Adsorption Of Sodium Ion On Quartz

WHEN a mineral particle is fractured, bonds between the atoms are broken. The unsatisfied forces that appear at the newly formed surface1 are considered to be responsible for the adsorption of ions at the mineral surface. A knowledge of the mechanism and extent of ion sorption from solution onto a mineral surface is of interest in the development of the theory of flotation.2,3 Study of the adsorption of sodium from an aqueous solution on quartz offers a simple approach to this complicated problem. The availability of a radioisotope as a tracer element meant that accurate data could be obtained.4,5 Three main factors which appeared likely to affect the adsorption of sodium are: 1-concentration of sodium in the solution, 2-concentration of other cations in the solution, and 3-anions present in the solution. Hydrogen and hydroxyl ions are always present in an aqueous solution. By controlling the pH, the concentration of these two ions was kept constant. The variation in the amount of sodium adsorbed with variation in sodium concentration was then determined under conditions standardized in regard to hydrogen ion. The effect of concentration of hydrogen ions and of other cations was also measured. A few experiments were made to get a preliminary idea on the effect of anions. The active isotope of sodium was available as sodium nitrate. Standard sodium nitrate solutions were used throughout these experiments except when the effects of other anions were studied. It was found that sodium adsorption increased with sodium-ion concentration, but less rapidly than in proportion to it. Increasing hydrogen-ion concentration, or conversely decreasing hydroxylion, brings about a comparatively slight decrease in sodium-ion adsorption. Increasing the concentration of cations other than hydrogen or sodium decreases somewhat the adsorption of sodium ion. It would appear as if the kind of anion is a secondary factor in guiding the amount of sodium ion that is adsorbed. Materials and Methods Quartz The quartz was prepared as in previous work in the Robert H. Richards Mineral Engineering Laboratory4 except for the refinement of using de-ionized distilled water for the final washing of the sized quartz, prior to drying5 To minimize the laborious preparation of quartz, experiments were made to determine whether the sodium-covered quartz could be washed free of sodium and re-used. The experiments were successful as indicated by lack of Na' activity on the repurified material and by its characteristic sodium adsorption. Table I gives the spectrographic analyses of the quartz used. The quartz ranged from 16 to 40 microns in size, averaging about 23 microns (microscope measurement), and had a surface of 1850 sq cm per g (lot I), 2210 (lot II) and 2000 (lot III) as determined by the Bloecher method.6 Radioactive Sodium Method of Beta Counting for Adsorbed Sodium: Na22, the radioisotope of sodium, possesses convenient properties.7 It has a half-life of 3 years, thus requiring no allowance for decay during an experiment. On decay it emits a 0.575 mev ß radiation and a 1.30 mev ? radiation. The decay scheme is illustrated in the following equation: [Y Nam S. - 'Net 3 years] The ß radiation is sufficiently strong to penetrate an end-window type of Geiger-Mueller counting tube. This, in turn, makes it possible to use external counting, a great advantage in technique. Furthermore, it permits the assaying of solids arranged in infinite thickness, while assaying evaporated liquors on standardized planchets. The equipment used was standard and similar to that employed by Chang8 The original active material was 1 ml of solution containing 1 millicurie of Na22 as nitrate. This active solution was diluted to 1000 ml. Five milliliters of this diluted active solution was found to give a quartz sample a sufficiently high activity for accurate evaluation of the sodium partition in the adsorption measurements. Also, 1 ml of final solution gave a sufficiently high count for precision on the liquor analyses. The sodium concentration of the diluted active solution was 1.2 mg per liter, so that 6 mg of sodium for 60 ml of test solution and 12 g of quartz was the minimum amount used. The active solution was stored in a Saftepak bottle. Procedure for Adsorption Tests: The method consisted of agitating 12 g of quartz with 60 ml of solution of known sodium concentration for enough time to establish equilibrium between the solution and the quartz surface. The quartz was separated as completely as possible from the solution by filtering and centrifuging. The activity on the quartz and in the equilibrium solution was measured and the partition of the sodium was calculated from the resulting data. The detailed procedure for the adsorption test is set forth in a thesis by Laxen5 In brief, it included the following steps: 1-Ascertainment of linearity between concentration of Na22 and activity measured. 2-Evaluation of factor to translate activity on solid of infinite thickness in terms of activity on an evaporated active film of minute thickness, on the various shelves of the counter shield. 3-Taking precautions to avoid evaporation of water during centrifuging.