The specific conductance of FeOx,-CaO melts in contact with iron was found to decrease from 200 ohm-1 cm-1 for FeO, to 40 ohm-1 cm-1 for a melt containing 26.3 pct CaO at 1400°C. The temperature coefficient was positive at all compositions, but became smaller at high CaO contents. Current efficiencies for electrolysis increased from 2.5 pct in FeOx to 17.3 pct at the high CaO composition, indicating a change from predominantly electronic conduction to conduction with a substantial ionic contribution. It was shown that Ca++ ions as well as Fe++ ions carry the ionic current. A subsidiary investigation on the apparent effect of atmospheres of argon, helium, and nitrogen on the electrical conductivity showed that this could be correlated with surface temperature losses, which varied with the thermal conductivities of the gases and resulted in precipitation of metal by the reaction 3 Fe++ = 2 Fe+++ + Fe. The work described in this paper is offered as a contribution to the general fund of knowledge concerning metallurgical slags. Measurement of electrical conductivity and electrolysis are comparatively trouble -free methods for investigating molten materials, but, although these methods had been used for complex slags, it was not until the work of Bockris et al.1 that the approach of examining simple binary slag systems was employed, and CaO-SiO2, MnO-SiO2, and Al2O3-Si9 were studied. Two groups have performed work of particular relevance to the present investigation. Inouye, Tomlinson, and chipman2 studied the conductivity of wustite as a function of temperature and of the addition of 5 mol pct of a number of oxides, including CaO. They concluded that molten FeOx in equilibrium with iron is a semiconductor. Simnad, Derge, and ceorge3 demonstrated the ionic nature of liquid iron silicate slags and also concluded that, although the conductivity of FeOx in equilibrium with iron is predominantly electronic in nature, there is a small ionic contribution. The work reported here on FeOx,-CaO slags consists of three main parts, namely, the determination of the specific conductance over a wide composition range, an investigation into the nature of the conductivity through current-efficiency measurements over the same composition range, and an attempt to identify the current-carrying ions, as well as a subsidiary investigation on the apparent effect of the nature of the inert atmosphere on the conductivity. EXPERIMENTAL Materials. The slags, varying in composition from FeOx to 27 pct CaO, were prepared by heating reagent- grade Fe2O3 in an ingot iron crucible with a suitable amount of CaCO3 and, in some cases, powdered iron, in air. This prefused material was then used for the runs. At the end of each run the cell was removed from the furnace and quenched by immersing the bottom half in water. After crushing, the slags were analyzed for calcium and total iron by the usual wet methods. The oxygen content was obtained by difference. Specific Conductance: Apparatus and Method. Fig. shows the experimental setup, with the conductivity cell and leads of ingot iron. The standard four-probe method for measuring high conductivities was used. In this, the potential drop across the unknown resistance is compared with the potential drop across a known resistance connected in series, i .e., same current through both resistances. Thus there are both current and potential leads to the center electrode and to the crucible, which acts as th other electrode. Both ac and dc circuits were available for the measurements; they have been described in earlier work performed in this laboratory.4,5 The geometry of the cell was such that the center electrode was equidistant from the bottom and sides of the crucible. This ensured that the current path was the same irrespective of the magnitude of the conductivity of the material in the cell. Cell constant were measured with KC1 or NaCl solutions, which have considerably lower conductivities (0.0013 to 0.25 ohm-' cm) than the slags, and this precaution in design made sure that the determined cell constants applied to the cells with contents of any conductivity. The cell-constant determinations were made with the ac measuring circuit to prevent polarization. The four-probe method eliminates lead resistance but not the resistance of those parts of the center

Jan 1, 1967

By Robert E. Ogilvie, Zvonimir Ban

Oxidation experiments were conducted above 600°C to investigate the oxidation products formed on the surface of MoSi2. Results are presented which indicate that minor iron impurities play a key role in the oxidation behavior of MoSi2 above 600 °C. Based on considerations of the crystal chemistry of the oxidation products, MoSi2 with rhenium and iron additions was found to be resistant to oxidation in the pesting temperature range. AS early as 1914, Honigschmidtl observed that some silicides of molybdenum exhibited high resistance to oxidation at elevated temperatures. This fact did not arouse much interest until 1950, when Kieffer and cerwenka2 examined this property in more detail. They found that Mo-Si alloys with approximately 70 pct Mo (by weight) could be heated to 1600°C in an oxidizing atmosphere without any significant damage. The surface was found to be protected by the formation of an extremely thin silica glass layer which had no tendency to spa11 during subsequent thermal cycling. In 1955, Fitzer3 discovered that even solid bodies made of MoSi2 completely oxidized within a relatively short time when exposed to the air in the temperature range from 300° to 600°C. To describe this phenomenon he proposed the name "molybdenum disilicide 'pest' ", clearly analogous to the previously observed "tin plague" ("tin pest") which, however, arises as the result of a phase transformation. Studies performed by Fitzer and, in particular, one published recently by Berkowitz, Blackburn, and Fel-ten,' comprise the most extensive research to date on the pest phenomenon in MoSi2, as far as the fundamen- tal mechanism of the process is concerned. The first of these studies revealed the existence of a crystalline phase which appeared at the surface at 750°C and dissolved in the glassy silica layer at 1150°C. The logical assumption was that this phase was some reaction product of MOO3 and SiO2. The formation of a reaction product of this type seemed probable since it had been mentioned by Glemser and Lutz6 in a paper describing their studies of molybdenum oxides; however, this assumption was later disproved.8 It is our belief that information concerning the exact nature of this crystalline phase may be important for a better understanding of both pesting and the protection mechanism. Therefore, since the only available general description of the pest phenomenon was that of Fitzer, it was decided to reproduce his experiments. These experiments established that, in addition to the "pest" and "nonpest" temperature range, an intermediate region exists between 600" and approximately 650°C. This region is characterized by the appearance of a variable amount of yellow to orange colored crystals. The electron-beam microanalyzer was used to qualitatively determine their composition. Iron and molybdenum were found to be major constituents. This result can be explained based on the following facts: 1) iron, according to literature data,* is the most common impurity in molybdenum powder, and its content can be as high as 0.25 pct; 2) technical silicon powder usually contains iron; 3) steel ball mills are often used for the crushing and grinding of MoSi2. In order to clarify the exact role of iron, it was deliberately added to a stoichiometric mixture of molybdenum and silicon. The observed results corroborated the previous experiment, proving that iron (probably as some silicide phase) concentrates along the grain boundaries. I) EXPERIMENTAL PROCEDURE A) Oxidation of MoSi2 with Iron Additions. 1) Specimen Preparation. Specimens were prepared by both

Jan 1, 1967

By C. M. Wayman, R. Bullough

The rediffraction of Bragg diffracted beams by differently oriented regions (such as twins) of a crystal may give rise to "extra" reflections or reciprocal lattice points. These two papers are concerned with predicting these additional reflections which result from twin related regions of a lattice. Analysis is made for {111}fcc twins, (112)bcc twins, and {hkil}hcp twins. It is first required, knowing the specific variant of the twinning plane in each case, to predict the positions of the twin reflections relative to the matrix reciprocal lattice. Once this is done, the positions of the "extra" multiply diffracted reflections may be deduced. Part I is devoted to establishing "selection ru1es" for twinning, i.e., the necessary and sufficient conditions for the existence of twinned reciprocal lattice points. 1. INTRODUCTION. Transmission electron diffraction patterns are frequently complicated by multiply diffracted beams. Pashley and stowell1 have recently demonstrated that certain extra reflections in evapo- rated films of gold result from the rediffraction of matrix Bragg diffracted beams by (111) microtwins in the gold. It was previously (and erroneously) suggested 2,3 that observed "irrational" reflections in fine-grained gold were due to the presence of some hcp gold. A similar situation exists, apparently, for some bcc materials; fine (112) twins in bcc martensite in Fe-Ni alloys4 give rise to extra reflections. There are many other examples. The number of transmission electron microscopic investigations is continually increasing, and because of the importance of double (and multiple) diffraction in the interpretation of diffraction patterns, it was judged that a detailed elaboration of the principles involved is desirable, as well as the extension of these principles in reasonably closed form to other crystal structures, particularly bcc and hcp. The present analysis considers double diffraction caused by (111) twins in fcc metals, (112) twins in bcc metals, and {hkil} = {hkl) twins in hcp metals. For each case of twinning, the various possible (variants of) twins give rise to a set of interpenetrating reciprocal lattices. The relative spatial arrangements of these reciprocal lattices can be deduced (Part I) and are expressed in terms of simple "selection rules". The resulting sets of interpenetrating reciprocal lattices are then analyzed for possible doubly diffracted reflections (Part II). The notation used, and some important formulas are given in Appendices I and 11.

Jan 1, 1967

By C. M. Wayman, R. Bullough

The selection rules fir twinning in fcc, bcc, and hcp lattices as established in Part I are used to predict the positions, relative to the matrix (untwinned) reciprocal lattice, of reflections due to double diffraction from the twins. These doubly diffracted reciprocal lattice points, which often coincide with ordinary matrix reciprocal lattice points, are deduced from kinematical considerations. 1. INTRODUCTION. A Bragg diffracted beam under certain conditions may be rediffracted to produce a third beam i .e., the incident beam, the first diffracted beam, and the rediffracted beam). In such a case an initial incident beam is diffracted by a set of planes; the diffracted beam may then be rediffracted by a second set of crystallographically different planes. The initially diffracted beam acts as an incident beam for the second set of planes, thus resulting in a twice-diffracted beam. This twice-diffracted beam may be regarded as a singly diffracted beam from a set of lattice planes whose structure factor is zero. In order to find the reciprocal lattice point corresponding to the doubly diffracted beam, it is customary1,2 to combine vectorially the component reciprocal lattice vectors which head to the extra reflections. For example, hcp metals may exhibit the forbidden (0001) reflections.* As Fig. 1 shows, the (0001) reciprocal lattice point results from: (1010) + (1011) = (0001) Similarly, combination of the beams (1011) and (1010) gives rise to: (1011)- (1010) = (0001) As Pashley and stowell2 have pointed out, even if in fact the double diffraction points lie on the Ewald sphere, they may not actually represent observed doubly diffracted beams because the initially diffracted primary beam, i.e., the source, must also correspond to a reciprocal lattice point which lies on the sphere of reflection; however, the reciprocal lattice point corresponding to the planes causing the rediffraction need not lie on the sphere. A little consideration of the Ewald construction in Fig. 2 makes this argument clear. In Fig. 2 the incident beam is represented by the wave vector ko. This beam is initially diffracted by the lattice planes (hkl) which are represented by the reciprocal lattice vector r(hk1) The reciprocal lattice point (hkl) of course lies on the Ewald sphere in order that the Bragg condition be satisfied. The initially diffracted beam is represented by the wave vector kl. If now kl is rediffracted by a second set of planes (h'k'l') resulting in k2 the lattice point (h"k"l") must lie on the Ewald sphere if the double diffracted beam k2 is to be observed. It is clear that (h"k"l") is the vector sum of (hkl) and (h'k'l'), and that (h'k'l') need not in fact lie on the Ewald sphere. In the usual1,2 analysis the origin (000) of the reciprocal lattice is shifted to the point (hkl). However the translation (000)— (hkl) automatically shifts the point (h'k'l') to the Ewald sphere, i.e., (h'k'l')— (h"k"1"). It is to be seen that (hkl), the source reflection, must lie on the Ewald sphere; if it does not the translation (000) — (hkl) places the "new" origin off the sphere, not satisfying the Ewald construction and hence the Bragg condition. The point (h"k"1") of course must lie on the sphere if it corresponds to an observed doubly diffracted beam. It is to be noted that crystals having the hcp structure, as just discussed, are intrinsically capable (i.e., without lattice defects such as twins) of double diffraction, as contrasted to fcc and bcc crystals which are extrinsically capable (requiring lattice defects or reoriented lattice regions). The "allowed" bcc reciprocal lattice points (which comprise an fcc lattice) are (110), (2001, (211), (220), (310), (2221, (321), (4001, and so forth. The combination

Jan 1, 1967

By S. Feuerstein, L. Rice

The effect of low pressures on the flow and fracture behavior of molybdenum is described. For poly crystalline samples, room-temperature tensile tests indicate greater ductility under 10 Torr than under intermediate pressures up to and including atmospheric pressure (760 Torr). In addition, tests conducted at 760 Torr under atmospheres of air, dry nitrogen, and purified argon exhibited no apparent difference in mechanical properties. Critical tests involving baking in situ as well as those involving single-crystal deformation further imply that the ductility effect is a pressure-dependent phenomenon related only to the fracture process. This dependency is discussed in terms of adsorption and diffusion contributions. THE effect of very low pressures on material properties has heretofore been presumed to be important only for substances possessing relatively high vapor pressures at ambient temperatures. Research has therefore been concentrated primarily on organic solids and liquids, and in some instances on metals such as zinc and cadmium. Most vacuum-effect studies' on the mechanical behavior of metals have been performed under conditions of either cyclic loading or creep rupture at elevated temperatures, i.e., over extended time periods. These studies were not restricted to high vapor pressure materials but also encompassed such metals as gold, copper, and nickel. Very little concern, however, was placed upon the importance of a vacuum environment on the mechanical behavior of metals subjected to a simple unidirectional deformation at ambient temperatures. A tension test is generally of short duration as compared to a creep test, and at room temperature vacuum effects if any would be expected to be surface-limited. In early 1963, Kramer and podlaseck2 reported a change in the bulk flow behavior of aluminum single crystals during room-temperature tension tests. The deformations were performed under pressure conditions of 760 to 3.4 X 10-8 Torr and indicated for the first time a vacuum surface effect contributing to the bulk tensile behavior of metal specimens. As a consequence, an experimental program was initiated in this Laboratory to study the effects of ultrahigh-vacuum conditions on the mechanical behavior of metals. The results of a preliminary study on poly-crystalline molybdenum3 revealed, unlike Kramer's observations of changes in the stress-strain behavior, only an increased ductility under ultrahigh vacuum. Flow behaviors were nearly identical for all tests re- gardless of pressure. This paper presents comprehensive results obtained in this area of research. 1) EXPERIMENTAL PROCEDURE Three material categories were used in this study: sintered and are-cast polycrystalline molybdenum of nominal purity 99.93+ pct and single-pass electron-beam zone-refined molybdenum single crystals having a nominal purity level of 99.99+ pct. The interstitial levels (weight percent) as determined by the Materials Testing Laboratories, Division of Magnaflux Corp., were as follows: sintered molybdenum (C— 0.005, H—0.0004, O—0.015, N—0.008); and arc-cast molybdenum (C-0.0038, H-0.0003, O-0.015, N-0.023). Single-crystal molybdenum obtained from Materials Research Corp. had a typical interstitial analysis of C-0.0015, H-0.00007, O—0.00045, and N-0.0001. Tensile specimens having a 5 mm diam by 50.8 mm length were prepared from these materials. An average grain diameter of 0.059 mm was obtained for the sintered specimens following a 4-hr, 1600°C heat treatment. Grain sizes from 0.019 to 0.149 mm were obtained in the arc-cast specimens following heat treatments from 1100° to 1600°C for 1 hr. This series of specimens was used exclusively for the grain-size effect studies. All samples were electrolytically polished in 97 pct sulfuric acid solution prior to testing. Experiments were performed at room temperature in an ion-pumped ultrahigh-vacuum system positioned in an Instron tensile machine, Fig. 1. A constant strain rate of 4.2 x 10-4 sec-1 as derived from crosshead displacement was assumed for the deformations. Starting vacuums ranged from 2 to 0.5 X 10-10 Torr. These pressure measurements were made using corrected values4 of an NRC Redhead gage. Comparative readings were also made against a G.E. triggered dis-

Jan 1, 1967

By W. A. Backofen, D. Lee

The deformation of textured sheet of titanium and several of its all-a (hcp) alloys was investigated with two kinds of experiments: tension testing along different directions in the plane of the sheet, and combined-stress loading along the principal axes of anisotropy (the rolling and transverse directions). Texture and plastic anisotropy were evaluated with pole figures and by measurement, as a function of orientation, of the tensile transverse-strain ratio, or R parameter. The results as a whole can be rationalized qualitatively with the present understanding of deformation mechanisms in titanium. Quantitative agreement between the orientation dependence of tensile yield strength and the Predictions of continuum ANISOTROPY in the properties of engineering materials is more the rule than the exception because anisotropy in structure is so common, and the one generally follows the other. Two broad categories of structural anisotropy are represented by mechanical fibering and crystallographic texture. The former is important in many aspects of fracture.' The latter has more significance for yielding and plastic deformation, theory, using the R measurements, was relatively poor. However, in tension-tension quadrants of the yield-locus diagrams, the difference between theory and experiment was hardly more than 10 pct. The maximum texture-hardening effect was found in a 4Al-1/4O2 alloy to be nearly 50 pct. In the compression-compression quadrant, {1012} deformation twinning prevented the locus from expanding much beyond the Position predicted for isotropic material. With increasing temperature the trend in R was downwards, approaching unity (isotropy) near the a-transus temperature; an accompanying development was large amounts of neck-free extension. which are of special concern in this paper. The tendency has been to view crystallographic texture more as a liability or curio than as an asset. The prominent exception is found in silicon-ferrite sheet for power-transformer cores, which is processed to develop a new optimum texture for high electrical efficiency. Yet it should be possible to find other examples, involving other kinds of properties. More specifically, there is good analytical reason to expect improved combined-stress yielding resistance in suitably textured material,2,3 and it has now been shown by experiment that texture hardening or softening is a potentially useful phenomenon in certain engineering devices and processes.'-I To date, work has included measurements of the transverse (width to thickness) strain ratios in the

Jan 1, 1967

Jan 1, 1967

By N. A. D. Parlee, M. M. A. El-Naggar, G. 8. Horsley

The apparatus was of a modified Sieverts type1&apos;2 with a reaction tube designed to function also as the cell component of an oxygen pressure gage. The reaction tube assembly is shown in Fig. 1 and described in Table I. The main body is a 1-in.-OD 15 mol pct calcia-stabilized zirconia tube. The ground-glass joint, g, the male part of which carried a prism for optical pyrometer use, was connected to the remainder of the Sieverts apparatus. The calibration of the cell (at its 1000°K operating temperature) for internal oxygen pressures (PO2in) in the range 0.2 to 10 9 atm was made against internal air pressures measured by mercury manometer and McLeod gage. At very low po2in values down to l<Tn atm the performance was checked by comparing pQ calculated from electromotive force measurement when the apparatus was filled with a) pure CO gas and b) a CO-CO2 mixture of the ratio CO-CO2 = 1:0.398, with Po, values calculated from the equilibrium constants of the following reactions at 1000°K:

Jan 1, 1968

By Akira Yazawa, Alžbeta Gubcova

RECENT lead-smelting techniques have tended toward use of high-grade concentrates with minimum amounts of flu, accompanied by profitable employment of roast reaction.1-5 In order to better understand these smelting processes, thermodynamical calculations have been carried out on the Pb-S-0 system, and the results obtained have been presented in isothermal reaction diagrams in which log Ps, and logPo, were the axes. The diagram thus constructed seems to be more convenient to grasp the equilibrium aspect than those published hitherto.6-8

Jan 1, 1968

By R. C. Hall

We are pleased to confirm some of the mechanical data presented by Dr. Detert on the 18 pct Ni marag-ing steel.15 Bar 3 in. in diam and containing 0.02 wt pct C, 18.5 Ni, 8.9 Co, 5.1 MO, 0.55 Ti, 0.05 Al, and balance iron has been examined in our laboratory. Cylinders 0.5 in. high and 0.4 to 0.5 in. in diam were cold-compressed from 3 to 40 pct reduction in height. Table VI shows some typical data; deformation in-

Jan 1, 1968

By J. Weertman

The paper of Gifkins and Snowden considers the interesting but difficult problem of determining the stress dependence of secondary (steady-state) creep at low stresses. These authors have concluded that at stresses below 250 psi (2 x 107 dynes per sq cm) the secondary creep rate of lead is proportional to the stress (viscous creep) and is not proportional to the stress raised to about a fifth power. The experimental data considered by them were obtained on tests conducted at room temperature and at 50°C. The lowest stress employed was 50 psi (3.5 X 106 dynes per sq cm). The authors pointed out the main difficulty in determining the stress dependence of creep at low stresses. The creep tests must be run for very long lengths of time. However they made no estimates of when an experimental creep rate determination must be rejected because it does not represent a true steady-state or minimum creep rate. In order to be certain that a creep curve is within the steady-state region, the total creep strain should be of the order of 0.1 to 0.2. For a creep test of a year&apos;s duration this requirement implies that a secondary creep rate smaller than about 10-3 per hr cannot be measured reliably. The corresponding creep rate for a 10-year test is 10-6 per hr. The creep rates of the tests that were considered by the authors to prove the existence of viscous creep were of the order of or less than 10-6 per hr. One can conclude reasonably that this data does not prove unambiguously that large strain steady-state creep rate of lead is proportional to the stress in the stress range of 50 to 250 psi (3.5 x 106 to 2 X 107 dynes per sq cm). Another technique can be used to obtain the stress dependence at low stress levels. The creep rate is a very sensitive function of temperature. The creep rate can be increased by very large amounts merely by increasing the temperature. We carried out steady-state creep tests on lead single crystals25 at temperatures up to 320°C. We were able to obtain creep rate data down to stresses as low as 35 psi (2.5 x 10&apos; dynes per sq cm). Our smallest creep rate was 8 x 10-5 per hr. Thus we obtained large strain, steady-state creep rates to even lower stresses than were considered by Gifkins and Snowden. No evidence was seen for viscous creep. The creep rate was proportional to the stress raised to about a 4.5 power down to the lowest stresses. Since there is no reason to believe that changing the temperature should change the stress dependence of steady-state creep, we feel that large strain viscous creep does not occur in the stress range quoted by the authors for lead single crystals or large-grain polycrystalline samples of lead. This conclusion does not imply that viscous creep may nat occur in a lower stress range or in the same stress range for fine grain material or at creep strains very much smaller than 0.1. Support by the U.S. Office of Naval Research is acknowledged. Authors&apos; Reply R. C. Gifkins and K. U. Snowden We thank Dr. Weertman for his discussion and although, as we hope to show, we do not agree with his reservations, we do concur in stressing the importance of ensuring that creep rates are reliably obtained. Dr. Weertman appears to be content to accept n = 1 for low stresses with fine-grained material but not for single crystals. We believe our results show that the former result cannot be accepted without also accepting the latter. We will also show that the probable errors in our minimum creep rates are insufficient to alter our conclusions, that the criterion proposed by Dr. Weertman is arbitrarily restrictive and his alternative experimental approach possibly invalid. 1) A principal result of our Fig. 1(a) is that n = 1 for polycrystalline specimens at room temperature and 50°C for stresses below -250 psi. There was evidence that crystal slip and grain boundary sliding contributed approximately equaily to the overall strain in this low-stress regime. This implies that either a) grain boundary sliding controls slip within the grains or b) both grain boundary sliding and crystal slip independently occur according to mechanisms which give n = 1. Alternative a does not seem acceptable, so we were forced to consider b. This led us to reexamine work on bicrystals by Strutt and Gifkins and plot curves Fig. l(b). Previously Strutt et al. (loc. cit.), had merged these points with others using the Zener-Holloman parameter and thus, we now believe, had been led to overlook the behavior where n = 1. Curves C and D in Fig. l(b) did appear to confirm the hypotheses that n = 1 for crystal slip at these low stresses and the sliding curve F was similarly of the expected form. It was comparatively easy to find a quantitative theory to account for n = 1 for sliding and the similarity of curves C and D to curve F (all obtained from the same set of specimens) led us to feel that the single-crystal curves were valid. 2) We believe the secondary creep rates for both the polycrystalline and single-crystal specimens to be in error by factors c2. In Fig. 6 creep curves for polycrystalline specimens of lead(1) and lead(II) are reproduced as curves a and b, respectively, and curve c is for a single crystal at 100 psi. It is clear that, although the attainment of secondary creep rate takes 2 years for a and 150 days for b, thereafter the curve is linear for periods of 7 and -1 year, respectively. The single crystal has a linear portion commencing after 20 and extending to 90 days. Creep extension was measured directly using a traveling microscope reading to 0.01 mm on gage lengths marked on the specimens; the gage lengths

Jan 1, 1968

By Ronald C. Koo

SMALL additions of potassium, aluminum, and silicon as oxides (referred to as dope) to tungsten have been known for several decades to have a very large effect in raising the recrystallization temperature and altering the recrystallized grain morphology of heavily drawn wire. Previous investigations of this doping effect1 6 have led to various speculations but all failed to deduce unequivocally the physical state or the mechanistic influence of the dopant. Recently, walter7 has observed, by transmission electron microscopy, strings of "fine particles" in heavily rolled and annealed doped tungsten sheet and concluded that they were particles of mullite (Al6Si2013). His conclusion was inferred from the electron diffraction patterns of large particles ex-trated by carbon replication of fractured surfaces of slabs rolled from sintered ingots. That the strings of "fine particles" in heavily rolled and annealed sheet were also mullite was an assumption for which no evidence was presented. A similar investigation has been carried out in this laboratory over the past 2 years on a variety of tungsten wire: doped tungsten, and undoped tungsten, as well as 218 doped tungsten purchased from the Lamp Metals and Components Department of the G.E. Lamp Division. Although the electron microscope observations are similar to those reported by Walter, the writer has reached a different conclusion concerning the physical state of the dopant in annealed tungsten. The purpose of this communication is to present evidence that the strings of "fine particles" observed in transmission specimens are not mullite, but are voids. In the present investigation, tungsten wire, 0.88 mm in diam, was rolled into ribbon 0.2 mm by 125 µ thick. The ribbons were annealed in vacuo at a pressure of -1 x 10-5 Torr and then thinned electrolytically in a 2 pct KOH solution. Fig. 1 shows a typical transmissicjn electron micrograph of a sample annealed at 1700°C for 30 min which reveals rows of closely spaced voids having a light contrast (referred to as "fine particles" by Walter) aligned parallel to the working direction. Stereo micrographs (by D. Moon, Westinghouse Research and Development Center) have shown that these voids do not exist on the surfaces of the specimens as a result of thinning but are within the thin-foil specimens. The following experiments have been performed to verify that these are indeed voids. I) Effect of Annealing. Voids are absent in unannealed specimens and appear only after annealing. This behavior cannot be explained if they were solid particles such as mullite. Precipitation (in an unquenched specimen) upon annealing requires solute elements having decreasing solubilities with increasing temperature. Although the solubility of aluminum in tungsten does decrease with increasing temperature, precipitation requires a concentration in excess of 1.4 wt pct,8 which is at least two orders of magnitude higher than the aluminum content in doped tungsten. It is also unreasonable to assume that particles aligned in rows initially present in unannealed specimens were too

Jan 1, 1968

By V. K. Grotzky, F. J. Fraikor

A number of investigators have noted the importance of various precipitation reactions on the properties of commercial-purity beryllium.1-5 Carrabine, for example, has demonstrated the interaction of iron and aluminum on the mechanical properties of hot-pressed polycrystalline beryllium.6 He considered the determining factor on elevated-temperature properties to be a reversible AlFeBe, precipitation reaction which could be directly related to the Fe/Al impurity ratio of the beryllium. Any aluminum in excess of the stoichio-metric amount required to form A1FeBe4 was presumed to remain primarily in the grain boundaries. We have observed, by transmission electron microscopy, such a grain boundary effect after various heat treatments of beryllium sheet. The starting material in this investigation was bare-rolled beryllium ingot sheet (0.001 to 0.005 in. thick), in contrast to the hot-pressed powder utilized by Carra-bine. It should be noted from the ingot sheet analysis shown in Table I that the Fe/Al weight ratio was near unity which would provide some free aluminum although the total aluminum and iron content was still small. Fig. l(a) shows some aluminum or aluminum-rich precipitates in the grain boundaries of a beryllium foil which had been quenched from 1200°C into brine at -TPC. Similar grain boundary precipitates were found, particularly at grain boundary intersections, in other samples quenched from 1100° and 1000°C. The length of annealing time at these elevated temperatures did not appear to substantially alter the amount of grain boundary precipitates, thus attesting to their relative insolubility. No matrix precipitates were observed other than the normal BeO and Be2C inclusions. A microprobe analysis of the larger precipitates at

Jan 1, 1968

By W. A. Nordland

BISMUTH can be readily grown into single-crystal form using the so-called "quick freeze" growth method.&apos; Some advantages of this method are that very large crystals can be grown in a relatively short time, and with comparatively simple apparatus. We have found the general quality of crystals grown by this method to be not as good as that of "pulled" crystals.&apos; This communication describes a "quick-freeze"

Jan 1, 1968

By J. Warner, M. J. Marcinkowski, B. Cullen, T. Prevender, J. Mcllwain, T. Carnahan, J. Pahlman, J. Demel, J. Munford

The following analysis was an outgrowth of a midterm examination given by one of the authors (M.J.M) in a course entitled Metallurgy 541 "Applications of Dislocation Theory&apos;&apos; at Iowa State University. Fig, l(a) shows the three-layer sequence of atoms lying in the (111) plane which characterizes the fully ordered AB3 fcc crystal, i.e., LI2 type. If any two-layer sequence of close-packed planes is constructed from Fig. 16)&apos; the structure would be hcp of the DO,, type. Consider for convenience that the circled atoms lie in the plane of the drawing while those shown square and triangular lie immediately above and below the plane of the drawing, respectively. It has already been shown&apos; that if a Shockley partial dislocation is passed over the plane of the paper, then the square atoms in Fig. 1(a) are displaced from their original positions as shown by the arrows in Fig. l(b). Not only is an intrinsic fault produced but the crystal is simultaneously disordered across the slip plane. In particular, 2AB bonds are converted to 1AA and 1BB bonds when referred to the area outlined by the solid line in Fig. 1. If, on the other hand, a Shockley partial is allowed to pass immediately above and immediately below the plane of the paper so as to displace the atoms in opposite directions as shown in Fig. l(c), an extrinsic fault is producedZ and twice the amount of disorder is introduced into the crystal as compared to the dislocation-produced intrinsic fault, if only broken first-neighbor bonds are counted. If an intrinsic stacking fault is produced by removing a close-packed plane of atoms in Fig. l(a) and displacing the two adjacent planes by 1/3a0[111], no wrong nearest-neighbor bonds are produced. Similarly, if an extra half plane of atoms with the same arrangement as any of those shown in Fig. l(a) is inserted between any two planes in the same figure, then an extrinsic stacking fault is produced in which once again no wrong nearest-neighbor bonds are produced. The latter two faults are bounded by Frank partial dislocations. Since, at least in the alloy CU3AU,3 nearly all of the ordering energy resides in the first nearest-neighbor interactions, intrinsic and extrinsic stacking faults and associated APB&apos;s of the Frank type are expected to have significantly lower energy than those of the Shockley type in CusAu in particular and quite likely in L1, and DO19 type alloys in general. Also, because of the higher degree of disorder plus loop interaction

Jan 1, 1968

By R. DiBella, H. Biloni, G. F. Bolling

A study of the detailed relationship between solidification substructure and microsegregation in dilute tin alloys has been continued. New observations reveal that depressions form at the solid-liquid interface not only as an initial form of segregation but throughout the range of increasing constitutional supercooling. In order to show the importance of this node formation it proves convenient to make two simplifications. Although substructure changes continuously as constitutional- supercooling increases,&apos; the following discrete stages may be used for discussion: 1) the planar solid-liquid interface; 2) ordered nodes, or depressions at the interface;&apos; 3) two-dimensional or elongated cells;3 4) regular or hexagonal cells;4 5) distorted cells, or hexagonal cells with branches;4 6) dendrites. It is also convenient to ignore observations made near grain boundaries which interact with the cellular substructure.2-4 And, it should be clearly pointed out that all singular depressions at the solid-liquid interface will be called nodes. Heretofore, the term "node" has been used without clear justification to describe both the truly isolated depression and the junction of cell walls appearing in a later stage of segregation. This usage is continued because it seems proved by the observations. Standard systematic growth of tin crystals was undertaken over a broad range of constitutional supercooling using various added solutes. Except for one or two chance observations, this research failed to reveal any appreciable range of growth conditions over which a disordered array of isolated nodes exists. Even though &apos;some finite range of random instability must exist, it is now concluded that stage one passes very rapidly to stage two. Next, after confirming that stage two passes to stage three by the elongation of isolated nodes: a reexamina-tion of stages three, four, and five followed. Standard metallography showed that pockets of higher solute concentration (for ko < 1) became more numerous in cell walls the more severe the growth conditions. These high-concentration regions must arise from depressions; however, in stage three their segregation is not distinguishable from the segregation of the nodes which join cell walls together. It seems, therefore, that the presence of nodes is causal in the formation of new cell walls, and that the mechanism by which stage three passes to stage four is initiated by nodes. If a similar reasoning is followed, the separation of stage four from stage five appears to be just a convenience that has arisen from the decanted interface observations made in the past. The present observations again show that more severe growth conditions relate directly to an increase in the number of nodes in the hexagonal cell walls. These nodes apparently serve as the origin for lines of segregation extending within the body of a cell, and can thus be assumed to represent the earliest form of branching,* as shown here in Fig. 1. The examination of stage six involved decanted-interface structures as in Fig. 2, which are similar to those considered by Rutter and Chalmers,5 Plaskett and winegard,6 and Hellawell and Herbert,7 and where distinct protrusions are each surrounded by a depressed boundary. The corresponding microsegregation behind the interface, but not far enough behind to allow a smearing of the segregation because of diffusion,4 is shown in Fig. 3. Both the shape of the decanted interface and the segregation pattern behind it

Jan 1, 1968

By N. A. D. Parlee, E. M. Sacris

OXYGEN solubility in liquid silver has been well studied.1-6 It has been established that the solubility follows Sieverts&apos; law reasonably well5&apos;6 up to po2

Jan 1, 1968

By Olav Idelgeland

FROM indirect evidence point defects have been believed to influence the fatigue behavior of metals and alloys.1,2 Measurements of changes in resistivity made after cyclicstressing at low temperatures indicate that a very high density of defects is present, part of which may be removed by room-temperature annealing.3&apos;4 These results are consistent with the generation of a high number of point defects at low temperatures. Corresponding measurements made after room-temperature stressing did not show any recovery effects.3 This was attributed to a stabilization of the dislocation network after a few thousand cycles without generation of vacancies. In this laboratory resistance measurements of copper single crystals, shaped as normal fatigue specimens ,5 have been made with a Kelvin double bridge at room temperature during and after cyclic stressing at 80 cps by comparing with a dummy at a close and constant temperature. Temperature differences were measured to ±0.025°C with fine thermocouples taped onto the gage lengths. Potential leads were tin-soldered into small holes in the gage length to give stable values. Corrections for differences in temperature and changes in mean length of the specimen were made according to the formula:

Jan 1, 1968

By T. L. Berger, M. C. lnman, M. F. Rose

AFTER shock loading, mechanical twinning has been observed by several authors1-4 for a variety of fcc metals and alloys. It has been shown2,3 that low stacking fault energy materials deform primarily by the formation of mechanical twins and stacking faults during dynamic loading. Further, Inman, Murr, and Rose2 have shown that a correlation exists between the average hardness and the volume percent of mechanically twinned material in stainless steel. It has been observed in nickel&apos; that mechanical twins are produced during shock deformation if the peak pressure associated with the shock wave is greater than 350kbar. It is the purpose of this work to discuss shock-hardening mechanisms in nickel and to determine to what extent the initial condition influences the final response. The "flying plate technique" was used to generate planar shock waves with peak pressures as high as 710 kbar. The details of the technique5" have been discussed elsewhere and will not be repeated here. The material used in this study was polycrystalline nickel of 99.98 pct purity and had an initial grain size of 0.18 mm. Prior to any deformation, all samples were given a stress-relief anneal of 6 hr at 600°C in a vacuum furnace. After annealing, the initial condition of the samples was changed by cold rolling individual samples from 0 pct to a maximum of 80 pct reduction in thickness. This provided samples with controlled initial histories for shock deformation. Immediately after shock loading, the specimens were slowed and quenched by suitable arrangement of buffer material and water bath. This technique minimized specimen damage and the effects of shock heating on the samples. Since deformation twins in high stacking fault energy fcc metals are only produced at high stress levels, the initial defect configuration prior to mechanical twinning should greatly influence the number of twins formed. In fact, Zukas and Fowler7 have found that prestraining in iron and steel greatly suppresses the formation of mechanical twins during the shock deformation process. Following the methods of Warren and warekois8 and Cohen and Wagner,9 X-ray diffraction profile analysis was performed to determine the incidence of stacking faults and mechanical twins in the deformed nickel. Analysis was made on samples in the annealed, cold-rolled, shock-loaded, and cold-rolled—shock-loaded states. The estimated accuracy of the peak position measurements is *0.01 deg in 2?. Therefore the accuracy in the measurement of the relative peak shifts between the (400) and (222) diffraction line profiles is on the order of *0.04 deg in 2?. None of our measurements indicated peak shifts greater than 0.04 in 28. This would correspond to a fault density of -1 pct and sets the limit on the sensitivity of our instrument. Similarly, analysis of the shift in the center of gravity of the diffraction line profiles yields the minimum measurable value of the twin fault probabilitya to be -0.002. Fig. 1 shows mechanical twinning in nickel shock-loaded to 400 kbar. In this photograph, fault intersections are clearly visible. The thickness of the individual fault lamellae was determined from the image widths of their lines of intersections by the

Jan 1, 1968

By N. A. D. Parlee

THE gas-liquid metal diffusion cell technique1-3 has been used to study the diffusion of nitrogen in Fe-C alloys. The actual apparatus and technique were the same as employed by the authors to study the diffusion of hydrogen in liquid iron.&apos; The diffusion cell&apos; was formed by immersing an alumina tube in a stagnant melt contained in an alumina crucible. The tube (hereafter called absorption tube) contained nitrogen gas at 1 atm and was connected to a sensitive gas-measuring system. The change in the average concentration of nitrogen in the melt in the absorption tube was determined by measuring the rate of absorption of nitrogen in the diffusion cell. Eq. [I], 1-3 derived from the appropriate solution of Fick&apos;s second law, was used to examine the data and to calculate chemical diffusion coefficients (D) in situations where the absorption appeared to be controlled by diffusion in the liquid: where V is the stp volume in cu cm, d is the diffusion cell diameter in cm, p, is the density of the melt in g per cu cm, pg is the stp density of nitrogen in g per cu cm, C, is expressed in wt pct, D is in sq cm per sec, and t is in min. According to Eq. [I], a plot of v vs vt should yield a straight line passing through the origin if absorption is controlled by diffusion in the liquid. The slope of this line could be used to determine the value of D under appropriate conditions. As discussed in earlier reports,1,2 the initial thermal expansion of the gas upon immersing the absorption tube distorts the line in the initial stages of a diffusion experiment. However, this is not a serious problem since the slope of V vs 6 plots can be determined from the data points obtained after the initial expansion ceases. The volumes reported on the data plot presented here represent absorption after this thermal expansion ceased. Several preliminary diffusion experiments were attempted with melts of pure iron and with Fe-C alloys containing up to 0.6 pct C. In these cases, no or very little absorption was observed. The only data obtained were for an Fe-C melt which was in addition thoroughly deoxidized by successive hydrogen and vacuum-degassing treatments. These treatments introduced an appreciable amount of aluminum into the melt and reduced its omgen content. The original charge material for this melt contained 0.23 pct s and approximately 0.001 pct &. After repeated hydrogen and vacuum-degassing treatments two diffusion experiments were performed. The analysis of the melt

Jan 1, 1968