Search Documents

By Arnaldo Forgas Júnior

Three techniques for ferrite quantification were applied in a duplex stainless steel UNS S31803 solution treated at three different temperatures, 1000, 1100 and 1200°C, in order to verify their compliance with the results from ThermoCalc® prediction. It is verified that only austenite and ferrite phases are present in the samples and that an increasing in solution treatment temperature led to the increase of the volume fraction of ferrite. It is also observed that quantitative stereology technique shows absolute values closer to ThermoCalc® predictions. On the other hand, measurements by ferritoscope and XRD show significant deviations, probably due to texturing effect imposed by the rolling process.

Aug 16, 2017

By João Paulo Ferreira Santos

Neste trabalho, foram obtidas estruturas compósitas constituídas por camadas alternadas de epóxi com mantas de nanofibras de nylon 6. As nanofibras foram produzidas pela técnica de eletrofiação. O comportamento mecânico destas estruturas sob tração e sob impacto pendular IZOD foram estudados. A incorporação das nanofibras na matriz epoxídica permitiu aumentos no módulo de elasticidade (6%), na resistência a tração (7%) e na energia de impacto (2%), ou seja, houveram ganhos de resistência mecânica sem sacrificar a resistência ao impacto, ao contrário do que ocorre na quase totalidade dos micro ou macromateriais modificadores do epóxi.

Aug 8, 2018

By Moisés Paulo Teixeira

The use of tailings for the synthesis of new materials is a worldwide concern today. This paper approaches the utilization of tailings of soapstone (steatite) in order to produce ceramics. The results show that the addition of soapstone in a ratio over 20% in the ceramic mass has enhanced the bending resistance of the ceramic samples when they were fired at temperatures of 900°C or 1000°C.

Oct 30, 2017

By Karl K. Bagger, Felipe Bertelli

The competitive scenario of steel industry requires studies and developments to improve manufacturing processes focusing on increasing productivity and reducing costs. The practice of coating rolls for cold rolling with the chrome aims to increase the rolling campaign, reducing their wear by increasing the surface hardness, which guarantees a greater homogeneity in the surface of the rolled products. The present paper presents a study on the effect of the chromium coat on a forged steel rolls on the wettability of a SkinPass solution. The hardness of the coated layer and the contact angle were measured for two concentrations of solution on two types of surfaces, comparing the coated and uncoated surfaces. The results show that there is an influence of the coating on the wettability of the fluid when comparison are made with chrome coated and uncoated materials, being verified through tests in Goniometer. The productivity of the coated rolls showed higher productivity than the uncoated ones.

Oct 1, 2019

By Marcelo Souza de Oliveira

Os cilindros de laminação, em conjunto com outras variáveis de processo, exercem influência direta no resultado de qualidade do produto e produtividade da linha de laminação. No caso do Novo Laminador de Acabamento da Usiminas-Cubatão, a especificação original de projeto definiu para utilização, cilindro de trabalho em material aço forjado. No entanto como havia dúvidas sobre a adequação deste material para esta aplicação específica, foi viabilizado teste de cilindro de material ferro fundido. O objetivo deste trabalho é comparar o desempenho entre os dois tipos de cilindros e a influência no resultado de produtividade da linha de laminação do Novo Laminador de Acabamento da Usiminas-Cubatão. Foi considerada a garantia da qualidade do produto final durante os testes feitos com este tipo de material do cilindro.

Jul 30, 2018

By Luiz Alberto dos Santos

. In this work, samples of the alloy with composition of 50.9 % at. Ni were machined and were subjected to hot tensile test, after the machining all the samples were solubilized so that all were in the same condition during the hot tensile test. The hot tensile tests were performed between the temperatures 350-650°C and the yield stress were between 800 and 597.1 MPa and area reduction between 17 and 75% with respect to the initial area. The test at 350°C shows a fragile fracture characteristic while the hot tensile test above this temperature showed a predominantly ductile fracture. The fragile fracture is evidenced by the river marks that are characteristic of this type of fracture, because in this condition does not promote much plastic deformation. The higher temperatures present ductile fracture, because present the dimples that also characterize this type of fracture. This work shows the temperature relationship in the mechanical properties, more specifically the hot tensile test, in the NiTi alloy.

Oct 30, 2017

By Neiclésio Nunes Ibiapina

No forno elétrico a arco (FEA) é realizado a fusão da carga metálica composta de sucata, gusa sólido ou líquido, fundentes e o aquecimento do banho líquido utilizando energia elétrica e química. O balanço correto dessas energias e a escolha adequada das matérias primas são fatores que determinam a otimização da eficiência energética e demais ganhos advindos. Para melhoria desses fatores foi utilizada a metodologia Delineamento de Experimentos (DOE) que permite estudar as variáveis do processo e a complexidade de suas interações, buscando solucionar problemas e melhorar a desempenho através de análises estatísticas. Este trabalho mostra os experimentos realizados no FEA da Sinobras objetivando otimizar a energia química do FEA para diferentes condições de carga. O resultado alcançado foi a redução no consumo de energia elétrica, no consumo de oxigênio, no power on e aumento da produção.

Jul 30, 2018

By Vera Lúcia Othéro de Brito

Literature has shown that spinel Co-Mn ferrite have potential application in magneto-mechanical sensors, due to its relatively high magnetoelastic sensitivity. In this work, Co-Mn ferrite was processed by means of the ceramic method, using Fe2O3, MnO and Co3O4 as raw materials. Samples were liquid-phase sintered, using Bi2O3 additive as liquid-phase former. X-ray fluorescence analysis was carried out in the raw materials in order to evaluate their impurity content. Atomic absorption spectrometry analysis was used for quantifying the Co/Mn/Fe proportion in the ferrite. The microstructure of the sintered sample was analyzed by means of Scanning Electron Microscopy. The magnetization and magnetostrictive behavior of the ferrite were evaluated, obtaining curves for magnetic hysteresis, magnetostriction and magnetoelastic sensitivity. The impurity inclusions and the Bi-rich particles formed from the liquid phase were characterized. The sintered ferrite had a total magnetostriction of -126ppm, which is lower than the values reported in literature for a Co-Mn ferrite of similar composition. It was verified that sintering was carried out within a critical temperature range, in which the decomposition of Mn ferrites may occur when sintering in air. This decomposition affects the magnetic properties of the material, and it may be avoided by using controlled sintering atmospheres.

Aug 8, 2018

By Bruna Brito Freitas

O lingotamento contínuo de tarugos é um processo extremamente complexo dependente de uma série de variáveis. Todas essas influenciam diretamente na qualidade do aço lingotado e na produtividade, quase sempre de maneira conflituosa. Para compreender o efeito dos parâmetros de processo, é necessário conhecê-los melhor e avaliar sua influência naquilo que é a base do lingotamento contínuo: a transferência de calor na interface metal/molde. Neste estudo foram levantados dados de temperatura durante o lingotamento de diversas corridas de aços em uma planta de aços longos especiais. As medidas de temperatura das paredes do molde da máquina LC foram obtidas, utilizando-se termopares estrategicamente posicionados ao longo do comprimento do molde e nas suas faces. Através da obtenção dos valores de temperatura desses termopares e do levantamento dos dados de processo de cada corrida monitorada, foi possível correlacionar o efeito da composição química com a transferência de calor na interface metal/molde. Por fim, os resultados mostram que aumentando o carbono equivalente observa-se um aumento na transferência de calor.

Aug 7, 2018

By Michael McDonald

The cold-rolled steel output of cold-rolling mill (CRM) complexes are sometimes constrained by their batch annealing facilities (BAF). This paper examines a cost-effective solution to increasing capacity and quality of the BAF thereby making additional capacity available for CRM output. The solution involves applying a structured system of scheduling and operation to the BAF, using a proven level-2 software model. The system presented has been applied to a wide variety of BAF with all the leading furnace brands. Whether using traditional HN atmosphere or 100% hydrogen, peak performance can be achieved when using a properly configured, on-line, physical thermodynamic model. Given that it is not practical to place a thermocouple in each coil that is being annealed, various methods have historically been used to estimate the time required to properly anneal all the coils in the charge. This paper examines how the latest technology, in wide use throughout the USA, uses a physical thermodynamic model to shorten average cycle times, thereby increasing productivity and reducing energy consumption. The paper also examines the benefit of building thermodynamically balanced charges to further optimize the BAF operation and improve quality consistency by decreasing mechanical property variations.

Jul 30, 2018

By Edgard de Macedo Silva

Aços inoxidáveis duplex apresentam boas propriedades mecânicas e de resistência à corrosão, mas quando são colocados para trabalhar em altas temperaturas como no processo de soldagem e de tratamento térmico ocorre o surgimento de fases que comprometem as suas propriedades. Dentre elas, a fase sigma (s) é a que apresenta um maior efeito de fragilização por ser rica em cromo e empobrecer a matriz desse elemento, bem como por apresentar dureza em torno de 1000HV. No presente trabalho, uma metodologia não destrutiva, baseada na interação entre densidade de linhas de campo e um aço inoxidável duplex, é apresentada para o acompanhamento da formação da fase s na temperatura de 800°C em um aço envelhecido por até 2 horas. Diferentes intensidades de campo foram geradas por um eletroímã e o fluxo de linhas de campo foi aplicado no material de estudo. A densidade de linhas de campo resultante foi medida por um sensor de efeito Hall. Os resultados foram correlacionados com resultados de microscopia eletrônica de varredura (MEV), dureza e difração de raios-X (DRX) e mostraram que os valores de tensão hall reduziram à medida que a fração volumétrica da fase s aumentou. A formação dessa fase não magnética influenciou no sinal obtido pelo sensor Hall. Existiu uma correlação entre a densidade de linhas de campo resultante e a presença da fase fragilizante, apontando para uma metodologia capaz de acompanhar a formação dessa fase.

Aug 8, 2018

By Wen Xuan

Oolitic iron ores have significant economical importance because of their extensive resources in the world. However, their utilisation is often quite limited due to the high content of phosphorus inside. The phosphorus is often finely disseminated in the oolite structure and generally not liberated in the form of free particles. The iron ore used in this work is a typical oolitic goethitic iron ore with high phosphorus. The process of phosphorus removal from this ore is difficult because the phosphorus is not present as distinct minerals. As a result, no physical beneficiation process is able to separate the phosphorus from the iron bearing phases. The current concentrate contains low iron grade (Fe ~49%) and high phosphorus content (P 0.7~0.8%). The acid leaching is a potential way to dissolve phosphorus. Previous studies have shown that the thermal treatment makes the phosphorus more accessible for the acids and enables more efficient phosphorus dissolution. Some chemical additives are reported to enhance this phenomenon. A series of tests have been carried out using roasting - grinding - magnetic separation - leaching technologies to remove the phosphorus from this current concentrate. In the first stage, several tests were performed at pilot scale under the same conditions as described in some publications. The achieved results were similar to those from previous tests at laboratory scale. In the second stage, new test conditions were investigated in laboratory scale in order to achieve better result and to reduce the operational cost.

Aug 1, 2018

By Gabriela Moreira Lana

A radiação solar apresenta uma enorme variedade de aplicações de engenharia, dentre elas, a conversão em energia térmica em concentradores solares. Os tubos absorvedores dos concentradores solares podem ser recobertos por cromo negro, com o objetivo de otimizar a absorção energética e a durabilidade. Esse trabalho é parte de um estudo complexo sobre esse tipo de recobrimento. Foram desenvolvidos filmes de cromo negro por eletrodeposição sobre aço inoxidável AISI 304 e tratados termicamente a 600°C por 2 horas. Os filmes foram caracterizados antes e depois do tratamento térmico, utilizando-se microscopia eletrônica de varredura (MEV), espectroscopia de energia dispersiva (EDS) e difração de raios X a baixo ângulo de incidência (GAXRD). Além do cromo, observou-se deposição de cobalto e elementos residuais do banho eletrolítico. O estudo da estrutura cristalina mostrou formação de óxidos após tratamento térmico. Microestruturalmente, foram observados filmes com estrutura lamelar ou nodular. O estudo permitiu sugerir modificações do banho eletrolítico, do substrato e métodos adicionais de caracterização.

Aug 17, 2017

By Patrícia Mundim Campos Faria

The process of particle size reduction by grinding is inherently inefficient and involves high capital and operating costs. In particular, ball milling is one of the important unit operations in the iron ore pelletizing process. The mill product, due to its physical properties, determines the efficiency of subsequent stages of classification, filtration and pelletizing, thus impacting the quality of iron ore pellets. The work demonstrates the application of the population balance model in the optimization of a full-scale ball mil circuit grinding pellet fines with the aim to evaluate the optimal solids concentration to improve iron ore pellet quality. Initially, detailed experimentation was carried out in a 25.4 cm diameter batch mill and a relationship for mill scale-up using a linear population balance model in wet grinding systems was established. The selection and breakage parameters and the specific selection functions were determined for pellet feed iron ore. It was possible to identify the non-normalizable nature of the breakage functions of the ore studied, which were modeled properly. Afterwards, as a result of incorporating the specific selection functions and breakage functions into the linear population balance model, it was possible to predict product size distributions in the pilot and plant scale mills (0.416 and 5.18 m diameter, respectively) from data obtained in the 25.4 cm diameter mill. Finally, with this scale-up procedure it was possible to appraise the plant scale optimization via laboratory scale grinding mill tests. The effects of changing percent solids were assessed in order to improve the industrial mill performance and the optimal value should be in the range from 76 to 80%.

Aug 1, 2018

By Talita Julha Pereira de Andrade

O Steel Frame é um sistema construtivo eficiente e sustentável. Sua estrutura é em perfis de aço e pode suportar até 4 pavimentos, e sua fundação é em radie. Por isso, os perfis da base são revestidos de manta asfáltica para serem protegidos de agentes degradantes. Após algum tempo, a manta perde sua eficácia, expondo o perfil ao meio. O objetivo dessa pesquisa é explicar a corrosão do perfil, através da investigação por MEV, EDS e teste de tração, mostrando a influência do concreto no mesmo, mediante a determinação de suas características mecânicas após o contato. Os resultados mostram difusão dos elementos do concreto no aço, afetando suas propriedades mecânicas através do aumento de limite de resistencia a tração e redução do módulo de elasticidade. Houve também redução na superfície de zinco, mostrando principio de corrosão.

Oct 30, 2017

By Antonio Adel dos Santos

Em agosto/2014 foi introduzido o gás natural, GN, na matriz de combustíveis dos fornos de reaquecimento de placas da Linha de Tiras a Quente, em Ipatinga, eliminando o óleo combustível deste processo. Isto demandou o ajuste dos parâmetros do modelo matemático de controle automático do reaquecimento, que estava ajustado para a queima de mistura de gases siderúrgicos e óleo combustível. O ajuste foi realizado com base em resultados de experiências de medição das curvas de aquecimento com placas especialmente instrumentadas. Verificou-se que os gases da combustão na presença do GN ficam mais quentes na região do início do forno, próximo do canal de fumaça, elevando com isso o perfil térmico do forno. Em consequência, as temperaturas de desenfornamento da placa ficam mais elevadas em relação ao aquecimento na ausência do GN, comparando-se condições de processo e de material similares. Os ajustes do modelo foram implantados dentro do escopo de uma melhoria geral introduzida no sistema de controle automático dos Fornos, permitindo a determinação correta da temperatura de desenfornamento e a operação otimizada dos fornos do ponto de vista de aquecimento da placa.

Aug 16, 2017

By Michelle Cardinale Souza Silva Macedo

Neste trabalho, o comportamento eletroquímico das ligas Ti-35Nb-xTa (x = 0; 2,5; 5,0; 7,5)Ta (% em peso), solubilizadas e resfriadas em água, foi investigado em meio de NaCl a 0,9% mol/L através de testes de polarização anódica e medidas de impedância, micrografias e DRX. Os ensaios eletroquímicos mostraram que as ligas contendo tântalo apresentam uma maior resistência à corrosão que a liga sem tântalo. Além disso, os ensaios eletroquímicos em conjunto com as micrografias e DRX indicam que a composição Ti-35Nb-5Ta é a que apresenta maior resistência à corrosão no meio estudado, pois além de ocorrer uma estabilização da fase ?, o refino do grão foi menos pronunciado e por esse motivo minimizou o surgimento de microcélulas eletroquímicas.

Aug 16, 2017

By Noan Tonini SImonassi

As fibras naturais extraídas das folhas do curauá estão entre as mais fortes fibras naturais utilizadas como reforço de compósitos poliméricos para aplicações em engenharia. Tais compósitos, até agora, são limitados em relação às propriedades mecânicas e energia de impacto. Assim o objetivo do presente trabalho é de investigar a possibilidade da melhora da resistência à tração bem como a energia de impacto dos compósitos de matriz poliéster reforçados com fibras de curauá com variados parâmetros de processamento. Os parâmetros observados foram a quantidade de fibras com diâmetro fino e pressão aplicada durante o processamento. Utilizando 60% de fração volumétrica de fibras finas (diâmetro médio variando de 50 à 80 µm) contínuas e alinhadas foi possível se obter resistência à tração superior 200 MPa. Ainda, aplicando-se 30 MPa de pressão durante a cura foram obtidos mais de 270 MPa de resistência a tração. Já para resistência a impacto Izod, uma resistência de 340 J/m foi obtido pelos corpos de prova com entalhe feito em sentido perpendicular ao alinhamento das fibras.

Oct 30, 2017

By Rodolfo da Silva Teixeira

As ligas de NiTi ricas em Ni tendem a exibir o efeito superelástico a temperatura ambiente. As amostras em estudo foram submetidas a tratamento térmico e mecânico a fim de avaliar o comportamento superelástico destas. Foram realizados ensaios a temperatura ambiente difração de Raios-X (DRX) para identificar as fases presentes e avaliaram-se as propriedades mecânicas via ensaios de ultramicrodureza instrumentada com pré-ciclagem térmica (aquecimento e resfriamento). Os resultados de ultramicrodureza instrumentada exibiram bons indicativos quanto ao uso prévio desta ferramenta para análises do comportamento superelástico destas ligas.

Oct 30, 2017

By Luís Marcelo Marques Tavares

Pelotas de minério de ferro representam uma parcela significativa do mercado transoceânico de minério de ferro, contando com uma participação importante de empresas brasileiras. Pelotas concorrem favoravelmente com granulados e sínteres de minério de ferro na carga metálica de fornos, em particular devido à sua elevada resistência à degradação durante o manuseio e transporte. Entretanto, pelotas ainda sofrem desse problema, que resulta na geração de finos, removidos previamente à alimentação do forno, ou de cacos, que podem resultar no aparecimento de clusters em fornos de redução direta. Esses efeitos danosos da degradação podem ser minimizados caso uma metodologia adequada de caracterização de pelotas e de simulação do processo de manuseio se encontrasse disponível. O presente trabalho trata do desenvolvimento de metodologia inédita e inovadora para previsão de resultados de degradação de pelotas, desde a usina pelotizadora até o pátio ou forno do cliente, desenvolvido como parte da parceria entre o Laboratório de Tecnologia Mineral da COPPE/UFRJ e a Samarco Mineração. O trabalho mostra ainda uma validação preliminar a partir de um ensaio de quedas múltiplas em laboratório, mostrando ótima aderência. Um simulador do processo foi desenvolvido, o qual permite inserir as características das pelotas produzidas, bem como o fluxograma de manuseio, permitindo prever a intensidade da degradação.

Aug 16, 2017