Stabilization of Chromium-based Slags with MgO

This work investigated the chemical and mineralogical properties of CaO-SiO2-CrOx-CaF2- MgO slags. Synthetic slags were prepared and the effect of the slag basicity (CaO/SiO2) and MgO contents on the stability of the mineralogical species formed was analyzed. The morphology and composition of the slags were analyzed by XRD and SEM-EDS, whilst their chemical stability was evaluated by leaching with an aqueous acetic acid solution. It was found that in slags with CaO/SiO2 = 1, the main Cr-compound was MgCr2O4 spinel, which forms octahedron crystals. Small amounts of CaCr2O4 and CaCrO4 were also observed. It was found that increasing the slag basicity from 1 to 2 the compounds MgCr2O4 and CaCr2O4 were formed together with the Cr(V)-containing compound complex Ca5(CrO4)3F which forms hexagonal crystals. The results showed that the highest chromium concentration levels in the leaching liquors corresponded to slags with CaO/SiO2 = 2, probably owing to the formation of Ca5(CrO4)3F.