystals at 1800°F; however, only [loo] and [110] orientations were studied. Work at high temperatures by Leber and Pughs on tungsten and Chen and Maddin9 on molybdenum suggests that conjugate slip on nonparallel (110) planes may account for the slip on (112) and (123) planes found by others working with bcc metals. The present paper presents evidence of three families or modes of slip in tungsten in the temperature EXPERIMENTAL PROCEDURE Material. Standard microtensile specimens, 0.160 in. diam by 0.640 in. gage length, were ground from commercial powder-metallurgy swaged tungsten rod, type MK. Specimens were heated for 10 min at 5150°F or 6 hr at 5400°F in vacuum of 1 x 105 Torr or less to produce single crystals. At the lower temperature an average of two out of seven specimens heated in a group developed single crystals throughout the specimen length as shown in Fig. 1, the rest remaining wholly poly crystalline. At the higher temperature, three or four out of seven specimens became single crystal. Other than to note that Laue X-ray photographs generally showed sharp, well-defined spots, no attempt was made to assess crystal perfection or measure dislocation density. Two tungsten single crystals grown from the melt by the plasma-arc process were also used for this study.

Jan 1, 1967

Jan 1, 1967

Jan 1, 1968

By Y. C. Liu, G. A. Alers

The anisotropy of Young's modules has been measured in a series of Cu-Zn alloys containing from 1 to 28 wt pct Zn and cold-rolled to 97.5 pct reduction in thickness. These modulus data show a transition in texture as a function of zinc content. In alloys containing 3 pct Zn or less, the texture is essentially that of copper. A transition is clearly seen to develop in 5 and 8 pct Zn alloys, and to have been completed in a 12 pct Zn alloy. Increasing the proportion of zinc to 28 pct does not produce any further changes in texture. The ease and clarity with which this texture transition can be seen in the modulus data is in great contrast with the inccertainty in the visual detertiination of the range of texture transition from a series of pole figures. It is also shown that the rolling texture of the high zinc content alloys cannot be a one-COIIIponenl texture, characterized by the (110)(112) ideal orientations, as usually assumed. A second, quite important component must also be present. Furthermore, the present data are inconsistent with matrix orientations on which the "oriented growth" hypothesis of the Formation of recrystallization textures is based. THE rolling textures of binary fcc alloy systems have generally been considered to lie between two terminal textures. One of these terminal textures is the copper type and the other is the 70:30 brass type. Alloys of intermediate solute content exhibit a texture which is said to be a transition between the two terminal textures. On the basis of efforts to correlate rolling and recrystallization textures, two concepts have been advanced in the literature on the nature of these transition textures. One school1 suggests that the addition of alloying elements, e.g., zinc, causes a gradual rotation about one of the (111) poles from the (358)( 523) ideal orientation of the copper-type rolling texture to the terminal {1 10)( 112) ideal orientation used to describe the rolling texture of 70:30 brass. This concept is depicted in Fig. 1 with the angle of rotation corresponding approximately to the zinc content and is designated here as the "rotational concept", since the ideal orientation of the transition textures varies continuously with alloy content. The other concept,' the "mixture concept", suggests that the copper-type rolling texture is a two-component texture. {358) (523) and {110)(112). The addition of alloying elements affects only quantitatively the relative amounts of these two components—a decrease in the amount of material in the {385}(523) orientation and an increase of that in the {110)(112) orientation with increasing solute content. An experimental distinction between these two concepts is essential to a better understanding of both the mechanism of formation of rolling textures and the subsequent formation of recrystailization textures in fcc metals. Because of the lack of resolution inherent in pole figures, it has not been possible to differentiate between the two concepts on the basis of this data. Both concepts, in fact, make use of the same set of pole figures but interpret them in a manner acco-rding to the view held.'" Experimental results obtained from inverse pole figures or selected-area electron diffraction3j4 simply -yield more refined pole figures but do not eliminate the ambiguity of interpretation. Quantitative measurement of an entirely different, orientation-dependent property must thus be considered

Jan 1, 1967

By C. M. Sellars, F. Maak

Electvomotie -force measurements hazle been made on ten Au-Ni alloys at temperatures 7754 825O, 900O, and 935°C using galvanic cells with solid electrolyte. Partial and ivtegral thermodynamic functions are derived from the determined activities. which show la9,ge positive deviations jvom Raoult's law. The enthalpies of mixing- are in close accord with calorinletric data and are of comparable accuracy. The results are used to determine the miscibility gap and the spinoidal curL1e, and are qlalitaticely interpreted in terms of the large size difference and electvonic interactions between gold and nickel. Tabulated nalues of the actielities and partial and inteqal free energies, entropies , and enthalpies of mixing are given in the appendix. The Au-Ni binary alloys are of particular interest thermodynamically as despite the large size difference between gold and nickel atoms they have a simple phase diagram.' This shows complete solid solubility above a miscibility gap with a maximum at about 71 at. pct Ni and 810°C. Activity measurements (over a range of temperature) have been made previously on this system using an electrolytic-cell method with a liquid chloride eletrolyte. The accuracy of this data has, however, been queried3'4 as it leads to values for the enthalpy of mixing which are too high when compared with calorimetric measurements.46 Also, the entropy of mixing is too high when compared with the values derived from specific-heat measrements. It was therefore considered worthwhile redetermining the activity data using a galvanic cell with a solid electrolyte (0.85 ZrO, 0.15 CaO). This method is based on a technique introduced by Kiukkola and aner'' and has been used to determine the thermodynamic data for Cu-Ni alloys.' THE ELECTROLYTIC CELL The cell used to determine the activity of nickel in Au-Ni alloys was: The cell reaction, which is discussed for a similar cell by Rapp and Maak, gives a direct measurement of the activity of nickel in the alloys as where aNi(alloy) is the activity of nickel in the alloy, 3 is Faraday's constant, E is the measured electromotive force, R is the gas constant, and T is absolute temperature. For the valid application of this type of cell the arrangement must be ther modynamic ally stable, which means that: 1) The free energies of formation of the oxides fulfill the relation 2) The vapor pressures or dissociation pressures of each component must be so small that during the time of the experiment the amount of any material transported by the gas is negligible. 3) Side reactions which change the alloy composition must be negligible. These reactions are possible both with the surrounding gas atmosphere and with neighboring solid material. The first two conditions are fulfilled by the above cell.' The third condition is approached by care in the experimental technique. The factors which control the attainment of equilibrium in this type of cell have been considered by Rapp and aak, who conclude that metallic diffusion in the alloy is the rate-control ling step. A lower temperature limit for the practical application of this cell is therefore set by the condition that equilibrium must be attained in reasonable times. EXPERIMENTAL MATERIALS AND TECHNIQUE The starting materials were mint gold (99.99 pct Au) and Mond nickel (99.9 pct Ni). Alloys, nominally 5 at. pct Ni and then each 10 at. pct across the system, were produced by vacuum-levitation melting compacts of mixed drillings of the pure metals. The nickel used for the reference tablets in the cells was melted in a similar manner. The alloy ingots, cast in boron nitride molds, were cold-forged and

Jan 1, 1967

By Ashok K. Kakar

THE occurrence of superplasticity in Al-Zn alloys is of interest because of its possible industrial exploitation.' The eutectoid composition (78Zn-22A1) has been the most extensively studied;'-= neck resistant flow and high strain rate sensitivity of flow stress (characteristic of superplasticity) are associated with a micron-size grain conferred on the alloy by an homo-genization and quench.5'6 Compositions away from the eutectoid have received comparatively little attention, especially from the viewpoint of relating the structural

Jan 1, 1969

By H. Morgolin, M. A. Greenfield, P. A. Farrar

In attempts to correlate mechanical properties with microstructure, it is desirable to determine the effect of ß grain size. Determination of 6 grain size is not a problem where a has precipitated at ß grain boundaries. However, in alloys which have been processed to produce an equiaxed a +ß structure the ß grain size is difficult to determine because ß grain boundaries do not etch. The ß grain size can sometimes be laboriously determined by searching for grains which have some a! outlining the 6 grains. This difficulty of ß grain size determination in equiaxed a + ß alloys can be overcome by heating below the ß transus temperature for a short time and water quenching. Fig. 1 shows the starting equiaxed a + ß structure of the Ti-5.25A1-5.5V-0.9Fe-0.5Cu alloy used in this investigation, and Fig. 2 shows the microstructure of the same sample water-quenched after heating 1 min at 1675"F, which is 25°F below the 0 transus. The heavily etched microstructure consists of some equiaxed a! in a structure showing considerable amounts of transformed ß. The ß grain

Jan 1, 1969

By H. I. Aaronson, W. L. Winterbottom, G. M. Pound

On the basis of a statistical thermodynamic treatment of the data of smithz2 on the activity of carbon in austenite, a Darken and smith23 deduced that the interaction energy, wy, between carbon atoms occupying nearest-neighboring interstitial sites is repulsive. Aaronson, Domian, and pound 24 (ADP) have applied two different statistical thermodynamic analyses to the same data. One analysis, a composite of the treatments of Darken and Smith,23 Speiser and Spret-nak," and Kaufman, Radcliffe, and Cohen,26 primarily takes account of the positional entropic effects of wy in dilute solutions. The other, due to Lacher 27 and Fowler and Guggenheim," is also applicable to more concentrated solid solutions. The equations which both analyses produce for a,, can be rearranged so that, when In a,, is plotted against the appropriate function of the carbon content of the austenite, the plot will have a slope of unity when the correct value of wy is employed. Since no other constant need be simultaneously evaluated in order to make this determination, ascertaining the most probable value of wy from Smith's data on the bases of these analyses was an elementary problem in least-squares statistics. ADP demonstrated that the wy's obtained from both analyses vary with temperature in a statistically significant manner. McLellan, Gerrard, Horowitz, and sprague 29 (MGHS), on the other hand, have recently made a new statistical thermodynamic study of a,, and have concluded from this study that wy is independent of temperature. The equation which they derived for a,, is: where 0 = ratio of the mole fraction of carbon atoms to that of iron atoms, z = number of sites from which occupancy is excluded by the presence of a carbon atom and the repulsive character of its interaction with nearest-neighboring carbon atoms (z = zb in Ref. 24), and x = a geometric parameter taking account of overlapping of the exclusion shells of nearby carbon atoms. z is 1 when wy = 0 and 13 when wy = Q. For a given value of z there is a definite value of X . In the absence of an equation connecting z and X, MGHS computed geometrically the value of x at several integral values of z; x increases from 0.47 to 8.67 as z is increased from 2 to 5. MGHS fitted Eq. [I] to the a,, data of Ellis, Davidson, and Bodsworth30 at 925° and 1050°C and to the data of smithz2 at 1000°C. Confining z to integral values in the range 4 to 6, and also somewhat restricting AG, the values of z, X, and AG were sought which would minimize the average root mean square percent deviation, D, of the calculated a,, values from those obtained experimentally. Finding that D was almost always smallest when z = 5, they concluded that z is independent of temperature. Since:23, 26 where R = gas constant and T = absolute temperature, and w,, was considered to be similarly invariant, this statement cannot be strictly true. The temperature range employed, however, was small and the interval between the values of z tested was sufficiently large so that the results could still be consistent with a constant The statistical treatment of the a,, data applied by MGHS is clearly quite approximate. Since more than three values of a,, are available at each temperature, z, and X, and AG have actually been over deter mined, rather than underdetermined as their treatment implies. In order to make more complete and exact use of the a,, data, we shall employ the Legendre Method of Least Squares, as described by Whittaker and Robinson. This technique permits conversion of the overdetermined system of equations produced by the substitution into Eq. [I] of the available pairs of a,, and 0 data at a given temperature into an even determined system. Solution of the latter system yields the most probable value of each of the three constants. This procedure will allow a statistically rigorous test to be made of the conclusion drawn by MGHS in respect of the temperature dependence of In order to obtain linear iiequations of conditions" from Eq. [I], the exact values of the three unknown constants are replaced by G/RT = =/RT + y, where z, i, and aG are estimated values of the constants. This allows the conditional equations to be written in the form:'l where fi -f6, i, =/RT) = the right-hand side of Eq. [I] for a given pair of ayi and values. When applied to Eq. [I], these relationships become: The i equations of condition are reduced to three "normal equations" in the manner discussed by Whittaker and Robinson. The normal equations are then solved for a, ß, and y. Both of these operations are most conveniently performed by means of the computer technique of Winterbottom and Gjostein.32 This technique was used iteratively until the value of 0 (the most sensitive of the three correction factors) became 10.01. (Until they became small, a, 8, and y

Jan 1, 1969

By D. A. Woodford

A number of observations have now been reported where the steady-state creep rate is apparently linearly dependent on the applied stress at high temperature and low stresses. This results in a creep rate greater than that predicted by extrapolation of high-stress data and has obvious practical implications. However, some of these observations are open to question. For example, the analysis by Harris and Partridge17 of the data of Greenfield et a1.18 was dependent on strain rates which, according to the original authors, were too low to be measured. Dr. Bernstein appears to have demonstrated a linear stress dependence at low stresses in two zirconium alloys. There are, however, a number of discrepancies in his treatment of the data and the subsequent theoretical analysis which require clarification. 1) It is incorrectly stated that steady-state conditions are revealed by a slope of unity on a plot of log i vs log (time). This objection is trivial if the author meant to say a slope of zero, although it is unclear how subsequent extrapolation was made to determine the steady-state creep rates at low stresses for the zircaloy-2. If the plot used was actually log c vs log (time), it is unlikely that a slope of unity would represent a constant creep rate. A plot of log (c - co) vs log (time), where c0 is the extrapolated intercept sf the steady-state creep rate on the strain axis, would have a slope of unity during steady-state creep. However, eo cannot be determined unless is is already known. 2) The author chooses to interpret his results based on the equation: where A, and B, are structure-sensitive parameters, Ql and Q, are the activation energies for the particular creep process, and n describes the sensitivity of the creep rate on stress. The first term represents a slip creep process and the second a diffusion creep process. However, it is stated later that "two distinct processes acting in parallel are involved". Eq. [I] surely represents two processes in series since each reacts to the total applied stress and t, is the sum of the individual creep rates. If the processes are acting in parallel, then the effective stress in each would be less than the applied stress. The component stresses would be given by sl + s2 = a but it is not clear how the magnitude of either, or the corresponding stress exponent, could be determined.

Jan 1, 1969

By Harold Margolin

The Ti-Al system certainly merits the investigative attention it has been receiving and this latest contribution by Blackburn is therefore to be welcomed. The titanium-rich end of the phase diagram shown here, as well as the diagram by crossley,17 Clark et a1.,18 and Tsujimoto and Adachi,29 reveal no other intermediate phase than Ti3A1, although a previous work by Ence and Margolin20 had reported an additional intermediate phase. Since then, Buerger Precession pictures of single crystals of 10.5, 11.5, and 12.5 wt pct A1 were made at New York university21 and the extinctions were found to be typical of a D6h a Ti structure. Some superlat-tice spots and/or streaks suggesting the presence of an Mg3Cd structure, i.e., Ti3Al, were also found. Since these specimens had been quenched from the y region20 and had revealed a Ti, it was concludedz1 that y does not exist and the structures interpreted as m + y could not be so considered. The absence of normal two-phase behavior in these structures had been indicated in the paper. Accordingly, the two-phase region y + 6 becomes a + Ti3Al and there is some agreement between the results of Blackburn and of Ence and Margolin20 as to both shape and existence above 900°C of an a + Ti3Al field. Crossley 17 proposed that Ti3Al is a line compound which decomposes congruently at 900°C. It is difficult to discount entirely the fact that clear two-phase structures, varying in amount with position in the two-phase field, could be detected above 900°C by Ence and Margolin.20 Precipitation during quenching could not have been so regular and the twin-phase syndrome17 does not apply. The heat treatment and quenching technique was essentially the same as was used by Crossley, whereas Blackburn, who used a rapid quenching procedure, also showed a two-phase a + Ti3A1 field above 900°C. If the two-phase field exists above 900° C, it is easy to picture a two-phase field which could account for the data of Crossley below 900°C without invoking a line compound existence of Ti3A1. All that would be necessary would be an 0 + Ti3Al/Ti3Al boundary which curved sharply to higher aluminum contents below 900° C. It is clear that the controversy must be solved by techniques which obtain data at elevated temperatures without quenching. It is conceivable that the difference in width of the a + Ti3N fields reported by Blackburn and by Ence and Margolin is due to the longer annealing times used by the latter investigators. The criterion for establishment of equilibrium in our work20 was the

Jan 1, 1969

By F. A. Crossley

The key to disagreements between Blackburn's findings and mine is the word equilibrium". My work attempted to define the equilibrium diagram of the titanium-rich end of the Ti-A1 system. It can readily be shown that Blackburn's conclusions are based primarily on the examination of structures substantially removed from equilibrium. The diagram presented in Fig. 16 is properly labeled a "phase diagram". However, it appears that Blackburn either does not understand or does not accept the difference between "phase diagram" and "equilibrium diagram" as defined in the Metals Handbook.17 The conflict lies not in Blackburn's data but in his interpretation of it, and his use of "transformation", "phase diagram", and "equilibrium diagram" as synonymous terms. I share his view that the light microscope is much inferior to the transmission electron microscope for the study of transformations; but this fact does not render the light microscope useless or untrustworthy. The difficulties experienced with the Ti-A1 system have not been due to the limitations of the light microscope, but rather to the extreme sluggishness in achieving equilibrium at temperatures below 1000° C. Were it not for the light microscope employed with polarized light, the twin phase syndrome' might still be unrecognized and, as a consequence, still adding to the confusion of Ti-A1 investigations. (Ref. 1 should read ... Contract No. N161-25952 ... vol. 236.) Other, more sophisticated techniques, including electron transmission, simply confirm the erroneous tentative conclusions drawn from observations of structures due to the twin-phase syndrome. By the standards of most of the investigations of the Ti-A1 systems, seven of the fifteen compositions investigated by Blackburn were seriously contaminated with oxygen. The writer has found that 0.1 wt pct 0 shifts the a + Ti3A1 boundary to 1 at. pct lower A1 content at 700°C. At constant aluminum content, this corresponds to a temperature shift of the boundary of +25°c.18 Blackburn advises that the first group of alloys contained 0.1 to 0.15 wt pct 0, bur he does say whether the analyses were performed on as-received material or on specimens in their final state of heat treatment. This is especially important considering the 20-mil-thick starting materials. If specimens had been annealed in the two-phase a + 6 region it would have provided an indication of the final degree of oxygen contamination since up to about 12 at. pct A1 the boundaries of this region are well-defined for low-oxygen alloys. Blackburn questions the capability of light microscopy in determining phase boundaries in the Ti-A1 system. I submit that the a/a + Ti3A1 boundary in Fig. 1 of Ref. 1 over the composition range from 10 to 18 at. pct A1 was determined by dilatometry and supported by electron diffraction. Specimens of alloys containing 8, 10, 12, and 14 at. pct A1 were aged at 550°C for 1000 hr (under stress of 5000 psi to accelerate the tendency to equilibrium) and then fractured in tension at room temperature. Collodion was applied to the as-fractured (unetched) surface and, when stripped, carried away particles identified by electron diffraction as Ti3A1. Perhaps Blackburn will explain why these electron diffraction data were ignored. At this time, a technique for revealing or indicating

Jan 1, 1969

By L. S. Castleman, R. K. Hotzler

We are currently studying the effects on recrys-tallization of impurities diffused into dispersion-hardened alloys. Our interest in this phenomenon was originally aroused by the observation that the recrystallization temperature range of tungsten "doped" with alumina and silica, or with thoria, is lowered drastically if nickel is plated onto the tungsten prior to heat treatment.' In this note, we report a similar effect that sulfur has on the recrystallization behavior of thoriated nickel. The experimental procedure for this exploratory phase of the investigation has consisted simply in heating commercially obtained stress-relieved samples of thoriated nickel for varying temperatures and times in sealed capsules containing air and small quantities of sulfur. The samples contain 2.4 vol pct thoria and initially less than 18 ppm S by weight; they are prepared either from 0.5-in.-ciiam rod stock or from 0.092-in. sheet and are in the "as-received" (stress-relieved) condition prior to exposure. In an atmosphere free of sulfur, such samples do not show evidence of recrystallization after being annealed for 1 hr at a temperature of 2500°F (1372C).2 The photomicrograph in Fig. 1 shows the microstructure of one of our samples annealed for 75 hr at 1000° C (1832°F) in a sulfur-free capsule. The grain structure is hardly evident (if at all) at 465 times magnification. In contrast, the photomicrograph of Fig. 2 shows the recrystallization that has taken place in a sample exposed to sulfur for 5 hr at 1000°C (1832°F). A nickel sulfide phase is visible at the grain boundaries of the light-appearing grains. We have also observed recrystallization to occur in a sample annealed at 600°C (1112°F) for 25 hr. This temperature is below the 637°C (1178°F) eutectic in the Ni-S system. In the latter case, no nickel sulfide phase is evident in the microstructure. Moreover, we have noticed the occur-

Jan 1, 1969

By David L. Holt

It is well-established that hydrostatic pressure distribution is hardly achieved during uniaxial compaction of powders. All the previous investigations1-4 give consistent results and this variation is attributed to the die-wall friction. The conclusions are based on measurements of the density of very small portions of the compact. Although the analysis of the density or the strain distribution in the compact is very helpful in obtaining information about the stress distribution within a powder compact, it does not describe the problem from a more fundamental point of view. The densification in metal powder compacts takes place chiefly by plastic deformation (ignoring particle rearrangement) at the points of contact of the powder particles. The onset of yielding and subsequent growth of the contact areas (for spherical powders) take place fixed by a constant stress equal to three times the yield stress in tension or compression,5-7 assuming little or no work hardening. Therefore, by deforming spherical powders in the die and measuring the contact areas on each particle, the load at each contact point can be determined. In the present investigation, this was done by hot-pressing uniform spheres of lead, K-Monel, and sapphire. The details of the experiment have been described elsewhere.' The spheres were studied for the size and the number of contact points on each particle using a specially designed goniometer. It was found that the deformed faces that were approximately normal to the direction of pressing were about 2.2 times larger than those parallel to the direction of pressing. Fig. 1 shows the typical deformed sphere. A detailed study showed that the mean value of the contact areas on each sphere was within 5 pct for all the spheres in the die (ignoring those touching the die walls and the top and bottom of the die).' The spheres touching the die walls and the top and bottom of the die were found to have larger contact areas (8 to 10 pct) which indicates higher pressures in these regions of the compact and thus higher compact densities in these regions. These results show that density distribution calculated from such an experiment will give results consistent with the previous investigators. It is concluded, therefore, that the pressure distribution in the die is better understood by studying contact areas on each particle. 'R. Kamm, M. A. Steinberg, and J. Wulff: Trans. TMS-AIME, 1947, vol. 171, p. 439. 'Pol Duwez and Leo Zwell: I. Metals, 1949, vol. 1, p. 137. 'G. C. Kucynski and I. Zaplatynskyj: Trans. TMS-AIIME, 1956, vol. 206, p. 215. 'R. P. Seelig and J. Wulff: Trans. TMS-AIME, 1946, vol. 166, p. 492. 'H. Hencky: Z. Angew. Math. Mech., 1923, vol. 3, p. 241. "J. Ishlinsky: I. Appl. Math. Mech. USSR, 1944, vol. 8, p. 233. 'D. Tabor: Proc. Roy. Soc. (London), Ser. A, 1948, vol. 192, p. 247. 'Ashok K. Kakar and A. C. D. Chaklader: 1. Appl. Phys., 1967, vol. 38, p. 3223. Superplasticity in 60Zn-40Al David L. Holt THE occurrence of superplasticity in Al-Zn alloys is of interest because of its possible industrial exploitation.' The eutectoid composition (78Zn-22A1) has been the most extensively studied;'-= neck resistant flow and high strain rate sensitivity of flow stress (characteristic of superplasticity) are associated with a micron-size grain conferred on the alloy by an homo-genization and quench.5'6 Compositions away from the eutectoid have received comparatively little attention, especially from the viewpoint of relating the structural

Jan 1, 1969

By R. T. DeHoff

A theoretical development is presented which reformulates Fick's first law for diffusion in the solid state. The diffusion flux of component i in a multi-component system, Ji, is related to its local concentration, ci, and local jump frequency, ri : where a is a geometric factor and d is the jump distance. The product, ciri , is defined as the local concentration of atomic jumps for component i. The analog to Fick's second law is also derived. A solution to this equation is presented, which permits the experimental determination of the variation of atom jump frequency with composition in multicomponent systems. HISTORICALLY, the description of diffusion in the solid state has been presumed to be best approached as an application of more general diffusion laws, known as the phenomenological equations. These equations relate the flux, Ji, of the various components, expressed in atoms, grams, or volume, to the driving force involved, expressed as either a compositional or chemical potential gradient, sumption that the flux is simply proportional to the driving force is the foundation of this approach. The phenomenological equations take the form: where the concentration gradients are assumed to be the driving force, and: if the chemical potential gradient is taken as the driving force. The coefficients Dij in Eq. [1.] are the "diffusion coefficients"; the elements of the corresponding matrix in Eq. [2], the Mij, are called the "mobilities". Eqs. [I] and [2] may be considered to be definitions of these phenomenological coefficients. A formidable body of literature has been generated about these equations; this literature dates back to their original formulation for the simplest case of binary diffusion in a fluid, by Adolf Fick, in 1855.' This description has been shown to be self-consistent. However, the "constants of proportionality", the Dij or ,Mij, are not constant: they vary with composition in all but the simplest systems. Even in the case of tracer diffusion, wherein it can be shown that the diffusion coefficient is constant, the mobility, which is considered in irreversible thermodynamics to be the more physically meaningful quantity, varies with the concentration of the tracer involved.' In more complex systems, it is necessary to evaluate the entire matrix of phenomenological coefficients, as a function of composition, in order to describe diffusion locally. Further, in order to determine this matrix experimentally, it is necessary to produce diffusion couples that have different sequences of compositions; the matrix may be evaluated only at points where these "composition paths" cross.* Finally, and perhaps most

Jan 1, 1969

By K. R. Evans

The deformation mechanisms occurring in polycrys-talline, commercially pure titanium and a Ti-8 pct A1 alloy have been investigated and compared to earlier results by Levine on high-purity titanium single crystals and by Conrad on commercially pure titanium. In accord with Levine, two consecutive deformation mechanisms are observed to exist below 500°K with the transition temperature between mechanisms, Tc, strongly dependent upon interstitial composition. T, is found to be 210°. 375° -430°, and 450°K for alloys A large number of investigations have been conducted to determine the rate-controlling mechanisms of plastic deformation occurring in fcc and bcc metals. Very few investigations of a similar nature have been conducted for hexagonal metals. In fact, until very recently, magnesium is the only hexagonal metal which has been systematically investigated for determination of the rate-controlling deformation mechanisms.1"3 From these investigations, it was concluded that basal slip below 420°K occurs by the intersection of forest dislocations,1'3 while for prismatic slip the Peierls mechanism is rate-controlling at low temperatures with interstitial compositions of 0.024, 0.42, 0.61, and 1.13 at. pct expressed in terns of oxygen equivalents. The low-temperature mechanism is found to be an impurity obstacle mechanism in contrast to Levine's earlier conclusion of the Peierls barrier. Measurement of the activation parameters for deformation and estimation of the force-distance profile of the obstacles show their retarding force to be effective over longer distances from the obstacle as the interstitial composition increases. and thermally activated cross slip at higher temperatures. 2 The potential technological importance of titanium alloys has prompted recent studies of the deformation and fracture characteristics of titanium and its alloys. 4-8 Levine' systematically investigated the low-temperature deformation behavior of high purity titanium single crystals oriented for either basal or prismatic slip. It was concluded that the Peierls mechanism was rate-controlling at temperatures below 210°K, while above this temperature an undefined mechanism was rate-controlling. Conrad 7,8 concluded from an analysis of the composition dependence of the critical shear stress at 0°K and measurement of the activation parameters that the low-temperature deformation of titanium is controlled by an impurity

Jan 1, 1969

By Joseph R. Stephens

Deformation substructures of' polycrystalline tungsten, W-2, 9, and 24 pct Re, and W-3 pct Ta were studied by tra?zsrnission electron microscopy. The stress-strain curve for unalloyed tungsten showed gradual yielding followed by work-hardening. Electron nzicrographs indicated a gradual increase in dislocation density with increase in strain up to 5.0 pct. Dislocations, although frequently jogged, were straight over moderate distances and were in a randorn array. Stress-strain curves for alloy specimens of W-2 and 9 pct Re and W-3 pct Ta exhibited a drop in stress at yielding followed by only slight work-hardening. Electron micrographs of these specimens after strains of 0.05, 0.1, and 0.5 pct revealed no change in dislocation substructure from the unstrained specimens. After 2.0 pct strain, the three alloys exhibited dense networks. W-3 pct Ta was characterized by straight, frequently jogged dislocations comparable with the dislocation structure in unalloyed tungsten after a similar amount of strain. In contrast, W-2 pct Re exhibited dislocations that contained widely spaced jogs, while W-9 pct Re had developed a cell structure after the relatively srnall strain of 2.0 pct. The W-24 pct Re alloy contained a few dislocations after 0.1 pct strain, while after 0.5 pct strain twins were evident. Dislocation slip bands apparently preceded the twins. The stress-strain curve for the alloy indicated that twinning commenced after approximately 0.25 pet strain. These results indicate that the primary effect of low rhenium concentrations (2 and 9 pct) in tungsten is to increase dislocation multiplication after macroyielding by reducing the Peierls-Nabarro force (lattice resistance to dislocation motion). The dislocation bands that precede twins in W-24 pct Re may be caused by localized internal stresses resulting fro a metastable structure, for example, clustering of rhenium atoms. The effect of high rhenium additions (22 a 65 pet* Rproperties of tungsten. Klopp, Witzke, and Raffo5 reported bend transition temperatures as low as -100°F (200°K) for dilute electron-beam-melted W-Re alloys tested in the worked condition. Recrystalliza-tion increased the bend transition temperature, but alloys with 2 to 4 pct Re were still markedly superior to unalloyed tungsten. Fractographic examinations of tungsten and W- 3 pct Re and W- 5 pct Re alloys by Gilbert 6 revealed that these low rhenium alloys showed a greater tendency toward cleavage failure than did tungsten. Garfinkle 7 showed that rhenium additions, up to 9 pct, to (100) oriented tungsten single crystals increased the proportional limit stress and decreased the flow stress and the rate of work-hardening. In addition, while deformation in unalloyed (100) oriented crystals apparently involved both (110)100) and (112) slip, crystals with rhenium contents of 5 andpct or more deformed primarily by (112) slip. The mechanism by which high and low rhenium additions affect the mechanical properties of tungsten is still not well-established. The present investigation was undertaken to determine by transmission electron microscopy the effects of low rhenium additions, 2 and 9 pct, and a high rhenium addition, 24 pct, on dislocation substructure in the early stages of deformation of polycrystalline electron-beam-melted tungsten. Unalloyed tungsten and a W- 3 pct Ta alloy were included for comparison. EXPERIMENTAL PROCEDURES Materials. Triple electron-beam-melted tungsten, W-2, 9, and 24 pct Re, and W- pet Ta were used for this investigation. Chemical analyses of the cast ingots are given in Table I. A description of the starting metal powders and melting and fabrication pro-cedures for unalloyed tungsten and the W-Re alloys is reported.5 The W-3 pet Ta alloy was processed in a similar manner. Compression specimens measuring 0.300 in. (7.6 mm) in length by 0.130 in. (3.3 mm) in diam were machined from swaged rods. All alloy specimens were annealed in a vacuum of 8 x 10- 6 Torr (10'2iVper sq m) for 1 hr at 3600°F (2255°K). The recrystallized grain size ranged from 0.06 to 0.08 mm diam for the alloy specimens. Unalloyed tungsten was annealed at 2400° F (1589°K) for 1 hr to produce a recrystallized grain diameter of approximately 0.12 mm. Specimens were electropolished in a 2 pet NaOH solution to a diameter of 0.125 in. (3.18 mm) to remove surface notches resulting from grinding and to improve reproducibility of t data. The ends o the compression specimens were ground flat, parallel to each other, and perpendicular to the longitudinal axes with 4/0 emery paper. Compression Tests. The compressive stress-strain apparatus used for compression tests is described in detail by Stearns and Gotsky.9 Room-temperature compression tests were conducted at a crosshead speed of 0.01 in. per min (0.25 mm per min).

Jan 1, 1969

By D. Webster

It has been found that cold work and annealing treatments greatly retard subsequent grain growth and re-crystallization in thoria-dispersed nickel and NiCr. It is suggested that this is due to cavities which form at the particle-matrix interface durilzg cold work. Some of' the cavities formed are stable at elevated temperatures and prevent the mouement of large-angle grain boundaries. The movement of these boundaries at elevated temperatures is known to start recrystal-lization and when they are pinned by voids recrystal-lization is made more difficult. TD Nichro,me had a maximun resistance to recrystallization when the initial structure was coarse-grained and had a low dislocation density. A precipitation reaction occurred between 700° and 1200° F in cold-worked TD Nichrome. It has been shown by Grant and his coworkers1-3 that a large part of the strength of dispersion-hardened materials is a result of the cold-worked structure produced during fabrication. In a comparison of the strength of cold-worked copper with and without an oxide dispersion, Grant4 has demonstrated that there is little difference in strength at room temperature. The function of the dispersion is essentially to maintain the cold-worked structure at higher temperatures than is possible in the base material. The dispersion accomplishes this by making recrystallization more difficult. The mechanism by which this is achieved is discussed in this paper. The fabrication history of the material has been found to greatly influence recrystallization behavior and this aspect is discussed in some detail. I) MATERIAL Three different thoria-dispersed materials were examined. 1) DuPont 2 pet thoria-dispersed nickel (TDNi) in 0.050-in. seeet. Thoria particle size is in the range 100 to 2500A. 2) DuPont 2 pct thoria-dispersed nichrome (20 pet Cr, 80 pct Ni) (TDNiC) in 0.125-, 0.060-, and 0.040-in. sheet. In the as-received condition these sheets have

Jan 1, 1969

By R. E. Fryxell, E. C. Duderstadt, P. K. Conn

Permeation rates for nitrogen through are-cast tungsten were measured in the temperature range 1800° to 2600°C at nitrogen pressure differentials of 1.0 and 0.1 atm. Gas chromatography was used to measure the quantities of nitrogen which permeated through 0.26-and 0.53-mm-thick membranes. Permeation rates were proportional to the difference between the square roots of the nitrogen pressure on each side of the membrane and inversely proportional to membrane thickness, indicating that atomic nitrogen was the difjusing species and that diffusion was the rate-limiting step of the process. Permeation coefficients calculated from the rates may be represented by the equation: where P is expressed in the units cu cm (stP)-mm per 1/2 sq cm-min-atm"' and 70.0 * 0.8 is the activation energy in kcal per mole of permeating species. In a previous paper' permeation rates were reported for hydrogen and for oxygen through tungsten. The permeation cells used for the hydrogen measurements were suitable for measuring nitrogen permeation under similar conditions, so the study was extended to include nitrogen. Permeation rates of nitrogen through the polycrys-talline arc-cast tungsten membranes were measured in the temperature range 1800" to 2600°C using two membrane thicknesses and two nitrogen pressure differentials. Permeation coefficients were calculated and the activation energy of the process determined. THEORY For diatomic gases which dissociate prior to diffusion, the quantity of gas which permeates through a membrane or wall at an elevated temperature where bulk diffusion is the rate-limiting step of the process is given by the equation: where: q = total amount of gas permeating a membrane, P = temperature-dependent permeation coefficient, A = area of membrane, t = time, p1 = gas pressure of high-pressure side, p2 = gas pressure of low-pressure side, and d = thickness of membrane. When bulk diffusion is the rate-controlling step, and the solubility of the gas obeys Henry's law, a further relationship is that, for any given temperature and pressure, the permeation is the product of diffusivity and the amount in solution. The permeation coefficient, P, is temperature-dependent according to the equation: where: Po = permeation constant, Q = activation energy, R = gas constant, and T = absolute temperature. EXPERIMENTAL PROCEDURES Cell Design and Experimental Apparatus. Two of the permeation cells used for the previous measurements of hydrogen permeation are shown in Fig. 1. Each consisted of a cylindrical chamber divided into two parts by a permeation membrane fabricated from high-purity (>99.9 pct W) wrought tungsten sheet made from vacuum arc-cast tungsten. The membrane in one cell was 0.26 mm thick and the other was 0.53 mm. The fabrication of these cells was described previously.' The permeation cells were mounted vertically in a high-temperature tungsten resistance furnace and the membranes and the center portions heated to test temperatures. Temperatures were measured by sighting an optical pyrometer on the edge of the membrane through a small hole in a tungsten plate which was fastened to the side of the cell. This arrangement provided an approximate black-body condition and eliminated the need for emittance corrections. Appropriate corrections were made for the quartz window through which the temperatures were measured. Argon gas flowed through the 10-liter volume of the furnace at the rate of 4.7 liters per min. An impurity

Jan 1, 1969

By D. H. Baldwin, R. E. Reed-Hill

Six compositions of polycrystalline ZY-0 alloys, containing up to 4.2 at. pct 0, were tested in tension between 77° and 600° K. The data obtained from each of the compositions corresponded closely to a rela-ion between yield stress and absolute temperature of the form In s/so = BT, where oo is the yield stress extrapolated to zero degrees and B is a constant. In agreement with others who have observed this relationship, it is shown that the activation energy may be expressed as Ho In so/s. In the present specimens Ho is approximately 18,000 cal per mole and is apparently independent of temperature and composition inside the limits of the investigation. It is also demonstrated that this form of activation energy cowesponds to a strain rate sensitivity parameter RT/Ho. Oxygen was also noted to have an effect upon the operative deformation mechanisms. With increasing oxygen concentration there was an increased tendency to observe both nonbasal slip and cross-slip phenomena. Oxygen does not seriously inhibit twinning more than it does slip. Twins were observed in all specimens tested. It is becoming increasingly evident that interstitial atoms in solid solution are able to interact strongly with mobile dislocations. Stein, Low, and seybolt,&apos; have shown that, if the carbon concentration in bcc iron is lowered below the solubility limit, its flow stress temperature dependence is markedly reduced. This suggests that carbon atoms in interstitial solid solution may be responsible for the pronounced temperature dependence of the flow stress normally observed in iron. This view has recently been challenged by Leslie and sober2 who observed a strong flow stress temperature dependence in iron to which a trace of titanium had been added in order to remove carbon atoms from solution. Since the interstitial concentration must be reduced below approximately 1 ppm in order to produce a pronounced effect on the flow stress temperature dependence,&apos; studies of the effect of interstitials on the flow stress in iron necessarily involve serious experimental difficulties in alloy preparation. There are other metals, however, in which strong effects of interstitial solutes upon both the flow stress and its temperature dependence are observed. Of particular significance is zirconium which, according to Domagala and Mcpherson, 3 is capable of dissolving 28.6 at. pct O. The O-Zr alloy system is an almost ideal system for studying the interaction of interstitial atoms with deformation modes since it is possible to form alloys capable of study over an extensive range of compositions. Mills has made such a study using single crystals oriented primarily for single prismatic slip4 and has found an effect of oxygen concentration on the flow stress temperature dependence analogous to that observed in iron due to carbon by Stein, Low, and Seybolt. The present paper is specifically concerned with the effect of oxygen on deformation in polycrystalline zirconium. Although plastic flow in this type of specimen is much more complex than that reported for the single-crystal work, and involves both slip (on several different types of planes) and mechanical twinning, the results of this investigation are in general agreement with the single-crystal observations concerning the effect of oxygen on the temperature dependence of the flow stress. In addition, they also demonstrate that oxygen affects the acting deformation systems. This is in contrast to single-crystal results4 that showed only single slip on a prism plane. EXPERIMENTAL PROCEDURE Material. High-purity hot-rolled zirconium strip, 0.2 in. thick by 4 in. wide, of 0.10-mm average grain diameter, was used for forming alloys. It was obtained from the Carborundum Metals Co., Akron, N.Y., whose analysis indicated the major impurities were, in wt ppm: Hf, 540, C, 145; Fe, 100; and 0, <80. The plate texture was similar to a wire texture, with basal planes generally parallel to the rolling direction and basal poles randomly distributed about the rolling direction. The heat treatments described below did not appreciably alter the basic texture. specimen Preparation. Small threaded-end tensile specimens were machined from the plate with axes perpendicular to the rolling direction. These transverse specimens had gage sections 1 in. long by 0.060 in. in diam. The small gage section diameter was dictated by the fact that the alloys were formed by dif-

Jan 1, 1969

By M. J. Marcinkowski, E. N. Hopkins

An investigation has been made of the ß(fcc) — a(hexagonal) transformation which occurs in lanthanum using both electrical resistivity and transmission electron microscopy techniques. It has been shown that the ß phase can be retained below the transformation temperature by rapid quenching but that the sample immediately begins to transform to the a phase. The transformation is observed to nucleate in the vicinity of inclusions. Based on the above observations, a detailed model of the transformation has been advanced which involves the nucleation of an extrinsic stacking fault bounded by a pair of Shockley partial dislocations in the vicinity of some heterogeneity, i.e., an inclusion. The stress field of the resultant dislocation pair acts to nucleate extrinsic faults in adjacent planes and leads quite naturally to the B-a conversion with a minimum of strain energy induced in the crystal. LANTHANUM possesses an fcc structure ß) (8) upon cooling transforms to a hexagonal modification (a) in much the same way as cobalt. The one exception, however, is that the stacking sequence of the closest packed planes in a La is ABAC ABAC, and so forth,1 whereas in cobalt it is ABAB, and so forth, i.e., hep. Mainly on the basis of transmission electron microscopy techniques, there seems to be little doubt that the 0 — a transformation in cobalt involves a dislocation mechanism2 although its exact nature still remains obscure. Although the ß - a transformation in lanthanum is somewhat more complex than that occurring in cobalt, it was thought that its very uniqueness would be helpful in understanding fcc — hexagonal transformations in general. Such a general understanding of these transformations is important since they represent what are perhaps the simplest of the martensitic class of transformations. The experimental techniques used were those of electrical resistivity and transmission electron microscopy. EXPERIMENTAL PROCEDURE The lanthanum used in this investigation was prepared by the calcium reduction of lanthanum fluoride in a tantalum crucible under an argon atmosphere as described by Spedding et al. The residual calcium was removed by vacuum remelting in a tantalum container. Portions of the metal were then analyzed by emission spectroscopy as well as vacuum fusion. The amounts of the various impurities that were found are listed in Table I. A portion of the lanthanum ingot was swaged at room temperature into 0.030-in.-diam rod for the resistivity samples while the remainder was rolled into 0.010-in.-thick sheet for the transmission electron microscopy phase of this investigation. In order to eliminate the plastic deformation induced in the samples during fabrication, they were sealed in evacuated tantalum lined quartz capsules and annealed for 1 hr at 700° C. Specimen resistances were measured using the conventional "four-wire" technique described by MacDonald, 4 employing a type K-3 Universal Potentiometer and a standard 0.001-ohm resistor, both manufactured by Leeds and Northrup Co. By taking into account all of the possible errors in the apparatus, it was felt that the absolute resistivities of the approximately 0.87-in.-long specimens measured are reliable to 3 pct. Resistances from room temperature to 700°C were measured using a vacuum furnace. In order to avoid sample contamination by the thermocouple, chromel-alumel leads were spot-welded into a tantalum shield which in turn was welded to the lanthanum specimen. Resistances below room temperature were obtained by transferring the sample to a helium gas-filled quench tube and slowly dripping liquid nitrogen into a surrounding dewar flask. A steady reduction of temperature to about —190°C was completed in about 23 hr, and the resistances were measured at various temperature intervals. As will be shown shortly, rapid quenching from above about 350°C was sufficient to suppress the B -a transformation initially but subsequent annealing at lower temperatures leads to a partial ß --a conversion. To investigate this aspect of the transformation, the samples were suspended in the hot zone of a helium-filled furnace from which they could be rapidly dropped into the quench tube mentioned previously which was now

Jan 1, 1969