Search Documents

By R. Littlewood

The concepts of "redox potential" and "oxide-ion activity" are suggested as measures of the fundamental slag properties of interest to the extraction metallurgist. Thermodynamic data for single oxides are presented graphically in these terms and a method of expressing desulfurization of steel in electrochemical terms is indicated. The application of the theovy to mixtures of oxides (slags) is discussed and the redox potential is shown to provide a link between all the redox equilibria in a slag-metal system. In particular, the redox potential of the slag, its basicity, and the oxygen partial It is now generally recognized that slags are mixtures of polymeric anions of silicates, aluminates, phosphates, and so forth, neutralized by cations. However, conventional thermodynamic treatments of slags have almost always been in terms of activities of the pure component oxides (e.g., SiO,, CaO, A1203, and so forth), which are known not to exist as such in slags. While this type of empirical treatment is perfectly acceptable and provides a rigorous and self-consistent way of considering thermodynamic properties, it can give little guide to the structure of slags, since its very nature ig- pressure are closely connected. Direct deternzination of these by electrode-potential measurements is possible. Literature calculations of ion activities in the system Ca0 -Fe0-SiO,/molten iron are used to evaluate redox potentials, which are shown to correlate with data on sulfur partition in the system. In addition to its application to equilibrium conditions, an electrochenzical approach to slag-metal reactions might provide a basis for new methods of studying the kinetics of these reactions and for plant-control instruments in the pyrometallurgical industries. nores such complications. Recently, the thermodynamic properties of some slags have been successfully interpreted in terms of activities of anions of varying degrees of complexity. (While these have been successful curve-fitting exercises, there is no direct implication that the anions used in the models are necessarily the ones which actually exist in slags.) The success of these ionic thermodynamic treatments is encouraging but a complete picture of slag structure is still a long way off. What is needed is a complete knowledge of the values of stability constants for all reactions in slags of the type:

Jan 1, 1965

By W. J. Slatosky

As a means of effecting better control of endpoint temperatirres at the Jones & Laughlin basic oxygen furnace plant, a set of mathematical equations has been developed. The eqlutions are the product of a themlochemical anaysis of the process and aye designed to calculate the required scrap, lime, and hot metal additions in terms of a number of independent variables. Results of test heats have warranted adoption of this technique by the Prodrrction Department. BECAUSE of the autogeneous nature of the basic oxygen steel-making process, bath temperature can be controlled without an external fuel supply by charging the furnace with additions that are thermally balanced. The thermal requirements of the charge materials are such that, during the refining process, they throttle the heat generated by the metallurgical reactions in a manner designed to result in a speci-fied temperature at the completion of the heat. In the past, operating personnel at the basic oxygen furnace plant of Jones & Laughlin's Aliquippa Works relied on their experience and technical knowledge of the process to determine the quantities of charge additions needed to result in a finishing temperature in the range 2880"to 2920" F. (The charge consists primarily of 93 tons of scrap and hot metal plus an amount of lime sufficient to maintain a basicity ratio of 2.8 to 3.2). Estimates of these materials are based on a consideration of the effects on finishing temperature of 1) iron silicon content, having a variation of 0.8 to 1.8 pct; 2) iron temperature, ranging from 2250°to 2600°F; and 3)any excessive cooling of the furnace due to a production delay. The end temperature of the preceding heat also serves as a guide in that, if a heat was within the specified temperature range, the succeeding heat could be charged with materials of nearly the same proportions, provided the hot metal used in each of the two charges was of approximately the same temperature and composition. On the other hand, if a heat was outside the specified tapping range, or if the hot metal used in that heat was of different analysis and temperature from that of the iron to be charged, an adjustment in the proportion of additions is in order for the following heat. Due to the complex thermochemical behavior of the process and to the inexact and subjective nature of the described method of determining charge additions, consistently accurate temperature control was not to be expected. Therefore, those heats out- side the specified tapping range necessitated subsequent adjustments by either reblowing the cold heats for a suitable length of time so as to elevate the bath temperature to the desired level, or cooling hot heats with a proper amount of scrap. Because extra time is required to make these adjustments, production is delayed. In an attempt to devise a method for improving temperature control, an analysis of the thermochemistry of the process was undertaken. This, in turn, led to the development of a set of mathematical equations which enable the calculation of the quantities of scrap, lime, and hot metal needed to result in any specified tapping temperature range. The analysis was not intended to be a repetition of work done by others such as McMulkinl or ~hilbrook.' It was meant to be an extension of their work so that charge additions could be calculated not in terms of silicon alone but, rather, as a function of all independent variables. This paper presents the derivation of these relationships, their effectiveness in controlling bath temperatures, and a method of utilizing them on an operational basis. The Heat Balance—The first step undertaken in the analysis of the problem was the enumeration of the pertinent variables. A list is presented in Table I where it is noticed that these quantities have been separated into the following three categories: important variables, variables considered as constants, and variables to be neglected. The breakdown was an arbitrary one designed to facilitate the analysis; otherwise, the mathematical treatment would have been exceedingly cumbersome and complex. Fortunately, experience has shown that these simplifying assumptions do not seriously impair the accuracy of the calculations. These variables along with the limiting assumptions listed in Table n were then used to write a heat balance of the process by applying the equation of continuity, Rate of Rate of Rate of Increase = Income - Outgo PI ] of Heat of Heat of Heat.

Jan 1, 1962

By H. A. Hancock, L. M. Pidgeon

Equilibrium carbon monoxide pressures were measured over the reaction between chromium oxide and a number of solid ferrochromium alloys in the composition range 0.4 to 4.8 pct C and 0 to 49 pct Fe. Measurements were also made for the carbides Cr23C6 and Cr7C3 which agreed well with previous investigations. Between 1050°and 1400°C the pvessures varied from 0.1 to 56 mm and increased markedly with the iron and carbon contents of the alloys. The data were used to estimate the activity of carbon in the alloys and to calculate the equilibrium conditions for the decarburization of a useful range of ferrochromium alloys. WHEN ferrochromium is produced by the reduction of chromite with carbon in an electric arc furnace it invariably contains up to 10 wt pct C. For many purposes such as the production of stainless steel, it is necessary that the carbon content be as low as from 0.02 to 0.05 pct. Thus an important part of the ferrochromium industry consists of the production of low carbon ferrochromium. The classical Bessemer steelmaking technique cannot be used to oxidize low carbon contents in chromium and ferrochromium alloys without also oxidizing the chromium. Recently a new commercial process2-4 has been introduced for oxidizing carbon from high chromium content alloys which consists of heating the solid alloy with such oxidizing agents as Cr2O3, Fe2O3, or SiO2 in a retort at reduced pressures. By maintaining the carbon monoxide pressure below the equilibrium value for the system, the carbon can be removed as carbon monoxide without oxidizing the chromium. The equilibrium conditions for the decarburization of solid chromium carbon alloys have been determined by Boericke5 who measured the carbon monoxide pressure over the reaction between the various chromium carbides and chromium oxide. A typical reaction is shown below. Cr23C6 + 2Cr2O3 =u 27Cr + 6CO [1] These values are not applicable to the decarburization of commercial ferrochromium alloys which invariably contain major amounts of iron. The present investigation was therefore undertaken to measure the change in the equilibrium carbon monoxide pressure brought about by additions of iron to the Cr-C-0 system, thus extending the work of Boericke into the region of the production of low carbon ferrochromium. MATERIALS AND METHOD Materials. Measurements were made on two carbides of chromium, Cr233C6 and Cr7C3, and fifteen Fe-Cr-C alloys. The chromium carbides were made

Jan 1, 1963

By Nev A. Gokcen

DISCREPANCIES and scattering in the equilibrium data on the reactions of hydrogen, and CO with dissolved oxygen in liquid iron are un- duly large. Available experimental results on the reduction of liquid ferrous oxide, i.e., wüs-tite, with hydrogen and CO are questionable, as pointed Out by Darken and Gurry'l Direct determinations of the solubility of oxygen in liquid iron are subject to errors which cannot be easily reduced by further experimental refinements, and therefore an accurate but indirect method is highly desirable. The purpose of this investigation was, therefore, 1)

Jan 1, 1957

By Donald B. Evans, Robert D. Pehlke

The solubility of nilrogen in liquid binary alloys of iron with Litanium. zivconium, columbium, vanndiurn, and tantalum was measured for alloy composiLions up to the solalbility limils of lhe alloy nitrides. All five alloying agents were found to decrease markedly the activity coefficient of nitrogen in liquid ivon. The metal/nitvogen mole ralios in the alloy nitrides formed were generally .found to be slighlly greater than 1.0, but in no case greater than 1.5. From the experimental data, the standard free energies of fortmation of titanium and zir-conium nitrides have been calculated for the Lemperaluve range 1550° to 1750 C. The solublily Products for columbium, tantalum, and vanadium nitrides are also reported. A number of research investigations have examined the effect of refractory metals on the solubility of nitrogen in liquid iron. Although data on zirconium are not available, investigators are in agreement that titanium, vanadium, columbium, and tantalum markedly increase the solubility of nitrogen in liquid iron. This fact alone makes desirable the acquisition of thermodynamic data for these elements in liquid iron. Since refractory metals are known to be stable nitride formers, they have been suggested as steel denitrifying agents, and some of their nitrides have recently been considered as containment materials for liquid iron and iron alloys. Most available thermodynamic data for these metals relate to their dilute concentrations, but effective thermodynamic treatment of these applications requires data at concentrations near the solubility limit of the alloy nitride. Although some work has been done at relatively high alloy concentrations in liquid iron (particularly for vanadium 2,3 and titanium 2,4), the results have been somewhat contradictory. Disagreement may be partly attributed to the fact that the compositions of most refractory metal nitrides have been shown to be nonstoichiometric, and to vary 2,5-8 depending on the temperature and nitrogen gas pressure with which the solid nitride phase is in equilibrium. One purpose of this study consequently has been to determine the compositions of the refractory metal nitrides precipitated from a liquid iron solution. EXPERIMENTAL PROCEDURE Rao and Parlee2 and Evans and Pehlke 9 have discussed the technique for measuring the solubility product of an alloy nitride phase in liquid iron by finding the point of departure of the nitrogen solubility from Sieverts' law. The method consists of measuring the solubility of nitrogen in a melt of iron containing a known concentration of a second metal as a function of the nitrogen gas pressure over the melt. In this study the second metal was one of the refractory metals titanium, zirconium, columbium, vanadium, or tantalum. When the nitrogen pressure at which the refractory nitride forms is reached, a deviation of the measured solubility of nitrogen in the melt from Sieverts' law is observed in the form of a "pressure halt." The concentration of nitrogen in the melt associated with this breakpoint in the nitrogen-absorption curve is then used to calculate the nitride solubility. The Sieverts method was used to measure nitrogen solubility as a function of nitrogen pressure and temperature. The experimental equipment for this technique has been previously described in detail. 1,9 Charge materials used were vacuum-melted high-purity iron (Ferrovac-E) and the best commercial grades of the refractory metals obtainable (in all cases at least 99.8+ pct pure). Recrystallized alumina crucibles were used to hold all melts except those containing zirconium, for which zirconia crucibles were necessary. Temperatures were measured by a disappearing-filament type optical pyrometer sighted vertically downward on the melt surface through a 1/4-in.-diameter sight hole in the crucible lid. By means of a technique previously described, 9 in which the refractory-metal nitride was precipitated at one temperature then redis-solved by raising the temperature 50°C and precipitated again at a higher temperature, it was possible to obtain data over a temperature range of up to 200°C on a single melt. It was found that this technique could not be used with melts containing zir-

Jan 1, 1965

By J. Chipman, N. J. Grant, H. L. Bishop, H. N. Lander

Data of several studies on the equilibrium between molten iron and open hearth-type slags have been combined to determine some of the chemical reactions involved in steel-making. Effects of slag composition and temperature on the iron oxide activity, distribution of sulfur between slag and metal, and the carbon content of the metal are discussed. Also, an overall reaction for the equilibrium between sulfur and oxygen is presented. DURING the past 15 years, a number of significant equilibrium studies have been carried out between liquid iron and simple basic and acid slags in an effort to throw light on the chemical reactions involved in steelmaking. This paper is a summary of the experimental reports on investigations which have been conducted at the Massachusetts Institute of Technology, and of related work in other laboratories. The investigations summarized in this paper include the works of Fetters and Chipman1 and Taylor and Chipman,' which dealt with simple slags that are similar to those found in the open hearth. The sulfur determinations of the slag-metal tests of Fetters and Chipman as reported by Grant and Chip-man" are included. Also, the investigations by Win-kler and Chipman' and Grant and ChipmanQ f more complex slag systems are included in this summary. The experimental procedure is described in detail in each of these papers and will not be discussed. Since the previous reports have been somewhat independent, it is desirable to review and combine the data of the various investigations to determine, as accurately as possible, the reactions in the slag-metal systems of the open hearth. It is the object of this report to present the combined data in such a way as to enhance their utility and applicability. Oxidizing Power of Slags of the System (CaO+MgO)-Si0,-FeO in Equilibrium with Carbon-Free lron The slags selected to determine the iron oxide activity in equilibrium with pure liquid iron were those containing less than 2 pct each of P,O,, MnO, or A1,0, on a weight percentage basis. The method used to calculate activities of iron oxide in liquid slags was that developed by Taylor and Chipman.' The solubility of oxygen in molten carbon-free iron under pure iron oxide slags can be expressed by the following eauation —6320 log (pctO)-------------— + 2.734 [1] where T is the absolute temperature. The oxygen solubility values as determined from Eq. 1 were used throughout this study to calculate the iron oxide activity. The iron oxide activities of slags of various iron oxide contents are plotted in Fig. 1 as a function of the basicity, which is defined as the ratio (pct CaO + pct MgO)/pct SiO,, and are based on molecular percentage values of the components. The percent (FeO), is the total iron content in the slag calculated to FeO. Fig. 1 shows that as the basicity increases at constant mol pct (FeO),, the iron oxide activity increases rapidly and reaches a plateau which extends on the basicity scale from about 1.3 to 2.3; the iron oxide activity then decreases rapidly until a basicity of about 3.0 is reached, where it tends to level off. The solid portions of the curves represent the experimental data of Fetters and Chipman and Win-kler and Chipman. Their experimental heats were made in magnesia crucibles, and hence the slags were saturated with magnesia. The broken lines on the left represent the experimental data of Taylor and Chipman, who used a rotating crucible. In general, these slags contained less than 3 pct MgO. The absence of data for slags containing less than about 40 mol pct (FeO), and basicity ratios greater than about 2.5 made it necessary to calculate curves using ionic concepts of slags. The broken lines on the right, which disregard the solubility limits of di and tricalcium silicate and lime, were obtained by following the treatment of Flood and Grjotheim,"

Jan 1, 1957

By E. W. Filer, L. S. Darker

ONE of the primary purposes of this investigation was to determine how far blast-furnace metal and slag depart from equilibrium, particularly with respect to sulphur distribution. In studying the equilibrium between blast-furnace metal and slag, there are two approaches that can be used. One method is to use synthetic slags, as was done by Hatch and Chipman;' the other is to equilibrate the metal and slag from the blast furnace by remelting in the laboratory. In the set of experiments here reported, metal and slag tapped simultaneously from the same blast furnace were used for all the runs. The experiments were divided into two groups: 1—a time series at each of three different temperatures to determine the t.ime required for metal and slag to equilibrate in various respects under the experimental conditions of remelting, and 2—an addition series to determine the effect of additions to the slag on the equilibrium between the metal and slag. An atmosphere of carbon monoxide was used to simulate blastfurnace conditions. The furnace used for this investigation was a vertically mounted tubular Globar type with two concentric porcelain tubes inside the heating element. The control couple was located between the two porcelain tubes. The carbon monoxide atmosphere was introduced through a mercury seal at the bottom of the inner tube. On top, a glass head (with ground joint) provided access for samples and a long outlet tube prevented air from sucking back into the furnace. The charge used was iron 6 g, slag 5 g for the time series, or iron 9 g, slag 7 % g for the addition series. This slag-to-metal ratio of 0.83 approximates the average for blast-furnace practice, which commonly ranges from about 0.6 to 1.1. A crucible of AUC graphite containing the above charge was suspended by a molybdenum wire in the head and, after flush, was lowered to the center of the furnace as shown in Fig. 1. The cylindrical crucible was 2 in. long x % in. OD. The furnace was held within &3"C of the desired temperature for all the runs. The temperature was checked after the end of each run by flushing the inner tube with air and placing a platinum-platinum-10 pct rhodium thermocouple in the position previously occupied by the crucible; the temperature of the majority of the runs was much closer than the deviation specified above. The couple was checked against a standard couple which had been calibrated at the gold and palladium points, and against a Bureau of Standards couple. The carbon monoxide atmosphere was prepared by passing COz over granular graphite at about 1200°C. It was purified by bubbling through a 30 pct aqueous solution of potassium hydroxide and passing through ascarite and phosphorus pentoxide. The train and connections were all glass except for a few butt joints where rubber tubing was used for flexibility. The rate of gas flow was 25 to 40 cc per min. As atmospheric pressure prevailed in the furnace, the pressure of carbon monoxide was only slightly higher than the partial pressure thereof in the bosh and hearth zones of a blast furnace—by virtue of the elevated total pressure therein. Simultaneous samples of blast-furnace metal and slag were taken for these remelting experiments. The composition of each is given in the first line of Table I. There is considerable uncertainty as to the significant temperature in a blast furnace at which to compare experimental results. This uncertainty arises not only from lack of temperature measurements in the furnace, but also from lack of knowledge of the zone where the slag-metal reactions occur. (Do they occur principally at the slag-metal interface in the crucible, or as the metal is descending through the slag, or even higher as slag and metal are splashing over the coke?) The known temperatures are those of the metal at cast, which averages about 2600°F, and of the cast or flush slag, which is usually about 100°F hotter. To bridge this uncertainty, remelting temperatures were chosen as 1400°, 1500" (2732°F), and 1600°C. For the time series the duration of remelt was 1, 2, 4, 8, 17, or 66 hr; crucible and contents were quenched in brine. The addition series were quenched by rapidly transferring the crucible and contents from the furnace to a close-fitting copper "mold." Of incidental interest here is the fact that the slag wet the crucible

Jan 1, 1953

By R. L. Hadley, G. Derge

The amounts of oxygen in liquid iron-titanium alloys up to 50 pct Ti were measured and the oxide phases in equilibrium with these alloys were determined by using TiO² crucibles. A minimum of about 0.003 pct 0 occurs at less than 1 pct Ti. The various liquid and solid oxide phases can be arranged on a ternary isotherm. THREE characteristics of titanium contribute to the interesting aspects of its reaction with oxygen in liquid iron: 1—It forms a number of stable oxides. 2—All oxides have large negative free energies of formation. 3—The pure metal exhibits high solubility for oxygen. In addition, the use of titanium as a stabilizing and strengthening element in alloys suggests a need for investigation of its reactions in amounts greater than those normally required for deoxidation. These higher compositions are also of interest because they occur during the addition of ferroalloys and produce deoxidation products before dilution is achieved. Titanium Deoxidation in the Literature While the use of titanium as an alloying element and deoxidizer has been common for several decades, the first detailed study of its deoxidizing characteristics was carried out by Wentrup and Hieber' in 1939. These authors determined the extent of deoxidation possible with titanium and identified, by microscopic examination, the products formed. They found that titanium in excess of 0.2 pct did not reduce the oxygen content of iron below 0.004 pct at 1600°C. They identified the spinel FeO-TiO² at low titanium concentrations and Ti2O³ in melts containing more than 0.2 pct Ti. A portion of the area surveyed by Wentrup and Hieber has been investigated recently by Evans and Sloman² using X-ray diffraction for inclusion identification. They concurred in general with the findings of Wentrup and Hieber, but reported the existence of Ti³O5 as a deoxidation product in the range near 0.1 pct Ti. Comstock, Urban, and Cohen³ discussed the deoxidation of iron with titanium, correlating the data of Wentrup and Hieber with free-energy data for the titanium oxides. Scatter at high titanium values was considered attributable either to the formation of an oxide exhibiting high solubility in liquid iron or to the entrainment of solid oxide particles leading to high apparent solubility. Chipman' has calculated the deoxidation curves for titanium based on free-energy data for titanium oxides. These calculations (Fig. 1) and those of Comstock, Urban, and Cohen involve assumptions as to the activity coefficients of oxygen and titanium in liquid iron, since such data have not been determined. Investigation of the deoxidizing characteristics of chromium" and vanadium0 have shown that these elements decrease the activity coefficient of oxygen in liquid iron, leading to a tendency toward relatively high oxygen values and experimental scatter in highly alloyed melts. Experimental This investigation involved two major objectives: 1—determination of the composition of the oxide phases in equilibrium with liquid Fe-Ti alloys, and 2—establishing the pattern of oxygen solubility in liquid Fe-Ti alloys at titanium concentrations in excess of that required for attainment of minimum oxygen content. Raw Materials Ingot iron was used having the following composition: 0.02 pct C, 0.017 pct Mn, 0.01 pct Si, 0.02 pct S, 0.006 pct P, and 0.03 pct 0. The titanium used

Jan 1, 1956

By S. Ramachandran, R. A. Walsh

Many investigations have shown that the manganese enhances the deoxidation power of silicon. Here it is suggested that this phenomenon could be explained in terms of the formation of impure silica. Data of Hilty and Crafts on the Fe-Mn-Si-O System has been evaluated on the basis of the reaction S_i + 20 = (SiO2) where (SiO2) denotes silica of variable activity. The activity of silica in this system is a function of aMn/aSi and the temperature, and can be described by the equation 12700 l°gaSiOz = -6.85+ - - 0.5 log aMn /asi PRACTICAL melting experience has shown that it is helpful to maintain a certain range of Mn/Si ratio in deoxidizing quality alloy steels. Herty,1 as early as 1932, reported a strong association between manganese and silicon as did schenck2 and Korber and Oelsen3 in later work. More recently, Hilty and crafts4 have studied the solubility of oxygen in the Fe-Si-O system, both with and without manganese. Their study confirmed the marked ability of manganese to increase the deoxidizing power of silicon. This phenomenon has remained unexplained in the liter,ature5 since it has been shown that manganese has virtually no influence on the activity coefficients of silicon or oxygen.= In this paper, an explanation for the role of manganese is suggested and equations are devised for quantitatively describing this influence. DISCUSSION Hilty and crafts4 equilibrated their melts under an argon atmosphere and the system established equilibrium with a self-generated slag which was not always the oxide of lowest free energy. Drawing on the early work of Korber and Oelsen,3 it was reasoned that the formation of complex Fe-Mn-silicates

Jan 1, 1963

By J. Chipman, M. N. Dastur

The importance of dissolved oxygen as a principal reagent in the refining of liquid steel and the necessity for its removal in the finishing of many grades have stimulated numerous studies of its chemical behavior in the steel bath. From the thermodynaniic viewpoint the essential data are those which determine the free energy of oxygen in solution as a function of temperature and composition of the molten metal. A number of experimental studies have been reported in recent years from which the free energy of oxygen in iron-oxygen melts can be obtained with a fair degree of accuracy for temperatures not too far from the melting point. Certain discrepancies remain, however, which imply considerable uncertainty at higher temperatures; also several sources of error were recognized in the earlier studies. It has been the object of the experimental work reported in this paper to reexamine these sources of uncertainty and to redetermine the equilibrium condition in the reaction of hydrogen with oxygen dissolved in liquid iron. The reaction and its equilibrium constant are: H2 (g) + Q = H2O (g); K1 _ PH2O / [1] Ph2 X % O Here the underlined symbol Q designates oxygen dissolved in liquid iron. The activity of this dissolved oxygen is known to be directly proportional to its concentrationl,2 and is taken as equal to its weight percent. The closely related reaction of dissolved oxygen with carbon monoxide has also been investigated:3,4,5 co (g) +O = CO?(g); K _ Pco2___ [2] K2= pco X % O [2] The two reactions are related through the wat,er-gas equilibriuni: H2 (g) + CO2 (g) = CO (g) + H2O (g); K2 = PCO X PH2O [3] PH2 X PCO2 and with the aid of the accurately known equilibrium constant of this reaction, it has been shown5 that the experimental data on reactions [1] and 121 are in fairly good, though not exact, agreement. Experimental Method Great care was taken to avoid the principal sources of error of previous studies, namely, gaseous thermal diffusion and temperature measurement. The apparatus was designed to provide controlled preheating of the inlet gases and to permit the addition of an inert gas (argon) in controlled amounts, two measures found to be essential for elimination of thermal diffusion. A known mixture of water vapor and hydrogen was obtained by saturating purified hydrogen with water vapor at controlled temperature. This mixture, with the addition of purified argon, was passed over the surface of a small melt (approximately 70 g) of electrolytic iron in a closed induction furnace. After sufficient time at constant temperature for attainment of equilibrium the melt was cooled and analyzed for oxygen. GAS SYSTEM A schematic diagram of the apparatus is shown in Fig 1. Commercial hydrogen is led through the safety trap T and the flowmeter F. The catalytic chamber C, held at 450°C, was used to convert any oxygen into water-vapor. A by-pass B with stopcocks was provided so that the hydrogen could be introduced directly from the tank to the furnace when desired. From the catalytic chamber the gas passed through a water bath W, kept at the desired temperature by an auxiliary heating unit, so that the gas was burdened with approximately the proper amount of water vapor before it was introdvced into the saturator S. All connections beyond the catalytic chamber were of all-glass construction. Those connections beyond the water bath were heated to above 80°C to prevent the condensation of water vapor. After the saturator, purified argon was led into the steam-hydrogen line at J, and finally the ternary mixture was introduced into the furnace. THE SATURATOR The saturator unit comprised three glass chambers, as shown in Fig 1, the first two chambers packed with glass beads and partially filed with water and the third empty. Each tower had a glass tube with a stopper attached for the purpose of adjusting the amount of water in it. The unit was immersed in a large oil bath, which was automatically controlled with the help of a thermostat relay to constant temperature, ± 0.05ºC, using thermometers which had been calibrated against a standard platinum resistance thermometer. The performance of the saturator over the range of experimental conditions was checked by weighing the water absorbed from a measured volume of hydrogen; the observed ratio was always within 0.5 pct of theoretical.

Jan 1, 1950

By J. Sibakin, R. D. Hindson

In order to devise a practicable soaking pit schedule for use at The Steel Co. of Canada Ltd.'s Hamilton Works, soaking pit heating temperatures, sooking times, pit capacity, and safe maximum mill drafts were correlated with fluctuations in the current or load of the bloom mill driving motor. Other variables such as total delays in the pit, rolling schedules, mill delays, and track times were also investigated. IN order to show an easily applied and accurate means of establishing soaking pit heating temperatures, soaking times, pit capacity, and safe maximum mill drafts, these various factors are correlated herein with fluctuations in the current or load of the bloom mill driving motor. Rolling practices have a considerable influence on the production capacity of a blooming mill. The maximum values of the torque, in particular, are of importance, since even instantaneous current peaks lead to the tripping of the motor by the overload relay and result in loss of mill time. The establishment of safe maximum drafts and accelerations for ingots of different sizes and of a soaking pit practice which would ensure a consistent and satisfactory plasticity of the metal is of considerable importance for increasing the efficiency of both the blooming mill and the soaking pits. The Bloom Mill Dept. of the Hamilton Works, The Steel Co. of Canada Ltd., is equipped with one 44 in. mill driven by a 7000 hp motor with the setting of the overload relay at 22.0 ka. The speed of rotation of the motor is regulated after the Ward-Leonard system. There are three basic speeds of 9.5, 28, and 47 rpm and a further possibility of increasing the speed by weakening the field. This last possibility is hardly ever used during practical operations. The rolling program of the blooming mill is varied, both in the size of the ingots to be handled and in the steel grades. The total tonnage handled by the mill is about 2,000,000 ingot tons per year. At the time of the investigation, the Bloom Mill Dept. was equipped with 22 soaking pits (6 regenerative, 14 bottom-fired, and 2 one-way top-fired pits) with a total bottom area of 2770 sq ft. The pits are fired with a blast furnace-coke oven gas mixture having a calorific value of 155 Btu per cu ft. The foregoing figures show that the production program was such as to impose the necessity of a most efficient usage of the available equipment. For this purpose, the operations of the 44 in. mill and of the soaking pits were investigated, and the results of the investigation were used as a basis for a revised soaking pit schedule and drafting practice. The plasticity of an ingot of a certain chemical composition when being rolled is determined mainly by the following factors: I—the ingot size, both thickness and width; 2—the length of the gas soak; and 3—the surface temperature. The first two factors determine the uniformity of the temperature distribution over the cross-section of an ingot. The third factor introduces the level of the heating of an ingot. The torque produced by an ingot being rolled is determined by the area of the metal displaced, its plasticity, and acceleration values. On the other hand, with shunt motors the torque is determined by the current. This can be assumed to be correct with only a small degree of error for compound motors with a relatively small effect of the series windings as long as the velocity is not regulated by weakening the field. Since the spread is relatively unimportant when compared to the width of an ingot and since it is also reduced several times during rolling by edging passes, the draft alone and not the area of the metal displaced may be taken into consideration with ingots of a similar size. It is therefore possible to determine the main features of the heating and drafting of an ingot by measuring the current and acceleration of the mill motor. After the acceleration has been taken into account, the amount of current will be an indication of how the motor responds to a heating and/or drafting practice and these practices can be adjusted in order to get the desired result. As peak currents are more likely when heavier ingots are rolled, the rolling of plate and slab ingots was investigated. Conditions prevailing when smaller ingots are rolled can be deduced from the results obtained on heavier ingots. All measurements were made when plain carbon grades under 0.15 pct C were rolled. The motor current, the voltage across the armature, and the rpm were recorded simultaneously on synchronized charts, Fig. 1, which moved with the speed of 6 in. per min. Each draft was recorded by a special observer. The rpm curve made it possible to establish the acceleration at any given moment. For purposes of correlation, the maximum current during a pass and the corresponding acceleration were used. The charts made it possible to establish the position of the roller's lever at any given moment as well as the total time of a pass. The slab ingots were divided into three groups (28x35, 28x45, and 27Mx53 in. ingots) and each group was investigated separately. Since they account for most of the current peaks, only flat passes were used for purposes of correlation, a total of 1373 having been investigated.

Jan 1, 1956

By J. F. Martin, L. M. Melnick, R. Rapp, R. C. Takacs

Recent studies on the determination of hydrogen in steel have shown that the hot-extraction method for removing hydrogen from a solid sample is preferable to its removal from a molten sample by vacuum fusion or by fusion in vacuum with tin. A number of techniques are available, however, for determining the hydrogen so extracted. They include: thermal conductivity, gas chromatography, pressure measurement before and after catalytic oxidation of the hydrogen to water and removal of the water, and pressure measurement before and after diffusion of the hydrogen through a palladium membrane. These techniques have been evaluated on the basis of initial cost, maintenance, speed and accuracy of analysis, and applicable concentration range. The results of this study showed that the palladium-membrane technique is best suited for routine use. FOR some time investigators have been concerned with the origin, form, and effect of hydrogen in steel. In such stdies', the analysis for hydrogen constitutes one of the most important phases. It is quite apparent that the results for hydrogen concentrations in a given steel are dependent on the method of obtaining the sample, storage of the sample until analysis, preparation of the sample, and analysis of the sample, including all the facets inherent in the calibration and operation of an apparatus for gas analysis. There are a number of means available for determining hydrogen. This is a critical study of some of the more common techniques in use today. In most conventional melting and casting methods, hydrogen concentrations of 4 to 6 parts per million (ppm) in steel are quite common. Because of the undesirable effects of hydrogen on steel there has been increased use of techniques such as vacuum melting,' vacuum casting, and ladle-to-ladle stream degassing, which lower the hydrogen content to levels on the order of 1 to 2 ppm. Therefore, the method used for determining hydrogen in steel must be sensitive and precise. In any analytical procedure for gases in metals there are two distinct operations—the extraction of the gas from the metal and the analysis of the extracted gas. To extract the gas from the steel, three methods have been employed: 1) fusion of the sample with graphite at high temperature; 2) fusion with a flux, such as tin, at a lower temperature; and 3) extraction of the hydrogen from the solid sample at a temperature below the melting point of the steel. Fusion with graphite is the least-acceptable method. The blank in this method is higher and more variable than in either of the other two methods. The hydrogen fraction of the total gas composition usually is between 10 and 50 pct; thus, a larger analytical error is possible. The vacuum-tin fusion4 extraction of hydrogen is probably the most rapid method in use today; the extraction time is usually about 10 min. However, with this system a bake-out of the freshly charged tin for 2 hr is necessary and a change of crucible and a charge of fresh tin are required after each day of operation whether one or thirty samples have been analyzed. In addition, frequent checks of blank rates are required since CO and Na are continually being given up by the steel samples dissolved in the tin bath. The composition of the gas in this method lends itself readily to analysis; although the hydroge concentration may fall to as low as 50 pct, more often it is above 90 pct, thus allowing a more precise analysis (because of less interference from other gases). In 1940 ewell' published the hot-extraction method for extracting hydrogen from the solid sample, comparing analysis for hydrogen extracted at 600°C with similar analysis for the gas extracted at 1700°C by fusion with graphite. Good agreement for hydrogen was obtained between these two methods, provided sufficient time was allowed for extraction at the lower temperature. carsone obtained good results in his comparison of this hot-extraction method with vacuum-tin fusion. Subsequent work by Geller and sun7 and Hill and ohnson' has shown that steel samples should be heated to at least 800°C to effect the release not only of the diffusible hydrogen but also of the "residual" hydrogen that may be present as methane. Since the rate of evolution of hydrogene9l0 depends on such factors as sample size and composition, thermal history, and extent of cold work, a fixed extraction time is not possible. Extraction times of 30 min are normal, but 2 hr are not unusual. Induction or resistance heating may be used in the hot-extraction method. With resistance heating the

Jan 1, 1964

By C. W. Sherman, N. J. Grant

The correlation of the high temperature chemical properties of slag-metal systems with some easily measured property of either slag or metal at room temperature has been the goal of both process metallurgists and melting operators for many years. There are several rapid methods for estimating various constituents in steel in addition to the conventional chemical methods which are quite fast, but these do not reveal the nature of the slag as a refining agent, which is of primary interest to the steelmaker. Furthermore, there are several methods for examining slag, the three principal ones being slag pancake, petrographic examination, and the previously mentioned chemical analysis. The main objection to the last two is the lime required to make a satisfactory estimate of the mineralogical or chemical components. The objection to the first is the inadequacy of the information obtained. A new technique has been developed by Philbrook, Jolly and Henry1 whereby the properties of slags are evaluated from an aqueous solution leached from a finely divided sample of slag. It is known that the pH or hydrogen ion concentration (of saturated solutions that have dissolved certain basic oxides, notably calcium oxide) will indicate a pronounced basicity. Philbrook, Jolly and Henry devised the pH measurement technique in order to supply open hearth operators with a fast, reasonably accurate method of estimating slag basicity. They offered the method as an empirical observation and made no claims as to its theoretical justification. The results were presented as an experi-metally observed relationship which applied over an important range of basic open hearth slags. They found that, in plotting the measured pH against the basicity, the best relationship existed between the pH and the log of the simple V ratio, CaO/SiO2. Extensive investigation also showed that there were several variables in the experimental technique that influenced the results and necessitated following a standard procedure to obtain reproducible pH readings. These variables were: 1. Particle size of the slag powder used. 2. Weight of sample used per given volume of water. 3. Time of shaking and standing allowed before the pH was measured. 4. Exclusion of free access of atmospheric carbon dioxide to the suspension. 5. Temperature of the extract at the time the pH was measured. In subsequent investigations of the pH method by Tenenbaum and Brown2 and by Smith, Monaghan and Hay3 the general conclusions of Philbrook's work were reaffirmed. It was the object of the present investigation to extend the technique to a point where it could be used to evaluate slags of all types. Experimental Results PARTICLE SIZK OF SLAG POWDER A large sample of commercial blast furnace slag of intermediate basicity (V-ratio 1.15) was selected for the study. The slag had been put through a jaw crusher until all of it passed through a 20 mesh screen. Five fractions of this crushed material were separated, -20 to +40, -40 to +60, -60 to +100, -100 to +200, and -200 mesh. A representative sample of 0.5 g was removed from each fraction and the pH determined using the method of Philbrook. Check pH analyses on the sample fractions varied due to the different amounts of shaking. To eliminate this variable, a mechanical shaker was employed. In order to know the exact time of contact between the slag and water, it was found necessary to filter the extract at the end of the shaking period. Using the mechanical shaker and a filtering apparatus, similar runs were made on the five fractions for contact times of 5, 10, 20, and 40 min. Random checks gave reproducible results within 0.02 pH. The data are plotted in Fig 1. It can be seen from the plot that each slag fraction is hydrolyzed to an extent that is roughly proportional to the surface area exposed to the water. The (—100 to +200) mesh material changed very little in pH after 10 min. shaking time. The curves are symmetrical and lie in proper relation to one another. The —200 mesh curve appears to be somewhat flatter than the others, but this can be attributed to the portion of very fine material that is not present in the other fractions. The closeness of the (-100 to +200) mesh curve to the —200 mesh curve and the fact that a —100 mesh sample would contain amounts of slag down to 1 or 2 microns in diam were considered sufficient reasons for selecting a —100 mesh sample as representative of the whole sample of slag for the purposes of this investigation.

Jan 1, 1950

By P. D. S. St. Pierre

IN recent years the use of high sulphur fuels and charges in steelmaking has necessitated rapid methods of slag control in order to insure the production of high quality steel. Several systems of control have been discussed in the literature, and of these the method described by Philbrook, Jolly, and Henry' has received the most attention recently. In their process the hydrogen ion concentration of an aqueous slag suspension is determined under controlled, but arbitrary conditions. The basicity of the slag may then be derived from a previously established pH-V ratio curve. Thus, by measuring the pH, some indication of the V ratio is gained, from which significant properties of the slag may be deduced. Philbrook et al. made no claims as to the theoretical justification of their treatment, but simply offered it as a rapid means of slag control. Encouraging results caused others to study the method and publish their findings.2-5 Although there was fair agreement on the efficacy of the method, no common parameter was evolved against which pH readings could be plotted. The results of the various determinations were related to such V ratios as CaO/SiO2 and CaO/ SiO2 + P2O5 by some,'-3 while others" plotted against "excess lime." Rivet,' however, found a simple proportionality between the hydrogen ion concentration and the sulphur content of the molten steel beneath the slag. Since slag control in North American practice is largely directed toward the efficient removal of sulphur from steel, Rivet's approach to the problem had the advantage of connecting directly a property of the slag with the impurity being removed. In view of the diversity of parameters used it seemed probable that some fundamental point was being overlooked in seeking a relationship. Examination of the literature revealed that much emphasis had been laid on experimental detail but scant attention paid to the fundamental aspects of the hydrolysis of the aqueous slag suspension. Consequently the present investigation was undertaken with the object of rectifying this deficiency and deriving, if possible, a parameter of general application. Petrographic studies on several matured Canadian open-hearth steel slags have shown that their major constituents are dicalcium and tricalcium silicates set in a complex matrix of iron oxides and ferrites. These phases are shown in Figs. 1 and 2. Free lime is frequently encountered in slags, but is not an equilibrium phase since on continued heating it dissolves forming silicates or ferrites. Thus, it appeared that a study of the hydrolysis of the major phases in steel slags would be profitable. The experimental technique used in the present work was a modification of that described by the other workers.'- Electrical conductivity measurements were also made on the suspensions, since Smith et al." had claimed advantages for this method in their paper on slag control. Experimental Procedure The compounds studied in this investigation were prepared in the laboratory by heating purified oxides

Jan 1, 1954

By D. J. Carney, E. C. Rudolphy

IT has been demonstrated that inclusion size, distribution, and composition affect the machin-ability of resulphurized steels. Merchant and Zlatinl concluded that large sulphide inclusions aided machining by forming a (lubricating) coating on the tool face. Boulger et al.² and Van Vlack³ noted that the size, distribution, and composition of the inclusions in the steel affected the machinability. Steel specimens containing large globular sulphide inclusions usually exhibited excellent cutting properties, while machinability was adversely affected by the presence of numbers of oxide-type inclusions. Consequently a thorough knowledge of all the factors which affect the inclusions in the final product is desirable. Since almost all the inclusions have their origin in liquid steel, it was necessary to begin a study of inclusions in free-machining steels by studying the inclusions and chemical segregation in the as-cast ingot. Very little information is available on the size, distribution, shape, and composition of inclusions in large, capped, free-machining steel ingots, particularly the B1113 grade. Gregory and Whiteley4 made a general study of the inclusions in a small, high sulphur, free-machining steel ingot. Also, numerous authors have described the solidification and segregation characteristics of the four basic types of steel ingots, namely, rimmed, capped,7 semikilled,7,8 and killed7,9,10 ingots. Most of these studies were made with plain carbon or low alloy, low sulphur steel. It was desirable to study not only the ingot but also the change in size, shape, and number of inclusions on rolling an ingot to a bloom and thence to a billet. This procedure was followed and it is hoped that this study may serve the dual purpose of adding to the general knowledge of ingot solidification as well as contributing to the knowledge of the size, shape, distribution, and composition of inclusions from the ingot to the billet in a high sulphur, free-machining steel. Procedure A 12.000-lb 23x35x75 in. slab ingot of the B1113 grade was cast, sectioned, and studied both macro-scopically and microscopically. An adjacent ingot from the same heat and of the same size was rolled to a 77/8x77/8 in. bloom and thence to a 21/2x21/2 in. billet. These various bloom and billet sections were also sectioned and studied macroscopically and microscopically. Sectioning the Ingot: The ingot herein described was obtained from the United States Steel Corp.'s South Works Bessemer Blow No. 0193, a B1113 mechanically capped heat. The 23x35 in. ingot (No. 2) was teemed according to normal procedures and after stripping and transportation to the rolling mill was not placed in the soaking pit but allowed to air cool in an upright position. When completely solidified, the ingot was cut into sections by means of a powder scarfing torch and further sectioned by saw cutting as indicated in Fig. 1. Cut No. 2 (1x10x12 in.) from sections A through H was cleaned thoroughly, macroetched in a solution of 50-50 water and hot muriatic acid and used to obtain a macrograph of a horizontal section from the surface to slightly beyond the center of the 23-in. ingot dimension. Cuts No. 5 and 3 (lx81/2xl0 in. each) from sections A through H were treated in a similar manner to obtain a macrograph of a horizontal section from the surface to slightly beyond the center of the 35-in. ingot dimension. The composite macrograph of these horizontal ingot sections, which shows a vertical section of the ingot from top to bottom, is shown in Fig. 2. It should be noted that sections No. 2 are normal to sections 5 and 3 in the composite. Drillings for chemical analyses were obtained from selected positions within the above-mentioned ingot sections as noted in Fig. 3. The oxygen content was determined by the vacuum-fusion method. Samples for microscopic examination were cut from

Jan 1, 1954

By C. E. Birchenall, G. Derge

IN studying the kinetics of slag-metal reactions, it has become increasingly apparent that a complete knowledge of all aspects of interface phenomena will be required to clarify these processes adequately. A part of the data required for all oxidizing slags used in the refining of impure iron to steel is the rate of exchange of iron between the slag and metal phases. The simplest equilibrium of this type is that between liquid iron and iron silicate slag when both phases are equilibrated with the silica crucible containing them. In this study, the exchange of iron between the two liquid phases has been measured by using radioactive Fe as tracer. The observed high exchange rate indicates the ease with which such interfaces may be crossed in refining processes. The experiments required for this study involved relatively minor and normal modifications of well established techniques. Melting was accomplished by induction heating in heavy walled, fused silica, rotating crucibles." Rotation was used to minimize dilution of the slag by crucible erosion. The melting stock was ingot iron. Slags were prefused in iron crucibles using chemically pure grade oxide reagents. The special conditions applying to the active iron additions will be described for individual experiments. Suitable precautions were observed with regard to protection against radiation hazards.' Identification of Activity This particular study was initiated several years ago, but held in abeyance because the radioactive iron available at that time contained a foreign activity which concentrated in the slag so as to mask the iron activity and render the results unin-terpretable. With the benefit of experiences from other studies, radioiron of suitable purity can now be prepared. As received from the Isotope Div. of A.E.C., the unit appears to contain Fe + Fe50 and a high activity cobalt. The cobalt and iron are separated by repeated ether extractions, and the purified iron stored for sufficient time for the Fe'7 44 day half-life) to decay to negligible activity, leaving only Fe as the active isotope. This was confirmed by the absorption curves for slag and metal samples from heat No. 1. In Fig. 1 the experimentally measured points for the absorption curves of slag and metal are fitted by the calculated slope of 5.8 mg per sq cm in aluminum, which corresponds to the Mn K doublet emission resulting from the capture of an orbital electron of Fe" by the nucleus. This shows that the radioactive species are the same in both slag and metal and identifies it as Fe55 Description of Individual Heats For the first heat, the radioactive iron was contained in the prefused slag. The active Fe55 had been precipitated with carrier and was added as Fe2O3 during fusion in the iron crucible. The charge of 500 grams of ingot iron was melted, the protective iron sleeve added, rotation started, and a prefused, inactive slag was added to allow the system to approach equilibrium. After about 5 min at temperature, the wash slag was skimmed and the active slag added. Initial slag and metal samples were taken as soon as the slag was molten. Additional samples were taken at indicated intervals thereafter. Slag samples were dipped with a small iron spoon and metal samples were sucked into 1/4 in. ID silica tubes. The slag and metal samples were pulverized and mounted for radioactive counting. The slag samples were analyzed chemically for FeO. Temperature was read after the last slag sample by immersion of a Pt-Pt-Rh thermocouple protected by a fused silica sheath. Since no significant variation of rate with temperature was observed

Jan 1, 1954

By F. L. Toy, C. E. Sims

PNEUMATIC processes for converting molten pig iron to steel were the major producers of steel during the latter half of the 19th Century and until shortly after the turn of the century, when these processes began losing ground to their rival—the basic open hearth process. The first pneumatic process for converting molten pig iron to steel was introduced almost simultaneously by Sir Henry Bessemer in England and by William Kelley in the United States during the decade 1850-1860, but it was Bessemer who pushed it to a successful commercial operation. The process itself is so basically simple that it has not lent itself to many extensive or revolutionary improvements since its inception. During the first 30 yr, numerous' designs of vessel and many modifications of practice were tried before the industry standardized on something resembling current practice. The evolution in construction has resulted in proportions and arrangements based more on mechanical expedience than on metallurgical requirements. Many of the early converters were stationary and had to be tapped similarly to the cupola or open hearth furnace. Such types were used for many years in Sweden and Germany, but the rotating or tilting types were favored in England and the United States. There was evident trouble with bottom tuyeres, becAuse about half of the early designs were constructed for side blowing with tuyeres submerged below the metal-bath surface. Even portable tuyeres, introduced from above, were tried. The principal advance, which made bottom blowing practical, was the invention, in 1863, by Henry Bessemer, and subsequent improvement by A. L. Holley, of a detachable bottom so that the tuyere section could be renewed. In the meantime, it was the demonstration, by Robert Mushet, of the value of manganese in overcoming hot-shortness in converter steel, that made the process metallurgically feasible. At first, only the acid practice was used, and Swedish pig iron, because of its low sulphur and phosphorus, was in great demand. The development of a suitable basic lining, by Sidney G. Thomas and Percy G. Gilchrist in 1876-1879, made the process applicable to the high-phosphorus ores of Europe. From the beginning of the use of the Thomas-Gilchrist process, trouble was experienced in obtaining sufficiently high temperatures in the blown metal, particularly in small heats. It is necessary, of course, to have the low-carbon blown metal at a considerably higher temperature for handling from vessel to ladle to molds than is needed for the molten pig iron. All of the increase in temperature in a pneumatic process must be obtained from the heat of combustion of the elements contained in the pig iron plus that from silicon when ferrosilicon is added. In bottom blowing practice, carbon is almost completely burned, but inasmuch as it cannot be oxidized to a higher state of oxidation than to CO when in contact with liquid iron, only a minor portion of the heat-producing capacity is utilized. Under such conditions, it is not considered to be an efficient source of heat. In the acid practice, therefore, silicon and manganese are the large heat producers, are quickly oxidized, and are efficient fuels. Too much manganese, however, thins the slag greatly and tends to promote excessive slopping or throwing of slag and metal from the converter during the blow. Most operators, therefore, like to keep the manganese content of the iron below 0.60 pct, and thus the main source of heat is the silicon, which must be at least 1 pct and sometimes 2 to 3 pct for small blows such as for castings. Ferrosilicon is sometimes added during the blow to obtain an adequate temperature level. In the basic (Thomas) practice, even more heat is required, because cold lime is added to flux the phosphorus after it is oxidized, and the basic slag must be maintained at a proper temperature. Silicon

Jan 1, 1951

By F. L. Toy, C. E. Sims

I. A. Sirel—I would like to ask Mr. Sims what would the preferred hot metal analysis be as far as manganese and silicon are concerned if you used specially made iron for this process instead of basic iron. C. E. Sims (authors' reply)—A preferred composition would contain somewhat less silicon than the basic pig iron used in these experiments. High silicon requires a large lime addition. Lime must be added in sufficient quantity to neutralize the silica formed and to leave an excess for dephosphorization. Manganese presents almost no problem in operation. It is almost completely oxidized and, in burning, develops considerable heat. The evidence indicates, however, that, in continuous commercial operation, there will be an excess of heat produced, and the bath will need to be cooled in some manner as by the addition of scrap or by utilizing the energy for the direct reduction of ore. There do not seem to be any serious limitations on composition of pig iron. One heat was made with an iron containing 2.27 pct silicon and the phosphorus finished at 0.007 pct. In another, the iron contained 0.45 pct phosphorus which was lowered to 0.019 pct. This indicates considerable leeway in composition. D. R. Loughrey—We are all very much interested in the recent discovery of very large deposits of iron ore both in Labrador and in Venezuela. I would like to ask Mr. Sims if the iron ore at either or both of these places is such that it would lend itself to the manufacture of iron suitable for use in the turbohearth. C. E. Sims-—According to my information, those ores are not essentially different from ores now used in this country for making basic pig. They should, therefore, be adaptable to this process. D. I. Brown—You have spoken about the leeway, or spread in analysis of the various irons you can use in the vessel. I would like to have you tell us, if you can, about the different kinds of steels which can be made in such a vessel. The turbohearth process, or it might more aptly be called pneumatic openhearth, is a little different from that used in most Bessemer shops and in the one in which I worked. If we had a blow in the air over 10 min, the boss was in the pulpit in a hurry

Jan 1, 1951

By W. A. Griffith

Fractional replication of factorial design, a general method for planning experimentation and for analysis of data obtained, is described as applied to a flotation investigation. This method leads to determination of optimum process conditions with minimum experimental effort. Its advantages over simple factorial design are demonstrated. A METHOD for planning experimentation and for analyzing the data secured will be demonstrated. This method, termed fractional replication of factorial design, employs a relatively small number of individual experiments to determine which of a large number of process variables are controlling, to determine which combination of levels of these variables is most likely to produce optimum results, and also to predict what results will be obtained with a particular combination of conditions not already tested. Although the general method is not new, having been developed by Finney in 1945,' the extent to which it can improve the effectiveness of applied research generally has not been recognized by metallurgists. The fractional replication procedure is particularly useful in flotation experimentation and an example from such an investigation will be used in the paper. However, it has equal value in any investigation in which similar experimental difficulties are encountered. In developing a flotation process for a particular mineral separation, the investigator is inevitably confronted with the following difficulties: 1—There are a large number of potentially important process variables. 2—Results of individual experiments are not highly reproducible, due in part to the difficulty in precisely controlling all the variables. 3—Considerable effort is expended in conducting individual experiments. 4—There are practical limits on the number of individual experiments which can be made. In situations of just such a type, modern statistical methods of planning experimentation and analyzing data have their greatest value. Applications of one such technique, called factorial design, to problems of this type have been described by Dorenfeld and others.'-' The simple factorial design is an efficient procedure when the investigator hopes to provide a comprehensive understanding of the effects and interrelationships of a small number of variables over a limited range. In applied research, this is seldom the main objective. Rather, the investigator usually wishes to determine which of the many potentially important variables are in fact controlling, which levels of the controlling variables will provide opti- mum metallurgical results, and what these results will be at optimum conditions. Interest in detailed trends is limited to the controlling variables and to levels in the region of optimum conditions. Simple factorial design has serious deficiencies for such objectives and is not the most efficient method of experimental design. Deficiencies of Factorial Design In a simple factorial design, an experiment must be made at every possible combination of each level of every variable, once these have been chosen and the levels of each to be included have been decided upon. As the number of variables or levels of each increases, the experimental program quickly reaches prohibitive size. For example, an investigation of only four variables, each at four levels, requires 256 individual experiments. Often upon completion of such an extensive program, it is found that one or more of the variables has metallurgically unimportant effects or that a poor estimate has been made as to the appropriate range of levels to be investigated. The result is that only a small proportion of the data obtained falls in the range of real metallurgical interest. Indeed, it frequently can be anticipated that certain combinations of levels of variables will not produce results of interest, but they still must be included so that the essential balance, or orthogonality, of the design will be retained. It may be true that factorial design will provide the greatest amount of information from a given number of experiments, but it does not necessarily follow that it will lead to the desired information with a minimum number of experiments. Much of the information provided may be of little value. Advantages of Fractional Replication The disadvantages of simple factorial design are overcome to a great extent by a modification known as fractional replication. This is a technique for sampling systematically the potential data of a full factorial experiment, that is, the data which would have been obtained if the complete factorially designed program had been completed. Only a fraction of the total array of experiments is made, but the experiments are chosen in such a way that the important advantages of factorial design and the accompanying analysis of variance are retained. The data obtained from the first group of experiments are used to determine which of several variables are controlling and which levels of these variables are most likely to produce the desired result. Unimportant variables and levels of variables then may be

Jan 1, 1956

By Takashi Katsura, Avnulf Muan

Equilibrium relations in the system FeO-Fe2O3 Cr2O3 have been determined at 1300°C at oxygen pressures ranging from that of air (0.21 atm) to 1.5 x 10-11 atm. The following oxide phases have stable equilibrium existence under these conditions : a sesquioxide solid solution with corundum-type structure (approximate composition Fe2O3-Cr2O3); a ternary solid solution with spinel-type structure (approximate composition FeO Fe2O3-FeO Cr2O3) and a ternary wüstite solid solution with periclase-type structure and compositions approaching FeO. The metal phase occurring in equilibrium with oxide phase(s) at the lowest oxygen pressures used in the present investigation is almost pure iron. The extent of solid-solution areas and the location of oxygen isobars have been determined. ThE system Fe-Cr-O has attracted a great deal of interest among metallurgists as well as ceramists and geochemists. Metallurgists have studied the system because of its importance in deoxidation equilibria, ceramists because of its importance in basic brick technology, and geochemists because of its importance for an understanding of natural chromite deposits. Chen and chipman1 investigated the Cr-O equilibrium in liquid iron at 1595°C in atmospheres of known oxygen pressures (controlled H2O/H2 ratios). The main purpose of their work was to determine the stability range of the iron-chromite phase. Hilty et al.2 studied oxide phases in equilibrium with liquid Fe-Cr alloys at 1550°, 1600°, and 1650°C. They reported the existence of two previously unknown oxide phases, one a distorted spinel with composition intermediate between FeO Cr203 and Cr3O4, the other Cr3O4 with tetragonal structure. They also sketched diagrams showing the inferred liqui-dus surface and the inferred 1600°C isothermal section for the system Fe-Cr-O. Koch et al3 studied oxide inclusions in Fe-Cr alloys and also observed the distorted spinel phase reported by Hilty et al. Richards and white4 as well as Woodhouse and White5 investigated spinel-sesquioxide equilibria in the system Fe-Cr-O in air in the temperature range of 1420" to 1650°C, and Muan and Somiya6 delineated approximate phase relations in the system in air from 1400" to 2050°C. The present study was carried out at a constant temperature of 1300° C and at oxygen pressures ranging from 0.21 atm (air) to 1.5 x 10-11 atm. The chosen temperature is high enough to permit equilibrium to be attained within a reasonable period of time within most composition areas of the system, and still low enough to permit use of experimental methods which give highly accurate and reliable results. These methods are described in detail in the following. I) EXPERIMENTAL METHODS 1) General Procedures. Two different experimental methods were used in the present investigation: quenching and thermogravimetry. In the quenching method, oxide samples were heated at chosen temperature and chosen oxygen pressure until equilibrium was attained among gas and condensed phases. The samples were then quenched rapidly to room temperature and the phases present determined by X-ray and microscopic examination. Total compositions were determined by chemical analysis after quenching. In the thermogravimetric method, pellets of oxide mixtures were suspended by a thin platinum wire from one beam of an analytical balance, and the weight changes were recorded as a function of oxygen pressure at constant temperature. The data thus obtained were used to locate oxygen isobars. The courses of the latter curves reflect changes in phase assemblages and serve to supplement the observations made by the quenching technique. 2) Materials. Analytical-grade Fe2O3 and Cr2O3 were used as starting materials. Each oxide was first heated separately in air at 1000°C for several hours. Mixtures of desired ratios of the two oxides were then prepared. Each mixture was finely ground and mixed, and heated at 1250" to 1300°C in air for 2 hr, ground and mixed again and heated at the same temperature for 5 to 24 hr, depending on the Cr2O3 content of the mixture. A homogeneous sesquioxide solid solution between the two end members resulted from this treatment. A Part of some of the sesquioxide samples thus prepared was heated for 2 to 3 hr at 1300°C and oxygen pressures of 10-7 or 1.5 x 10-11 atm. Reduced samples (either iron chromite

Jan 1, 1964