By Shuo Wang, Yu Wang, Bing Xie, Rui Tang, Hong-Yi Li, Kun Wen

"During present converter vanadium extraction process, phosphorus could not be removed from hot metal due to absence of CaO in slag though it is an efficient way for vanadium extraction. In order to improve the phosphorus remove and produce CaO-containing vanadium slag, which could be directly used in subsequent roasting process, during the converter vanadium extraction process, lime dissolution in FeOx-Si02-V203-Ti02 slag was investigated by using a rotating cylinder technique and the slag-lime interface was characterized by SEM/EDS. Results showed that changes in the slag chemistry and phase compositions during the lime dissolution process were similar to that in CaO-Si02-FeOx based slag during the BOF process. The V and Ti in the slag were expected to diffuse into the lattice of2CaO·Si02 solid solution, which formed a rather thinner layer in thickness at the slag-lime interface than that in BOF process, leading to improvement of lime dissolution in the slag.IntroductionVanadium is important material that widely applied in industries. The traditional technique to extract vanadium was to leach vanadium after sodium salt roasting. However, the sodium salt roasting process has several problems including lower yielding rate[!] and environmental pollution[2]. Therefore, the more environment-friendly technique of calcium roasting[3-4] was proposed. In order to increase roasting efficiency of vanadium slag, it is essential to study the dissolution/reaction mechanism between lime and vanadium slag. Many investigations about the dissolution reaction of lime in molten slag have been carried out from the standpoints of rapid slagging to De-Pin steelmaking process[5-6]. However, their studies were focused on BOF slag and the reaction mechanism between solid lime and slag containing vanadium has not been reported yet. In present work, the dissolution process was studied with rotating cylinder technique and the reaction interfaces were observed and analyzed by SEM/EDS to elucidate the dissolution mechanism of lime in vanadium slag. This work was supported by National Natural Science Foundation of China No. 51090382."

Jan 1, 2013

By Haldun Kurama, Cenk Karakurt, Ilker Bekir Topçu

"The usage of binders or pozzolanic materials in the production of concrete is not new. However, in recent years, the use of the pozzolanic siliceous material such as natural zeolite and coal combustion ash (CBA) has received re-attention due to the generated considerable interest in the economical use of both naturally occurring raw materials, recycling of the waste material and saved energy. In this study, the potential and utilization opportunities of natural zeolites and bottom ash (BA) in concrete applications were reviewed. Case studies, conducted to determine the possible usage of the natural zeolite and BA in concrete production, i.e. light weight concrete (LWC) were also presented. The physical and mechanical properties of cured concretes were examined to find out the competitive material usage on the final product properties. Autoclaved aerated concrete (AAC) with 1.1 nm tobermorite (5CaO 6SiO2 5H2O) as binder is a lightweight construction material that mainly uses in place of concrete to manufacture various building materials, including blocks, panels, slabs and the like. The material is a mixture of sand, lime, cement, gypsum, water and an expanding agent, which causes the raw material to rise like bread dough, with countless small air pores. AAC can be molded and cut into precisely dimensioned units and cured in an autoclave, which steam cures the concrete under pressure. During this process, the ingredients combine to form the calcium silicate hydrate gels that establish the special properties of the finished product. The process produces a material that is only one-fourth to one-third the weight of a conventional concrete block (bulk density of 400-800 kg /m3) of the same size. Regular AAC offers considerable advantages over other construction materials such as high thermal and sound insulation, excellent fire resistance, high resource and energy efficiency, low environmental impact, and finally outstanding structural performance (especially for earthquake zones) [1]. Its lightweight also makes it easy to use during construction, and its aerated structure gives it better thermal insulation and sound absorption properties than conventional concrete."

Jan 1, 2008

By Ruth Marlene Campomanes Santana, Michel Tieccher, Marcondes Mafacioli Pacheco, Juliano Urach

"IntroductionThe gaseous emissions of fuel burning by mobile sources are responsible for incidence and increase of many lung and cardiovascular diseases (Braga et al., 2007). These implications can watch in morbity as much as mortality, even when the levels of pollution are considerate restrained or lower. (Leite et al., 2002).Sample of mobile sources exhausts contain not only particles directly shaped by burning, but also secondary particles that results of reaction between other compounds (Burtscher, 2004).One of the principal pollutants produced by combustion process with major toxicity and raiser of adverse effects to health is the particulate material. In its constitution there are fine and ultrafine particles that can to extend deep portion of breath system, break epithelial barrier and reach the interstitial of lungs and then, to unleash inflammatory process (Arbex, 2004).The Particulate Material is employed to define a mixture of solid particles and liquid drops suspense in atmosphere. Queiroz et al. (2007) declare that this material can be divided in two types separated by size interval that together, represent the major class of disperse particles: the fine particles type of 2,5 µm de (breath particulate) and the type of earthliness particles, major than 2,5 µm to 10 µm (inhale particle). The difference of size between the particles influences on the physics and chemistry properties. They affirm that exist correlation between size of particle and heavy metals; how many lower was the dimension of particulate materials, major is the concentration of heavy metals.The inhale particulate (MP10) that is object of present study can exhibit in your composition sulfates, nitrates, amoniacal, marine salt (NaCl), soil elements (Al, Ca, Fe, Si, Ti), metals (Cd, Cr, Cu, Ni, Pb, V, Zn) and water (Queiroz et al., 2007).Recent studies have exhibit strong relation between daily levels of particulate material inhale (MP10) with diameter until 10 µm and others pollutants and one infinity of effects to health that go since total mortality of population, sicken for specific causes until congenital bad formation or even difficult win weight by the fern during gestation (Gouveia et al., 2006)."

Jan 1, 2008

By Alhondra de los Santos, Jesús L. Valenzuela, Jose R. Parga

"The present study evaluated the feasibility of using iron species generated by electrocoagulation (EC) as an adsorbent for removal As(III/As(V) from aqueous media. The full potential of EC was evident in that more than 99 percent of arsenic was removed without addition of chemical reagents. The adsorbent iron-species generated by EC was characterized by Chemical Analyses, X-Ray Diffraction and Scanning Electron Microscopy. The experimental data were correlated by employing a Langmuir adsorption isotherm. Thermodynamic parameters such as ?H o , ?S o and ?Go were calculated. The adsorption process was found to be exothermic and spontaneous.1. IntroductionArsenic contamination in potable water supplies is a serious health problem in many countries around the world. Groundwater arsenic contamination in La Comarca Lagunera Mexico was first reported 30 years ago [1]. Arsenic concentration has been found in well water from several communities ranging from 0.25 to 1.0 ppm. The elevated concentration of arsenic in water, above that originating from natural sources, has been attributed to the use of organoarsenical pesticides in the cotton fields and also to the millions of tons of waste slag generated at a local lead smelter [1]. The main arsenic species present in natural waters are arsenate ions 3- 4 AsO (oxidation state V) and arsenic ions H3AsO3, - 2 3 H AsO and 2- 3 HAsO oxidation state III). However, As(V) ions are most prevalent in oxygenated water while As(III) is found for anaerobic conditions, such as in well water or in groundwater. Conventional methods of arsenic removal rely on chemical-based treatment with lime, alum coagulation, iron coagulation and chemical oxidation. Other processes used with varying degrees of success include adsorption onto activated carbon, reverse osmosis, nanofiltration, manganese dioxide, magnetite and ionexchange resins [1-3]. These conventional processes generate a considerable quantity of secondary hazardous waste such as solid sludge, which also pose serious environmental problems. These drawbacks have forced various industries to search for effective, alternative treatment technologies for arsenic with a preference for electrochemical methods."

Jan 1, 2008

By Djalma Souza, Rubén Sánchez, Regina Maria Pinheiro, Carlos Maurício Fontes Vieira, Sergio Neves Monteiro

"This work has for objectives to characterize a waste generated in the form of sludge during the treatment of the effluent of a paper making industry and to evaluate the effect of its incorporation up to 10 wt.% on the properties of a clayey body used for brick production. For the characterization of the waste the following techniques were used: X-ray diffraction, X-ray fluorescence, differential thermal analysis and termogravimetric analysis with mass spectrometry. Specimens were prepared by uniaxial pressing at 20 MPa before firing at 750 °C. The physical and mechanical properties evaluated were: linear shrinkage, water absorption and flexural rupture strength. The results showed that, in agreement with the characteristics of the waste, its recycling into red ceramic can contribute to decrease the consumption of fuel during the firing stage. However, the waste changes the physical and mechanical properties, generating a deleterious effect on the water absorption and flexural rupture strength of the ceramic.IntroductionAccording to the Brazilian Association of Pulp and Paper, in the last 10 years, the global production of paper grew 35%. Brazil produced 8,2 million tons of paper in 2004 and held the position of the seventh largest world manufacturer of pulp, with about 9,4 million tons per year [1]. The pulp and paper industry generates effluents that present problems related to their disposal, even after the treatment. Among the solid wastes generated by this industry, the main waste is the primary sludge from the effluent treatment plant (ETP).After the initial treatment the decanted solids go through a dewatering stage, generating the solid form denominated primary sludge. This sludge resembles a paper paste of dark gray color when humid, and clear gray color when dry. This primary waste is composed basically of kaolin, pulp, traces of chemical substances and water. This waste generated in the pulp and paper industry depends on the characteristics of the process and of the employed techniques. It can vary significantly from one industrial unit to another, even in the case that the final products are similar. Its composition is approximately 60% of kaolin and 40% of pulp, and these percentages can vary in some moments as a function of the process [2,3]."

Jan 1, 2008

By H. Kamarudin

The behaviour of cassiterite-sulphosuccinamate flotation system was examined in the light of zeta potentials measured by micro-electrophoresis method. It was observed that sulphosuccinamate substantially affects the zeta potentials of cassiterite, lowering its i.e.p. to pH 2.5 and indicating a specific adsorption and/or chemical interaction. The optimum concentration for flotation, as seen in micro-flotation tests, was found to be associated with the most effective lowering of the zeta potentials, the optimum pH being 3.0. The effect of cations in the pulp was examined for the presence of ferrous, ferric, aluminium and lead ions. The ions ferric and aluminium were observed to create an intense effect of increasing the potentials to positive side, possibly due to adsorption of cation hydroxy complexes, as indicated by their respective species distribution diagrams.

Jan 1, 1994

By J. E. Dutrizac

Mineralogical studies were carried out on nodulated copper cathodes from three primary refineries to characterize the nodular growths and to elucidate the causes of the nodulation. Nodulation is often initiated at the surface of the starter sheet or the stainless steel plating blank, although a layer of smooth copper sometimes is deposited before nodulation commences. In some instances, the "roots" of the nodules exhibit a pronounced dendritic texture that is associated with an abundance of cavities. Slimes particles are not usually associated with these growth features which lead to a globular surface deposit. The globules sometimes develop into larger nodules, and this type of nodulation is likely caused by improper addition agent concentrations. The nodules on most cathodes, however, exhibit "roots" at the contact with the substrate that are associated with microcavities and large clusters (>40 µm) of slimes particles. The slimes constituents are commonly Ag powder, PbSO4 and Cu2(Se,Te) but not AgCu(Se,Te) or Ag,(Se,Te). The size of the slimes clusters, rather than their composition, appears to be the important factor causing the copper to grow into nodules. Tiny individual slimes particles themselves do not appear to cause cathode nodulation.

Jan 1, 1999

By Fumito Tanaka

The Converting Furnace (C-furnace) of the Mitsubishi process has solely provided opportunities for producing blister copper continuously from molten matte. Continuous converting originates from the proven technology for controlling the behavior of magnetite in lime-ferrite slag of the CaO-FeOX-Cu2O system. Recent improvements in the C-furnace operation have included the slag controls reflecting the impact of minor oxides on magnetite behavior. Although previous investigations focused on magnetite behavior, sulfur has also affected the C-furnace operation because it is of practical importance to avoid the precipitation of gypsum from lime-ferrite slag and the separation of matte from blister copper. This paper will quantify the behavior of sulfur in C-furnace with respect to the gypsum formation and matte separation, and discuss better controls for C-furnace operation.

Jan 1, 2006

By Jens Kristen Laursen

In 1999, Molymex S.A. de C.V. (Molymex), Mexico. (a company wholly owned by Molibdenos y Metales S.A. (Molymet), Chile) decided to install the Haldor Topsrae Wet gas Sulphuric Aicd (WSA) process for cleaning of the 4-5% SO2 off-gas from their molybdenum sulphide master in Cumpas, Mexico to produce sulphuric acid. The decision to install a WSA plant was based on the successful operation of a WSA plant at Molymet's molybdenum sulphide roaster in Santiago, Chile since 1993. This paper describes the process layout of the Cumpas plant, the operating experience of the Santiago plant, and the, differences in. process design between the two plants. It will furthermore summarise the applications of the WSA process for other roasting plants and smelters within the non-ferrous. metals industry producing metals such as copper, lead, and molybdenum.

Jan 1, 2002

By Catherine Williams-Beam

Thallium is more toxic to humans than mercury, cadmium, lead, copper or zinc. Its chemical behavior resembles the alkali metals (K, Rb, Cs). It occurs almost exclusively in natural waters the monovalent thallous cation. The solubilities of thallous compounds are relatively high so that monovalent thallium is readily transported through aqueous routes into the environment. The major sources of thallium are the base metal sulfides and precious metal bearing sulfides. Therefore, it is often present as a contaminant constituent in waters emanating from heavy metal sulfide bearing deposits. Thallium can be effectively removed from wastewater to <2 µg/L by reductive precipitation of thallium sulfide. Effective thallium sulfide precipitation requires a controlled solution potential/pH combination. The required potential can be effectively achieved by utilizing a particulate iron slurry or packed column environment. Experimental results will be presented and discussed.

Jan 1, 2003

By Ricardo Ponce

In recent years, ENAMI implemented modernisation plans at its two smelters in order to meet the government&apos;s environmental regulations introduced in the early 1990s. The modernisation plans defined the new SO2 and particulates emission targets, deadlines for compliance, and the revised treatment capacities of the smelters. At Las Ventanas smelter, the principal process change consisted of eliminating the reverberatory furnace. All the smelter feed is currently processed in a 4m diameter, 14m long Teniente Converter, using up to 34% oxygen enriched air. Dry concentrate is injected into the bath through tuyeres. A fuel oil burner compensates for any process heat deficiency. The Teniente Converter high copper content slag is cleaned in an electric furnace. This furnace is also used to melt internal reverts. This paper will discuss the successful operation of the slag cleaning electric furnace.

Jan 1, 1999

By S. Ikenobu

This paper describes a method for processing high-silicate zinc concentrates by hydrometallurgical zinc refining. Silica in concentrates reacts to form zinc silicate during roasting. The zinc silicate readily dissolves and slowly precipitates in sulfuric acid solutions during leaching. However, if proper operating parameters are not maintained, the colloidal silica may form an unfilterable gel. That is, according to the investigation results obtained, the silica concentration in the reactor has to be maintained at 5 g/1 or less (preferably 2 g/1 or less) by promoting the precipitation reaction. The proposed method has made it possible to precipitate silica in a form having excellent solid-liquid separation characteristics, without the need for facilities having a high filtration capacity, and to maintain a low silica concentration in the reactor by feeding a composition containing pre-adjusted silica contents.

Jan 1, 2000

By S. Suda

Hydrogen storage materials have been investigated for more than 30 years, particularly on metal hydrides. These materials are, however, considered today impractical because of their poor hydrogen capacity measured by mass density and their poor surface properties and characteristics against impurities. Recent R&D activities have been located in new categories of materials such as complex hydrides and chemical hydrides. Among these materials, NaAlH4 (one of alanates), Li-based complex hydride, and NaBH4 (SBH: sodium borohydride) are 3 major candidates as hydrogen storage materials. In the presentation, SBH as a non-reversible on-site but recyclable off-site is described in view of its practical availability as the source of H- (protide) applied for a new type of fuel cell named Direct Borohydride Fuel Cell (DBFC) and H2 (hydrogen) for Proton Exchange Membrane Fuel Cell (PEMFC).

Jan 1, 2006

By Banqiu Wu, Ramana G. Reddy, Robin D. Rogers

Experimental studies on aluminum recycling via electrolysis in ionic liquids were carried out at the temperature of 105°C. Impure aluminum was dissolved at the anode and pure aluminum was deposited on a copper cathode. The products were characterized using an optical microscope, micro-image analyzer, X-ray diffraction, emission spectrometer, and atomic absorption analyzer. The electrorefining process with a current density of 310 - 730 AJm2, and current efficiency of about 99% was obtained. Impurities such as Si, Cu, Zn, Fe, Mg, Cr, Ni, Mn and Pb were removed as anode residue. Impure aluminum was purified from 79.8wt% to 99.9wt%. At a cell voltage of 1 volt, the energy consumption of about 3 kWh/kg-Al was obtained. The process has advantages of low energy consumption and low pollutant emissions, compared with the current industrial refining process.

Jan 1, 2000

By Jesús L. Valenzuela

The solvent extraction for gold from alkaline cyanide solutions has been investigated using LIX 79 guanidine-based extractant. Different variables that could affect the extraction system were evaluated: equilibrium time, aqueous pH and extractant and modifier concentrations. The extraction isotherms of the aurocyanide complex with respect to other cyanoanions were compared and the following order of selectivity Au>Ag>Cu>Zn>>Fe was observed. From the pH isotherms it was found that aurocyanide can be extracted in alkaline media and a better separation with respect to other cyanoaniones was obtained in the range of 10.5 < pH < 11.2. Better selectivity was observed when using LIX 79 and tridecanol at 10% and 5% vol, respectively. Stripping gold from loaded organic was carried out at pH>12, using NaOH and NaCN solutions.

Jan 1, 2003

By Takeshi Yoshikawa

For the sake of effective control of titanium-compound inclusions in the steel-making processes, especially for stainless steel production, the influences of alloying elements of chromium, nickel, manganese, molybdenum, copper and oxygen on the thermodynamic property of titanium in molten iron were investigated at 1873K. At a certain titanium potential controlled by the coexistence of Ti3O5 and Ti2O3 doubly saturation of steels, the interaction parameters between alloying elements and titanium in molten iron were determined as follows. [ ] From the investigations on the equilibrium of titanium deoxidation in molten iron, the activity coefficient of titanium and the first order interaction parameter between oxygen and titanium were determined as follows. [ ] Also, deoxidation equilibrium for titanium in molten 304 stainless steel was measured and compared with the calculated results using the determined interaction parameters.

Jan 1, 2006

By R. J. Chesher, J. C. Anzalone, T. F. Krusmark

The BHP Copper Refinery at San Manuel, AZ employs conventional electro-refining technology, plating at a current density of 335 A/m2 on six kilogram copper starter sheets. In 1995, a combination of variable anode chemistries and increasing current density in the tankhouse created periods of increased bismuth in cathode. Bismuth in electrolyte was minimized by bleeding electrolyte to the nearby BHP leaching facility. However, the expected drop in cathode bismuth was not achieved. Investigations indicated that starter sheets contained a significant concentration of bismuth. The bismuth was found to occur in combination with antimony on the surface of the sheet adjacent to the mother blank. Studies were conducted to determine the mechanism by which Group VB elements are incorporated into the starte sheets. Operational practices were introduced to minimize bismuth in starter sheets and improve cathode quality.

Jan 1, 1997

By W. G. Davenport

The paper "Copper Smelting to the Year 2000" was presented at the CIM Conference of Metallurgists in Sudbury, August 1979. That paper predicted, in part, that high matte grade, high oxygen smelting - particularly in flash furnaces - would dominate copper smelting until the beginning of the next millennium. The present paper re-evaluates that prediction and examines the changes that have occurred and will occur in copper extraction in the 1990&apos;s. Of particular interest is the question as to whether major competitors are on the horizon for flash smelting and Peirce-Smith converting. Recent results with direct-to-blister smelting, lance smelting and submerged-tuyere smelting are reviewed and their roles in future copper smelting are predicted. Requirements for H2SO4 plants which handle the off-gases from modern smelting/converting processes are also examined.

Jan 1, 1993

By Matsufumi Takaya, Yukihiro Sakamoto

"Electric field emission properties from CVD diamond fabricated using pulse-modulated microwave plasma CVD were studied. Diamond was synthesized by microwave plasma CVD apparatus equipped with a pulse-modulated microwave power supply. Pulse conditions were varied from 1 to 10 seconds for pulse periods and from 0.1 to lHz for pulse frequency either. Surface morphologies of the deposits were differed by pulse frequency and duty cycle. As a result, FE properties prepared by different pulse duty cycle were different from continuous film which synthesized using continuous microwave significantly. Highest current density was obtained from the uneven morphology diamond film prepared at 17.5% pulse duty cycle.FE properties of the CVD diamond were depended on surface morphologies that related to the pulse conditions.1. IntroductionDiamond has excellent physical and chemical properties as an industrial material. Especially, hydrogen terminated diamond had the negative electron affinity (NEA) 1) and CVD diamond has this NEA property either as deposited 2). So the electron emission source to the FED is expected as one of this application of CVD diamond as cold cathode of electric devices. We studied on FE properties of various CVD diamond, pulse microwave plasma CVD diamond showed better property than those of other CVD diamond 3).This report studied on· the effect of the duty-cycle of pulse modulate microwave condition on FE properties of the diamond fabricated by pulse modulated microwave plasma CVD."

Jan 1, 2000

By Victor Bredykhin

The report is devoted to the investigation and improvement of processes taking place at contact of large quantities of water insoluble liquid and particles of solid phase in a pulp. Theoretical analysis and simulation of acting conditions have allowed to determine that after attaching of oleophilic particles on the «water-reagent» separation surface the break of a formed complex is taking place according to the reagent volume and for oleophobic minerals along the «solid-reagent» separation surface. As a result particles are selectively treated if the magnitude of the reagent adhesion to the surface of solid phase in water is great. The results of dispersion are influenced significantly by availability of sharp edges on the surface of real particles. They keep tree phase perimeter of moistening. It is possible to fix reagent in the form of lens whose contact angle is significantly smaller in comparison to the thermodynamic angle. In adhesion dispersion the reduction of reagent volume, covering the equal area of particles surface is possible when the reagent is in a pulp in the form of thin films on the «water-gas» separation border. The process is tested in laboratory conditions as well as at pilot concentrating mills in flotation of sulfide ores, non-ferrous metals (copper-molybdenum ore), native sulfur and coal.

Jan 1, 2006