Jan 1, 1940

Jan 1, 1940

By E. S. Grumell

The correct sampling of coal and coke is becoming important to an ever increasing number of producers and consumers. This, therefore, may be an opportune moment to examine where we stand with regard to existing and proposed methods. In this paper an attempt will be made to review, as briefly as possible, some of the considerable amount of painstaking research which has been done in the last 10 years, and which has unquestionably led to a much better understanding of the subject. In so doing we shall try, on the one hand, to make clear where substantial progress has been made, and on the other hand, to draw attention to points that require further investigation. The paper is divided into sections in order to emphasize the major divisions of the subject; further, in order to retain this emphasis, detailed consideration of some of the points has been relegated to appendixes. No attempt has been made to give a complete survey of the literature, as this has already been done by L. A. Bushell.2 The following abbreviations will be used: A.E., average error; P.E., probable error; S.W.R., size-weight ratio; B.S.I., British Standards Institution. Section 1.—Cost It has often been stated that the cost of sampling should bear some relationship to the value of the product, and since coal is a relatively cheap raw material it would be a major error to specify, for ordinary commercial purposes, elaborate and costly methods of sampling which nobody would adopt. Specifications must be of such a nature that they will be used. We believe that one of the achievements of the last 10 years has been to reduce the cost of sampling. There is, however, another point to be considered; via., that the cost of sampling should bear some relationship to the value of the investigation. Correct sampling is a cog (possibly a small one) in the wheel

Jan 1, 1940

By Paul Weir

During the past decade, methods of producing bituminous coal in the state of Illinois, which ranks third in production among the states in which bituminous coal is mined, have undergone great changes. From less than one million tons in 1923, the strip-mine production has gradually increased to a high of 11,725,870 tons in 1937. From a negligible amount prior to 1927, the amount of coal mechanically loaded underground had increased to a high of 28,374,362 tons in 1937. The amount manually loaded in 1937 reached a low of 12,332,023 tons. In this same year, this state ranked first in strip-mine production, also in mechanically loaded production. For this reason a study of the influence of mechanization on location of production in Illinois may be helpful in anticipating what may happen in other producing states. The reason for the changes in methods lies in the differences in costs of production. The Bureau of Research and Statistics of the National Bituminous Coal Commission has made public the following costs of production by various methods in the state of Illinois (district 10) for the last nine months of 1937: all mines, $1.7602 per ton; strip mines, $1.4319; mechanical loading mines, $1.7457; hand loading mines, $2.1793; all underground mines, $1.8703. These are weighted averages for the entire district. Inasmuch as production in 1937 was reported from 58 counties scattered over two-thirds of the area of the state and from five different seams varying in thickness from less than 3 ft. to as much as 12 ft., it is apparent that the location of production must be influenced by the extent of mechanization possible in the various producing counties. SHIFT in Production The term "mechanization" is commonly used to designate the coal-loading operation. However, in a broader sense it embraces the use of any and all mechanical and electrical equipment on the surface and underground. Strip mining is an intensive form of mechanization. The mechanical cleaning of coal is a form of mechanization. Cutting machines and motor haulage likewise are forms of mechanization, hence

Jan 1, 1940

By G. Stuart Jenkins

Conditions at the properties of the Consolidated Coal Co. had reached a point where improvements were almost impractical. The mines, sunk years ago, had shafts and entries so small as to preclude the use of large mine cars. A radical change was necessary in the type of mining and also in the type of mine to accommodate such haulage units. After due consideration, the company decided to enter the field of trackless mining, utilizing belt conveyors and chain-flight conveyors, the belt conveyors to take the long haul, and the chain-flight conveyors to be used for gathering. It was decided not to sink a shaft, hut to drive a slope on an inclination of 17½°, which the company believes to be about the limit on which coal can be carried on a belt without rolling back unduly. Sinking the Slope It was decided, in sinking the slope, to make an opencut until rock was reached, which was some 65 ft. below the surface, and then to drive the slope through an inclined tunnel from that point. In making the open-cut, the schedule called for the removal of about 25,000 cu. yd. of clay, holding the banks on an inclination of one and a half to one, the thought being to make this cut in a minimum of time, put in a reinforced concrete slope, and then back-fill. Difficulty was experienced because the clay was of a sort that was called "subsiding base" material by contractors visiting the job. In other words, a "squeeze" occurred, the pressure causing the floor of the cut to move up just as it does in many mines where the coal is underlain by thick fire clay and inadequate pillars have been left. It was necessary to move the waste banks back from the edge of the cut 700 or 800 ft., and even then the floor could not be controlled, the result being that almost 100,000 cu. yd. of clay was handled before the rock was reached. A concrete slope was then rapidly constructed, using 95 tons of special-shaped reinforcing iron. The floor of this slope was made 30 in. thick at the bottom, and 17 in. thick at the top, the sidewalls being 18 in.

Jan 1, 1940

By John S. Marshall

The purpose of this paper is to present to the profession data and experience obtained over a period of 5 years in the operation of 87 shaker-conveyor units, and the production of 2,169,638 tons of run-of-mine anthracite coal. The data are not generally available and should be of interest to those concerned with the operation of anthracite and bituminous mines. To simplify comparison, a ton of 2000 lb. of raw run-of-mine coal has been used as the production unit throughout this paper. Mining Methods and Equipment The mine is in the vicinity of Wilkes-Barre, Pa., in the Buried Valley area of the Susquehanna River. Seven veins were mined, varying in thickness from 18 in. to 8 ft. The cover overlying the veins varied from 200 to 800 ft. Three-fourths of the 1200 acres of property was covered with from 100 to 200 ft. of water-bearing gravels and clays, which prevented first mining under rock cover less than 50 ft. and pillar removal under rock cover less than 100 ft. The property was opened by two shafts sunk on the mountainside to avoid the sand and gravel present in the river valley. The veins dipped an average of 5" from the shafts. In certain areas the veins were practically flat and in some places a reverse pitch as high as 5" was encountered for short distances. A daily output of 3800 tons was hoisted on a two-shifi; hoisting operation. The mining consisted of 75 per cent pillar removal, and of the total production in the later years of operation 80 per cent was loaded by shaker conveyors, chain conveyors and scraper loaders. Shaker conveyors accounted for 70 per cent of the total output; chain conveyors and scraper loaders for 10 per cent. All conveyor work was double-shifted and 25 per cent was triple-shifted. A total of 87 shaker-conveyor units were on the property, of which 75 were kept in operation at all times.

Jan 1, 1940

By H. P. Greenwald

Those interested in the early developments and experiments, both in the United States and abroad, that led to modern rock dusting, will find an excellent summary in a paper by George S. Rice,13 published in 1914. The period from 1914 to 1924 was one of intensive experiment on coal-dust explosions in the United States; abroad, war activities and rehabilitation stopped this work over a large part of that decade. American findings were published by the Bureau of Mines, particularly in Bulletins 167 and 268. It is convenient to consider that in the United States rock dusting to prevent coal-dust explosions in mines was initiated in 1924 with the publication of tentative specifications.17 This was followed in 1925 by an investigation of methods and costs12 and approval by the American Engineering Standards Committee of a Recommended American Prac-tice.18 Approximately 13 years have elapsed since this approval, and inasmuch as changes in rock-dusting practice in the United States have been evolutionary, it is necessary to consider this entire period as "recent" in some phases of the work. There have been no official changes in the Recommended American Practice since its approval. This paper reviews as briefly as possible knowledge acquired since the issue of the earlier papers mentioned, through experience in mines and experiments conducted by different organizations engaged in the promotion of mine safety. Size of Rock Dust The Recommended American Practice states that the dust shall be 100 per cent minus 20-mesh and 50 or more per cent minus 200-mesh. Results of large-scale tests on the relative effectiveness of rock dust of different sizes were published by the Bureau of Mines15 in 1933 and are reproduced here as Fig. 1. The limiting curve of this figure shows that

Jan 1, 1940

By Raymond Mancha

The number of installations of propeller mine fans completed during the years of 1936 and 1937 is evidence of the increasing popularity of the propeller fan with the American mining industry. During the period from 1931 to 1936, there were several different low-pressure, low-efficiency propeller fans available, which filled a definite need in replacing inefficient centrifugal fans operated at comparatively low pressure by means of purchased power. Since 1936, however, the trend toward the propeller fan has greatly increased, as propeller fans are now available practically without pressure limitations and capable of efficiencies high enough to warrant replacement of efficient centrifugal fans in many instances. Few manufacturers of propeller mine fans base their fan-operating characteristics upon similar test methods, primarily because of inadequate facilities for testing in the factory and the need of a test code incorporating a calibrated duct or nozzle that makes possible the testing of large propeller fans quickly, accurately and without prohibitive expense and space requirements. As a result, fan manufacturers have resorted to various methods for testing large propeller fans in the factory, and different yardsticks have produced uncomparable and often inaccurate performance data. It is the purpose of this paper to describe and discuss in detail the test procedure of the Jeffrey Manufacturing Co., which has been proved both accurate and practical. Fig. 1 shows a plan, a side elevation and two end elevations of the test duct with a propeller fan of the exhaust type in place. Testing propeller fans exhausting permits greater accuracy than testing these fans blowing, because in the former uniform flow conditions are more easily established at Pitot tube stations where fan pressure and air-volume measurements are desired. Any residual rotation remaining in the air discharged from a propeller fan blowing into a test duct must be removed before an attempt is made to obtain accurate pressure and volume readings. Although various devices for straightening the air may be placed between the blowing fan and the volume-measuring station without resulting complications, uniform flow so obtained at the pressure-measuring station necessitates corrective calculations to compensate for duct resistance

Jan 1, 1940

By John Chapman, J. C. Vaughan

Although a considerable amount of practical importance attaches to systems involving gases and molten metals, little is known regarding the effects of alloy elements upon the solubility of gases in liquid iron. The solubilities of hydrogen1 and nitrogen2,3 in pure liquid iron arc known and it has been shown that small amounts of silicon and aluminum3 exert only a small effect upon the solubility of nitrogen but greatly increase its rate of solution. This paper presents the results of a study of the solubility of nitrogen, at pressures approximately one atmosphere, in molten iron containing up to 15.8 per cent silicon. EXPEBIMENTAL METHOD There are two general methods by which the solubility of a gas in a molten metal may be determined. In the first, which Sievertsl employed, the gas is measured from a burette into the enclosure containing the metal and the amount absorbed is found by subtracting from the total volume that of the dead space in the container. The second method, which was used successfully for pure liquid iron, is to expose the molten metal to the gas until absorption ceases, then to solidify and analyze the metal. In either method the stirring produced by inductive heating prevents the development of a stagnant layer at the metal surface and ensures actual attainment of equilibrium. Obviously the second method is accurate only when the saturated metal is capable of solidifying without gas evolution. Since the rate of solution of nitrogen in iron is increased by the presence of silicon, it was to be expected that the rate of evolution would be correspondingly increased and for this reason the first method was selected. A sketch of the furnace is shown in Fig. 1. A small high-frequency coil having 17 turns fitted closely around a fused silica tube, 2 in. in diameter, in which was placed, on a bed of 60-mesh alumina sand, an

Jan 1, 1940

By Walter Crafts, W. D. Forging, John J. Egan

Although many elements reduce the tendency to porosity in steel castings, manganese, silicon, aluminum, calcium, titanium and zirconium appear to be most generally suitable for the purpose. The manganese and silicon contents are usually maintained in a fairly constant range. Silicon-killed castings often are made to be sound with little or no addition of the stronger degasifiers. In many cases, however, it is more practical to utilize the stronger degasifying elements, aluminum, calcium, titanium and zirconium. Since they greatly modify the composition, shape, and distribution of the nonmetallic inclusions, and thereby the ductility, the strong deoxidizers must be used in such a way as to form the least harmful types of inclusions. As the reasons for failure always to obtain good results have not been obvious, an effort has been made to determine the mechanism of solidification of steels deoxidized to produce certain types of inclusions. Diagrams representsing the mechanism of their formation have been constructed from the appearance of the nonmetallic constituents and have not only illustrated the limiting features of specific deoxidizing treatments with respect to inclusion formation and ductility, but have also indicated a relation between inclusions and resistance to hot tearing. Three different types of deoxidation treatment have been used for obtaining sound castings with relatively high ductility. The first method is to make and cast the steel under such conditions that deoxidation with silicon and a small addition of a strong deoxidizer assures soundness. The effective addition that will promote soundness without causing the formation of intergranular inclusions varies with the furnace practice and composition, but may be limitled to about 0.025 per cent Al, Zr or Ti. Up to 8.10 per cent Ca and 0.15 per cent V are also used for this purpose. The inclusions in these steels are characteristically glassy silicates and round or irregular sulphides. As pointed out by Sims and Lillieqvist,1 the formation of fine intergranular inclusions, which are detrimental to ductility, limits the amount of strong deoxidizers that may be added.

Jan 1, 1940

By Henry Seltz, Cyril Wells, Hugh J. MacDonald

Several investigators have measured the heat capacity of cementite, using different methods of attack, but the agreement between the values obtained cannot be considered good. Naeserl has made measurements of "average heat capacities" of iron carbide between 1026" and 85" K., using a water calorimeter. His computed true specific heat at 78.1" K. is 11.22 cal. per gram-formula mass, which, if correct, is much too high for any reasonably accurate extrapolation to 0" K. The cementitc used by Naeser was obtained from a steel containing 0.9 per cent carbon, by electrolytically dissolving out the iron in a neutral bath of ferrous chloride. The cementite remained as a coarse, crystalline, gray powder. Andes2 has measured the specific heat of iron carbide, from 102" to 323" K., as it exists in steel. The specific heats of several slugs of steel of known iron carbide content were determined, and the specific heat of the iron carbide (Fe3C) calculated by plotting specific heat versus percentage of carbon, and extrapolating to pure Fe3C (6.7 per cent C). The heat-capacity values for temperatures below 100" K. were obtained by comparing the temperature-specific heat curve for Fe3C to that of Fe. Since the two were very similar in the range examined experimentally and approach more closely at low temperatures, it was assumed that near the absolute zero the form of the curve for Fe3C would be similar to that of Fe. Andes calculates for the entropy of Fe3 C,S298 = 23.55 e.u. The heat of formation of Fe3C has been studied by several workers. Kelley3 has reviewed these measurements and calculations, and selects those of Roth* and Naeser6 as worthy of most consideration. Roth has given AH = 5400 cal. + 30 per cent as a result of his own and other work. Naeser has determined the heat of formation from Fe and different forms of carbon, and for graphite (0) he finds AH = 5600 cal. Kelley accepts the rounded figure AH = 5500 as the heat of formation at 298.1" K., but this value is quite uncertain.

Jan 1, 1940

By Cyril Wells, Robert F. Mehl

The diffusion of carbon in gamma iron plays an essential role in many metallurgical processes. In carburizing, in graphitizing, in homogenizing, in the formation of pearlite from austenite, and in other processes, migration of carbon in gamma iron occurs.1'2 A full understanding of the rate at which these processes occur obviously requires a knowledge of the rate of diffusion of carbon. In carburizing, for example, the depth of carbon pentration is determined by the carbon concentration in solid solution at the surface, and by the rate of diffusion inward of the carbon. Until reliable data on the rates of diffusion of carbon are available it is unlikely that a full quantitative description of this process will be obtained. In the formation of pearlite from austenite, the segregation of carbon and alpha iron from the austenite obviously requires the diffusion of carbon; the rate at which pearlite nodules grow is evidently controlled at least in part by the rate of diffusion of carbon; it is unlikely that we shall understand the factors that determine the rate of growth unless data on rates of diffusion of carbon, and the variation of these with composition, grain size, and temperature are available. Accordingly it was decided: (1) to determine, more accurately than hitherto, the diffusion coefficients of carbon in austenite over a wide temperature and a wide concentration range, (2) to study the influence of grain size and impurities on this diffusion coefficient, and (3) to study the effect of manganese and nickel on the rate of diffusion of carbon in the austenite of manganese and nickel steels, respectively; the influence of carbon on the rate of diffusion of manganese and of nickel will be made the subject of later papers. The rate of diffusion of carbon in gamma iron has been studied by Runge3 by Tammann and Schonert4, by Bramley and co-authors,5-14 and

Jan 1, 1940

By Alden B. Greninger, Alexander R. Troiano

Metallurgists have long believed that martensite in steel forms as plates along the octahedral {111} planes of austenite. Much has been written about mechanisms whereby units of the austenite lattice are pictured as transforming to martensite by shearing movements initiated along the octahedral planes of austenite, supposedly resulting in plates of martensite lying parallel to these planes of shear. A critical inspection of two or three photomicrographs of quenched hypereutectoid steel led us to the conclusion that the orientation habit of martensite, at least in hypereutectoid austenite, could not possibly be octahedral. Inasmuch as recent studies,30,31 of the martensite-type reaction in nonferrous alloy systems have established the irrational orientation habit as characteristic of this type of lattice transformation, the need for a thorough restudy of the crystallography of martensite formation in steel was evident. The present paper reports the results of such a study, extended to include both cementite and some of the products of constant-temperature decomposition of austenite. Also reported are a few of the results obtained from a microscopic and X-ray study of the austempering process in very high-carbon steel. I. The Martensite Transformation Previous Work Microstructure and Crystal Structure of Martensite.—Among the best series of published photomicrographs of quenched steels are those of Whitely,1 Robertson,2 Hanemann and Schrader,3 and Lucas.4 The crystal structure of martensite is body-centered tetragonal, with axial ratio varying from 1 near 0.0 per cent carbon to 1.08 for 1.75 per cent

Jan 1, 1940

By Norman P. Goss

It is generally agreed that cold-working mechanically refines the grains into smaller fragments and with continued working these are oriented with certain crystallographic directions bearing a relation to the direction in which the metal is worked. Some of the energy expended on the metal during plastic deformation appears in the form of heat, but a very small portion remains in the metal as stored energy. The entropy, specific heat capacity, temperature at which recrystallization will just begin, density, ductility, elasticity, tensile strength, and resistance to corrosion are affected. These properties have been studied extensively and some of the changes in the physical properties due to cold-working were attributed to lattice distortion.l-8 The broadening of the Ka lines on the X-ray diffraction diagrams of plastically deformed metals is believed to indicate lattice distortion, and consequently the existence of internal stresses. The evidence supporting this theory rests solely upon the observed experimental fact that the diffraction lines are broadened and the Ka doublets are completely diffused. Elam9 has reviewed the matter of lattice distortion in relationship to the hardening of metals by plastic deformation. The X-ray diagrams of plastically deformed metals differ in general from annealed metals. The hardening of a metal was believed due to lattice distortion.9 The resolution of the doublet is lost when a metal is cold-worked and the Laue spots are elongated. At one time this elongation was thought to indicate the elastic bending of the crystal planes. However, more careful work showed that the asterism was due to new orientations developed within the fragmented grains during plastic deformation. Some theories attributed the hardening to fragmentation of the grains into smaller units. Jeffries and Archer,ll after carefully considering the problem of work-hardening from many angles, came to the conclusion that cold-working mechanically refines the grains into smaller crystal fragments, some of which at least differ in orientation from the parent grain. The increase in

Jan 1, 1940

By J. T. Burwell

The crystal orientation in silicon iron that has been given a particular treatment described by Goss,l has been studied by Goss, by Bozorth2 and by Sixtus,3 but their results do not agree and are almost entirely qualitative. The following pages give a description of the orientation of the crystals in the material as determined by means of X-rays and expressed graphically in a pole figure. The treatment consists of hot-rolling the material into strip and then giving it two cycles of cold reduction followed by recrystallization. This produces remarkably good properties in the rolling direction, the product having a maximum permeability in this direction of more than 25,000 and a permeability at 16,000 Gauss of more than 2200. It is now generally agreed that Goss's original conclusion1 that the crystals in the final product are randomly oriented was incorrect, since Bozorth2 and Sixtus,3 using different methods, have shown that there is a decided preference in orientation. Those writers, however, expressed their results only in terms of one or more ideal orientations with deviations therefrom. X-ray Data A strip of the material containing 3.1 per cent Si, prepared by Goss,† 1.2 by 0.0125 in., was etched rapidly in warm dilute hydrochloric acid until it was 0.005 in. thick, in order to eliminate the effect of the two surface layers. The specimen was then mounted in an integrating camera similar to one described in the literature.4 The purpose of this camera is to translate the specimen during exposure, so that a statistically large number of grains contribute to the pattern photographed. The camera also allows the plane of the specimen to make various angles with the X-ray beam. An area 5 by 1.2 in. was scanned by a beam of unfiltered radiation from a molybdenum target tube operating at 37 kv., and the measurements were made principally on the peak of the white radiation. X-ray photographs were taken at intervals of 15" in a plane

Jan 1, 1940

By George Sachs, J. Spretnak

The process of recrystallization has not as yet been explained satisfactorily. Some definite conclusions could be drawn from recent investigations, such as, for example, that recrystallization is a process of nucleus formation and crystal growth1 and that the orientations of the nuclei correspond to some fragments of the original crystals, which have been considerably distorted during deformation.2 There are, however, a number of metals and alloys crystallizing in the face-centered cubic system, which form a particularly simple orientation if recrystallized as a sheet.3 Such a shect is almost a single crystal with the cubic axes parallel to the rolling, transverse, and normal directions of the sheet. This preferred cubic or (100) orientation of the recrystallized sheet has been considered to be very different from the rolling structure of the same metals,4 but there are two reasons why this last supposition remains open to controversial discussion. The first reason is academic: In practically all cases except the one mentioned above, close correlations and similarities between rolling and annealing orientations have been observed; for instance, in iron and steel sheet.6 Secondly, no deformed metal actually forms a simple orientation. In any thoroughly investigated case a number of different orientations and considerable scattering or deviations from the ideal orientations have been found.6 It is generally true that investigations on single crystals have shown that a definite orientation is approached in stretching or in compression of an originally undisturbed crystal.7 In the special cases, however, where the initial orientation was close to an important crystallographic direction that differed from the final "ideal" orientation, the resulting orientation changed very little by deformation, staying somewhere in the vicinity of the initial orientation.8 Such deviations

Jan 1, 1940

By John Wulff, R. Buehl, H. Hollomon

Although the main features of the transformations occurring in 18-8 have been published already, certain conclusions merit questioning and discussion. The questions may be summarized as follows : 1. If ferrite is formed by cold-working austenite, what happens to the carbon with which the ferrite and austenitc are both presumably supersaturated? 2. What is the nature of the alpha-ferrite formed at grain boundarices by chromium-carbide precipitation at these boundaries?

Jan 1, 1940

By H. H. Uhlig

In our study of the mechanism of and the prevention of corrosion in stainless steels, it was considered of fundamental importance to obtain knowledge of the surface structure of such alloys. If corrosion resistance is due to a self-healing oxide layer, which like a paint film protects the underlying metal, it would be obviously relevant were the effort made to make the film less permeable and more adherent; for example, the surface might be expected to respond to an anodizing process, which is found successful in increasing the film thickness and corrosion resistance of aluminum. However, if passivity and corrosion resistance of stainless steels are due to another cause, the attack of the problem would follow another path. One of the most effective techniques for studying passivity and corrosion tendency is the measurement of the electrochemical potential. Not only can one determine by potential measurements whether a metal is active or passive, but also one can determine the degree of passivity and rate of transformation of passivity with time. Chemical media that build up or destroy passivity when in contact with the steel can also be classified by potential measurements. Something can be learned, too, of the effect of alloy additions such as molybdenum to 18-8, known to decrease corrosion of the alloy in chloride solutions. A study of alloys in previous investigations has sometimes included data on the electrochemical potentials. Tammann and Sotterl measured the electrochenlical potentials of alloys of iron-molybdenum and iron-chromium and reperted the critical concentration of molybdenum or chromium at which passivity initiates. Strauss2 made similar measurements for the iron-chromium system. The electrochemical potential3 has also been used to indicate carbide precipitated 18-8. In 18-8, heat-treated to precipitate carbide, active metal exists at the region of the grain boundaries, contrasted with passive metal within the grains, the active metal accounting for a resultant active potential. Several

Jan 1, 1940

By H. H. Uhlig

Soon after general use of stainless steels began, it was observed in practice that certain combinations of factors tended to induce corrosion by pitting. For most applications this was a serious drawback, not SO much because the structural properties of the metal were impaired but because of the rapidity with which heavy sections of the alloys were penetrated by small elongated pits. These pits seemed to initiate readily in oxidizing metal salt solutions like ferric chloride and in chloride solutions like sea water. It was observed that in sea water pitting was more frequent in stagnant or polluted waters than in highly aerated, moving waters. The steels in these chloride solutions were observed to be sensitive to long contact with material such as sand grains or attached barnacles. At points of attachment or contact it was not uncommon to discover initiation of corrosion. Pits once begun at contact faces were observed to grow rapidly, usually elongating phenomenally in the direction of gravity until the metal was perforated. Hydrochloric acid and other nonoxidizing acids, on the other hand, were observed to corrode stainless steels generally; the weight losses often were higher, but the penetration less than for the pitting type of corrosion. The causes of pitting, a type of corrosion recognized as characteristic not only of stainless steels but of many additional metals and alloys, are important in corrosion studies. A possible explanation bears practical significance, for once it is known why pits begin where they do and continue to grow after initiation, intelligent direction can be given to diminishing corrosion. This can be done either by some alteration in the composition and treatment or' the alloy or by some alteration in the environment. It appears foremost in importance to discover the nature of pit foci, for if initiation of pits can be discouraged their growth will be no longer a factor to be considered. In a multi-component alloy containing many impurities normal to production of such an alloy, each of which may play a part in pitting, and whose corrosion resistance is sensitive to heat-

Jan 1, 1940

By Russell Franks, W. O. Binder

In recent years a considerable tonnage of the 18 per cent chromium and 8 per cent nickel steels has been used in lightweight high-strength structures that must be resistant to deterioration under atmospheric conditions. These steels are austenitic in character and their strength can best be increased by cold-working. Although a marked increase in tensile strength is obtained, claims have been made that the cold-worked steels do not possess fully satisfactory elastic propertics. Under certain conditions, however, this has caused no great concern, because, as explained by Ragsdale,1,2 he cold-rolled steels have been widely applied for construction of lightweight, high-strength trains using spot welding for joining purposes. Ffield3 agrees that the ease with which thin sections of the cold-rolled 18-8 steels can be joined by spot welding is greatly in their favor, but that they would be more satisfactory if higher elastic properties and a higher modulus of elasticity could be obtained. He states that, as far as the mechanical properties are concerned, the straight chromium stainless steel is superior to the cold-worked 18-8 steel, and in order to illustrate, he prcsented the data of Fig. 1, which also give a stress-strain curve for a low-carbon 13 per cent Cr steel. Ffield† proposed that columbium-bearing or titanium-bearing cold-rolled 18-8 steels be given a heat-treatment (preferably for 1 hr.) in the range 400" to 600°C. to precipitate carbides in order to obtain better mechanical properties. Discussions by Sutton,4,5 de Ganahl,6,7,8 Krivobok and Lincoln,' Knerr,l0 and Thaden11 have given further information on the properties of the cold-rolled 18-8 steels compared with other materials used in lightweight, high-strength structures. These investigators and others point out that the ultimate tensile strength of the cold-rolled 18-8 steel can be increased to 200,000 lb. per sq. in. or higher; Krivobok et al. indicate that

Jan 1, 1940