By Bingchen Chen, Zhitong Sui, Junwei Ma

"In the blast furnace slag, titanium disseminated in various mineral phases Titanium could be concentrated mainly in perovskite, which could be selectively precipitated and grown by optimizing the operation factors like the slag composition, temperature of heat treatment and additive agents. This study aims at establishing the titanium slag mineralogy and its distribution in the treated slag and the as-received slag, as well as the methods of perovskite separation. After heat treatment, the grain size was grown from 5 - 20µm to 80 - 200µm, the distribution of Ti02 in perovskite was increased from 48% to 81 %, the morphology was changed from snow-shaped grain to coarsening dendrites or equiaxed crystals. A concentrate were produced by gravity separation analyzing 35.25% Ti02 with a recovery of 68.28% and a tailing analyzing 9.53% Ti02 , and a possibility of flotation upgrading was discussed. I INTRODUCTION CHINA is rich in mineral resources of titanium, 92.4% of which is vanadium-titanium bearing magnetite. About 53% titanium were in iron concentrate after mineral processing, by which the blast furnace slag containing about 25% TiO2 were produced[11 • The content of TiO2 in such slag is too low to separate titanium dioxide, and it is also too high to produce slag cement[21. It has been accumulated to 50 million tons so far, which is still increasing at a rate of 3 million tons per year, and results in a waste of titanium resources and pollution of environment. Due to the dispersed distribution of titanium component in various mineral phases, very fine grain(<10µm) and complex interfacial combination, it is very difficult to recovery titanium component from the slag by traditional separating technique. In this paper, a novel technique to recovery titanium from the waste slags was proposed [3H4l, on which three continuous processes were involved: selective concentrating, selective growing and selective separating. Perovskite was designed as a titanium-rich phase, in which the most titanium was concentrated promptly, then perovskite could be selectively grown and coarsened by optimizing the heat treatment and the appropriate additives [ 5l[6l. The grain size of perovskite phase was larger than 80 µm, and the crystals appeared as coarsening dendrites or equiaxial grains like lump."

Jan 1, 2000

By S. M. Copley, M. Yankova, E. Y. Yankov, J. A. Todd

"Nanophased coupled growth structures, with spacings of -10 nm, have been observed in banded microstructures produced by laser melting hypoeutectic Ag-Cu alloys. These coupled growth structures comprised a Cu-rich phase of width - 1 nm and a Ag-rich phase of width - 9 nm. In this paper, microstructural observations of nanophased coupled growth structures in hypo eutectic AgCu alloys are presented. Laser beam velocities for the transition from banded to microsegregation free microstructures are modelled and compared with experimental values. Models are presented to show that, at a critical undercooling, initial growth of a Ag-rich, metastable, extended solid solution is rapid but slows to a halt as copper is partitioned into the liquid at the solid/liquid interface. Following nucleation, the coupled growth structure then grows until the partitioned copper is consumed, at which point growth of the Ag-rich solid solution is again accelerated. This cycle then repeats resulting in banded microstructures comprised of 750 nm of the Ag-rich extended, metastable solid solution, followed by 250 nm of the coupled growth structure.1. Structural Studies of Laser Melted and Resolidified TrailsPresented here are observations of laser melted and resolidified trails in Ag-Cu alloys obtained at beam velocities ranging from 0.7 to 34 cm S·I. When the laser beam is scanned along the surface (positive x-direction) with a velocity Vb a melt pool with the shape given in Fig. 1a moves with the beam. The isotherms move with the velocity, Vi,. = Vb cos.p. Calculations employing the thermal analysis of Kou, Hsu and Mehrabian [1] for the beam velocities of this investigation and for the thermal properties of AgCu alloys, indicated that, .p, the angle between the isotherm velocity and beam velocity should be small at the surface where microstructural studies were made. This prediction was supported by observations of trail cross-sections. Based on these observations, and the calculations which include latent heat effects, the isotherm velocity for observations near the surface in our investigation was taken to be 27 cm S-I."

Jan 1, 1994

By P. R. Taylor

Diamond films have been successfully formed in an inductively coupled plasma (ICP) chemical vapor deposition (CVD) system from several gas mixtures: CH,-H,, C2112-112, and C2112-112-02&apos; Our previous thermodynamic study indicated that the substrate temperature could be lowered by the presence of oxygen species at moderate system pressures (0.3-0.5 atm) and that higher volumetric growth rates required a high temperature source and a moderate pressure system in CVD processing. The principal experimental results were consistent with the thermodynamic predictions. The deposited films were characterized by laser Raman spectroscopy, scanning electron microscopy, and X-ray diffraction. The films were well faceted and uniform, with the growth rates over 10 pm/hr on molybdenum substrates. The crystal size ranged between 1 and 2 microns for a two hour experiment. It was possible to decrease the substrate temperature to below 800 °C in this system.

Jan 1, 1995

By Tamas Kekesi

Anion exchange in HCl media is considered an efficient alternative to the combination of the conventional purification methods. Anion-exchange distribution functions have been determined for cobalt and the main impurity elements by the technique of batch equilibration. Results were confirmed by spectrophotometric investigations and elution tests. Based on the new and the available distribution functions, combined with the assessment of thermodynamic stability, a procedure of anion exchange separation has been devised to eliminate virtually all the impurities from the cobalt-chloride solution. Separation of copper has been enhanced by the introduction of a preliminary step under reduced conditions. The rest of the impurities are eliminated in a second anion-exchange step applying rinsing and elution stages under oxidized conditions. The optimum parameters of the procedure have been determined according to performance characteristics (purification ratios, yields and volume efficiencies) derived from the analysis of elution curves obtained with laboratory scale ion-exchange columns. Special computer programs have been developed to facilitate thermodynamic simulation, analytical correction and data processing.

Jan 1, 2003

By C. Dupuis

Thiourea is a promising reagent for gold extraction especially from refractory ores that cannot be treated by traditional cyanidation route. In this study recovery of gold from thiourea leaching solutions was investigated by direct electrowinning. The electrolysis cell consisted of a carbon flow-through cathode and a lead anode. The anodic and cathodic compartments were separated by a membrane. Galvanostatic mode was chosen for operation of the cell. Factors affecting recovery efficiency such as cathode thickness, linear flowrate, current intensity, thiourea and gold concentrations were investigated. The influence of some species in solution on efficiency and selectivity of recovery was investigated. Gold recovery reached 99% but current efficiency was lower than 10%. The complex formed with ferric ion and formamidine disulfide are reduced before gold-thiourea complex. Thiourea consumption occurred during leaching mainly by oxidation and reaction with dissolved copper.

Jan 1, 1989

By A. Onozaki

The Iijima Refinery was put into operation in 1972 and today has an annual production capacity of 156,000 tons of SHG electrolytic zinc. At the Iijima Refinery, the recoveries of gold and silver are 98.0% and 98.2%, respectively. Gold contained originally in the zinc concentrates reports in the Cu-Pb-Ag residue produced in the residue treatment process. Silver contained in the concentrates is distributed between the Cu-Pb~Ag residue and the copper cake produced in the purification process. The Cu-Pb-Ag residue, which contains gold and silver, is sent to the Oyachi flotatfon plant of the Kosaka Smelter; about 82% of the gold and about 85% of the silver are recovered in the copper flotation concentrate.. In this paper, the distribution of gold and silver in the Iijima. Refinery is discussed and operational results of the Oyachi flotation plant are presented.

Jan 1, 1990

By Yiling Zhang, Paul A. Salvador, Gregory S. Rohrer

"Photocatalysis utilizes solar energy to produce hydrogen by splitting H2O. When a thin film of photocatalyst TiO2 is supported on a ferroelectric BiFeO3 substrate (band gap ~2.5 eV), the TiO2/BiFeO3 heterostructure is capable of photochemically reducing Ag+ to Ag0 in aqueous solutions under blue light with enhanced efficiency. The observation of spatially selective silver patterns on surface of the heterostructure after reaction suggests that photogenerated electrons and holes in ferroelectric BiFeO3 are driven in opposite directions to reduce their chance of recombination. Comparisons of the amounts of reduced silver on TiO2 film grains with distinct phases/orientations show that the reactivity is mildly preferential on anatase TiO2 phase and does not strongly depend on crystallographic orientation of BiFeO3.IntroductionTitania (TiO2) is capable of photocatalytically converting H2O to hydrogen and oxygen under the irradiation of ultraviolet light. [1, 2] One of the limiting factors for titania to be used as an effective photocatalyst is its band gap. Because the absorption edges of rutile and anatase titania are at 3.0 eV and 3.2 eV, respectively, they can only absorb light in the UV portion of the spectrum, which is about 3% of the available solar energy. [3-5] This limitation has motivated attempts to modify the absorption edge of titania so that it can absorb visible light.One strategy is to substitute a portion of the titanium and/or the oxygen with other atoms. There are numerous reports on visible light absorption of titania by doping and co-doping of Cr, V, Mo, Sb, Fe, N, S, C, and F. [6-34] Another strategy is to add an adsorbed molecular species that absorb visible light and donate an electron or hole to the titania, such as organic dyes [33, 35, 36] and Ce3+/Ce4+. [37, 38]The strategy in the present work takes the approach of depositing a pure titania thin film on a visible light absorbing substrate BiFeO3 to induce visible light activity of the heterostructure. BiFeO3 is a semiconductor with a band gap of about 2.5 eV [39-41] and is photocatalytically active in visible light. [42, 43] It is also ferroelectric with spontaneous polarization along pseudo-cubic <111> directions of 6.1 µC cm-2. [44] The spontaneous polarization gives rise to internal electric fields that drive photogenerated charge carriers, namely electrons and holes, in opposite directions to reduce their chance of recombination. [45-47] Additionally, the separation of electrons and holes leads to the spatial separation of reduction and oxidation half reactions so that the back reaction of intermediates is also suppressed. Such charge carrier separation has been reported in TiO2/BaTiO3 heterostructures with UV light illumination. [48-51] The TiO2/BiFeO3 heterostructures in this work combine both advantages of the relatively narrow band gap and the internal fields in BiFeO3 to enhance the overall photocatalytic activity."

Jan 1, 2014

By N. L. Piret

Reprocessing of low zinc-bearing residuals with a zinc content of less than 10%, originating from the iron and steel industry, has been given more and more attention in the last few years, due to the potential landfill liability and the increasing cost of disposal by dumping. Whereas, recycling of hazardous electric arc furnace dust is already being performed commercially on a large scale in the U.S., Japan and Western Europe, almost no reprocessing takes place in the case of these low grade zinc-bearing materials. In blast furnaces and basic oxygen furnaces dusts and / or sludges are generated at a rate of 1 to 2 % of the respective production. The technologies for the retreatment of these types of materials, either commercially available or still being developed are briefly described hereafter. They involve internal recycling, upgrading by physical separation methods, separate hydrometallurgical processing and pyrometallurgical treatment. Their scope and limitations are critically assessed in terms of technological applicability, economic feasibility and environmental compatibility. Since, the possibtlity of achieving economic profitability is unlikely with this type of material, the main criteria for acceptability of the treatment process are: generation of a iron-rich material, suitable for treatment by the iron/steel industry, acceptance of the non--ferrous metal-bearing sub-product by zinc smelters, generation of non-hazardous waste materials.

Jan 1, 1992

By K:-I. Rhee

The recovery of tellurium from Te-cement obtained during the processing of copper anode slimes was carried out by a series of hydrometallurgical processes, i.e. leaching Te-cement in NaOH solution, precipitation of impurites with the addition of Na2S followed by direct electrowinning of tellurium in NaOH solution. The optimum conditions for each process were determined and discussed in terms of various parameters associated with each step to maximize the recovery and purity of tellurium. The final purity of tellurium from electrowinning in alkaline solution was found to be more than 99.9 %.

Jan 1, 1997

By F. Kongoli

Viscosity is an important parameter of copper smelting and converting processes. It affects the settling of matte or metal droplets in the slag, distribution of elements etc. Despite this importance, confusion exists on the viscosity of copper smelting slags as a result of disagreements found among the measured viscosity data of several authors especially in the slags of high ferric iron content and close to magnetite precipitation. In this work a critical review of the existing data on the viscosity of copper smelting slags has been first carried out and the effect of oxygen potential on the viscosity of copper smelting slags has been clarified through a coupled quantification of viscosity and liquidus temperature. The confusion in the literature has been clarified and the importance of the relation between the viscosity and the liquidus temperature is discussed.

Jan 1, 2003

By D. Papazoglou

This work was undertaken to investigate the thermodynamic and kinetic feasibility of using hot sulfur dioxide bearing gases from smelting processes to selectively sulfate the nickel in nickel laterite ores for subsequent extraction in water. The environmental benefits ofthis approach, as opposed to releasing the gas to the atmosphere, and the economic benefit of directly utilizing the S02 rather than converting it to sulfuric acid are strong drivers for such a process. A thermodynamic analysis indicated that selective sulfation of the nickel could be feasible under appropriate conditions and these were explored through a series of laboratory scale experiments. Laterite samples were reacted at temperatures between 500 and 800°C with an equilibrated mixture of sulfur dioxide, oxygen and nitrogen in a fixed bed reactor. Tests were conducted on saprolitic ore from Bulong, Western Australia, limonitic ore from New Caledonia and garnieritic ore from Indonesia. Nickel extractions were highest from the limonite and relatively low from the other ores. The maximum selective extraction of nickel from the limonite in a single stage sulfation was 73%. Sulfation of other elements present in the laterites was also examined. A two-stage process was also identified which involved sulfation using a strong sulfation potential followed by weaker sulfation potential to attempt to convert ferric sulfate formed in the first stage to ferric oxide. This increased the extraction for the limonite ore to around 84% Ni, 95% Co and 2% Fe. Direct sulfation of laterite could be feasible in locations where sulfide smelting or roasting operations are relatively close to laterite deposits.

Jan 1, 2003

By Masaru Tomoguchi, Tom Nishiyama, Naoto Sasamoto

"In Hanaoka Mine, which was one of the major ""black ore"" (Kuroko) mines in the north part of Japan, mining has finished in 1994, and only mineral processing plant is available now. Recently this mineral processing plant has been applied to the soil washing. Soils contaminated with heavy metals are excavated and transported to the plant. The soils are separated to cleaned soil and metal enrichment through the process which consists of scrubbing, classification, extraction, insolubilization, flotation, and so on. The process is flexibly designed for each contaminated soil, in order to the products can be recycled as cleaned soils or metal sources. . Soils contaminated with arsenic and lead were treated in 1999, which were entrusted from Environmental Agency of Japan.IntroductionDowa Mining has had the mine site named ""Hanaoka Mine"" and ""Kosaka Mine"" in the north part of Japan. Those mines consisted of some ore deposits and produced ""black ore"" (Kuroko) and ""yellow ore"" (Oko), which are complex sulfide ore. The ""black ore"" mainly consists of sphalerite, galena and barite with accessory chalcopyrite, tetrahedrite and Au, Ag minerals. The ""yellow ore"" mainly consists of powdery and clayey ore containing chalcopyrite and. pyrite, with a little sphalerite and galena. Each mine site had mineral processing plant respectively, ""Hanaoka Mine"" had two and ""Kosaka Mine"" had one plant. Those plants were operated by flotation process to separate each mineral, and produced concentrates of copper, lead, zinc, pyrite, barite and so on.Unfortunately, the mine had closed one by one because of change in economical circumstances and the lack of ore reserves. Mill plants were also closed and dismantled, but the last ""Matsumine mill plant"" of Hanaoka Mine was remained to be utilized usefully. In the circumstance like that, we came across with soil remediation business. Recent reports say that subsurface contamination in Japan is being grown substantially and that it can be a serious matter beyond the imagination of our society. So nowadays we have a tendency to pay attention to the environmental issues including subsurface one."

Jan 1, 2000

By Teruo Bitoh, Shogo Izumi

"The effect of B203 flux melting on the structure and the soft magnetic properties of the (Feo.1sBo.20Sio.os)96Nb4 bulk metallic glasses prepared by casting has been investigated. The ringshaped bulk specimens were prepared by the B203 flux melting and copper mold casting. It was confirmed that the flux melting promotes the precipitation of the a-Fe(-Si) and Fe2B phases in the central region of the specimens. The ring-shaped bulk specimens show a flat hysteresis curve, indicating a good linear relationship between the magnetic induction and the applied magnetic field. These results show that it is possible to develop a new soft magnetic material that exhibits constant permeability, which is necessary for producing inductors and choke coils.IntroductionSince the success of forming Fe-based bulk metallic glasses (BMGs) with good soft magnetic properties, great attention has been developed to synthesis and properties of the BMGs [l, 2]. The BMGs have high glass-forming ability (GFA) and, therefore, they can be used to prepare bulk amorphous alloys with a thickness of the order of a few millimeters by casting. The soft magnetic properties of Fe-based BMGs are better than those of ordinary amorphous alloys; therefore, these BMGs have wider applications as soft magnetic materials [3-5]. It is often required for soft magnetic materials that the shape of the hysteresis curve is changed according to the demands of applications. For example, materials with ""flat hysteresis curves,"" which means the magnetic flux density (B) and the applied magnetic field (H) show a linear relationship up to rather high magnetic field, are necessary for producing inductors and choke coils. Flat hysteresis curves can be easily achieved by creating an air gap in the magnetic path. However, magnetic flux leakage generated in the air gap inhibits high-density packing of the electronic components. In order to achieve flat hysteresis curves without creating an air gap, Fe-based ordinary amorphous alloys are subjected to crystallization by annealing and transformed into thin surface layers of a-Fe; the crystallization results in the compression of the remained amorphous phase [6]. Another way to achieve flat hysteresis curves is the formation of secondary phase (such as Fe2B) that act as pinning site of magnetic domain wall displacements [7]."

Jan 1, 2013

By Lin Yang, Yuanbo Zhang, Zhuoxuan Li, Guanghui Li, Jinghua Zeng, Tao Jiang

A technique has been proposed for recovering iron from hematite-rich diasporic-type bauxite ore in this study. Direct reduction roasting followed by low intensity wet magnetic separation process was carried out. The parameters including reduction temperature and time, sodium salts, grinding conditions and magnetic field intensity for separation of iron were determined. The optimum process parameters as follows: roasting temperature of 1050 oC, time of 60 min, sodium salts involving sodium sulfate, borax, sodium carbonate with dosages of 10 wt%, 2 wt%, 35 wt% respectively, and magnetic field intensity of 1000 Gs with fineness of pulp reached 92.75% passing -0.074mm. Under the optimal conditions, an iron concentrate containing 88.17% total iron grade and iron recovery of 92.51% was obtained, 4.55% total iron grade in tailings. This novel technique provide a potential route for utilizing hematiterich diasporic bauxite ore, recovering iron resource firstly, and extracting alumina from magnetic separation tailings further.

Jan 1, 2015

By Pengfu Tan

In order to understand and control the formation of dioxins and furans in iron ore sinter plants and to possibly avoid expensive end-of-pipe removal stages, thermodynamic calculations on the stability of PCDD/Fs have been combined with sinter process modeling by means of kinetic simulations and computational fluid dynamics. Three thermodynamic databases of PCDD/Fs, derived using the Group Additivity approach and two computational molecular modeling methods, MNDO and PM3, respectively, combined with the SGTE database have been used to model the PCDDIF formation and the PCDD/F isomer distributions in iron ore sintering. The results show very similar conditions for the PCDD/F formation using the different databases. Concerning the isomer distributions of toxic PCDD/Fs, the calculated data derived from the MNDO method showed optimum agreement with measured values from industrial furnaces. The thermodynamic calculations also proved that the isomer distributions found in combustion processes are equilibrium values, while the concentration ratio of PCDDs and PCDFs in the wind boxes does not represent an equilibrium state. A CFD model of iron ore sintering was developed including the kinetics of 15 relevant chemical reactions with the aim of describing the temperature fields and the gas flow patterns in the sintering bed. On the basis of these information and experimental observations reported in the literature possible pathways for the PCDD/F formation in sinter plants have been identified: PCDD/Fs are formed in the critical temperature region of 250 to 450°C below the combustion zone, are then carried downwards with the gas and condensed close to the bottom of the sinter bed. Transported to the discharge end with the solid mixture, they are again released into the gas phase when the flame front approaches the bottom. PCDD/Fs are also formed in the last wind boxes when the hot off-gases cool down and reach the critical temperature range. Consequently, methods to reduce the dioxin formation reactions are proposed including inhibitor addition to the sinter feed and off-gas quenching.

Jan 1, 2003

By Amy Nelson

In the electrolytic production of zinc, cobalt is removed from the zinc electrolyte by cementation with zinc dust prior to electrowinning. Although the thermodynamics for this reaction are favourable, kinetic barriers to cobalt reduction render the method almost useless in practice unless activators such as copper and antimony or arsenic are added. There is a large body of work studying the effect of these additives, yet the mechanism by which they act is still poorly understood. Even when the target conditions are met, zinc dust consumption is excessively high: satisfactory operation requires up to 300 times the stoichiometric amount of zinc dust. The objective of this work is three-fold: (1) to examine the effects of activators and elucidate the characteristics that make a good activator; (2) to identify new additives that could lead to a more efficient purification process; and (3) to test the new additives with synthetic and real electrolyte solutions. The present paper gives a status report on this project.

Jan 1, 1998

By Du Sichen, S. Seetharaman, A. Jakobsson

"In the Present paper, the principles of oxygen potential measurements have been discussed along with the design details for oxygen sensors that are used in copper industry. A description of some of commercial probes is presented along with their salient features. The application of these sensors in flash smelting, converter and casting sections of copper production are discussed along with their implications on process optimization.I. IntroductionThe high temperature galvanic cells have come into prominence on account of their numerous applications in both fundamental as well as applied measurements. Since the inception of the oxygen-ion conducting electrolytes like ZrOrCaO·by Kiukkola and Wagner [1], the oxygen concentration cells have been extensively used in laboratories as well as in industries. In metal-production technology, these cells have been used to monitor the oxygen potentials in metallic, slag as well as gas phases and also to control and styr metallurgical processes. The pioneer among the various industrial users of such cells is the copper industry. To-day, high temperature solid electrolyte cells involving oxygen ion conducting electrolytes have become an integral part of copper pyro-refining and continuous casting. In the present paper some of the applications according to the industrial processes are described including the developments that are going on in the European scene."

Jan 1, 1997

By Rak-lun Choi

Plasma-induced damage of InGaN/GaN multiple quantum well (MQW) light-emitting diodes (LEDs) has been studied in terms of forward turn-on and reverse breakdown voltages, together with etch rate and surface morphology. The physical degradation of sidewall along with rough surface morphology of n-GaN caused by increased ion scattering induced the deterioration of the forward and reverse voltages. It was found that the turn-on voltage is sensitive to the surface roughness of the etched n-GaN and the breakdown voltage is strongly affected by the sidewall contamination. Annealing under nitrogen after the mesa etching improved the electrical properties of the InGaN/GaN MQW LEDs. Efficient blue light-emitting diodes (LEDs) were fabricated using InGaN/GaN triangular MQWs. The LEDs with triangular QWs showed a lower operation voltage and 2.4 times higher light output power than those with the rectangular MQW LEDs at 20 mA and 20 °C. The intensity of electroluminescence (EL) at 20 mA was almost independent of ambient temperature in the triangular QW LED, but decreased substantially in the rectangular one.

Jan 1, 2003

By Armin D. Ebner

A hetero-f1occulation model is developed to calculate the net force exerted on a paramagnetic nanoparticle that is moving in the proximity of a magnetite particle that is fixed or supported within an open flow and magnetically energized packed bed. Important variables investigated include the size and surface charge of the particles, the magnetic field, the ,flow velocity, the electrolyte concentration and the magnetic susceptibility of ,the nanoparticle. The ?influence: of other naturally occurring forces, such as hydrodynamic and DLVO(Le., van der Waals and electrostatic) forces on the magnetic attractive forces between the magnetite particle and the nanoparticle are also examined. This model reveals the feasibility of using magnetite particles instead, of stainless steel as the energizable element for high gradient magnetic separation.

Jan 1, 1999

By Dolf Gielen

This paper discusses the results of a Western European energy and materials systems engineering study that analyses the impact of greenhouse gas (GHG) emission reduction on the future of the steel and aluminum industry. he technology selection will be significantly affected by future CO2 policies. The avail- ability of C02 removal and storage technology and the social acceptance of this strategy for GHG emission reduction is of key importance for the strategy selection. The use of coal based smelting reduction technologies is optimal in case of weak C02 policies or in case of strong C02 policies and low CO2 removal and storage costs. The selection of CCF or Corex technology depends on the penalty regime. However, if C02 removal proves to be problematic, CCF development fails and strong C02 policies are introduced, the gas based DRI production processes will become more attractive. In both cases, the energy efficiency of the iron and steel industry will further increase in the next decades. The impact of GHG emission reduction on aluminum prices and aluminum use can be significant. However contrary to common notions the aluminum production will be positively affected by GHG emission reduction, notwithstanding the currently high emissions in aluminum production. A combination of emission mitigation in production and significant GHG emission reduction effects further down the product chain cause this effect. A significant potential exists for improved materials efficiency. This potential is generally neglected in energy efficiency and CO2 reduction studies. However improved steel qualities are of similar importance for C02 emission reduction as increased energy efficiency. It remains to see if this potential will be used to its full extent in the next decades. Model calculations indicate that the impact of C02 policies on the competition with other materials will be limited. Greenhouse gas emission mitigation will have much more impact on materials production and waste handling than on materials consumption.

Jan 1, 1999