Jan 1, 1912

Doctor David Yang has presented an important new flotation development in the area of fine particle flotation technology; at the same time Dr. Yang presents an explanation for the effectiveness of this improved new fine flotation system in terms of an optimum dispersion state. The same statement is made for the case of carrier flotation (ultraflotation), in the removal of anatase from kaolinite by addition of calcite (selective flocculation of the anatase - calcite system and dispersion of kaolinite). Dr. Yang's data and statements raise some important questions, and I will adress myself to the more fundamental aspects of this new flotation system. The addition of sodium silicate, well known as a good depressant-dispersant agent for siliceous gangue minerals, is proved to be greatly enhanced by the incorporation of polyvalent metal salts into sodium silicate prior to flotation, producing in this manner a condition, as described by Dr. Yang, of optimum dispersion, which in the case of fine-grained oxidized taconite can be described as selective flocculation (coagulation) of hematite and almost complete dispersion of siliceous gangue components. Dr. Yang recognizes that the main mechanism, while not completely understood at this time, seems to operate by modifying the surface characteristics of the gangue slime particles so as to prevent collector from bonding there to, and making the particles strongly hydrophilic so they will become fully dispersed and consequently will not float during froth flotation. At the same time it appears that the conditioning reagent also modified the surface characteristics of the floated minerals (hematite and spodumene in this case) so that they will aggregate and tend to more readily adsorb the collector, resulting in an improved flotation kinetics and selectivity.

Jan 1, 1979

By P. Shahinian, M. R. Achter

P. Shahinian and M. R. Achter (U.S. Naval Research Laboratory)—We should like to point out another instance where concentration of impurities in grain boundaries led to an embrittlement. In this case an impure nickel (99.8 pct) developed many more in-tergranular cracks during creep in a nitrogen atmosphere than in vacuum.5 In comparison high-purity nickel (99.99 pct) exhibited a much smaller atmosphere effect. We concluded that the interartion of the nitrogen with nitride-forming impurities concentrated at grain boundaries promoted inter-granular cracking.

Jan 1, 1965

By Frank S. McKenna, Myron A. Pugacz, Clarence E. Jackson

THE notched-bar impact test has proved worth while in certain applications as a test for control of the quality or the heat- . treatment of steel. In view of the serious thought that even so simple a test as the tensile test, has evoked during the past years, it is not surprising that the notched- bar impact test should have inspired much experimental work. The correlation of the great number of data has not been successful, although steady progress has been made toward a better understanding of this test. Progress has been made, especially, in the isolation of the effects of the many variables that control the results. The stress system imposed on a specimen with a notch is so complicated and un- predictable that no simple evaluation of the test has been possible. Because of this uncertainty, many engineers hesitate to use the notched-bar impact test, and this attitude may well continue until a better understanding of the effects of the variables in the test are available. Without doubt, any additional data that may be presented should be accompanied by as complete a description of the details of test as possible, so that it may be added to the general fund of information that is to serve as the basis for the theory of the notched-bar impact test. The many factors that may control the test results have been pointed out repeatedly. The importance of the effect of the type and dimensions of the specimen has been recognized. Most of the work reported by American investigators has been limited to small- size (Charpy) specimens tested as a simple beam; two types of notches (Fig. I) have been commonly used. Considerable data have also been presented by many investigators using a small specimen tested as a cantilever beam; this commonly being called the Izod test. Here, however, a shear component of stress makes the stress system even mare complex than that present in the simple beam type of test, hence a critical analysis is difficult. Much work has also been reported by investigators using the tension type of specimen. A second variable that must be con- trolled is the testing temperature. An indication that the tests were performed at room temperature is not sufficient, since in many steels a variation of a few degrees in the actual testing temperature may be sufficient to give an entirely different range of results. Other factors. such as the com- position and condition of the material being tested and the speed of test, should also be considered. Many investigators have contributed data and theoretical discussions on the problems encountered in notched-bar test-

Jan 1, 1944

By B. E. Fernow

In order to ascertain to what extent the mining industry has been dependent upon forest-supplies, for the purpose of a report upon

Jan 1, 1889

By Edward L. Clark, Garrett A. Muilenburg

THE first record of the discovery of iron ore in Missouri was Marquette's observation in 1673 of brown iron ore, or limonite, in the Mississippi River bluffs just north of the mouth of Apple Creek in southeastern Perry County. There is no record of any attempt to mine or smelt Missouri iron ores until 1815, when the Ashebran furnace was erected at the Stouts Creek shut-in near Arcadia, Iron County. Some limonite was treated in this furnace, the first iron furnace west of Ohio, but most of the ore was hematite from Shepherd Mountain and adjacent deposits. Eight years later, in 1823, the Perry furnace five miles north of Caledonia, Washington County, was constructed to smelt limonite ore. It was not until 1890 to 1900, however, that these ores attracted considerable attention. Nearly 300,000 tons had been produced by 1911, and this production had come from 24 counties in the Ozark region. For the next two decades, until 1931, essentially all activities ceased. During the depression years of the thirties when employment was low many people turned to the brown ores for subsistence; consequently production was increased. World War II produced another stimulus to the industry. The availability of risk capital in the past three years has revived interest in these deposits, although no appreciable increase in production has resulted.

Jan 1, 1954

POSITIONS VACANT (Under this heading will he published notes sent to the Secretary of the Institute by members or other persons.) Mine and mill accountant for Mexico. Knowledge of Spanish desirable. Salary $150 to $200 gold per month with living quarters. No. 60. Master mechanic familiar with mine and cyanide plant machinery for Mexico, $200 gold per month and living quarters. No. 61. Electro-metallurgist for production of ferro-alloys, salary $200 to $400 depending on experience. No. 62. Man familiar with ferro-tungsten products of electric furnaces to draw up specifications for machine tools, to watch these tools in service and revise specifications accordingly. Salary $150 to $200 per month. No. 63. Man to take entire charge of the sales of a steel company making electric alloy steels in the shape of ingots, billets and bars. To the right man an opportunity will be offered for taking a leading position in the management of the company and of participating in its results. No. 68. Chemist wanted by Electric Steel concern in the East. Must be fully acquainted with alloy steel analysis. Send full particulars and references. No. 73.

Jan 3, 1916

By L. S. Panyity

THE Cleveland (O.) gas pool described by Frank R. Van Horn,1 is the northern extremity of the great "Clinton" sand gas development in LAKE ERIE General Trend of "Clinton" Sand Pools in Ohio Richland Township, Vinton County FIG. 1. Ohio. Numerous gas pools have been developed in this formation, which are now more or less connected, link by link, forming an almost' continuous gas pool, starting at Cleveland, and running thence southward through Cuyahoga, Medina, Wayne, Ashland, Richland, Knox, Licking,

Jan 6, 1917

By R. G. Davies, P. Beardmore, T. L. Johnston

The flow stress of a series of Ni-Cr-A1 alloys consisting of a dispersion of y' (based on Ni3Al) in a rnatrix of nickel-base solid solution y has been measured at temperatures up to 950°C as a fwzction of the volume fraction of y'. At high temperatures the flow stress is controlled by the amount of Y' in the alloy, i.e., the higher the volume fraction of y', the greater is the flow stress. This simple relationship is not obeyed at low temperatures in so far as a peak in the flow stress-volume fraction relation occurs at about 25 pct y'. The variation in the mechanical properlies of these alloys as a function of both temperature and volume fraction of y' has been correlated with changes in distribution of both the dislocations and y'. The results are interpreted on the basis that at low temperatures the y matrix is strengthened significantly bv the presence of a hyperfine y' precipitate due to decomposition on cooling; at high temperatures the y matrix is a single phase of low strength. It is clearly recognized that the high temperature strength of most nickel-base superalloys depends upon a dispersion of the ordered fcc phase y', based on Ni3A1, in a fcc solid solution matrix y based on nickel. Although the volume fraction of y' varies widely from about 0.2 in Nimonic 80A to about 0.6 in Mar-M200, all such nickel-base alloys manifest an unusual insensi-tivity of the flow stress with respect to temperature. In Mar-M200 for example, the 0.2 pct flow stress remains essentially constant from room temperature to 750°C. The conclusion has been drawn1 that the characteristically low temperature dependence of the flow stress of y-y' nickel-base alloys is obtained when the state of dispersion of y' is such that dislocations are forced to cut through the y' particles at the onset of yielding. When the spacing between the y' particles is so large that the flow stress is controlled by dislocation bowing between particles, then the initial flow stress decreases progressively with an increase in temperature at a rate determined by changes in elastic properties. The same conclusion is inherent in the detailed, mechanistic model of the deformation process in commercial superalloys which has been developed by Copley and ear' in which the temperature independent flow stress is attributed primarily to the contribution of the antiphase boundary energy created in the y' particles during deformation. In this theory the temperature insensitivity of the flow stress is a reflection of the constant antiphase boundary energy as a function of temperature. An important microstructural parameter that is relevant to the explanations that have been suggested' to account for the temperature insensitivity of the flow stress is the volume fraction of y'. To vary the latter to any significant extent in a given commercial alloy is clearly difficult. However, it is possible in a relatively simple Ni-Al-Cr ternary system which manifests analogous microstructures in terms of the distribution of y' in y and contains specific alloys which have flow properties that depend on temperature in a manner quite similar to their more complex commercial counterparts. Hornbogen et . have studied precipitation phenomena and deformation mechanisms in such alloys but only where the y' volume fraction was small (less than 0.2) and the y' particle size varied from less than 100A up to a maximum of -1000A. In the present study, a series of alloys was prepared in which the volume percent of y' at 900°C was varied from 0 to 100 pct with the y' particle size (of the order 0.5 p) comparable to the sizes obtained in commercial superalloys. Particular attention has been given to the relationship between variations in the volume fraction and distribution of y' and the temperature dependence of the flow stress EXPERIMENTAL TECHNIQUES The Ni-Cr-Al system was selected because it is well characterized, bears a close relationship to commercial alloys, and offers the advantage of an extra degree of freedom over a binary system. In the present investigation, a series of alloys across the tie line between NisA1 and Ni3Cr (Ni3Cr is not an in-termetallic compound, the nomenclature is only used to designate the composition) were vacuum cast. The pseudobinary6 and the composition of the alloys used are shown in Fig. 1. It is important to note that the compositions of the y phase and the y' phase in the two-phase alloys was always the same. Alloy compositions were selected from the binary diagram, Fig. 1, in order that aging at 900°C would produce from 0 (100 pct y) to 100 pct y' by volume percent. (The size of the y' particles produced during the equilibrium aging treatment increased as the volume fraction of y' increased, ranging from about 0.2 p at low volume fractions up to about 0.8 p at the highest volume fraction.) The y' phase is based on the inter-metallic compound Ni,A1 which has the fcc LIZ type superlattice structure, and chromium substitutes for aluminum in the structure. The y phase is a disordered fcc solid solution. The alloys were heat treated at 1150°C for 2 hr, air cooled to room temperature, and finally annealed for 16 hr at 900°C. The rods were then centerless ground to 0.25 in. diam and cut into compression samples 0.5 in. long. The compression tests were made on an In-stron machine at a strain rate of 7 x 10"4 sec-'. A rapid heating radiant heat furnace was used which minimized the heating and temperature stabilization time to 10 min for the highest testing temperature. All the tests were stopped after 5 pct plastic strain.

Jan 1, 1970

By R. F. Mehl, M. Gensamer

THE stresses which initiate deformation processes in metals are fundamentally important in the study of the mechanical properties of metals. A point of inflection in the load-elongation curves obtained for single crystals1 has been rather too readily interpreted as a true yield point, and the critical resolved shearing stress on the plane of slip taken as a material constant. Even early work showed that the stress at this point varies with rate of loading, but it has not been generally appreciated that creep tests under static loads alone are suited for determining the existence or nonexistence of a yield point.2 It has now been shown by Miller that single crystals of zinc3 when loaded statically begin to yield at loads too small to measure; as a result there is no case now known, apart from that cited in the present paper, in which a true critical stress for yielding has been demonstrated for single crystals of metals. The case of iron has especial interest: the existence of an upper and lower yield point and of an elongation at the yield point in ordinary iron and steel marks this substance as unusual, though the effects have been found to a very minor degree in other metals and alloys. ‡ Most alloys do not show such marked phenomena when appreciable yielding begins, and accordingly modern practice is to speak of the yield strength of such materials, a stress read from the load-elongation curve after elongation has begun, rather than yield point. The special behavior of iron suggests that it is more likely that single crystals of iron should have a true yield point than other metals. The study of the mechanical properties of metals and alloys requires a determination of the crystallographic mechanism of deformation, whether deformation proceeds by slip, twinning, or cleavage, or a combination of these, and a determination of the stresses that induce these modes of

Jan 1, 1938

I strongly endorse Mr. Jackson's (Inland Steel Company) oral comment on the authors' paper that, as blast furnace slag is removed from the BOF charge, lime solution may be retarded. After two or three pourings, the blast furnace slag will contain some iron oxide and considerable manganese oxide, and it is hot and possibly still liquid. A few thousand pounds of this slag will speed up the slag development rate considerably and could be considered a good auxiliary flux. Although the removal of blast furnace slag from the BOF charge lowers the total sulfur load by 40 to 50%, we must have a good, quick slag development in the BOF to bring .030 to .035% sulfur hot metal to .020%, a requirement on a high percentage of our steels today. In discussions at off-the-record meetings and one not published at last year's annual meeting as well as discussions with many operators over the past 1-1/2 years, I predicted that the removal of blast furnace slag could slow down lime dissolution and that, if a shop had dissolution problems before, the problem could be quite serious.

Jan 1, 1972

By J. Szekely, G. P. Martins

A formulation is given for describing the rate of expansion of spherical bubbles rising in liquids the freeboard of which is evacuated. The computer solution of the resultant differential equations has shown that, for low freeboard pressures (less than about 5 mm Hg), on approaching the free surface the bubbles expand much less rapidly than predictable from equilibrium considerations. In other words, in this region the pressure inside the bubbles will be significantly larger than the static pressure in the liquid corresponding to the position of the bubble. These theoretical predictions were confirmed by experimental work, using two-dimensional air bubbles rising in mercury. The important consequence of these findings is that the expansion of gas bubbles in vacuum degassing operations will be a great deal less than expected from hydrostatic considerations. This would lead to a significant reduction in the available interfacial area and may explain the apparent poor efficiency of many vacuum degassing units. VACUUM degassing as a treatment for liquid steel has gained widespread popularity in recent years; the number of known installations exceeds several hundred at the present time.' Although much information is available on both the thermodynamics of the system and the overall performance of various industrial units, much less is known about the fundamental aspects of the process kinetics.2-4 The basic physical situation common to virtually all vacuum degassing operations is the interaction between gas bubbles (swarms of bubbles) and the surrounding molten metal, held in a container, the freeborad of which is at a low absolute pressure. Once formed (or introduced from an external source) the bubbles will ascend, due to the buoyancy forces, and, during this ascent, a significant increase in their volume will occur. This progressive increase in the bubble volume is due to two factors: a) the continuous reduction in the static pressure acting on the bubble during its rise; and b) mass transfer into the bubble from the surrounding molten steel. In a recent paper Richardson and Bradshaw developed equations5 for describing mass transfer into gas bubbles from molten metals at reduced pressures. However, in deriving these expressions it was assumed that the pressure inside the bubble was identical to the static pressure in the adjacent liquid. In other words, the volume of the bubble was considered to be in equilibrium with the pressure of the fluid adjacent to it. This assumption, thus their analysis presented, was thought to be reasonably accurate for most of the bubble's ascent; however, it was unlikely to be valid in the immediate vicinity of the free surface, held at a low pressure. It was pointed out in the discussion6 that the region close to the surface may be of considerable importance as both the driving force and the interfacial area available for mass transfer are at their highest value here. The ' 'anomalous" behavior of gas bubbles when approaching a free surface at low pressures was recently confirmed in a preliminary investigation by Szekely and Martins. ?1 Here high-speed motion photography was used to study air bubbles rising in a column of n-tetradecane with a freeboard pressure of 0.1 mm Hg. It was found that significant distortion of the bubbles occurred on approaching the free surface; furthermore, the expansion observed was much less than what one could expect from hydrostatic considerations, i.e., factor a previously discussed. It follows from the foregoing that a detailed study of these phenomena would be justified both from fundamental considerations and because of their potential relevance to technology. The purpose of the paper is to present a more realistic formulation for the expansion of a gas bubble approaching a low-pressure region, together with a comparison of the theoretical prediction with experimental measurement. An inert bubble will be considered in the first instance; it is thought that the understanding of the fluid mechanics is an essential first step toward the realistic formulation of the mass transfer process. This latter problem will be the subject of a subsequent publication. FORMULATION The Physical Model. Consider a spherical bubble, of initial radius Ro, rising in a fluid, having a density pL. Initially let the bubble be at a distance H from the free surface, and at a pressure Pgo, as illustrated in Fig. 1. Pgo, the initial pressure in the bubble, is given by the following equation: pgo = Po = Ptp +pLgH [ la] where Po is the pressure in the liquid corresponding to the initial position of the bubble and Ptp is the pressure at the free surface. The fluid pressure at

Jan 1, 1970

By W. A. Doble

Opinions differ as to whether the water-wheel almost universally known as the Pelton type belongs to the impulse, the tangential, the reactive, the jet or the percussion class, or to a cross between two or more of these classes. The fact is, that for an almost infinitesimal part of a second the axis of the jet of water strikes the bucket of this wheel at a true tangent to its base-line. The percussion of the water, striking the bucket, imparts an impulse to the wheel, causing rotation; and generally the bucket is so shaped that the direction of the jet is

Jan 1, 1900

By P. A. Laxen, H. R. Spedden, A. M. Gaudin

WHEN a mineral particle is fractured, bonds between the atoms are broken. The unsatisfied forces that appear at the newly formed surface1 are considered to be responsible for the adsorption of ions at the mineral surface. A knowledge of the mechanism and extent of ion sorption from solution onto a mineral surface is of interest in the development of the theory of flotation.2,3 Study of the adsorption of sodium from an aqueous solution on quartz offers a simple approach to this complicated problem. The availability of a radioisotope as a tracer element meant that accurate data could be obtained.4,5 Three main factors which appeared likely to affect the adsorption of sodium are: 1-concentration of sodium in the solution, 2-concentration of other cations in the solution, and 3-anions present in the solution. Hydrogen and hydroxyl ions are always present in an aqueous solution. By controlling the pH, the concentration of these two ions was kept constant. The variation in the amount of sodium adsorbed with variation in sodium concentration was then determined under conditions standardized in regard to hydrogen ion. The effect of concentration of hydrogen ions and of other cations was also measured. A few experiments were made to get a preliminary idea on the effect of anions. The active isotope of sodium was available as sodium nitrate. Standard sodium nitrate solutions were used throughout these experiments except when the effects of other anions were studied. It was found that sodium adsorption increased with sodium-ion concentration, but less rapidly than in proportion to it. Increasing hydrogen-ion concentration, or conversely decreasing hydroxylion, brings about a comparatively slight decrease in sodium-ion adsorption. Increasing the concentration of cations other than hydrogen or sodium decreases somewhat the adsorption of sodium ion. It would appear as if the kind of anion is a secondary factor in guiding the amount of sodium ion that is adsorbed. Materials and Methods Quartz The quartz was prepared as in previous work in the Robert H. Richards Mineral Engineering Laboratory4 except for the refinement of using de-ionized distilled water for the final washing of the sized quartz, prior to drying5 To minimize the laborious preparation of quartz, experiments were made to determine whether the sodium-covered quartz could be washed free of sodium and re-used. The experiments were successful as indicated by lack of Na' activity on the repurified material and by its characteristic sodium adsorption. Table I gives the spectrographic analyses of the quartz used. The quartz ranged from 16 to 40 microns in size, averaging about 23 microns (microscope measurement), and had a surface of 1850 sq cm per g (lot I), 2210 (lot II) and 2000 (lot III) as determined by the Bloecher method.6 Radioactive Sodium Method of Beta Counting for Adsorbed Sodium: Na22, the radioisotope of sodium, possesses convenient properties.7 It has a half-life of 3 years, thus requiring no allowance for decay during an experiment. On decay it emits a 0.575 mev ß radiation and a 1.30 mev ? radiation. The decay scheme is illustrated in the following equation: [Y Nam S. - 'Net 3 years] The ß radiation is sufficiently strong to penetrate an end-window type of Geiger-Mueller counting tube. This, in turn, makes it possible to use external counting, a great advantage in technique. Furthermore, it permits the assaying of solids arranged in infinite thickness, while assaying evaporated liquors on standardized planchets. The equipment used was standard and similar to that employed by Chang8 The original active material was 1 ml of solution containing 1 millicurie of Na22 as nitrate. This active solution was diluted to 1000 ml. Five milliliters of this diluted active solution was found to give a quartz sample a sufficiently high activity for accurate evaluation of the sodium partition in the adsorption measurements. Also, 1 ml of final solution gave a sufficiently high count for precision on the liquor analyses. The sodium concentration of the diluted active solution was 1.2 mg per liter, so that 6 mg of sodium for 60 ml of test solution and 12 g of quartz was the minimum amount used. The active solution was stored in a Saftepak bottle. Procedure for Adsorption Tests: The method consisted of agitating 12 g of quartz with 60 ml of solution of known sodium concentration for enough time to establish equilibrium between the solution and the quartz surface. The quartz was separated as completely as possible from the solution by filtering and centrifuging. The activity on the quartz and in the equilibrium solution was measured and the partition of the sodium was calculated from the resulting data. The detailed procedure for the adsorption test is set forth in a thesis by Laxen5 In brief, it included the following steps: 1-Ascertainment of linearity between concentration of Na22 and activity measured. 2-Evaluation of factor to translate activity on solid of infinite thickness in terms of activity on an evaporated active film of minute thickness, on the various shelves of the counter shield. 3-Taking precautions to avoid evaporation of water during centrifuging.

Jan 1, 1952

By Ben Gumpertz

THE important factors in any study of the screening of sand with a gravel enve-lope, as applied to use in oil wells, are: (r) sand size and shape, (2) gravel size and shape, (3) ratio of gravel size to sand size, (4) flow velocity, (5) viscosity of the fluid. Perhaps the first extensive investigation of the function of gravel in screening sand was performed by Coberly and Wagner,1 from which the following conclusion was drawn: "The diameter of the largest grains in a single classified sand suitable for gravel packing is approximately 23 times the grain size at the ten-percentile analysis of the formation sample." This applies to sands classified by Tyler screens and is for gravel grains of the maximum size that could be used to form a stable bridge. Field practice has shown that the screening effect of a given gravel for a given sand apparently varies with the flow velocity.2 Also, it has been assumed by some opera-tors that the thickness of the walls of the gravel envelope surrounding the well has little effect upon the screening process. It is thought by others that a narrow envelope of gravel might form an ineffec-tive screen. Thus the purposes of this work are: I. To investigate the effect of gravel-sand size ratio upon screening action under the condition of varying flow velocities. 2. To investigate the effect upon screen-ing action of varying the thickness of the gravel screen.

Jan 1, 1940

HAVING already shown you the methods of making the moulds for casting and how they are to be prepared so that they may receive the melted metals well, it is now necessary, in order to complete the casting with perfection, that I show you not only the operations and instruments by which metals are softened, but also how metals can be made as liquid and fluid as water so they may easily enter into all the hollows of the moulds that you have made. Of these, besides the fire which is the prime agent, there is a very powerful furnace, which is called a reverberator.* I believe this is chosen not only for convenience but also because it is necessary in large casts. This is made of baked bricks, or of crude ones if desired or of suitable fire-resistant stones. Although all masters have the same objective, each one proceeds to make this kind of furnace according to his own ideas so that it can be said that there are almost as many different shapes of such furnaces as there are masters. This can be seen in the place that contains the metal, which is of such a shape that the force of the fire may operate better. Thus some masters are called good who, seeing no farther than what has been shown them, make them circular like a bread oven. Some others make them oval across the fire en- trance, while others extend them lengthwise. Also, there are some who make a single outlet for the flames, some two, and some three. Some make the entrance for the fire high and narrow and others, wide and low. The same is true of the place where the flames are generated, which is called the firebox. Some put the wood in from the side, some lengthwise in the same direction as the entrance for the flames, and some from above by means of a little hole. Also, one makes the vault low, and another makes it high. And while one puts an entrance for air underneath so that the

Jan 1, 1942

By E. P. Valby

A method is presented in which the hydrocarbon weight fractional analyses of the well effluents from a true gas-tip-portion well and a true dark-oil-ring well furnish the basic data for determining the properties of any mixture of production from the two sources. The effect of injected gas on these properties can be computed. Comparison of similar properties of a given well effluent to the properties of mixtures of the basic well effluents will give the relative amounts of production from the two sources and injected gas. Presentation of Problem Oil fields having an area of gas-cap, or light-oil production, over the dark-oil area present a problem of increasing gas-oil ratios during the production of an oil well. The use of pressure maintenance in a field such as above, or a cycling project, wherein residue gas from an absorption plant is injected into the reservoir, adds to the problem, because a part of the increased gas-oil ratio may be due to the production of injected gas. The usefulness of a means to determine the amount of injected gas in a well effluent led to the development of a method in which well-effluent analyses of a true gas-cap-portion well and a true dark-oil-ring well furnish the basic data needed to determine whether injected gas of a known composition is present in a given well effluent. Development op Method The method presented herein is based upon the principle that if two fluids, or well effluents, having different properties are mixed in known proportions by weight, • the properties of their mixtures can be computed. Conversely, if these basic data are known, the properties of a mixed well effauent can be used to compute the relative amounts of each type of well effluent in the mixture. A convenient way of making these computations is to have the fractional analyses of the base well effluents and mixtures expressed in weight fractions The mathematical equations expressing the properties of mixtures will be developed for a two-component system consisting of the well effluents from the dark-oil ring and the gas-cap area. The added effect of injected gas, a third component, will also be developed. The following assumptions have been made in developing the method: 1. The gas-cap and dark-oil fluids exist initially in separate portions of the reservoir. 2. The fluids in each portion exist in a single phase at pressures above the saturation pressure for the dark-oil fluid. 3. The composition of each fluid is substantially constant throughout its respective portion of the reservoir. 4. Changes in reservoir pressure and temperature will not change the composition of the fluid entering the well bore. 5. The injected gas displaces original gas-cap fluid 100 per cent. •• 6. AS the injected gas travels through a

Jan 1, 1945

By E. S. Wheeler

THE rapid increase in the use of monel metal and malleable nickel in the form of sheet, rod and tube has resulted in a similar increase in the demand for these metals in the form of castings. These castings range in size from small valves and pipe fittings weighing a few ounces to large centrifugal pumps, gate valves and marine propellers, some of the latter weighing as much as 24,000 lb. A group of such castings is shown in Fig. 1. A large nickel agitator is shown in Fig. 2. FIG. 1.-A GROUP OF MONEL METAL AND NICKEL CASTINGS. Monel metal castings are widely used in accessories for steam power plants and in a variety of chemical plant. equipment where the corrosion resistance, high strength and toughness characteristic of this metal render it particularly valuable. Nickel castings find extensive use in the construction of corrosion resistant apparatus, and are often used in conjunction with wrought nickel sheet and tube in the fabrication of equipment for handling a variety of chemical and food products, particularly dairy products. In response to this demand for castings, numerous foundries have undertaken the production of castings of these metals and have met with varying degrees of success.

Jan 1, 1930

By S. Nenno, T. Saburi, Y. Mizutani, M. Yomarnoto, K. Komatsu

In the equilibrium phase diagram of the Ni-Mo sys-tem1,2 available at present, intermetallic compounds (or ordered phases)ß(Ni4Mo) and ?(Ni3Mo) are known to exist to the nickel rich side. In our recent investigations on Ni-Mo alloys, however, it has been found that the quenched alloys from the high temperature region containing more molybdenum than the Ni4Mo do not decompose directly into 0 and when annealed isothermally below the peritectoid temperature, i.e., 865°C. This note is to report the existence of Pt2Mo type superlattice (possibly ordered Ni2Mo) as a metastable phase in the early stage of decomposition. Alloys containing 20.1, 22.7, and 24.4 at. pct Mo were prepared by vacuum-melting electrolytic nickel of 99.9 pct purity and molybdenum powder of 99.9 pct purity in an alumina crucible. From the resulting ingots, sheets 0.3 mm thick were obtained by forging, hot-, and cold-rolling. The sheet specimens were water-quenched from ! region and subsequently annealed for various periods of time at temperatures below the peritectoid temperature. On these specimens were made optical-microscopic and transmis-sion-electron-microscopic observations. Fig. 1- Optical micrograph of the 22.7 at. pct Mo specimen annealed for 100 hr at 700°C after quenching. (ß + ?) region, B, nucleated along a grain boundaries are invading the preexisting (ß + Ni2Mo) region, A. Details of A are observable only by electron microscopy. Etchant: 60 pct HNO3-40 pct CH3COOH.

Jan 1, 1970

By M. S. Abrahams

Germanium has been rolled in the temperature range of 700o to 800°C. The thickness has been decreased by as much as a factor of four, from a thickness of 0.032 in. to a thickness of 0.008 in. For deformations below 60 pet, the true strain per pass is found to be a constant; from the temperature dependence of this slope, an activation energy of about 2.5 ev is obtained. This energy agrees with that for dislocation climb in germanium . For reductions greater than 60 pet, complete rings are seen in the Lave photographs, new grains are observed in the microstructure, considerable softening occurs, and the hole mobility is very low. This evidence indicates that the recrystallization of gertnanium has occurred. GERMANIUM has been deformed in many ways1 including tension, compression, torsion, and bending since Gallagher2 first described its plastic nature at elevated temperatures. All of these studies indicate that the glide plane in germanium is (111) and that the glide direction is (110). Rolled germanium specimens were used by Kolm, Warekois, and Kulin3 in their X-ray study of deformed semiconductors, but no information is given on the rolling itself. The present experiments deal with the rolling of germanium at various temperatures and for different orientations. In all previous deformation studies, the phenomenon of recrystallization (i.e., the transformation of a single crystal into a polycrystal) in germanium has not been observed4 despite relatively large deformations at elevated temperatures. The proposed reason4 for this was that sufficient energy could not be stored in the deformed germanium lattice. In contrast to the earlier studies this work will present evidence indicating that recrystallization occurs in germanium during rolling at an elevated temperature. I) EXPERIMENTAL PROCEDURE A) Test Specimens. The samples used for rolling were in the form of rectangular parallelepipeds measuring 0.3 in. long, 0.06 in. wide, and 0.035 in. high. They were cut from an undoped single-crystal ingot of p-type germanium with a resistivity of 24.4 ohm-cm, a Hall mobility of 2300 sq cm v-' sec-l, and a hole concentration of 1.1 x 1014 cm"3 at room temperature. The surfaces of the specimens were metallographically polished prior to rolling. The initial dislocation density of the samples was about 10' cm-' as determined by etching in CP4. Two different specimen orientations were used. In the first case, the direction of rolling was parallel to (251), the surfaces in contact with the rolls were of the form (1021, and the normal to the third face was parallel to (211). The corresponding di-

Jan 1, 1964