By Hidekazu Nakagawa

We investigated the anodic dissolution behavior of titanium in TMHA-Tf2N molten salt, which has a wide electrochemical window of about 5 V, in order to develop an electrodeposition method for titanium. By etching a titanium electrode in HF?HNO3?H3PO4 solution, the titanium electrode became electrochemically active, and a redox reaction was observed at around -0.15 V vs. I-/I3- in (TMHA-Tf2N)?HTf2N solution. We identified the redox reaction consists of the reduction of the proton and the oxidation of hydrogen. The diffusion coefficient of the proton in TMHA-Tf2N was calculated to be 6.9 10-8 cm2 s-1 at 50 °C from the cathodic peak current in the cyclic voltammogram. Anodic decomposition of the molten salt was not observed up to 6.0 V vs. I-/I3- on titanium electrode, while it was observed at around 2.0 V vs. I-/I3- on platinum and glassy carbon electrodes. Cathodic decomposition of the molten salt was observed at around -3.0 V on the titanium electrode, as well as on the platinum and glassy carbon electrode.

Jan 1, 2006

By A. V. Tarasov

Investigations of thermodynamic properties of Cu-Ni and Cu-Ni-S systems and mattes have been conducted with the aid of a MC-130 I mass-spectrometer designed for studies of processes of vapor formation of hardly volatile substances. The instrument comprised a combination of an evaporator of Knudsen chamber type with a mass-spectrometer for analysis of the vapor phase. In the process of studies of molten Cu-Ni-S systems and commercial-grade mattes within a temperature interval of 1400-1800 K the partial pressure of sulfur was measured by means of complete isothermal evaporation and the partial pressure of copper and nickel by comparison of ionic currents. The partial pressure values of the components above the molten Cu-Ni-S were used for calculation of activities of the respective components in the melt. The copper and nickel activity data obtained was used for assessing the amount of dissolved losses of these metals in autogenous smelting slags.

Jan 1, 2003

By B. R. Adams

This paper discusses the use of a reacting CFD model to determine chalcopyrite kinetics in a drop tube furnace and to predict the reaction of a chalcopyrite concentrate in the reaction shaft of an industrial smelter. Reacting CFD codes can be applied to determine the consequences of the interaction of gas with particles and therefore improve the ability to derive kinetic parameters that take into account the temperature and oxidation histories that different particles will see. This paper describes the application of such a model to derive improved kinetic parameters for the pyrolysis and oxidation of chalcopyrite. The reaction shaft model includes the effects of turbulent fluid mechanics, entrained flow mixing, turbulent particle dispersion, heterogeneous particle reactions, radiative and convective heat transfer, and' surface and bath deposition rates. Particle reaction and composition characteristics are predicted as a function of particle trajectory and deposition and are used to aid in evaluating shaft performance.

Jan 1, 1999

By M. Drozd

Multi-use pad operators require an efficient and economic method to destroy cyanide in their process residues so new material can be stored on the pad and leached. Operators of the dedicated or single-use pads require an effective cyanide destruction method for pad closure. Cyanide destruction can be accomplished by utilizing oxidants such as hydrogen peroxide or calcium hypochlorite, or by utilizing ferrous sulfate which sequesters the cyanide in strong acid dissociable complex. Ferrous sulfate can be the preferred method of cyanide destruction because it is a less costly chemical, reaction rates are almost immediate and unlike oxidants, it can penetrate the total depth of a pile without being destroyed by side reactions. Literature indicates that the (Fe(CN)6)-4 com~lex is produced slowly but it appears that complexes such as Fe(CN)4(H20)2-or Fe(CN)4(OH)2)-4, are formed quickly and should have no U.V. sensitifity, unlike (Fe(CN)6)-4. Stoichiometry of the testwork indicates that Fe«CN)4(OH)2)-4 complex may be the species formed. The usage of ferrous sulfate has the advantage of being able to bring ~ level down that divalent metal ions such as Cu++, Cd++, Hg++, Pb++ and Zn will form insoluble complexes and precipitate from solutions does not destroy weak acid dissolvable complexes and can leave a heavy metal problem behind after cyanide destruction.

Jan 1, 1990

By F. E. Wagner, L. J. Cabri, Y. G. Safonov, N. S. Bortnikov, A. D. Genkin, J. Friedl, G. N. Gamyanin

"A multidisciplinary investigation (including INAA, SIMS, EPMA, and Mossbauer Spectroscopy) was used to characterize gold in four of the largest Siberian mesothermal sulfide gold deposits. These are the Olympiada (""'750 metric tons gold) and Veduga (estimated at 75-100 metric tons gold) deposits in the Enisei Mountain Range and the Nezhdaninskoye (z500 metric tons gold) and Sentachan deposits in the Verchoyansk-Kolyma area. It was found that some of the mineralization is refractory in all four deposits, largely due to the occurrence of ""invisible"" gold in arsenopyrite as well as within pyrite, but with a lesser concentration. The gold concentration and its distribution varies considerably both within and between arsenopyrite grains, with implications for processing options such as heap leaching. The ore most likely to be amenable to heap leaching is the oxidized ore of the #4 orebody of the Olympiada deposit, but further quantitative mineralogical investigations are recommended for this orebody's sulfide ore and for the ores of the Nezhdaninskoye deposit. Following a full mineralogical characterization, it is possible that economic viability will depend on a combination of pre-concentration with or without pre-treatment, followed by heap leaching of some tailings products.Acknowledgements· The Russian authors performed this study under an ""Eco res"" Project which was financially supported by the Ministry of Science and New Technology of the Russian Federation. C.J. Stanley wishes to thank John Spratt and Terry Williams for help with EPMA. F.E. Wagner acknowledges the Deutsche Forschungsgemeinschaft for a grant supporting the Mossbauer studies. L.J. Cabri is grateful to the following: M. Beaulne, D. Carson and J.H.G. Laflamme for technical support, K.E. Haque for technical comments, and D.M. Hausen and W. Petruk for editorial suggestions."

Jan 1, 1997

By Levente Becze

The zinc bottom dross is obtained as a by-product from hot dip galvanizing operations and contains at least 92 % zinc, which is recycled mainly by pyrometallurgical processes. The overall costs of such a treatment, however, are often relatively high, and the very strict environmental protection regulations might also cause additional difficulties for the high temperature procedures in the future. Therefore, a novel hydro-electrometallurgical process has been developed in our laboratory, by which one can reclaim zinc of high purity, while attempting to achieve low energy consumption and making allowances for all the environmental restrictions. This aqueous processing technique, based on electrolytic refining in a cell equipped with anion-exchange membrane to separate the anode and cathode compartments, allows the indirect purification of the anolyte. Zinc is dissolved from the anode along with some of the impurity elements, while the intermetallic compounds (Fe-Zn, Fe-AI- Zn) are accumulated in the anode slime.

Jan 1, 2003

By V. Vergara

Four copper composites were obtained by mechanical alloying, using as dispersed phases of four carbide powders; they were: boron carbide, chromium carbide, silicon carbide and zirconium carbide. The purpose of this work was to study some characteristics of these compounds and their feasibility for use as materials for electrical equipment. Raw materials used were copper powder finer than 150 mesh, and 2-4 vol % of powder carbides finer than 325 mesh. The alloying process was carried out using both a Spex 800-D mill with tungsten jars and balls and a hardened stainless steel jar and balls, the purpose of which was to measure the degree of contamination induced by the milling media. The changes in particle size, morphology and microstructure of copper alloys were studied with SEM and TEM for each alloyed powder. The degree of saturation of copper by the carbides was measured by X-ray diffraction. Sound samples were obtained by hot isostatic pressing at 1073°K. The best characteristics were obtained for the compound copper-chromium carbide, based on their hardness, tensile strength and electrical conductivity values. The other alloys failed due to their excessive brittleness after hot pressing.

Jan 1, 1999

By F. Nava-Alonso, O. Alonso-González, A. Uribe-Salas, R. Pérez-Garibay

"Cyanidation is the most used method to recover gold and silver from their ores. In this process, other metals besides gold and silver may sometimes dissolve and interfere with the efficiency of extraction. Copper is one of those metals, reaching concentrations as high as 1000 mg/L in some cyanidation plants, making difficult the extraction and purification processes, and increasing the operating costs.This preliminary work was intended to study the feasibility of using amines to form a precipitate and to eliminate copper from a synthetic solution containing high copper and cyanide concentrations, as is the case of some cyanidation effluents. The solid formed is removed from the solution using conventional filtration techniques. Seven amines were evaluated at different pH values and amine additions. Up to 90% of copper present may be removed at the natural pH of the effluent (alkaline). The remaining copper would permit to recycle the solution back to the cyanidation process. IntroductionCopper is generally considered the most problematic metal in gold leaching due to the rapid formation of copper cyanide complexes when some readily-soluble minerals are processed (e.g., azurite, malaquite, cuprite, chalcocite and bornite). The copper solubilization as cuprous cyanide complexes leads to a significant economic penalty in terms of excessive cyanide consumption and high cost for cyanide elimination. When activated carbon is used to recover gold and silver, the copper-cyanide complexes decrease the efficiency of the process because of the competition of the cuprocyanides with the aurocyanide for the adsorptive sites on the activated carbon (Rees and Deventer, 1999).Several techniques have been developed to attempt to overcome the problems caused by the copper presence in cyanidation solutions, notably: acidification-volatilization-regeneration (AVR), ion exchange-electrolysis or solvent extraction-electrowinning (Lu et al., 2002). In this work the use of some amines is proposed to remove the copper-cyanide complexes by precipitation of a copper-cyanide-amine solid. The process was evaluated for different amine additions and pH values, using copper-cyanide synthetic solutions of composition similar to that presented by some cyanidation plants with high copper."

Jan 1, 2008

By Qionghua Zhou, Wei Liu

"Nanocrystalline silver bulk material with average grain size of 20.3 nm was prepared by warmvacuum- compaction method. The as-prepared nanocrystalline silver was characterized by X-ray diffraction (XRD), differential scanning calarmeutry analysis (DSC), thermogravimetric analysis (TG), and 6157 type Electrometer test, respectivily. The experimental results show that the average grain size and microstrain of the nanocrystalline silver are 20.3 nm and 0.088%. The melting point and melting enthalpy are 1228.7 Kand 82.34 Jig, which are lower than that of coarse-grained silver by 6 Kand 22.6 Jig, respectively. The electrical resistivity of nanocrystlline silver increases with higher temperature when the range of temperature is between 233K and 293K. The electrical resistivity at 293 K is 1.475xlO -7 Q·m, which is higher than that of coarsegrained silver by a factor of 9.IntroductionN anocrystaline ( nc) materials or nano structured ( ns) materials are three-dimensional (3 D) bulk materials with average grain size typically smaller than 100 nm. Ne materials have been of great interest for their unique properties, such as superior tensile strength [1-2], high microhardness [3- 4], superplasticity [5-6], magnetically quasi-isotropic [7-8] , and so on, making them one of the most promising nano-scale materials with wide applications. Ne materials with average grain size of 5-10 nm were firstly fabricated by Gleiter et al. [9] in 1980s, using inert gas condensation (IGC) method. Unfortunately, the large surface to volume ratio creates a high surface energy component in the total free energy of the system and results in a metastable state in the materials. Therefore, due to the signfica nt disordered grain boundary regions, nanomaterials are thermally unstable and are subjected to a strong driving force for grain growth. The grain growth even occurred at room temperature [10].The conflict or deviation of measured date, e.g. strength, microhardness, thermal stability, partly due to the grain boundary ratio or the distribution of grain size, and partly derived from imperfections such as voids and microcracks while earlier processing techniques are known to result in incomplete dens:fication [11-12]. Therefore, the higher quality samples produced in subsequently years still show such a general trend."

Jan 1, 2011

By Deventer Johanna van

Ore bodies around the world are declining in grade, whilst increasing in complexity. The level of impurities relative to the valuable metal is steadily increasing, posing new challenges to existing operations. Ion exchange is widely used in the hydrometallurgical industry for both primary recovery of metals and the removal of impurities. The superior selectivity of ion exchange resins makes them exceptionally suitable for the removal of target impurities to very low levels, thereby saving operating costs, increasing the value of the final product and significantly improving revenue. The ion exchange process in these applications is very simple, using standard ion exchange equipment and acid regeneration. The process can be fully automated, requiring minimal operator interference and supervision Examples of impurities that are successfully removed via ion exchange include iron, antimony and bismuth from copper electrolyte. In the copper electrolysis process, antimony, bismuth and arsenic tend to form slimes which are dispersed in the electrolyte. These slimes contaminate the cathode and/or decrease the quality of the copper deposition. A special chelating resin was developed to remove antimony and bismuth, while at the same time ensuring minimal chloride leakage to the sulphate matrix. The work is described in more detail in this paper. Ion exchange is also used to remove copper, zinc and nickel from cobalt electrolyte. This paper addresses a few of these examples in more detail.

By Moto Goto

PT Smelting, located in Gresik, East Java, is the first copper smelter and refinery in Indonesia. Since the first charging concentrate in December 1998, many equipment troubles have been systematically eliminated, and the present operation is smooth and has accomplished the design capacity of 200,000 tonnes per year of LME, grade-A copper cathode. This paper describes troubles and countermeasures, which were experienced until now.

Jan 1, 2002

By Xiyun Yang

Magnetite was prepared by hydrogen reduction method. For a conversion to cobalt-modified magnetite, magnetite particles were suspended into a solution containing Co2+ and Fe2+ to precipitate a cobalt ferrite layer on the surface. pH value influences the particle composition directly, the desirable CoFe2O4 is obtained when pH value is 12. The coercivity increases with the increase of cobalt content, cobalt efficiency reaches a maximum value at cobalt content of 2.71wt%. With cobalt modification, magnetite particles have similar lattice constant and squareness ratio to that without cobalt modification. TEM and XPS analyses indicate that acicular morphology is retained during the coating process, the epitaxial growth layer consists of CoFe2O4and 0.3Co2O3CoFe2O4 at cobalt content of 2.71wt% and 5.03wt%, respectively.

Jan 1, 2006

By Roger C. Urquhart

Copper-nickel-sulphide ores mined in the Rustenburg district of South Africa are generally smelted in electric furnaces because of the high-temperature slag produced, the availability of cheap electric power, and the smaller pollution problems. Apart from melting, the functions of the electric furnace are to recover most of the matte content in the converter slag by physical and chemical interaction with the furnace bath and to provide adequate time for the optimum separation of matte and slag. Smooth, efficient operation will denend on fluid slags for settling, balanced by high resistivities to obtain adequate concentration and distribution of power by way of current heating. To obtain a greater understanding of the processes involved, an investigation was undertaken at Rustenburg Platinum Mines on the smelting of copper-nickel concentrates in a 19.5 MVA furnace with six in-line electrodes. The matte- and slag-tapping temperatures, slag temperatures, slag analyses, electrical data, and electrode position were measured. Radioactive tracers were introduced into the slag, and quantitative results relating to the flow pattern within the furnace were obtained. These studies were augmented by scaled laboratory investigations relating to the determination of cell constants and current distribution within the furnace. Instantaneous field and power distribution plots were determined by use of an on-line mini-computer. The applicability of these results to furnace operation is discussed.

Jan 1, 1976

By Serge Lavoie

Alcan's Guillaume-Tremblay plant, located in Jonquiere, Quebec, has been in operation since 1990. This was the first plasma dross processing plant ever built. In addition to the use of the plasma heating technology, Guillaume-Tremblay has other unique features making it a modern and efficient dross processing facility. This paper presents a general overview of the practical experience at the Guillaume-Tremblay plant. In particular, the utilization of plasma heating in industrial conditions, the metallurgical performance, the unique dross handling system, the control and information management system and the reclaiming of the by-products will be discussed. Finally, the use of the plasma process for salty dross will be addressed' briefly.

Jan 1, 1995

By K. S. Han, M. Yoshimuura, H. Fujita, Y. Sato, S. W. Song

"Film of LlCoO2 as cathode material for rechargeable lithium microbatteries has been fabricated on the platinum metal substrate by electrochemical-hydrothermal method in concentrated LiOH solution at 200 °C as Soft Solution-Processing. The film fabrication has been understood in terms of dissolution of cobalt metal powders and subsequent oxidative deposition on the substrate. The film structure was characterized using scanning electron microscope, X-ray diffraction analysis; X-ray photoelectron spectroscopy and micro-Raman spectroscopy.IntroductionRapid growth of wireless communications and emerging integrated optoelectronic circuits caused the miniaturization· cif electronic devices, thus the demand for high energy density microbatteries as a power source for the microelectronics increases. In this regard, all solid-state lithium microbatteries including LiCoO2 and LlMn2O 4 [l-4], the most promising intercalation cathode material, have been developed. However, major difficulty of .fabrication of a lithium microbattery arose from the preparation of cathode film, according to a· recent report on Rare Metal News [5]. Although many attempts have been made to deposit the cathode films, all those methods are mostly chemical vapor deposiiton (CVD), various evaporation, sputtering techniques and spray pyrolysis. These methods require preparation of bulk cathode materials cir its precursor, then deposition with complicated instruments including high· vacuum system, and even postsynthesis annealing to obtain desire electrochemical 'properties. It is clear that all of these techniques are neither economic nor environmentally friendly. Compared to those methods, film form.ation from an aqueous solution is thought to be simpler and more economical, and requires much· less energy consumption. Our .group has demonstrated the utility of Soft SolutionProcessing [6,7], which is defined as environmentally friendly processing using (aqueous) solutions, to produce films of a variety of functional solid materials. According to the Pourvaix's diagram [8], some metal can be dissolved in an alkaline solution and consequently combined with hydroxyl group or oxygen anion forming metalate or metalite. Cobalt also seemed to form cobaltite, HCoOi in strong alkaline solution in the Pourvaix's pH-potential diagram. Based on this information, it was expected that LiCoO2 could be prepared using the cobalt metal in Li OH solution by Soft Solution-Processing. Recently, we reported the successful single step fabrication of electrochemically active LlCoO2 films on the cobalt metal substrate by hydrothermal methods without any post-synthesis annealing as Soft SolutionProcessing [9,10]. Film formation mechanism could be elucidated by the following evidences. . As expected from Pourvaix's diagram, cobalt metal was dissolved in concentrated LiOH solution forming dissolved cobalt species which was detected by an observation of absorption band in UV-VIS absorption spectrum [10]. Thus the reaction was assumed to be started from dissolution. Time dependent potential of Co electrode exhibited only one-step evolution with 0.6 eV from Co metal to LiCoO2 [10]. Another strong evidence was the finding of LiCoO2 powder precipitates at the bottom of tetlon beaker after the reaction [11]. Based on those experimental findings, it was understood that film is formed by dissolution-precipitation mechanism [9-11]."

Jan 1, 2000

By J. H. Huang

In this investigation, the selective precipitation of cobalt and molybdenum from Co-Mo aqueous solutions was studied in order to recover efficiently valuable elements from industrial effluents generated from a novel electrodeposition of nanocrystalline Co-based alloys process and reduce the effluent impact on environment. It was found that the behavior of cobalt in aqueous solutions was substantially affected by the presence of molybdenum. When adding 11.6 to 46.6g/L molybdenum to a 50g/L cobalt solution, the co-precipitation of molybdenum and cobalt started to occur at pH value of 3-4. However, without the presence of molybdenum, cobalt could only be precipitated out of the solution at about pH 6. Most of the molybdenum was found in the solid phase when the solution pH reached 5. After further increasing pH to greater than 7, the molybdenum dissolved back into the solution. Cobalt kept precipitating as the pH increased. When the pH was greater than 7, most of the cobalt was present in the solid phase. The chemical and physical characteristics of the precipitated materials were investigated by SEM, XRD, AAS and EDX. It was revealed that the precipitate was initially present as cobalt molybdate oxide hydrate and subsequently transformed as sodium cobalt molybdenum oxide. With further increasing the solution pH, the precipitate was transformed into cobalt hydroxide. Further investigation implied that most of molybdenum was chemically tied to the precipitate produced at the low pH, yet at the same time, physically entrapped at the high pH. The paper also presents the influence of reaction temperature and time on the precipitation process and kinetics.

Jan 1, 2003

By Ko-ichiro Ohno

It is recently recognized that the iron reduction and melting as well as the slag separation of a composite of granular iron ore and coal are completed in a very short period of about 10 minutes when the composite is rapidly heated up to approximately 1673K. These phenomena are expected to be applied to a new iron-making process. The mechanism of iron ore reduction and iron-slag separation during rapid heating has not yet been revealed and the fundamental research has just started. Carburization of the reduced iron is regarded as one of the most important steps in this process. In the present work, the composite was prepared from four kinds of coal or graphite as a carbon source and electrolytic iron powder as a completely reduced iron ore. The temperature at which the liquid formation and iron carburization occurred was monitored. Direct observation of smelting reduction behavior was made by a confocal laser-scanning microscope combined with the infrared image-heating furnace to clarify the effect of molten ash on iron carburization. It was found that the meltdown temperature of composite became lower as the melting temperature of coal ash decreased. From the observed result, it was presumed that the liquid slag would act as an important media for the carbon transfer from coal to iron. The carburization mechanism during the smelting reduction was estimated as follows. When slag containing iron oxide melted down and contacted carbon, iron oxide in the slag was reduced and the formation of the metallic iron particle as well as the its carburization occurred simultaneously at the slag-carbon interface. Carburized iron particle was carried from slag-carbon to slag-iron interfaces due to the slag convection flow caused by the difference of the interfacial tension between the carbon-slag and iron-slag interfaces. Carburization of reduced iron could proceed with a repeat of the above-mentioned process.

Jan 1, 2003

By I. M. Richardson, M. Janssen, W. Geerstma, I. J. Bennett, V. A. Popovich

Avoiding wafer breakage is a big challenge in the photovoltaic silicon industry, limiting production yield and further price reduction. Special fracture strength tests suitable for thin silicon solar wafers and solar cells, to be used in combination with Weibull statistics, finiteelement (FE) modelling and digital image correlation have been developed in order to study the mechanical stability of solar wafers. The results show that removal of the saw damage significantly increases the strength of crystalline silicon wafers. Furthermore, it was found that silicon crystallinity and the location where the wafer is extracted from the cast Si ingot have a significant effect on the strength, namely samples taken from the bottom of the ingot are 30% stronger than those taken from the top. The study also showed that there is a decrease in fracture strength when an anti-reflective SiNx coating is applied, which is caused by high thermal stresses.

Jan 1, 2015

By Lee Fergusson

"The primary features of ViroMine™ Technology are introduced and applications of ViroMine™ Technology to mine site remediation and the treatment of a variety of intractable waste-streams, including a technical discussion of acid neutralizing capacity, metals binding capacity and longterm stability of results. Outcomes from four applications at high-profile international mine sites are presented: 1) the superfund site at the Gilt Edge Mine, South Dakota, USA (four years of data on the treatment of acidity, TDS and metals such as Al, Co, Fe, Mn and Zn); 2) one of Australia’s most polluted sites at King River Delta in Tasmania (treatment of TAA and TPA, and metal and metalloid contaminants such as As, Cr and Hg); 3) The Aljustrel “Aqua Forte” mine site in Portugal (high acidity, metal and metalloid contaminants such as Al, As, Cu and Zn) and 4) the Ulsan Iron Ore Mine at Ulsan, South Korea (treatment of metal and metalloid contaminants such as As, Cd and Ni).IntroductionThe commercialisation of ViroMine™ Technology has resolved some of the most intractable pollution issues associated with historic mining ventures on a global scale and has facilitated the neutralisation of Acid Rock Drainage (ARD), remediation of acidic and metal contaminated impoundments (including tailings dams) and promoted revegetation on tailings deposits and waste rock dumps. ViroMine™ Technology also enables current mining ventures to manage effluent simply and efficiently to meet increasingly stringent environmental standards and is enabling the mining sector to reconceptualise the management of mine spoil. The abilities of ViroMine™ reagents to neutralise the actual and potential acidity of sulphidic mine spoil coupled with the ability to bind metal and metalloid contaminants into non-bio-available forms are the key features delivering environmental and economic benefits to the mining sector and the broader community. Results from four projects utilising ViroMine™ Technology are presented to highlight the suitability of ViroMine™ Technology to treat all forms sulphidic mining wastes. 37"

Jan 1, 2008

By Nils Eivind Kamfjord, Roar Jensen, Ingeborg Solheim

"SINTEF has carried out several pilot scale silicon process experiments in the past, but always with an open off gas system. In order to test the possibilities in running a semi closed furnace operation, a new off gas hood has been designed and tested. The off gas hood is designed to collect all off gases to gain insight into the phase compositions in the off gas and at the same time have the opportunity to monitor and maintain the charging/stoking of the furnace. The furnace hood has regulation and control of the air inlet into the combustion zone in two different heights. The off gas temperature and composition was continuously monitored and analyzed during the experiment. In order to expand the knowledge on NOx- formation in silicon metal production, such information is vital.IntroductionBecause of the negative environmental impact, the attention towards all kinds of NOX emissions increases in Norway. The authorities’ demand towards better surveillance and control of emissions increases as well.Earlier and new industrial measurements in FeSi- and Si-metal furnaces reveal quite high NOX-emission. The measurements also show that the NOX formation (mainly as thermal NOX) is distinct connected to the formation of dust (SiO?SiO2) in the combustion chamber above the furnace surface, when the temperature is high and the access to N2/O2 is good. This means that stoking, charging and temperature straight above the furnace surface is important factors for the NOX formation."

Jan 1, 2012