By Bowen Li

Andalusite is an excellent raw material for refractory applications due to its high aluminum oxide content and phase transformation to mullite at high temperature. Granular andalusite in particle sizes of about 1 to 2 mm was traditionally utilized for the manufacturing of refractory brick. However, if powder andalusite in micron particle size is utilized in high-alumina refractory products, reinforcement on the refractory brick can be obtained and the sintering temperature can be decreased. The phase transformation of powder andalusite plays a key role for the difference.

Jan 1, 2006

By Wang Zhi

High-Mg-content concentrates are usually treated in Jinchuan flash smelting Furnace. Because the viscosities of high-Mg-content slag is very high, the operation of flash smelting becomes very difficult. To solve this problem, the viscosities of the semi-synthesized FeO-MgO-SiO2 slag of different compositions were measured. The results showed that when in the slag the weight percentage of MgO [w(MgO)] is 6-10%, the ratio of the weight percentage of iron to that of Si02, w(Fe)/w(Si02) is 1.1-1.4 and the temperatures are within 1473-1773K, the slag viscosities increased with the increase of W(MgO) and w(Fe)/w(SiO,). When w(Mgo)<6%, the smelting temperature should be controlled at I 300°C in order to to keep the smooth operation. When w(MgO)>10%, the temperature should be kept above I 633K. When the content of MgO is higher, a lower viscosity slag can be produced by decreasing the ratio of w(Fe)/w(SiO,). The appropriate ratio of w(Fe)/w(SiO,) for Jinchuan flash smelting furnace is about 1.2.

Jan 1, 2003

By Torben Edens

Norddeutsche Affinerie?s (NA?s) primary smelter continually increased production in the past decade. The smelter?s concentrate capacity was expanded from 500,000 in 1993 to 1,000,000 t/a dry concentrate in 2000 and the goal of the present upgrade is 1,150,000 t/a. These goals were reached without erecting new equipment in the anode area, but instead by refitting the existing plant. The life-span extension of the casting moulds was absolutely necessary to increase the casting performance from 260,000 to 450,000 t anodes per year on a single casting wheel. Different mould manufacturing processes and alloys were tested in order to find the optimal mould. In the past the moulds were cast directly, now the anode mould is milled into NA copper cakes. Accompanying measures taken were the shortening of maintenance and repair times as well as improvements in the refining furnace equipment.

Jan 1, 2005

By Shenghui Guo, Ying Lei, Wei Li, Jinhui Peng, Libo Zhang, Yu Li

"Abstract: In this work, low temperature carbothermic reduction of Panzhihua low grade ilmenite after ball milling were investigated. The ball milling of ilmenite and graphite were processed in a ball mill. The milling process can attenuate the particle of ilmenite, and the ilmenite characteristic peak were broadened and weakened. The reduction temperature and behaviors are studied on the thermo gravimetric apparatus; lower temperature and higher reaction rate were obtained for the reduction of ilmenite with graphite after milled. The reduction temperature and times of ilmenite decreased to 1000-1025°C and 40-60min via milled for 4 or 8h; Low down the reduction temperature can eliminate the solution of Mg2+ and FeTi03 in a certain degree; the reduced ilmenite has an obvious loose structure, can favored the subsequent procedure such as leaching.1 IntroductionThere is about 9.66 billion tons of Vanadic Titan-magnetite deposited in Panzhihua, China. In this reserve, there is about 8.73x108 t ofTi02, Accounting for 90.54% of the Chinese reserves, and 35.17% of the international reserves and ranking first in the world. [JJ Titanium mineral deposits major classified into Rock type and Placer type. Rock type is the igneous mineral, which have great content of FeO (Relative to Fe20 3) and gangue. The rock textures are compact and almost are complex ore. Rock type Titanium mineral major are ilmenite and titan magnetite ore, difficult to separate the metal ore and gangue. l.21 Thus, the Ti02 grade of Rock type ilmenite much lower than the Placer type (Table land 11). Panzhihua ilmenite are the typical Rock-type, due to the higher contents of MgO, CaO and Si02 and the complex mineralogy in ilmenite in Panzhihua region, making its direct reduction progressively more difficult. Mechanical activation, usually carried out by energetic milling or ball milling, was reported to significantly decreased the reduction temperature and accelerate the reaction rate of reduction of ilmenite with carbon, silicon and Magnesium. f3·(>J It reported that the process temperature were decreased to 600-1000°C and the annealing time were reduced to 30-120min after milled for 50-400 h. Shorter milling time involved was imported for else procedure such as direct leaching. 171 Hardly any research had referred to the carbothermic reduction reactivity of ilmeite milled for a short time as 1-1 Oh. In the present work, the aim is to investigate the reactivity and reaction temperature of carbothermic reduction of Panzhihua ilmenite. The Phase composition and micro morphology of samples are characterized."

Jan 1, 2011

By Xue Sun, Dengfu Chen, Yuting Chen, Mujun Long, Song Xu, Helin Fan

In order to seek an effective extraction process for vanadium, the recovery of vanadium from a high Ca/V ratio vanadium slag was studied by sodium roasting and ammonia leaching. In the present paper, the oxidation and leaching process of vanadium slag was investigated by X-ray diffraction (XRD), scanning electron microscopy and energy dispersive X-ray spectrometry (SEM/EDS) techniques. The effects of ammonium carbonate concentration, leaching temperature and leaching time on the leaching ratio of vanadium were discussed. As indicated in the experimental result, the optimal (NH4)2CO3 concentration was 120g/L, leaching temperature was 60°C and leaching time was 20 min. Approximately 92% of the vanadium was recovered under the optimal conditions. Furthermore, by means of X-ray diffraction analysis, the phase transformations of the vanadium slag during roasting and leaching processes were analyzed and discussed.

Jan 1, 2014

By Geoffrey S. Plumlee

The Summitville gold mine, located in southwestern Colorado, received tremendous publicity in the 1980&apos;s and 1990&apos;s for leaks of cyanide solutions from its heap leach facility. As is typical with cyanide spills, real time, geochemically rigorous assessments of the environmental effects were not performed. Past United States Geological Survey (USGS) research used simple mixing experiments to model the influx of alkaline cyanide heap leach solutions from Summitville into a nearby stream, whose waters were highly acidic due to severe acid-rock drainage (ARD) from the mine. These experiments indicated WAD cyanide rapidly degraded due to formation of Fe-Cu-CN solids and lesser HCN volatilization. The alkaline heap leach solutions also precipitated hydrous iron-and aluminum, oxides and hydroxysulfates (iron and aluminum &apos;supplied by the acid. rock drainage (ARD]), which then sorbed copper and other heavy metals from the ARD. These results indicate that mixing of cyanide heap leach solutions with ARD may be a cost-effective remedial method at mine sites where treatment of both is required. New experiments are currently in progress to further refine a potential remedial process.

Jan 1, 1998

By M. Bilal Khan

Thermal stress relief by means of a typical heat treatment cycle (660oC for one hr) is compared with the one achieved through vibratory stress relief at resonant and multiple resonant frequencies for the D-406 HSLA material. Our analysis of the data is based on the microhardness profiles measured for the entire length of scales, namely, base metal, heat affected zone (HAZ) and the weld bead itself. The profiles obtained using the two techniques mimic each other, for an equivalent 70% stress relief level. The data are further qualified by impact testing wherein the zone of interest is projected in the retention groove to provide impact by the pendulum striker in the Charpy mode. Higher equivalent energy absorption in the treated specimens confirms the efficacy of the vibratory method. The present work rectifies earlier anomaly where heat treatment has been reported at 310oC for the same material.

Jan 1, 2009

By Yoshinobu Fukumori, Testuya Watanabe, Futoshi Shikata, Hiroyuki Tokumitsu, Hideki Ichikawa, Masahito Miyamoto

Nano-particulate systems have attracted much attention recently in pharmaceutical field as drug carriers and functional components of pharmaceutical dosage forms. This paper describes our approaches in design and preparation of nano-particulate systems, including lipid nano-emulsions, chitosan nanoparticles and thermosensitive acrylic nanoparticles, for certain pharmaceutical applications mentioned below. The lipid nano-emulsions with their particle size smaller than 100 nm were prepared for gadolinium neutron-capture therapy (Gd-NCT) of cancer by a thin-film hydration method with sonication, and intraperitoneally injected into Greene's melanoma (melanotic No. 179)-bearing Syrian hamsters. This provided such a high gadolinium concentraton in tumor as 107 µg/g tumor (wet basis) at 48 h after administration. As an alternative gadolinium nano-carrier for Gd-NCT, biodegradable and highly gadopentetate-loaded chitosan nanoparticles (Gd-nanoCPs, 426 mTI in particle diameter and 9.3% in Gd content) were prepared by a novel emulsion-droplet coalescence technique. A significant tumor-killing effect could be obtained when Gd-nanoCP suspension was injected intratumorally twice 24 and 8 hours before neutron irradiation into B 16Fl O melanoma-bearing mice and subsequently thermalneutron was irradiated toward tumor site with a flux of 2 x 109 n/cm2/sec for 60 min. As one another application of nanoparticles, a novel acrylic composite latex with a hydrophobic core and a thermosenstively swellable shell was designed for fabricating microcapsules showing thermosensitive mode of drug release. The microcapsules with the composite latex-dispersing membranes exhibited an exceptionally rapid on-off response of drug-release in a thermosensitive manner.

Jan 1, 2000

By Y. W. Chung, W. I. Chia

"The interaction of water vapor with single crystal Ni3(Al,Ti) and polycrystalline Ni3Fe, with and without the presence of oxygen, has been studied with Auger electron spectroscopy, photoemission spectroscopy, thermal desorption and isotope exchange. Water dissociates to produce atomic hydrogen above 200 K on both Ni3(Al,Ti) and Ni3Fe surfaces. For Ni3(Al, Ti), the reaction is structure-sensitive. Pre-adsorbed or co-adsorbed oxygen on Ni3(Al,Ti) and Ni3Fe significantly suppresses hydrogen production due to water dissociation. This suppression process occurs more efficiently on Ni3Fe than Ni3(Al, Ti).IntroductionOrdered intermetallic compounds such as aluminides, silicides and titanides are very attractive for structural applications at high temperatures. This is because these intermetallics tend to form adherent oxides in oxidizing environments which protect the base materials from excessive oxidation and corrosion. In addition, they have low density, relatively high melting points and good high-temperature strength. However, the moisture in air severely embrittles many ordered intermetallics such as FeAl [1-3], Fe3A1 [4,5], C03Ti [6,7], (Co,Fe)) V [8], Ni3Si [9], Ni3(Si,Ti) [10], Ni3(AI,Mn) [Ill, and Ni3A1 [12-14], resulting in low 'ductility and brittle fracture at room temperature. Recent studies by Liu and coworkers (see review by George and Liu [15]) provide a qualitative description of the mechanism for this moisture-induced embrittlement. During elongation testing, cracks are formed, thus exposing fresh alloy surfaces. One or more active components of the alloy react with water vapor in the environment to produce atomic hydrogen which penetrates into crack tips and causes hydrogen embrittlement. This is similar to that proposed for moisture-induced embrittlement of aluminum alloys [16]."

Jan 1, 1996

The effect of rare earth element Y (0-2.0at.%) on the microstructure of TiAl alloys at the as cast and rapidly solidified conditions has been investigated. The results show that the addition of Y greatly refined the microstructure of TiAl alloys at both conditions. The refinement is more significantly with higher Y content. The refinement of Y in the cast alloys is attributed to that the strip-shaped Y-rich phase locating on the grain boundaries impedes the grain growth during solidification. In the rapidly solidified alloys, Y-rich phase dispersing uniformly as spherical particles in the matrix acts as heterogeneous nucleation sites which increases the nucleation rate of ??phase during the ????phase transformation, and produces a refined initial microstructure during solidification. Higher cooling rate restricts the grain growth during subsequent cooling.

Jan 1, 2010

By Hector Carreon

Due to elevated temperatures, excessive stresses and severed corrosion conditions, turbine engine components are subject to creep processes that limit the components life such as a turbine bucket. The failure mechanism of a turbine bucket is related primarily to creep and corrosion and secondarily to thermal fatigue. As a result, it is desirable to assess the current condition of such turbine component. By using eddy current images, it was shown that the eddy current technique could be used to monitor creep damage in a nickel base super-alloy. The eddy current results also show a significative variation in the electrical conductivity on the creep damage zone with respect to the background zone in nickel-base super-alloy samples. In addition, the absolute thermoelectric power coefficient show also a strong dependence associated with creep damage in nickel base super-alloy samples using a copper hot tip reference. The eddy current and thermoelectric power techniques seems to show promise as nondestructive evaluation tools for monitoring the level of creep damage in metallic alloys.

Jan 1, 2010

By Xuan Li

Aluminum slag is generated when aluminum metals are recycled through a smelting process in the presence of salt. There are small amounts of aluminum metals trapped in the aluminum slag. This research aims at evaluating the use of aluminum slag as an expansion agent for the production of lightweight concrete by taking advantage of the residual aluminum metals in the slag. The research identified key elements of producing lightweight concrete products through utilizing various mixture components including sodium hydroxide (NaOH), lime (CaO), cement, and gypsum. The volumetric expansion rate was investigated and the density and strength of the products were determined. The results show that aluminum slag can be utilized for the production of lightweight concrete products.

Jan 1, 2010

By NRMR Bhargava

With the increasing use of lead-free solder alloys, low melting point alloy is often required due to the heat- sensitive parts or substrates in modern electronic devices. For such demand of low melting point, the nanostructure lead- free solder alloy, having excellent metallurgical characteristics and a melting point of <215oC, were developed by mechanical attrition of conventional lead free solder alloys (Sn-Ag-Cu, Sn-Ag and Sn-Cu). The decrease in melting point due to nanosize effect was calculated theoretically as function of particle size and the theoretical results were compared with experimental values measured by differential scanning calorimetry. The newly developed alloys have eutectic composition of Sn-3.5Ag-0.7Cu, Sn-3.5Ag and Sn-0.7Cu and the melting point depression found to be 5.10C, 4.10C and 6.20C when the bulk alloys reduced to 80 nm, 92nm and 96nm sizes respectively.

Jan 1, 2009

By WU Jian-hui

Keywords: metallic material, precursor synthesis, precipitation, nickel, fibrillar powder The composition and morphology of the precursor of fibrillar nanocrystalline nickel powder prepared by oxalate precipitation are characterized by XRD,IR and SEM analysis, and the effects of temperature, nickel concentration, pH, surfactant and drying process on the morphology and the dispersion of the precursor are investigated. By the experiment results, the fibrillar precursor is a complicated nickel salt. The precursor prepared in the of 60~70°C,0.6~0.8 mol/L nickel ion, pH=8.4~8.6 and with addition of PVP surfactant is well dispersive and in fiber form. The powder dried by azeotropic distillation is dispersive.

Jan 1, 2005

By R. G. Reddy

Viscosities of alkaline metal oxide-silicate melts were estimated using our previously developed mathematical model. The structural based model considers depolymerization effects and related breakdown of the silicate network structure, on the addition of metal oxides to the melt. The developed expression: n =4.9x10 9 NO 0 T ½ exp(E/RT) poise was used to calculate the viscosities of various binary silicate systems such as, CaO-SiO,, MgO-SiO, and MnO-SiO,, as a function of temperature and composition. Excellent agreement was obtained between the calculated and experimentally determined viscosities.

Jan 1, 1991

By Merete Tangstad, Fei Li

This paper studies the quartz and carbon black pellets at elevated temperature with varying temperature and gas atmosphere. High-purity quartz and commercial ultra-pure carbon black was mixed (carbon content wt.15%), and then pelletized into particles of 1-3mm in diameter. The stoichiometric analysis of the pellet during heating is studied in thermogravimetric analysis (TGA) furnace at different temperature in CO and Ar atmosphere. The microstructure, phase changes and element content of sample before/after heating is characterized by X-ray diffraction, scanning electron microscope, X-ray fluorescence and LECO analyzer. The reaction process can be divided into two stages. Higher temperature and argon atmosphere are the positive parameters for SiC formation.

Jan 1, 2016

By Paul-Dominique Oudenne

For many years, CMI NESA has gained considerable experience in the field of alternative thermal processing processes by which useful by products result in addition to the destruction of the raw wastes. The CMI NESA pyrolysis process has been extensively applied to a wide range of sewage, industrial sludge and residues. This paper describes in details the development works carried out at the pilot stage as well as the key parameters of the process. Some of the industrial realisations are briefly described, the most recent one being the erection of a sludge pyrolyser on predried sludge at 90% dryness of a capacity of 100 tons of dry matter per day for the Valenton plant of the SIAAP (city of Paris).

Jan 1, 2006

By A. J. Sideris

It is known that Mg can act as a catalyst/solvent in the high pressure high temperature diamond synthesis. However, above pressure levels of the order of 7 GPa, and temperatures from 1700 ? 1800oC, it was not possible yet to use Mg for the industrial production of diamond. A possible alternative is the use of MgNi based alloys. However, owing to the great Mg reactivity, it was consider, so far, a difficult task to deal with such alloys. The present work presents successful results regarding the production of MgNi alloys, with different composition, at high pressure conditions. The behavior of the alloys and their microstructural characterization is analyzed.

Jan 1, 2006

By Hugo Cabrera-Real

This work investigated the chemical and mineralogical properties of CaO-SiO2-CrOx-CaF2- MgO slags. Synthetic slags were prepared and the effect of the slag basicity (CaO/SiO2) and MgO contents on the stability of the mineralogical species formed was analyzed. The morphology and composition of the slags were analyzed by XRD and SEM-EDS, whilst their chemical stability was evaluated by leaching with an aqueous acetic acid solution. It was found that in slags with CaO/SiO2 = 1, the main Cr-compound was MgCr2O4 spinel, which forms octahedron crystals. Small amounts of CaCr2O4 and CaCrO4 were also observed. It was found that increasing the slag basicity from 1 to 2 the compounds MgCr2O4 and CaCr2O4 were formed together with the Cr(V)-containing compound complex Ca5(CrO4)3F which forms hexagonal crystals. The results showed that the highest chromium concentration levels in the leaching liquors corresponded to slags with CaO/SiO2 = 2, probably owing to the formation of Ca5(CrO4)3F.

Jan 1, 2010

By D. M. Dabbs

A static dew point technique has been used to evaluate the solubility of arsenic in ?slag and its dependency on P02 at temperatures of 1458 and 1523K. The ferrous-ferric ion ratio of the slags ranged from 3.9 to 23.8. These values correspond to partial pressures of 02 ranging from 10-8 to 10-12 atm. The solubility of arsenic in slag was found to be independent of? P02? The data indicate that elemental arsenic exists in silicate ?slags. This result was further substantiated by mass .spectrometric analysis of doped slag specimens.

Jan 1, 1983