Preparation And Structural Characteristic Of Cobalt-Modified Magnetite

Magnetite was prepared by hydrogen reduction method. For a conversion to cobalt-modified magnetite, magnetite particles were suspended into a solution containing Co2+ and Fe2+ to precipitate a cobalt ferrite layer on the surface. pH value influences the particle composition directly, the desirable CoFe2O4 is obtained when pH value is 12. The coercivity increases with the increase of cobalt content, cobalt efficiency reaches a maximum value at cobalt content of 2.71wt%. With cobalt modification, magnetite particles have similar lattice constant and squareness ratio to that without cobalt modification. TEM and XPS analyses indicate that acicular morphology is retained during the coating process, the epitaxial growth layer consists of CoFe2O4and 0.3Co2O3CoFe2O4 at cobalt content of 2.71wt% and 5.03wt%, respectively.