By Henry E. Wood

In my opinion, the concentration of minerals by flotation is the most interesting problem in ore-dressing, and will command eventually far more consideration than it has at present. For many ores it furnishes a complete method of concentration absolutely independent of specific gravity, and thus simplifies the milling of many difficult combinations. Not having to recognize the influence of specific gravity, we are also able to dispense with some of the complications resulting from classifying-conditions. Where flotation cannot be used for a complete separation of the minerals from the gangue, it will be found, in nearly all cases, to save those portions which are generally lost by reason of their fine state of division. For this reason, it should be looked upon mainly as an aid to general concentration, although there are many ores so well adapted to flotation that more than 90 per cent. of the valuable metals can be recovered from them in one operation by this process. In presenting the results of my investigations in flotation, I have endeavored to theorize as little as possible. That side of the subject has been extensively discussed by others. My earliest work with flotation was done in 1895, when I used various oils, grease, soap, etc., with results that were remarkable. I did not realize then that with water alone equally good separations could be made. Up to 1906, my endeavors were confined to attempts to keep the concentrates on the tables well wetted and away from exposure to the air. In common with others, I observed that when there mas any obstruction in the wash-water on the table of sufficient size to divert the water to either side, the concentrates collected, and, on exposure to the air, would promptly float away. This convinced me that the sulphides were all good "swimmers," and that if,

Jan 1, 1913

By C. D. Wiseman

THE concept of alloying to increase the strength of metals originated during the bronze age. However, at the present time there is no single theory capable of explaining all of the observed strengthening effects of alloying elements on the mechanical properties. In general, it may be said that solid solutions are stronger than the pure metal and that the strengthening effect increases with increasing alloy content. Various theories for solution hardening have been proposed, the first of which was presented by Rosenhain who suggested that the alloying elements roughened the slip planes, thereby requiring a higher stress to initiate slip. Recent work by French and Hibbard2 confirmed Norbury's3 conclusion that those alloying elements which cause a greater change in lattice parameter have larger effects on hardness. However, a given change in lattice parameter produced by different alloying elements does not cause the same change in hardness. A further refinement was suggested by Dorn, Pietrokowski, and Tietz4 who considered differences in valence between the solute and solvent with the change in lattice parameter to explain the plastic properties of aluminum alloys. Allen, Schofield, and Tate5 further investigated the valency contribution to solution strengthening by testing some copper-base solid-solution alloys having constant electron densities. Tensile tests performed on these alloys gave identical stress-strain curves even though the atomic size effect, which varied by a factor of two, was neglected. The advent of dislocation theory6-8 provided a new and powerful tool capable of explaining many phenomena of plastic deformation and indicated new approaches to solution hardening. The basic con- cept of recent theories is that solution hardening is not due to stresses associated with randomly dispersed solute atoms, but rather to a nonuniform distribution of the solute. This conclusion was reached by consideration of the effective tension present on each dislocation line and the ability of a dislocation to pass an obstacle. cottrell suggested the possibility that the internal stresses due to randomly distributed solute atoms would offer essentially no resistance to the passage of dislocations. He reasoned that an edge dislocation may be considered as a rigid line discontinuity. As the dislocation moved through a crystal, the random stress fields would be equally distributed along its length. Since half of the stress fields would be acting to move the dislocation forward and the other half trying to move it back, the net effect on the dislocation would be zero. Thus the randomly distributed solute atoms would not contribute appreciably to solution strengthening. Mott and Nabarro10 considered the dislocation as a flexible, rather than a rigid, discontinuity. They obtained a simple model for a dislocation moving in a lattice having precipated particles, where the dislocation would actually bend around the obstacle until it would loop back onto itself to rejoin and then continue onward. Their work indicated that the minimum radius of curvature of the dislocation line, under the action of an external stress and in the region of an internal stress, would be such that the dislocation would be unable to pass through a matrix containing small closely spaced precipates by the looping process. The dislocations would tend to remain rather straight, approaching the condition of Cottrell's rigid dislocation. Hence, the strengthening must not be due to random solute atoms; however, it might be due to the concentration of atoms, either as clusters of like atoms or as short-range ordered regions, or to the concentration of solute atoms around dislocations. To date, four mechanisms of solution strength-

Jan 1, 1959

By D. D. Pollock, D. I. Finch

Relationships between the compositions of specially prepared manganin-type alloys and some of their electrical properties have been established. Empirical equations, based upon the electronic configurations of the alloying elements, are given which describe the resistivity, temperature coefficient, peak temperature, and thermoelectric power of Cu-Mn-Ni-Fe alloys at approximately room temperature. Calculations based upon these relationships are correlated with experimental data. SECURING suitable alloys for the construction of stable resistors, for use in precise electrical measuring devices, has been important ever since the art of electrical measurement was begun. German silver, Pt-Ag, and Platinoid are examples of some of the alloys in early use. These early alloys were un- satisfactory for one or more of the following reasons: l—insufficient stability of electrical properties with time, 2—poor reproducibility of electrical characteristics from melt to melt, 3—excessive temperature coefficients of resistance, and 4—excessive cost. Weston introduced the Cu-Mn-Fe and Cu-Mn-Ni-Fe alloys of the type now generally known as manganins. His patents are believed to represent the first disclosure of any alloy with a negative temperature coefficient of resistance. After this work, the German company, Isabellenhutte, in conjunction with Feussner and St. Lindeck, produced alloys of

Jan 1, 1957

By P. W. Davies, B. Wilshire

PREVIOUS investigations on the effect of stress changes on the high-temperature creep and fracture behavior of metals have been confined mainly to the testing of complex alloys.172 Most of these alloys are structurally unstable during creep because of such effects as recrystallization, overaging, and so forth, so that the results are of limited application. The only pure metals on which observations have been made appear to be lead3,4 and aluminum5 tested under conditions which allow rapid recovery to take place. The present work describes the effect of a single stress change on the creep and fracture properties of a metal in which recovery is very slow. A Ni 0.1 at. pct Pd alloy was used so that grain growth and recrystallization did not occur during creep testing. Specimens of this material were heat-treated to give a uniform grain size of 10 grains per mm. Creep tests were carried out at 500°C using Denison T.47 machines; details of the creep-testing procedure have been given elsewhere.' All specimens were tested at a constant initial stress of 5 tpsi which gives, in an uninterrupted test, a minimum creep rate of ~10-3 pct per rnin and a life of -7000 min. Specimens were loaded under these standard conditions and after 1500 min, when secondary creep was well-established, the stress was changed to either 8, 7, 6, 4, 2, or 0 tpsi for a period of 180 min. After this time the original load was reapplied and the tests continued to fracture. The results are shown in Fig. 1. No detectable creep occurred during the period of reduced load, even at 4 tpsi, and on reverting to 5 tpsi the creep rate returned to its original value immediately. Increasing the stress to 8, 7, or 6 tpsi resulted in an instantaneous extension followed by a period of transient creep leading to a new steady creep rate. On returning from these higher stresses, the resulting creep rate at 5 tpsi was very low compared with the original value. Furthermore, the higher the stress during the stress change, the lower was the final creep rate. It is significant that the rupture life is comparatively unaffected by any of these stress changes.

Jan 1, 1965

By Emile Gyss

THE speed of drilling rock has become an impor-tant factor in mining operations, while the place-ment of holes, kind, and quantity of explosive used. are equally important. These are a function of the rock hardness and toughness. Both of these fac-tors must be considered in compiling a table that will enable a mine operator or engineer to estimate drilling speeds in a given rock, knowing its hardness, and from its toughness, the dynamite required. The hardness of a homogeneous rock may be defined as its resistance to a penetrating medium, such as a drill-steel bit, and toughness, its resistance to with-stand rupture by the tearing apart of its minerals or parts of the same mineral. Rock hardness, as it has here been defined, is a function of the hardness of the component grains composing it, as well as grain size, shape, arrangement, and binding minerals. Rock tough-ness depends on substantially the same factors, but is measured by a totally different method. The units in which rock hardness is usually ex-pressed are either relative values or alphabetical desig-nations which carry no definite quantitative meaning. R. M. Raymond has suggested the measurement of com-posite rock hardness, based on mineral hardness as ob-tained by the Moh scale. This is done by multiplying the percentage of each mineral in a rock by the Moh mineral hardness and dividing by 100. These values convey a clearer conception in the minds of men in-terested in rock work -and are the basis of the units used in Tables 1 and 2. The hardness of rocks as it has been variously de-fined may be determined by different methods. The first method is one in which the proportionate average of the hardness of minerals making up a rock is the basis for classification. The other factors of grain size, shape, arrangement, and binding power are not considered.

Jan 6, 1927

By C. R. Van Hise

Introduction.............29 The Three Zones of the Lithosphere ..30 Zone of fracture............31 Zone of flowage............ 31 Factors influencing depth at which flowage occurs.. 32 Zone of combined fracture and flowage.. 33 The Water-Content and Openings in Rocks....36 Condition of rater in the zone of fracture.. 36 The openings in rocks...........38 Size and number of openings..... 40 Ore-deposits derived from zone of fracture..45 The source of underground water......... . 47 The cause of the flowage of underground water..47 Belts of underground circulation.. 51 Upper belt of underground circulation.. 51 Lower belt of underground circulation.. .... .52 Capacity of water for work in the lower belt of underground circulation........... 53 Movementsof water in the lower belt of underground circulation. 54 The preferential use by water of large channels.. 60 Physico-Chemical Principles Controlling the Work of Under ground Waters..........62 Chemical action............63 Underground aqueous solutions..64 The relations of solution and temperature..... 65 The relations of solution and pressure..66 Precipitation........... 67 Precipitation by change in temperature..68 Precipitation by change in pressure..69 Precipitation by reactions between aqueous solutions.. . 69 Precipitation by reactions between liquid solutions and solids. 70 Precipitation by reactions between gases and solutions. and solids............71 The General Geological work of Underground Waters.. . 71 Division of the zone of fracture into a belt of weathering and a belt of cementation............72

Jan 1, 1901

By Guy Crane

I. INTRODUCTION THE geology of the Tintic mining district, fully treated, would occupy an elaborate monograph. This less comprehensive paper is devoted primarily to the occurrence and origin of the orebodies of the district, while space is given to those phases of the general geology only which seem necessary to a proper setting of such a discussion. The first geological report on the Tintic district to be issued was that by Tower and Smith, published in 1899, in the form of a paper in Part III of the Nineteenth Annual Report of the U. S. Geological Survey, and also as Folio No. 65, Geologic Atlas of the United States. About four years ago a second investigation was begun by Waldemar Lindgren and G. F. Loughlin, of the U. S. Geological Survey. With the exception of a paper on the oxidized zinc ores of the Tintic district by Mr. Loughlin, the results of their work are still unpublished. The writer's acquaintance with the district began in the fall, of 1913, and has extended over a period of about two years.

Jan 10, 1915

By H. A. J. Wilkens, H. B. C. Nitze

From time to time papers treating of specific cases of Southern gold-mines and mining have appeared in the Transactions of this Institute, as well as in other journals and publications. Mr. George I?. Becker, of the United States Geological Survey, made a reconnaissance of the Southern Appalachian gold-belt during the fall of 1894; the results of his investigations are published under the title of "A Reconnoissance of the GoldFields of the Southern Appalachians," in the Sixteenth Annual Report of the Director of the United States Geological Survey, 1894-95 : Part III., " Mineral Resources of the United States." Mr. Becker has treated the subject mainly in a scientific geological manner. We present this paper to the members of the Institute as requested by the Secretary last May, with the object of covering the ground from a more practical and technical standpoint. The notes for this paper were made in a large measure from personal observations, gained chiefly during the past summer on a trip through the field. In connection with this trip we collected a suite of typical hand-specimens, representing the gold-ores and wall-rock from the more important localities. This collection forms a part of the exhibit

Jan 1, 1896

By Dorsey Lyon

INTRODUCTION THE electric furnace has always been found to be especially adapted to melting, refining, and finishing processes throughout its gradual acceptance by metallurgists, as a practical apparatus for conducting metallurgical operations. In the steel industry, the electric furnace is firmly established in the manufacture of steel of the highest grade, equal to crucible steel. For the production of the cheaper grades of steel in large tonnage, the electric furnace gives a higher-grade product than the open-hearth or converter, but due to the high cost of power prevailing in steel centers, considered from the electric furnace standpoint, it is not economical to produce tonnage steel in the electric furnace. As a refining and finishing agent for open-hearth or Bessemer steel, the electric furnace has had some degree of success in the production of tonnage steel. After a study of the use of the electric furnace in the steel industry, it appears that there may be a possibility of its use to advantage for the melting of cathode copper. In the case of copper the problem is not one of actual refining, because the copper if refined properly y the electrolytic method needs no further refining; it needs simply to be cast into a marketable shape. The name" refining". is applied to the present finishing process, because in the operation oxygen and other impurities are removed, which the electrolytic copper absorbs in being melted in the reverberatory furnace. Considering that processes may be positive, negative, and neutral; the electrolytic method would be positive; reverberatory melting of cathode copper, negative; and electric furnace melting, neutral. The electrolytic method produces about as pure a copper as is possible, if operated properly and the anodes are not too impure. The final reverberatory melting of this cathode copper lowers the grade of the final product, due to the absorption of gases and impurities.

Jan 8, 1914

Open pit operators have found the dropball crane a great aid in cutting costs and hazards of secondary breakage. But a common problem in using the unit has been with the shock absorbing connection from the cable to the dropball itself. Blair Limestone Div. of Jones & Laughlin Steel Corp. has come up with a new connector to solve this problem and to save the time usually lost in frequent replacement of the cable slings, chains, or old tires hitherto used at this point. J&L personnel solved the problem by combining three ideas from other dropball crane owners. Their unit consists of two long U-bolts running through a heavy spring originally made for use on a vibrating screen. Heavy duty swivels attached to the bent ends of the U-bolts provide attachment points for the crane cable and the special chain to the dropball. Connection at the dropball is by an eyelet welded directly into the mass of steel, and a special alloy chain is connected to this with a clevis.

Nov 1, 1955

A-Metal Mining B-Minerals Beneficiation F-Coal H-Industrial Minerals

Jan 11, 1950

By B. L. Sackett

LEAD smelting has been an important industry in Utah for many years. The first lead smelting was done, over 60 years ago, at the Rollins mine in Beaver County, by burning heaps consisting of alternate layers of wood and high-grade carbonate ore. The lead thus obtained was. molded into bullets. With the development of. the mines, the problem of cheaper handling of the ore became important. The only outlet for this ore was Swansea or the Atlantic Coast but to ship to either cost $150 per ton or more for treatment and handling. From 1864 to 1871, experimenting was done with blast, Scotch hearth, and reverberatory furnaces, with the blast furnace surviving as, the standard plant. The first crude furnaces were circular or hexagonal in shape, and were made of adobe and stone, which quickly burned out. They were small, about 2 1/2 ft. in diameter, and smelted from 3 to 10 tons. in 24 hr. The metal had to be tapped from the bottom of the crucible, necessitating a shut down of the furnace during this process. This pro¬cedure caused salamanders to form around the tap hole when the furnace was started again, which frequently resulted in freezing. The campaign lasted until a tap of bullion was made. The first successful plant of the crude stone type was operated in 1870. From 1870 to 1872, there was a smelter building craze in the state. During that period, about 20 furnaces were built, chiefly near the mines, and their operation was limited and sporadic. The work was then placed in the hands of trained metallurgists, who standardized on the rectangular form of furnace. In 1871, Daggett, at the Winnamuck mine in Bingham, installed water-jackets around the smelting zone of the furnaces. These furnaces were circular; the diameter at the tuyere line was 3 ft. 6 in. and at the charge floor 5 ft. 3 in. The height from tuyere line to charge floor was 14 ft., height of tuyere line above top of crucible was 3 ft. 8 in. Fur-

Jan 8, 1925

By J. O. Lewis

Oil wells usually reach their maximum daily output shortly after they are completed. From that time they decline in-production, the rapidity of decline depending on the output of the wells and on other' factors governing their productivity. The production curve of a well shows the mount of oil produced per unit of time for several consecutive periods; if the conditions affecting the rate of production are not changed by outside influences, the curve will be fairly regular, and, if projected, mill furnish useful knowledge as to the future production of the well. By the aid of this knowledge the value of a property may he judged, and proper depletion and depreciation charges may be made on the books of the

Jan 2, 1918

By H. H. Hausner, H. S. Kalish

IN recent years zirconium and beryllium have become of great interest because of their special properties. Zirconium is known for its remarkable ability to absorb the gases oxygen, nitrogen and hydrogen, has extensive use as a getter in electron tubes and has indeed become the primary metal in the manufacture of photoflash bulbs. Beryllium is of interest because it is light metal and as such could supplement aluminum and magnesium in light metal applications. The late development of zirconium ductile at room temperature produced by both the iodide and calcium reduction methods has stimulated frequent articles on this metal in the recent literature. Beryllium is so closely akin to zirconium crystall-ographically that some investigators are of the opinion that beryllium should be ductile at room temperature if it were pure enough. The crystallographic relationship of beryllium and zirconium, the interest created in Be-Zr alloys where the zirconium is believed to function as a remover of solid solution gas in beryllium and thus increase the ductility of the beryllium rich alloy, and the amenability of these metals to powder metallurgy methods stimulated this approach to an investigation of the system Be-Zr. Preliminary work showed that a zirconium compact melted when pressed in contact with a beryllium compact and sintered at 1250°C, without any apparent final bond between the two. A search of the literature revealed nothing pertinent about the Zr-Be system or about any zirconium - beryllium alloys. In 1936 Misch³ vaguely identified the compound ZrBe2 and reported that it has a deformed cubic structure. Two patents," , were issued to Mach-lett Laboratories in 1943 and in 1946 regarding the addition of small amounts of zirconium to beryllium in order to improve the ductility of beryllium so that it may better be used for X ray windows. In considering the alloy formation of beryllium with other metals Raynor thought it unlikely that zirconium would have any solid solubility in beryllium. From this indefinite information nothing could be ascertained about the possible use of Zr-Be alloys or the use of these metals intimately. A brief preliminary study of the system Zr-Be by powder metallurgy methods was undertaken to provide regions for more intense studies of Zr-Be alloys and as a guide to a formal phase diagram determination. The investigation described in the following pages was completed in less than three weeks. The usefulness of this rapid method to facilitate phase diagram studies and new alloy investigations will be shown. Materials and Procedure Zirconium powder was produced from crystal bar stock of high purity supplied by Foote Mineral Co. The crystal bar was converted to hydride at 730°C, crushed, and the hydride decomposed in purified argon at 850°C. 60 pct of the powder passed through a 325 mesh screen, 40 pct of the powder was —140 mesh, +325 mesh and the average particle size of the total was 8 to 12 microns. The beryllium powder was used as re-

Jan 1, 1951

By E. A. Anderson, P. W. Ramsey, E. J. Boyle

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By P. W. Ramsey, E. J. Boyle, E. A. Anderson

Only a few zinc-rich alloys are in commercial use today, and these depend largely upon solid solution effects for their desirable properties. Typical examples are rolled alloys containing about 1 Per cent of copper, with Or without additions of elements such as magnesium, and die-casting alloys containing about 4 Per cent of aluminum with small amounts of magnesium and sometimes copper." A number of elements are capable of forming alloys with zinc, Which do not enter into solid solution except in limited degree. The Present Paper considers One such system, zinc-titanium, in which alloys having potentially useful properties in the rolled form were found. Zinc-titanium System The zinc-rich portion of the zinc-titanium diagram, as determined by standard methods in this laboratory,3 is shown in Fig. I. The portion of the diagram of significance in the present work extends from 0 to about 0.5 per cent titanium. Gebhardt4 places the eutectic at 0.45 per cent, but the evidence in favor 01 the composition given in Fig. I is considerable. The solid solubility of titanium in zinc is very low indeed and possibly places these alloys in a somewhat different category from the commercial alloys previously mentioned. Alloy Preparation All of the alloys used in this work were prepared with titanium metal of 98.9 per cent purity. In most cases high-purity zinc (99.99 per cent) was used but sufficient work was done later to show that zinc of about high-grade composition would yield approximately equal results. Best practice in alloy manufacture seemed to be to prepare a zinc-titanium hardener by adding about 4 per cent of titanium metal to molten zinc and holding under a boric acid cover, with frequent stirrings, at 750°C, until the titanium had dissolved. The desired titanium content could readily be obtained in the final alloy by adding the calculated amount 01 this hardener. The alloys proved to be quite stable in composition, unless overheated, and, with reasonable temperature control, required no cover or flux to prevent loss of titanium content by oxidatioll, Hot-rollig Tests Three alloys containing, by analysis, 0.05, 0.12, and 0.23 per cent titanium were selected for preliminary study. Slab cross sections a a marked grain refinement* (Fig. 2) in the two alloys of highest titanium content. Cast unalloyed zinc has a columnar grain structure similar to that shown for the alloy of lowest titanium content but without the scatter of small equiaxed grains at the center.

Jan 1, 1944

By Fred L. Morritz, Harold M. Manasevit, Richard Nolder, Arnold Miller

Experimental evidence is presented which confirnis the epitaxial relationship between the deposited silicon and the sapphire substrate. Four distinct modes of orientation relationships have been established. These have been shown to be Single-crystal gvowth retention as a function of surfaces oriented off ideal has been qualitatively indicated. Both full-circle goniometer X-ray techniques and replica electron microscopy have indicated varying amounts of microtwinning in the silicon. film, which may he caused by the mode of silicon formation. Parameters have been found where twin density is less than I pct. The early stages of' epitaxy of silicon m sapphire have been examined by electron-microscope techniques... and mechanisms have been proposed. THE first report of the deposition of single-crystal silicon on sapphire (single-crystal aluminum oxide) was made at the American Physical Society Meeting in Canada' by one of us and was subsequently published in the Journal of Applied physics.* This paper summarizes some of the work carried on in this area since that time, in addition to reviewing some of our earlier observations. The initial single-crystal deposits of silicon on sapphire reported were obtained on sapphire planes produced by cutting a sapphire rod perpendicular to its fastest growth direction, which is approximately 60 deg from the C axis. Direct correlations between the microstructure and X-ray data as to the single crystallinity as shown in Fig. 1 are evident. These deposits were identified as (111) silicon on the substrate oriented near the (1123) of sapphire. (Sapphire notations are designated according to the c over a ratio of 2.73.) It became evident that substrate quality and surface play an important part in successful epitaxy. For example, in Fig. 2 we observe an interesting

Jan 1, 1965

By L. VOGELSTEIN

OUTSTANDING among the year's events in copper has been the reimposition of an import duty of 4r. per pound in this country which became effective June 21. In consequence of this action by Congress, the Ottawa Empire conference recommended a duty of 2d. per pound equivalent at normal rate of exchange to our 4c. duty, on all copper originating outside of the Empire. Lip to the middle of this year only Russia and Japan had a closed market; the import duty on copper in Russia is 30 per cent ad valoremm and in Japan about 2c. Russia's consumption has always been in excess of production and she has imported from 2(1,000 to 40,000 ton, of copper per annum. Japan, with a production of 6,000 to 7,000 tons per month, has absorbed, in normal times, its production, but during recent: sears has exported varyiug quantities in 1929. 2,200 ton-: in 1930, 2,700 tons, and in 1931. 3,600 ton-. Aside from the-e two countries, the international market has heretofore been free. It and when the British Empire duty become, effective the world's markets will be divided into four unit: 1. Russia and Japan, 2. United States. 3. British Empire. 4. Rest of the world. The world's production at present is rennin it the rate of 930.000 tons per annum. This year's production will be over 1,000,000 tons because the several curtailment did not become effective until the second quarter. consumption will be slightly in excess. Deducting from 30,000 tons Russia's and Japan's production of 121.000 tons, 806,000 tons is left divided a, follows:

Jan 1, 1932

By David L. Pentz

This paper discusses exploration objectives and requirements for a nuclear repository in the U.S.A. The importance of designing the exploration program to meet the system performance objectives is emphasized and some examples of the extent of exploration required before the License Application for Construction Authorization is granted are also discussed.

Jan 1, 1984

By J. T. Burwell

The crystal orientation in silicon iron that has been given a particular treatment described by Goss,l has been studied by Goss, by Bozorth2 and by Sixtus,3 but their results do not agree and are almost entirely qualitative. The following pages give a description of the orientation of the crystals in the material as determined by means of X-rays and expressed graphically in a pole figure. The treatment consists of hot-rolling the material into strip and then giving it two cycles of cold reduction followed by recrystallization. This produces remarkably good properties in the rolling direction, the product having a maximum permeability in this direction of more than 25,000 and a permeability at 16,000 Gauss of more than 2200. It is now generally agreed that Goss's original conclusion1 that the crystals in the final product are randomly oriented was incorrect, since Bozorth2 and Sixtus,3 using different methods, have shown that there is a decided preference in orientation. Those writers, however, expressed their results only in terms of one or more ideal orientations with deviations therefrom. X-ray Data A strip of the material containing 3.1 per cent Si, prepared by Goss,† 1.2 by 0.0125 in., was etched rapidly in warm dilute hydrochloric acid until it was 0.005 in. thick, in order to eliminate the effect of the two surface layers. The specimen was then mounted in an integrating camera similar to one described in the literature.4 The purpose of this camera is to translate the specimen during exposure, so that a statistically large number of grains contribute to the pattern photographed. The camera also allows the plane of the specimen to make various angles with the X-ray beam. An area 5 by 1.2 in. was scanned by a beam of unfiltered radiation from a molybdenum target tube operating at 37 kv., and the measurements were made principally on the peak of the white radiation. X-ray photographs were taken at intervals of 15" in a plane

Jan 1, 1940