Institute of Metals Division - Thermomechanical Treatments of the 18 Pct Ni Maraging Steels

Thermomechanical treatments applied to the maraging steels include a) cold working in the austenitic condition at 650°F, followed by transformation to martensite and aging, b) cold working in the murtensitic condition and aging, and c) cold working in the aged condition with and without subsequent reaging. The strength increases in these steels are very small compared to the increases observed in conventional carbon and alloy steels. The changes that are observed are compatible with the strengthening mechanisms operative during thermomechanical treatment of conventional steels, however. Differences are caused by the absence of a carbide precipitate and the low work-hardening rate in both the solution-treated and the aged conditions. ThE 18 pct Ni maraging steels represent a class of steels which are finding great interest for high-strength applications.1~2 They are essentially carbon-free, and contain 7 to 9 pct Co, 3 to 5 pct Mo, and 0.2 to 0.8 pct Ti. Although austenitic at elevated temperatures, they can be air-cooled to room temperature to form a martensite, which because of the absence of carbon is relatively soft. On subsequent reheating age hardening occurs and strength levels of 250 to 300 ksi yield strength can be attained. These steels appear to be particularly suitable for studying the response to various thermome-chanical treatments for additional reasons other than the obvious one of attempting to improve their already attractive properties. Thermomechanical treatments can be defined as treatments whereby plastic deformation, generally below the recrystal-lization temperature, is introduced into the heat-treatment cycle of a steel in order to improve the properties. With an absence of intermediate transformation products on air cooling the maraging steels have good hardenability and hence can readily be cold-worked in the austenitic condition prior to transformation to martensite. Further, they can be worked in the martensitic condition prior to aging, and even can be deformed in the fully aged condition. Finally, it is of interest to compare their re- sponse to that of the more conventional alloy and carbon steels, where the role of carbides is important in the strength increase by thermomechani-cal treatments. The thermomechanical treatment of conventional steels has been the subject of a recent review.' I) MATERIALS AND PROCEDURE The steel used in this investigation was a commercially produced vacuum-melt heat, which had been rolled to 0.090 in. and mill-annealed. The composition of the alloy was as follows: 0.02 C, 0.08 Mn, 0.10 Si, 0.009 P, 0.009 S, 18.96 Ni, 7.34 Co, 5.04 Mo, 0.29 Ti, 0.05 Al, 0.004 B, 0.01 Zr, and 0.05 Ca. Unless otherwise stated the heat treatments used were the standai-d solution treatment at 1500°F for 1 hr, air cool, followed by a 900°F, 3 hr age. In this condition, the material exhibited 232 ksi yield strength and 239 ksi tensile strength. Mechanical properties were determined by Vicker's hardness measurement (20 kg) and by tensile tests on standard 1/2-in.-wide, 2-in.-gage-length sheet tensile specimens. Notch tensile tests were run using the 1-in.-wide NASA type, edge-notched specimen.4 Fracture-toughness determinations were made on 3-in.-wide, center-notched, fatigue-cracked specimens, following the recommendations of the ASTM Committee on Fracture-Toughness Testing.4 An electric-potential technique was used for measuring the crack size at the onset of rapid crack propagation5 which is necessary for calculations of Kc, the critical stress-intensity factor under plane-stress conditions. The critical stress-intensity factor under plane-strain conditions KI, was also calculated, using the stress at which the first observable crack growth occurred. 11) RESULTS A) Cold-Worked in the Austenitic Condition. The reported M, temperature for the 18 pct Ni maraging steel is about 310°F.1 Therefore, a temperature of 650°F was selected as suitable for rolling in the austenitic condition. Specimens were solution-treated at 1500°F for 1 hr, air-cooled to 650°F, and rolled varying percentages from 0 to 60 pct, at 20 pct reduction per pass. Tensile and hardness properties after aging at 900°F for 3 hr are shown in Fig. 1. The tensile strength increases from 253 to 271 ksi and the yield strength from 247 to 265 ksi as a result of a reduc-