By L. S. Castleman, R. K. Hotzler

We are currently studying the effects on recrys-tallization of impurities diffused into dispersion-hardened alloys. Our interest in this phenomenon was originally aroused by the observation that the recrystallization temperature range of tungsten "doped" with alumina and silica, or with thoria, is lowered drastically if nickel is plated onto the tungsten prior to heat treatment.' In this note, we report a similar effect that sulfur has on the recrystallization behavior of thoriated nickel. The experimental procedure for this exploratory phase of the investigation has consisted simply in heating commercially obtained stress-relieved samples of thoriated nickel for varying temperatures and times in sealed capsules containing air and small quantities of sulfur. The samples contain 2.4 vol pct thoria and initially less than 18 ppm S by weight; they are prepared either from 0.5-in.-ciiam rod stock or from 0.092-in. sheet and are in the "as-received" (stress-relieved) condition prior to exposure. In an atmosphere free of sulfur, such samples do not show evidence of recrystallization after being annealed for 1 hr at a temperature of 2500°F (1372C).2 The photomicrograph in Fig. 1 shows the microstructure of one of our samples annealed for 75 hr at 1000° C (1832°F) in a sulfur-free capsule. The grain structure is hardly evident (if at all) at 465 times magnification. In contrast, the photomicrograph of Fig. 2 shows the recrystallization that has taken place in a sample exposed to sulfur for 5 hr at 1000°C (1832°F). A nickel sulfide phase is visible at the grain boundaries of the light-appearing grains. We have also observed recrystallization to occur in a sample annealed at 600°C (1112°F) for 25 hr. This temperature is below the 637°C (1178°F) eutectic in the Ni-S system. In the latter case, no nickel sulfide phase is evident in the microstructure. Moreover, we have noticed the occur-

Jan 1, 1969

By H. J. Engell, W. Frank, A. Seeger

SWISHER and ~urkdogan' have determined the solubility of oxygen in a iron. They found it to lie between 7 and 10.5 at.-ppm at 881°C. Using earlier work on the permeability of oxygen in bcc iron,' they arrived at the following expression for the diffusion coefficient of oxygen in bcc iron (k = Boltzmann's constant, T = absolute temperature): where The present authors3 have estimated the activation energy QD for the diffusion of oxygen in bcc iron in two different ways from various experimental data.2'4"6 In the first method QD + QS (QS = heat of solution for oxygen in bcc iron in thermodynamic equilibrium with solid FeO) was determined either from data on the reduction of FeO with hydrogen4 or from measurements of the internal oxidation of silicon in a iron.5 Using an estimate of QS from investigations of the oxygen solubility in 6 iron2 (in thermodynamic equilibrium with molten FeO) Q = 0.97 ev or Q~ = 1.06 ev were obtained. From the magnitude of these values it was concluded that oxygen migrates interstitially in bcc iron and that consequently the activation energy QD for diffusion of oxygen has to be identified with the migration energy E~ of the oxygen atoms. Therefore, for a second estimate of QD from the diffusion coefficient of oxygen in 6 iron at 1450" ~,~ we used the theoretical expression:3 (a = length of elementary cube edge, m = mass of interstitially diffusing atom, sM = migration entropy), applicable to diffusion via the octahedral interstices in bcc lattices. Taking sM = 3.8 k (migration entropy of carbon in a iron), one gets Q = 0.90 ev. Hence, in Ref. 3 Q = (0.98 *0.1) ev was proposed as a plausible value for the diffusion energy of oxygen in bcc iron. sM + 9 (9 = solution entropy for oxygen in bcc iron) can be determined from permeability measurements.4 Using the above-mentioned estimate for QS , the following expression for the solubility c (atomic concentration) of oxygen (in thermodynamic equilibrium with solid FeO) in bcc iron was derived: From [4] the solubility of oxygen at 881°C in a iron is calculated to lie between 0.6 and 12 at.-ppm. We see that the solubility determined by Swisher and

Jan 1, 1969

By J. H. Bechtold, R. Kossowsky

1 HE superplastic behavior of the eutectoid A1-78 wt pct Zn alloy has been thoroughly investigated by Back-ofen et al.' The superplastic elongations and the marked resistance to necking were rationalized in terms of high strain rate sensitivity. In a subsequent paper2 superplastic behavior was formulated to show Nabarro-Herring diffusional creep as rate controlling at low strain rates, giving way to a dislocation climb process at higher strain rates. In a paper devoted to an interpretation of superplasticity in two-phase alloys, Packer and sherby3 have included the results of an examination of the structure of an Al-Zn eutectoid specimen before and after superplastic deformation. No significant change in grain size or directionality was observed in the deformed microstructures. This one observation led the authors3 to suggest that con- tinuous recrystallization or grain boundary migration was responsible for superplasticity. The purpose of this note is to report our observations on the superplastic behavior of the Al-Zn eutectoid alloy which differ in certain respects from works previously reported. Following Hayden et al., the results are discussed in terms of dislocation climb as the important factor during superplastic deformation. A heat of nominally high (99.995) purity 22 wt pct A1-78 wt pct Zn was induction-melted and cast into a 0.5 by 6 by 12 in. slab. The slab was heated to 350°C and rolled to 1/8-in.-thick plate. The plate was then cold-rolled to 0.040-in. thickness, annealed at 35OaC, and rolled to the final thickness of 0.020 in.* Speci-

Jan 1, 1969

By A. U. Seybolt

DURING the course of an investigation of hot corrosion of nickel-base superalloys (combination oxidation-sulfidation attack at high temperature), it was considered possible that sulfur might gain entrance to the alloy in part, at least, by diffusion through the scale. Cr203 is nearly always observed as a prominent component of the oxide scale, and hence some experiments were carried out to examine the tracer diffusion of sulfur through Cr203 at 1000° C in the upper temperature range experienced by jet engine blades and vanes. Some hot-pressed Cr203 discs of quite high density were available from an earlier investigation1 on the rate of crf3 migration through Cr203. The Cr203 was 99.3 pct pure and contained -0.06 pct Fe as the largest metallic impurity. Additional data is given in Ref. 1. In this earlier work it was found that the rate of cation diffusion was independent of the atmosphere of thermal equilibration when using nitrogen, argon, or air, and also that the electrical conductivity of the hot-pressed Cr203 compacts was likewise independent of atmosphere in this range, thus indicating that the de-

Jan 1, 1969

By David L. Holt

It is well-established that hydrostatic pressure distribution is hardly achieved during uniaxial compaction of powders. All the previous investigations1-4 give consistent results and this variation is attributed to the die-wall friction. The conclusions are based on measurements of the density of very small portions of the compact. Although the analysis of the density or the strain distribution in the compact is very helpful in obtaining information about the stress distribution within a powder compact, it does not describe the problem from a more fundamental point of view. The densification in metal powder compacts takes place chiefly by plastic deformation (ignoring particle rearrangement) at the points of contact of the powder particles. The onset of yielding and subsequent growth of the contact areas (for spherical powders) take place fixed by a constant stress equal to three times the yield stress in tension or compression,5-7 assuming little or no work hardening. Therefore, by deforming spherical powders in the die and measuring the contact areas on each particle, the load at each contact point can be determined. In the present investigation, this was done by hot-pressing uniform spheres of lead, K-Monel, and sapphire. The details of the experiment have been described elsewhere.' The spheres were studied for the size and the number of contact points on each particle using a specially designed goniometer. It was found that the deformed faces that were approximately normal to the direction of pressing were about 2.2 times larger than those parallel to the direction of pressing. Fig. 1 shows the typical deformed sphere. A detailed study showed that the mean value of the contact areas on each sphere was within 5 pct for all the spheres in the die (ignoring those touching the die walls and the top and bottom of the die).' The spheres touching the die walls and the top and bottom of the die were found to have larger contact areas (8 to 10 pct) which indicates higher pressures in these regions of the compact and thus higher compact densities in these regions. These results show that density distribution calculated from such an experiment will give results consistent with the previous investigators. It is concluded, therefore, that the pressure distribution in the die is better understood by studying contact areas on each particle. 'R. Kamm, M. A. Steinberg, and J. Wulff: Trans. TMS-AIME, 1947, vol. 171, p. 439. 'Pol Duwez and Leo Zwell: I. Metals, 1949, vol. 1, p. 137. 'G. C. Kucynski and I. Zaplatynskyj: Trans. TMS-AIIME, 1956, vol. 206, p. 215. 'R. P. Seelig and J. Wulff: Trans. TMS-AIME, 1946, vol. 166, p. 492. 'H. Hencky: Z. Angew. Math. Mech., 1923, vol. 3, p. 241. "J. Ishlinsky: I. Appl. Math. Mech. USSR, 1944, vol. 8, p. 233. 'D. Tabor: Proc. Roy. Soc. (London), Ser. A, 1948, vol. 192, p. 247. 'Ashok K. Kakar and A. C. D. Chaklader: 1. Appl. Phys., 1967, vol. 38, p. 3223. Superplasticity in 60Zn-40Al David L. Holt THE occurrence of superplasticity in Al-Zn alloys is of interest because of its possible industrial exploitation.' The eutectoid composition (78Zn-22A1) has been the most extensively studied;'-= neck resistant flow and high strain rate sensitivity of flow stress (characteristic of superplasticity) are associated with a micron-size grain conferred on the alloy by an homo-genization and quench.5'6 Compositions away from the eutectoid have received comparatively little attention, especially from the viewpoint of relating the structural

Jan 1, 1969

By J. A. Goebel, S. Rosen

IN the NiAl phase diagram the NiAl (CsC1-type) phase field extends over a large composition range. At elevated temperatures the nickel-rich phase boundary extends to a composition of about 70 at. pct Ni, a value which is within 5 at. pct of the Ni3A1 (Cu 3 Au-type) phase boundary.' At room temperature, however, the maximum nickel content is only about 60 at. pct. Experiments have shown that alloys containing greater than 63 at. pct Ni when quenched from temperatures below 1000°C contain the equilibrium phases NiAl and Ni3A1. On the other hand, when these same alloys are quenched from temperatures above 1000°C and examined microscopically, a typically martensitic decomposition product appears in the microstructure as shown in the micrograph of Fig. 1. The structure of the martensitic phase has been determined by employing powder X-ray diffraction techniques to be an "ordered" AuCu type (Strukturbericht Llo, space group P/4 mmm - DL). The diffraction pattern of this phase differs from that of AuCu in the appearance of superlattice lines. The structure is shown in Fig. 2. The open circles represent nickel atoms and the half-shaded circles represent nickel and aluminum atoms which are randomly distributed. The sites represented by half-shaded circles would be occupied solely by nickel atoms at a stoichiometry of Ni3A1. The alloys used in this investigation were prepared from 99.99 wt pct Al and 99.99 wt pct Ni by arc melting charges of varying compositions in a water-cooled copper hearth using a tungsten electrode in a gettered argon atmosphere. In all cases chemical analysis agreed within $ at. pct with the nominal compositions of the alloys. Annealing treatments were carried out in a vertical resistance furnace through which a stream of argon gas was flowing. Specimens, which were wrapped in tantalum foil, were quenched by allowing the specimens to drop into a bucket containing iced brine. X-ray diffraction patterns were obtained from -325 mesh powder specimens by using a 114.8-mm

Jan 1, 1969

By J. Pinto, F. Galasso

THE current emphasis in preparing boron fibers by reduction of gaseous boron compounds on a resistively heated metal wire substrate has renewed interest in the borides of those metals which have relatively high melting points and are available as fine wires. A knowledge of the structures and properties of the borides, which are formed when boron diffuses into the metal core during boron deposition, can be of assistance in the understanding of the boron fiber formation process and the fiber properties. Many of these borides are well-known and their properties have been measured. However, when an unidentified boride is found in the core, it may be difficult to establish its composition because of the small amount of material available, the preferred orientation effects on the reflections in its X-ray pattern, and the possible overlap of X-ray reflections if several borides are present in the core. For example. the proper indexing of the X-ray pattern of WB4, which was formed in the tungsten substrate core during boron fiber formation, was accomplished only after small single crystals of this boride were grown and X-ray precession investigations were conducted.' This note presents the results of a study of the phases formed in the core when tungsten, tantalum, and molybdenum metal wires were used as substrates in the boron fiber preparation process with particular emphasis on the identification and characterization of a higher boride of molybdenum analogous to WB,. Boron was deposited on resistively heated stationary 0.0012-in.-diam tantalum, tungsten, and molybdenum wires at 1050°C for various times up to 60 sec using boron trichloride and hydrogen as the reactant gases. After 60 sec of boron deposition the fibers were approximately 0.006 in. in diam. Examination of photomicrographs of fiber cross sections showed that the boron had diffused nearly to the center of the tungsten and molybdenum cores in 15 and 30 sec, respectively, and only halfway to the center of the tantalum core in 60 sec. X-ray diffraction photographs of the fibers indicated that it was also after 15 and 30 sec deposition times that the tungsten and molybdenum metal reflections, respectively, had disappeared from the X-ray patterns of the fibers. The patterns of the boron fibers produced using tantalum wire as a substrate showed that amorphous boron, TaB2, and tantalum metal were present after a few seconds deposition time and remained even after deposition times of 60 sec. Until a deposition time of 15 sec was reached, the tungsten substrate fibers contained amorphous boron,273 6WB, W2B5, and WB4 as well as tungsten metal, while the molybdenum substrate fibers contained amorphous boron, MoBa, Mo2B5, and molybdenum metal for deposition times up to 30 sec. Just before the molybdenum metal pattern disappeared, a pattern similar to that of WB, appeared, suggesting that a phase, MOB,, isomorphous with WB,, was present in the fiber. This same pattern was obtained from the product formed by heating a mixture of molybdenum metal and excess boron powder in a boron nitride crucible at 1960°C in an argon atmosphere. As was the case with the WBn pattern, this pattern could best be indexed on the basis of a hexagonal unit cell rather than the tetragonal unit cell Chrktien and Helgorsky reported for ~0~4,~ see Table I. The unit cell parameters for MoB4 were calculated to be a, = 5.214A, co = 6.358A. Assuming the space group P63/mmc and positions5 2M01 in 2b and 2MoII in 2c found for tungsten in WB~,' a logical structure for MOB, was determined using geometrical considerations to place the boron

Jan 1, 1969

By S. K. Tarby, V. S. Robinson III

A number of experimental determinations of the vapor pressure of liquid silver have been reported in the literature. 1-8 This communication presents additional data for the vapor pressure of liquid silver measured in the temperature range of 1450° to 1600°C and summarizes the results of previous investigations. The results reported here were obtained as part of a

Jan 1, 1969

By R. T. DeHoff

A theoretical development is presented which reformulates Fick's first law for diffusion in the solid state. The diffusion flux of component i in a multi-component system, Ji, is related to its local concentration, ci, and local jump frequency, ri : where a is a geometric factor and d is the jump distance. The product, ciri , is defined as the local concentration of atomic jumps for component i. The analog to Fick's second law is also derived. A solution to this equation is presented, which permits the experimental determination of the variation of atom jump frequency with composition in multicomponent systems. HISTORICALLY, the description of diffusion in the solid state has been presumed to be best approached as an application of more general diffusion laws, known as the phenomenological equations. These equations relate the flux, Ji, of the various components, expressed in atoms, grams, or volume, to the driving force involved, expressed as either a compositional or chemical potential gradient, sumption that the flux is simply proportional to the driving force is the foundation of this approach. The phenomenological equations take the form: where the concentration gradients are assumed to be the driving force, and: if the chemical potential gradient is taken as the driving force. The coefficients Dij in Eq. [1.] are the "diffusion coefficients"; the elements of the corresponding matrix in Eq. [2], the Mij, are called the "mobilities". Eqs. [I] and [2] may be considered to be definitions of these phenomenological coefficients. A formidable body of literature has been generated about these equations; this literature dates back to their original formulation for the simplest case of binary diffusion in a fluid, by Adolf Fick, in 1855.' This description has been shown to be self-consistent. However, the "constants of proportionality", the Dij or ,Mij, are not constant: they vary with composition in all but the simplest systems. Even in the case of tracer diffusion, wherein it can be shown that the diffusion coefficient is constant, the mobility, which is considered in irreversible thermodynamics to be the more physically meaningful quantity, varies with the concentration of the tracer involved.' In more complex systems, it is necessary to evaluate the entire matrix of phenomenological coefficients, as a function of composition, in order to describe diffusion locally. Further, in order to determine this matrix experimentally, it is necessary to produce diffusion couples that have different sequences of compositions; the matrix may be evaluated only at points where these "composition paths" cross.* Finally, and perhaps most

Jan 1, 1969

By Klaus Schwerdtfeger, Leo Zwell

The equilibrium between Ir-Fe or Rh-Fe alloys, iron oxide (wüstite or magnetite), and CO2-CO atmospheres has been determined at 1200°C. The data are used to derive the activities in these binary solid solutions. Both systems show negative deviations from Raoult's law. The lattice parameters are given for the investigated Ir-Fe and Rh-Fe alloys. IRIDIUM and iron form a continuous series of fcc solid solutions at elevated temperatures.' Rhodium-rich Rh- Fe alloys have fcc structure.' In the medium concentration range an ordered bcc phase is stable at temperatures up to about 1300°C. Phase relations in iron-rich alloys are not well-known. No thermody-namic data are available for these alloys. EXPERIMENTAL METHOD The experimental method used was to measure the equilibria between a gas phase of known CO2/C0 ratio, the alloy, and iron oxide (wüstite or magnetite). In one series of experiments the alloys of known composition were heated in CO 2-CO gas mixtures. After treatment (usually 1 day) the sample was quenched to room temperature and its surface examined visually to determine whether an oxide tarnish had formed. The procedure was repeated at slightly higher CO 2/CO ratios until the CO 2/CO ratio of incipient oxidation was found. Subsequently, the CO 2/C0 ratio was lowered again in small increments until the tarnish was reduced. In other experiments mixtures of alloy and iron oxide powders were pressed into pellets and equilibrated with the CO2-CO gas phase. In order to ensure that equilibrium was attained, two specimens with different starting iron content were heated side by side; in most cases, equilibrium was approached in one pellet by reduction of iron oxide and in the other pellet by oxidation of metallic iron. The sample was quenched to room temperature, and the composition of the equilibrated alloy was determined by X-ray measurements of lattice parameters and comparison of these values with calibration curves obtained from alloys of known composition. The oxides present in the specimens were identified by comparison of their diffraction patterns with those in the ASTM Card File. It may be expected from the noble character of iridium and rhodium that no appreciable amount of iridium or rhodium is dissolved in wiistite and magnetite under the present experimental conditions. The activity of iron in the alloy is then equal to that established in the iron oxide by the COrCO atmosphere. The activities of iron in wüstite and magnetite, as a function of oxygen pressure, were taken from the work of Darken and Gurry,

Jan 1, 1969

By David R. Poirier

Activity data of carbon as a function of both temperature and composition throughout the stable austenite range is correlated by mearts of an equation derived from a quasi-chemical model. The carbon activity data of austmite for temperatures between 800° and 1200°C are utilized in conjunction with the activity of carbon calculated for the y solidus using the activity of carbon in liquid iron and published austenite-liquid equilibria. The results agree very well with Chip-man's correlation; however, a small difference in the activity of carbon in the high-temperature range of the austenite field is evident. Excellent agreement is found for the heat of solution of graphite in infinitely dilute austenite; from this study the value is 10,550 cal as compared with Chipman's value of 10,680 cal. AS part of a program to study microsegregation in dendritic solidification of ternary Fe-C-Cr alloys, it was desirable to be able to describe the equilibria between austenite and liquid iron in Fe-C-Cr alloys. In this regard, it was necessary to correlate existing data on the activity of carbon in Fe-C austenite as a function of both temperature and composition. At that time, Chipman's analysis1 of the thermodynamics of binary Fe-C austenite was not available. It will be shown that this study and Chipman's study agree rather well throughout the stable austenite range of temperature and composition; however, some small differences appear at temperatures greater than the eutectic temperature. Benz and Elliott 2 presented isoactivity lines for austenite superimposed on their revised Fe-C phase diagram. Using an expression from Darken and Gury 3 representing Smith's4 activity data between 800" and 1000°C, they found that the activities extrapolated above 1000°C to the solidus did not agree with the activities determined from the corresponding liquidus compositions. It is the purpose of the following argument to reconcile carbon activity data of austenite with the activity in liquid Fe-C alloys as determined by Rist and Chipman. 5 In addition, a simple analytical expression is sought for computational convenience. ACTIVITY DATA OF CARBON IN ZRON Fig. 1 shows the activity of carbon in Fe-C austenite as determined by Smith, 4 Schenck and Kaiser, 6 Scheil et a1.,7 and Bungardt et al.' The lines are merely drawn to separate the data into the respective isotherms. These data are inadequate to determine the activity of carbon at temperatures greater than 1200°C. The activity coefficient in Fe-C liquid alloys was assumed by Rist and chipmans to obey the following

Jan 1, 1969

By J. S. Pascover, S. V. Radcliffe

The structures and transformation temperatures of high-purity Fe-Cr alloys have been investigated as functions of composition (0 to 10 wt pct Cr) and rate of quenching from the high-temperature Y phase field (up to 40,000°C sec-1). The structures were chmacterized by transmission electron microscopy. The transformation temperatures for each alloy exhibited the progressive decrease to a constant value with increasing cooling rate which has been shown to be characteristic of several iron binary systems. The corresponding structures were found to become increasingly finer in scale with increasing cooling rate and solute content, but to remain essentially equiaxed in character. In all the materials except the high-purity iron and one of the alloys, an additional and lower transformation temperature than the constant value for the equiaxed structures was observed. The structures of specimens which transformed at these lower temperatures (only single thermal wrests were observed in any given run) were martensitic and consisted of arrays of fine ferrite laths which varied in size and morphology with changing solute content. The factors controlling the nature of these transformations are discussed. The composition dependence of the martensitic transformation temperature, ME, in Fe-Cr alloys together with those reported for other iron binary systems indicate that MB for pure iron is some 700°c, rather than the values of 550° and 760°C reported previously. This conclusion is further supported by the results of a compmison of the thermodynamics of mmtensite formation in several systems. ThE extensive investigations of the structures formed on athermal transformation in iron and its alloys have led to the characterization of several forms of martensitic or "military"1,2 transformations and, in addition, a "civilian7' transformation to ferrite or "equiaxed a"* which occurs athermally and at a very high rate.374

Jan 1, 1969

By R. A. Corley, W. R. Wilcox, J. R. Teviotdale

Chemical vapor deposition of hafnium carbide yielded whiskers, needles, dendrites, faceted crystals, and adherent coatings. The gas stream compositiom and the mass transfer conditions determined the habit of the deposit. The deposits were obtained at temperatures ranging from 1100" to 1800°C. HAFNIUM carbide has the highest melting point of any binary compound; therefore, its various potential applications are a subject of vital interest to the aerospace industry. The experiments described herein were performed to investigate the chemical vapor deposition of hafnium carbide with particular interest being placed upon the possible production of high-strength single-crystal whiskers for composite materials. In 1931 Moers 1 used a gaseous mixture of HfC14, Hz, and toluene to vapor deposit crystalline hafnium carbide on a tungsten filament heated to 2400°to 2800°C. More recently Lepie 2 deposited hafnium carbide on graphite using HfC14 and methane in a helium gas carrier. The pyrolytic depositions described here were accomplished in graphite tubes by using various gas mixtures and dopants. The resulting crystal habits included whiskers, needles, needle dendrites, bulbous dendrites, faceted crystals, and smooth, adherent poly-crystalline layers. EXPERIMENTAL The depositions were carried out in an induction-heated graphite tube, 1.2 cm ID, which was contained in a vertical 9-cm-ID quartz tube. (A more detailed account of the experimental procedures and results is given in Ref. 3.) Refractory oxide fiber and tubes and graphite felt were utilized jointly and singly for therma1 insulation. A typical temperature distribution is shown in Fig. 1. The reactant gases were introduced at the top and removed at the bottom of the tube. Table I summarizes the experimental conditions and results. Many deposition habits were obtained. X-ray analyses showed that they possessed the hafnium carbide structure. Almost invariably these formed well above the point of maximum temperature in the graphite tube. The habit depended strongly on the gas composition. In a series of runs (e.g., run A) using HfC14 and toluene in H 2, hafnium carbide coatings, Fig. 2, were reproducibly obtained at the position where the tube wall was 1400°C, and bulbous dendrites, Fig. 3, were

Jan 1, 1969

By K. R. Evans

The deformation mechanisms occurring in polycrys-talline, commercially pure titanium and a Ti-8 pct A1 alloy have been investigated and compared to earlier results by Levine on high-purity titanium single crystals and by Conrad on commercially pure titanium. In accord with Levine, two consecutive deformation mechanisms are observed to exist below 500°K with the transition temperature between mechanisms, Tc, strongly dependent upon interstitial composition. T, is found to be 210°. 375° -430°, and 450°K for alloys A large number of investigations have been conducted to determine the rate-controlling mechanisms of plastic deformation occurring in fcc and bcc metals. Very few investigations of a similar nature have been conducted for hexagonal metals. In fact, until very recently, magnesium is the only hexagonal metal which has been systematically investigated for determination of the rate-controlling deformation mechanisms.1"3 From these investigations, it was concluded that basal slip below 420°K occurs by the intersection of forest dislocations,1'3 while for prismatic slip the Peierls mechanism is rate-controlling at low temperatures with interstitial compositions of 0.024, 0.42, 0.61, and 1.13 at. pct expressed in terns of oxygen equivalents. The low-temperature mechanism is found to be an impurity obstacle mechanism in contrast to Levine's earlier conclusion of the Peierls barrier. Measurement of the activation parameters for deformation and estimation of the force-distance profile of the obstacles show their retarding force to be effective over longer distances from the obstacle as the interstitial composition increases. and thermally activated cross slip at higher temperatures. 2 The potential technological importance of titanium alloys has prompted recent studies of the deformation and fracture characteristics of titanium and its alloys. 4-8 Levine' systematically investigated the low-temperature deformation behavior of high purity titanium single crystals oriented for either basal or prismatic slip. It was concluded that the Peierls mechanism was rate-controlling at temperatures below 210°K, while above this temperature an undefined mechanism was rate-controlling. Conrad 7,8 concluded from an analysis of the composition dependence of the critical shear stress at 0°K and measurement of the activation parameters that the low-temperature deformation of titanium is controlled by an impurity

Jan 1, 1969

By F. A. Veer, W. G. Burgers, B. H. Kolster

Starting-- from Cu-Si diffusion couples a study of diffusion in the intermetallic compound Cu3Si of the Cu-Si system has been made. Mmker experiments showed copper to be the diffusing element. From the rate of growth of the Cu3Si phase diffusion coefficients were derived. The activation energy for diffusion is 18.6 kcal per mole. The couples show some interesting microscopic features, for which a tentative explanation is given. THE synthesis of dimethyldichlorosilane, (CH3)2SiC12, an important compound in the manufacture of methyl-silicones, takes place at the surface of a thin Cu3Si layer deposited on a mass of silicon particles."' By passing CH3C1 vapor at about 350°C, silicon atoms are consumed from Cu3Si in forming the volatile silane molecules, thus leaving copper atoms at the surface. It is well-known that copper acts as a poison for the above-mentioned reaction by catalyzing the dissociation of methylchloride.' However, no poisonous effect is observed, at least not before most of the silicon from the particles is converted into silane.3 This would be understandable, if either the copper atoms diffuse through the Cu3Si deposit to the underlying silicon or silicon atoms diffuse in the reverse direction to the copper, both processes resulting in the formation of new Cu3Si and so ensuring the proceeding of the reaction. In this paper experiments are described, demonstrating copper to be the diffusing element. Also a very low activation energy for the diffusion is observed. EXPERIMENTAL The silicon used contained 1 ppm Mg and 1 ppm Cu; the copper was spectroscopically pure (Fe: 2 ppm; Ag, Mg, Si: 1 ppm). The copper and silicon samples were prepared in the form of blocks of approximately 10 by 10 by 5 mm with two parallel sides by spark-machining. The blocks were ground on emery paper (grit 600), etched (copper with nitric acid, silicon with a 4:l nitric acid:hydrofluoric acid mixture), and cleaned with alcohol. As the brittleness of the silicon did not allow a welding procedure to prepare the diffusion couples, the copper and silicon blocks were pressed together in a steel clamp. The pressure exerted by the clamp brought about contact between the parts of the couple and so ensured proceeding of the diffusion. The couples were heated in a vacuum furnace (about 10"5 Torr). The temperature was stabilized within 1 pct. After a heat treatment a section parallel to the direction of diffusion was examined in the microscope and in the X-ray scanning microanalyzer. To determine whether copper or silicon is the diffusing element marker experiments were carried out using tungsten wires with a 20-p diam. EXPERIMENTAL RESULTS Figs. 1, 2, 3, and 4 give micrographs of diffusion zones of Cu/Si couples. Analysis by the electron mi-croprobe of the Cu/Si samples after a definite heat treatment revealed the existence of only one intermetallic phase as can be seen from the line scan shown in Fig. 5. From the X-ray diffraction pattern it could be deduced that this phase was CU 3 Si.4 Even when diffusion zones of considerable width (up to 600 p) were obtained, no other phases occurring in the Cu-Si system could be detected, neither by the electron microprobe nor by X-ray diffraction analysis. The optical anisotropy of the Cu3Si phase made it possible to observe the columnar shape of the crystal-

Jan 1, 1969

By Joseph R. Stephens

Deformation substructures of' polycrystalline tungsten, W-2, 9, and 24 pct Re, and W-3 pct Ta were studied by tra?zsrnission electron microscopy. The stress-strain curve for unalloyed tungsten showed gradual yielding followed by work-hardening. Electron nzicrographs indicated a gradual increase in dislocation density with increase in strain up to 5.0 pct. Dislocations, although frequently jogged, were straight over moderate distances and were in a randorn array. Stress-strain curves for alloy specimens of W-2 and 9 pct Re and W-3 pct Ta exhibited a drop in stress at yielding followed by only slight work-hardening. Electron micrographs of these specimens after strains of 0.05, 0.1, and 0.5 pct revealed no change in dislocation substructure from the unstrained specimens. After 2.0 pct strain, the three alloys exhibited dense networks. W-3 pct Ta was characterized by straight, frequently jogged dislocations comparable with the dislocation structure in unalloyed tungsten after a similar amount of strain. In contrast, W-2 pct Re exhibited dislocations that contained widely spaced jogs, while W-9 pct Re had developed a cell structure after the relatively srnall strain of 2.0 pct. The W-24 pct Re alloy contained a few dislocations after 0.1 pct strain, while after 0.5 pct strain twins were evident. Dislocation slip bands apparently preceded the twins. The stress-strain curve for the alloy indicated that twinning commenced after approximately 0.25 pet strain. These results indicate that the primary effect of low rhenium concentrations (2 and 9 pct) in tungsten is to increase dislocation multiplication after macroyielding by reducing the Peierls-Nabarro force (lattice resistance to dislocation motion). The dislocation bands that precede twins in W-24 pct Re may be caused by localized internal stresses resulting fro a metastable structure, for example, clustering of rhenium atoms. The effect of high rhenium additions (22 a 65 pet* Rproperties of tungsten. Klopp, Witzke, and Raffo5 reported bend transition temperatures as low as -100°F (200°K) for dilute electron-beam-melted W-Re alloys tested in the worked condition. Recrystalliza-tion increased the bend transition temperature, but alloys with 2 to 4 pct Re were still markedly superior to unalloyed tungsten. Fractographic examinations of tungsten and W- 3 pct Re and W- 5 pct Re alloys by Gilbert 6 revealed that these low rhenium alloys showed a greater tendency toward cleavage failure than did tungsten. Garfinkle 7 showed that rhenium additions, up to 9 pct, to (100) oriented tungsten single crystals increased the proportional limit stress and decreased the flow stress and the rate of work-hardening. In addition, while deformation in unalloyed (100) oriented crystals apparently involved both (110)100) and (112) slip, crystals with rhenium contents of 5 andpct or more deformed primarily by (112) slip. The mechanism by which high and low rhenium additions affect the mechanical properties of tungsten is still not well-established. The present investigation was undertaken to determine by transmission electron microscopy the effects of low rhenium additions, 2 and 9 pct, and a high rhenium addition, 24 pct, on dislocation substructure in the early stages of deformation of polycrystalline electron-beam-melted tungsten. Unalloyed tungsten and a W- 3 pct Ta alloy were included for comparison. EXPERIMENTAL PROCEDURES Materials. Triple electron-beam-melted tungsten, W-2, 9, and 24 pct Re, and W- pet Ta were used for this investigation. Chemical analyses of the cast ingots are given in Table I. A description of the starting metal powders and melting and fabrication pro-cedures for unalloyed tungsten and the W-Re alloys is reported.5 The W-3 pet Ta alloy was processed in a similar manner. Compression specimens measuring 0.300 in. (7.6 mm) in length by 0.130 in. (3.3 mm) in diam were machined from swaged rods. All alloy specimens were annealed in a vacuum of 8 x 10- 6 Torr (10'2iVper sq m) for 1 hr at 3600°F (2255°K). The recrystallized grain size ranged from 0.06 to 0.08 mm diam for the alloy specimens. Unalloyed tungsten was annealed at 2400° F (1589°K) for 1 hr to produce a recrystallized grain diameter of approximately 0.12 mm. Specimens were electropolished in a 2 pet NaOH solution to a diameter of 0.125 in. (3.18 mm) to remove surface notches resulting from grinding and to improve reproducibility of t data. The ends o the compression specimens were ground flat, parallel to each other, and perpendicular to the longitudinal axes with 4/0 emery paper. Compression Tests. The compressive stress-strain apparatus used for compression tests is described in detail by Stearns and Gotsky.9 Room-temperature compression tests were conducted at a crosshead speed of 0.01 in. per min (0.25 mm per min).

Jan 1, 1969

By D. Webster

It has been found that cold work and annealing treatments greatly retard subsequent grain growth and re-crystallization in thoria-dispersed nickel and NiCr. It is suggested that this is due to cavities which form at the particle-matrix interface durilzg cold work. Some of' the cavities formed are stable at elevated temperatures and prevent the mouement of large-angle grain boundaries. The movement of these boundaries at elevated temperatures is known to start recrystal-lization and when they are pinned by voids recrystal-lization is made more difficult. TD Nichro,me had a maximun resistance to recrystallization when the initial structure was coarse-grained and had a low dislocation density. A precipitation reaction occurred between 700° and 1200° F in cold-worked TD Nichrome. It has been shown by Grant and his coworkers1-3 that a large part of the strength of dispersion-hardened materials is a result of the cold-worked structure produced during fabrication. In a comparison of the strength of cold-worked copper with and without an oxide dispersion, Grant4 has demonstrated that there is little difference in strength at room temperature. The function of the dispersion is essentially to maintain the cold-worked structure at higher temperatures than is possible in the base material. The dispersion accomplishes this by making recrystallization more difficult. The mechanism by which this is achieved is discussed in this paper. The fabrication history of the material has been found to greatly influence recrystallization behavior and this aspect is discussed in some detail. I) MATERIAL Three different thoria-dispersed materials were examined. 1) DuPont 2 pet thoria-dispersed nickel (TDNi) in 0.050-in. seeet. Thoria particle size is in the range 100 to 2500A. 2) DuPont 2 pct thoria-dispersed nichrome (20 pet Cr, 80 pct Ni) (TDNiC) in 0.125-, 0.060-, and 0.040-in. sheet. In the as-received condition these sheets have

Jan 1, 1969

By P. R. Sahm, T. V. Pruss, D. A. Gandolfo

Cb 3 Sn powders were hot-pressed to estahlish densi-fication conditions and assess the possible use of such compacts in multiphase structures with ceramic or magnetic inclusions. Superconducting transition temperatures, Tc, were measured as a function of powder particle size, pressing temperature, and second-phase admixtures. The highest transition temperatures were found in coarse powder (5 to 500 u) compacts and were only weakly depended on pressing temperatures up to 1200°C. Fine powders (below 5 p), however, both single-phase CbsSn and Cb3 Sn-composites, showed a stronger dependence on hot-pressing temperatures. While Al2 O3 phase admixtures did not affect T, much more, a Pronounced T, degradation was observed upon the addition of ferrimagnetic Fe2 Mno. 5 Zno.5 O4 powders. Likewise, critical current densities, Jc, at 4.2° K were lowered appreciably in the ferrite doped samples, whereas the neutral A1203 inclusiow gave slightly improved Jc values. MULTIPHASE structures in electronically active materials have recently gained in interest as pointed out by Galasso in a review article.' In superconductors the most widely reported group are eutectic alloys which have been mostly investigated with respect to the proximity effect.2"4 In addition, "artificial eu-tectics", for example in the form of mercury-vycor glass sponge5 or fine niobium wires imbedded in a copper matrix,= have been prepared to attain higher critical fields and critical current densities. The idea was to enhance flux pinning phenomena by second-phase inclusions or ho1es. 7 Flux pinning should also be possible by the introduction of insulator inclusions into a superconducting matrix. Ceramic-metal combinations are most easily produced by hot pressing (= pressure sintering), as it permits an almost unlimited selection of material combinations. Cb 3 Sn has been prepared by vapor phase growths or in the form of thin films. Large compacts must be sintered,1° however, and normally present difficulties. At temperatures below 1350°C insufficient densities are obtained and at higher temperatures the loss of tin due to dissociation upsets the stoichiometry. Hot pressing is a natural approach to circumvent the problems, since one can obtain satisfactory densities despite low sintering temperatures. This work was mostly concerned with establishing conditions to hot press Cb3 Sn and Cb3 Sn multiphase structures (= composites), because no data are presently available, and to evaluate these with respect to their transition temperatures. However, a few measurements on critical current densities were also carried out, in particular to assess the value of ferrimagnetic inclusions. I) EXPERIMENTAL PROCEDURE The experimental procedure involved the preparation of feed material and powders, hot pressing, and evaluation of the resulting ingots. As no attempts were made to synthesize Cb3Sn from the elements during hot pressing, feed material had to be produced. For this purpose, a stoichiometric Cb-Sn powder mixture was compacted into a 3-cm-diam ingot (80,000 psi) and then inserted into a quartz tube and evacuated. Rf heating was employed. Above the tin melting point (230°C) liquid tin was forced out of the ingot, but was pulled back by capillary action after approximately 0.5 hr of continuous pumping at 700°C. Thus, it appears that evacuation at this temperature caused desorption of impurity gas creating wetting surfaces which, later on, favored alloying at relatively low temperatures. After a presintering period of 17 hr at 800°C, the quartz tube was tipped off and sealed into another such larger-diameter tube which, in turn, was connected to a pump system. This configuration permitted a temperature treatment at 1400°C, carried out for 65 hr, without collapsing of the glass walls or unfavorable chemical interaction of Cb3Sn with the quartz. The resulting material was

Jan 1, 1969

By Robert D. Pehlke, Weldon L. Daines

The reduction of manganese oxide from a basic slag by silicon dissolved in liquid iron at steelmaking temperatures was studied to determine the rate-controlling step for the process. The experiments were carried out under an argon atmosphere in a resistance-heated vertical-tube furnace. The two liquid phases, slag and metal, were held in zirconia crucibles. Sampling and chemical analysis of the slag phase led to time-concentration curves for the system. Results obtained by varying parameters such as temperature, stirring rate, concentration, and melt geometry defined the limiting reaction mechanism. The reduction of manganese oxide by silicon is a fast reaction and reached equilibrium within 90 min. The rate of stirring has a marked effect on the reaction rate, while, on the other hand, the effect of temperature is very small. This identifies the rate-controlling step as diffusion rather than interfaciul chemical reaction. The variation of other parameters revealed that a) diffusion of manganese in the iron phase is the slow step, b) the value of D/6 for manganese in iron at 1550°C is 7x 10-4 cm per sec, c) the energy of activation for the apparent rate constant is 7 kcal per mole, and d) increasing the amount of silicon in the iron decreases the diffusion coefficient of manganese. THE equilibrium relations pertinent to the reduction of manganese oxide from a steelmaking slag by silicon dissolved in liquid iron have been studied, but little is known about the mechanisms that control the rate of the process. The purpose of the present investigation was to study the rate of reduction by silicon and to determine the rate-limiting step. The effects of stirring rate, temperature, composition, and melt geometry were investigated as a means of identifying the controlling step. On the laboratory scale, relatively little work has been done in the area of slag-metal kinetics, primarily because of the problems confronted in attempting to contain liquid slags and metals in laboratory crucibles at steelmaking temperatures. Since graphite is an ideal material for a crucible, several investigations have been carried out on the reduction of various oxides from a slag by carbon in graphite-saturated iron and on the transfer of sulfur between a slag and graphite-saturated iron. Most of this work has been performed in induction furnaces. Studies where the container was not graphite are extremely limited. A single kinetic study of manganese transfer between molten iron and basic slags was carried out by Sano, Shiomi, and Matsushita.' These investigators prepared calcium oxide and titanium oxide crucibles to contain the two-phase system. Only a few experiments were carried out and the results had to be treated qualitatively. Despite the paucity of kinetic data, a large quantity of information is available in the literature concerning the thermodynamics2-12 and physical properties'3-21 of the slags containing manganese oxide and the dilute liquid iron alloys containing manganese and silicon which were involved in this research program. EXPERIMENTAL METHOD A vertical-tube resistance-heated furnace was used in this investigation to study the slag-metal reaction Although most previous slag-metal studies were carried out in induction furnaces, a resistance furnace has several advantages including better control of temperature and stirring rate. Hence, a resistance furnace was selected for this study, and its design is shown schematically in Fig. 1. Slip-cast, fine-grained, low-porosity, lime-stabilized cubic zirconia crucibles were used for the kinetic experiments. The crucibles were 4 1/2 in. high and 2 1/8 in. OD with a 1/16-in. wall. The crucibles were only slightly

Jan 1, 1969

By N. J. Grant, B. C. Giessen, U. Wolff

With the aid of the splat-cooling technique of rapid quenching, metastable alloy phases based on antimony ad bismuth have been prepared. At room temperature, simple cubic phases were found in the Sb + Au, 56 + Yd, and Sb + Ni systems. Another phase was retained in the Au-Bi system at -190°C; in this systent, a microcrystalline phase and a rhombohedrally distorted phase were also observed. The crystal chemistry of these phases is discussed in terms of their valence electron concentration range. A remarkable five-step Phase sequence was found upon heating and equilibration of certain metastable Au-Bi alloys. USING the splat- cooling technique of rapid quenching from the liquid,' a large number of metastable intermediate alloy phases have been prepared in recent years. Thus, Hume-Rothery phases of the hexagonal type based on the valence electron concentration have been produced in systems where they are missing in equilibrium, e.g., Ag-Ge 1 or AU-Sb. 3 In a comprehensive study of metastable alloys based on tin, simple hexagonal metastable y phases were found, raising the total of stable and metastable y phases from 3 to 13. 4 In the In-Bi system, five new metastable intermediate phases were retained.' In most cases, the new metastable phases have some crystal chemical characteristics in common: a) They have rather simple, elementlike structures with few atoms per unit cell, e.g., y phase,4'5 or the metastable primitive cubic phases in the Ag-Te and and Au-Te systems.= b) Their structures are often related to those of the terminal phases, or to elements that are straddled in their position in the periodic table by the constituent elements; this is the case for metastable ß (In-Bi) with the structure of white ß Sn,' or metastable a (Cd-sn). 4 c) They seem to represent the crystal structures appropriate to certain average group number (AGN) ranges in which no or few single-phase structures exist in equilibrium. These average group number ranges can probably be equated in the case of many elements of the Ba(Zn)-Bs(As) groups with the averaged valence electron concentration. In the present work, the splat-cooling technique has been applied to the alloys of antimony and bismuth. In equilibrium, neither element forms intermediate alloy phases with other B elements from groups Bl(Cu) to B4(Si) that contain more than 66.7 at. pct of Sb or Bi, respectively, e.g., AUSb 2. 7 Thus, antimony- or bismuth-rich phases, which might be closely related to antimony or bismuth, and which would reflect struc- tural changes occurring on alloying with small amounts of addition elements, do not exist. Also, the terminal solubility of antimony and bismuth for all B metals is very small. It was therefore of interest to investigate the influence of enforced, nonequilibrium solid solution of addition elements in antimony and bismuth on their crystal structures. It was found that additions of group B 2-B4 metals act distinctly differently than additions of group T 10 and B1 metals. The latter set of additives will be treated here. EXPERIMENTAL TECHNIQUES Alloy preparation and splat-quenching followed closely the procedures described in Refs. 1, 4, and 5; they consisted of the preparation of master alloys from high-purity starting materials (99.99+ pct) and blast-atomizing of 20-mg quantities onto copper sheets. The resulting approximately 1 to 5 u thick foils were investigated by X-ray diffraction. The cooling rates obtained are of the order of 107 to 10 8 C per set,'" causing solidification to proceed at a rat; of approximately 100 cm per sec.' Powder patterns of the resulting fine-crystalline materials were taken with filtered CuK, radiation. For antimony alloys the substrates were held at room temperature and for bismuth alloys at -190°C both during splat foil deposition and X-ray investigation. Annealing treatments at several

Jan 1, 1969