By A. W. Ambrose, C. E. Beecher

It is the purpose of this paper to summarize data on unitization projects in Oklahoma and Kansas as obtained from replies to questionnaires sent out by the A. I. M. E. committee for these states. The information received indicates that unitization is growing rapidly in this area, but has not been in operation for a sufficient length of time to develop production history. It was impossible to obtain a record of all unitization projects in the time available. The magnitude of such projects is indicated by the fact that reports were received covering a total of 171,420 acres in Kansas and 49,350 acres in Oklahoma. Most of these units have been formed during the past 2 years, the greater number having been completed in 1929. It is anticipated that even more will be formed during the present year. The following important facts have been emphasized by answers to the questionnaire and discussion with various operators: 1. Unitization is growing rapidly, as evidenced by the number of units and the large total acreage now included in units as compared with practically no acreage 2 years ago. 2. Operators are convinced that unitization is reducing development and operating cost and they anticipate greater reductions as experience is gained in unit operation. 3. Producing units have not been in operation for a sufficient length of time to give significant production history from which to estimate the ultimate recovery of oil, but the general opinion seems to be that more oil will be recovered. 4. In view of the benefits to be derived from unitization, many operators are refusing to carry on wildcat operations unless a unit has been formed. If this attitude continues to grow there will be no large pools developed in Oklahoma and Kansas in the future except under unit control. Summary The following tabulation gives a condensed summary of the information received on unit operations in Oklahoma and Kansas, but does not include all units, because many were not reported.

Jan 1, 1930

By C. H. Li, R. J. Stokes, S. H. Bendel, J. A. Sartell, T. L. Johnston

The mechanism of the oxidation of high-purity copper has been studied at temperatures from 500° to 981°C employing gravimetric, high-temperature microscopic and inert marker techniques. An investigation of the adhesion of copper oxides was also made. The oxidation of copper is found to be parabolic at all temperatures. It is concluded that the controlling mechanism is the outward diffusion of CU+ ions through the Cu2O layer, but the mechanism of diffusion is modified by the state of compressive stress in the oxide layer at the oxidation temperature. At temperatures below the transition from elastic to plastic behavior of Cu2O the growth stresses reach a value sufficiently high to cause CuO whiskers to be extruded. The extrusion of whiskers results in the injection of a large number of vacancies into the CuO. The Cu20 layer grows by the advance of the CuzO/CuO interface into vacancy-rich CuO. Since there is an adequate supply of non -thermally created vacancies, the activation energy for oxidation is that required to move the Cu+ ion through the appropriate saddle point to a neighboring vacancy, which has been determined to be 20,000 cal per mole. At temperatures at which the Cu20 can deform plastically the stresses are never high enough to cause whiskers to form. thus vacancies must be supplied by themal activation and as a result the activation energy increases to 40.000 cal per mole. ALTHOUGH extensive studies of the oxidation kinetics of pure copper have been made in the past. the mechanism has received relatively little attention. As a result, certain features of the kinetic data have not been satisfactorily explained' For example, several workers1,2 have reported that the activation energy for oxidation in the range from 500° to 700° C was about 20,000 cal per mole whereas that above

Jan 1, 1960

By J. S. Kasper, R. M. Waterstrat

IN view of the recent findings of a pronounced ordering of atoms in s phase alloys containing elements of the first long row of the periodic table (and including molybdenum),l it is of interest to resolve the question of ordering for s phases containing second and third-row elements. Examples of the latter have been provided recently by Greenfield and Beck2 and two of them, Re-Cr and Ru-Cr, would appear to be favorable for a study of ordering by X-ray diffraction methods because of the considerable differences in the scattering factors concerned. In addition, s phase is found to occur in the Os-Cr system, where the difference in scattering factors is even larger. Accordingly, X-ray powder intensities have been measured in an attempt to learn the nature of the ordering, if any, in these three v alloys. Since there is no reported work on intermediate phases in the Os-Cr system, an exploratory investigation was made in this system, and it was found that, in addition to the s phase, the phase with the A-15 or ß-W structure also occurs. Specimen Preparation—The alloys were prepared by compressing mixed powders of —200 mesh size and sintering in an atmosphere of pure dry hydrogen. All alloys were rapidly cooled from the annealing temperature to room temperature in a stream of cold dry hydrogen in a water-cooled chamber. Table I lists the sources and purities of the starting materials, as well as the details of processing for each of the alloys investigated. Intermediate Phases in the Os-Cr System—In the absence of information on intermediate phases in the Os-Cr system, it was suspected that this system would resemble that of Ru-Cr, where a s phase, RuCr2,2 and a phase with the A-15 structure, RuCr3,3,4 have been identified. Both these phases were found in the Os-Cr system and at compositions

Jan 1, 1958

By W. H. Emmons

Although gold is one of the rarer metals, it is widely distributed; it is found on all of the continents and in each of the grand metallogenic provinces of the earth. It is prominent particularly in the shield areas of the earth; these areas have produced a large part of the world's lode gold and in most of them gold lodes are more important than the lodes of other metals. The Scandinavian shield is the only one that has not produced much gold. Nearly all of the world's gold has been derived from lodes and from sands and gravels where gold placers formed by the destruction of lodes. The gold derived from magmatic segregations, from pegmatites and from contact metamorphic deposits is quite subordinate to that derived from auriferous lodes. The lodes include all veins and related deposits that are formed by hot waters that move along fissures or other openings and that deposit vein 'matter :in the fissures and by replacement of the country rocks along the fissures. All of the shield areas of the earth are characterized by large areas of granitic rocks including granitic gneisses, granodiorites and other acid intrusives which here are included in the general term "granite." The granites are intruded into schists, ancient lavas and other rocks which here are designated as the "invaded" rocks. The granites are parts of what once were great batholiths: that is, they are the remaining portions of great deep-seated bodies that slope outward, have very irregular roofs and so far as known have no floors but extend downward to great though unknown depths. Some of them are scores or hundreds of miles across and contain islands or "roof pendants" of the invaded rocks at places where the roofs of the batholiths were low—that is, where erosion has not yet completely unroofed the batholiths. It is in these islands of older rocks and in the narrow marginal belts and cupolas of the batholiths that practically all of the gold lode deposits of the shields are found. Valuable lodes are lacking generally in the granites themselves except in grahite within a mile or less from .the contacts with rocks of the islands (Fig. 1). It is probable that the great areas of granites and gneisses that surround the islands are not all of the same age, and that at places unmapped granite intrudes gneiss or older

Jan 1, 1932

By W. M. Albrecht, M. W. Mallett

The solubilities of hydrogen in titanium and several of its alloys were determined at 600 to 1000°C and pressures of 0.05 to 10µ of mercury. Solubility increases with increasing beta phase in the alloys. Factors found to affect degassing rates are specimen size and presence of thick surficial oxide. Removal of hydrogen by heating in vacuum and in flowing inert atmospheres was studied. Practical curves predicting minimum degassing times are presented. THE presence of hydrogen in titanium and titanium alloys has detrimental effects on the mechanical properties of the metal.'"," The hydrogen content of commercial titanium is sometimes of the order of 200 ppm by weight' and varies with alloy composition. As a consequence, titanium and some titanium alloys as normally processed are sometimes not ductile unless treated to lower the hydrogen content. The best known hydrogen-removal treatment is heating the material in a vacuum. The rate of removal (degassing) at a give temperature determines the duration of the treatment required to attain a satisfactory low hydrogen level.

Jan 1, 1959

By F. C. Schora, H. P. Meissner

COUNTERCURRENT staged processes involving chemical reactions between solid and gas streams are becoming more common. Such operations are generally carried out in a series of fluidized beds with each bed acting as a stage. Fig. 1 is a schematic illustration of a series of stages located in a single column, with a solid stream moving down through this column from stage to stage counter to a rising gas stream. The reduction of iron oxides with hydrogen and carbon monoxide is one of the reactions which can be advantageously carried out in such a countercurrent system. Calculation of the performance of a countercur-

Jan 1, 1961

By H. E. Doerr

The writer has been unable to find much information relative to tests made to determine the effect of forging on the specific density of steel. The opinion, however, among men engaged in the business, seems to be that forging greatly compresses or consolidates the steel. While such is doubtless the case with spongy or porous steel, the following experiments indicate that there can be little or no change in the density with steel initially free from cavities. Ten ingots of basic open-hearth steel cast as shown in Fig. 1 were used in the experiments. All the specimens were 0.53 carbon with all other elements the same, the analysis being determined from drillings taken midway between the center and outside of the upper end, as shown in Fig. 2. The specimens were selected from over one thousand ingots so that the tests could be comparative for the work done in forging only, but no two of the ingots were cast in the same heat. Each ingot remained in the mold approximately 30 min., when it was removed and sir-cooled. About 12 hr. later, when the temperature had been reduced to approximately that of the surrounding atmosphere, the head was discarded and the ingot heated in an oil furnace to approximately 2250" F. (1235" C). Approximately 1 min. was required to forge under the steam hammer to 1 1/4 in. (31.75 mm.), rough diameter, as shown by the dotted lines in Fig. 2. All ingots were allowed to air-cool after forging. Cylinders 1/2 in. (17.7 mm.) in diameter and 1/2 in. high were then turned from the forged and unforged parts of the ingots and numbered. The ten pairs of specimens were submitted to Louis E. Endsley, Professor of Railway Mechanical Engineering, University of Pittsburgh; A. N. Talbot, Professor of Applied Mechanics, University of Illinois; L. Z. Slater, chief chemist, Scullin Steel Co., St. Louis, Mo. NO information was furnished as to which specimens were forged or unforged and each laboratory used the same specimens, submitting the average of three independent determinations, a tabulation of which is shown in the accompanying table in which the laboratories are designated by the letters A, B, and C. While there is considerable difference in the individual determinations for a number of the specimens, the averages

Jan 1, 1920

By J. E. Warren

The mathematical problem considered by the author1 can be given another physical interpretation which is of some practical significance. The alternative physical problem involves the approximate behavior of a single well which is producing at a constant rate through an axially symmetric, horizontal fracture of infinite flow capacity which is located at the center, top or bottom of a uniformly thick, horizontal, homogeneous, anisotropic reservoir of infinite lateral extent which contains a single, slightly compressible fluid. Using Coats' asymptotic results, the wellbore pressure in the fractured system is given by the following equation.

By J. H. Swisher

The solubility of graphite in CaO-S2O2-Al,O3 slags was measured by equilibrating slag samples with graphite crucibles and CO gas. Carbon contents as high as 2 ut pct were obtained in CaO-saturated, CaO-A1,O3 slags, and 1.3 wt pct in slags of the composition CaO.Si0,. Although the observed conditions for Sic formation were in agreement with those predicted from thermodynamic data, CaC, was found to form at a lower temperature than predicted frotn thermodynamic data. From measurements of the equilibrium carbon content as a function of CO Partial pressure, it was found that carbide ions dissolve in CaO-A12O3 melts with a valence of minus two. The carbon content increased with CaO concentration in Ca0-Al,O3 melts and increased with SiO, content along the CaO'AlO3-CaOSi0 join in the ternary system. When solid CaC2 was added to CaO-A12O3 and CaO-SiO2-A12O3 slags, it was found that one of the oxides in the slag was reduced by the carbide (Al2O3 in the forrner and SiOz in the latter). In electric furnace steelmaking, a double-slag practice is frequently used to meet alloy specifications. Initially a flush slag, which is oxidizing in nature, is used to remove phosphorus and carbon from the steel bath. Later in the refining period, the flush slag is replaced by a highly reducing carbidic slag. When calcium carbide is formed in or added to a finishing slag, the slag is effective as a desulfurizing agent and also permits alloying elements such as chromium, vanadium, and tungsten to be added to the slag in the form of oxides. The oxides are readily reduced by calcium carbide, thereby minimizing the use of expensive ferroalloys. More work has been done on the thermodynamics of silicon carbide in slags than on calcium carbide. Baird and alor' and Kay and alor' determined the free energy of formation of Sic by measuring the partial pressure of CO in equilibrium with solid silica, silicon carbide, and graphite. Using a similar technique, they determined SiOz activities in CaO-SiOz and Ca0-Si0,-A1203 slags. Rein and chipman3 also determined the free energy of formation of Sic using slag-metal equilibrium measurements. A literature survey has uncovered only one experimental study of the behavior of CaC, in slag systems. Shanahan and cooke4 report the results of some preliminary experiments on the solubility and stability of CaC, in a CaO-A1,03 and a Ca0-Si0-A1,03 slag at a temperature of about 1500". The carbon solubility as CaC, in a slag containing 50 pct CaO and 50 pct A1203 was reported to be 0.6 pct. They also review earlier work on the binary CaO-CaC, system. A eutectic exists in this system, but various investigators disagree on the eutectic temperature and composition. eal has given an explanation for carbide furnace erruptions in terms of the thermodynamic properties of CaC,; his analysis is not based on experimental data, but on compiled data for the free energies of formation of CaC, and CO.' , These data for steel-making temperatures are all extrapolated from the results of low-temperature measurements. In the experiments described in this paper, slag samples were equilibrated with graphite crucibles and with mixtures of CO and argon or with CO gas at 1 atm total pressure for measurement of the carbon solubility. Most of the work was done on Ca0-A1203 binary slags, although in some experiments CaO-SiO, and Ca0-Si0,-A1,03 slags were used. EXPERIMENTAL Slag samples of the desired composition for the solubility measurements were obtained by blending pre-fused master slags. The master slags were prepared by fusing mixtures of reagent-grade CaC03 with either A1,03 or Si0, in a graphite crucible. The master slags were crushed, then decarburized in air in a muffle furnace at 1200O C. A schematic diagram of the apparatus is shown in Fig. 1. The source of carbon for the solubility meas-

Jan 1, 1969

By P. C. Johnson, B. A. Stein

This paper describes a study of the effects of combined heat treatment and explosive loading on the mechanical properties of high-strength steels. nis program investigated two distinct areas: 1) the effect of shock waves, without gross irreversible defmmution, on a 3-Cr steel at various stages of heat treatment; and 2) the effect of rapid deformation (explosive forming) on H-11 and D6-AC steels in the metastable austenitic state. The mechanical properties of these steels were improved, in some cases markedly, as a result of these treatments. ,AUSFORMWG, which requires the plastic deformation of metastable austenite, is a process which can appreciably improve the properties of selected alloy stee1s.l,2 The Ausform process significantly increases the strength of these steels without decreasing their ductility. The properties at high temperatures are also improved through a change in the response of the steels to tempering. Although the mechanism by which ausforming alters the properties of these steels is not fully understood, it appears that the dislocation arrays produced by deformation of the metastable austenite influence the structure of the martensite on subsequent transformation. This, in turn, affects the strength, ductility, and tempering response of the martensite. This research used chemical explosives to deform steels at various stages in their heat treatment in order to improve the properties of these steels. The explosive energy is used in two ways; 1) high-pressure shock waves are propagated through the steel to produce extensive microscopic shear strain without causing a large irreversible change in shape, and 2) explosive energy is used to cause extensive macroscopic plastic strain in the metastable austenitic state (explosive forming). I) AUSFORMING WITH INTENSE SHOCK WAVES The steel used in this phase of the research was an alloy having a nominal composition 0.43 pct C, 3.0 pct Cr, 1.5 pct Ni, and 1.5 pct Si. The steel was subjected to intense shock waves in three conditions: 1) in the metastable austenitic state, 2) in the tempered mar tens itic state, and 3) in the tempered martensitic state after ausforming by conventional techniques. The specimens were in the form of disks 2.75 in. in diam and 5/16 in. thick. These were incorporated into a specimen assembly consisting of two disks pressed into a 5 by 5 by 1 in. block of stainless steel, Fig. 1. Spalling (or scabbing) is confined to the front disk. The specimen is protected from oxidation and decarburization by the surrounding metal. The temperature of the assembly is monitored by a thermocouple inserted into one side of the stainless steel block. The assembly is positioned over an oil reservoir which serves both as a means of catching the disks and as quenching medium for the disks shocked under ausforming conditions. Plane shock waves are introduced into the assembly by a metal driver plate impacting the top surface of the block. The driver plate is accelerated by a chemical explosive sheet supplied by E. I. du Pont de Nemours & Co. All the specimens were subjected to plane shock waves having a peak pressure of approximately 430 kbar. The pressure is that quoted by G. E. Dieter for the plane wave generator used in this work.' The driver plate used was 1/4 in. thick, so that the initial pulse was essentially a l/2-in.-wide square wave. The attenuation of the peak pressure during the subsequent 1/4 in. is estimated to be less than 5 pct. The shock front induces a temperature rise, a portion of which is irreversible. Rough estimates (+25 pct) of this temperature rise have been made for iron shocked at room temperature.4 For a 500-kbar shock wave, the temperature rise in the shock front is about 700°F, and is held for a time of the order of microseconds. The irreversible temperature rise, which remains after the shock wave passes, is about 450°F.4 The disks are quenched to room temperature within a few seconds of the shock treatment. It should be emphasized that the temperature rises given above are estimates for pure iron at room temperature, and are not necessarily true for the tests made in this work. The disks shocked at temperatures in the metastable austenitic range were austenitized in the stainless steel assembly in a furnace protected from the firing area. The assembly was removed from the furnace and placed over the recovery reservoir. The plane wave generator was then positioned and

Jan 1, 1963

By J. T. Williams

The equilibria in the V-Zr alloy system were investigated by solidus temperature determinations, thermal analysis, dilatometry, electrical resistance measurements, microscopic examination, and X-ray diffraction analysis. There is a eutectic reaction at 1230°C between a compound, V2Zr, and a solid solution containing 10 pct V in ß zirconium. V2Zr decomposes at 1300°C into liquid and a solid solution containing about 10 pct Zr in vanadium. The eutectic composition is probably about 30 pct V. A eutectoid reaction between V2 Zr and a zirconium takes place at 777°C at a very high rate. The eutectoid composition is 5 wt pct V. The limit of solubility of zirconium in vanadium was estimated to be 5 pct at 600°C. No attempt was made to determine the liquidus for the system. THE recent availability of large quantities of high purity zirconium has stimulated the study of zirconium binary systems. The equilibrium diagram for the V-Zr system has received little attention, however. Wallbauml appears to have made the first report concerning the equilibria in these alloys. He reported the existence of a compound, V2Zr, having the MgZn2 ((214) type of structure with a, = 5.277 kX and c° = 8.647 kX. Anderson, Hayes, Roberson, and Kroll2 made a survey of some potentially useful zirconium binary alloys and found that zirconium probably dissolves a small amount of vanadium. They reported the probable existence of a compound between the two elements and suggested that the zirconium-rich solid solution undergoes a eutectic reaction with this compound. Pfeil," in a critical review of the existing information, estimated that the solubility of vanadium in zirconium is less than 4.7 pct and probably less than 1.8 pct. Rostoker and Yamamoto' proposed a partial diagram for the V-Zr system in a survey paper on vanadium binary alloys. Their diagram indicates the compound, V,Zr, a eutectic reaction at 1360°C, a peritectic reaction at 1740°C, and a limit of solubility of zirconium in vanadium of about 3 pct. They obtained no information on the equilibria in the zirconium-rich alloys. In view of the potential utility of the V-Zr alloys and the incomplete knowledge concerning the equilibria in the system, an attempt was made to establish the constitutional diagram. Preparation of the Alloys Raw Materials: The vanadium for making up these alloys came from the Electro Metallurgical Corp. Zirconium came from two sources. In the beginning of the investigation, sponge zirconium from the Bureau of Mines was used in making some of the alloys. Later, iodide metal made at the Westinghouse Atomic Power Development Laboratories became available. This material was used in the preparation of all the dilatometric and resistance specimens and about two-thirds of the solidus temperature specimens. A typical manufacturer's analysis of the vanadium is shown in Table I. No other analysis of the vanadium was made. The metal contained a dispersed second phase and did not have a sharp melting point. Typical results of spectrographic analysis of the Westinghouse zirconium are shown in Table 11. These data indicate a very high purity. The Bureau of Mines sponge metal was probably less pure but had good ductility. Melting: All of the alloys used in the investigation were made by melting pieces of vanadium and zirconium together in a dc electric arc furnace similar to those of Geach and Summers-Smith, craighead, Simmons, and Eastwood," and others. Melting was done in an atmosphere of helium scavenged of residual air by the preliminary melting of a separate charge of zirconium. Each ingot was turned over and melted at least three more times before removal from the furnace to aid in the attainment of homogeneity. Alloys prepared for use in the investigation are listed with the results of solidus determinations in Table III with the exception of the following compositions upon which no solidus determinations were made: 0.29, 0.54, 4.57, and 5.55 pct V. Analysis: The weight of each ingot made from iodide zirconium was within 0.1 g of the total weight of the initial charge, about 90 g. Since each component of each charge was weighed to the nearest 20 mg for amounts less than 10 g and to the nearest 0.1 g otherwise, the gross composition of an ingot could be calculated accurately. Chemical analysis for the vanadium content of several alloys agreed

Jan 1, 1956

By W. A. Gibson, Zay Jeffries

It has been known for a number of years that certain aluminum alloys could be hardened by quenching from a temperature of about 500' C. Immediately after quenching the total increase in hardness is not marked, but the hardness increases gradually so that after about 4 days, it has reached a maximum. The actual increase in hardness probably continues for weeks or even months, but in order to detect the differences after 4 days, it is necessary to make tests at rather long intervals. So far as is known to the authors, Alfred Wilm was the first to discover these properties in aluminum alloys.' The aluminum-copper alloys are amenable to this treatment and the addition of magnesium makes the heat-treatment effect more pronounced. Until recently heat treatment of aluminum alloys has been confined to the worked alloys in the form of sheet or extruded products. The alloy that has been most used in this connection is known commercially as duralumin and has about the following composition: copper not exceeding, 6 per cent.; magnesium not exceeding, 2 per cent.; manganese not exceeding, 1 per cent.; commercial aluminum,2 balance. A typically good alloy in this range consists of: copper, 4 per cent.; magnesium, 0.5 per cent.; manganese, 1 per cent.; commercial aluminum, balance. This alloy can be rolled into sheets or extruded; and in this condition it can be heated in the ordinary furnace atmosphere to a temperature near 500° C. and quenched in water. After about 4 days it will have the following physical properties: tensile strength 55,000 to 60,000 1b. per sq. in. (3866 to 4218 kg. per sq. cm.); elongation in 2 in., 15 to 20 per cent. No harmful effects of the furnace gases or even the air, if the heating is effected in an electric furnace in an air atmospherc.

Jan 1, 1921

By S. Ramachandran, R. A. Walsh

Many investigations have shown that the manganese enhances the deoxidation power of silicon. Here it is suggested that this phenomenon could be explained in terms of the formation of impure silica. Data of Hilty and Crafts on the Fe-Mn-Si-O System has been evaluated on the basis of the reaction S_i + 20 = (SiO2) where (SiO2) denotes silica of variable activity. The activity of silica in this system is a function of aMn/aSi and the temperature, and can be described by the equation 12700 l°gaSiOz = -6.85+ - - 0.5 log aMn /asi PRACTICAL melting experience has shown that it is helpful to maintain a certain range of Mn/Si ratio in deoxidizing quality alloy steels. Herty,1 as early as 1932, reported a strong association between manganese and silicon as did schenck2 and Korber and Oelsen3 in later work. More recently, Hilty and crafts4 have studied the solubility of oxygen in the Fe-Si-O system, both with and without manganese. Their study confirmed the marked ability of manganese to increase the deoxidizing power of silicon. This phenomenon has remained unexplained in the liter,ature5 since it has been shown that manganese has virtually no influence on the activity coefficients of silicon or oxygen.= In this paper, an explanation for the role of manganese is suggested and equations are devised for quantitatively describing this influence. DISCUSSION Hilty and crafts4 equilibrated their melts under an argon atmosphere and the system established equilibrium with a self-generated slag which was not always the oxide of lowest free energy. Drawing on the early work of Korber and Oelsen,3 it was reasoned that the formation of complex Fe-Mn-silicates

Jan 1, 1963

By B. M. Loring, I. R. Kramer, F. M. Walters

No observations on the mechanical properties of iron-manganese alloys have been published since pure manganese became readily available, either distilled manganese or electrolytic manganese. The purpose of this investigation was to determine whether iron-manganese alloys are essentially brittle, as reported by Hadfield,1 or whether the lack of ductility observed was due to impurities in the alloys that he studied. EXPERIMENTAL METHODS The alloys were melted in a 100-lb. high-frequency induction furnace with a magnesia crucible, using ingot iron and electrolytic manganese. The heats were split, the first giving six 18-lb. ingots and the second three. Each successive heat was higher in manganese and about 0.3 per cent silicon [ ] was added as ferrosilicon. The alloys forged without difficulty-and were given a 90 percent reduction to 3/4-in. rounds. The chemical analysis of the alloys is given in Table I. The forged rods were homogenized for [ ] 24 hr. at 1150°C. (2100°F.) and air-cooled. The alloys were tested in two conditions of heat-treatment: (I) as normalized from 870°C. (1600°F.) and (2) normalized from 870°C. and tempered for z hr. at 540°C. (1000°F.) and air-cooled. The tensile specimens were 0.505 in. in diameter with a 2-in. gauge length, and the impact specimens were V-notch Charpy. The proportional limit and yield strength were taken from the stress-strain diagrams drawn by a Peters recorder. The data obtained from the tensile test and the hardness measurements are given in Table 2. Specimens that were normalized are designated by N; those that were normalized and tempered by T. Alloy G was tempered after forging (D).

Jan 1, 1941

By C. P. Karr

FOR several years, the Bureau of Standards has been working in cooperation with an Advisory Committee on non-ferrous metals on various phases of the production and testing of zinc bronzes. The work has dealt, especially with the type of metal known as "Admiralty bronze" in England and as "Government bronze" in this country and consisting of 88 copper, 10 tin, and 2 zinc. Several reports have been made on this subject and these should be considered in connection with this paper.1 FIRST SERIES OF FIVE FOUNDRY TESTS A very brief summary of the first series of five foundry tests has been made,2 but for the sake of clearness the results are given here in different form. The five foundries cooperating in this investigation were: Ohio Brass Co., Mansfield, Ohio; Titanium Alloy Mfg. Co., Niagara Falls, N. Y.; Packard Motor Car Co., Syracuse, N. Y.; National Cash Register Co., Dayton, Ohio; Bureau of Standards, Washington, D. C. The object of the work was to determine whether uniform results could be obtained with this alloy in different foundries working under definite instructions. One of the participating foundries prepared, from virgin metal, a stock of ingots of the composition 88 copper, 10 tin, 2 zinc, and at the same time poured nine test bars from this melt of virgin metal. The results of the physical tests of these bars are shown in Table 1. Examination of this table shows that the highest and most nearly uniform results were obtained when the virgin metal was cast flat in chill molds and the lowest and most variable results were encountered when it was cast vertical in green-sand molds. In this, as in all other tables, the mean

Jan 9, 1919

By Woolsey McA. Johnson

In metallurgical circles it is known widely, but somewhat vaguely, that the ease of reduction of metallic oxides depends largely on the way they hare been prepared. It is likewise known that different forms of carbon have different and greatly varying reducing powers. It is the purpose of this paper to show somewhat more definitely and scientifically these facts. Some years ago the writer published an account of pyrometric determinations of the reduction temperature of zinc oxides variously prepared and of several kinds.' In said paper it was shown that the temperature at which zinc oxide evolves zinc according to the equa-tion ZnO + C = Zn + CO depends upon the nature of the two reacting bodies. The determina-tions had a range of accuracy of from 2° to 6°C., whereas differences were found to amount to an extreme of 90' C. So the differences are real ones and must have a definite cause. The equation of boiling water, (H2O)4 D 4 (H2O) has a fixed temperature for equilibrium of 100° C. at 760 mm. pressure. In general, all equations reacting in the liquid or the gaseous phase have well-defined constant physical conditions which govern the equilibrium point and reaction velocities. In a reaction where we have one or more solid phases, the tempera ture conditions requisite for the unbalancing of the stable system are found to vary. These variations are due to the fact that in a solid there is a very complex molecule and it is not a question solely of the tearing away of two interlocked atoms, but also of the destruction of a complex molecule containing hundreds, or possibly thousands, of smaller molecules. In other words, there are two forces to be overcome: a certain

Jan 1, 1914

By Samuel Daniels

Aluminum-base alloys containing small amounts of copper and magnesium possess but ordinary physical properties as sand cast, but may be treated to give a remarkable range of tensile values and of Brinell hardness. The high-copper (4.5 per cent.) duralumins must be given a protracted treatment which in nature resembles the malleableizing of white cast iron; the low-copper (2.25 per cent.) duralumins develop an excellent combination of strength and ductility with a treatment which requires a maximum of 5 hr. to be completed. THE wrought alloys of aluminum with small amounts of copper and of magnesium have, with the development of the automotive and aircraft industries, sprung into prominence through the medium of duralumin; but the cast alloys remained in the background because their possibilities in the heat-treated condition were either not recognized or not fully investigated. In 1919, the Bureau of Standards published a preliminary survey1 of this field, which pointed out that, in general, the ultimate strength and the percentage of elongation of the alloys of aluminum with and without magnesium could be improved by so simple a treatment as heating to 932° F. (500° C.) for 2 hr., cooling in, air, and aging at room temperature for several days. British investigators, too, working with chill-cast material, found that " considerable improvement in the mechanical properties of copper-aluminum alloys' may be obtained from suitable heat treatment applied to castings."2 Jeffries and Gibson3 made the first contribution to the literature dealing exclusively with the heat treatment of sand-cast aluminum-base alloys, describing the effect of small additions or of combinations of copper, magnesium, and iron on the response to a short heat treatment comprising heating at 932° F. in a

Jan 7, 1924

By O. K. Riegger, L. H. Van Vlack

The median angle of relatively few two-dimensional observations provides a satisfactory value for dihedral angle determinations. Those data that contain bimodal or non-equilibriated dihedral angle distributions are readily detected. THIS paper is concerned with a statistical simplification for determining dihedral angles in solids. Microstructures are partially controlled by relative energies of interphase boundaries and grain boundaries. smith1 has shown rather conclusively that such boundaries may be equilibrated to give a vectorial balance at grain and phase edges. Thus if an accurate measurement is made of the dihedral angle associated with grain and phase edges, an accurate calculation of the relative energies may also be made. The accurate measurement is difficult because the dihedral angle involves two planes in three dimensions, and only a two-dimensional cut through the dihedral angle is usually observed. Such a two-dimensional cut is statistically random provided there is no preselection or orientation. Harker and parker2 have shown that the mode of the frequency distribution of observed angles is within 5 deg of the true angle if the true dihedral angle is 120 deg. smith1 had calculations made to show that the same generalization could apply to dihedral angles of 30, 60, 90, and 150 deg. This procedure of requiring the determination of the statistical mode is time consuming because experience has shown that more than 200 angle observations are necessary before the mode is clearly indicated. It is possible to determine the dihedral angle with equal accuracy with only 25 angle observations if the median angle is used in place of the mode angle. Use is made of Harker and parker's2 basic equation tan =2 sin x cos

Jan 1, 1961

By T. S. Lundy, C. J. McHargue

HE diffusion rate of v48 in single crystals of bee vanadium has been determined at temperatures from 1002° to 1888°C. Standard techniques of lathe sectioning were used for specimens annealed above 1500°C while sectioning by grinding was used for specimens annealed at lower temperatures. As will be seen, the lower-temperature data is enhanced on an Arrhenius-type plot relative to values expected by extrapolation of the high-temperature data. Single crystals were obtained from Linde Co. In Table I the analysis supplied by the vendor is compared with an analysis at Oak Ridge National Laboratory of a sample after a diffusion anneal. The isotope v4' was prepared by the Isotopes Division of Oak Ridge National Laboratory. Proton bombardment of a titanium target in the 86-Inch ORNL Cyclotron was followed by a carrier-free chemical separation. Nineteen specimens, 1/2 in. diam and 3/8 in. long, were cut from the as-received vanadium single crystals. Each specimen was machined with the flat face perpendicular to the longitudinal axis. Specimens were polished through 1/0 emery paper and were etched with 25 pct HF-10 pct H2SO4-10 pct HNO3-55 pct H2O. The polishing and etching steps were repeated until a satisfactory surface finish was achieved. The isotope was electroplated onto the specimens from a neutral solution. Counting rates of the deposited layers were approximately 100 counts per sec. At temperatures above 1200°C specimens were annealed in a tantalum resistance furnace under an argon atmosphere. Temperatures were measured with a Pyro micro-optical pyrometer and a Pt-Pt 10 pct Rh thermocouple. At lower temperatures the specimens were sealed in evacuated quartz ampoules and annealed in Kanthal wire-wound horizontal tube furnaces. A severe reaction occurred at 1200°C between the quartz and the vanadium. This

Jan 1, 1965

By Thomas L. Watson

The occurrence of zircon in pegmatites of acidic composition is recorded by many observers both in this country and abroad, and they form one of the most important geologic modes of occurrence of the minera1. As is well known, commercially the most important American locality for zircon is near Zirconia in Henderson County, North Carolina, where many tons of the mineral have been obtained from a kaolinized pegmatite dike 100 ft. wide and traced for 1 1/2 miles along the direction of strike N. 50" E. Zircon may be developed in pegmatites as inclusions in the principal rock-forming minerals, chiefly quartz and feldspar, and as a separate megascopic constituent in the form of grains and crystals not exceeding, as a rule, 2 in. in size, and usually smaller. In the Henderson County, North Carolina, pegmatite, zircon occurs in prismatic crystals with pyramidal terminations measuring up to 30 mm. in diameter, associated chiefly with the feldspar. In some of the apatite veins of Canada, which are closely allied to pogmatite dikes, zircon is reported in crystals upward of 6 in. in length and 2 in. and more in thickness. Zircon in large masses occurs in Virginia in the well-known pegmatites near Amelia in Amelia County, and near Gouldin in Hanover County. Both localities are in the middle eastern portion of the Piedmont Plateau province, and are separated by a distance of about 40 miles in a northeast-southwest direction. The rocks of both areas, including the pegmatite bodies, are in an advanced stage of decay, and the hard and moderately fresh rocks are concealed beneath a cover of variable thickness of rock decay derived by the normal processes of weathering. Exposures, there-

Jan 1, 1917