By E. W. Cawthorne, R. I. Jaffee, C. M. Craighead

SOLUTION of a solid metal or alloy in a molten metal bath is used daily in melting operations, extractive metallurgical processes, and in brazing. It is generally recognized that temperature, time, agitation, and the composition of the solute metal and the solvent bath all affect solution rate. However, there is little information available in the literature on the kinetics of the process or the relative effect that these variables have on solution rate. In connection with an aluminum brazing study, data on the solution of aluminum in an A1-Si* bath to promote rapid solidification. The chemical analyses were made on drillings taken from the cast plates. The results of this work are listed in Table I. The thermal-analysis data were obtained on 200 gram samples cooled at approximately 1.5" per min. A calibrated chromel-alumel couple was used. The thermal arrests were recorded autographically on a General Electric photoelectric potentiometer recorder. The instrument was calibrated to 22.5 pct. The thermal emf was bucked with a Leeds and Northrup semiprecision potentiometer so that 1 mv represented the full scale of the GE recorder. Referring to Table I, it will be noted that the analytical results tend to be lower than the intended compositions by about 0.3 pct Si in the higher ranges. In view of the known difficulties in obtaining accurate silicon determinations by wet analysis when the silicon content is high and in view of the care that was employed in weighing and preparing the alloys, the intended compositions are believed to be more accurate than the analyses. Furthermore, when the thermal-arrest data are plotted against the intended compositions, a smooth curve is obtained, as shown in Fig. 1. This is not the case when the data are plotted against the analytical results. It will be noted from Table I that the 12.5 pct Si alloy (melt 4) showed a primary arrest at 577.6"C and the eutectic at 576.l°C. The metallographic examination of this chill-cast plate sample showed a small amount of primary silicon. These results, Fig. 1, place the eutectic at slightly less than 12.5 pct Si and are in rather good agreement with the unpublished Hanford data. In all of the subsequent work, the composition of the A1-Si dipping baths was determined by thermal analysis (spread between the primary arrest and the eutectic temperature) employing 12.5 pct Si and 577.2 °C as the composition and temperature of the eutectic. Material Preparation and Selection of the Techniques: At the beginning of this work, it was anticipated that, owing to oxide film present on the surface of the aluminum, difficulty would be encountered in obtaining rapid uniform wetting of aluminum specimens dipped in the A1-Si bath. The following etchants were investigated as possible methods of providing a thin uniform oxide film on the specimen surface: 1—phosphoric acid (H³O4), 2—fluoboric acid (HBFI), 3—sodium hydroxide (NaOH), and 4—hydrofluoric acid (HF). Tests with sheet .specimens (2x½x0.06 in.) of 2s aluminum prepared with these etchants indicated that the fast uniform wetting required for this work could not be obtained if any oxide film existed on the specimen surface. Tests were then conducted by dipping similar specimens etched in 5 pct NaOH and given a thin

Jan 1, 1956

By D. G. Westlake

Polycrystalline tensile specimens of various Zr-0-H alloys have been tested at 298°, 178°, and 77°K. Solute oxygen and hydride precipitates in quenched alloys made individual contributions to the yield strength at 0.2 pct strain which combined to produce a resultant strength increment, a,., Ductility changes which were ohserved can he interpreted in terms of the various oxygen and hydrogen concentrations, testing tem -peratures, and dispositions of the hydride. ADDITIONS of oxygen in solid solution were known to increase the yield and tensile strengths of polycrystalline zirconium as early as 1951.' More recently, the critical resolved shear stress (CRSS) for prism slip in zirconium single crystals was also shown to be affected by the solute oxygen impurity.' This latter work also demonstrated that large increments of strength could be contributed by the finely dispersed zirconium hydride precipitates that are present in quenched Zr-H alloys.3 It was concluded that the combined strengthening due to alloying could be expressed by where to is the increase in the CRSS due to solute oxygen alone and TH is the increase due to finely dispersed hydride precipitates. Eq. [I] is analogous to one used to express the combined strengthening effects of work hardening and neutron radiation damage.4 Eq. [1] was verified only indirectly and for only small amounts of the impurities—up to 0.14 at. pct 0 and 0.63 at. pct H. The present investigation was undertaken to obtain a more direct verification of the validity of the form of Eq. [1] for this system and also to determine the combined effects of oxygen and finely dispersed hydride precipitates on the tensile strength and ductility of polycrystalline zirconium. EXPERIMENTAL PROCEDURE Tensile specimens were machined from the same rolled billet of Kroll zirconium used in the earlier study.' These measured 38 by 4.7 by 0.5 mm and had 10-mm gage lengths which were 2.8 by 0.5 mm. Each specimen was ß-annealed in vacuo at 1173°K for 15.5 hr and a-annealed at 1073°K for 4 hr to D. G. WESTLAKE, Member AIME, is Associate Metal l ur-gist, Metallurgy Division, Argonne National Laboratory, Argonne, III. Manuscript submitted July 17, 1964. IMD______________ give an equiaxed structure with grain diameters averaging 0.06 mm. Oxygen was added by allowing the metal to react with a known quantity of oxygen during the 0 anneal and known quantities of hydrogen were added during the a anneal. Each alloy was encapsulated in Pyrex under vacuum, annealed at 873°K for 4 hr, quenched into ice water, and polished by immersion in a solution of 46.75 vol pct H2O, 46.75 vol pct concentrated HNO3, and 6.5 vol pct HF (49 pct) at 298°K. Special heat treatments given to a few specimens are described in the results below. Tensile tests were done on an Instron machine and were begun within 20 min after the quench, except where specified otherwise. Tests at 298°K were in air, at 178°K in acetone, and at 77°K in liquid nitrogen. All tests were at a strain rate of 8x sec-1. RESULTS AND DISCUSSION Yield Stress at 298°K. The compositions of alloys and the corresponding yield stresses (0.2 pct strain) are given in Table I. A plot of the yield stresses of the oxygen alloys, A, B, C, and D, indicates that varies linearly with CO1/2, where Co is the oxygen concentration, Fig. 1. This is in accord with Fleischer's6 theory for solution strengthening if the oxygen atoms do not cluster, or the cluster size remains constant with increasing oxygen concentration. In Fig. 1, it appears that if one could prepare some oxygen-free zirconium its yield stress would be very low. Therefore, we shall assume that for the oxygen alloys is equivalent to O0, the strength increment contributed by the presence of oxygen. The relationship between0.2and Co is expressed by 0.2 = 31.3 CO1/2, when the yield stress is in kg per sq mm and the concentration is in at. pct. Each of the hydrogen alloys, Al, A2, A3, and A4, contained 0.081 at. pct 0 as an impurity. In Fig. 1, it appears that this small amount of oxygen makes a significant contribution to the strength which cannot be ignored when we evaluate the contribution of the finely dispersed hydride. Let us assume the validity of the following equation: a0.2 = (a2o+a2R)1/2 [2] which is analogous to Eq. [I] for single crystals, and calculate values of UH for the hydrogen alloys by using the experimental values of 0.2 and o (0.081 at. pct) = 8.9 kg per sq mm. For 0.36 at. pct H, oH = 6.47; for 0.72 at. pct H, OH = 11.30; for 2.16 at. pct H, OH = 19.4; and for 3.60 at. pct H,

Jan 1, 1965

By Whitman E. Brown

The installation in 1948 of a Humphrey spiral concentrator section at the Hill-Trumbull plant of The Cleveland-Cliffs Iron Co. is the latest commercial method on the Mesabi Range being used for the recovery of fine iron ore. In two stages of concentration 84 spirals treat approximately 120 long tons per hour of minus 1/8 in. ore. These spirals augment the production of the heavy-density plant which recovers the plus 44 in. iron from the plant crude ore. Structure of the ore is such that, when crushed, about 50 pct of the plant crude is minus 1/8 in. size. After desliming in a 66 in. Akins classifier, grinding the classifier product in a ball mill and again desliming in a 78 in. Akins classifier about 15 pct of the crude ore remains to be treated in the spiral plant.

Jan 1, 1949

By J. Alfred Berger, O. M. Katz

Selected samples of hydrided Zr-Hf alloys were rapidly quenched to voom temperature and exrtrnined metallographically, by X-ray diffraction, and through micro hardness studies to confirm high-temperutuve data Confirming experiments sllowed that there were five phases in this Lernary system: 1) hextrgonal with lattice parameters similar to that of the initia1 Zr-Hf alloy but slightly enlarged due to dissolved hydrogen; 2) fee with properties of a brittle, intermediate, hydride compound; 3) fct with c/a crvoltnd 1.07 and which appeared as a neetilelike precipitale; 4) hexagonal, designated ?, with c/a ratio of 2.37; and 5) orthorhombic, designated X, with a = 4.67, b = 4.49, and c = 5.093 and whose tnicro-st?ruct~ival nppetrl-nnce depcncled o/i, heat lvecrt~r~ent. The tetragonrrl phase never crppeal-erl witkorct the cubic hydricle. Abpecrrtrnce of 0 and A also tlependet on the hafnium content of the zirconium. A previous paper' on the Zr-Hf-H system described the thermochemical data obtained with a high-vacuum, high-sensitivity mirrogravimetric apparatus. This data presented a fairly complete picture of the phase relationships at elevated temperatures. However, it could not establish the actual crystal structures, lattice parameters, or metallographic disposition of the hydride phases. The present complementary study utilizes X-ray powder patterns along with light and electron microscopy to characterize completely the five hydrided phases found in Zr-Hf-H alloys quenched to room temperature. Crystallographic features of the zr-Hf,2,4 zr-H,5-7 and Hf-H8 systems have been summarized in Table I. Designations of a, ß, and ? were retained in the Zr-Hf-H system for the phase regions through which the pressure-composition isotherms always sloped. However, it was not firmly agreed that these were single-phase regions.' In fact, the region designated y always contained a cubic as well as a tetragonal phase after quenching to -196°C. MATERIALS Preparation of the high-purity Zr-Hf alloys has been described.' The four zirconium alloys which were hydrided contained 37 wt pct Hf (23 at. pct), 51 wt pct Hf (37 at. pct), 73 wt pct Hf (58 at. pct), and 91 wt pct Hf (82 at. pct), respectively. These were designated B-2, B-4, B-6, and B-8. Photomicrographs of the initial alloys showed the material to be quite clean as would be expected from the precautions exercised in producing them. However, there were a number of annealing twins but no other subgrain structure. In addition to the four original alloys, fifteen hydrided samples were observed at room temperature. Hydrogen compositions are given at the top of Tables I1 to V. APPARATUS The phases present at elevated temperatures were studied by quenching hydrided samples to room temperature by two different methods, both under vacuum: 1) fast cooling of the sample tubes of the microgravimetric apparatus1'9 with flowing air and 2) rapid quenching into liquid nitrogen. The cooling rate for 1) was 750° to 250°C in 30 sec. Since the microbalance chamber was not designed to permit very rapid cooling of a hydride sample, all liquid-nitrogen quenching was done in an auxiliary experiment. The auxiliary quenching apparatus consisted of a small-bore, high-temperature furnace, a sealed SiO2 tube containing the sample, and a dewar quenching flask filled with liquid nitrogen. The hydrided sample, previously quenched in the microgravimetric reaction chamber, was placed in a platinum boat in a vacuum-degassed SiO2 tube. A zirconium wire getter and degassed SiO2 rod, to reduce the internal volume, were also in the tube. After sealing the tube under vacuum the zirconium getter was heated to absorb the last traces of gas. Only the sample was heated at the reaction temperature for the desired length of time, and then the tube dropped through the opposite end of the furnace into the dewar. A quenching rate of 200" to 400° C per sec was estimated. Analyses of samples after the auxiliary experiment also showed practically no increase in oxygen or nitrogen content from heating in the SiO2 tube. All of the samples were examined at room temperature by the X-ray powder method. The majority of the powder patterns were obtained with double nickel-filtered CuKa radiation after 8- and 16-hr exposures in an 11.48-cm-diam camera. Cobalt and chromium radiation were also used to spread out the high d value end of the Pattern. Such patterns readily identified the minor phases. NO oxide or nitride lines were found. Where sharp back-reflection lines existed it was possible to reduce the

Jan 1, 1965

By Robert S. Williams

NO new ferrous alloys have been produced in the last five or six years that are as outstanding contributions to civilization as were the high-speed steels of the early part of the century or the stainless steels announced at the close of the World War. There have been, however, many developments of major importance having to do either with modifications of existing alloys or with new methods of treatment of older iron or steel alloys. Only a limited number of these new developments can be discussed and their selection does not necessarily imply that these are the most important but merely that they are of general interest rather than perhaps of greater importance in highly specialized fields.

Jan 1, 1939

By William C. Hagel

Oxygen-18 exchange between gaseous oxygen, held at a pressure of 125 mm Hg in a PL-IORh chamber, and splzeres of a Fe2O3 containing three or less grains was determined from 9000 to 1250°C. Isotope equilibrum on crystal surfaces appears to be quickly established, and the rate-determining factor is self-difiusion confbvrning to the relation D = 2.04 esp(- 77,900/RT) sq cin sec-'. Changing sphere diameters caused no detectable variation in diffusion coefficients. Oxygen ions diffuse faster than cations at low temperatures, but a crossover may occur at about 1150°C. INVESTIGATIONS by Davies et al.' and Himmel et al2 have suggested that the mechanism of iron oxidation above 600°C involves a predominance of cation migration in the wüstite (FeO) and magnetite (Fe301) layers and oxygen-ion migration in the hematite (a Fe2O3) layer. Evidence for little cation migration during hematite growth consists of: 1) the disappearance of radioactive-silver markers, presumed to vaporize from the oxide-gas interface, and 2) a large discrepancy between parabolic rate constants for magnetite oxidation and those calculated from Lindner's3 data for cation self-diffusion, D:, using Wagner's theory.4 Reversing the calculations gave anticipated self-diffusion coefficients, D:, for oxygen ions of 3.6 x 10-9 sq cm sec-1 at 1100°C and 5.9 x 10-10 sq cm sec-1 at 1000°C. Since then Kingery et a1.5 reported three values for oxygen-ion diffusion in polycrystalline, sintered hematite. These were obtained near 1200°C, at an oxygen pressure of approximately 150 mm Hg, and could be represented by the Arrhenius expression, Dg = 1 x 10 11 exp(-146,000/RT) sq cm sec-1. Extrapolation to temperatures below 1100°C infers that oxygen ions are less mobile than cations. This contradicts the aforementioned oxidation evidence and also coble7s study of the initial sintering of hematite. From the latter, apparent diffusion coefficients for the slowest rate-controlling species could be calculated, and fair agreement was found with an extension of Lindner's data for cation diffusion. Fig. 1 depicts such comparisons graphically. Three points have been included for the determinations of Himmel et al. on cation diffusion in large, natural hematite crystals surrounded by pure oxygen at atmospheric pressure. No dependence on crystal log raphic direction was noted. Since the value of 10-l4 sq cm sec-' at 1000°C actually represents an upper limit, one might interpret that there is a small decrease in D: when single crystals are employed. On the whole, however, cation diffusion appears relatively well-defined,* while the few results tension to lower temperatures. After having gained experience measuring oxygen-ion diffusion in certain glasses7 and in the corundum oxide, a Cr2O3, the purpose of this work was to determine D; values for hematite and thus possibly assist a mechanistic understanding of the kinetics of the oxidation and reduction of solid iron oxides. I) EXPERIMENTAL PROCEDURE A) Material. Hematite powder of moderately high purity was received from the Columbian Carbon Co. An accompanying lot analysis listed 0.03 H2O, 0.008 weight percents, with the remainder Fe2O3. Subsequent treatments were ball milling, drying, prepressing, and hot-pressing for 60 min at 1350°C under 5000 psi. Since graphite dies coated with a slurry of alumina were used for hot-pressing, the surrounding atmosphere at temperature was sufficiently reducing to form some magnetite on the outer surface of each cylinder. After removing any attached alumina, a stabilizing anneal of 50 hr at 1300°C in oxygen was added. The final product was nonmagnetic and exceeded 97 pct of the density (5.24 g cm-3) usually given for FezO3. On polishing cylindrical ends, counts were made of the number of grain boundary intercepts per

Jan 1, 1967

By George C. Gibbons

ALMOST everyone in any of the five counties embracing the great East Texas field depends heavily upon oil for his living whether or not he actually owns a well or piece of royalty himself. Oil is a natural resource that, when utilized, spreads its benefits over a vast area and into many channels. Depending then almost entirely upon agriculture: what is now known as the East Texas oil field a decade ago had a scattered farming population. For many of its people, tomatoes and other vegetable crops coupled with the old southern stand-by of cotton, furnished an adequate living and a small cash surplus. Some farm families on the red hills, however, were not far re- moved from the sowbelly and black- eyed peas, or cornpone and potlikker, standard of living. Kilgore of that day, was a village of less than 850 per- sons. Longview, with just over 5000, apparently had reached the limit of its growth. Tyler was an overgrown farming town of around 17,000 persons, de- pending largely upon the agricultural income of Smith County and surrounding territory for which it was a trading center.

Jan 1, 1941

By B. G. Reisdorf

This paper describes the microstructural changes that occur when quenched ultrahigh-strength steels containing OA pet C and various amounts of nickel, silicon, and cobalt are tempered. The changes that occur in hardness, yield strength, and martensite diffraction-peak widths when these steels are tempered are related to the precipitation of the carbide phases. An unea$ectedly high silicon content (about 30 pct) was found in the E -carbide phase in a steel containing only 1.5 pct Si. TEMPERED martensitic steels have such wide-spread utility that they have been the subject of numerous investigations, and a sizable amount of literature has developed on this subject.M This investigation, which is a part of a larger program to correlate microstructure with mechanical properties at a variety of strength levels, is limited to the microstructural changes that occur when a quenched 0.40 pct carbon steel (USS Airsteel X-200 steel) is tempered, and to the effects of the alloying elements—nickel, cobalt, and silicon—on these microstructures. Used in this investigation were electron microscopy, electron-diffraction identification of the carbide phases, electron-probe micro-analysis of the carbides, X-ray determinations of retained austenite, and measurements of martensite X-ray diffract ion-peak widths. MATERIALS AND METHODS The chemical analyses of the eight heats examined eats No. 30 through 37) are shown in Table L Heat No. 30 has the chemical com~osition of Airsteel X-200, and the remaining seven heats contain various amounts of nickel, chromium, cobalt, and silicon. The heats were air-melted in an induction furnace and cast into 8 by 8 in. ingots that were subsequently heated to 2300 and rolled to 1-in.-thick plate. Oversize 0.505-in.-diam tensile specimens were rough-machined from the plates and austenitized in air at 1700° F for half an hour and oil-quenched. The specimens were then tempered in air at temperatures of 400° to 1000 for tempering times of 1, 4, and 16 hr, and finish-machined to 0.505-in.-diam tensile specimens. Electron micrographs were prepared from Formvar replicas of the midthickness of tensile-specimen shanks that had been electrolytically polished and etched in nital. Electron-diffraction patterns were obtained from carbon-extraction replicas. The replicas were prepared by etching the sample surface in the same manner as for microscopy, evaporating carbon on the etched surface, and re-etching the sample to free the carbon film and the precipitate particles. Electron-probe microanalysis was performed on some of the extraction replicas. To obtain adequate fluorescent X-ray intensities, several thicknesses of replica were exposed to the electron beam so that the results represent an average composition of the extracted particles rather than an analysis of single precipitate particles. The retained austenite contents of the specimens were determined by an empirical X-ray diffraction

Jan 1, 1963

By M. M., Fine

In a laboratory study of grinding and classification' of silica sand, a satisfactory means of producing the medium-fine specification sand desired by producers of flint-glass containers was developed. The best procedure consisted of ball-mill grinding and double classification, which gave a properly sized sand containing less iron than the feed.

Jan 1, 1950

By Leon Borgman, Michael P. Lipkewich

Orebodies at or near the surface are generally amenable to open pit mining. The development of a mining program involves designing an ultimate pit and a production schedule. This pit maximizes total profit while the production schedule maximize6 the present value of the property. Optimum pit limits can be approximated by two-and three-dimensional numerical techniques. These techniques presuppose that the mineralized area has been sufficiently sampled to allow a reasonably accurate prediction of grade at any spatial location.

Jan 1, 1969

By Edmund J. Korber, Donald E. Raab, Frank A. Burns

During the early 1960s, the advent of self- advancing longwall roof supports triggered serious consideration by Bethlehem management to introduce the technique of longwall mining at one of our central Pennsylvania coal mines. Although longwall mining was initially justified as a means to cope with the severe roof conditions at our Mine 32 (Watson, B., 1971), the result of the endeavor has been a consistent and reliable level of coal production, first from Mine 32 and then later from Mine 33, over a period of fifteen years. Longwall production from the Cambria Division has been the mainstay of the low volatile coal required by Bethlehem Steel for steel production. Let us review the events that led to this accomplishment, as well as where we stand today.

Jan 1, 1981

By Charles E. Lundin, Albert S. Yamamoto

The phase eqrtilibria of the binavy system, Nb-Al, weye established by metallographic, X-ray diffraction, hardness, and thermal-analysis techniques. Three intermediate phases were identijied, Nb3.41, Nb2Al, and NbAl,. The N6,Al and NbAl phases have extensiue ranges of solubility. The maximum solubility of aluminum in niobiuitz is 23.0 i0.5 at. pct (8.0 wt pct) A1 clt 1960" i 10°C. The maximumt solinbility oj niobiunz in alunzinutz is less than 0.3 i0.1 at. pct (1.0 tut pct) fib. The A'h,Al and Nbgl interinediate phases forr peritectically at 1960° 1UcC and 1870" i 1U9C, respectively, zuhereas the NbAl, phase fornts congvuently fio11t the melt at 1605" 10°C. A eutectic reaction oc- The intent of an over-all research program was to develop niobium-aluminide-base coatings for refractory metals since these coatings exhibit useful high- curs at 57.8 i 0.5 at. pct (28.5 wt pet) A1 and 1500" 10°C between NbAl and NbAl3. The aluminum-rich region of the system has a peritectic reaction where liquid reacts with NbAL, to form aluminum solid solution. Structural and lattice -pavarneter data /or the intermediate phases were determined by X-ray diffraction analyses. An unusual transfov?nation having charactevistics of nucleation-growth and martensitic nleclanisils occurs on cooling the niobium solid solution in the region from 18 at. pct (6 wt pct) Al to 23 at. pct (8 wt pct) Al. The transfornzed product on rapid quenchirzg is an acicular NhAl. temperature resistance to oxidation. As a prerequisite, the phase equilibria of the system, Nb-A1, were necessary. A literature survey revealed that the phase-equilibria data reported by various investigators were rather incomplete and conflicting. Therefore a complete determination of the system was undertaken by the authors from 0 to 100 pct of solute addition.' In 1959 Savitskiyz presented a tentative diagram which

Jan 1, 1967

By J. T. Ryan

POISONOUS, irritating, or explosive gases are found in almost every industry, and manufacturers of gas masks are called upon to provide gas mask protection for a great variety of conditions, such as operators in horseradish factories, fumigators of homes and ocean liners, and men engaged in the manufacture of tetra-ethyl-lead, the new motor fuel. The modern type of gas mask and respirator, to provide protection against all such industrial gases, is an outgrowth of the gas mask developed during the World War to protect the soldiers against the poisonous war gases. So far, it has been possible to develop ample mask protection from all known noxious gases and fumes present in atmospheres encountered in mines, metallurgical works, and chemical and other industries, so long as there is sufficient oxygen present to support the flame of an oil lamp. The most important development of the gas mask was in providing protection against carbon monoxide- which is the noxious gas that mining men are most concerned with and, in fact, is the noxious gas that man is most frequently exposed to. This paper will be con- fined largely to the discussion of masks for underground use in metal mines. Gases that contaminate the normal air in mines can be divided into two classes: those that are given off normally by the workings, and those that are produced in mine operation.

Jan 1, 1926

By W. L. Chen

The Batac jig was first introduced in the US for fine coal cleaning in 1973 (Tackett, 1977; Hake, 1976). Since then, a total of six such jigs of various sizes have been installed in five US plants for a total capacity of 2346 t/h. The raw coal size ranges from 19 mm x 0 to 9.5 mm x 0-fraction sizes previously fed to heavy medium cyclones, Deister tables, or water only cyclones. Growing interest in the Batac jig as a replacement for the above equipment is due to the following reasons: • Unlike heavy medium cyclones, no magnetite is required. As a result, the operating cost of the plant is reduced. • The compactness of equipment is unique on a unit ton per hour basis as compared to other equipment. • Solid state electronic control of jig stroke length, frequency, and jig bed depth makes the equipment highly efficient. Installations of Batac jigs in the US as of June 1980 are shown in [Table 1]. Use of the Batac jig is even greater outside the US (Anonymous, 1980; Chen, 1980). Its use is not limited to fine coal but is applied to coarse coal as well, with 102 mm size in the feed (Zimmerman, 1975). In countries where consumption of magnetite associated with the heavy medium system of coal cleaning is considered a waste of iron ore resource, the Batac jig is regarded as the primary choice in the selection of cleaning equipment (Chen, 1980).

Jan 1, 1981

By Sherwin F. Kelly

THAT gold ores occur in Georgia is a fact apparently not widely known outside of that state, yet in the last hundred years nearly $18,000,000 worth of gold has been mined there. The discovery of gold-hearing quartz was made in 1823 on the "Forty Acre Lot" (which now belongs to the Columbia Mining Co.), in McDuffie County, and about seven years later the first stamp mill on record was erected near there. In recent years Georgia's gold production has dwindled to an insignificant figure. However, with the increase in gold price, interest in this district has been revived, so an electrical geophysical survey was undertaken to aid in discovering new quartz veins, on a part of the Forty Acre Lot, the adjoining Hamilton mine, and the nearby Woodall property.

Jan 1, 1934

By J. H. Swisher

The rate of internal sulfidation of austenitic Fe-Ti alloys in H2S-H2 gas mixtures is controlled primarily by sulfur diffusion, with counterdiffusion of titanium playing a minor role. At temperatures below 1100°C, enhanced diffusion along grain boundaries becomes important. The rate of internal sulfidation at 1300°C is approximately equal to the rate computed from the sulfur diffusion coefficient. The diffusion coefficient of titanium in y iron has been determined from electron microprobe traces in the base alloy near the subscale interface. The solubility of sulfur in Fe-Ti alloys has been measured in the temperature range from 1150° to 1300°C. The equilibrium sulfur content is found to increase with titanium content, due to the large effect of titanium on the activity coefficient of sulfur. The Ti-S interaction becomes stronger as the temperature decreases. TITANIUM as an alloying element in stainless steels is an effective scavenger for interstitial impurities, carbon in particular. Titanium is known to form stable sulfides; however extensive thermodynamic data on the Ti-S system are not available. Schindlerova and Buzek1 have shown that the Ti-S interaction in liquid iron is moderately strong. There have been no previous studies of the Ti-S interaction in solid iron. Internal sulfidation of Fe-Mn alloys was the subject of a recent investigation by Herrnstein.2 He found the rate of internal sulfidation to be an order of magnitude greater than predicted from available solubility and diffusivity data. A satisfactory explanation for the discrepancy could not be given. In the present study, the solubility of sulfur in austenitic Fe-Ti alloys was measured using a standard gas equilibration technique. Fe-Ti alloy specimens were also internally sulfidized. The rate of internal sulfidation was measured as a function of temperature and alloy composition. Supplementary electron micro-probe measurements were made to provide additional information on the nature of the internal sulfidation process. EXPERIMENTAL The starting materials were alloys containing 0.12, 0.24, 0.38, and 0.54 wt pct Ti. The alloys were made in an induction furnace by adding titanium to electrolytic iron that previously had been vacuum-carbon-deoxidized. The major impurity in the alloys as determined by chemical analysis was carbon. The carbon content of the alloys averaged about 100 ppm; metallic impurities were presented in concentrations of 50 ppm or less. Specimens were made in the form of flat plates, 0.03 by 2 by 4 cm for the equilibrium measurements and 0.5 by 1.5 by 3 cm for the rate measurements. The experiments were performed in a vertical resistance furnace wound with molybdenum wire and containing a recrystallized alumina reaction tube. In the gas train, flow rates of the reacting gases were measured using capillary flow meters. The source of H2S was a mixture of approximately 2 pct H2S in H2, which was obtained in cylinders from the Matheson Co. A chemical analysis was provided with each cylinder. The H2-H2S mixture was diluted with additional hydrogen to obtain the desired ratio of H2S to H2, and the resulting mixture was diluted with 30 pct Ar to minimize thermal segregation of H2S in the furnace. Argon was purified by passage over copper chips at 350°C and subsequently over anhydrone. Hydrogen was purified by passage over platinized asbestos at 450°C and then over anhydrone. The H2-H2S mixture was purified by passage over platinized asbestos and then over Pas. The samples used in the solubility measurements were analyzed for sulfur by combustion and iodometric titration. The subscale thickness in the internally sulfidized samples was measured on a polished cross section, using a microscope with a micrometer stage. Electron microprobe traces for titanium in solution were made on several samples that had been internally sulfidized. A Cambridge microanalyzer was used, and the known titanium content at the center of the specimen was used as a calibration standard. The procedure for the microprobe measurements will be described further when the results are presented. RESULTS AND DISCUSSION Equilibrium Data. Fig. 1 shows the sulfur concentration as a function of gas composition for three alloys equilibrated at 1300°C. The dashed line is based on data published by Turkdogan, Ignatowicz, and pearson3 for pure iron. The breaks in the curves are the saturation points for the alloys. The fact that the initial slope decreases with increasing titanium content indicates that titanium interacts strongly with sulfur in solution. To obtain information on the composition of the precipitating sulfide phase, the measurements described in Fig. 1 were extended to higher sulfur partial pressures. These results are shown in Fig. 2. (The initial portions of the curves are reproduced from Fig. 1.) The highest PH2s /pH2 ratio used is believed to be below the ratio required for the formation of a liquid sulfide phase. Time series experiments were used to study the approach to equilibrium in the samples. It was found that equilibrium with the gas phase was reached in less than 4 hr at 1300°C.

Jan 1, 1969

By P. R. Bradley

NO thought had been given to deep level mining at the Alaska Juneau mine prior to 1930, but in that year a prospect winze was started and continued for 1000 ft. vertically below the main haulage or adit level. The point at which this winze was started was selected entirely by the prevailing physical conditions, such as proximity to established workings, convenience, and the presence overhead of a substantial pillar of dimensions sufficient to lo¬cate the sheave wheel and loading pocket. It was, therefore, with some surprise that the unusually high-grade ore found just below the collar of the winze persisted, with certain vari¬ations, to a full depth of 1000 ft. vertically. Likewise this unusually high-grade ore was found to persist on the various crosscuts driven on levels at 200-ft. vertical intervals. To be brief, this deep level work found richer ore than any yet found in the mine over like areas, and inasmuch as the area was sufficient to plan for extensive deep level mining, plans for such work were given extended consideration.

Jan 1, 1936

By N. E. Rogen, N. J. Grant

WHILE direct measurements of the growth of precipitate particles during aging is of fundamental value, few such measurements have been made. Direct measurements by means of optical or electron-microscopy and X-ray techniques are preferred, however, many of the aging studies have been based on indirect methods such as electrical resistivity and hardness. Because of the minute size of most precipitate particles (less than 1000A) the light microscope is of limited use while electron microscopy is subject to slowness, etching problems and consequent resolution problems. It is fortunate that alloys of the Nimonic type, based on Ni-Cr-Ti-Al, lend themselves to accurate and relatively easy particle size measurements. With proper balance of titanium and aluminum, the only aging precipitate is the gamma prime (r') Ni3,(Al, Ti)2 phase and this phase is the basis of the high-temperature strength of these allos.3-6 The Ni3(Al, Ti) phase is a face-centered-cubic, ordered structure with nickel atoms occupying the cube faces. Titanium atoms can replace three out of every five aluminum atoms and when substituting do so preferentially.2 Electron microscopy has shown that during aging of most of the commercial alloys of this type, precipitate particles are unusually uniform in size and distribution, and that the volume of (r') phase is large (20 pct).4,7 The aim of this investigation was to measure the growth of (y') phase during aging. In so doing, it was hoped that a clearer understanding of the aging process would be attained. X-ray line broadening was used as the measure of precipitate particle size. This technique was selected because it can measure and average the diameter of thousands of particles in one operation. The variations in hardness and matrix lattice parameter with aging were also studied and related to the particle size. EXPERIMENTAL PROCEDURE An alloy of the following composition was studied: Cr Ti A1 C Ni Wt pct 20.71 2.98 1.43 0.04 bal. At. pct 22.06 3.47 2.95 0.18 bal. The alloy, a 15- lb vacuum melt, was forged to 1/2-in. diam at a temperature of 1900" to 2200°F; was solution heat treated for 4 hr at 2000°F and water quenched; and was then aged in various ways. The ASTM grain size was 4 to 5. No (7') phase could be detected by X-ray analysis after solution treatment and electrolytic extraction. Aging was performed on 2-in. long specimens at 1400°, 1500°, and 1600°F for increasing times. One-half inch sections were removed after each time increment and were then electropolished in a solution of H3P04 saturated with chromium trioxide at a potential of 30 v and rectified with a tantalum electrode. Rockwell hardness measurements were taken using one side of the polished specimen. Matrix lattice parameter determinations were made on the other side using filtered chromium radiation references with the position of the (220) line of a silicon standard. To enable the precipitate particles of the (y') phase to be measured using X-ray line broadening techniques, it is first necessary to separate and concentrate this phase by electrolytic extraction. Extraction is necessary because the difference between matrix and precipitate lattice parameters is only approximately 0.5 pct and intensities of.the (y') phase lines are very weak relative to those of the matrix. The extraction techniques employed have been described before and found to produce a reasonably quantitative separation.398 A water solution of 15 pct H3Po4 is used at a current density of 0.5 amp per sq in. at 6 v. The precipitate particles are separated from the liquor by centrifuging and decanting and are then washed, dried and repowdered. A plot of the X-ray intensity vs diffraction angle for the (111) line of the precipitate particles was used as a measure of particle size. The intensity curve approximated the shape of Gaussian distribution function and its breadth was measured at the half height. The (220) line of a silicon standard was used to correct the measured line breadth for instrumental and other broadening errors. The Scherrer formula was used to calculate particle

Jan 1, 1961

By Robert H. Hafner, Irvin R. Kramer

IN recent years considerable interest has been shown in surface-alloyed metals, particularly those of chromium (chromized steels), which have excellent corrosion [ ] resistance under a variety of severe conditions, and may undergo bending and flanging operations without spalling. An early method1 employed to produce a high-chromium case on steel was developed by Kelley in 1921. It consisted of heating a low-carbon steel in intimate contact with powdered chromium in the presence of hydrogen at temperatures sufficiently high to permit diffusion of chromium into the steel. The usefulness of this process was limited because the extremely high temperatures of 1200° to 1400°C. (2200° to 2550°°F,) caused excessive grain growth and warpage, Louenstein and Ulmer2 packed iron castings in ferrochromium and com- [ ] mon salt, and heated for approximately three hours at 930° to 1040°C. (1700° to 1900°F,). A recent and more practical method of depositing chromium on steel surfaces has been developed in Germany by Daeves, Becker and Steinberg3-8 and in Russia by Izgaryshev and Sarkisov.9 This process consists of passing gaseous chromium chloride over the steel to be chromized at temperatures of 900° to 1000°C., or packing them in a porous, ceramic material that previously had been saturated with chromium chloride. They reported obtaining a chromized layer, 0.004 in, thick, on low-carbon steels. Later, Daeves4 established a relationship between the carbon content

Jan 1, 1942

By Frederic Brunton

I. INTRODUCTION THE smelting plant of the British Columbia Copper Co. at Greenwood, B. C., now closed because of the decline in the price of copper due to the European war, is of special interest to metallurgists for several reasons. It was successfully smelting in blast furnaces the lowest grade copper ore of all plants in America. In order to do so, it had to run at' very high efficiency, which necessarily required a large tonnage per square foot of hearth area, together with the minimum amount of labor and other costs. The furnaces smelted daily 2,250 tons of ore (6.62 tons per sq. ft. of hearth area), carrying 0.85 per cent. of copper, at a smelting cost of $1.18 per ton. The entire plant required 130 men to operate it and keep up repairs, showing a labor efficiency of about 17.5 tons per man per day. In the present paper, the method of obtaining these results is shown. Most of the information contained in this description I obtained as Assistant Superintendent, during the two years preceding the present shutdown. Other sources of information to which I am indebted are: The British Columbia Copper Co., Ltd., by Alfred W. G. Wilson, in The Copper Smelting Industry of Canada; Greenwood Smelting Works, by J. E. McAllister, Engineering and Mining Journal, vol. xci, pp. 1011 to 1015 (May 20, 1911); and Description of the Copper Smelter of The British Columbia Copper Co., by W. L. Bell, in Transactions of the Canadian Mining Institute, vol. xvi, pp. 151 to 154 (1913).

Jan 7, 1915