Search Documents

By Richard W. Brummett, Robert L. Dubms

Located some 180 miles east of Los Angeles in Riverside County, California, the Eagle Mountain mine supplies iron ore concentrates for the Kaiser Steel Corporation steel plant in Fontana, California, and for export to Japan. Although the deposits were first discovered in the early 1890's, no production was realized from the area until 1948 when Kaiser Steel Corporation commenced operations. A part of the large Basin and Range province, the Eagle Mountain area's geologic column comprises a thick series of metasediments resting on Precambrian gneisses and schists that have been intruded by sill-like masses of porphyritic quartz monzonite. The metasediments are composed of three quartzite units that are separated by a schistose meta-arkose and by two ore zones. They have been folded into a large east-west trending anticlinal structure that extends completely across the Eagle Mountains. The iron ore deposits occur in two well-defined horizons in the metasedimentary series, and they are found only along the north limb of the major anticline. Host rocks for the ore zones were a series of limestones and dolomites with associated quartzites. Magnetite plus pyrite comprised the primary mineralization that formed many replacement lenses and stringers of ore within the ore zones. The primary ore has been oxidized to hematite and goethite in a broad zone at higher elevations in the deposits. Hydrothermal alteration formed actinolite- tremolite granofels, local phlogopite, and minor tourmaline in the ore zones. This alteration and the ore deposition seem related to the same magmatic event that formed the porphyritic quartz monzonite intrusion

Jan 1, 1968

By R. A. Burmeister, P. E. Greene

Two methods for the synthesis and growth of single crystals of B6 P are described: a solution-growth process employing nickel as the solvent, and a vapor-growth process employing BBr3 and pH3 as the reac-tants. Relevant portions of the Ni-B-P phase diagram have been examined and liquidus data are presented for an isobaric section at an equivalent P2 pressure of 3.8 Torr, and an isothertnal section at 1300°C. Solution-growth techniques are described and the purity and crystalline perfection of the resulting material is discussed. Epitaxial growth of BeP on &P substrates has been obtained using the vapor-phase system. Evidence is presented which supports the assignment of the stoichioknetry B6P to boron sub-plwsphide. THE B-P system differs from other III-V systems in that it contains two distinct compounds. The existence of the monophosphide (BP) has been known for some time,' whereas the subphosphide (B6P) was reported only recently.' Both of these compounds are large bandgap semiconductors (Eg = 2.0 ev for BP~ and 3.3 ev for B6P4), and are therefore of interest for optoelectronic applications. The crystal structure of B6P is quite different from those of most semiconductors, being derived from that of a-rhombohedral boron by the incorporation of the two phosphorus atoms in the intericosahedral sites of the a-boron unit cell?76 B6P also exhibits a number of unusual characteristics, including a high degree of chemical inertness, hardness, and high-temperature stability. No information concerning other physical properties is available in the literature. The present study is part of a broader investigation of the preparation and properties of B6P. This paper considers methods of growing single crystals of B6P of suitable size and quality for physical-property measurements. A detailed discussion of the electrical and optical properties of B6P will be given elsewhere.' GENERAL CONSIDERATIONS The method first used to synthesize B6P was the disproportionation of BP' according to the reaction The equilibrium P2 pressures corresponding to this reaction were also determined .'" It is therefore possible, in principle, to apply several of the reactions reported for the synthesis of BP to the synthesis of B6P merely by selecting lower phosphorus pressures or higher temperatures, in accordance with the equilibrium data. Other techniques for the direct synthesis of microcry stalline B8P have also been reported.1°

Jan 1, 1968

By H. V. Makar

Laboratory tests were performed to obtain a quantitative description of the effectiveness of sodium sulfate (Na2SO4) for removing copper from molten iron and to determine the effectiveness of Na2SO4 on actual auto scrap. The tests were conducted on induction melted heats of iron averaging 0.58 and 1.50 percent initial copper and on cupola-melted auto scrap containing 0.45 percent initial copper. The Na2SO4 was added in powder form in amounts ranging from 2.9 to 43.8 percent of the weight of iron being treated. The data showed that copper removal for the various Na2SO4 treatments followed a similar trend, regardless of the iron composition that was tested. The equation Y = 1 - e-3.23x approximately reflects the relationship between copper removal and amount of Na2SO4 added, where Y is the fraction of copper removed and x is the ratio of the weight of Na2SO4 added to the weight of metal treated. Copper removals ranged from 3.3 to 74.5 percent and reductions down to less than 0.10 percent final copper were achieved in the auto scrap. Copper removals were generally accompanied by sulfur removal, and initial sulfur contents ranging from 0.10 to 0.20 percent were reduced to as low as 0.02 percent. High temperatures and long slag reaction times tended to induce copper and sulfur reversion from the slag, but, generally, the Na2SO4 treat¬ments were effective up to approximately 2,820° F with reaction times not exceeding 7 minutes.

Jan 1, 1968

By D. G. Westlake

The electrical resistance of a series of V-H alloys (0 to 3.5 at. pct H) has been measured over the temperature range G° to 360°. Interstitial impurities made contributions to the residual resistivity, but not the ideal resistivity. The contribution of hydrogen in solid solution is expressed by Ap = 1.12 microhm-cm per at. pct H; but the contribution of precipitated hydride was negligible. A portion of the so1vu.s for the V-H phase diagram is presented. The solubility limit is given by In N (at. pct H) = (5.828 i 0.009) - (2933 i 44)/RT. Comparison of critical temperatures joy hydride precipitation and published critical temperatures for hydrogen embrittlement suggests the two are related. ThiS study was initiated as part of an investigation of the mechanism by which small concentrations of hydrogen embrittle the hydride-forming metals at low temperatures. It has already been shown that, in the case of hcp zirconium, a reduction in ductility accompanies the strengthening resulting from precipitation of a finely dispersed hydride phase.''' Our attempts to detect a similar precipitation of a second phase at low temperatures in V-H alloys by transmission electron microscopy have been thwarted because we have been unable to prepare thin foils that are representative of the bulk material with respect to hydrogen concentrati~n.~'~ The present investigation establishes the solvus of the V-H system at subambient temperatures. Subsequently, we hope to be able to determine whether the embrittlement temperature is related to the critical temperature for precipitation of the hydride in a given V-H alloy. veleckis5 has proposed a partial phase diagram for the V-H system based on extrapolations of the pressure-composition relations he measured at higher temperatures. Kofstad and wallace' conducted a similar study of single-phase alloys but did not attempt to establish the phase diagram. Zanowick and wallace' and ~aeland' have studied a portion of the phase diagram by X-ray diffraction, but they investigated no alloys in the hydrogen concentration range 0 to 3 at. pct, the range of interest to us. EXPERIMENTAL PROCEDURE The vanadium was obtained from the Bureau of Mines, Boulder City, Nev., in the form of electrolytic crystals. The analyses supplied with them listed 230 ppm by weight metallic impurities, 20 ppm C, 100 ppm N, and 290 ppm 0. The crystals were electron-beam-melted into an ingot that was rolled to 0.64 mm. Strips, 60 mm long and 4.2 mm wide, were cut from the sheet, and both rolled surfaces were ground on wet 600-grit Sic paper to produce specimens 0.4 mm thick. They were wrapped in molybdenum foil, vacuum-encapsulated in quartz, and annealed 4 hr at 1273°K. The specimens were annealed in a dynamic vacuum of 2X lo-' Torr for 30 min at 1073°K for dehydrogenation, and charged with the desired quantity of hydrogen by allowing reaction with hydrogen gas at 1073°K for 2 hr and cooling at 100°K per hr. Purified hydrogen was obtained by thermal decomposition of UH3. Sixteen specimens were studied: two contained no hydrogen and the others had hydrogen concentrations between 0.5 and 3.5 at. pct (hydrogen analyses were done by vacuum extraction at 1073°K). Electrical resistances were measured by the four-terminal-resistor method on an apparatus similar to the one described by Horak.~ The specimen holder was designed so that both current and potential leads made spring-loaded mechanical contact with the specimen. The potential leads were 30 mm apart, and the current leads were 55 mm apart. The current was 0.10000 amp. We used the following baths for the indicated temperature ranges: liquid nitrogen, 77°K; Freon 12, 120" to 230°K; Freon 11, 230" to 290°K; and ethanol, 290" to 340°K. Temperatures lower than 77°K were achieved by allowing the specimen to warm up after removal from liquid helium. Temperatures above 77°K were measured by a calibrated copper-constantan thermocouple (soldered to the specimen holder) and below 77°K by a calibrated carbon resistor. The temperature of the bath changed less than 0.l0K between duplicate measurements of the resistance. RESULTS AND DISCUSSION Typical plots of resistivity p vs temperature T are shown in Fig. 1. In the interest of clarity, only five curves are presented and the data points have been

Jan 1, 1968

Open cut mining of the Black Rock chalcocite ore started in 1963. A ground movement monitoring programme was commencing in the early stages of mining when signs of instabilityof the western wall became apparent. Eventually 100.000 cu vd, of overburden Were removed beyond the rim of the western wall in an attempt to stabilize the slope. Subsequent decpenlug and mining till the final batter angle of 45 resulted in deterioration and mining was stopped 38 ft short in the ulltimte design deplh of 520 ft.Investigations showed that the geology of the western wall , was a major factor in the instability of this wall. A block jointed model was made 10 illustrate some of the pehomena observed. Quallatative agreement was found between the model deformation and the field measurements obtained.The results of the monitoring programme clearly show the value of this work In respect to the conlrol of the mining operatIon...

Jan 1, 1968

By M. C. Flemings, G. E. Nereo

General expressions are given to describe macro-segregation in castings and ingots which results from mass flow of solute-rich liquid to feed solidification and thermal contractions. Analytical solutions are given for solidification with planar isotherms (unidirectional and bidirectional heat flow). These solutions describe inverse segregation and centerline segregation. Numerical examples are given for A1-4.5 pct Cu alloy. In 1540, Vannoccio Biringuccio published one of the first references to macrosegregation, describing the problem of exudation and inverse segregation in the manufacture of bronze gun barrels.' Since then, a great many studies of macrosegregation have been reported. Recent work of particular engineering interest includes that of Marburg 2 and others:" on centerline segregation and other types of segregation in large steel ingots, and work of Adams,5 Scheil, 6 and Kirkaldy and youdelis7 on inverse segregation in nonferrous ingots. In most studies on this subject, the various types of macrosegregation have been treated as separate phenomena. For example, quite different mechanisms have been proposed for formation of centerline segregation, negative cone of segregation, inverse segregation, banding, and so forth. In this, and in several papers to follow, it is proposed that these as well as other types of macrosegregation result from the same basic mechanism and can be quantitatively described by the same basic equation. It has often been suggested that some types of segregation (such as centerline segregation and banding) occur as a result of buildup of solute at the tips of growing dendrites.2-4 ,8-10 As example, banding can be induced in centrifugal castings by mechanical vibration, and Northcott 10 suggests this might be due to the influence of the vibration on the boundary layer at the dendrite tips of the growing dendrites. However, in view of the extremely small boundary layer known to exist at the tips of the dendrites,11,12 any interpretation of macrosegregation based on this boundary layer is clearly incorrect. Note that experiment has shown that significant buildup of solute does not occur at dendrite tips in ingot solidification, but even if such buildup occurred the thickness of the enriched zone would only be the order of D/U where D is liquid diffusion coefficient and U is dendrite tip velocity. For usual casting or ingot solidification this solute-enriched layer is 10"3 cm, far too small to account, for example, for centerline segregation.11'12 It has also been suggested that convection in the bulk liquid (ahead of the advancing dendrites) might cause segregation by sweeping away the solute-rich boundary layer in front of the dendrites.3 However, since there is no significant boundary layer, this explanation must be incorrect. The convection might directly cause segregation by penetrating between the dendrite arms, and presumably in a rimming steel ingot it is sufficiently vigorous to cause some segregation in this way. Centerline segregation, however, cannot be interpreted as resulting from this convection since a sharply segregated zone is usually found near the centerline, with the bulk of the ingot being nearly of nominal composition. If convection in the bulk liquid were the direct cause, a gradual change in ingot composition over the entire cross section would be expected. It is known that sudden changes in convection of the bulk liquid during solidification can result in banding,14 but it is not clear that the banding results directly from the effect of convection on solute distribution. Changes in convection also affect thermal conditions in the liquid-solid region of a solidifying ingot. It will be seen later in this paper, and in a paper to follow, that macrosegregation is strongly influenced by these thermal changes. Recognizing that in some cases of ingot solidification (as in solidification of rimming steels) convection in the bulk liquid may have a direct effect on solute distribution, we neglect it in this paper and in the several to follow. We then derive general expressions describing macrosegregation which results from the mechanism of interdendritic flow of solute-rich liquid

Jan 1, 1968

By W. L. Eaton

This report is the second in a series concerning the Bureau of Mines program for microfilming maps of abandoned mines in the Pennsylvania anthracite region; a catalog of the microfilmed maps of mines in the Wyoming Basin of the Northern anthracite field is presented. The first report I.C. 8274, published in 1965, was a catalog of microfilmed maps of mines in the Eastern Middle anthracite field. Additional catalogs will be published as the microfilming of significant mining areas is completed.

Jan 1, 1968

By David P. Shoemaker, Clara Brink Shoemaker

The I phase was discovered by Bardos, Malik, Spiegel, and Beck1 in the V-Ni-Si system at 1100°C and in the Mn-Co-Si and Mn-Ni-Si systems at 1000°C. Kuzma and Hladyshevskii2 and Kuzma, Hladyshevskii, and cherkashin3 have reported a new phase, which they named the S phase, in the Mn-Co-Si and the Mn-Ni-Si systems at 800°C at approximately the I phase compositions. The powder diffraction diagrams of the I and S phases, compared by Bardos el al.,1 are related but show distinct differences in relative intensities. Professor Paul A. Beck kindly sent us a specimen of the (v-Ni-Si) I phase for single-crystal study. Precession and Weissenberg diagrams taken with a tiny single-crystal fragment showed that the structure is monoclinic with a large unit cell. The cell dimensions were refined from a powder diffraction diagram taken with CrKa radiation in a 57.3-mm camera with our computer program LSCELP4 using only the indices of those reflections that were observed on Weissenberg diagrams (hnl, with n = 0 through 9 and n = 12) and precession diagrams (Okl, lkl, Izk0, hkl, hk2). Table I shows the agreement obtained between the l/d values calculated with the final values for the cell dimensions and the l/d values observed by Bardos et al .1 for I(V42Ni33Si25), by US for I(V41Ni36Si23), and by Kuzma and Hladyshevskii2 for S(MnpCoSi). The powder patterns contain many broad and diffuse lines. In fact practically all powder lines observed are near-superpositions of several reflections. The refinement program is not set up to handle several reflections contributing to one observed line: the position of each line is refined with the aid of one set of indices only. The final values for the cell dimensions were obtained from the lines of strong or medium intensity with the indices indicated by asterisks in Table I: a0 = 13.403(6), bo = 23.336(15), co = 9.129(6)A ß = 99.11(6) deg The standard deviations (given in parentheses) are those calculated by the refinement program from least-squares theory and do not take into account that the lines included in the refinement may not have been correctly indexed in every case or that the position of a line may also be partly determined by the overlapping reflections. The agreement between the calculated and observed I phase patterns is fairly good, although some discrepancies occur. Not all observed lines could be indexed with the incomplete set of sin-

Jan 1, 1968

By A. Hellawell

Specitlrens of the Al-Ge eutectic alloy have been frozen unidivectionally at rates between 2.5 x 10-6 and 2.5 x 10-4 cm per sec and the structure examined by optical and X-ray methods. There is no epitaxial relationship between phases, the aluminum having random orientation and the germanium a preferred (011) fiber textuve. Lamellar colonies which are BINARY eutectic alloys occur between either silicon or germanium with the metals aluminum or silver. common in this alloy are constructed from axial and nonaxial (111) plates of germanium which are related by a variety of twin configurations. Irregular or globular regions of the microstructure are composed of continuous single crystals of each phase, the germanium being heavily twinned. There is limited solid solubility in these systems, and the eutectic phases all involve diamond cubic with fcc crystal structures. In the microstructures of these eutectic mixtures the silicon and germanium crystals exhibit an almost infinite variety of shapes which are notably sensitive to

Jan 1, 1968

By R. Taggart, D. H. Polonis, J. C. McMillan

Thin foil electron microscopy techniques have been used to study the micros tructure of a Ti- 7.5 wt pct vanadium alloy in the quenched and aged cond_itions. Selected area diffraction has identified a (1011) twinning mode accompanying the martens ite t9.an.sfo?rn~ation. Precipitation of the 0 phase during the aging of quenched alloys has been obsevced to occuv in the form of plates and needles with preferential growth along the (1120) direction in the a' matrix. In the present work, the micro structures of quenched and aged alloys of the 0 isomorphous Ti-V system have been investigated by means of thin-foil electron-microscopy techniques. Most of the previous studies of martensitic phases in titanium-base alloys have utilized optical microscopy and X-ray diffraction techniques. The application of transmission electron microscopy is more recent, and only a few such studies have been reported.1-5 This paper is concerned particularly with the crystallographic nature of substructures formed in the martensitic a' plates. The early stages of aging or tempering have also been examined to determine the modes of precipitation from the martensitic solid solutions. Such information is essential in studying strengthening mechanisms and in determining the feasibility of high-strength rnartensitic alloys based on titanium. Liu and Margolin6 reported several types of substructures within the martensitic plates of quenched Ti-Mn alloys. It was later suggested by Liu7 that the structure of martensitic plates might be very complex and not single crystals as normally assumed. The sub-markings could not be identified with the two possible habit-plane orientations {334}ß and {344}ß, and it was not positively determined whether they are associated with mechanical twinning. The recent studies by Armitage5 on titanium martensites in a variety of commercial alloys have indicated that twinning does not generally accompany the transformation. This observation is in accordance with the Mackenzie and Bowles model for the transformation in pure titanium8 which suggests that twinning is not to be expected. However, a number of other recent investigators have reported twinlike substructures in the martensitic plates of several titanium systems including commercia1 titanium,2,3 Ti-Cu,5,9 Ti-Ta,1 and the commercial alloy Ti-8A1-1Mo-1V. Blackburn* has reported that the structure of quenched Ti-8A1-1Mo-1V depends on the prior solution temperature. He identified two types of martensitic structures, one of which is described as a heavily faulted hcp or twinned fcc structure and the other an hcp structure with a high internal dislocation density. The latter type exhibited some twinning with a (1011) twin plane. EXPERIMENTAL PROCEDURES AND RESULTS The alloy used in the present work was a 7.5 wt pct V alloy that was prepared by conventional arc-melting techniques. This alloy composition was selected

Jan 1, 1968

By J. C. White

"This paper was prepared for and presented at a lecture series on ""Materials Randling"" at McGill University. The development of trackless mining at Gaspe Copper Mines, Limited is described, showing the changes in mining method and the part played by the mobile equipment in the evolution of this highly mechanized underground operation. Comparisons of loading and hauling machines are given and an attempt is made to predict some possible future developments.INTRODUCTIONTHE PROPERTY OF GASPE COPPER MINES LIMITED is located in the Gaspe Peninsula of the Province of Quebec, 60 miles west of the village of Gaspe and 25 miles south of the St. Lawrence River. The original discovery of low-grade ore was made at Copper Mountain in 1921. Subsequent exploration revealed the richer Needle Mountain orebodies, and eventually in 1951 the decision was made by Noranda Mines to build the mining, concentrating and smelting complex (Figure 1). Construction and development of the mine was commenced in 1952 and production started in 1955."

Jan 1, 1968

By S. Lipson, H. W. Antes, H. Rosenthal

A study was made of the effect of ingot structure on the strength and ductility of high-strength wrought-aluminum alloys. It was found that a fine-cast structure facilitated complete homogenization which, in turn, resulted in significant increases in ductility and strength. A completely homogenized 7075-T6 alloy developed tensile properties of 85,000 psi UTS, 75,000 psi YS, with 40 pct RA. Completely homogenized 7001-T6 alloy tensile properties were 102,000 psi UTS, 99,000 psi YS, with 19 pct Ra. A method was devised for making small ingots having secondary dendrite arm spacing of less than 10 u. This method involved multiple-pass arc melting of commercial rolled plate with a tungsten electvode. This material could be completely homogenized after 3 hr at 900°F; homogenization of the original plate material was not complete after 120 hv at 900°F. Degree of homogeneity was determined by use of metallographic and electron-microprobe analyses. The electron-micro-probe study also showed the preferential segregation of solutes in the microstructure. HIGH-strength aluminum alloys, such as those of the 7000 series, usually freeze by the formation and growth of dendrites. The dendrite arm spacing (DAS) depends on the rate of solidification.' Commercial ingots are usually direct chill-cast to promote more rapid solidification, but, due to the large mass of the ingot, localized solidification times are long and a large DAS results. During solidification, solute elements are rejected by the solid as it forms, causing enrichment of the liquid and ultimately solute-rich interdendritic regions. In order to attain a homogeneous ingot, the segregated solutes must diffuse across the dendrite arms. The larger the DM, the longer the time for complete homogenization. In the case of commercial ingots, the DAS is so large that the time for complete homogenization is prohibitively long and, therefore, second phases or compounds are always present. These un-dissolved phases are carried over to the wrought material during processing, resulting in an impairment of strength and ductility. In addition, the mechanical fibering of the undissolved second phases or compounds during working results in mechanical property anisotropy. If complete homogenization could be attained, higher ductility could be expected. The realization of higher ductility at current strength levels is a desirable objective; however, if higher-strength alloys were wanted, it might be possible to sacrifice some of this ductility by adding more solute elements and produce even higher-strength alloys than are currently available. Further, if complete homogenization leads to more efficient utilization of solute elements, then more dilute alloys should have relatively high strengths with very high ductility. In all instances, it would be expected that the degree of mechanical property anisotropy due to mechanical fibering would be reduced. Therefore, it was the purpose of this investigation to produce cast structures that would facilitate homogenization and to determine the effect of homogenization on the properties of high-strength, wrought-aluminum alloys. MATERIAL CLASSIFICATION Commercial Alloys. In order to illustrate the non-homogeneous condition that exists in commercial high-strength, wrought-aluminum alloys, typical micro-structures of 7001, 7075, and 7178 are shown in Fig. 1. The chemical compositional specifications of these alloys are given in Table I. It can be seen in Fig. 1 that a considerable amount of undissolved second-phase material is present in each of these alloys. The solute elements associated with the undissolved phases were identified by electron microanalyses. Back-scattered electron images and characteristic X-ray images of the three commercial alloys are shown in Figs. 2, 3, and 4. These data indicate that the second phases are regions of high copper and high iron-copper concentrations. The second-phase material also was analyzed for magnesium, zinc, manganese, chromium, and silicon, but no significant enrichment above that of the matrix was found. Therefore, the problem of homogenization resolved itself into one of dissolving the copper-rich and the iron-copper-rich second phases. In order to accomplish this objective, two approaches were made. The first was to reduce the iron as low as possible since this element has a maximum solid solubility of 0.03 pct in aluminum. The second was to produce cast structures with finer DAS to facilitate dissolving the second phases. Commercially Produced High-Purity Alloys. A special high-purity, 2000-lb ingot of 7075 alloy was made by a commercial producer. This alloy contained the following weight percentages of solutes: 5.63 Zn, 2.48 Mg, 1.49 Cu, and 0.21 Cr. All other elements combined were less than 0.02 pct by wt including iron and silicon at less than 0.01 pct each. The ingot was cast and processed into rolled plate using standard commercial techniques. Microstructures of standard commercial 7075 and the special high-purity 7075 are shown in Fig. 5. It can be seen from this figure that the high-purity alloy has less undissolved second-phase material, but a significant amount was still present. The second phase in the high-purity material did not contain iron but it was found to be enriched with copper. The slight effects of the increased purity and de-

Jan 1, 1968

By D. S. Burgess

The characteristics of gas-phase detonations were observed in 20 instrumented firings within earthen tunnels, in 100 such detonations in a 24-in-diam by l63-ft-long steel pipe, and in about 200 smaller scale firings. Most of the fuels studied were representative hydrocarbons--acetylene, propane, gasoline, and a roughly equimolar mixture of methylacetylene, propadiene, and propane. In a pipe with two closed ends, the detonable limits were demonstrated to be very nearly the same as reported limits of flammability. The side-on impulses (pressures integrated over 200-msec intervals) were shown to be the same function of concentration regardless of whether deflagration or detonation had occurred. In a pipe with only the initiation end closed, the impulses of all fuel-air systems tended toward the same level when averaged over comparable ranges of fuel concentration; the lower pressures with saturated hydrocarbons were nearly compensated by longer durations of pressure transient. In all fuel-air systems, unexpectedly high impulses were obtained with slightly lean mixtures. In earthen confining structures, the impulse, of the explosion was efficiently converted into momentum of the failing wall. In the configurations studied, an earth velocity of about 20 fps was critical to overcome the soil's resistance to shear. The destructive effect was determined by gas pressure rather than by total energy release. The assignment of a "TNT equivalent" to an explosive gas mixture is discussed in terms of the confinement of the mixture.

Jan 1, 1968

By Clark L. Corey, Bogdan Lisowsky

Electrical resistivity, X-ray line positions, degree of order, and microstructures have been investigated for Ni-A1 alloys near the Ni3Al composition. The results indicate that Ni3Al undergoes disordering between 1250oC and the mp; also supersaturated y, produced in y + y' alloys by gas quenching, is extensively ordered prior to y' (Ni3Al) phase separation. The latter reaction, if not both, must follow the cooperative phenomena model. Shifts in line position as a function of quench-indulced super satulration are shown. Lattice pavarneters of equilibriunz and nonequilibrium phases are given. THE objective of this investigation was to determine the mechanism and kinetics of the reactions which occur in Ni3A1 and hypostoichiometric Ni3A1 alloys. The results are of particular significance relative to pre-precipitation phenomena. Early work on Ni-A1 binary compositions near the Ni3A1 composition (13.6 wt pct Al) has been adequately reviewed by Hanssen,1 whose phase diagram is presented in Fig. 1. williams2 verified the suggestion made by Taylor and Floyd3 and others4 that y', Ni3A1, may precipitate coherently on (100) planes of the y phase (see Fig. 1 for phase nomenclature); he further suggested a two-step precipitation mechanism consisting initially of probably short-range ordering followed by actual precipitation of y'. The precipitation stage in low-aluminum hypo-eutectic compositions has been studied by a number of investigators;*"7 short-range order or "zone" formation have been suggested as explanations for various diffuse X-ray scattering effects. The ordering reaction in Ni3A1 alloys is characterized by a) a very rapid rate of ordering in nonstoi-chiometric compositions, b) absence of a disordered phase region for the stoichiometric compound, y', or Ni3A1, c) precipitation phenomena as a dominant aspect in hypoeutectic alloys, and d) an increase in elec-trical resistivity on ordering.' The latter two factors were found by Newkirk to characterize ordering in Co-Pt, for which an extensive and detailed analysis was made.' An electrical-resistivity increase on ordering has also been reported for cuAu3.10 PROCEDURE Ni-A1 alloys in the form of 1300-g chill-cast ingots were prepared by vacuum melting electrolytic nickel and high-purity (99.99 pct) aluminum. Very small heats prepared from high-purity carbonyl nickel, supplied through the courtesy of Dr. Goff of the Naval Research Laboratory, were used for comparison with the larger ingots and no differences were noted. The cast material was homogenized in purified argon for a minimum of 72 hr at 1200°C and water-quenched from 1350°C. Compositions studied are given in Table I. The 10 pct A1 alloy was both hot- and cold-rolled. X-ray superlattice line intensities and peak positions were obtained from -270 mesh filings, using CuK, radiation with a LiF crystal monochromat adjusted to receive both 01 and a2. One-degree slits and a 1/8 deg per min scan rate were used to record line traces. A standard tungsten powder, obtained through the courtesy of G.E. Research Laboratory, was used to calibrate line positions.

Jan 1, 1968

By D. M. Clippinger, J. J. Eidel, J. E. Frost

At Ithaca Peak, one of three peaks situated on Duval Corporation's Mineral Park property, a 'Single pulse of quartz monzonite magma intruded the isoclinally folded Precambrian Cerbat complex consisting of schist, quartzfeldspar gneiss, and amphibolite. The magma reacted with the Precambrian rocks, yielding a quartz-diorite rim. As the magma crystallized within the rim, it produced, progressing in'ward, annular bodies of quartz monzonite porphyry, quartz porphyry, and a distinctive quartz porphyry containing abundant podiform, tabular, and irregular quartz masses. These quartz masses are spatially associated with discontinuous crenulate and tabular quartz veinlets. Following crystallization, the Ithaca Peak stock and part of the surrounding Cerbat complex were fractured, producing a stockwork of predominantly northwest and northeast-trending fractures. The stockwork was then mineralized during a period of decreasing temperature by: ( 1) quartz-pyritechalcopyrite veinlets without distinct selvages and with distinct alteration envelopes in which orthoclase was altered to quartz and sericite; (2) quartz-pyrite-chalcopyrite veins and veinlets with distinct selvages and without distinct alteration envelopes; and (3) pyrite-chalcopyrite- galena-sphalerite veins. The Ithaca Peak stock was pervasively sericitized or argillized. The Mineral Park property is surrounded by a zone of propylitization Alteration and mineralization are coextensive in space and were, at least in part, coincident in time. The Mineral Park property possibly was elevated and exposed twice prior to its present exposure. The protore has been enriched by a factor of three. The Ithaca Peak supergene ore body is conformable with present topography and lies above the present water table. The shape of the ore body was controlled by erosion and oxidation of the previously enriched mineralization. Hematite, goethite, and jarosite present at the surface indicate a high primary pyrite environment, but it is possible to recognize that a small proportion of veins and veinlets contained greater amounts of chalcocite and chalcopyrite than pyrite. The igneous facies on Ithaca Peak are the products of differentiation within a solidifying rim according to Bowen's Reaction series. The innermost facies contain more quartz and orthoclase than the outer facies. Late magmatic quartz in the case of Ithaca Peak contains small amounts of pyrite and molybdenite. It is suggested that this quartz-sulfide mineralization, may also have been the product of differentiation the product of differentiation, may indicate that the later hydrothermal mineralization may also have been the product of differentiation.

Jan 1, 1968

By E. L. Raymond

The effect of heat treatment on the microstructure and resultant notch-bar rupture life of ZNCONEL alloys X- 750 and 718 was studied. It was found that the primary effect of heat treatment in rendering these alloys notch-ductile is the elimination of any y' denuded zone adjacent to the pain boundaries. The mechanisms by which such a denuded zone can arise and be eliminated by heat treatment are discussed. InCONEL Ni-Cr alloy X-750 and INCONEL Ni-Cr alloy 718 are age-hardenable austenitic materials. Alloy X-750 is used for its corrosion and oxidation resistance and high creep-rupture strength up to 1500°F. Alloy 718 is used most effectively up to 1300°F. One of the most important areas in their development has been establishment of consistently good rupture properties, especially in the presence of a stress concentration, such as imposed by a notch. A desire to improve these properties has led to extensive studies of the effect of heat treatment on the micro structure of these alloys and their performance in stress-rupture tests. In earlier investigations"~ of INCONEL* alloy X-750, *INCONEL i s a Registered Trademark of The International Nickel Co., Inc. grain boundary carbide morphology was linked with stress-rupture properties. If, during heat treatment, the carbide MZSC was precipitated in the grain bound-ary in a cellular form, poor rupture properties re-

Jan 1, 1968

By Don H. Baker

THE need for new or improved refractory materials has caused metal phosphides to be given renewed scrutiny. Some metal phosphides show high-temperature inertness, are exceptionally hard, and exhibit a marked resistance to chemical attack. Various metal phosphides have been prepared for study by direct combination of the elements,'-' by reaction of metal or metal compounds with phosphine or phosphorus trichloride,'"' by thermal decomposition of a metallic phosphate or phosphite,"-'8 and by molten salt electrolysis.19 Electrolytic preparation of phosphides of titanium, manganese, and chromium from their oxides is reported in this paper. An externally heated 3-in.-ID by 6-in.-deep graphite cell, that served as the anode as well as a container for the electrolyte, was used in these investigations, and a suspended, centrally positioned graphite rod served as the cathode. A closely fitting silicon carbide furnace liner minimized atmospheric oxidation of the crucible. Electrolyses were performed for predetermined periods and current settings. Preliminary research had indicated the more efficient current and potential settings that could be used. Upon completion of the deposition period, the deposit was hot-stripped from the cathode. The mass of crystalline deposit, plus occluded and adhering salt, was crushed to minus 10 mesh and hot-leached in dilute hydrochloric acid. The leached crystalline material was water-washed, dried, and sampled for analysis. Products were identified by X-ray diffraction and standard analytical procedures. Electrochemical studies were initiated to establish the optimum conditions necessary to produce manganese phosphide (MnP), titanium phosphide (Tip), and chromium phosphide (CrP). Among the factors studied were the operating temperature, the imposed current, and the electrolyte system. If the temperature, or imposed current, was too high, deposition of phosphorus resulted, and if either were too low, partially reduced lower oxides were deposited. The operating conditions established for repetitive high-quality production of metal phosphides of the MP structure are presented in Table I. The metal phosphide crystals varied in size, but all had a definite metallic appearance. Typical are the crystals of CrP shown in Fig. 1. Evaluation data and analysis of the crystals are presented in Table 11. Efforts to measure resistivity of these three compounds over the temperature ranges of 250o to 400°K were hampered by the small physical size of the crys-

Jan 1, 1968

By J. A. Solomon, H. E. Shafer

As a result of the great demand for metallic aluminum and the scarcity of domestic bauxite, numerous processes have been proposed and developed to extract the oxide of this metal (Al2o3) from clays, shales, and other low-grade raw materials.1-4 An exploratory study was made to extract alumina with sulfuric acid from relatively impure coal-associated draw-slate and to establish an optimum calcination temperature for maximum recovery. Draw-slate is the term used to describe the hard, slaty material directly overlying many coal seams and may range from a few inches to a few feet in thickness. Alumina content of these draw-slates may range from as low as 15% to over 35%. Although the following results are limited in scope, some of the data should prove beneficial for further work. Coal-associated clay, shale, and gob heretofore have been considered nuisance products; any successful alumina extraction process would greatly enhance the worth of these almost limitless resources. This research demonstrated that an optimum calcination temperature for alumina extraction could be established for a coal-associated draw-slate and that this temperature was lower than those suggested in previous work with unspecified clay types. It should be noted that slightly higher acid concentrations and somewhat finer particle sizes were used in this series of tests as compared to previous work. EXPERIMENTAL WORK Essentially, alumina extraction proceeded in four steps: 1) grinding, 2) calcining, 3) acid leaching, and 4) precipitating of aluminum sulfate. An initial series of reference tests to determine the optimum temperature of solubility for alumina was run using relatively pure kaolin. Kaolin forming clays are hydrous aluminum silicates of the approximate composition 2H2O A12O3 2SiO and kaolinite is the mineral that predominates in most kaolins. 5 The kaolin was ground to -30 mesh and subsequently calcined at temperatures ranging from 100°C to 700°C. Each sample was calcined for 1 hr in a muffle furnace and in turn subjected to sulfuric-acid leaching (H2SO4, 9 molar) for a 2-hr period. The filtrates were analyzed for the amount of dissolved alumina recovered.637 Also, each sample of leached or barren residue was

Jan 1, 1968

Jan 1, 1968

By B. H. Kear, S. M. Copley

Stress-stvain curves are presented for Ni3Al (y') cvystals in several ovientations, deformed in tension and compression at constant displacement rate, at temperatures from 70° to 2000°F. Both the yield stress and wovk havdening increase with temperature, with the magnilude of the effect dependent on ovientation. The yield stress maximum occurs at 1500°F in [001], at 1400°F in [011], and at 1200°F in [111]. The suppression of the yield stress peak in [011] and [111] orientatiorzs is due to the onset of cube slip, rather than octahedval slip, a1 elerated temperatures. The temperature and orientalion dependence of work hardening in nominal single slip orientations corvelates with changes in the CRSS ratio for octahedral slip and cube slip, in agreement with a model for work hardening based on pinning of screw dislocalions by cross slip from an octahedral plane into a cube plane. It is concluded that the unique plastic properties of y' have a decisive influence on both ductility and strength characleristics of y +y' nickel-base superalloys. It has long been recognized that the strength of y + y' nickel-base superalloys depends on the precipitation of the y' phase [basically Ni3(Al,Ti)]. This paper presents new data on the strength characteristics of single crystals of simple y' (Ni3Al), and forms the first step in a systematic program aimed at elucidating the mechanisms of hardening in the complex commercial alloys. 1) EXPERIMENTAL PROCEDURE Single crystals of off-stoichiometric NiA1 were grown from the melt under vacuum by a modified Bridgman method. The melt was poured into a preheated alumina mold and crystal growth was promoted from one end by gradient cooling. The crystals were homogenized by annealing in hydrogen at 2400° F for 72 hr followed by furnace cooling. Chemical analysis of samples taken from several crystals gave an average composition of 88.2 wt pct Ni. Spectrographic analysis gave as the principal impurities in weight percent— Si (0.02), Mg (0.01), Fe (0.02), Ti (0.002), Cu (0.008), and Co (0.03). Tensile specimens with specifications as in Fig. 1 were prepared by a series of operations involving electrical discharge machining, precision grinding, and electropolishing. Compression specimens with dimensions 1/4 by 1/4 by -3/4 in. were prepared in a similar manner, except for the initial shaping operation using a precision cut-off wheel/two-circle goniometer unit to give selected crystal orientations. Specimens were deformed in a Baldwin-Wiedemann testing machine with furnace attachment, using a strain rate of 5 x 10-4 sec-1. The strain measuring device consisted of extension arms attached to the tensile grips (or compression plattens) at one end and leading out of the furnace to an LVDT at the other. Temperature was controlled by a thermocouple placed in contact with the specimen. According to the known phase diagram for the Ni/A1 system,' when an alloy of the specified composition is cooled from the melt, primary y (nickel solid solution) dendrites grow at the expense of the liquid phase, which becomes enriched in aluminum. At the eutectic composition the remaining liquid freezes as a two-phase mixture of y + y' (Ni3Al). Upon further cooling, a solid state transformation occurs, involving the precipitation of y' in the primary dendrites, and the complete transformation of the eutectic mixture to massive y'. The as-cast structure consists, therefore, of y + y' dendrites with interdendritic regions of massive y', i.e., transformed eutectic, Fig. 2. 2) DISCUSSION OF RESULTS 2.1) Stress-Strain Curves. Fig. 3 shows tensile stress-strain curves for crystals in orientations close to [001] deformed at temperatures from 70° to 2000°F. Both the yield stress and total elongation are strongly temperature-dependent. At 70°F, easy glide is absent, and the work hardening coefficient BIT - G/300. At T > 1500°F, the negative slope of the stress-strain curves is due to pronounced necking in the crystals. The yield stress maximum at 1500° F corresponds with a minimum in the ductility, Fig. 4. The extensive duc-

Jan 1, 1968