Dissolution Mechanism of Lime in FeOx-SiO2-V2O3-TiO2 Slag

"During present converter vanadium extraction process, phosphorus could not be removed from hot metal due to absence of CaO in slag though it is an efficient way for vanadium extraction. In order to improve the phosphorus remove and produce CaO-containing vanadium slag, which could be directly used in subsequent roasting process, during the converter vanadium extraction process, lime dissolution in FeOx-Si02-V203-Ti02 slag was investigated by using a rotating cylinder technique and the slag-lime interface was characterized by SEM/EDS. Results showed that changes in the slag chemistry and phase compositions during the lime dissolution process were similar to that in CaO-Si02-FeOx based slag during the BOF process. The V and Ti in the slag were expected to diffuse into the lattice of2CaO·Si02 solid solution, which formed a rather thinner layer in thickness at the slag-lime interface than that in BOF process, leading to improvement of lime dissolution in the slag.IntroductionVanadium is important material that widely applied in industries. The traditional technique to extract vanadium was to leach vanadium after sodium salt roasting. However, the sodium salt roasting process has several problems including lower yielding rate[!] and environmental pollution[2]. Therefore, the more environment-friendly technique of calcium roasting[3-4] was proposed. In order to increase roasting efficiency of vanadium slag, it is essential to study the dissolution/reaction mechanism between lime and vanadium slag. Many investigations about the dissolution reaction of lime in molten slag have been carried out from the standpoints of rapid slagging to De-Pin steelmaking process[5-6]. However, their studies were focused on BOF slag and the reaction mechanism between solid lime and slag containing vanadium has not been reported yet. In present work, the dissolution process was studied with rotating cylinder technique and the reaction interfaces were observed and analyzed by SEM/EDS to elucidate the dissolution mechanism of lime in vanadium slag. This work was supported by National Natural Science Foundation of China No. 51090382."