By N. A. D. Parlee, E. M. Sacris

OXYGEN solubility in liquid silver has been well studied.1-6 It has been established that the solubility follows Sieverts' law reasonably well5'6 up to po2

Jan 1, 1968

By Olav Idelgeland

FROM indirect evidence point defects have been believed to influence the fatigue behavior of metals and alloys.1,2 Measurements of changes in resistivity made after cyclicstressing at low temperatures indicate that a very high density of defects is present, part of which may be removed by room-temperature annealing.3'4 These results are consistent with the generation of a high number of point defects at low temperatures. Corresponding measurements made after room-temperature stressing did not show any recovery effects.3 This was attributed to a stabilization of the dislocation network after a few thousand cycles without generation of vacancies. In this laboratory resistance measurements of copper single crystals, shaped as normal fatigue specimens ,5 have been made with a Kelvin double bridge at room temperature during and after cyclic stressing at 80 cps by comparing with a dummy at a close and constant temperature. Temperature differences were measured to ±0.025°C with fine thermocouples taped onto the gage lengths. Potential leads were tin-soldered into small holes in the gage length to give stable values. Corrections for differences in temperature and changes in mean length of the specimen were made according to the formula:

Jan 1, 1968

By T. L. Berger, M. C. lnman, M. F. Rose

AFTER shock loading, mechanical twinning has been observed by several authors1-4 for a variety of fcc metals and alloys. It has been shown2,3 that low stacking fault energy materials deform primarily by the formation of mechanical twins and stacking faults during dynamic loading. Further, Inman, Murr, and Rose2 have shown that a correlation exists between the average hardness and the volume percent of mechanically twinned material in stainless steel. It has been observed in nickel' that mechanical twins are produced during shock deformation if the peak pressure associated with the shock wave is greater than 350kbar. It is the purpose of this work to discuss shock-hardening mechanisms in nickel and to determine to what extent the initial condition influences the final response. The "flying plate technique" was used to generate planar shock waves with peak pressures as high as 710 kbar. The details of the technique5" have been discussed elsewhere and will not be repeated here. The material used in this study was polycrystalline nickel of 99.98 pct purity and had an initial grain size of 0.18 mm. Prior to any deformation, all samples were given a stress-relief anneal of 6 hr at 600°C in a vacuum furnace. After annealing, the initial condition of the samples was changed by cold rolling individual samples from 0 pct to a maximum of 80 pct reduction in thickness. This provided samples with controlled initial histories for shock deformation. Immediately after shock loading, the specimens were slowed and quenched by suitable arrangement of buffer material and water bath. This technique minimized specimen damage and the effects of shock heating on the samples. Since deformation twins in high stacking fault energy fcc metals are only produced at high stress levels, the initial defect configuration prior to mechanical twinning should greatly influence the number of twins formed. In fact, Zukas and Fowler7 have found that prestraining in iron and steel greatly suppresses the formation of mechanical twins during the shock deformation process. Following the methods of Warren and warekois8 and Cohen and Wagner,9 X-ray diffraction profile analysis was performed to determine the incidence of stacking faults and mechanical twins in the deformed nickel. Analysis was made on samples in the annealed, cold-rolled, shock-loaded, and cold-rolled—shock-loaded states. The estimated accuracy of the peak position measurements is *0.01 deg in 2?. Therefore the accuracy in the measurement of the relative peak shifts between the (400) and (222) diffraction line profiles is on the order of *0.04 deg in 2?. None of our measurements indicated peak shifts greater than 0.04 in 28. This would correspond to a fault density of -1 pct and sets the limit on the sensitivity of our instrument. Similarly, analysis of the shift in the center of gravity of the diffraction line profiles yields the minimum measurable value of the twin fault probabilitya to be -0.002. Fig. 1 shows mechanical twinning in nickel shock-loaded to 400 kbar. In this photograph, fault intersections are clearly visible. The thickness of the individual fault lamellae was determined from the image widths of their lines of intersections by the

Jan 1, 1968

By N. A. D. Parlee

THE gas-liquid metal diffusion cell technique1-3 has been used to study the diffusion of nitrogen in Fe-C alloys. The actual apparatus and technique were the same as employed by the authors to study the diffusion of hydrogen in liquid iron.' The diffusion cell' was formed by immersing an alumina tube in a stagnant melt contained in an alumina crucible. The tube (hereafter called absorption tube) contained nitrogen gas at 1 atm and was connected to a sensitive gas-measuring system. The change in the average concentration of nitrogen in the melt in the absorption tube was determined by measuring the rate of absorption of nitrogen in the diffusion cell. Eq. [I], 1-3 derived from the appropriate solution of Fick's second law, was used to examine the data and to calculate chemical diffusion coefficients (D) in situations where the absorption appeared to be controlled by diffusion in the liquid: where V is the stp volume in cu cm, d is the diffusion cell diameter in cm, p, is the density of the melt in g per cu cm, pg is the stp density of nitrogen in g per cu cm, C, is expressed in wt pct, D is in sq cm per sec, and t is in min. According to Eq. [I], a plot of v vs vt should yield a straight line passing through the origin if absorption is controlled by diffusion in the liquid. The slope of this line could be used to determine the value of D under appropriate conditions. As discussed in earlier reports,1,2 the initial thermal expansion of the gas upon immersing the absorption tube distorts the line in the initial stages of a diffusion experiment. However, this is not a serious problem since the slope of V vs 6 plots can be determined from the data points obtained after the initial expansion ceases. The volumes reported on the data plot presented here represent absorption after this thermal expansion ceased. Several preliminary diffusion experiments were attempted with melts of pure iron and with Fe-C alloys containing up to 0.6 pct C. In these cases, no or very little absorption was observed. The only data obtained were for an Fe-C melt which was in addition thoroughly deoxidized by successive hydrogen and vacuum-degassing treatments. These treatments introduced an appreciable amount of aluminum into the melt and reduced its omgen content. The original charge material for this melt contained 0.23 pct s and approximately 0.001 pct &. After repeated hydrogen and vacuum-degassing treatments two diffusion experiments were performed. The analysis of the melt

Jan 1, 1968

By G. R. Leverant

RECENT investigations1,2 of the low-cycle fatigue behavior of pure copper under strain cycling conditions have shown that a unique saturation stress level is eventually attained for each value of applied plastic strain amplitude. The dislocation substructure of copper at the saturation stress level is in the form of cells whose diameter decreases with increasing saturation stress level, i.e., plastic strain amplitude. In addition, both the saturation stress level and the cellular substructure are completely reversible. That is, the saturation stress level and accompanying cell size are determined solely by the present conditions of testing and are, therefore, independent of any previous cyclic history. The mechanical and substructural reversibility observed in pure copper, which has a relatively high stacking fault energy, is not observedz for Cu-7.5A1 which has a much lower stacking fault energy. This implies that easy cross slip (wavy slip) is a prerequisite for reversible fatigue behavior. A dispersion of fine, nondeformable particles of a second phase in a metal matrix tends to stabilize substruc- tures introduced by forming operations during subsequent elevated-temperature heat treatments.3 This raises the question as to whether a finely dispersed second phase can induce an element of irre-versibility into the cyclic deformation behavior of a wavy slip material at room temperature, due to partial stabilization of the initially introduced substructure. Since nickel has a higher stacking fault energy than copper,6 pure nickel should be characterized by cyclic reversibility. Therefore, TD-nickel* (Ni-2ThO.r) was

Jan 1, 1968

By John R. Hutchins

1ms is a report of nickel (wire) oxidation studies designed to test the validity of Valensi's1 equation developed for the kinetics of a reaction controlled by diffusion in a continuously growing product layer on cylindrical surfaces. The equation is:

Jan 1, 1968

By S. F. Bartram, G. A. Chase

COMPUTED X-ray diffraction powder patterns of YNi3, YNi5, and CbBe3 are available on request from either author.

Jan 1, 1968

By Arnulf Muan, R. E. Johnson

Equilibrium CO2 /CO ratios of a gas phase coexisting with selected oxide phase assemblages of the system CaO-"Fe0"-SiOz and vnetallic iron have been determined at 1080°C. The data obtained are used to calculate activity-conzposition relations for metasili-cute, orthosilicate, and CaO- "FeO" solid solutions, and to determine a new value for the free energy of formation of C&S&0,. The metasilicate solution is practically ideal, whereas large deviations from ideality exist in the othe,r two solid solutions. BECAUSE of the geochemical and metallurgical importance of the oxides CaO, "FeO", and SiOz, the system CaO-"FeO"-SiO2 has been the subject of several experimental studies during the past 30 years. Following the delineation of phase relations at liquidus temperatures by a group of investigators at the Geophysical Laboratory of the Carnegie Institution of Washington in 1933,1 Chipman and associates in the early forties2,3 determined activities of FeO in liquids of this system. Since that time, many attempts have been made to interpret the data of Chipman et al. in terms of the constitution of the silicate liquids and the interaction parameters among the various constituents of the system (see for instance papers by Richardson4 and by Flood and coworkers5). One of the assumptions made in some of these interpretations4 is that the binary silicate systems CaSiO3-FeSiO3 and CazSi04-Fe2SiO4 mix ideally in the solid state. The objective of the present study is to provide experimental data on activity-com position relations in solid solutions of the system CaO-"FeO"-SiO2. Such data will contribute toward an understanding of the thermodynamics of silicate solid-solution phases in general, and will serve specifically to confirm or refute some of the assumptions made in interpreting liquid slag behavior. PREVIOUS WORK Phase relations in the system CaO-"FeO"-SiO2 in contact with metallic iron were determined by Bowen, Schairer, and Posnjak,1 and additional phase-equilibrium data for this system have been presented by Allen and snow.' A reproduction of the most up-to-date phase diagram for this system is shown in Fig. 1.7'8 Of particular interest in the present investigation are the relations among the various crystalline phases slightly below the lowest solidus temperature in the system, as shown in Fig. 2. The present work will be concerned primarily with some of the composition

Jan 1, 1968

By A. G. Guy, T. B. Lindemer

A second intepation of the Fick law has been developed and applied to three-place data generated from the Gosting and Fujita solution of the diffusion equation. This integration provides new mathematical techniques for the analysis of experimental data. Through use of the synthetic data it is shown that for concentration-independent interdifiusion coefficients these techniques permit a more accurate determination of the coefficients than does the usual Boltzmann-Alatano analysis. Another technique, applicable to the most general concentration-dependent diffusion coefficients , can be used to determine whether given sets of coefficients are consistent with the experimental ternary concentration-distance curves. DURING the past 10 years the subject of three-component diffusion has advanced from the stage of a laboratory curiosity to the status of an accepted portion of physical metallurgy.1 In the course of this development the underlying treatment for two-component sys- tems was extended and generalized to accommodate the added component, but fundamentally the analyses currently employed for ternary systems are analogous to those previously developed for binary systems. There are several indications that an improved analysis is needed for the ternary case. First, the two cross coefficients, D312 and D321 are typically an order of magnitude smaller than the direct coefficients and consequently are difficult to determine with adequate precision. Second, instead of a single concentration-penetration curve (as in binary diffusion), there are four such curves in the usual determination of ternary diffusion coefficients. These curves have definite theoretical interrelationships, but actual experimental curves exhibit significant departures from these relationships. Finally, the amount of data needed to adequately describe the diffusion behavior of a ternary system is so large that radically new methods are needed to facilitate the gathering of these data. ICirkaldy2j4 has proposed several possible analyses of ternary diffusion data, including some of the methods in current use. A "second-integration" procedure proposed by him4 differed in important respects from that presented here and was not carried to the point of application. Two other methods have been explored by the authors and will be published separately; these are a numerical analysis technique and a method for the analysis of a single ternary diffusion couple. Still other analyses are being explored by various investigators. At present it seems likely that the final analysis of ternary diffusion that evolves will be a composite

Jan 1, 1968

By Victor A. Phillips

A series of strips of a Ni-12.7 at. pct A1 alloy were Prepared containing cubical y'(NisAl) precipitates with edge lengths from 60 to 500A. A particle-free solution-tveated strip was included for cornparison. They weve cold-rolled 95 pct and the effects of particle size on the isochronal (1/2 hr) annealing behavior between 300° and 950°C studied (by hardness and light and electron microscopy). It ulas inferred that the particles deformed with the lnatvix becoming lamellae which remained coherent. Comparison with published data fov pure nickel showed that aluminum greatly re-tavded softening and recrystallization, but it made little difference whether or not particles were present. The presence of pakticles led to a heterogeneous distribution of precipitates after annealing at 700" to 750°C. Recovery was not detected. Recrystallization occurred by the growth of new grains into unrecrys-tallized material. In a previous study by the author,' the growth of Ll2-type ordered yl(Ni3Al) precipitates was followed in Ni-12.7 at. pct A1 alloy as a function of aging at 600" and 700°C. The particles were showo to be cubical in shape in all sizes from 50 to 3000A and remained coherent. This work was used as a guide in preparing the starting structures for the present study of the effect of these particles on the annealing behavior of heavily cold-rolled strip. Another question of present interest was whether dislocation and particle hardening were additive, since the structures before rolling ranged from solution-treated to peak-aged to overaged. Also, precipitation might occur on annealing after cold-rolling. Reference may be made to other papers2"5 for previous work in this relatively unexplored field and only some recent work will be mentioned her:. phillips2 studied the effect of deformable 0 to 590A-diam cobalt particles on a Cu-3.23 pct Co alloy rolled 95 pct and found that the particles, which rolled out into thin lamellae, impeded softening and recrystallization. Tanner and servi3 likewise studied the annealing of cold-swaged Cu-2 pct Co alloy containing 150A-diam particles and found impeding effects. Haessner et a1.,4 on the other hand, found that incoherent 2-p-diam non-deformable particles of B4C (0.04 vol pct) tended to increase the rate of recrystallization of copper rolled up to 95 pct reduction. They attributed this to the formation of new grains at the particle interfaces. Humphreys and artin' found that nondeformable silica particles in copper rolled to 30 pct reduction accelerated recrystallization if the particle spacing was large and retarded it if the spacing was smaller. Haessner et a1 4 also studied a rolled Ni-Cr-A1 alloy; however, the particles of y'(Ni3Al)-type precipitate were not put in before rolling, but separated during the isothermal annealing at 750°C. No previous work appears to have been carried out on the effect of y' (Ni3A1) particles on the annealing of Ni-A1 alloy. Hornbogen and ICreye7 redetermined the solubility c of aluminum in nickel as a function of temperature T and showed that it was given by c = 32.6 exp(-1940/RT). This relation gives aluminum solubilities of 15.1, 14.2, 12.0, and 10.7 at. pct at 1000°, 900°, 700°, and 600°C, respectively. The phase precipitated from the nickel-rich solid solution is fcc y1 (Ni3A1) which has a Cu3Au -type ordered structure8 and remains ordered up to 1000°C.B EXPERIMENTAL PROCEDURE The alloy used was identical with that used before. Chemical analysis showed 6.27 wt pct (12.71 at. pct) Al, the principle impurities being 0.065 pct Fe, 0.022 pct Co, 0.020 pct Cu, and 0.004 pct C. Bar stock of 1 in. diam was cold-swaged to % in. diam, cold-rolled to 0.300-in.-thick strip, and annealed at 900°C in dry hydrogen. It was cold-rolled to 0.100-in. thickness and solution-treated for 1 hr at 1000°C while sealed in a quartz tube in argon, quenching in iced brine with the aid of a device to snap off the nose of the tube. Lineal analysis gave an average grain size of 0.055 mm. Pieces of strip were aged at 700°C in vacuo for 30 min, 51/4 hr, and 1 week to produce nominal average particle widths of 60, 150, and 500A, respectively, as known from the previous work.' The average diamond pyramid hardness was determined. The heat-treated strips were rolled from 0.100 to 0.005 in., a reduction of 95 pct, and the rolled strips stored at about -5°C. Small pieces were annealed within 1 week for 30 min at temperatures from 300° to 950° ±2°C in a horizontal vacuum furnace. Strips were withdrawn into a cooling zone, giving an estimated initial cooling rate from 950°C of about 50°C per sec. Average diamond pyramid hardnesses were determined on a lightly electropolished spot on the surface of each strip using 300-g load. Each point on the softening curves represents a separate annealed specimen. Sections containing the rolling direction were examined by optical metallography. Selected specimens were electrothinned to the center plane' and examined by transmission at 100 kv in a Siemens Elmiskop I electron microscope. It is well-known that changes in the structure tend to occur when a deformed strip is electrothinned below a thickness of a few hundred angstroms, although this is less serious with a material such as nickel which has a high melting point, and also is apt to be less serious when particles are present. Observations were nevertheless confined to thicker regions of the foils with estimated thicknesses over 1000A. No changes were observed due to beam exposure.

Jan 1, 1968

By John L. Walter

A sintered compact of iron containing 0.007 vol fraction of glass , prepared 6). powder rnetullurgtcal lechniques, was rolled lo foil, 0.001 in. /hick. The foil sullrples were anneuled a1 650° to 850°C in hydrogen. Pri,narj recryslullization prodtnced large grains which Lc3ere highly elongnled in the rolling direclion und which had an unusual prgferred orientation. The glass parlicles assumed a stringerlike dispersiorz on working; llie slrinyers were parallel lo the rolling direction and to the long axis of the grains. The same unusual grain structure, preferred orientation, and stringerlike dispersion of purticles are found in heal-ily rolled and annealed foil of tungsten which has heen doped wilh small amounts of aluminum, silicon, and polassiutvt. Both the proper dispersion of the particles and severe working (reductions in excess of 98 pct) are necessary to produce the elongzcted grain structure. RECENTLY, the author reported on the origin of the elongated or "nonsag" grain structure in tungsten foil which was doped with aluminum, silicon, and potassium.' It was observed that particles, identified as mullite (Al6Si2Ol3), were present in the doped ingot (as sintered) and at all stages of processing from ingot to sheet or wire. It was shown that the particles, being plastic at tungsten working temperatures (up to 1550"C), underwent a "stringing out" parallel to the working di-direction. It was concluded that these strings of particles were responsible for the formation of the highly elongated interlocking grains observed in doped tungsten wire or sheet. To give further credence to this explanation of a long-observed but not understood phenomenon, it was decided to design a new system, one which was analogous to the doped-tungsten system. Thus, a bcc metal, iron, was chosen to be doped with glass which would be plastic at reasonable working temperatures for iron. The glass chosen was a #0080 Corning lime glass which melts at about 810°C. This is approximately the same fraction of the melting point of iron (0.6) as the melting temperature of mullite is of tungsten. It will be shown that all the observed unusual features of the doped tungsten are duplicated in the glass. doped iron, even to the preferred orientation of the grains in the recrystallized sheet. In the tungsten sheet the preferred orientation consists of two components, (1i3)(691) and (013)(362), neither of which has been observed as a component in textures of primary recrystallized bcc metals. EXPERIMENTAL PROCEDURE The glass, in the form of fine powder, was added to high-purity electrolytic iron powder and mixed dry. The particular composition chosen was 0.007 vol fraction of glass. After mixing, the powder was mechanically pressed to a disk 0.5 in. diam and 0.15 in. thick at a pressure of 5000 psi. The pellet was sintered, in pure dry hydrogen, for 2 hr at 8 50°C. The sintered pellet was then heated to 750°C and rolled to 50 pct reduction of thickness in two passes, with reheating between passes. The rolling temperature was then reduced to 600°C and the slab was rolled to a thickness of 0.050 in. Rolling to 0.010 in. was accomplished in several passes at 300°C. Final reductions to 0.003 and 0.001 in. were taken at room temperature. This rolling temperature schedule was similar, in terms of the fraction of the melting point, to that used in the rolling of the doped tungsten. The total reduction of thickness was in excess of 99 pct. Samples of the rolled foil were lightly electro-polished and annealed for 1 to 6 hr at temperatures of 650" to 85O°C in hydrogen. Samples for transmission electron microscopy were thinned on a Disa Electropol using AC-1 electrolyte.

Jan 1, 1968

By L. C. Brown, E. B. Hawbolt

The formation of grain boundary precipitates has been studied in Ag-5.64 wt pcl Al alloys at 688°C. Large-grain specinzerzs were used and the boundary misorientation measured by X-ray diffraction. At low-angle grain boundrrries Primary sideplates form. u)hile abore a 17-deg misorientation lenticular precipitates predominate. Growth of the lenticular precipitates was studied on individual grain boundaries using a statistical technique. The thickening and lengthening rates appeared to be independent of &apos;pain boundary misorientation, indicating that grain boundary diffusion was not significant in this system. The precipitates grew urith constant shape, with both the length and thickness increasing parabolically with time. The parabolic lengthening rates were unexpected since previous theory and experimerztal results had indicated linear growth. By approximating the shape of the precipitate to that of an oblate spheroid grouling with constant shape an equivalent diffusion coefficienl was calculated. The zlalue obtained was in good agreement with nleasurements obtained fron, diffusiorz couples. IF a single-phase alloy is heated or cooled to a temperature such that the phase becomes supersaturated, there is a tendency for a second phase to precipitate from it in order to remove the supersaturation. Precipitation takes place initially on grain boundaries due to preferred heterogeneous nucleation, but subsequently Widmans kitten plates may form in the grain interiors if the grain size and supersaturation are sufficient. The type of grain boundary precipitate formed depends on the nature of the boundary. Aaronson1 and clark2 have shown that grain boundary misorientation can be characterized by the simple parameter R, where and X, Y, and Z represent the minimum rotations about three orthogonal axes required to bring the two lattices forming the grain boundary into coincidence. The maximum value for R is 60 deg. In using this parameter the orientation of the grain boundary itself is, of course, neglected. However it was found in both Fe-si3 and A1-Ag2 that the precipitate shape depended only on the parameter R. Clark found that the vast majority of precipitates formed were allo-triomorphs— lens-shaped precipitates that grew along the grain boundaries. At low-angle boundaries, however, (R < 15 deg) Widmanstatten sideplates nucleated at the grain boundaries and grew into the adjacent grains. It has been reported that the rate of growth of grain boundary precipitates is controlled by diffusion within the supersaturated phase.&apos; The theories which have been developed for growth rates have assumed the diffusion coefficient constant over the composition range of the supersaturated phase. This is a fairly good approximation if the composition range involved is not large. Thickening rates have been calculated using the theory developed by Zener4 and by Frank5 for the growth of planar precipitates. A parabolic growth law

Jan 1, 1968

By Frank Woolley, John F. Elliott

The high-temperatzrre solulion calorimeter has been modified and an extension dynamic analysis of i/s transient behavior has provided an improved basis for interpretation of the experimental data. The partial molar heats of mixing, Him, of aluminum, copper, and silicon in the corresponding binary liquid-iron alloys haz,e been measured directly at 1600°C. The resulls in kcal per g-alom are: THE high-temperature1,2 solution calorimeter was planned and designed to obtain directly the partial molar heat of solution of solute elements in a variety of liquid metals that might serve as solvents. Results obtained in the temperature range of 1000° to 1200°C were described in the two earlier publications. However, a long-term goal in the program has been to obtain measurements at 1600°C of the heats of solution of elements in liquid iron. Hence, subsequent to the work last reported,2 and based on the experience of the first two studies, the calorimeter system has been modified and operated at 1600°C to obtain measurements on the Fe-Si, Fe-A1, and Fe-Cu systems. This paper reports the results of the work. THE MODIFIED SYSTEM It was clear from the earlier results that the most precise measurements can be obtained with the high-temperature solution calorimeter when the solution time is less than approximately 30 sec. This can be achieved only when the bath temperature, Tb, is above the melting (liquidus) temperature of the solute material being dropped. A second point of importance is that the refractories used earlier liberated considerable water so that, although the oxygen potential of the atmosphere in the system was satisfactory for work with nickel and copper, it was too high for work with iron, silicon, and so forth. Third, for work at 1550" to 1650°C, an improved temperature-sensing unit is needed. The modified calorimeter in its latest form is shown schematically in Fig. 1. The refractory brick and the Kanthal-Super heating elements which formed the furnace for heating the solute addition have been replaced by a smaller resistance-heated tube furnace which is insulated with bubble-grain alumina. A more elaborate gas purification system was installed to maintain a satisfactorily low oxygen potential in the atmosphere of the calorinieter chamber and of the solute addition furnace. As was the case in the earlier work, at the beginning of a run the calorimeter chamber is evacuated and then filled with purified argon so that a total pressure slightly in excess of 1 atm is maintained during the run. When either of the furnaces within the enclosure attains a red heat, 6 pct H2 is added to the atmosphere. Throughout the run, gas from the calorimeter is circulated through a de-oxidation system at the rate of approximately 5 standard liters per min; the changeover time for the gas within the calorimeter enclosure is approximately 1 hr. The essential stages of the deoxidation system are: a copper furnace at 600°C, a drying tube of anhydrite, and a titanium furnace at 800°C. The oxygen potential of the gas stream in the purification system can be monitored at several points by a stabilized zirconia oxygen cell. This cell is invaluable in detecting the development of leaks in the container vessel and the gas circulating system. The installation of the solute-addition furnace allowed either of two types of temperature-sensing units to be mounted on a water-cooled probe. The first was a small optical device using a silicon diode that was

Jan 1, 1968

By J. C. Scully, G. Sanderson

The electrolytic formation of y hydride in thin foils of Ti-5Al-Z.5Sn alloy and four Ti-A1 binary alloys has been studied by electron microscopy and electron diffraction. Two orientation relationships have been found: THE adsorption of hydrogen by titanium alloys from aqueous solutions has been widely reported. This can occur, for example, in both alkaline&apos; and acidic2 pickling baths, in chemical polishing374 and electro-polishing Solutions,3,4 during cathodic polarization5" and under certain corrosion conditions,7,8 Etching reagents may also produce visible precipitates, sometimes after an aging period.9 During an investigation into the stress corrosion susceptibility of a titanium alloys by thin foil electron microscopy many observations have been made of hydride precipitation which has been deliberately promoted by techniques that are described below. The characteristics of hydride precipitation are reported and the observed crystallographic orientation relationships are discussed with reference to distortion in the titanium lattice created by the presence of the hydride. EXPERIMENTAL TECHNIQUE One grade of commercial titanium and five alloys were examined. Their composition and hardness values are shown in Table I. All the materials were in the form of thin sheet, 0.05 to 0.065 cm thick, which had been annealed after cold rolling. Foils suitable for transmission electron microscopy were made in two ways: a) by chemical polishing; and b) by elec-tropolishing. The solution used for chemical polishing was a mixture of 44 pct HF and 73 pct HNO3 in the volumetric ratio 2:3. During this polishing specimens were manually moved up and down in the solution. The reaction was veFy rapid, specimens thinning to foil thickness (2000A) in 5 min. Since chemical polishing solutions tend not to cause hydride contamination if they are kept cool3 no attempt was made to prevent the solution from becoming hot during the thinning operation. Electropolishing was performed at -30° C with a mixture3 composed of 295 cu cm methyl alcohol, 175 cu cm n-butyl alcohol, and 30 cu cm perchloric acid with an applied voltage of 40 v after chemically thinning specimens to approximately 0.017 cm thickness in a cool solution of 44 pct HF, 40 vol H2O2, and water in the volumetric ratio 1:6:3. EXPERIMENTAL RESULTS 1) Ti-5A1-2.5Sn Alloy. The Ti-5A1-2.5Sn alloy was severely contaminated by hydrogen during the chemical polishing. Foils obtained in this way contained large amounts of the y hydride phase. A typical micrograph is shown in Fig. l. The laths were identified as the hydride phase by selected-area diffraction of a large number of foils examined in a tilting stage that could be turned through 40 deg. Using the lattice spac-ings of the alloy obtained by X-ray diffraction as a standard the a value of the hydride was determined fromo the electron diffraction patterns to be 4.38 to 4.40A. The accuracy of this figure is only about ±2 pct. Further evidence of the identification was obtained by vacuum annealing chemically polished foils of the alloy at 500°C. This resulted in the dissociation of the hydride with the production of dislocations and possibly vacancy loops as shown in Fig. 2. The hydride

Jan 1, 1968

By E. A. von Hahn, T. R. lngraham

Cementation rates ulere studied by rotating an elec-tropolished or etched copper strip in aqueous solutions, of either perchloric acid or alkaline cyanide, containing silver ions. The rates of cementation were more rapid in acidic media than in cyanide media. In both, the rates varied with the rate of rotation of the copper strip. The deposits formed in the acidic solutions were finely divided, loosely adhering powders. Those formed in the cyanide solutions were dense and adherent. The presence of the deposits influenced the cementation rates. In the acidic solutions the rate was enhanced, possibly because of the increased cathodic area. In the alkaline solutions the rates were decreased in the presence of the deposits. This has been attributed to restricting the diffusion of the copper ion from the rnetal outward into the bulk of the solution. In an earlier paper1 the authors described a kinetic study of the cementation of palladium on copper in perchloric acid solutions. That work indicated that there were two stages in the palladium cementation process. The first, more rapid stage was consistent with rate control by the diffusion of Pd11 ions to the copper surface and/or by chemical reaction at the surface. The second stage was consistent with rate control by the diffusion of copper ions from the copper surface, through the deposit, out into the main body of solution. The effect of the type of deposit on the rate of cementation is of particular interest because it may be one of the primary features involved when large quantities of metal are to be cemented from solution. No substantial investigations of the effect seem to have been made. Accordingly, an extension of the previous work was arranged to study the cementation of silver on copper. This system was selected because of the convenience of the analytical methods, the previously established technology with copper, and the fact that the system could be studied in both acidic and alkaline media. By selecting perchloric acid and alkaline cyanide solutions as the media, it was hoped that some assessment might be made of the effects, on cementation, of having the silver ion present in a virtually uncomplexed state and in a highly complexed state. EXPERIMENTAL The cementation rates were studied, as previously described,&apos; by rotating a copper strip (1.0 by 23.2 cm) clamped to the peripheral surface of a lucite cylinder. The solutions were kept at constant temperatures (±0.05°C) under an atmosphere of purified nitrogen, and samples were taken periodically for analysis. The initial solution volume was 1000 ml and the sample volume 5 ml. The initial silver(1) ion concentrations were made low (0.5 to 1.0 x 10-4 moles per liter) to minimize the influence of the cemented deposit on rates. The solutions were prepared by dilution of suitable aliquots of silver perchlorate and silver cyanide stock solutions. Both stock solutions were prepared from purified silver powder (Johnson, Matthey, and Mallory Ltd.) with redistilled deoxygenated water, and they were kept under an atmosphere of purified nitrogen. To prepare the stock solutions, weighed amounts of silver powder were dissolved with nitric acid. For the AgC104 stock solution the silver nitrate solution was evaporated twice to near dryness with perchloric acid and then made up to volume: For the NaAg(cN)2 stock solution, the silver ions were precipitated with sodium hydroxide solution. The precipitate was filtered, washed thoroughly with redistilled water, dissolved with 1.1 times the required stoichiometric amount of sodium cyanide solution, and made up to volume. The small amounts of free perchloric acid and sodium cyanide present in the stock solutions were disregarded in the preparation of the solutions. The copper strips were cut accurately from 0.025-in. sheet (American Metal Climax OFHC brand) and annealed for 1.5 hr at 470°C in a stream of nitrogen. Analyses of the solution samples for silver and copper were done with a Techtron Model AA-3 atomic absorption spectrophotometer. Calibration standards of the same composition as the experimental solutions were prepared and analyzed simultaneously with the samples. No difficulty was experienced in the analyses, and the reproducibility was within 1 to 2 pct in both alkaline cyanide and perchloric acid solutions.

Jan 1, 1968

By G. R. Heckman, H. J. Murphy, C. T. Sims

An incestigation has been made of the effects of heat treatment and alloy composition on the long-time stress-rupture properties and structural stability of the similar nickel-base alloys Udimet-500, Lrdimet-520, and Udimet-700. Rupture test data are presented at stresses ranging from 4 to 50 ksi at temperatures from 1450° to 1900°F for times up to 14,000 hr. Ductility response is emphasized. Optical and electron tnicroscopy were complemented by X-ray diffraction analyses of extracted phases to relate microstructural stability to the observed rupture properties. Particular attention is paid to Udimet-520 since structural characteristics of this alloy appear to vary somewhat from its sister alloys. Both cast and wrought performance of Lrdimet-500 are discussed. The computerized PHACOMP calculational technique, based on electron-vacuncy theory, is discussed and related to structural stability where appropriate. Electron microscopy and microprobe techniques were used to conduct evaluation of the oxidation characteristics of Udimet-500 exposed in air for 16,100 hr. The steady advance in strength and reliability of nickel-base superalloys continues to be one of the high points of modern metallurgy. The stress capability of these materials has increased steadily, allowing higher and higher operating temperatures in the highly sophisticated aircraft and industrial gas turbines now on the market. The attendant increase in efficiency, of course, means greatly improved power output. Gas turbines for industrial and marine use have long been designed with these objectives paramount the usual design requirements in terms of time of service being 100,000 hr. High-efficiency, long-life aircraft such as the supersonic transport require superalloy engine materials with high-strength and long-time structural stability. Thus, materials studied for and operating experience from industrial gas turbines provide a good reservoir from which technology of high value to the SST program can be drawn. This study is one such case. Three prominent nickel-base super alloys—Udimet 500, Udimet 520, and Udimet 700 were extensively evaluated for industrial gas turbine bucket use. Particular attention was directed toward structural stability as a requisite property. Within the present context, structural stability is defined as freedom from the propensity to form strength-robbing or embrittling phases such as u,p,x,or Laves, and the ability to maintain useful rupture strength and ductility throughout design life. MATERIALS The three alloys, cast Udimet 500 (U-500C), Udimet 520, and Udimet 700, were chosen for detailed evaluation based on preliminary studies which indicated that U-500C and U-520 possessed comparable rupture strength capabilities, and that U -700 had a greater strength capability but somewhat poorer ductility than wrought U-500. The nominal compositions of the three alloys, along with the compositions of the heats investigated, are presented in Table I. PROCEDURE Dimensionally rejected U-520 buckets from Special Metals Corp. heat 63370 were heat-treated using the four cycles delineated in Table 11. Cycle A was investigated to determine the effects of a shortened 1700°F primary age. Cycle B was considered a "standard" treatment. Cycle C investigated a higher solution temperature in combination with a shortened primary age, while cycle D assessed the effect of the higher solution temperature alone. These heat treatments were designed to produce optimum combinations of rupture strength and ductility through maximum y&apos; development, the development of a y&apos; grain boundary cushion, promotion of MC carbide degeneration reactions, and agglomeration of resultant M23CB. Since one of the premises of the evaluation of U-520 was that rupture strength would be equivalent to U-500, forged U-500 buckets from Special Metals Corp. heat 62916 were heat-treated with cycles A, B, and C to provide comparison. The heat-treated structures of U-520 and U-500 are illustrated in the 8700 times electron micrographs of Fig. l. The U-700 tested was all from 3-in.-diam hot-rolled and centerless-ground rod from Special Metals Corp. heat 2-1426. Two heat-treatment cycles were employed, E and F of Table 11. Cycle E is a standard four-step, triple-age treatment intended to provide an optimum match of strength and ductility through well-developed matrix and grain boundary y&apos;, as recommended by U-700 vendors. Treatment F is a shortened , single-age cycle which could provide a significant processing cost reduction should adequate strength and ductility be maintained. Following heat treatment, rupture specimens of U-500 and U-520 were machined from the buckets and tested. Standard rupture bars of U -700 were machined from the heat-treated rod and rupture-tested. Failed and withdrawn rupture bars were prepared and examined by optical and electron microscopy. Select specimens were electrolytically digested, and the residues analyzed for carbide and topologically close-packed phases using CrKa or CoKo radiation. Of the six different U-500C heats evaluated, five were cast by Misco Precision Casting Co. and one was cast by Haynes Stellite Co. Cast-to-size rupture bars

Jan 1, 1968

By D. T. Peters

To better understand the Co-Mo interaction in maraging steels, the precipitate reversion behavior of two alloys closely related to the 18 Ni-250 grade has been studied. The reversion experiment is carried out by aging at a low temperature, T1 (preaging temperature), for some period of time and then aging at a higher temperature, T2, called the reversion tetnperature. Aging and reversion tmzperatures used were in the range 679 to 1050°F. Reversion is marked by an increase in resistivity and a decrease in hardness. It teas found that some reversion took place at all cornbinations of T1 and T2 but that pronounced rei3ersion resulfed for an Fe-18 pct Ni-5 pct Mo-8 pcl Co alloy exposed to preagz&apos;ng&apos; temperatures at or below 850°F. A similar alloy not containing cobalt exhibited no such discontinuity in reversion behazior with TI. The results are interpreted in terms of two types of molybdenum-rich precipitates, one nucleated at dislocations and the other in the matrix. The increased supersaturation resulting from the presence oj- cobalt evidently provides sufficient energy to nucleate the matrix phase. Anotnalies in the temperature dependence of the resistivity decrease and peak hurdness in the Fe-18 pct Ni-5 pct Mo-8 pct Co alloy as a junction of aging temperature noted in an earlier study are explained on this basis. SEVERAL investigatorsl-9 have studied the details of the precipitation-hardening reaction of the maraging steels. The great majority of conclusions have been drawn from transmission electron microscopy. Although much has been learned by this method, alternate techniques which will give information earlier in the aging process are needed for a more complete understanding of the series of precipitation steps probably involved in the aging reaction. Peters and cupp&apos;&apos; have recently shown, by measurements of the kinetics of precipitation, that an 18 pct Ni-Co-Mo maraging steel shows a distinct change in precipitation behavior at aging temperatures below 850°F. The results were interpreted in terms of the existence of two types of precipitates at low aging temperatures. Only one precipitate type is present at higher aging temperatures. The low-temperature precipitate was found to be a particularly effective strengthener. No evidence for the additional low-temperature precipitate was found in the 18 pct Ni-5 pct Mo ternary alloy. The object of this investigation was to study further the characteristics of the two types of precipitates and the interaction between cobalt and molybdenum characterizing this system. Some preliminary experiments indicated a difference in reversion behavior in specimens aged above and below 850°F. This suggested that knowledge of the reversion behavior might shed some light on these two questions. Hardy and Heal11 have defined reversion as the loss of hardness, electrical conductivity, or other properties caused by heating for a very short time at temperatures above the aging temperature. The precipitate reversion referred to in this paper is entirely distinct from "austenite reversion" often referred to in maraging steel literature. This latter phenomenon could more accurately be called the diffusion-controlled formation of austenite. Much has been written about reversion in several of the aluminum-base binary and ternary alloys.&apos;2-16 Two explanations for reversion have been advanced. Based on the classical nucleation theory of Volmer-Weber-Becker-Doring,17 Konobeevski18 suggested that reversion was due to the size of the precipitate particles

Jan 1, 1968

Jan 1, 1968

By R. H. Tien

This paper presents an analytical solution of the problem of freezing of a semi-infinite slab with constant surface temperature; in this analysis accoz~nt is taken of the heat evolution during the solid-state transformations in the frozen skin. The regions where transformations occur are treated as plane isothermal heat sources; i.e., the rates of transformations are assumed to be infinite. In the model considered, three plane heat sources are assumed to be present in the frozen solid. The solution yields the temperature distribution in the solid, the rates of movement of the heat sources , and the rate of movement of the solidification front. It is shown that, although the sum of the heats of transformations in the solid is about 20 or 43 pct of the heat of fusion of iron or manganese, respectively, the effect of the heat evolution in solid-state transformations on the rate of solidification is insignzficant. IN several recent mathematical studies of solidification of liquid metals&apos;-3 no account was taken of the heat evolution accompanying the solid-state transformations. In the case of, for example, steel, there are several phase transformations 6 -y, y -a, and the magnetic transformation. Whether or not a significant error is introduced into the mathematical simulation of solidification processes by the omission of the heat effects associated with these phase transformations is not known. The purpose of the present study is to investigate the effect of these phase transformations on the temperature distribution and the rate of solidification based solely on the heat transfer point of view. That is, for the sake of simplicity, freezing of a pure metal with solid-state transformations will be considered. The mathematical model which represents the present problem includes four moving heat sources representing freezing and phase transformations, 6— y — a — ferromagnetic. The thermal properties such as conductivity and specific heat, and so forth, are different from one phase to the other. But they are considered to be uniform over any particular phase. The usual Fourier heat flow law is employed. The concept of conservation of energy is applied at every heat source in order to estimate their rate of movement. The temperature distribution in the solid and the positions where transformations occur are expressed analytically in terms of error function solutions and four coefficients which are determined from four nonlinear algebraic equations. These coefficients can be calculated either by trial and error or by any numerical method. MATHEMATICAL ANALYSIS Fig. 1 is a schematic diagram showing the zones of different phases 1, 2, 3, and 4 in the solidified portion of a semi-infinite pure liquid metal. The heat is subtracted from the system at x = 0 which is maintained

Jan 1, 1968

By Robert Maes, Robert de Strycker

The Fe-Ni-As phase diagram has been established by the study of about a hundred alloys, by microscopic observation, and by thermal analysis, with arsenic contents up to 50 pct. The iron and nickel arsenides present extensive solid-solution fields, owing to the substitution of nickel by iron and vice versa; the extent of the solubility field of each compound has been determined with an accuracy of ±1 pct. In the investigated range of compositions, the solidification reactions were established, and the temperatures of the invariant reaclions detevmined with a preciston of iZ°C in the most favorable and ±5°C in the least favorable cases. The isothermal lines of the liquidus surface have also been drazum, with an accuracy estimated at i5°C. Reactions in the solid state, which take place for the formation or the decomposition of certain phases , were investigated in detail. ThE constitution diagram of the Fe-Ni-As system is fundamental for the understanding of the properties of nickel speiss; these by-products of the extraction of certain nonferrous metals indeed often contain the three elements iron, nickel, and arsenic as main constituents. The Fe-Ni-As system has already been the object of earlier investigations. In 1932, Guertler and Savels-berg&apos; have presented some elements of the ternary phase diagram, for arsenic contents up to 55 pct (all percentages in this paper are given in weight percent), including the vertical section FezAs-Ni&s2. This investigation is, however, incomplete and certain anomalies suggested the necessity to verify the results published by these authors: the section Fe2As-Ni5AsZ, for example, is presented as quasi-binary, with a field of complete miscibility in the solid state, even though these compounds do not have the same structure. Recently, ~useck&apos; established an isothermal section at 800°C in the Fe-Ni-As system by X-ray diffraction and microscopic examination of water-quenched alloys. These techniques are sometimes inaccurate for the determination of the fields where alloys are liquid at the investigated temperature, and they may lead to erroneous conclusions when a compound exists at the investigated temperature but is not stable at room temperature and cannot be maintained by quenching. LIMITING BINARY PHASE DIAGRAMS The Fe-As constitution diagram has been the object of several investigations which have been reviewed by Hansen and Anderko.3 For the Ni-As phase diagram, a recent study has been effected by Yund.4 In this system, Heyding and calvert5 have determined the existence of a compound of unidentified structure at arsenic contents slightly higher than those corresponding to Ni5As2 and at temperatures lower than about 200°C; by analogy with iron and cobalt arsenides, this compound could correspond to the formula Ni2As, as suggested by Kulle-rud; although this is not definitely established. In the region of arsenic contents from 35 to 55 pct, Fried-rich7 detected anomalies in the solidification reactions; an interpretation of these anomalies was given by Hansen ,8 which assumed that the solidification reactions in practice are not in equilibrium, but are meta-stable. The main features of the Fe-Ni constitution diagram are the existence of a complete miscibility field, at least at high temperatures, for the fcc phase (which will be designated by My in the remainder of this work) and of a limited solubility field for the bcc phase (designated by Ma). EXPERIMENTAL METHODS The fundamental technique used in this investigation was microscopic observation, which allowed the determination of the reactions occurring during solidification of the alloys, and possible reactions in the solid state.

Jan 1, 1968