Search Documents

By K. G. Davis, P. Fryzuk

The diffusivity of silver in liquid tin has been determined, using the capillavy-reservoir technique, over the temperature range 250° to 500°C. The new value, D = 2.5 x 10'* exp(-2480/ RT) sq cm per sec, differs from that obtained by other workers in an earlier investigation. The analysis of data from the capillary-reservoir technique is discussed. In a recent investigation of the solidification of dilute alloys, values for the diffusion constant of silver in liquid tin were required in the analysis of the formation of impurity substructures. AS a result, measurements were made of the diffusion constants in the temperature range 250° to 500°C (melting point of tin 232°C), for the alloy concentrations used in the solidification experiments and at higher concentrations, to verify previous determinations.I)2 The capillary-reservoir method was adopted, using experimental procedures similar to those followed by Ma and Swalin,1 with the main exception that radioactive silver was used in the present investigation to facilitate solute-concentration measurements. EXPERIMENTAL PROCEDURE a) 100 ppm Samples. Glass capillary tubes of 2 mm inside diameter and approximately 5 cm- long were sealed at one end, evacuated, and filled with tin of 99.999 pct purity. The region of shrinkage near the mouth was cut off, and the tubes were then placed in a graphite holder and immersed, with the open end up, in an unstirred bath of alloy containing 100 ppm Ag 110, where they remained for periods of up to 30 hr. On removal from the bath they were cooled by an air blower. The bath was kept under a small positive pressure of argon, and the temperature controlled to within +1°C. A 10-hr diffusion period was used in the majority of the tests, scatter on runs of less than 5 hr being rather large. The procedure outlined above was chosen in preference to putting alloy in the capillary and pure tin in the bath, in order to avoid segregation when the tubes filled with alloy were first solidified. To minimize segregation when the diffusion period was complete and the capillaries again solidified, the earlier samples were held in thin-walled silica tubes which could be cooled very rapidly. Later tests were made in precision-bore Pyrex tubes, to eliminate effects caused by variations in the capillary diameter. No consistent differences in diffusivity as measured in the two types of tube were detected. After removal from the glass tubing, the samples were sectioned into 2.5 mm lengths and counted for y activity, using a scintillation counter with fixed geometry. Samples were also drawn directly from the bath and counted, so that values for C/C,, the ratio of the weight of Ag 110 in the sample to that in the bath, could be obtained. b) 5000 ppm Alloy. To check for possible effects of concentration, the silver content of the bath was increased to 5000 ppm. Complete mixing was found to have taken place in the capillary after a 10-hr period at 300°C. It appears that the greater density of the alloy was sufficient for buoyancy forces to cause instability in the alloy-tin interface, leading to rapid convective mixing. For the 5000 ppm alloy, therefore, the bath was of pure tin and the capillary tube was filled with alloy. With this arrangement, values of D consistent with those for the 100 ppm alloy were obtained, Fig. 1. CALCULATIONS OF DIFFUSIVITY The terminology used applies to a capillary of pure tin immersed in a bath of alloy. 1) Error-Function Method. under the present experimental conditions, the rod of liquid tin into which silver is penetrating may be considered semi-infinite. Assuming the concentration at the mouth of the tube to remain constant at Co, the concentration C at distance x from the mouth of the tube at time / is given by3 Plots of the inverse error function of (1 -C/Co) vs .v gave straight lines passing through the origin with slope 1/2-, x being corrected for shrinkage both on solidification and while cooling to the melting point (total correction about 6 pct at 500°C). Values for log D obtained in this manner are shown in Fig. 1. A least-squares fit to the relation D = Do exp(-Q/RT)

Jan 1, 1965

By S. Feuerstein, J. M. Galligan

SURFACE effects in the deformation of metal single crystals have been noted by a variety of workers.&apos; A large majority of these experiments have used surface roughening or a second chemical constituent at the surface. We performed the following experiment to see how the presence of a fine polycrystalline layer influenced the stress-strain behavior of single crystals of zinc. Spherical single crystals oriented for single slip were acid-machined into cylindrical dumbbell-shape shear specimens having a gage length of 3.2 mm and a cross section of 20 sq mm. The crystals were then deformed varying amounts at the surface of the gage section with emery paper. Following this treatment, the crystals were heated for approximately 8 hr at 200°C. This resulted in a polycrystalline surface layer, with an observed grain size of approximately 1/10 mm in diameter. Deformation of these crystals was undertaken at 78°K in pure shear, the shear direction <1120> lying in the basal plane. The deformation apparatus has been described elsewhere.2 The presence of a polycrystalline layer markedly raises the first observed plastic deformation, as can be seen from Fig. 1. This yield stress is then followed by a region of low work hardening comparable to that observed in shear tests on similar untreated zinc single crystals. However, the extent of easy glide is quite seriously curtailed, and is followed by a more rapid increase in work hardening, reminiscent of Stage II observed in the deformation of fcc crystals. The higher yield can probably be attributed to the difficulty of penetrating the grain boundaries by dis locations from sources interior to the boundaries. If we associate this yield stress with this breakthrough, then we might expect that more dislocations would be trapped in the crystal than is normally the case. If there is an increased density of trapped dislocations, this could lead to an increase in the amount of trapping with increasing strain, giving a larger strain hardening in the crystal. Although other explanations can be given, it is quite tempting to characterize the region of increased work hardening as a manifestation of Stage II-type deformation. This seems reasonable if the polycrystalline layer is quite efficient in holding up a large number of dislocations. In zinc crystals, since it is well-known that the slip distance can be as large as the specimen dimensions, one would only expect to entrap a large number of dislocation with very large crystals or by applying surface layers. If this interpretation of increased strain hardening is correct, it might present a method of studying Stage II in single crystals of zinc. This research was supported, in part, by the Office of Naval Research (1959). The encouragement and stimulation given by Professor E. R. Parker is gratefully acknowledged.

Jan 1, 1965

By J. B. Morgan

The mechanical behavior of MgCu2 from 20 o to 725°C has been determined by "brittle-ring" tensite-test techniques, axial compression, and bending experiments. Compressive ductility begins at 450°C (0.65 T/Tm) and slowly increases with increasing temperature white the tensile ductility is characterized by an abrupt brittle-ductile transition at 600°C (0.8T/Tm). The compressive strength increases eightfold from room temperature to 400°C with a "normal" decrease as the temperature is further increased. The tensile strength goes through a rather abrupt threefold increase above 600°C with a subsequent decrease at higher temperatures. The slip system is (111)[110] and the twinning system is (111)[112]. At high temperatures MgCu2 is quite rate-sensitive, and dynamic yield points are observed that are extremely orientation-dependent. The high-temperature creep behavior under constant load is characterized by an increasing strain-rate with time. The general characteristics of the mechanical behavior make it possible to classify MgCu2 with those materials in which initial mobile dislocation density and the dislocation velocity-stress dependence are significant in determining mechanical response. Mgcu2 is the C15 prototype of the cubic Laves phase. Its range of homogeneity extends from 32.8 to 35.5 at. pct Mg at 500°C and narrows at lower temperatures. The lattice parameter is reported to vary from 7.02 to 7.05A,1 and the compound is completely ordered to the melting point of 819°C. MgCu2 has a brassy metallic appearance, is extremely brittle, and many of its physical properties are intermediate between those of the constituent elements: the electrical resistivity is 3.5 x 10-6 ohm-cm, Young&apos;s modulus is 10x 106 psi, the shear modulus is 6 x l06 psi, and the thermal coefficient of expansion is 18.7 x 10-6 cm per cm per "C from 20" to 250°C. Usually, properties of intermetallic compounds as functions of temperature have been determined by hardness, compression, or impact behavior, and almost all of these experiments have been performed on polycrystalline materials. Tammann and Dahl,2 for instance, determined the onset of ductility in a series of binary intermetallics by ball-hardness measurements and found the onset to range between 0.71 and 0.96 T/T,. Lowrie&apos;s3 investigations included some tensile properties, and he found ductility beginning around 0.65 T/Tm for most materials examined. His work did include some data on polycrystalline, nonstoichiometric MgCu2, however. The present work is an attempt to extend the examination of the particular compound MgCu2 in single-crystal form in order to aid the formation of general concepts about mechanical be-

Jan 1, 1965

By B. B. Sandiford

It has been known for many years that the efficiency of a water flood can be improved by lowering the water-oil mobility ratio in the system. Such a change leads to better sweep efficiency and also to more efficient oil displacement in the swept zone. Data from our laboratory water-flood tests of both small cores and long sand packs are presented which show that water mobility can be reduced and oil recovery increased by the addition of certain polymer solutions to flood water. The reduction in mobility, in many cases, is greater than would be expected from conventional viscosity measurements. These solutions, however, do not cause significant reductions in oil mobility. The over-all effect of these mobility changes is increased waterflood oil recovery. Encouraged by results of our laboratory work, we expanded our study to include pilot field tests of floods with such solutions. One such test, made in the West Cat Canyon field, Santa Barbara County, Calif., is described in detail in this paper. Three other field tests are also discussed. INTRODUCTION Oil production from most reservoirs following primary depletion and/or water flooding is often less than 50 per cent of the original oil in place. Heavy oil reservoirs seldom yield over 15 per cent of their original oil. With new reservoirs becoming harder to find, the improvement of oil recovery efficiency is one of our very important problems. We describe here some of our attempts to increase the efficiency of oil displacement by adding a water-soluble polymer, partially hydrolyzed polyacrylamide, to flood water. This technique will be termed "polymer solution flooding". The concept of using high-viscosity water to increase the efficiency of water flooding is not new. In 1944 Detling (Shell Development Co.) obtained a patent covering the use of several additives for viscous water flooding.&apos; His objective was to improve water-oil mobility ratios by increasing the viscosity of the flood water. Other patents2-27 have been granted covering specific water-SO~LIble polymers or specific conditions of viscous water flooding. Barnes&apos;" described his laboratory model study of the injection of a viscous water slug into a reservoir which had been partially invaded by bottom water. He concluded that, for this type of reservoir, "the cost of viscous water should not exceed a few cents per barrel for viscous water slug injection to be economically feasible" Our studies have led us to a somewhat different conclusion in a number of cases where hydrolyzed polyacrylamide solutions have been injected into reservoir models or actual reservoirs. Possible reasons for this difference are discussed in this paper. Our studies have shown that polymer solutions may lead to an increase in oil recovery over that from an ordinary water flood by (1) improving sweep efficiency, (2) improving microscopic displacement efficiency, or (3) a combination of these mechanisms. In the work of Barnes, only the benefit of improved sweep efficiency was considered. Also, our work has shown that there are marked differences in the effectiveness of different water-soluble polymers as flood water additives. Partially hydrolyzed polyacrylamide is better than many other water-soluble polymers we have tested because, even in very low concentrations, it can lead to increased oil recovery. This is an important advantage when either a dilute polymer solution is injected continuously or a relatively concentrated slug is injected followed by water. In the latter case! portions of the slug become diluted and function in the formation as very dilute solutions. As dilution takes place the effective slug size will increase which, in turn, will reduce the cost per barrel of the effective flooding medium. The reason that partially hydrolyzed polyacrylamide solutions are more efficient at low concentrations than certain other polymer solutions of equivalent viscosity (when measured in conventional viscometers) is not fully understood. We do know that the shapes and sizes of macro-molecules dissolved or suspended in liquids influence the flow properties of their solutions or suspensions. Solutions of partially hydrolyzed polyacrylamide cause greater reductions in water mobility than would be expected from conventional viscosity measurements. LABORATORY STUDIES Laboratory water floods were run in linear and radial systems with different water-soluble polymers and under varying conditions of flow. including reservoir conditions of temperature, pressure and fluid composition. Some of these runs are considered in this section. OIL DISPLACEMENT IN LINEAR MODELS In this group of runs the sweep efficiency approached 100 per cent because the linear sand packs used were as nearly uniform as possible. Results reflect primarily the micro-scopic displacement efficiencies. The laboratory models were unconsolidat-ed sand packs the lengths of which varied from about 4 in, to 40 ft. Further information on the flow models used is listed in Table 1. Using conventional procedures, water floods were run on sand packs containing either refined or crude oil at restored state. Frequently, a repeat run, similar to the first, was made as a check. Then a third run was made on the restored-state model using either polymer solution or a combination of polymer solution (slug) and water. Details of these runs are also reported in Table 1. In Figs. 1 and 2 results of two different groups of runs are shown in which the oil used was a 62-cp refined oil and the flooding medium

Jan 1, 1965

By L. F. Mondolfo, W. T. Collins

A study of the relationship between undercooling for nucleation and structure in Sn-Cu alloys with 0.1 to 5 pct Cu has shown that in hypereutectic allojls the halo of tin that surrounds the primary crystals of Cu3Sn5 is larger, the larger the undercooling for nucleation o,f the tin. This increase of halo size results in a decrease of coupled eutectic, and, in alloys far from the eulectic composition, may produce its complete disappeavance, with the formation of a divorced eutectic structure. This was confirnred by the excrrnination of other alloys in which divorced eutectic slructuves are formed, and leads to the conclusion that they ave only an extrenle case of halo forrtzalion , which results when the two phases freeze one at a time and solidification of the first is completed Defove the second starts. It was also found that under proper conditions of nucleation all types of eutectic structures can be formed in the sartte system , and therefore divorced eutectics, like normal and anomalous, are not characteristic of the syslett~, but are mainly controlled by nucleatiorz. Dizlovced eutectics are formed when the phase that tutcleates the eulectic vequires a large undevcooling for ils nucleation and when the cotnpositiorz of the alloy is far from the eutectic., on the side of the primary phase that does not nucleate the other phase. It is recommended that the tevm "divorced" be used in preference to degenerate because it is more desct-iptice of the morphology and mode of forinalion of the structures. ThE variety of structures found in eutectic alloys has been extensively investigated and classified. The most accepted classification is the one by ~cheil,&apos; in which three different types of eutectic were distinguished: 1) normal, 2) anomalous, 3) degenerate (divorced). ATornlal eutectics are typified by the simultaneous growth of the two phases ("coupling") by which the two phases appear as interpenetrating crystals. The presence of a crystallization front, in which the two phases grow side by side, creates the eutectic grains, with the boundaries where the fronts meet. The presence of eutectic grains is the .distinguishing feature of a normal eutectic, according to Scheil. Straumanis and Brakss2 examined the Cd-Zn system and showed that there was a crystallographic relationship between the phases. Later, others4 also investigated additional systems and found definite crystallographic relationships in the coupled eutectics. The anornalous eutectic shows much less coupling than the normal; the two phases are intimately mixed but &apos;grow without a uniform crystallization front—a consistent crystallographic relationship— and the eutectic grain is conspicuously absent. As in the normal eutectics faster rates of growth result in a finer structure, but there is not the typical uniform spacing of normal eutectics. The degenerate eutectic shows no coupling; in fact the two phases attempt to minimize their area of contact and to form separate crystals. It has been suggested5" that slow cooling may favor this type of structure. Scheil believes that normal eutectics are formed when the two solid phases are present in more or less equal proportions, whereas both anomalous and degenerate eutectics form when one of the phases is present only in small amounts. spengler7 extended much farther this qualitative relationship between the eutectic type and the ratio of the two phases, and added a relationship to the melting point of the constituents. On this basis he proposed two equations for determining into which of Scheil&apos;s classifications an alloy belongs. The first equation is: where TI is the melting temperature of the lower-melting component, Tp of the higher-melting component, and Te the eutectic temperature. The second equations is: where is the volume percent of the lower-melting phase and $2 of the higher-melting phase at the eutectic composition. If 0 and/or 4 are in the range 0.1 to 1, a normal eutectic is formed; if in the range 0.01 to 0.1, anomalous; if less than 0.01, degenerate. Although the examples given by Spengler show a good agreement with the formulas, chadwick found that the Zn-Sn eutectic is normal to all growth rates, even though the volume ratio is 12/1, and Davies9 reports that the A1-AlgCo2 eutectic is normal, with a volume ratio of more than 30/1. Many more discrepancies of this type can also be found. Neither Scheil nor most of the other investigators have considered nucleation as a factor in the formation of divorced eutectics. Daviesg states that divorced eutectics form when neither phase acts as

Jan 1, 1965

By J. E. Warren

In their analysis of Eqs. 29 and 30, the authors correctly deduce the following behavior limits for the "differential capacitance model". 1. When the rate group a is sufficiently large, the model reduces to that implied by Eq. 1, i.e., the simple convection-diffusion model. 2. When the rate group a is sufficiently small, the model reduces to that implied by Eq. 1 with 1 replaced by 1, i.e., the simple convection-diffusion model with a total pore volume equal to that occupied by the mobile fluid in the original model. Unfortunately, the authors&apos; solution, Eq. C-1, to the transformed versions of Eqs. 29 and 30 does not exhibit the same limiting behavior. For example, as a approaches zero, Eq. C-1 reduces to the solution to Eq. 1 or, equivalently, the solution to Eqs. 29 and 30 for sufficiently large values of a. Therefore, it can be concluded that Eq. C-1 is not a general solution to Eqs. 29 and 30; this conclusion can be easily verified by substitution. I suggest that the correct form of Eq. C-1 is the following: It is generally realized that accounting for dispersion effects is an extremely tricky business; therefore no one should criticize the pragmatic approach of Coats and Smith who proceeded by accessible theory, made use of some available phenomenology, and who then took the trouble to check the consequences, against their own carefully undertaken experimental results. Here I should like to defend three assertions: (1) Coats and Smith copy the error of previous authors in the formulation of the so-called simple diffusion model (which error is then retained in their differential capacitance model); (2) improving the fit between data and the predictions of an arbitrary model by increasing the number of parameters is a triviality unless the parameters are disposable by being independently determined; and (3) existing experimental procedures lack sufficient resolution to clarify some current theoretical uncertainties. Taking first the view that all theoretical approaches (whether constructed by statistical, finite difference, or continuum arguments) tend to reduce to the same model form as fixed by the number and nature of the disposable parameters, one notices that the "finite-stage" model of Deans1 is equivalent to the Coats and Smith so-called differential capacitance model for the pertinent case where a

Jan 1, 1965

By R. W. Smith, T. J. Smolik

Recent work indicates that fluosilicate ions and or fluosilicate amine complex ions play important roles in fluoride activation of bery and feldspars in cationic flotation systems. In an attempt to further confirm conclusions reached in this earlier work, an infrared and X-ray diffraction study of the action of fluorides in cationic flotation of silicates was undertaken. It should be noted that in recent years considerable use has been made of infrared spectroscopy in studies of surface phenomena,2-4 and these studies have established the excellence of the technique. In the present study infrared spectra were obtained for various products of the reaction of HF and dode-cyclamine hydrochloride with quartz, microcline and beryl. These spectra were compared with one another and spectra of several inorganic and organic substances. In addition to infrared spectra, X-ray diffraction patterns were run on many of the reaction products obtained. A model 137 B Perkin Elmer Infracord double beam spectrophotometer containing sodium chloride optics was used to obtain the spectra. Infrared samples, except for the dodecylamine sample, were prepared by thoroughly mixing the substance to be analyzed with purified KBr in steel vessels on a Wig-L-Bug amalgamator. One-half in. pellets weighing 100 mg were than pressed under vacuum. Details concerning percentage of the substance to be analyzed in the pellets are indicated on the spectra. In all cases except for dodecylamine a KBr pellet was placed in the reference beam of the spectrophotometer to cancel bands due to possible impurities in the KBr. The dodecylamine sample on which an infrared spectrum was obtained was prepared by placing pure dodecylamine between two salt plates. X-ray diffraction patterns were obtained with a Norelco instrument, using a copper target tube, nickel filter and Geiger tube detector. The samples were ground into powders and either placed on glass slides with glue or placed into regular powder sample holders for diffraction studies. Goniometer scanning speed varied from 1°/min to 1/8°/min. EXPERIMENTAL RESULTS AND DISCUSSION Infrared spectra of microcline, beryl and quartz were obtained first and are shown in Fig. 1. These spectra agree reasonably well with previously reported spectra.5,6 The microcline (Fig. 1 a) and beryl (Fig. 1 b) were from good Black Hills crystals. The quartz (Fig. 1 c) was from a large, clear Brazilian crystal. It is not clear whether absorption bands of minerals are due to molecular vibrations, lattice vibrations or both. Fig. 2 shows infrared spectra of dodecylamine (Fig. 2 a) and dodecylamine hydrochloride (Fig. 2 b). The dodecylamine spectrum checks quite closely with that reported in Sadtler.8 Little is known of the spectra of hydrochloride salts of amines,9 and a spectrum of dodecylamine hydrochloride could not be

Jan 1, 1965

By D. Havlena, A. S. Odeh

The use of the straight-line method of solving the material balance equation is illustrated by means of six field cases. Also, the application of statistical criteria to arrive at the most probable answer is shown. The theory underlying the straight-line method of solution and the applicability of the statistical criteria was presented in a previous paper.&apos; The field cases include saturated and undersaturated oil reservoirs with and without water drive. The aquifers discussed are: limited radial, infinite radial, very small aquifer and infinite linear. The field cases also include a gas reservoir producing under water drive. INTRODUCTION In a previous paper,&apos; the authors presented the theory underlying the solution of the material balance as an equation of a straight line. The appropriate equations for various material balance cases as well as the methods of analysis and interpretation with comments and discussion were also included. To illustrate the various theoretical cases treated previously, five field cases are analyzed in this paper by employing the straight-line method of solving the material balance equation (MBE) and one example previously published is referred to. The use of statistical criteria to arrive at the most probable answer is also shown. All the field examples presented, except Case 2, are excerpts from complete reservoir studies. To illustrate the method, only sections specifically dealing with the material balance principles are included. Additional geologic information and basic data are reported to better acquire an understanding of the cases and thus to better follow the reasoning that suggested the successful application of the straight-line method of solving the MBE. The six cases are: (1) saturated reservoir, small gas cap, limited aquifer; (2) saturated reservoir, very small gas cap, infinite aquifer; (3) undersaturated-saturated reservoir, very small aquifer; (4) highly undersaturated reservoir, no water drive; (5) high undersaturated one-well reservoir, limited aquifer; and (6) gas reservoir, infinite linear aquifer. THE D4 SAND, GUICO FIELD, VENEZUELA The D, sand, which was discovered in 1943, is presently in a depleted state. Since its discovery it has produced under water drive, gas-cap-gas expansion, and solution gas drive. In Nov., 1947, water injection was initiated to arrest further pressure decline. When discovered, the D, sand was a saturated reservoir with a gas cap /oil zone volume ratio m estimated volu-metrically at 0.0731, an average permeability of 500 md, a porosity value of 25 per cent, and an oil viscosity at reservoir conditions of 0.3 cp. The volumetrically determined stock-tank oil initially in place was 23.1 million bbl. The volumetrically weighted physical data and production data available until Nov., 1953 are reported in Table 1. In Ref. 1, the effects on the straight-line plot of various values of ro/r for a constant ?to, or of various dimen-sionless times for a constant r8/r10 were theorized and were illustrated in Fig. 3A of that reference. In this field case, the previously theoretically predicted effects are established. Thus, the MBE calculations using Eq. 3c of Ref. 1 were performed for various r6/r10 and dimension-less time values. Eq. 3c of Ref. 1 is:

Jan 1, 1965

By Tasuku Fuwa, John Chipman, David H. Kirkwood

Fe-C-Si alloys in silica crucibles were held at 1600°C in a controlled atmosphere of CO and Co2 and the approach to equilibrium was obsertsed. Results were not of sufficient precision to establish the activity and interaction coefficients. Observations 012 the equilibrium provided an average value for the standard free-energy change which differed by + 1.1 kcal from the earlier accepted value. The C-SL relation at other temperatures is calculated and shown graphically. IN the refining of steel in an acid-lined furnace, it is well known that, unlike in basic refining, a very significant amount of silicon may remain dissolved in the metal even when the carbon content approaches a final endpoint. Further, it is known that the residual silicon increases with increasing temperature. The quantitative relation between silicon and carbon can be calculated for equilibrium conditions from data already available on the Fe-C-O and the Fe-Si-O systems. Such equilibrium calculations could show us approximately the limitations within which the reaction would be expected to operate in practice. In the oxidation of a bath containing both carbon and silicon it is well known that at low temperatures silicon is preferentially oxidized first. It can be shown by calculation that at high temperatures carbon will be oxidized preferentially. It is the purpose of this paper to record direct observations on the Si-C relation by means of experiments carried out in an atmosphere of carbon monoxide for Fe-C-Si alloys contained in silica crucibles. When such a system is brought into equilibrium, at a fixed temperature, the composition of the liquid metal is governed by the following equations: Both K1 and K2 are known with a fair degree of accuracy, and may be calculated from the tabulated In general the percentage of CO2 is extremely small compared to that of CO and in the experiments to be described the partial pressure of the latter was generally only slightly below 1 atm. EXPERIMENTAL METHOD The induction furnace employed was the same as that described by Rist and chipman&apos; and by Fuwa and chipman.2 It was modified slightly in view of the change from alumina to silica crucibles. The small silica crucible was surrounded by a thin susceptor of molybdenum sheet which in turn rested inside a zirconia crucible. Since the zirconia was subject to breakage, it was supported inside an alumina crucible. The charge consisted of 30 to 35 g of electrolytic iron along with the required amounts of refined silicon and graphite to produce a melt of required composition. Purified carbon monoxide and carbon dioxide were passed into the furnace through carefully calibrated flow meters. Two separate and independent series of experiments were carried out. In Series I (D.H.K.) the melt was held in the furnace at 1600°C for periods of time up to 6 hr. Samples were taken at intervals in silica tubes and were analyzed for carbon and silicon. The results of the last one or two samples taken from each experiment and the direction in which equilibrium appeared to be approached are shown in Table I. In Series II (T.F.) the silica crucibles were of less satisfactory strength and the melts were held at 1600° C for periods of only 2 to 4 hr. In heats number 29 to 45 inclusive, the metal was cooled in the furnace and the ingot itself served as a sample for analysis. In heat 46 and all subsequent heats, samples were withdrawn in silica tubes at the termination of the heat, and these samples were analyzed. The results of all of these experiments in which equilibrium appeared to be approached are listed in Table II.

Jan 1, 1965

By M. Cohen, P. E. Beaubien, D. Caplan

Addition of 1 pct Mn to Fe-26 CY ca/(ses a12 increase in scaling rate at 870° and 1090°C. Whereas only the rhombohedral oxide, formrs on tire manganese-free alloy, with manganese present major amounts of the spinel .Mn0 . Pro-duced through which diffusion is more rapid. At 1090°C the scale formed OH Mn is highly, irregular due to blistering and sintering, This is a second cause of faster oxidation Since much of the blistered oxide does not participate as part of the protective layer. The oxide phases that form at different times depend on the degree to which the surface metal has become depleted, in manganese by preferential oxidation. PREVIOUS work has demonstrated that the oxide scales formed on chromium steels at high temperature consist of both spinel and rhombohedra1 phases and may contain considerably more manganese, especially in the spinel phase, than is present initially in the alloy.&apos; It has further been observed that a binary Fe-26 Cr alloy scaled less rapidly than an equivalent commercial steel and formed no spinel.&apos; However, it is not established if manganese in chromium alloys actually promotes formation of spinel nor if it affects oxidation resistance. It seemed expedient to try to evaluate the specific effect of manganese by oxidizing an Fe-26 Cr alloy containing a small manganese addition under the same experimental conditions as used for the manganese-free alloy.&apos; EXPERIMENTAL Table I shows the composition in weight percent of the Fe-26 Cr-1 Mn alloy and of the Fe-26 Cr alloy used as reference. The alloy with manganese was prepared from the vacuum-melted Fe-26 Cr alloy by remelting in vacuum with the proper manganese addition. The ingot was rolled to strip and specimens 1.1 by 0.035 by 5 cm and 1.1 by 0.5 by 4 cm cut out or machined. As previously described2 the specimens were smoothed by abrading through 600-grit Sic paper, electropolished in acetic-perchloric acid (20 to 1) to remove 10 p of metal, annealed at 1100°C in 20 torr of purified argon, and electropolished to remove a further 10 p of metal. They were then either rinsed in water and methanol and blotted dry or immediately etched for 45 sec in deoxy-genated 4 N HC1 under cathodic polarization at 10 pa per sq cm. Oxidation runs were carried out in a vertical tube furnace in a flow of purified oxygen at 1 atm while the weight increase was recorded continuously on a* automatic balance.3 Alter 98 hr at 870.C or 20 hr at 1090"C the specimens were removed to flowing argon and observed microscopically for evidence of spalling as they cooled. Subsequently they were examined by X-ray diffraction, the oxides analyzed chemically, and metallographic cross settions prepared. RESULTS Figs. 1 and 2 show the oxidation curves of Fe-26 Cr-1 Mn at 870&apos; and 1090C. The Fe-26 Cr reference runs are shown as dashed curves. Experimental details of the six runs are included in Table 11. The first 20 hr of run 1 is repeated in Fig. 2 to show the effect of temperature. At 8&apos;70°C the weight gain for Fe-Cr-Mn is about twice that of Fe-Cr (curve 1 vs curve 2, Fig. 1). Both alloys show regular oxidation curves. On parabolic coordinates (right-hand scale of Fig. 1) the

Jan 1, 1965

By H. Siebel, N. A. D. Parlee

MIZIKAR, Grace, and parlee&apos; studied rates of absorption of oxygen in stagnant liquid silver in a new type of open-ended gas-liquid metal diffusion cell, where the capillary diameters used were 1.5, 2, and 3 mm. They reported that the rates appeared to be controlled by the rate of diffusion of oxygen atoms in liquid silver and they used their data to arrive at the following equation as a reasonably good representation of the diffusivity (D) of oxygen in liquid silver: D = (14.7)10-4 exp (-7100 ± 3200)/RT cm2/sec Since this type of diffusion cell offers a promising method of measuring diffusivities of gas atoms in liquid metals, the senior author of this note and his students are carrying on a critical examination of the method, and are attempting to improve and extend the technique. The research reported briefly here was designed to examine more carefully the earlier conclusion1 that the absorption rate is diffusion-controlled, and to find out whether the diameter of the cell could be greatly increased and thus extend the method to systems where gas solubilities and diffusion rates are much smaller than in the case of oxygen in silver. For the purpose of these experiments, the open-ended capillary cell used by Mizikar, Grace, and Parlee was replaced by a small cylindrical crucible (1 to 1.7 cm in diam) containing pure silver (to a depth of 1.3 to 3 cm) resting in the bottom of a closed-ended vertical quartz tube, with an evacuated quartz filler tube just above the crucible to reduce dead volume. The method of measuring the rate of absorption was otherwise very similar to that of Mizikar, Grace, and Parlee and all the same precautions were taken. A much smaller and shorter tube furnace was used for heating, but simi- lar precautions about temperature gradients were observed. This technique was nothing more than the application of a Sieverts apparatus to the measurement of rates of absorption in small crucibles of stagnant liquid silver. In each run the volume of gas absorbed (V) was plotted against the square root of time (vt) and apparent diffusivities were calculated from the slope of the line, as described by Mizikar, Grace, and parlee.&apos; Care was taken to use only the data obtained during the early part of the total absorption period while the cell functioned as one of infinite depth. The results at 1000°C are summarized in Table I and Fig. 1. The following conclusions may be drawn: 1) Diffusion cells up to 1.7 cm in diam yield, within experimental error, the same values for the diffusivity of oxygen (D) as the capillary cells of 1.5, 2, and 3 mm in diam employed by Mizikar, Grace, and Parlee. Cell diameters as large as 1.7 cm are probably not desirable for the most precise work. Intermediate sizes, perhaps 0.5 cm, will be most practical. 2) All absorptions measured were consistent with a model where the rate is controlled by the diffusion of gas atoms in the metal. The fact that runs at absorption pressures ranging from 0.1 to 1 atm (at any one temperature) give

Jan 1, 1965

Jan 1, 1965

Jan 1, 1965

By T. L. Chu, G. A. Gruber

Silica films hare been rleposited 011 silicon substmtes at 400° to 600°C by a chemical-transport technique using hydrogen fluoride as the transport agent ill a closed system. This transport takes place from a source materia1 1071: temperature to substrates at higher temperatures, as indicated by the thermochemistry of the transport reaction. The experimental variables of- the transport process, such as the substrate temperature, the pressure pi the transport agent, and so forth, have been studied. The rate -determining step of the transport process appears to he the ),ale of chemical reaction in the source region. The transported films are similar to thermally grown silica films in physical proper-ties with the exception of &apos;some what higher dissolrrtion rates. SILICA films deposited on suitable substrates serve many purposes in electronic devices. They are used for the fabrication of tunneling devices, the surface passivation of devices, and the shielding of devices from nuclear radiation: and as selective masks against the diffusion of specific impurities into semiconductors. Doped silica films can also be used as sources for the diffusion of impurities into semiconductors. Several oxidation and deposition techniques for the preparation of silica films have been developed to meet the requirements of these applications. The therma1 oxidation of silicon by oxygen or steam at temperatures above 900 C is commonly used in silicon technology. The deposition techniques are perhaps more advantageous since they usually require lower temperatures and are not limited to silicon substrates. Silica films have been deposited on silicon and other substrates by reactive sputtering and chemical reactions. The sputtering of silicon in an oxygen atmosphere is capable of depositing good-quality silica films on silicon&apos; and gallium arenide. Many chemical reactions are known to yield silica at room temperature or higher. These reactions may involve intermediate steps. However, the final step yielding silica should take place predominately on the substrate surface in order to produce adherent films. When silica is formed in the gas phase by volume reactions, no adherent deposit can be obtained. Generally, the experimental conditions of a reaction can be varied so that the surface reaction predominates over the volume reaction. The chemical reactions which have been used successfully for the deposition of silica films are briefly as follows. The pyrolysis of alkoxysilanes in an inert atmosphere or under reduced pressure has been employed to deposit silica films on germanium3 and silicon4 at 650" to 750°C in a flow system. The deposition of silica films from alkoxysilanes has also been achieved at nearly room temperature by a low-pressure plasma. Device quality silica films have been deposited on germanium and gallium arsenide by the deposition of an amorphous thin silicon film followed by oxidation at 600" to 700" . Silica films for high-temperature capacitors have been produced by the hydrolysis of silicon tetrabromide at 950°C in argon and hydrogen atmospheres.7 We have developed a chemical-transport technique for the deposition of silica films on semiconductor substrates at relatively low temperatures. The thermochemistry of the transport reaction, the experimental variables of the transport process, and the properties of the transported silica films are described in this paper. THERMOCHEMICAL CONSDERATIONS The transport of solid substances by chemical reactions in the presence of a temperature gradient has been used for the preparation of films and crystals of many electronic materials. In this technique, a gaseous reagent is chosen so that it reacts reversibly with the solid substance under consideration to form volatile products. Since the equilibrium constants of most reactions are temperature-dependent, the transport of these products to regions of suitable temperature in the reaction system would cause the reverse reaction to take place. depositing the original solid. When the equilibrium is shifted toward the formation of the solid as the temperature is decreased, the solid is transported from a high-temperature zone to a lower-temperature region, and vice versa. This chemical-transport technique can be carried out in a closed or gas-flow system. In a closed system, chemical equilibrium is presumably established in the different temperature regions of the system, and the transport agent regenerated in the deposition region repeats the transport process in a cyclic manner. The local chemical equilibrium may not be approached in a flow system: however, this system offers a greater degree of flexibility. Silica reacts reversibly with hydrogen fluoride and this reaction was chosen for the transport process. The over-all reaction between silica and hydrogen fluoride may be written as: SiO2(s) + 4HF(g-) = SiF4Ur) + 2H2O(^)

Jan 1, 1965

By J. G. Y. Chow, S. B. McRickard

The tensi1e properties of Ferrovac iron have been studied from 4° to 300°K. The stress required for macroscopic yielding was found to he constant below approximately 50°K. The effect of mechanical twinning on this low -temperature stress plateau was investigated. The onset of twinning occurs in this iron between 130° and 150°K and depending on its previous thermal history the twinning-stress curue may drop below or remain above the vield-stress curves as the temperature is lowered. Twinning has been shown to initiate slip in quenclzed iron at low temperatures. In no instances, however, did the onset of twinning alter the continuity of the yield stress -tempwature curve. Our data shows that carbon inhibits twinning and slip at low tem-peratures. This observation nay be used to explain the ductile-to-brittle transition in iron. The effect of fast neutron irradiation on yielding and embrittlement in iron and Fe-C alloys is offered as supporting evidence for this viewpoint. THE mode of yielding in iron at low temperatures was studied in an attempt to find an expression based on a single mechanism to describe the thermal dependence of the yield stress of iron. There are two types of inflections observed in the variation of the yield stress with temperature in iron and Fe-C alloys. The first is associated with ductile behavior and consists of a region extending 50" to 100°K above absolute zero in which the yield stress is independent of temperature. The second is observed in more brittle materials such as Fe-C alloys and irradiated iron and consists of an abrupt discontinuity in the yield curve as the temperature is lowered through a ductile-to-brittle transition point. The temperature dependence of the yield stress for iron with four grain diameters as found in this study is shown in Fig. 1. To varying degrees all the curves appear to flatten or approach an asymptotic value as the temperature is lowered below 50°K. Several other investigators1,2 have observed a plateau in the yield stress of iron and steel at low temperatures and in 1956 Louat3 presented a theory which contained an explanation for this behavior. In a subsequent exchange with Erickson and Low4&apos;5 who attributed the plateau to the onset of mechanical twinning Louat8 showed that twinning first occurs in iron and steel tested in tension at temperatures as high as 140°K which is well above the observed plateau in yield stress. Furthermore he pointed out that both twinning and slip are basically dislocation processes and that with modified parameters his original theory still applied when deformation is initiated by twinning. Variables which affect the ductile-to-brittle transition in iron are test temperature, strain rate, composition and grain size.7 LOW,8 Hahn et al.,9 and Hull10 have provided evidence which links brittle fracture at a given temperature with the specimen grain size and the onset of twinning. In fact, Hull equates the brittle fracture stress to the twinning stress. On the other hand brittle fracture has been observed in the absence of twinning and priestnerl1 has given a fracture criterion which is valid whether or not fracture is preceded by extensive twinning. The data presented here clarify the role of twinning in the low-temperature deformation of iron. Strong evidence is given that the amount and distribution of interstitial impurities such as carbon are of

Jan 1, 1965

By O. D. Gonzalez, R. A. Oriani

A thermo-osmosis technique has been used to measure the heat of transport, Q* , of hydrogen and of deuterium dissolved in a iron and in nickel, and of hydrogen in Feo.6Nio.4 in the tempevature range 400° to 600°C. For all these systems, Q* is negative and has a large temperature coefficient; an isotope effect can be established for the solutes only in nickel. The magnitude of Q* is considerably larger than the activation energy, E , for migration in the case of these isotopes in a iron, so that all variants of the Wirtz model must be rejected. The phenomenological definition of Q* is developed to show that Q* is related to the mechanisms by which the activation energy is dissipated back into the lattice, and that Q*/E is a function of the ratios of the mean free paths of electrons and of phonons to the distance of jump of the diffusing atom. A correlation is shown to exist between the sign of Q* in thermal diffusion and that of the effective charge in electro migration, and may be understood as due to the large ratio of the mean free path of electrons to that of phonons. THE study of nonisothermal diffusion in the solid state is of interest because certain aspects of the mechanism of diffusion are made manifest which remain concealed though still present in the isothermal case. The thermodynamics of irreversible processes characterizes nonisothermal diffusion, known as thermal diffusion or as the Ludwig-Soret effect, by a quantity, Q*, called the heat of transport, which essentially measures the sign and the magnitude of the steady-state concentration gradient produced by the imposed temperature gradient. The problem then is to understand the quantity Q* at the atomistic level. There does not exist a theory for the atomistic interpretation of the heat of transport. There are, however, two classes of simple models which seem to afford some physical insight into Q*. Wirtz&apos;s model1, z and its subsequent generalizations partition the activation energy, E, for the migration of the atom spatially about the region of the migrating atom, so that Q* is the difference between the portion of the activation energy centered about the original site of the jumping atom and that portion about the arrival site. Clearly, the magnitude of Q* cannot on this model be larger than the activation energy for migration. The model of Oriani3 also considers the spatial distribution of E not only before but also after the atomic jump, and Q* is related to the variation of the spatial distribution of E that is produced by the jump. The simplest kind of system with which to compare the consequences of these ideas is the interstitial solid solution, since one may easily choose a temperature at which only the interstitial component moves, the solvent lattice serving as a completely satisfactory frame of reference. Thus, one avoids complications arising when both species in a binary system move. In addition, one avoids the necessity of knowing the energy for the formation of a vacancy, something which is needed for the analysis of thermal-diffusion data on metals which diffuse by the vacancy-exchange mechanism. However, the number of well-measured interstitial systems is extremely small, and, in particular, there are almost no data in the published literature for the temperature dependence of the heat of transport. If one works with solutes which are gases in the pure state at ordinary temperatures, one may use the technique of thermo-osmosis4 which permits thermal diffusion to be measured over a small temperature difference so that the temperature dependence of Q* can be more easily determined. The choice of dissolved hydrogen in iron and nickel was based on these considerations as well as on the desire to look for an isotope effect associated with localized

Jan 1, 1965

Quarrying and crushing 500 tons of limestone plus burning some 240 tons of limestone per day are the two initial phases in the production of borax, soda ash, sodium sulfate and related chemicals at Stauffer Chemical Co.&apos;s plant in Westend, Calif. These processing steps have been upgraded in recent years by the installation of new primary and secondary crushers, an 8 x 340-ft rotary kiln plus kiln feed, control and cooling components-all designed and manufactured by Traylor Engineering and Manufacturing Division of Fuller Co. As a result of this new equipment, a new product- quicklime-has been added to the West End product family and considerable reductions have been realized in fuel and manpower costs.

Jan 1, 1965

By R. J. Pearce, I. Whittle, J. J. Stobbs

The oxidation kinetics of UCu5 in carbon dioxide have been studied over the temperature range 350° to 850°C. At any one temperature, two successive parabolic rate constants are obtained. Up to 650°C, the temperature dependence of the reaction is snzall and the first parabolic rate constant is higher than the second. At temperatures of 690°C and above, there is a very marked temperature dependence and the second rate constant is the higher. Metallo-graphic examination has shown that attack proceeds via internal oxidation. THE oxidation behavior of the U-Cu intermetallic compound, UCu5, in carbon dioxide was briefly examined during investigations aimed at selecting oxidation-resistant uranium-alloy coatings.&apos; It was found that an extremely thick, coherent scale was formed coated at the scale-gas interface with a thin, apparently continuous layer of copper. A more detailed investigation of the oxidation of UCus has now been made. Previous published work2 has been limited to a brief examination of UCu5 in connection with the oxidation of a U-1 wt pct Cu alloy in carbon dioxide. No attempt was made to explain its behavior, but the work indicated that attack proceeded by intern oxidation, with the formation of a layer of copper on the surface of the specimen. EXPERIMENTAL UCus was prepared by arc melting the stoichio-metric amounts of high-purity copper* and uran-

Jan 1, 1965

By T. B. Massalski, Horace Pops

Martensitic transformations were observed by optical metallography and electrical-resistivity measurements during cooling at cryogenic temperatures of the bcc pr-phase Au-Zn alloys. The com-position dependence of the MS, MF, AS , and AF temperatures have been determined. It is concluded that the martensitic platelets which grow mainly in the lengthwise direction and which are associated with a very small temperature hysteresis are "thermoelastic" martensite. In some cases the observed structure seems to have no definite crys-tallographic habit or consists of a mixture of- plates and broad transformed areas. THE majority of the bcc /3-phase alloys in systems of copper, silver, and gold with zinc and cadmium are unstable at low temperatures and undergo a transformation upon further cooling into another structure. A large number of such transformations are martensitic. The composition dependence of the Ms temperatures has been determined and reported for CU-~n,&apos; Ag-Cd,&apos; and AU-C~~ alloys. The 50 at. pct ordered Au-Zn p&apos; alloy has been reported by Jan and pearson4 to transform martensitically at 58°K in connection with their study of the de Haas-van Alphen effect The p&apos; phase in the Au-Zn system has the ordered CsC1-type structure. The phase field is shown in Fig. 1: it has the typical V shape which is characteristic of all copper-, silver-, and gold-based binary /3-phase alloys. There appears to be no a priori reason why the transformation should be limited to the equiatomic composition and the availability of a cryogenic stage for optical metallography5 has permitted studies down to the liquid-helium temperature of a series of alloys in this system. EXPERIMENTAL PROCEDURE Predetermined weights of 99.999 pct pure gold and zinc were melted and cast under a partial atmosphere of helium in sealed quartz capsules. Thorough mixing of the molten metals was achieved by vigorous shaking, followed by a rapid quench into a brine solution. All ingots were homogenized at 640°C for 4 days. The loss in weight was usually less than 0.04 wt pct and was assumed to be due to

Jan 1, 1965

By Paul E. Blackburn, Joan B. Berkowitz-Mattuck, Edward J. Felten

The oxidation behavior of MOSi2 has been studied between 450° and 650°C, the temperature region where "pesling" occurs. Disintegration ("pest-ing") of MoSi2 is shown to occur in the presence of oxygen, but not nitrogen, carbon dioxide, carbon monoxide. or argon. The rate of disintegration is extremely sensitive to oxygen pressure. The crack density of polycrystalline MoSi2 increases ivith lime at temperature. All kinds of cracks are observed: THE excellent oxidation resistance of MoSi, at temperatures of 1000 to 1700°C promises to have important technological benefits. However. the ap- Ihose which are confined within a single grain, those that ci&apos;oss grain boundaries transversely, and those that follow grain boundaries. Laue photographs verify the existence of Iranscryslalline cleavage. Single crystals of MOSi2 do not "pest". Tlrcd solrlbility of oxygen in MoSi2 is extremely low, no lattice changes being observed as a result of exposure of MoSi2 to oxygen in the "pest" temperature range. plicability of MoSi2 is somewhat restricted by the occurrence of a completely destructive oxidation of the intermetallic phase at intermediate temperatures (300" to 6003C). This phenomena was ternled to be the "MoSi2 pest" by Fitzer who first observed it.&apos; Molybdenum disilicide is a metallic material in both physical appearance and electrical properties.

Jan 1, 1965