By M. I. Kalashnikova

Gipronickel Institute has developed the technology of treatment of difficult to concentrate sulphide Pb-Zn concentrates (Zn-19,9%, Pb-8,4%, Cu-0,34%, Fe-8,8%, Ba-6,8%, S-18,7%, Ag-106 g/tonne). The technology consists of pressure leaching, impurity removal from leaching solution, electrowinning and Pb-Ag containing cake treatment. Despite low zinc content in initial concen-trate the technology allows production of solution which is suitable, after standard procedure of impurity removal, for electrowinning with production of zinc grade SHG. Comparing to the standard technologies the flowsheet developed provides the lesser expenses per zinc unit because of decreasing of liquid to solid ratio at pressure leaching stage. The initial concentrate is characterized along with low content of principal metals by high con-tent of barite, which makes flotation of pressure leaching residue more difficult. That is why in this case the hydrometallurgical treatment was chosen. At optimal parameters of chloride leach-ing found during laboratory experiments the principal components extraction was 99.5% for Pb and up to 92% for Ag.

Jan 1, 2006

A sinter plant baghouse dust has been treated as a hazardous solid waste, and disposed at a very high price. A series of leaching tests were conducted to examine the possibility to produce high grade potassium chloride from the solid waste. It is found that around 40% of the solid wastes can dissolve into water, and a deposit with more than 90% KCl can be produced after simply drying the solution.

Jan 1, 2009

By Heikki Jalkanen

The mineralogical composition and morphology of solidified copper smelting and converting slags are of some interest from slag cleaning (by froth flotation), impurity elimination, and environmental points of view. Properties result from both the state of molten slag before solidification and processes taking place during solidification and cooling. In solidification and cooling, copper and sulfur dissolved in molten slag are .precipitating substantially from the silicate phase. Even in water quenching of slag, dissolved copper is pushed out of the solution in the form of finely divided precipitate. Elements present in the raw materials are distributed in a distinct manner between the solidified slag and non-silicate solidification products. Arsenic, antimony, and tin are strongly accumulated in copper precipitate, but not the other metallic constituents common in copper concentrates. Smelting and converting slags differ remarkably on their mineralogical composition and morphology although resulting principally of same chemical processes. Converter slags are more inhomogenous; they often contain solid particles and copper content is .as a rule higher than in matte smelting slags. The final copper content of converter slags was observed to be in a distinct manner dependent on iron oxide - silica ratio. Slag forming, solidification, and precipitation phenomena are discussed on the basis of mineralogical and morphology analysis of smelter slags and laboratory scale experiments.

Jan 1, 2002

By Yong Kuk Park

The horizontal cold chamber die casting process can produce a wide range of near-net shape, non-ferrous castings with small dimensional variation, excellent surface finish and very complex geometries. However, top quality die castings can be achieved only when optimal performance of the cold chamber and plunger is maintained during the molten metal injection phase of the process. Cold chambers (shot sleeves) are known to deteriorate fast and sometimes fail catastrophically because of poor design. Catastrophic fracture and wear due to deformation are leading causes to degrade quality, increase downtime and thereby decrease productivity and profitability. Therefore, a systematic approach to minimize irregular and adverse conditions which prevent an intended injection profile, is highly desirable. To eliminate them, design criteria for shot sleeves were developed using analytical tools and available experimental data. The correlation between design and mechanical failures of shot sleeves was shown by the data obtained from the die casting industry. Also, the relationship between die casting process parameters and deterioration/ failure mechanisms were carefully evaluated.

Jan 1, 1996

By B. P. Sereda

The properties, characteristics and phase structure of chamotte refractories produced with the usage of mullitecorund chamotte and caoline have been given. The comparison of new refractory C-45 obtained by us and refractory C-43 produced by traditional method has done. The physical-chemical properties of refractories is reviewed. The visual porosity, density and pore characteristics of given refractories was calculated. It is established that C-45 has the less gas permeability then C-45 that gives melting units more stability. The petrographical microstructures of refractories have been done. The main phase structures and their influence on refractories properties have been observed. It is established that refractories with mullitecorund chamotte adition has more advantages then refractories gained by traditional method and can be applied to melting units.

Jan 1, 2010

By Marc Verhaege

The effluent under investigation results from a catalic oxidation unit in which paraxylene is oxydised to terephtalic acid. The solution contains cobalt and manganese as their acetates in a concentration range of 0,4 - 1,2 g/I of cobalt and 0,8 - 2,4 g/l of manganese. Before being fed into the main waste stream treatment unit of the plant it is advisable to apply a petreatment step in which both metals are eliminated to a great extent from this effluent. Conventional treatment is done by precipitation of both metals either through pH increment with a base or by adding a suitable reagent producing insoluble species. The aim of this study was to look for a treatment (elimination of both metal species) in which no sludge or precipitate is formed.

Jan 1, 1995

By Ahmadzadegan. Arash, Anil Saigal, Michael A. Zimmerman

"In this study, the rheology of liquid crystalline polymer (LCP) melts through simplified 2-D and 3-D die geometries is simulated using Polyflow™. It is known that rheological properties of LCPs are close to long chain polymers and their directionality is close to those of small molecule liquid crystals (SMLCs). As a result, different rheological models (both viscoelastic and generalized Newtonian) for long chain polymers in Polyflow™ were investigated based on the available capillary rheometer data. By varying the parameters in these models, it is possible to adjust the effect of shear viscosity, normal stress differences and relaxations times on the rheology of the polymer. The free surface of the extrudate coming out of the die is simulated and the amount of die swell for different types of rheological models is compared. This study indicates that the Bird-Carreau model best applies to thermotropic LCP materials as quantified by die swell. Since the rheology of the LCPs affects the orientation of the crystals, the result of this simulation can be further used to predict the orientation of crystallines inside and outside the die.IntroductionAny rod like molecule or crystal tends to orient itself in the direction of shear as it moves within a flow. Since polymers consist of long chains of molecules, they experience the same phenomena when flowing in the melt condition. For most polymers, the molecules change direction and distribute uniformly in space during the solidification. However due to the higher inertia of the crystals in the liquid crystalline polymers, the oriented crystals will keep their order during the solidification and as a result the final product will show anisotropy in material properties."

Jan 1, 2012

By Dachun Liu, Baoqiang Xu, Bin Yang, Yong Deng, Heng Xiong, Xiumin Chen

"In this paper, vacuum distillation technology has been employed to study the possibility and regularity of separating copper and enriching lead, silver and other valuable metals from copper- based multi component alloys. The result of experiment indicated the practicability of vacuum distillation dealing with copper base complex multi-component alloy to separating lead and silver, when the vacuum distillation temperature was 1637K, distillation time was 60min; residual gas pressure was 20-30Pa, the removal rate of silver was 95.86%, of lead was 99.63%; the evaporation rate of copper was 0.745%. The removal rate of arsenic, antimony and tin respectively were 83.09%, 48.12% and 24.54%. Vacuum distillation method is applicable for dealing with the copper-based multi component alloys, silver and lead can realize effective recovery.IntroductionCopper generally go with lead mineral, therefore, to remove copper from lead becomes an inevitable link in lead smelting. Dross from removed copper usually contains lead, arsenic, antimony, tin and noble metal silver. In abroad, soda ash-iron dust is adopted to process copper dross of this kind. The outcomes of this process are lead matte, wet lead, scoria smoke dust etc[1~5] The dominant components of all the outcomes are copper and lead. Moreover, in the process of tin smelting, copper contained by-products are produced, such as, crude tin alloy, tin lead electrolytic anode slime and so on. Copper content of all the products are ranging from few percentages to several tens percentage. Those products, no matter merge into main producing process, or separate treatment cost losses of valuable metal. For one hand, the containing of copper of outcomes from pyrogenic attack is less than 50%, for the other hand, a lot of valuable metal need to be processed, which increase the cost of retrieve."

Jan 1, 2013

By Esher Hsu

Keywords: Recycling, Consumer Battery, Fee rates On November 11, 1999, all types of spent consumer batteries are proclaimed to be collected in Taiwan. Under current recycling system, all producers and importers of consumer batteries have to pay a collection/recycling fee to the Recycling Management Fund (RMF) of EPA based upon the rate approved by EPA. Collectors and recycling plants receive subsidies from RMF according to the collected and treated amounts audited by an independent auditing organization. Collected spent consumer batteries only reached 923 tons in 2002 equivalent to 10% of the total quantity sold at the same year. How to increase the collection efficiency of used batteries becomes an important issue for EPA in Taiwan. The objective of this study is to explore current recycling system of spent consumer battery in increasing collection efficiency. Results provide some suggestions to Taiwan EPA regarding recycling route, recycling system, recycling rates, and recycling subsidies.

Jan 1, 2005

By Y. Suzuki, J. Nagao, Y. Ueda, K. Shimokawa

"A Ti- Ni intermetallic compound could be formed rapidly from Ti and Ni powder compact with SHS process. Microgravity experiments using a drop shaft are carried out, This report shows the effect of microgravity or high gravity on formability of an intermetallic compound. It is concluded that the specimen forms a porous and nearly amorphous alloy by rapid cooling under microgravity but with rapid cooling under high gravity after microgravity, the specimen forms a uniform and dense structure with better crystallinity.IntroductionTi - Ni inter1etallic co1pounds have been produced and have beco1e si1ilar to the a1orphous and porous structure as a result of the SHS (Self Propagating High-te1perature Synthesis) process under 1icrogravity. SHS process is being applied to the synthesis of cera1ics and inter1etallic co1pounds (1). The technique is characterized by a large a1ount of heat being emitted within a very short ti1e interval as regards the sistering reaction. One SHS process, acco1panying 1elting by a reaction was observed, and that was due to the quick heating of a Ni-Ti co1pact containing 50 ato1ic percent of Ti under a low pressure (2-4). In this report, we have researched the use a drop shaft which is 1ore effective during a short ti1e under 1icrogravity and high-gravity, so as to obtain high dense speci1ens with the exception of porous specimens (5). Mechanical properties of each specimen were esti1ated from these 1icro-structures with a discussion about the effect of changing gravity regarding 1elting and solidification of the Ti-Ni intermetallic comounds."

Jan 1, 1996

By Cajsa Samuelsson, Theo Lehner

Converting and refining play a central role in the extraction of metals. Sweden has a long tradition as an experimental play ground for metallurgists, chemists and alchemists, developing new methods and technologies. Presenters of papers are usually happy in recording successful developments. But reporting failures can be as great a value as the former. In the paper experiments and experience in process development are illustrated, differences between ferrous and non-ferrous developments are highlighted and industrial learning curves are discussed. 53

Jan 1, 2009

By Zhouhua Jinag

The attempt has been made to manufacture high nitrogen austenitic stainless steels by pressurized electro-slag remelting furnace with maximum nitrogen pressure of 7MPa. To obtain high nitrogen content in steels, the compound electrodes with different nitrogen sources (FeCrN, Si3N4) were prepared. Using the Si3N4 as the nitrogen alloying source, the silicon contents in ingots were prone to be out of the specification range, and the electric current fluctuated greatly and the surface qualities of the ingots were poor. The surface qualities of the ingots were improved using FeCrN as nitrogen alloying source. The sound and compact macrostructure ingot with the maximum nitrogen above 1.0wt% could be obtained. A series of high nitrogen austenitic stainless steels have been successfully developed by this method. The mechanical and pitting corrosion resistance properties of high nitrogen austenitic stainless steels were investigated. The results show that the steels exhibit excellent mechanical and pitting corrosion resistance properties.

Jan 1, 2009

By Jason Ganley, Yingjia Liu, Adam Dekich, William Tilson, Jeffrey Fergus, Dileep Kumar CJ

"Manganese cobalt spinel oxide coatings have been shown to be effective for preventing chromium volatilization from interconnect alloys, and the associated cathode poisoning, in solid oxide fuel cells. During high temperature exposure a reaction layer consisting of chromium containing spine! forms due to reaction with the chromia scale formed on the alloy. The electrical conductivity of this reaction layer is much lower than that of the coating material and thus can increase the overall area specific resistance (ASR) of the system. The approaches to reducing the ASR are to reduce the thickness and/or increase the electrical conductivity of the reaction layer, which includes both the high-chromium spinel phase and the chromia scale. In this paper the effects of transition metal dopants on the amount and properties of reaction products formed during the reaction of spine! oxide coating materials with chromia are presented.IntroductionThe high cost and difficulties involved with the processing of chromia based ceramic interconnect materials for SOFCs are driving the search for metallic interconnects [1, 2]. The reduction in the operating temperature of SOFC has allowed for the use of high chromium alloy steels for this application [3]. However, the volatilization of chromium from the chromia scale, and the associated poisoning of the cathode, remains a problem which needs to be addressed [ 4]. Though the application of manganese cobalt oxide spine! coatings on the alloy surface substantially reduces chromium poisoning of the cathode [5], the low electrical conductivity of the reaction layer formed between the chromia scale and coating affects the performance of interconnect. Incorporating transition metal ions in the reaction layer could alter the electrical characteristics and improve the performance. Copper and nickel doped manganese oxide spinels are widely used as thermistors due to their high electrical conductivity and negative temperature co-efficient of resistance characteristics [ 6, 7]. Hence doping of copper and nickel in manganese-cobalt spine! oxide composition may improve the electrical characteristics of interaction layer as well and is attempted here."

Jan 1, 2012

By Randall M. Gennan

Generally sintering is focused on the bonding of particles at high temperatures; possibly with simultaneous densification. However, an important aspect of sintering occurs during heating at relatively low temperatures where polymer processing aids are removed via control of the atmosphere, heating rate, or hold time at intennediate temperatures. New insights into burnout processes show impact from the polymenype, particle size, amount of polymer, atmosphere, part geometry, and thermal profile. This presentation focuses on the key parameters to demonstrate improved mechanical property levels are available in traditional powder metallurgy alloys by proper selection of the processing polymer and proper care in its thermal extraction. The focus is on mechanical property, where gains up to 40% are demonstrated due 10 changes in the processing polymer. Further, atmosphere control during polymer burnout provides a benefit by allowing formation of desirable carbonitrides, giving strength levels over 3 GPa (over 400 kpsi). Insight is? gleaned from powder injection molding, where high polymer contents mandate proper processing control.

Jan 1, 1996

By Atsushi Shibayama

The aim of this research was to develop a copper recovery process from mine tailings (0.34%Cu) using flotation followed by high-pressure oxidative leaching (HPOL) and solvent extraction. The results of HPOL using the concentrate of mine tailings obtained by flotation under the optimal conditions of the previous study shown that an efficient copper dissolution of 94.4% was achieved in an H2O media, while the copper concentration of PLS reached to be 2.9 g/L. The solvent extraction of PLS obtained from the optimal HPOL showed that 91.3% copper was recovered in stripped solution under the determined optimum conditions, in which the copper concentration achieved to be 44.8 g/L. Finally, a proposed copper recovery process from the concentrate of mine tailings was developed by combination of HPOL and solvent extraction, while a total copper recovery of 86% was achieved.

By Eulogio Velasco, Jose Nino, Marcos Cardoso

"Recycling of aluminum scrap for production of secondary alloys used for automotive applications is increasing continuously. Automotive alloys require a strict control to remove alloy impurities, inclusions and excess of magnesium. The advantage of aluminum is its recyclability with large energy and emission savings with minimal loss in material properties. The aim of this work is to study the magnesium removal from recycled aluminum by chlorine injection in a reverberatory furnace, and removal by an oxidation process at high temperature in an industrial rotary furnace.The magnesium removal by gas injection is carried out by the reaction between chlorine and magnesium, with its efficiency associated to kinetic factors. In the rotary rapid oxidation of aluminum and magnesium elements at high temperature is characterized by the formation of surface films composed of magnesium oxide. Additionally this work reviews the benefits of an efficient demagging process.IntroductionThe advantages of using light alloys for automotive applications include fuel economy improvement, greenhouse gas reductions and polluting emissions. These characteristics makes the aluminum alloys an attractive option for automotive components such as powertrain products and other critical parts like cylinder heads and blocks. [1]Aluminum alloys coming from recycled automotive components, used beverage cans (UBC) and wrought alloys have positive effects in the energy savings and current environmental trends. Producing a scrap recycled aluminum ingot consumes approximately 5% of the energy required to produce a primary aluminum ingot from bauxite ore. [2]"

Jan 1, 2011

By Jewel A. Gomes

Keywords: Electrocoagulation, arsenic removal, fuel cell, windmill, energy simulation, combined Fe-Al electrode assembly Arsenic contamination of well-water in different countries has caused signs and symptoms of arsenic poisoning. Although several physicochemical treatments are presently used for the removal of arsenic compounds from drinking water, an electrochemical treatment, electrocoagulation, is a promising processing technology and currently is the most efficient (above 99% removal) and environmentally friendly technique, particularly if combined with alternative energy sources. Wind and fuel cell technologies can be considered the most promising developmental clean power sources. We will discuss new insights into the materials processing mechanisms and show the coupling of electrocoagulation with fuel cells and simulated wind energy sources. Different electrocoagulation plate materials were considered, along varied currents from the fuel cell to produce maximum arsenic removal. Coupling these technologies will remove carcinogenic arsenic from water sources, and will exhibit efficient usage of these energy sources by producing pure water for human and agricultural consumption.

Jan 1, 2005

By Sven Eck, Andreas Ludwig, Menghuai Wu

"Phase separation is a frequently occurring phenomenon during solidification accompanied by melt convection, sedimentation or, in the case of two unmixable liquids, a Marangoni driven motion. In order to describe these phase separation phenomena a two-phase volume-averaging model was employed for globular equiaxed solidification of binary alloys and decomposition and solidification of hypermonotectic alloys. The model considers nucleation and growth of equiaxed grains or second phase droplets, motion and sedimentation of grains or droplets, feeding flow and solute transport by diffusion and convection. It allows the prediction of macro segregations and the distributions of grain size or droplet size. Evaluations were made by comparing the numerical predictions with experimental results. For example it is shown that the numerically predicted grain size distribution in a plate casting (Al-4wt%Cu) agrees reasonably well with the experimental analyses.IntroductionModeling of metallurgical processes is a rapidly expanding field and the research activities in the last decades cover a wide range of areas including melt pre-treatment, solidification and subsequent manufacturing routes. Among those activities solidification stands in the central position, because the primary structure of the materials, and even many defects such as porosity, (macro or micro) segregation and inclusions form during solidification. Those primarily formed structures or defects once existing are difficult to be removed or modified by the subsequent material processing.Solidification is a multi-disciplinary field involving thermodynamics, fluid dynamics and solid mechanics, heat and mass transfer, and other disciplinesr1 -31• One of the most challenging problems in solidification modeling is the complex interactions between physical phenomena occurring on different length scales ranging from atomic rearrangement over single crystal-melt interactions to heat extraction, momentum and species transport at the system level. Modeling an industry process on atomic scale is umealistic, even on grain scale (e.g. phase field method) it would need another 40 years to be able to model the exact grain morphology in a casting space envelope of 10x10x10 cm3 [ 4]. Therefore, the realistic models for industry process are based on the solution of the macro transport equations (mass, momentum, enthalpy and species) on system scale. The microscopic phenomena such as thermodynamics, nucleation law, crystal growth kinetics and interactions at the liquid-solid interface are considered with simplified models, which are coupled with the macroscopic transport equations."

Jan 1, 2004

By Sebastian Schmuck, Petrico von Schweinichen, Dieter Senk, Mohammad Peymandar

"At Department of Ferrous Metallurgy of the RWTH Aachen University in Germany steels in the system Fe-Mn-C(-Al) are investigated and produced in the framework of the SFB 761 ""steel-ab initio"". A new world of steel grades leads to special challenges regarding the production and recycling at the end-of-life cycle of product. In order to recycle high manganese steel alloys the EAF has to be chosen preferentially. A good slag practice is necessary avoiding loss of manganese content during melting in the EAF. This paper investigates on the reaction kinetics at the interface of slag and steel containing Mn (17-22 wt.-%) and up to 3 wt.-% Al. The effect of changes in the composition of slag and steel on the interfacial reaction kinetics is studied. The thermodynamic software FactSage™ is utilized to calculate the composition of slag and steel at equilibrium.IntroductionTRIP and TWIP steels are highly alloyed steels which show superior strength and ductility when compared to standard carbon steel and stainless steel alloys. These TRIP- and TWIPsteel grades contain typically 15-30 wt.-% manganese, 0-4 wt.-% silicon and aluminum, and up to 1 wt.-% carbon. Steels containing 18-28 wt.-% manganese and 0.7-1.2 wt.-% carbon together with aluminum addition from 3 to 12 wt. -% and without silicon refer to TRIPLEX high manganese steel alloys. These alloys combine high strength at even large ductility [ 1-4]. At the Department of Ferrous Metallurgy (IEHK) of the RWTH Aachen University in Germany, steels in the system Fe-Mn-C(-Al) is under investigation at the collaborative research center, SFB 761 ""Steel-ab initio"". In this project, high manganese alloyed TRIP and TWIP steels are in the focus.The mechanical properties such as high strength and high ductility make this kind of steels perfect candidates for impact absorption applications in auto body such as vehicle doors and bumpers [2, 5]. With increasing the use of TRIP-, TWIP- and TRIPLEX-steels more high manganese steel scraps will be available at the end of life cycle of products, which need to develop the technologies and metallurgical processes to recovery of high manganese steel. A new steel grade brings new challenges in recycling. In order to recycle high manganese steel scraps the electric arc furnaces (EAF) have to be chosen preferentially [1]. Nevertheless it's not easy to prevent the manganese loss during the process in EAF. During the oxygen refining of high manganese molten steel in EAF the manganese content decreases strongly by oxidation and vaporization, which is affected by slag composition, slag properties such as basicity and viscosity, slag weight as well as melt temperature [6-8]."

Jan 1, 2014

By R. Hamar, G. Lamanthe

"To realize complex shaped pieces, like turbine blades, superalloys are cast with the lost-wax process. The end properties of these parts depend upon their microstructure as well as upon the occurence of casting defects such as micropores and hot tears. Such features are governed by the local solidification conditions which may be describe by the calculation of thermal transfers between alloy and mould. It needs the evaluation of numerous parameters which are fitted from experimental measurements in real castings. In further simulations, any parameter may be changed, in order to determine its influence. Such a single modification is quite impossible to realize in real castings, which shows that numerical modeling is a very good way to study casting processes.This modeling technique of casting is applied here to the real study of a typical low pressure turbine blade of a civil engine.IntroductionAircraft engine manufacturers use superalloys to produce turbine blades. They have to obtain a given microstructure and to avoid solidification defects to give good mechanical properties to theirs castings. For example, microporosity is induced by a large shrinkage that cannot be completely fed with the remaining liquid alloy .The optimization of casting processes needs a good Knowledge of the solidification process, that must be controlled at every place in the casting, and at every time of its freezing. Material and heat transfers that occur during the solidification, can be estimated from rather complex calculations. To model these physical phenomena, the evaluation of many parameters must be made. In this aim, some casting experiments are fitted with numerous thermal captors. The identification of experimental and computed thermograms let us estimate these parameters.A long-range scientific cooperation between SNECMA and INPG has enabled the realization of such studies on this topic. From all of them, this paper describes an experimental and computed investigation which has been led on a typical low pressure turbine blade of a civil engine."

Jan 1, 1986