By M. Herman, G. J. London

A series of dilute Fe-Co alloy specimens were prepared from zone-melted iron. The iron used was given ten floating-zone passes in purified hydrogen. Alloying was accomplished by plating a gradient of metallic cobalt onto a 1/4-in.-diam bar of material from a pure plating bath. The deposit was radioac-tively tagged by a small addition of co80 to the plating bath. Alloy homogenization was accomplished by passing an additional floating-zone pass through the plated section of the bar. The final concentration gradient achieved was from residual to about 1000 ppm (0.1 pct) added Co. After homogenization, the bar was swaged to 0.057 in. wire and cut to tensile specimen blanks 1-1/16 in. long. Each specimen was counted in a well-type scintillation counter. The concentration of cobalt was computed by combining the normalized specimen counting rate with the known weight (measured to the nearest 0.01 mg) of cobalt added during plating. Fig. 1 shows the cobalt gradient obtained, exclusive of residual cobalt which was estimated by neutron-activation analysis to be approximately 50 ppm. Results of recrystallization for 1 hr at 750°, 700°, 650°, and 600°C with specimens containing 40, 170, 470, and 870 ppm added Co are shown in Figs. 2, 3, 4, and 5. Recrystallization was accomplished in a dynamic vacuum of less than 1 x 10 torr. The specimens were mounted and polished parallel to the swaging direction. The recrystallization re- sults show a radical coarsening of structure with increasing cobalt concentration. The coarsest structure obtained was at the 470-ppm level (at all recrystallization temperatures) with a slight grain refinement at the 870-ppm level shown. A more normal solid-solution effect is seen in Fig. 5 (60OoC, 1 hr) where the only specimen completely recrystallized is the one containing 47 ppm Co. Since the possibility existed that some atmosphere-contamination phenomenon might be responsible for the observed results the recrystallization series was repeated using sealed quartz capsules. These were filled with purified argon which was gettered during heat treatment on metallic titanium included in the capsules. The results obtained were essentially the same as shown. Another identical alloy was made using a 5-mm-diam bar of Westinghouse Puron. Specimen preparation and recrystallization treatment were also as described. The results obtained (see Table I) were somewhat erratic. Some coarsening in structure does appear at the highest cobalt concentrations. There is no apparent relationship between the coarse, columnar, directionally solidified structure of the as-melted bars and any of the recrystallized grain structures observed, all of which are much finer than the former structure. A recrystallization process can be most simply described as one of homogeneous nucleation of recrystallized grains in a cold-worked matrix followed by more or less uniform growth of the strain free grain into the cold-worked material.' An impurity element may influence one or both of these processes. Aust and utter' have shown that impurities strongly influence grain boundary mobility in lead. Moreover, definite recrystallization textures are produced by small concentrations of tin,3 while additions of silver or gold4 produce large boundary in-

Jan 1, 1964

By W. D. Robertson, D. A. Koss, A. J. Goldman

THE significance of the hcp (E) structure, which appears when Fe-Cr-Ni alloys (stainless steels) are transformed martensitically, has been the subject of considerable study and speculation.'-7 It has been proposed that the hcp structure is an intermediate phase in the transformation: fcc (austenite) — hcp (E) -bcc (0, martensite). However, recent studies by transmission electron microscopy6,7 have indicated that the hcp structure may be a consequence of the large shear strain (10 deg) associated with the fcc to bcc transformation. That is, the transformation to a bcc structure is accompanied by extensive dissociation of dislocations in the parent austenite, which has a low stacking-fault energy.'-'' X-ray diffraction analysis of the transformed alloy reveals a pattern of lines corresponding to an hcp structure, together with the parent austenite and the bcc product. The fact that the hcp structure is observed only in association with the bcc product in these alloys1'4'6'7 lends support to the conclusion that the hcp structure is a secondary product of the transformation. But, the evidence is circumstantial and more definite resolution of the two possibilities mains to be obtained. If the hcp structure is an intermediate product of the transformation, as in 1) above, then two distinct Ms temperatures should be observed, Ms and To evaluate this possibility, three different techniques that are particularly sensitive to the structural changes accompanying such transformations have been used in an attempt to detect two transformation temperatures in an Fe-15.1 Cr-11.7 Ni alloy: 1) high-sensitivity differential thermal analysis, 2) the temperature dependence of resonant frequency (elastic moduli), and 3) internal friction of cylindrical specimens vibrating in either longitudinal or torsional modes. To obtain the necessary sensitivity, a differential thermal analysis technique was developed for the purpose, Fig. 1. The differential temperature between a nickel standard and the specimen was amplified to produce a sensitivity of 0.02OC (0.7 v) in temperature difference. The specimen and the standard were surrounded by a copper block and the entire assembly was immersed in a solution of methyl and ethyl alcohol, freezing point, - 140OC, which provided the necessary thermal stability to reduce temperature fluctuations to negligible proportions. A cooling rate of about 1.5OC per min was obtained by bubbling liquid nitrogen through the liquid bath. In order to calibrate the experiment with respect to the evolution of heat in the transformation from fcc to hcp structures, differential cooling curves were obtained for an Fe-19.8 Mn alloy, which transforms martensitically to E.'"-' a Ms(e) temperature of 145°C was clearly defined by a temperature

Jan 1, 1964

By N. J. Grant, B. C. Giessen, R. Koch

The system Nh-Ir was investigated over the complete concentration range by metallography and X-my techniques, using forty one alloys. The solubility limits of terminal and intermediate phases and the solidus temperatures were determined. Five intermediate phases were found: a Nb3Ir, cubic, Cr3O type; tetragonal, ofecr thorhomhic, isostruc-turn1 with (ta-Rh); and a Nhlr3. cubic, AuCu, type. a Nb3lr and a Nbfr3 melt congruently; three eutectic and three pentectic reactions occur. The phase diagram of the Nb-Ir system had not been fully treated in the literature; only surveys of intermediate phases were found.1"5 In this study, the details of the phase boundaries were investigated as well as the crystallography of the intermediate phases. EXPERIMENTAL METHODS The experimental procedures such as arc melting of powder compacts, heat treatments, solidus measurements, X-ray, and metallographic observation were identical with those used in the work on the Nb-Rh phase diagram.&apos; They will therefore not be repeated here except where the conditions differed. The purity of the niobium powder was as stated in Ref. 6; the iridium powder of 99.9+ pct purity from J. Bishop and Co., Malvern, Penn., did not contain impurities exceeding 100 ppm, except rhodium (200 ppm). The melting points and vapor pressures of both elements are very similar. This fact contributed to a very small weight loss on melting and facilitated preparation of homogeneous alloys. As shown in Ref. 6 for Nb-Rh, no oxygen pick-up exceeding 200 ppm had to be considered; this was regarded as valid also for Nb-Ir. A total of forty one alloys were used in the determination of the phase diagram; their concentrations are shown in Fig. l, which presents the phase diagram. The concentration limits as determined by the weight-loss method averaged <0.2 at. pct, and never exceeded 0.5 at. pct. Heat treatments were carried out as described in Ref. 6. Depending on the concentration, only tantalum, tungsten, or iridium containers were employed, avoiding oxide crucibles altogether. Alloys from 0 to 25 and from 65 to 100 at. pct Ir were homogenized at 2095°C for 15 hr, intermediate compositions from 25 to 65 at. pct Ir for 65 hr at 1780°C. A typical annealing-time schedule is presented in Table I. Solidus points were measured as described in Ref. 6 with the modification that samples rich in niobium were held between pieces of tantalum foil and samples of high iridium concentrations were held between rhenium platelets or in iridium wire. After each run it was ascertained metallographically that no reaction with the holder had occurred. Rhenium was selected as holder material after it had been shown in separate tests that the melting points of Re-Ir alloys rise continuously from 2440°C. Metallographic examination was carried out as described in Ref. 6, and the same procedure and etchants were used successfully. While metallographic discrimination between a Nb3lr and o was easily possible, X-ray diffraction was necessary to separate al and ct2. X-ray powder patterns were taken and evaluated as for Nb-Rh6 yielding the error limits indicated in Table 111, to be introduced later. For the determination of the invariant reactions and phase boundaries, the same techniques as for Nb-Rh6 applied. The general accuracy of invariant concentrations is regarded as somewhat higher than for Nb-Rh due to the small slope of most solvus lines.

Jan 1, 1964

By J. J. Gilvarry

Recently, Gilvarry1,2 has given a rigorous derivation of the proper distribution function for fragment size in single fracture, based on a closely defined physical model and deduced strictly by the laws of probability. The physical point of departure is Griffith&apos;s theory of brittle strength, identifying sub-microscopic flaws as the cause of the low strength of a solid in comparison with values implied by cohesive energies. Gilvarry and Bergstrom,4-7 and Gilvarry8 have compared the predictions of the theory with experiment, and have found excellent agreement, in general. The purpose of this communication is to sketch the extension of the theory to the case of comminution, and to indicate the applications to some examples in nature. The present treatment represents an amplification of a brief discussion appearing elsewhere. 9 Although the basic ideas of the Griffith theory are perfectly general for rupture of brittle solids, it was originally formulated with very brittle materials such as glass in mind. Moreover, Griffith&apos;s original experimental work was carried out on glass specimens. Recently, however, the theory has been extended by race" to apply directly to rocks. This extension makes the theory immediately applicable to the materials generally of interest from the standpoint of comminution. GENERAL CASE To obtain the distribution function for fragment size in single fracture, three assumptions are made, that: 1) Fracture proceeds by activation of preex-istent Griffith flaws in the volume, faces, and edges of a fragment; 2) the distributions of flaws of these three types are independent of each other; and 3) activated flaws of a particular type are distributed at random, individually and collectively, in the sense of Fry.11 The last assumption implies that each distribution is separately of Poisson type.

Jan 1, 1964

By H. Becke, D. Stolnitz, D. Flatley, W. Kern

Zinc difhsions in gallium arsenide having surface concentrations as low as 5 x 10&apos;&apos; atoms per cu cm have been attained. A multiple-difhsion sequence is employed during which zinc enters the gallium arsenide from a silicon dioxide film in a solid-to-solid diffusion step. The technique is illustrated for the case of a zinc surface concentration of -1 x 1017 atoms per cu cm and a junction depth of 1.2 p. Radiotracer measurements of -0.1-p layers of gallium arsenide are used to delineate the resulting profile. A diffusion coefficient for zinc in pyrolytically deposited silicon dioxide is reported. ZINC is frequently used as an acceptor impurity in gallium arsenide. As examples, p-n junctions are formed using zinc-diffused layers in solar cells, lasers, and varactor diodes. For these purposes surface concentrations of 10&apos;&apos; to over loz0 zinc atoms per cu cm are desired and readily obtained from a vapor source. Diffusion of zinc into gallium arsenide to yield surface concentrations of about 1017 atoms per cu cm, however, is more difficult. For instance, oldstein&apos; reports that large changes in the vapor density of zinc produce only small changes in surface concentration. Such low surface concentrations are necessary in forming the diffused base of a gallium arsenide double-diffused n-p-n transistor in order to obtain an adequate emitter efficiency. An alternative approach to zinc diffusion which can provide reduction in surface concentration of several orders of magnitude is the introduction of the diffusant from a solid source. This can be conveniently accomplished by using oxide films of the type generally employed for selective diffusion masking. Such oxides also serve to prevent the dissociation of the gallium arsenide surface at the high temperatures of diffusion. DIFFUSION PROCEDURE Fig. 1 illustrates the diffusion sequence which is employed for obtaining zinc surface concentrations in the range from 5 x lom to 1 X 10" atoms per cu cm. The description of technique will be given for the instance of -1 x 1017, which is typically utilized in double-diffused gallium arsenide transistor investigations at this laboratory. Tin- or germanium-doped gallium arsenide wafers drawn from crystals grown by horizontal Bridgman or Czochralski techniques are used, with bulk concentrations ranging from 1 to 3 X 10" carrier atoms per cu cm. Each wafer is chemically polished on the (iii) arsenic face using a mixture of five parts concentrated sul-furic acid, one part water, and one part 30 pct hydrogen peroxide at room temperature, followed by rinsing in deionized and quartz-distilled water. Pyrolytic silicon dioxide was chosen as the oxide coating because of the high quality of the films obtainable, the ease of their preparation, and the excellent control over film thickness and uniformity.

Jan 1, 1964

By J. D. Mote, A. Rosen, J. E. Dorn

The effect of strain rate and temperature on the critical resolved shear stress for (1100) [1120] prismatic slip was determined for the intermediate hexagonal phase containing about 67 at. pct Ag and 33 at. pct Al. Whereas the flow stress increased only slightly as the test temperature was first decreased below room temperature, a rapid increase inflow stress was obtained with yet greater decreases in temperature from about 240" to 4°K. The effect of both temperature and strain rate on the flow stress over the low-temperature range could be completely rationalized in terms of the Peierls mechanism when the deformation is controlled by the rate of nucleation of pairs of kinks. A few years ago Mote, Tanaka, and Dorn1 observed that the critical resolved shear stress for prismatic slip of a 67 at. pct Ag plus 33 at. pct A1 hexagonal intermediate phase by the (1100)[1120] mode decreased precipitously as the test temperature was increased from 4" to about 160°K. Their results for both basal and prismatic slip are given in Fig. 1. It is obvious that only the flow stress for prismatic slip is strongly temperature-dependent, whereas the flow stress for basal slip is independent of temperature. If the temperature dependence of the flow stress were primarily due to interstitial impurities, it might be expected that they would influence the flow stress for basal slip as well. Since the activation volume at 115°K for prismatic slip was determined to be about 15b3, where b is the Burgers&apos; vector, this thermally activated deformation process was tentatively ascribed as being due to the Peierls mechanism. But the various analyses of the Peierls mechanism then available as formulated by Seeger2 and also by Lothe and Hirth3 did not agree well with the experimental data. Since that time a more realistic theory for the operation of the Peierls mechanism under conditions where the strain rate is determined by the rate of nucleation of pairs of kinks has been presented by Dorn and Rajnak.4 The present investigation was, therefore, undertaken in order to provide the essential data for a careful check on the agreement between this theory and the low-temperature deformation by prismatid slip of the above-mentioned Ag2A1 intermediate phase. EXPERIMENTAL TECHNIQUE Single-crystal specimens so oriented that the [1120] direction and the normal to the (1100) plane were at 45 * 2 deg to the tensile axis were grown from the congruent melting composition of about Ag2Al for the intermediate hexagonal phase by the

Jan 1, 1964

By J. J. Scott, L. Adler3

L. Adler (Assoc. Professor, Department of Mining Engineering, Virginia Polytechnic Institute, Blacks-burg, Va.) - Dr. Scott is to be commended for undertaking the arduous and specialized task of applying three-dimensional photoelastic techniques to a mining problem. However, 1 feel his analysis suffers seriously from a lack of clarification on one important matter, among several others; and that the paper as a whole lacks balance and thus tends to confuse the reader. 1) The major technical criticism refers to the fact that nowhere are the boundary conditions for his mod-

Jan 1, 1964

By V. R. Thompson, R. C. Westgren

In a recent paper,1 the solid-solution strengthening of tungsten and tantalum in a portion of the W-T;-MO-C~ alloy system was described. Additions of tantalum and columbium to tungsten led to significant strengthening, and the introduction of dispersions into these alloys was suggested as a means of further increasing strength. Dispersion strengthening of columbium and molybdenum alloys has been studied extensively.2-4 The approach used to dispersion-strengthen molybdenum alloys appeared equally suitable for tungsten alloys, and, therefore, a brief study was undertaken to determine to what extent the introduction of carbide dispersions would strengthen a solid-solution tungsten-base alloy. A base composition of tungsten and 10 to 12 pet Cb was selected; previous work1 had shown that the tensile strength of this solid-solution alloy was 50,000 psi at 3000°F. For the study of the effects of small additions of

Jan 1, 1964

By R. G. Davies

Isothermal annealing of quenched Fe3Al reveals that the superlattice forms by the nucleation and growth of ordered domains. The activation energy for isothermal ordering and initial domain growth is -29 keal per mole, which is thought to he the activation energy for vacancy migration. Domain growth, in the absence of excess vacancies, has an activation energy of -100 keal per mole. A maximum in the hardness is observed when the structure consists Of ordered domains, -35-4 in size, growing into a short-range ordered matrix and, also as a function of degree of order, S, with an infinite domain size at S = 0.4 to 0.5. It is proposed that both maxima are due to a transition from deformation by unit dislocations to deformation by superdislocntions. FE-AL alloys containing more than -23 at. pet Al, when quenched from above the critical temperature for the Fe3A1 type of order, always contain the maximum possible amount of FeAl (B2) type of order&apos; (see Fig. 1). Thus when the Fe3A1 superlattice forms, in a 25 at, pet A1 alloy, it does so from an imperfect FeAl structure. The formation of the Fe3Al superlattice has been the subject of several recent X-ray,1, 2 electrical-resistivity,3"6 and dilatometric3 investigations. McQueen and Kuczynski3 concluded that the isotherma1 ordering of Fe3Al, after quenching from 800°C (T,, the critical temperature for order, is 55O°C), takes place by the nucleation and growth of ordered domains. However, Feder and Cahn4 found that the isothermal ordering was complex but more like a homogeneous nucleation process than a nucleation and growth process. Lawley and Cahn2 reported that the degree of order is a continuous function of temperature which is a characteristic of a homogeneous nucleation process. Thus, the evidence is conflicting as to the nature of the Fe3Al ordering reaction. Lipson7 was the first to suggest that ordered domains should exist in the Fe3A1 structure since, as

Jan 1, 1964

By George Mah, Charles Wert

Internal-friction peaks caused by diffusion of oxygen and nitrogen have been observed in ytterbium. They are thought to be caused by the redistribution, under stress, of strain dipoles around an interstitial oxygen or nitrogen and a neighboring substitutional impurity. With the use of a simple geometrical model, diffusion coefficients for oxygen and nitrogen between special interstitial sites have been calculated. a) APPLICATION OF INTERNAL FRICTION TO MEASUREMENT OF DIFFUSION RATES IN DISSOLVED INTERSTITIAL ATOMS In bcc metals, the interstitial atoms occupy the centers of cube faces (0, 1/2, 1/2), or their equivalents, the center of the cube edges (0, 0, 1/2). An interstitial atom in this position causes an aniso-tropic distortion in the lattice. When stress is applied, mechanical relaxation can take place by the movements of the interstitial atoms. This relaxation has been used to obtain information concerning the movements of the interstitial atoms in the bcc metals. Data for these alloys have been compiled by Stanley and Wert. Other researchers have extended the investigation of interstitial diffusion to the close-packed metals. Gupta and weinig2 found an oxygen peak in a titanium, the height of which is linearly dependent on the oxygen concentration. They assumed, therefore, that they were dealing with movement of atomic ally dispersed oxygen in titanium. KG and wang3 determined that the diffusion coefficients of carbon in fcc steels and in nickel obtained by internal-friction methods were consistent with those obtained by macrodiffusion methods at much higher temperatures. Bisogni found oxygen and nitrogen peaks in hafnium by use of which he deduced the diffusion coefficient of these gases in hafnium. He observed further that the half-widths of these peaks corresponded almost exactly with those of a single-relaxation process; he assumed it to be caused by movement of atomically dispersed oxygen and nitrogen. From these studies, the deduction can be drawn that, in general, diffusion data can also be obtained for the interstitial diffusion in close-packed metals (or more precisely, in slightly impure close-packed metals). One group of such metals for which little data exist for the diffusion of dissolved oxygen and nitrogen is the rare earths. They have great affinity for gases, which enter solution interstitially. In this investigation results were obtained for the Yb-O and Yb-N interstitial solid solutions with traces of substitutional impurities; these solid solutions are of fcc structure. b) MECHANISM OF THE RELAXATION IN FCC CRYSTALS In the fcc structure, an interstitial gas atom is usually situated in the octahedral position (1/2, 1/2,

Jan 1, 1964

By P. G. Shewmon, J. Y. Choi

The surface-diffusion coefficient for , has been measured on (111) and (100) surfaces of copper from 1000" to 620°C. D,(Ge) on the (111) is two to three times that on the (100) as was found earlier for copper and gold on copper. D, (Ge) on both (111) and (100) is about thirty times that found for gold or copper tracers on the same surfaces, while in the temperature range where both D,(Ge) and Ds(Au) have been measured the activation energy for germanium is the same as that for gold. The apparent activation energy for Ds(Ge) is not a constant, but decreases with temperature. In a recent paper we reported on the application of a new tracer technique to the determination of the surface-diffusion coefficient (D,) for gold and copper on (111) and (100) surfaces of copper.&apos; In this paper, we shall give the results obtained when the same technique was used to measure Ds for germanium on the (111) and (100) surfaces of copper. In addition to providing data on D., for an additional element on copper, the longer half-life of germanium (275 days) meant that Ds could be measured down to a much lower temperature and thus over a much wider temperature range (1000" to 620°C) than was used in our gold-tracer work (1060" to 780°C) or copper mass-transport studies (1060" to 800). The apparent activation energy for D, (Ge) is essentially the same as that found for gold or copper in the same temperature range, though the values of D, (Ge) are thirty times greater than those found for gold or copper tracers. The most interesting new result found is that the apparent activation energy for Ds(Ge), and thus Do, definitely increases with temperature. Such a trend was much more apparent in Gjostein&apos;s mass-transport work on copper than in our own, though in an earlier paper we mentioned the difficulty of fitting all of our points with one straight line:= No real explanation of this is given though experiments done on grain boundary groove growth at various ambient pressures demonstrate unequivocally that vapor transport plays no part in the increase in activation energy with temperature.

Jan 1, 1964

By L. C. Raymond

Valuations in the mineral industry differ from those of other enterprises because mines and oil wells have a definite life so cannot be considered a perpetuity. This requires that in any mineral-property evaluation the recovery of invested capital is necessary during the life of the property. Capital writeoffs for nonextractive industries are assumed to be continuously plowed back to sustain the operation and produce yields on the capital invested. The extractive or mineral industry, however, generally attempts to return to the investor both interest and principal during the life of a property. Normally this is done currently and the dividend includes both items. Where the mineral properly possesses large reserves and the life factor approximates a perpetuity, the return on investment is generally comparable to that of industrial stocks. The valuation of a mineral property, at best, is based on educated estimates and judgment factors. This is particularly true as it relates to estimating selling prices over a long term or assessing the quality of management. Also, it is possible to make various assumptions as to rapidity of working out the deposit, varying time for start-up of operations, varying earning rates, so as to obtain different results with the same basic facts. Thus it is not surprising that two engineers, irrespective of their abilities, may not agree exactly even when given the same facts, but their results should be close enough to be used in establishing a fair value for trading purposes. The valuation is no better than the source of basic data and the soundness of judgment factors. Fundamentally the basic principles of mineral valuation are similar for base metals, sulphur, oil, or any other mineral. Each mineral, however, requires an engineer to have a knowledge of such factors as its occurrence, distribution, mining and processing methods, and marketing problems in order to gather and analyze all the facts and data that have a bearing on the earning potential of the property. PRESENT VALUE OF A MINERAL PROPERTY In essence the present value of a mineral property is a sum of money in today&apos;s dollars that future earnings from the property are worth. It differs

Jan 1, 1964

By Charles F. Hickey, Eric B. Kula

Thermomechanical treatments applied to the maraging steels include a) cold working in the austenitic condition at 650°F, followed by transformation to martensite and aging, b) cold working in the murtensitic condition and aging, and c) cold working in the aged condition with and without subsequent reaging. The strength increases in these steels are very small compared to the increases observed in conventional carbon and alloy steels. The changes that are observed are compatible with the strengthening mechanisms operative during thermomechanical treatment of conventional steels, however. Differences are caused by the absence of a carbide precipitate and the low work-hardening rate in both the solution-treated and the aged conditions. ThE 18 pct Ni maraging steels represent a class of steels which are finding great interest for high-strength applications.1~2 They are essentially carbon-free, and contain 7 to 9 pct Co, 3 to 5 pct Mo, and 0.2 to 0.8 pct Ti. Although austenitic at elevated temperatures, they can be air-cooled to room temperature to form a martensite, which because of the absence of carbon is relatively soft. On subsequent reheating age hardening occurs and strength levels of 250 to 300 ksi yield strength can be attained. These steels appear to be particularly suitable for studying the response to various thermome-chanical treatments for additional reasons other than the obvious one of attempting to improve their already attractive properties. Thermomechanical treatments can be defined as treatments whereby plastic deformation, generally below the recrystal-lization temperature, is introduced into the heat-treatment cycle of a steel in order to improve the properties. With an absence of intermediate transformation products on air cooling the maraging steels have good hardenability and hence can readily be cold-worked in the austenitic condition prior to transformation to martensite. Further, they can be worked in the martensitic condition prior to aging, and even can be deformed in the fully aged condition. Finally, it is of interest to compare their re- sponse to that of the more conventional alloy and carbon steels, where the role of carbides is important in the strength increase by thermomechani-cal treatments. The thermomechanical treatment of conventional steels has been the subject of a recent review.&apos; I) MATERIALS AND PROCEDURE The steel used in this investigation was a commercially produced vacuum-melt heat, which had been rolled to 0.090 in. and mill-annealed. The composition of the alloy was as follows: 0.02 C, 0.08 Mn, 0.10 Si, 0.009 P, 0.009 S, 18.96 Ni, 7.34 Co, 5.04 Mo, 0.29 Ti, 0.05 Al, 0.004 B, 0.01 Zr, and 0.05 Ca. Unless otherwise stated the heat treatments used were the standai-d solution treatment at 1500°F for 1 hr, air cool, followed by a 900°F, 3 hr age. In this condition, the material exhibited 232 ksi yield strength and 239 ksi tensile strength. Mechanical properties were determined by Vicker&apos;s hardness measurement (20 kg) and by tensile tests on standard 1/2-in.-wide, 2-in.-gage-length sheet tensile specimens. Notch tensile tests were run using the 1-in.-wide NASA type, edge-notched specimen.4 Fracture-toughness determinations were made on 3-in.-wide, center-notched, fatigue-cracked specimens, following the recommendations of the ASTM Committee on Fracture-Toughness Testing.4 An electric-potential technique was used for measuring the crack size at the onset of rapid crack propagation5 which is necessary for calculations of Kc, the critical stress-intensity factor under plane-stress conditions. The critical stress-intensity factor under plane-strain conditions KI, was also calculated, using the stress at which the first observable crack growth occurred. 11) RESULTS A) Cold-Worked in the Austenitic Condition. The reported M, temperature for the 18 pct Ni maraging steel is about 310°F.1 Therefore, a temperature of 650°F was selected as suitable for rolling in the austenitic condition. Specimens were solution-treated at 1500°F for 1 hr, air-cooled to 650°F, and rolled varying percentages from 0 to 60 pct, at 20 pct reduction per pass. Tensile and hardness properties after aging at 900°F for 3 hr are shown in Fig. 1. The tensile strength increases from 253 to 271 ksi and the yield strength from 247 to 265 ksi as a result of a reduc-

Jan 1, 1964

By H. R. Peiffer, R. Geckle

The silver phase of silver and finely divided alumina composites is shown to grow as single crystabs upon solidification from the melt. These crystals grow without the aid of an externally applied thermal gradient or a mold. The single-crystal growth is more readily disrupted as the alumina content varies from the optimum concentration of 20 wt pct. Pretreatment such as variation of fabrication pressure, and presintering of the specimens appear to play a lesser role in this phenomenon. In actual practice the growth of single crystals of metals from the melt is a tedious, painstaking process.&apos; Care must be taken to insure the proper thermal gradients and rate of growth in a vibration-free environment. Excellent single crystals can be grown when these variables are controlled. When a second insoluble and finely divided phase is present in the melt the growth of single crystals is difficult, if not impossible, even under the most favorable conditions outlined above. During the past few years, a composite of silver and alumina has demonstrated an ability to resist flow even though the major phase, silver, is mo1ten. 2 A more surprising feature of this material is the ease with which single crystals of silver grow upon cooling the composite from temperatures above the melting point of silver to temperatures near room temperature. Observations have been made that demonstrate that single crystals of silver will grow even when conditions most unfavorable for growth of pure silver crystals exist. The crystals grown in this manner are imperfect in that a great deal of subgrain structure exists. It is the purpose of this manuscript to qualitatively describe this process and to attempt to isolate the influencing factors of this behavior. MATERIAL PREPARATION The composite material is prepared by powder-metallurgical techniques. Two items of great importance are the introduction of oxygen into the system and the obvious need for a thorough mixing of the metallic and refractory oxide phases. The oxygen is necessary in order that the silver wets the alumina. Without oxygen the phases separate and the material shows no unusual properties. In order to supply the needed oxygen the silver is added in the form of silver oxide which is readily decomposed to oxygen and silver upon heating. The silver oxide is readily obtained in a finely divided form that allows a uniform mixture of the alumina and silver oxide to be prepared. The correct ratio of alumina to silver oxide is mixed in the presence of alcohol in an ordinary food blender. The mixture has the consistency of a thin slurry and after mixing for approximately 20 min is dried and pressed into billets at various pressures. As is shown in Fig. 1, there is no limit to the shape of the specimens obtainable as single crystals. These billets are heated in air in a predeter-

Jan 1, 1964

By L. Ianniello

AMONG the more interesting peculiarities of plutonium is the brittleness of its room-temperature monoclinic phase, a, since the adjacent higher-temperature phase (transformation temperature, 112C), ß, is also monoclinic but very ductile. Other elements, e.g., tin and manganese, have phases which exhibit similar contrast in plasticity. However, it was considered unusual when the a phase which has less than 0.1 pet tensile elongation&apos; was rolled to 90 pct reduction in thickness at room temperature.&apos; Since brittle behavior often is a structure-sensitive property, but could also be the result of covalent-type bonding, further experiments reported here have been conducted in an attempt to illuminate the problem. Electrorefined plutonium was rolled under various conditions and examined to determine the strain-hardening characteristics and also to determine under what conditions rolling could be performed. The rolling mill had 6.0-in.-diam heatable rolls with a variable roll speed (6.25 to 445 in. per min). Microhardness measurements were taken using a square-base diamond indenter with loads from 50 to 1000 g. The method used for rolling plutonium at room temperature consisted of prior

Jan 1, 1964

By C. H. Li, R. J. Stokes, T. S. Liu

Poly crystalline silver chloride specimens having different micro structures were prepared by extruding monocrystals or precompressed powder at varying temperatures. Extrusion at high temperature (370°C) produced a Fully recrystallized equi-axed material which was brittle and fractured by simple cleavage below its transition temperature (60°C for notched specimens). Extrusion at low temperatures (down to -196°C) produced an extremely tough cold-worked material with grains elongated in the extrusion direction. This material fractured below its transition temperature (which varied from —20" to —200°C) by an intergranular mode. It is concluded that cold work increases the resistance to transgranular cleavage. Fracture is then de-flected to propagate intergranularly ouer surfaces making an angle with the tensile axis with a corresponding improvement in notch toughness. This deflection is greater for extruded powder than for extruded monocrystals because of the extremely elongated grain shape. PREVIOUS work1,&apos; on the fracture properties of fully recrystallized silver chloride under notch impact conditions has indicated that the fracture behavior is rather invariant. Thus polycrystalline materials originating from a number of sources ranging from relatively pure Harshaw single crystals to commercial-purity powder and prepared by hot extrusion at 370°C all fracture by simple cleavage with a ductile-brittle transition at 60°C, see Fig. 1. This behavior is also typical for fully annealed single crystals and appears to be fundamental to silver chloride for the particular loading conditions and notch configuration adopted. One way in which this characteristic fracture behavior can be modified is by the dispersion of alumina particles in the silver chloride matrix.&apos; Then, particularly when the alumina particles are in the shape of spheres, the duc tile-brittle transition is much less sharply defined and occurs over a range of temperature, the transition temperature is lowered considerably and the fracture mode changes from simple cleavage to a fibrous or shear mode. The reason for this change is believed to be partly due to the nucleation of cavities in the region of the dispersed alumina particles which influences the state of stress locally and the distribution of plastic constraint at the root of the notch. It is emphasized however that this is not the sole factor responsible for the increase in toughness. In extruded materials it is reasonable to expect that the resultant grain size, texture, and the residual cold work will be influenced by the presence of a dispersed phase. The present experiments were initially designed to determine the extent to which cold work influenced the fundamental ductile-brittle transition temperature and fracture mode of silver chloride. They were stimulated by the discovery that silver chloride could be extruded at temperatures as low as -25°C when commercial-purity powder was used and as low as -196°C when single crystals were used. This working temperature was far below that previously used (370°C) and it was found that such extruded material was exceedingly tough. The reasons for the enhanced toughness and its relation to the previous work on silver chloride-alumina compacts will be discussed. EXPERIMENTAL PROCEDURE Materials Used. Two forms of silver chloride were used in this study: i) silver chloride powder

Jan 1, 1964

By L. B. Harris

Continuous cyclic unloading during tensile work hardening of polycrystalline zinc at room temperature enables specimens to sustain greatly increased extension. Such enhanced ductility is associated with creep-type extension, during which the cyclic component appears to promote relaxation of internal strains. It is possible to trace the transitions from tension, through enhanced cyclic extension, to fatigue and relate the observed behavior to simpler types of deformation. DISTINCTIVE deformation behavior has been shown to occur when loading includes both cyclic and unidirectional components. For aluminum and copper extended by a sequence of progressively biased strain reversals, coffin1 observed greater fracture ductility and lower flow stresses than during monotonic tension. This may be compared with the reduction in hardness obtained from conventional fatigue softening. But fatigue softening is accompanied by enhanced fatigue life,&apos; whereas Benham3 found that fatigue life was reduced when copper continuously extended during axial load cycling. The corresponding specimen elongation, for large cyclic load amplitudes, was greater than during normal tension. Under different conditions, Bendler and wood4 found that torsional fatigue initiated extension in copper under low tensile loads previously in equilibrium with the specimen; fatigue life was again reduced. Thus there is a type of cyclic softening which is associated with reduced fatigue life and which occurs when the cyclic loading is accompanied by a unidirectional strain component. Further, the fracture ductility or extension obtained from the unidirectional component can exceed that obtained in the absence of cyclic load. Specimen extension was not initiated by axial fatigue at small load amplitudes;3 hence Benham&apos;s work distinguishes between fatigue at large and small amplitudes, the former often being linked with unidirectional deformation because of similarities in strain Structure. The initiation of tensile extension during torsional fatigue,4 however, occurred with small amplitudes. Comparable changes in behavior have been ob- served during creep. kennedy&apos; found that combined cyclic and creep stresses on lead at 32°C increased the rate of elongation over that for simple creep, the consequence being a reduction in creep life. It was also demonstrated that small cyclic stresses applied after creep deformation initially increased recovery, but that prolonged application produced only normal fatigue hardening. It is clear that physical properties can be changed by interaction between the cyclic and unidirectional deformations, but owing to the number of different ways in which the deformations can be combined and the large number of possible variables for each combination, trends of behavior become easily obscured. One definite conclusion is that enhanced ductility or increased extension can be obtained by cyclic action, and it is this process that has been investigated for the tensile test by measurements of the extra tensile strain produced by the addition of a cyclic tensile component. EXPERIMENTAL PROCEDURE Material. Specimens were 99.99 pct Zn wire of 1.6 and 2.0 mm diam. Mean grain diameter was 0.02 mm, sufficiently small to give a ductile necked-down fracture under all loading conditions. All experiments were conducted at an average temperature of 20°C. Normal Tension. Unidirectional tensile curves at different strain rates were obtained from an In-stron testing machine, on which load-time curves were recorded autographically, using gage lengths of 5 and 10 cm. Straining was at constant cross-head velocity, and quoted strain rates are with reference to initial specimen length. Measurements of total elongation under simple tension were also made on the tensile machine that had been modified to incorporate an added fluctuating load. Combined Tension and Rapid Cyclic Load. An electromagnetic vibrator was coupled to the elastic beam of a Hounsfield ensometer- and driven sinus-oidally from a power amplifier at frequencies from 20 to 360 cps, the flexible connecting links on the tensometer being replaced by rigid fixtures to eliminate lateral vibration in the specimen. One end of the specimen was pulled by the normal extension drive of the tensometer while the other end, fixed to the elastic beam and vibrator, was subjected to rapid oscillations of load. It was thus possible to apply cyclic load to a tensile test without altering the rate of extension of the specimen

Jan 1, 1964

By R. G. Garlick, H. B. Probst

Tungsten single-crystal specimens of various orientations were deformed in tension at room temperature. Slip traces indicated both (112)(111) and (110) (111) slip; however, about 10 pct plastic dejormation was required bejore these traces could he seen. Resolzled shear-stress considerations indicated that at least some of the particular systems observed were not those on which slip initiated hut were secondary systems. This is highly probable, considering the high plastic strains involved. Analysis of the stress data with respect to possible slip systems indicated that slip must have been initiated at stresses below the proportional-limit stresses measured. ALTHOUGH there is general agreement that slip deformation in fcc and hep metals takes place on the plane of close packing and in the direction of close packing, there is no such agreement for slip in bcc metals. It is generally agreed that the close-packed direction (111) is the slip direction, but investigations have led to conflicting descriptions of the slip plane. As Hoke and Maddin1 point out, there are essentially four points of view. 1) Deformation in bcc metals is composite shear on (112) and (110) planes or on nonparallel (110) planes, and any apparent slip on other planes can be accounted for completely by slip on these planes. Chen and Maddin have reported this to be the possible case for molybdenum." 2) Slip occurs in the (111) direction and is limited to {110), {112), and (123) planes (the three closest packed planes of the lattice). 3) Slip occurs in a (111) direction, but not necessarily on planes of close packing (banal slip). 4) Slip occurs in those directions and on those planes for which ß, the ratio of Burgers vector to interplanar spacing, is a minimum. The slip systems of the bcc metal tungsten have never been fully determined, although several investigators have reported pertinent results.3"7 The present work was initiated to determine the active slip systems in tungsten at room temperature, the critical resolved shear stresses associ- ated with these systems, and the orientation dependency of operative systems. These features of tungsten deformation at room temperature have never been reported in the literature. The authors find this somewhat surprising, particularly in view of the availability of tungsten single crystals since the advent of electron-beam zone-melting techniques and the widespread interest in refractory metals. It would seem apparent that such work has been attempted but the results have not been reported, possibly due to the conflict with deformation theory. The results of the present work conflict with any straightforward description of deformation based on the proposed explanations of slip in bcc metals. Although these conflicts have not been resolved, a presentation of the problem seems in order and should be of value to others working in this field. MATERIALS AND PROCEDURE Single-crystal tungsten rods of 1/8-in. diameter were grown from undoped commercial rod by one-pass electron-beam zone melting in apparatus previously described by witzke.8 Representative analyses of the rod before and after melting are given in Table I. There was no detectable zoning of impurities during melting. Buttonhead tensile specimens, as shown in Fig. 1, were machined from single crystals. Two flats 90 deg apart were ground in the gage length of each specimen. These flat surfaces facilitated the analysis of slip traces. No attempt was made to position these flats with respect to the crystal orientation. The worked surface layer of the machined specimens was removed by electrolytic polishing in a NaOH solution. Tensile-axis orientations were determined by standard Laue back-reflection techniques. The sharpness of the Laue spots indicated that the crystals were free of strain.

Jan 1, 1964

By Robert T. Ault

The nature of fracture in unnotched tensile and notched tensile sheet and round specimens and V -notched and precracked Charpy-type sheet specimens of both wrought stress -relieved and re-crystallized molybdenum was investigated over the temperature range of -78° to 300°C. The sharp rise in fracture stress, for unnotched tensile samples, as the temperature is increased above the brittleness transition temperature (Tb), is found to be a result of an increase in flow stress due to plastic constraint and an increased strain rate which results from the onset of necking at Tb . Quasi-brittle fracture in notched tensile samples is found to occur when the tensile stress at the elastic-plastic interface, beneath the root of the notch, reaches a maximum critical value, which is independent of test temperature over the range from —78° to 25°C, but dependent on microstructure. In the temperature range between 150° and 300°C, unnotched tensile and notched tensile samples alike are found to fracture by a ductile fibrous tearing process which is discontinuous in nature, as a result of the competition between the processes of tearing, through continued plastic flow, and local work hardening. Results from the V-notched and fatigue-cracked Charpy-type impact tests demonstrate that crack initiation is the governing factor in the low-temperature (-78° to 25°C) fracture process for molybdenum. In recent years, there has been considerable interest, and a commensurate number of investigations, concerning the duc tile-to-brittle transition in refractory metals. There has not developed, however, a satisfactory explanation for the uniaxial tensile fracture-stress transition which accompanies the well-known ductility transition. This matter therefore warranted investigation. In a similar manner, the increased importance of notched tensile strength values in evaluating materials and in design criteria requires a better understanding of the factors which control the fracture behavior of notched tensile samples. In a previous investigation1 of the nature of initial yielding and fracture in notched sheet molybdenum at room temperature, it was suggested that plastic constraint was the controlling factor in governing the fracture behavior of notched samples. The final portion of this investigation was concerned with the fracture toughness of molybdenum. Of particular interest was the comparison of effective surface energies for fracture in V-notched samples with fatigue-cracked, Charpy-type samples in order to ascertain the relative importance of the initiation and propagation phases of the fracture process. MATERIALS AND TEST PROCEDURE Sheet tensile, notched tensile, and V-notched Charpy specimens were prepared from 50-mil, stress-relieved molybdenum sheet.* Half of these specimens were vacuum-annealed for 1 hr at 1200°C and 7.5 x l0-5 Torr and furnace-cooled to produce a relatively uniform grain size of 0.30 mm diameter. Round notched and unnotched tensile specimens were prepared from warm-rolled and swaged 5/8-in.-diam bar.* These specimens were vacuum-annealed for 1 hr at 1350°C and 5 x lom5 Torr and furnace-cooled to produce a grain diameter of 0.11 mm. Material analyses in ppm were: C N O H Sheet 290 10 4 1 Bar 50 30 30 2 The unnotched tensile sheet specimens had a 1/4-in. gage width and a 1-in. gage length. The unnotched tensile round specimens had a 9/32-in. gage diameter and a 1-1/4-in. gage length. The sheet and round notch tensile specimens are shown in Fig. 1. All of the notched tensile specimens tested were tandem-notched in order to study the location and mode of fracture initiation. The tandem-notched specimens were carefully machined so that the largest variation in notch depth on a single specimen was 0.001 in. Thus, when fracture occurs, the extent of plastic deformation that exists in the un-fractured notch section is that which exists just prior to fracture. All of the tandem-notched sheet specimens were electrolytic ally polished and chemically etched prior to testing. The V-notched Charpy-type specimens machined from the 50-mil sheet material had the standard dimensions of 2.125 in. long, 0.394 in. deep, and a 0.010-in. root radius. The unnotched tensile and notched tensile tests were conducted over the temperature range of -78° to 300°C, in a 10,000-lb Instron Universal Testing Machine, at a constant crosshead speed of 0.020 in. per min. The V-notched Charpy-type

Jan 1, 1964

INCREASING realization that pouring and ingot-mold practices involve many factors of fundamental importance to ingot quality and general steel-mill operations has caused these phases of steelmaking to become major concerns of operators and metallurgists engaged in control of quality and costs. Methods of pouring steel from the ladle into the ingot molds have some direct effects on ingot quality. The mold itself governs solidification and dimensions of the ingot and in so doing exerts some very tangible influences not only on ingot quality but also on product yields and general steel-mill processing. In addition, practices are employed in the handling of molds during daily open-hearth operations that are important to quality and production costs. Therefore, pouring and mold practices must be considered highly specialized and important steps in steel-mill operations. MOLD DESIGN Mold design is difficult to discuss in a precise manner because it varies greatly throughout the industry, both in theoretical concepts and practical application, and few well developed data are available. Most ingot molds are designed to meet conditions peculiar to a given plant wherein quality standards are dictated by end-use requirements, which may differ considerably even for the same grade of steel. The mold designer must also consider the equipment available to process ingots and the product obtained from them. Such equipment, used for stripping, heating, blooming and finishing operations, is seldom, if ever, exactly the same in any two steel plants. Thus, pronounced contrasts in mold designs can be expected to continue, even among plants making strictly comparable types of product, particularly because some producers are just beginning to realize the benefits possible from specialized designs. Certain fundamentals are used in mold design but even these

Jan 1, 1964