By R. E. Head

Under existing economic conditions, the treatment of gold ores occupies an outstanding position in metallurgical activity. The increased price of gold has automatically brought about a reclassification of old dumps and low-grade orebodies, and many that formerly were considered valueless are now being vigorously investigated and worked. This situation has developed problems that have taxed the ingenuity and ability of metallurgists to the utmost. Some gold ores give a high extraction of gold by standardized methods of treatment; other ores of apparently similar character yield but a relatively small percentage of their gold when treated by the same processes. Surface Contamination The experience gained by microscopic study of numerous gold ores and tailings has shown that there are pronounced differences in the physical characteristics of the minerals composing them, more especially of the gold. Repeated studies of tailings from flotation and cyanidation of gold ores has established the fact that surface contaminations on gold particles are often directly responsible for high gold losses; comparison of gold particles isolated from flotation concentrates and the resulting tailings have showed that the clean gold has been recovered and the tarnished or contaminated gold invariably lost in the tailing. Obviously, it is not possible to make such a comparison of gold ores treated by cyanidation, as the clean gold has been taken into solution; but when the gold found in cyanide tailing has a tarnished or coated surface, one may infer, with a reasonable degree of certainty, that the clean gold has been extracted. This premise is supported by experimental evidence obtained by isolating particles of tarnished gold and exposing them to cyanide solution in small parting cups. In one such experiment, tarnished gold particles picked from a cyanide tailing showed but slight evidence 01 dissolving at the end of 27 days. In this test, a cyanide solution of 1.6 11). per ton was used and the leach solution was decanted arid renewed every

Jan 1, 1939

By D. E. Swets, R. C. Frank

It is well known that hydrogen is introduced into iron or steel as a result of many chemical processes (acid pickling, electrolytic cleaning, plating, etc.). One of the reactions that has been of recent interest1 is the reaction between an iron surface and water vapor. It was shown a few years ago2-4 that hydrogen can be introduced into steel at an accelerated rate during abrasion as a result of this reaction. Grun-berg and Scott have also observed that water in mineral oil lubricants increases pitting failure in ball bearings5 and they have suggested that hydrogen from the water is the primary cause of this effect.' In this laboratory, the question was raised as to whether or not hydrogen is also introduced into the metal surface of a bearing as a result of the decomposition of the hydrocarbon lubricant itself, and an experiment was performed to try to find a satisfactory answer. All steel parts contain some residual hydrogen. Therefore, it appeared that the best way to carry out this experiment without the need for highly accurate quantitative analyses was to use deuterium as a tracer. The natural abundance of deuterium in H2 is only 0.015 pct. The tracer was obtained in the form of deuteroparaffin (CD,(CDJ, CD,) and 0.25 g were dissolved in 20 cc of mineral oil to form the lubricant to be used in the tests. The bearings used were New Departure Type QOLOO ball bearings with a ball diam of 0.187 in. Prior to adding the mineral oil-deuteroparaffin lubricant, the bearings were cleaned in warm trichloroethylene to remove the packing grease. After packing with the new deuterated lubricant, the bearings were operated in a bearing fatigue test machine under a radial load of 190 lb and a thrust load of 190 lb at a speed of 3800 rpm. The expected life under these conditions is about 500 hr. Two tests were made; one for a period of 27 hr and the other for a period of 102 hr. The bearings achieved a temperature of 120o F during the tests. When the tests were stopped the balls were mechanically removed from the bearings and were immediately placed in liquid nitrogen to reduce degassing until the analysis for deuterium could be made. Before analyzing, the balls were warmed to room temperature and scrubbed with several degreasing agents to remove all traces of the deuteroparaffin mixture. This cleaning procedure was shown to be satisfactory by running a control test in which one ball bearing was subjected to all parts of the test except running in the fatigue machine. The hydrogen and deuterium were removed from the balls using a hot extraction apparatus attached to a mass spectrometer. Four balls from each bearing were analyzed. Each one was analyzed separately by removing it from a cold storage volume of the hot extraction apparatus and transferring it to the oven tube with a magnet. As the gases were evolved they were analyzed with the mass spectrometer. Since the hydrogen and deuterium pass through steel in the atomic form and since there are many more hydrogen atoms than deuterium atoms in the sample, the probability of forming an HD molecule is greater than forming a D2 molecule. For this reason the evolution of HD and H was followed as each ball was placed in the oven. The results showed that as each ball from the test bearing was dropped into the oven, the mass spectrometer recording of the HD evolution increased by about ten divisions. When balls from the control test bearing were dropped into the oven, the increase was about one division or less. The hydrocarbon background in the mass spectrometer was also monitored to see if hydrocarbons or deuterocarbons were given off when the balls were dropped into the oven, but no change in the hydrocarbon peaks was observed. Since the balls contained a fair amount of residual hydrogen, isotope ratio measurements were made on the gas obtained from each ball. The D/H value found for those balls which had been operated in the fatigue testing machine was consistently about 0.3

Jan 1, 1962

By William B. Phillips

The possible sources of potash salts in the United States have been considered from many points of view during the last several years, but it is only within the last two or three months that the situation has become acute. We import from Germany, the only sourcc of large supply, more than $10,000,000 worth of potash salts annually, and this business has been badly crippled by the European war. If there was ever a time in our industrial existence when the necessity of providing for our own needs was more acute than it is now, we are not aware of it. One has only to study the price lists of chemicals sent out by the large supply houses to see the change wrought within a very short time. Whether or not these prices are to maintain for a considerable time, no one can say; but it appears to be probable that we shall not see prices materially lower for a period of uncomfortable length, to say the least. It is not my purpose at this time to discuss the various sources of supply of potash salts that have been suggested or recommended. Some of them might afford a pleasing relief but all of them combined would not affect the situation seriously. If we are to have our own sources of potash salts, they will have to compare, in some efficient manner, with the sources upon which we have drawn during the last 20 or 30 years; i.e., they must exist in minable quantities. It seems to me to be quite idle to speculate upon our domestic sources of potash if those sources are not of a character similar to those upon which we have so long depended. A few thousand or, perhaps, a few hundred thousand dollars' worth of chemically derived potash may be produced under the stress of present conditions, but when we consider that each year demands more than $10,000,000 worth, we must look to underground sources; we must look to mines similar to the famous Stassfurt and Halle deposits. If we cannot mine potash salts, we shall have to do without them for a while.

Jan 1, 1915

By J. L. Gillson

Historically, rock deposits and sand deposits of titanium minerals came into production about the same time, although there may be some argument as to what is meant by production. Beach de- posits of heavy minerals in India (Figs. 1-4) and Brazil (Figs. 5) were worked for monazite about the turn of century, but as there was then no market for titanium minerals, these were thrown away. The rock rutile deposits at Roseland, Va., Fig. 6, were worked to supply rutile for titanium chemicals and for coloring ceramics long before there was a titanium pigment business. The pigment industry started about the middle twenties, both in Europe and the U. S., and almost simultaneously the rock deposits at Ponte Vedra Beach near Jacksonville, Fla., were worked for titanium content. Since those days, production from both types of deposits has continued to grow at a rapid rate; many deposits of both types have been found, and reserves have grown to very large figures. In total tonnage of reserves, there is no doubt that the rock deposits are far ahead of the sand deposits; nevertheless there is a very large tonnage of commercial sands available. It is the quality of titanium mineral in the sand and the relatively lower costs of operating sand deposits that have kept them abreast, at least in annual tonnage produced, with the rock deposits.

Jan 4, 1959

By Werner Joseph, Richard R. Knobler

When the first batch of refined copper ingots was cast at Mantos Blancos in January 1961, eight years of exploration, development and metallurgical pioneering by Mauricio Hochschild & Co. had come to a successful conclusion. This Chilean copper deposit, located in the Atacama Desert 30 miles from Antofagasta, is now producing approximately 20,000 tons of copper per year. The Mantos Blancos deposit has been known since 1912 and various attempts had been made to work the high-grade zones before the present operation was started. The major drawback of the ore to any previous development was its chloride content which varies between 0.4% and 1.5% C1. Although the chloride ruled out the conventional leaching-electrolysis scheme, it did lend itself to the process of precipitating the copper as cuprous chloride.

Jan 1, 1962

By GEORGE O. SUMAN

IN THE operation of oil properties there are various difficulties with pumping wells which can often be overcome or greatly lessened if sufficient attention is, directed towards pump and tubing problems. The difficulties referred to are the wearing out of pumps, sanding up of pumps, and the sanding up of the hole. As the perforations in the oil strings are large and the oil and sand loose and unconsolidated considerable trouble is often encountered in pumping wells due to the ease with which' the sand can come into the holes. DETERMINING FLUID LEVEL In determining the proper depth at which to tube a well it is essential to first find out something about the behavior of the fluid in 'the hole: Facts in regard to this natter can be obtained by finding the fluid level on pulling the tubing, by making a pumping test on the well tubed to various depths, and by bailing tests during cleaning out work. In ordinary oil field operations it is customary to take the fluid level at the time of pulling the tubing. This 'can only be done when the pump is not sanded up. There are two methods used in obtaining the fluid level. One method is to note where the outside of the tubing starts, to be covered with fluid when pulling the

Jan 1, 1925

By John E. Dowis

Ore distribution being what it is, many of today's mining companies are forced to develop foreign reserves to satisfy the demands of their customers. This necessity complicates the economic picture for a company, because management must look well be- yond grade and tonnage to determine the feasibility of developing a foreign orebody. Above all, the taxes on such a development must be assessed. The difference that taxes can make in mining profits will be illustrated here for three countries-Canada, Mexico and the United States. For purposes of comparison, identical orebodies will be assumed to occur in all three countries. Only the taxes on these properties will vary. Grade, tonnage, gross income, production costs and production rates will all be the same. The discussion will be limited to federal taxes, because state and provincial taxes are usually negligible by comparison. Assumptions relative to the orebody and the nature of the company undertaking the operation are as follows: (1) Copper is the only value to be recovered. (2) Sixty million tons of ore have been delineated. (3) Underground mining is required, and the production rate will be 3 million tpy. (4) The life of the property is 20 yr. (5) Operations in Mexico or Canada will be handled by a subsidiary of a U.S. parent company. (6) The subsidiary will offer stock.

Jan 1, 1970

By H. C. George

IN 1901, the United States produced 69 million barrels of crude oil, which was 41.4 per cent of the world production. By 1931, these figures were 850 million barrels and 62.1 per cent respectively, showing over this period of thirty years an increase in the world production of 718 per cent. Over this same period, the increase in the demand for technically trained men in the industry was much greater than the increase in crude-oil production. This was because much of the increase in production was secured by the application of geology and physics to the finding of new oil fields and by .the development of engineering methods and equipment incident to drilling and producing from much greater .depths.

Jan 1, 1934

By David R. Mitchell, R. M. Fleming

MANY trends were evident in the coal industry during 1951. Some were favorable for the industry; others were not. Probably those having the most far-reaching consequences are those affecting coal's markets. The rapid dieselization of many railroads and the continued trend toward oil and natural gas for home heating has caused serious dislocations in various mining districts. Mines have been forced to close down or to work on a reduced time basis. Conversely the increased activity in the metallurgical industries has increased the demand for coking and special purpose coals, and the growing production of electric energy has increased the demand in certain areas for steam coals. The increased demand for metallurgical coal and for steam raising by the large utilities is more than equal tonnage-wise to the loss of coal to railroad dieselization and conversions to oil and gas in the domestic market. Since much of the expansion is at captive mines of large corporations, many commercial operators supplying railroad and domestic users have had their markets curtailed without any compensating demand from other sources. Feverish activity was in evidence in many areas by commercial operators attempting to find new markets. The Norfolk and Western Railway is the, only major American railroad committed to the burning of coal. It has an exceptionally good cost record. During 1951, fifteen additional modern coal-burning steam switching locomotives were authorized for construction in the company's Roanoke shops at a cost of about $1,450,000. When the new order is completed the road will own a total of sixty locomotives of the modern-switcher type, including thirty acquired by purchase last year. The Norfolk and Western today is the only American railroad building its own motive power. All of these locomotives burn coal. Production Coal production in the year 1951 will approximate 570 million tons of anthracite, bituminous coal, and lignite. Of this, approximately 7 pet is anthracite. Total production is approximately 30 million tons more than in 1950 and reflects the increase in general industrial activity. Exports are expected to be close to 50 million tons. The industrial stockpile is close to 75 million tons, the highest it has been since 1943. With the exception of the usual local stoppages the year 1951 was unmarked by labor disputes. It was a year of good labor-management relations with a negotiated wage increase unmarred by a work stoppage. This may be the beginning. of an era of sensible negotiations to find agreeable settlements of disputes without the usual protracted bickering and industry-wide strike. The United Mine Workers of America has condemned wildcat strikes, stating that in nearly every, instance proper grievance procedures have not been instituted. Government defense organizations, perhaps profiting by their experiences during World War II, are pursuing a more enlightened program with regard to the fuel requirements of the nation. Many prominent officials have stated that wherever possible coal should be considered the primary source of fuel in all defense expansion. With the increased consumption of steel by defense projects, approval of transportation facilities for liquid and gaseous fuels have been refused where these fuels would enter a coal producing area. Liquid and gaseous fuel producers also have failed to provide satisfactory evidence that they have sufficient reserves and are capable of supplying their product in adequate amounts for the periods of time required. Realization has at last become prevalent that the hydro-electric power installations in several areas are insufficient to handle increased demands.' Steam generating plants are being constructed in these areas and equipped to burn coal. Most notable of these, is the TWA area whose supplemental steam power plants are expected to consume 10 million tons of coal per year when completed. The Pacific Northwest is another area which is expected to follow the same pattern. Nearly all new steam-power generating plants are being equipped to burn coal either as a primary fuel or as an emergency measure. Metallurgical Coal The steel and other metallurgical industries are expanding rapidly to meet increased industrial demands and defense orders. Since these industries are dependent on coke, coke has had a year of high production and can be expected to break all existing records when steel-plant expansions are completed. Most notable of the expansion projects is that of the Delaware River area where the iron ore will be received by ship from Canada and South America. U. S. Steel is only one of several steel corporations that are planning on putting integrated steel producing units in this area. The Defense Solids Fuels Administration announced in December that through. November 30, 1951. 29 projects in eight states, with a total cost of

Jan 1, 1952

By Louis D. Huntoon

(New Haven Meeting, February, 1909.) THE Hammond Mining and Metallurgical Laboratory is the gift of Prof. John Hays Hammond to the Sheffield Scientific School of Yale University. Professor Hammond was graduated from this school in the class of 1876, and has always shown great interest in its welfare and progress. In 1903, he offered to build and equip for it a mining and metallurgical laboratory. This offer was gratefully accepted by the trustees; and in October of the same year the architect, W. Gedney Beatty, and the writer were employed to draw up plans for the building, which is the largest of its kind in this country. The Treasurer's report shows the total gift of Professor Hammond, including land, building, and equipment, to have been $128,741.53. This does not include $5,000 given by Professor Hammond to defray incidental expenses. The detailed cost of the machinery and installation, included in the above sum, is as follows: Machinery, $9,846.00 Pipe and fittings, 925.05 Hangers, shafting, pulleys, belts, etc., . 357.83 Steel-work, tanks, launders, etc., . 272.19 Screens for sizing ore, 411.37 Lumber, 1,896.36 General Supplies Hardware, . $135.96 Tools, 263.66 Paints, . 04.63 Electric and incidental, . 439.57 - 1,043.82 Machine-shop material, 259.44 Labor, 722.29 - 981.73

Mar 1, 1909

By J. O. Brittain, E. P. Lautenschlager, D. A. Kiewit

Compression tests were run in the temperature range of 700° to 900°C ox 0' phase NiAl intermetal-lic alloys of several grain sizes. At these temperatures the minimum strengths were observed at the stoichiometric composition. While significant increases in strength occurved in both the low-nickel (vacancy) and high-nickel (substitutional) regions, the highest strengths were found in the high-nickel region. During deformation serrated flow was sometimes observed in the low-nickel alloys. After deformation transgranular cvacking and deformation striations were observed in all compositions tested. AS part of a general investigation of the properties of NiAl inter metallic compounds, a preliminary study of the role of point defects upon plasticity was made by high-temperature compression tests on ß' NiAl specimens of several grain sizes and compositions. ß' NiAl is an intermetallic compound having a CsCl structure and a rather wide range of composition from A1-45 at. pct to 60 at. pct Ni.1 According to Bradley and Taylor2 and to cooper,' it possesses a defect lattice in which departures from stoichiometry in the direction of decreased nickel content lead to the presence of vacant nickel sites (although Cooper's work indicates that a small amount of substitution also occurs) whereas departures on the high-nickel side lead to substitution of nickel on aluminum sites. NiAl forms congru-ently from the melt at approximately 1650°C,1 and thus has a higher melting point than either of its component elements. Up to this time, although this and other high-melting intermetallic compounds have been suggested for elevated-temperature usage,4 only the hardness4 and a few tensile-strength measurements5 have been reported for NiAl at high temperatures. In the present investigation the effects of composition upon the compressive-strength properties in a range of 700° to 900°C have been measured for NiAl of several grain sizes. EXPERIMENTAL PROCEDURES The alloys were made as described elsewhere6 from an A1-46.8 at. pct Ni master alloy furnished by the International Nickel Co. with additions of high-purity nickel and aluminum. The charges were vacuum-induction-melted in A12O3 crucibles with small amounts of helium added to the atmosphere to suppress vaporization. They were cooled slowly from the melting temperature to achieve uniform grain size. In order to refine the as-grown grain size a special rolling technique was developed. Alloys were packed into 0.10-in. wall-type 302 stainless-steel tubes which were partially filled with magnesium oxide to prevent bonding between the alloy and the steel jacket. The ends of the tubes were closed by hot forging, and the packets were then hot-rolled. The alloys with greater than 50 at. pct Ni were rolled at 1100°C, but it was found necessary to increase the temperature to 1350° C before alloys with less than 50 at. pct Ni would roll without cracking. With these temperatures, reductions as high as 48 pct were achieved in a single pass. The rolled alloys will hereafter be referred to as "fine grained" whereas the as-grown material will be designated "coarse-grained''. The compression specimens were made by cutting square cross-sectional pieces, approximately 3/16 by 3/16 by 1/2 in., with a water-cooled diamond cut-off wheel from the as-grown or the rolled alloys. Specimens were ground to their final dimensions by polishing through 3/0 grit silicon carbide papers. The final shape was a rectangular parallelepiped of square cross section having a height-to-width ratio of 3:1. Compression testing was carried out in a compression rig of our own design mounted on an In-stron Floor Model. The specimen chamber could be heated to 1000°C and was controlled within ±2°C. The compression rig was enclosed within a bell jar and was maintained at a 50 µ of mercury vacuum throughout the duration of the test. The test cham -ber was heated from room to test temperature within 15 min. Specimens were then held at the test temperature 30 min prior to testing. Previous experiments indicated that no grain growth would occur within this time. An Instron Variable Crosshead speed unit was used to adjust for small variations in specimen lengths in order to have a constant initial strain rate, €, for all specimens of a group. For the fine-grained specimens the strain rate was changed rapidly at constant temperature by a factor of 10 with the speed lever on the Instron. For a given € the compression data was analyzed in terms of true plastic strain (E) and true compressive stress (0).

Jan 1, 1965

By Thomas L. Kesler

Essentially all of the barite produced in Georgia has come from the Cartersville district in the northwest part of the state. The earliest recorded shipment of ore, 60 tons, was made in 1894.1 With the exception of the four-year period 1931 to 1934, the separate yearly output has been recorded and published since 1915, whereas the total yearly output of the United States has been published since 1880. The separately recorded production of Georgia (Cartersville) through 1947 is 2,232,544 short tons valued at $14,900,746,2 but unpublished data on the period 1931 to 1934, plus the estimated unrecorded output prior to 1915, make the actual total about 2,400,000 short tons. This is about 21 pct of the total production of the United States, which, through 1947, is 11,328,440 short tons valued at $71,683,386.2

Jan 1, 1949

By W. E. Keck, Paul Jasberg

The flotative properties of the principal minerals in Michigan's potential iron ores have been investigated to develop methods of bene-ficiation for the ores. One of these minerals, magnetite, is of considerable importance as a source of iron. Study of its flotation was similar to that of hematite1, another iron mineral in these potential ores. The present research consisted essentially of: (1) a survey of the literature on magnetite flotation, (2) the preparation of pure magnetite, (3) the development of laboratory procedure and (4) flotation experimentation. Literature on Magnetite Flotation.—For the purpose of this discussion, the results of previous work on the flotation of magnetite can be summarized as follows. The mineral has been floated with pine oil2, and it has also been separated from synthetic mixtures with silicates by the use of the same reagent2. Magnetite and apatite in iron-ore slimes have been separated by flotation of apatite with sodium palmitate3. These data were utilized in the present investigation. Preparation of Magnetite.—The pure mineral was prepared from the magnetic-separator concentrate of an iron ore (obtained from the Wither-bee Sherman Corporation, Port Henry, N. Y.). This concentrate was slowly comminuted with laboratory rolls and pulverizer to pass 65-mesh and was then tabled several times. Tabling yielded a relatively coarse magnetite concentrate, tailing and slimes. The two latter materials were rejected insofar as the present work is concerned, and treatment of the magnetite (table concentrate) was continued by separating it into — 65 + 200 and — 200-mesh sizes. Separation of the sizes was made by first dry screening and then wet screening. The —200-mesh material was rejected to eliminate possible introduction of error into flotation

Jan 1, 1939

By W. E. Keck, Paul Jasberg

The flotative properties of the principal minerals in Michigan's potential iron ores have been investigated to develop methods of bene-ficiation for the ores. One of these minerals, magnetite, is of considerable importance as a source of iron. Study of its flotation was similar to that of hematite1, another iron mineral in these potential ores. The present research consisted essentially of: (1) a survey of the literature on magnetite flotation, (2) the preparation of pure magnetite, (3) the development of laboratory procedure and (4) flotation experimentation. Literature on Magnetite Flotation.—For the purpose of this discussion, the results of previous work on the flotation of magnetite can be summarized as follows. The mineral has been floated with pine oil2, and it has also been separated from synthetic mixtures with silicates by the use of the same reagent2. Magnetite and apatite in iron-ore slimes have been separated by flotation of apatite with sodium palmitate3. These data were utilized in the present investigation. Preparation of Magnetite.—The pure mineral was prepared from the magnetic-separator concentrate of an iron ore (obtained from the Wither-bee Sherman Corporation, Port Henry, N. Y.). This concentrate was slowly comminuted with laboratory rolls and pulverizer to pass 65-mesh and was then tabled several times. Tabling yielded a relatively coarse magnetite concentrate, tailing and slimes. The two latter materials were rejected insofar as the present work is concerned, and treatment of the magnetite (table concentrate) was continued by separating it into — 65 + 200 and — 200-mesh sizes. Separation of the sizes was made by first dry screening and then wet screening. The —200-mesh material was rejected to eliminate possible introduction of error into flotation

Jan 1, 1939

REPUBLIC STEEL CORP. and Armco Steel Corp. have joined in a $160,000,000 project for the production of iron ore from Taconite in the Lake Superior mining region. The two companies announced acquisition in equal shares of 100 pct ownership of the stock of Reserve Mining Co., which controls a vast deposit of magnetic Taconite iron ore on the eastern end of the Mesabi range in Minnesota. Through Reserve Mining the two companies will build a plant for manufacturing high grade ore from Taconite near Beaver Bay on the north shore of Lake Superior. The first announcement calls for about a $60,000,000 plant which will be built as soon as plans are completed and will have an annual capacity of about 2,500,000 tons of iron ore pellets. Longer range development plans call for future expansion of the plant to provide an annual capacity of 10,000,000 tons. This will amount to an additional investment of

Jan 10, 1950

No. 576.-Graduate mining engineer, married, 32 years of age. Have had 10 years' experience in mining from position of mucker to that of general superintendent. For past four years have been in Copper River District of Alaska as mining engineer, and superintendent of gold and copper mines. Desire position in U. S. Best of reference. No. 577.-Member, technical, age 27, married. Open for engagement. Past year in war mineral field work, operation and production. Ten years thorough experience in both subordinate and executive positions, gold, silver and copper in the U. S., Mexico and South America. Devel-

Jan 5, 1919

By M. F. Burr, F. V. Lenel, G. S. Ansell

The mechanism of materials transport was studied in a model experiment in which a silver sphere was sintered to a silver plate under an applied external stress near 800° C. For this purpose the rate of growth of the neck between the sphere and the plate which is proportional to the strain rate of the creep process involved in a neck growth was determined by measuring the change in electrical resistance of the away. This rate of neck growth will depend upon the magnitude of the applied external stress. By measuring the rate just before and just after a change in the external load and therefore the applied stress, the relationship between strain rate and stress can be derived. For material transport by slip in a pure metal it is expected that the strain rate should be proportional to the 4.5th power of the stress, while for transport by diffusional flow the strain rate should be proportional to the first power of the stress. It was found that for stresses above 5 X 10' dynes per sq cm (70 psi) the exponent in the stvain rate-stress relationship was near 4.5 while for a stress of 0.7 x 108 dynes per sq cm (10 psi) an exponent of 1.8 was determined indicating that under the conditions of the experiment the transport mechanism for creep in silver shifts from diffusional flow to slip in the region of 0.7 x 106 dynes per sq cm (10 psi). The importance of these findings for an understanding of the mechanism of material transport in conventional sintering (without an external load) is pointed out. In a paper by Early et al.,' the mechanism of material transport during sintering was treated as a creep process. It was pointed out that two possible types of creep processes could operate during sintering. In one of these material transport takes place by vacancy diffusion due to a gradient in chemical potential. The vacancy sinks in this diffusion process may be either grain boundaries, as in Herring-Nabarro microcreep, or regions beneath a surface of small radius of curvature. The diffusive transport may be by volume, grain boundary, or surface diffusion. In the other mechanism, creep takes place by slip, i.e., dislocation motion with its rate generally controlled by dislocation climb. One method of distinguishing between these two modes of materials transport is to investigate the creep rate, i.e., the rate of material transport as a function of stress. For material transport by vacancy diffusion, the creep rate is proportional to the stress.' For creep by slip, controlled by dislocation climb, the creep rate is proportional to a power of the stress. For pure metals this power is 4.5;374 for dispersion-strengthened material a fourth power relationship can be derived.5 This difference in the stress dependence of the strain rate is illustrated schematically in Fig. 1, in which the logarithm of strain rate is plotted vs the logarithm of the stress for material transport in a pure metal by vacancy flux and by dislocation climb. The stress range in which the two types of material transport overlap would be expected to be relatively small. In the experiments described by Early and coworkers compacts pressed from spherical copper powder were sintered isothermally under an applied axial external load in a dilatometer. During sintering the magnitude of the applied external load was changed and the rate of axial shrinkage of the compact before and after the load change determined. In order to find the stress dependence of the strain rate the magnitude of the stress acting on the neck area between the spherical particles before and after the load change had to be calculated. This stress is the resultant of the stresses due both to the externally applied load and to surface tension. The stress due to surface tension is a function of the geometry of the powder compacts. It can be determined, at least for simple geometrical arrays,'76 but it is difficult to obtain exact values of the stresses for actual powder compacts when only average values of particle diameters and of neck diameters between particles are available. The calculation of stress and the strain rate-stress relationship is therefore only very approximate.

Jan 1, 1968

By William P. Blake

The Rainbow Lode is situated at Walkerville, in the Summit Valley mining district, Silver Bow County, Montana Territory, about one mile from Butte City. It was so named ill 1876 by Mr. J. E. Clayton, in recognition of the broadly-sweeping curve of the outcrop across the rounded surface of the eastern slope of a granitic mountain, at an elevation of about 6000 feet above the sea-level. It is on the western side of the range which divides the waters of the Missouri from those of the Columbia. History.—The history of the district is an instructive one. The water-courses and flanks of the hills were worked for years for placer gold. Millions of dollars' worth of low-grade gold have been washed out of the surface gravels below the veins of the district. Missoula Gulch and Silver Bow creek, just below Butte, are noted for their rich placers, and they continue to yield largely, producing within narrow limits from $50,000 to $100,000 dollars' worth of golddust yearly. It is ragged vein-gold, and evidently is near its parent source. It is no doubt derived from the disintegration of the veins of the district, and this conclusion was soon forced upon the miners. The veins which were seen outcropping boldly upon the slopes above them were located, and prospecting commenced. These outcrops were found heavily stained and blackened with oxide of manganese, and were porous and honey-combed in places, showing that the quartz was formerly filled with pyritous ores, and that these ores had decomposed and dissolved away, leaving, however, portions of the precious metal behind, especially at and near the surface of the ground. Assays of the croppings gave variable and often contradictory results; but the fact. that these were the outcrops of lodes bearing gold and silver in depth was patent to any experienced observer of mineral veins. The lodes of the district were first brought prominently to notice by Mr. Clayton in 1876, and in October of that year the Alice mine, upon the central portion of the lode, was opened by Mr. Marcus Daly, now so well known as the superintendent of the Anaconda Copper mine, upon another extremely interesting lode, in the same region.

Jan 1, 1888

By James Park

The principal gold-bearing formation is of volcanic origin, consisting of a great accumulation of andesitic lavas, tuffs, breccias and agglomerates of lower Tertiary age. These rocks everywhere bear evidence of having been subjected to the prolonged leaching-action of thermal waters, doubtless accompanied by steam and acid vapors. They are found in all stages of decomposition or alteration; and in many mines the hard blue andesite can be seen to pass by a series of almost insensible gradations into a soft, or fairly hard, greyish yellow or blue

Jan 1, 1900

By R. Taggart, R. H. Ericksen, D. H. Polonis

Transmission electron microscopy techniques hare been used to study the spontaneous marfensite phase that forms during the thinning of Ti-Cr alloys. The structure of this phase has been found to differ. from the hcp martensite and has been identified as a clisforted fcc lattice. The spordaneous marlensile in this system is interpreted as a metastable isomorph of the equilibriunz TiCr, phase. WHEN thin-foil specimens for transmission electron microscopy were prepared from metastable alloys of the Ti-Cr system, a spontaneous transformation occurred' when the foils contained the untrans-formed 0 phase or two-phase mixtures of the 0 and w phases. The purpose of this paper is to examine the relationship that exists between the crystal structure of the spontaneous product and that of the matrix. The differences between the martensite transformation that occurs in the bulk material and the spontaneous reaction that occurs during the preparation of thin foils are compared with the observations that have been reported for similar phenomena in a commercial titanium alloy.' A spontaneous reaction that exhibits characteristics similar to a martensite transformation has been reported to occur in thin foils prepared from the retained metastable structures of several alloy systems.1'3"7 ~ull~ observed such a spontaneous reaction in 0 brass and attributed the apparent increase in the martensite transformation temperature to a decrease in the non-chemical free energy associated with bulk strain energy. He also showed that the spontaneous product did not have a specific habit plane, but that its orientation relationships to the parent matrix were dependen on the thickness of the transforming region. It has also been pointed out by Breedis6 that in thin films the absence of the constraints imposed by a bulk matrix can cause different requirements for the martensite plate interface and lattice distortion which is reflected bv a dependence of the transformation mechanism on the specimen geometry. In the case of the spontaneous reaction reported for Au-Zn alloys7 a definite habit plane was determined and shown to correspond with the habit plane calculated on the basis of the Bowles and Mackenzie crystallographic theory of the martensite transformation.'- lo EXPERIMENTAL PROCEDURE A series of titanium alloys containing 5.5, 5.9, 6.4: 7.6, 8.0, 11.3, and 18.7 at. pct Cr were prepared from high-purity (iochrome) chromium and iodide-grade titanium by levitation melting. The experimental procedure used for sectioning the alloys and for thin-foil preparation has been reported in an earlier paper.' X-ray diffraction patterns were obtained using a 114-mm Debye-Scherrer camera and Cu-Ka radiation. In order to minimize fluorescent radiation from the specimen, a strip of aluminum foil 0.002 in. thick was placed in contact with the X-ray film. After a specimen was removed from the camera: an additional X-ray experiment was performed, to insure that no spurious lines were obtained due to the presence of the aluminum foil. The interstitial impurity analysis for the alloys used in this study was as follows: oxygen, 100 ppm: hydrogen, 30 ppm: nitrogen, 28 ppm. EXPERIMENTAL RESULTS Electron diffraction patterns were obtained from several individual crystals of the spontaneous marten-

Jan 1, 1970