By C. E. Lundin, M. Hansen, D. J. McPherson

PRIOR work on the Zr-Cu phase diagram by Alli-bone and Sykes,' Pogodin, Shumova, and KUGU cheva,' and Raub and EngeL3 as confined largely to copper-rich alloys. The investigations of Raub and Engel were the most recent and seemingly the most complete of these. Alloys from 0 to 68.3 pct Zr were studied principally by thermal analysis and microscopic examination. These authors reported an inter metallic compound ZrCu, (1116°C melting point) and two eutectics, one at 86.3 pct Cu (977°C mp) and the other at 49 pct Cu (877°C mp). The solubility of zirconium in copper was reported to be less than 0.1 pct at 940°C. The zirconium melting stock consisted of Westing-house "Grade 3" iodide crystal bar (nominally 99.8 pct pure). It was treated by sand blasting and pickling (HF-HNO, solution) to remove the surface film of corrosion product, resulting from grade designation tests. The crystal bar was cold rolled to strip, lightly pickled again, and cut into pieces approximately 1/32 in. thick and 1/4 in. square. These were cleaned in acetone, dried, and stored for charging. The high-purity copper (spectrographic grade) was supplied by the American Smelting and Refining Co. with a nominal purity of 99.99 pct. These copper rods were rolled to strip, cut into squares the same size as the zirconium platelets, cleaned in acetone, dried, and stored. Equipment and Procedures The equipment used for melting and annealing the zirconium binary alloys and for the determination of solidus curves has been described in connection with previous work on the Ti-Si system' and in recent papers in this series describing the studies on eight binary zirconium systems.5-' Techniques employed for preparing and processing the alloys were also similar to those used in the above references. Ingots of 20 g were melted under a protective atmosphere of helium on water-cooled copper blocks in a nonconsumable electrode (tungsten) arc furnace. The ingots were homogenized and cold-worked prior to isothermal annealing to aid in the attainment of equilibrium. The specimens were heat-treated in Vycor bulbs sealed in vacuo or under argon, depending on the temperature of the anneal. Quenching was accomplished by breaking the Vycor bulbs under cold water. Temperature control was within ±3OC of reported temperatures. Thermal analysis was primarily relied on to determine eutectic levels, peritectic levels, and compound melting points. The induction furnace incipient melting technique was also used but did not provide the accuracy obtained by thermal analysis in this system, which involves much lower solidus temperatures than the other zirconium systems. A special technique for the determination of characteristic temperatures was employed in the case of several intermediate phases and their eutectics which displayed very small differences in melting temperatures. Specimens were sealed in Vycor bulbs and annealed at a series of very accurately controlled temperatures. Metallographic examination was then employed to reveal incipient melting. Furnaces and techniques in general were described previously.' The echant used was 20 pct HF plus 20 pct HNO3 in glycerine unless otherwise stated. Results and Discussion The chemical analyses of the majority of alloys prepared for the determination of phase relationships in this system are given in Table I and a brief summary of the equilibrium anneals employed is given in Table 11. In a preliminary program, alloys containing 1, 4, and 7 pct Cu were annealed for three different times at each of the temperatures 700°, 800°, and 900°C. No change in the relative amounts of phases present was detected after 350, 150, and 75 hr at the above temperatures, respectively. The times listed in Table II were accordingly chosen as a result of these preliminary tests. Zirconium-rich alloys containing from 0.1 to 10 pct CU were reduced by cold pressing from 58 to 8 pct, depending upon thk alloy content, homogenized for 7 hr at 900°C, and then reduced 80 to 13 pct by cold rolling, again depending upon copper content. Other alloys were studied in the cast, or cast and annealed conditions. The contracted scope of investigation for this system included the range 0 to 50 atomic pct Cu. This approximate region is shown in Fig. 1. Due to evidence of phase relationships departing considerably from those proposed by Raub and Engel" in the 50 to 100 atomic pct range, the investigation was extended to cover this composition area rather thoroughly also. Fig. 2 is a drawing of the entire diagram. The labeling of some phase fields was omitted in Fig. 2 for the sake of clarity. An expanded view of the zirconium-rich region, with the experimental points necessary for its construction, is given in Fig. 3. The generally accepted value of Vogel and Tonn8 or the allotropic transformation a + 862' ±5OC, was employed in the construction of these diagrams. A careful study revealed that the "Grade 3" crystal bar used in this investigation actually transforms over the approximate range 850" to 870°C, due to impurities. It must be expected that this two-phase field in unalloyed zirconium will cause some departures from binary ideality in the very dilute alloys. Zirconium-rich Alloys: The a + ß transformation temperature is decreased from 862" to about 822°C by increasing amounts of copper. Thus, a eutectoid reaction, fi ß a+ Zr,Cu, occurs at a composition of about 1.6 pct Cu. The eutectoid level was determined to lie between the alloy series annealed at 815" and 830°C. The placement of this eutectoid temperature

Jan 1, 1954

By Jacques Steininger, Robert E. England

Single crystals of ZnTe and ZnTe1-,Sex with x up to 0.13 have been grown from the elements by temperature gradient solution zoning using excess tellurium as a solvent. Best results have been obtained with charges with the compositions 45/55 at. pct Zn, Te, for ZnTe and increasing amounts of selenium for ZnTe1-xSex. The temperature in the molten zone was maintained at about 1070°C with a gradient of about 10°C per cm. Chemical analyses of quenched ZnTe ingots show tellurium concentrations in the molten zone as high as 70 pct with concentration differences across the zone of 1 to 2 at. pct Dark dots which are observed by transmitted light microscopy in as-grown crystals can be removed by annealing in zinc vapor at 900 C. INTEREST in wide band gap semiconductors has led to a new study of ZnTe and ZnTel-xSex crystal growth. ZnTe is the only II-VI compound with a wide band gap (2.3 ev) that can be made p type with low resistivity. Attempts to make it n type with low enough resistivity to be useful for p-n junctions have so far been unsuccessful.1 ZnSe has a band gap of 2.65 ev but can be made n type only. However, ZnTel-xSex solid solutions with x as low as 0.36 have been made both highly n and p type2 with a minimum band gap around 2.12 ev3 at room temperature and appear to hold the best promise for efficient injection electroluminescence in the visible. ZnTe has the lowest melting point of the zinc chal-cogenides (1295°C) and consequently attempts have been made to grow crystals from both the liquid and the vapor phase.4 Complicated apparatus is required for growth from stoichiometric melts because of the high vapor pressures of the elements at the melting point of ZnTe and because of the problem of quartz devitrification. Small crystals have thus been grown in high-pressure equipment by Fischer5 and by Narita et a1.6 with pressures of the order of 50 atm of argon to prevent excessive evaporation from the melt. Large crystals of ZnTe can be obtained by growth from the vapor phase4 but they often present numerous dislocations and inclusions. An improvement in the quality of vapor- grown ZnTe crystals was reported by Albers and Aten7 by equilibration of mixtures of small crystals with compositions lying on either side of the solid single-phase field at fixed temperature. The same technique was later applied by Aten8 to the growth of ZnTe1-xSex crystals with less than 1 pct inhomo-geneity. Because of the higher liquidus temperatures of the solid solutions and the high vapor pressure of selenium, previous attempts to grow ZnTel-xSex from the melt have been limited and unsuccessful.9 The phase diagram of the Zn- Te system is reproduced in Fig. 1, based on data from Kobayashi10 and Kulwicki.11 Carides and Fishher12 have reported lower liquidus temperatures on the tellurium-rich side, but their data would require confirmation. The liquidus temperature on the tellurium-rich side decreases rapidly with increasing tellurium concentration and the Te2 vapor pressure over the liquidus also decreases accordingly.'3 The decrease in liquidus temperature and vapor pressure therefore makes it possible to use conventional apparatus if there is a sufficient excess of tellurium in the melt. Single crystals of ZnTe have thus been grown by Kucza,14 in a modified Bridgman technique, from solutions containing up to 60 at. pct of Te by lowering unsupported quartz ampoules through a temperature gradient at about 1200°C. Under these conditions, the phase diagram indicates that the entire charge is initially molten. Crystal growth can therefore proceed by normal freezing and rejection of excess tellurium into the melt. The modified Bridgman technique has several major limitations. Because of the rejection of excess tellurium into the melt during freezing, the melt composition and the temperature at the growth interface vary continuously. They tend to follow the liquidus until the eutectic which is very close to pure tellurium (447°C, >99 pct Te). Since the solidus composition also varies with temperature,15 crystals grown by this method are inhomogeneous. They present small variations from stoichiometry which may affect their structure and physical properties. The simultaneous increase in tellurium content and decrease in melt temperature also combine to reduce the rate of diffusion of tellurium away from the growth interface, thereby causing constitutional supercooling and possibly dendritic growth. To minimize these effects, the initial melt composition is in practice kept relatively close to stoichiometry (less than 60 pct Te). This however limits the possibilities of operating at low temperatures and pressures. This paper describes a modified method of crystal growth by temperature gradient solution zoning (TGSZ) which is an adaptation of the temperature gradient zone-melting technique developed by pfann16 and of the traveling solvent method of Mlavsky and weinstein.I7 The TGSZ method now applied to the growth of ZnTe and ZnTel-xSex crystals is characterized by its very simple experimental arrangement and sample preparation technique. Unlike the modified Bridgman technique, there is no increase in the tellurium concentration in the melt and therefore it is possible to operate at lower temperatures and pressures. This method is also suitable for maintaining a constant temperature at the growth interface.

Jan 1, 1969

By S. A. Braley

DRAINAGE water from coal mines is probably the most serious water pollution problem today, varying in importance according to location of the mines and geological structure. Drainage may be either acid or alkaline in character. Acid discharge, the most severely detrimental to a stream, is caused by natural oxidation of the sulfuritic material (FeS2) in the strata associated with the coal seam. Since the acid is the result of a natural reaction the acid water differs because it does not cease with abandonment of the mining operations. There is no known economical method of neutralizing acid mine water or any practical method to prevent oxidation of exposed pyrite. Since production of acid from a mine does not stop when mining stops, the total quantity produced depends entirely upon the excavated areas. The increasing volume of acid water in manv mines has greatly increased operating costs. Pumping is expensive and acid mine waters are destructive of all equipment, especially metals in pumps and piping, and necessitate the use of corrosion-resistant materials. Discharge of the acid mine drainage into streams neutralizes their normal alkalinity, causes them to become acid, and produces an environment unfavorable for aquatic life and unsuited for industrial or domestic use without costly treatment. Mine drainages vary in percentage composition over wide limits, although the usual dissolved substances are ferrous and ferric iron, aluminum, calcium and magnesium sulfates, and lesser amounts of sodium, potassium and manganese sulfates and chlorides. Some alkaline discharges may contain heavy concentrations of iron as iron bicarbonate. These waters may produce iron hydroxide deposits in the receiving stream but do not cause it to become acid. In the extensive literature on acid mine water there appears to be a great deal of confusion about the importance of various components and the methods for their determination. In many instances faulty conclusions have been drawn from use of unsuitable methods of analysis. It is desirable that the factors and terms used in evaluation of analyses of mine waters should be so clearly defined that any interested person could properly appraise any analytical report. Some analysts report complete chemical analyses of mine waters and neglect to record drainage volumes. Others report only a minimum of analytical data after taking no precautions to preserve the original composition of the water during the time elapsing between collection and analysis. Some use methods of analysis intended for so-called pure waters of the potable and boiler water classes. These methods are not applicable to highly buffered waters such as mine water. Probably the most common criteria for evaluation are pH, free acidity, or acidity or alkalinity to methyl orange or methyl red, total acidity or acidity to hot phenol-phthalein, and the sulfate content. If these determinations are made on carelessly collected samples after a few days to weeks standing in warm rooms, they do not in any way represent the character of the water flowing from the mines. It is hoped that a brief discussion of the fundamental value of some of these factors may lead to a bettqr understanding of the need for more careful evaluation of mine water discharges. The term pH is one used by chemists to express relative acidity or alkalinity in terms of concentration of effective hydrogen ion in a solution. It is defined as the negative logarithm of the hydrogen ion concentration or activity in equivalents per liter. pH = logarithm A neutral solution, which is one containing the same number of hydrogen and hydroxyl ions, has a pH of 7. As the hydrogen ions increase and the solution becomes more acid, the pH decreases toward zero; and as the hydroxyl ions increase and the solution becomes more alkaline, the pH approaches 14. When dissolved in water to a dilute solution acids like sulfuric and hydrochloric, commonly known as strong acids, ionize completely, and the pH or hydrogen ion concentration varies with molar concentration of the dissolved acid. However, in high concentrations of such acids, the pH or hydrogen ion concentration is less than the acid concentration because the acid does not completely ionize. In only very dilute solutions does the pH represent the total amount of acid that can be neutralized by an alkali. All ionization reactions are equilibrium reactions. If other chemicals are added to the solution of an acid and the added chemical produces an ion that is the same as one of the ions of the acid, the degree of ionization of the acid is altered and the pH changes to some value that represents the active hydrogen ion of the new solution. Thus if iron sulfate is added to a solution of sulfuric acid the pH increases, since the common sulfate ion suppresses the degree of ionization of the sulfuric acid and decreases the effective hydrogen ion. However, the total acidity of the solution is increased. There are two salts composed of iron and sulfate— ferrous and ferric sulfate. In these salts there is no hydrogen ion that can ionize to give an acid solution, but when they are dissolved in water, the pH is less than 7 and the solution becomes acid. This is caused by a reaction known as hydrolysis and is represented by the equations FeSO4 + 2H2O ? Fe(OH)2 + 2H + SO,: or Fe,(SO,)3 + 6H2O ? 2Fe(OH)3 + 6H+ + 3504 A solution with a total acidity of 5000 ppm according to the first equation will have a pH of 4.40 but one with an acidity of 75 ppm, according to the sec-

Jan 1, 1958

By E. Mille, R. Geffken

The Mg-Si and Mg-Ge phase diagrams were rede-levtnined by thermal analysis, and the existence of a single congruent melting compound in each system was confirmed. The melting points of the two compounds Mg2Ge and ,Wg2Si were found to be 1117.4° and 1085.0°C respectively. The euteclics for the Mg-Ge system occur at 635.6°C (1.15 at. pcl Ge) and 696. 7°C (64.3 at. pct Ge); for the Mg-Si system the eutectics are at 6376°C (1.16 at. pct Si) and 945.6°C (53.0 al. pcl Si). The phase diagrams and known thermodynamic data were used to calculate activity values for both systems. The activities calculated for the Mg-Ge system agreed very well with those previously published. Partial molar enthalpy values for the Mg-Si systetn were calculated from the phase diagram for the composition region where no experimental values have been reported. THE phase diagram for any system is an important source of thermodynamic data. Steiner, Miller, and Komarek1 have derived equations which permit calculation of the activity in binary systems with an inter-metallic compound! if the liquidus and enthalpy data are known. The thermodynamic properties of the Mg-Ge and Mg-Si systems have recently been determined in this by by an isopiestic method, and it was considered that it would be interesting to compare these directly determined values with those computed from the phase diagram. The basic features of the Mg-Ge and Mg-Si systems are essentially similar. The one intermediate compound present in each system. Mg2X, crystallizes in the antifluorite structure and melts congruently. Raynor4 has accurately determined the temperature and composition of the magnesium-rich eutectic in both the Mg-Ge and Mg-Si systems. Klemm and West-linning5 investigated the entire Mg-Ge liquidus, employing sintered alumina crucibles; the purity of the magnesium and germanium starting materials was not reported. The melt was not stirred, and the temperature was automatically recorded to an accuracy of ±3°C. The authors reported large weight changes due to magnesium evaporation between 50 and 67 at. pct Mg. The Mg-Si system has been studied by a number of investigators, and the results have been compiled by Hansen and Anderko.6 Significant discrepancies exist between the two principle investigations of voge17 and Wohler and Schliephake.8 Two different grades of silicon were used by Vogel, one of 99.2 pct purity and the other quite impure, containing 6 pct Fe and 1.7 pct Al. The magnesium purity was not specified. The melts were contained in graphite crucibles with porcelain thermocouple protection tubes under an atmosphere of hydrogen. Samples weighing 10 g were rapidly heated to 50° to 100°C above the liquidus: held, and then rapidly cooled without stirring. Accuracy was ±1 at. pct which is equivalent to a maximum error in temperature of ±18°C. Wohler and Schliephake used 97.9 pct Mg and 99.48 pct Si. The graphite crucibles contained a stirrer and the 15-g samples were melted under an atmosphere of streaming hydrogen. The samples were chemically analyzed after each run. Because of the scarcity of the data, the impurity of the starting materials, and the resultant uncertainty and inconsistency in the published liquidus values, it was decided to undertake a reevaluation of the Mg-Ge and Mg-Si phase diagrams by thermal analysis. EXPERIMENTAL PROCEDURE Alloys were prepared from 99.99+ pct Mg (Dominion Magnesium Ltd.) with impurities in ppm: 20 Al, 30 Zn, 10 Si, <1 Ni, <1 Cu. <10 Fe; 99.999 pct Ge (United Mineral and Chemical Corp.), and 99.999 pct Si (Wacker Chemie Corp.). All graphite parts were machined from high-density (1.89 g per cu cm) G-grade graphite obtained from Basic Carbon Corp. with a total ash content of 0.04 pct. Boron nitride parts were machined from rods of National-grade H.B.N. boron nitride. All graphite and boron nitride pieces were baked out under running vacuum at 1100°C for 24 hr before us Cylindrical graphite crucibles (1; in. OD, 23/4 in. long, l3/8 in. ID) were tightly closed with threaded graphite covers which had 21/4-in.-long thermocouple wells and 1/4-in.-diam off-center holes for stirrers. The cover and thermocouple well were machined from a single piece of graphite. A stirrer was made from a flat cylindrical graphite plate perforated with five 3/16-in.-diam holes and a 1/2-in.-diam central hole, and was held parallel to the crucible bottom by a 1/4-in.-diam. 4-in.-long graphite rod which screwed into the plate and extended up through a tightly fitting hole in the crucible cover. An iron core enclosed in a glass capsule was attached to the stirrer with an 18-in.-long molybdenum wire, so that the stirrer could be magnetically raised and lowered from outside the system. One crucible and stirrer with essentially the same dimensions given above was made entirely of boron nitride. Chunks of magnesium were premelted, cast into 11/2-in.-diam. rods, and then cut into lengths varying from a to 1 in. A 5/16-in. hole was drilled through the center of each piece to accommodate the thermocouple well and the individual pieces were then cleaned and rinsed with acetone. The total weight of an alloy was 50 to 70 g in the Mg-Ge system and 40 to 60 g in the Mg-Si system. The pure components were weighed to an accuracy

Jan 1, 1969

By Ashok K. Sinha

During the course of an in~*estigation into the occurrence of ordered AB3 structures, the following new phases have been found —CrRh3 (AuCu3 type), CrCo3 (MgCd3 type), HfCo4 (Ths Mn23 type), and WPt, MoPh type). The composition of the TiPt3-x phase (TiNi, type) is close to Ti23Pl77. The alloy chenzistry of transition rnetal AB3 structures is rezliewed in the light of electron concentration correlations of hex-agonality recently obtained for quasi-binary alloys. The relatizte colurne contraction in the AB3 structures increases with increasing difference in volume of the conzponents. A family of ordered close-packed layered structures is formed by stacking identical layers of composition AB, in various sequences, such that the coordination is twelvefold throughout and there are no A-A contacts. Previous work&apos; on quasi-binary AB3 alloys has led to the conclusion that the stacking sequence of the AB, structures changes with increasing radius ratio RA/RB from a purely cubic, through different mixtures of hexagonal and cubic stacking to a purely hexagonal stacking. However. for binary AB3 alloys, a correlation between the type of the crystal structure and the position of the components in the various volumns of the periodic table has been noted.2-5 It has been noted6 that this correlation appears to hold even though the radius ratio RA/RB may vary over a considerable range with the location of the components in the three long periods. Another study7" of several quasi-binary systems led to the conclusion that an increase in hexagonality of the stacking is associated with increase in the electron concentration e/a. as defined by the average per atom of the total number of electrons outside the inert gas shells. In apparent conflict with this conclusion, it is known that seven binary alloy structures isotypic with TiNi3 which is 50 pct hexagonal occur at a higher electron concentration (e/n = 8.5) than that (e/a = 8.25) for the 100 pct hexagonal MgCd3 type structure present in seven binary AB3 alloys. Table 111. In the present work, an investigation into the occurrence of binary AB3 structures in transition metal alloys was made, and a survey of binary AB3 structures is presented. EXPERIMENTAL The starting materials were pure metals of 99.9 wt pct purity. The alloys were arc-melted under partial pressure of argon and annealed in sealed silica capsules lined with molybdenum foil under argon at- mosphere. The total weight loss upon melting and subsequent annealing was always less than 1 pct and hence the alloys will be referred to by their intended (unanalyzed) compositions. Wherever the constitution permitted. the alloys were given a homogenizing treatment at 1200°C (3 days) prior to annealing. Unless otherwise stated all alloys were annealed at 900°C for 1 week and water-quenched. Sometimes the final annealing treatment was carried out on powders to accelerate the attainment of equilibrium. X-ray powder patterns were taken using a Guinier-de Wolff focusing camera (CuK, radiation) or an asymmetrical focusing camera (Co or CrK, radiation). For lattice parameter determination. internal silicon standards were employed. The intensity calculations were made using a Fortran IV program written by Jeitschko and parthe.9 RESULTS Twenty AB3 and three AB4 alloys were investigated. Table I lists the crystallographic data on some of the intermediate phases encountered in the present work. Table II contains the X-ray data for HfCo, (Th,,Mn,, type). The positional parameter, x. was assumed to be 0.378. the value for Th6Mnn2310 The X-ray pattern of ZrCo, was very similar to that of HfCo, and the previous structure determination of ZrCo, by Kuzma el al." was confirmed. Ordering in the alloy CrCo could be ascertained by the presence of only one weak super lattice line (101). the others being too weak presumably owing to the small difference in the scattering powers of chromium and cobalt. This line was observed in the X-ray pattern of powder from the massive sample annealed at 830°C (7 days) after the powder had been reannealed at 600°C (24 hr). The diffraction pattern of the powder similarly reannealed at 830°C (24 hr) contained only the lines due to a mixture of hcp and fcc Co(Crj solid solutions. Therefore, it appears reasonable to assume that O2 and/or N2 contamination which would be less likely to occur during the 600°C anneal was not responsible for the observed weak reflection. Also. this reflection cannot be identified with any of the strong lines of the neighboring s phase which is present in the Co-Cr system at higher chromium contents. The composition corresponding to the TiNi3 structure observed by Raman et al.12 in the two-phase alloy Ti,zt,, has been established in the present work as being between There was satisfactory agreement for the low-angle lines (up to d = 1.997A) between the observed diffraction pattern of TiCua and that calculated assuming the ZrAu, structure. as recently proposed by Pfeifer-et a1.I3 However. some of the superlattice lines. e.g., at d = 1.937 and 1.919A. predicted by the ZrAu, structure were not actually observed eve? though neighboring lines. at d = 1.947 and 1.986A. of comparable calculated intensity were present. The ZrAu

Jan 1, 1970

By O. F. Walker, W. C. Hahn, V. A. Johnson, J. D. Wood

The diffusion coefficients of zinc in single-crystal zinc and carbon in single-crystal and poly crystalline nickel were measured by means of radioactive tracer techniques both with and without the application of ultrasonic vibrations under conditions such that the temperature of the sample was closely controlled. The results of this investigation indicate no enhancement of diffusion in any of the samples. It is suggested that previously reported enhancement may have been due either solely to temperature increases caused by ultrasonic vibrations or in combination with changes in the boundary conditions. A number of observations have been reported in the literature in which it has been implied or inferred that the application of ultrasonics enhances diffusion (see, for example, Refs. 1-5). The present study was undertaken in an attempt to observe this effect under carefully controlled conditions, particularly with regard to measurement and control of the temperature of the sample. Two different types of systems were studied; these were the self-diffusion of zinc and the diffusion of carbon in nickel. EXPERIMENTAL For diffusion with ultrasonic energy applied, the samples were included as part of a resonant ultrasonic system operating at 58.5 kcps. The ultrasonic generators used were rated at 100 and 250 w and could be tuned over a frequency from 10 to 100 kc. A PZT (lead titanate/lead zirconate) ceramic transducer provided the driving vibration. This system requires no metallurgical joining of the specimen to the acoustical transmission line since the ultrasonic driver and the follow-up section clamp the specimen in position by means of a constant pressure of 50 lb developed by an air cylinder. The ultrasonic driver and follow-up section, both made of titanium, were 4 in. in length from clamping point to the end in contact with the specimen. Using the relationship given by Mason,6 A = V/f, the resonant wavelength, A, in titanium is calculated to be 3.3 in. at a frequency, f, of 58.5 kc, taking the velocity of sound in titanium, V, as 1.95 X 105 in. per sec. The 4-in. driver and follow-up section, therefore, are each 4.0/3.3 =1.21 times the resonant wavelength. Clamping pressure must be applied at stress nodes of the transmission line in order to preserve resonance. Therefore, a specimen length of 0.58 times the wavelength in the specimen was required to place the clamping pressure application points at stress nodes exactly three wavelengths apart. A stress antinode was contained in the center 3 in. of the specimen. A small PZT ceramic disc attached to the follow-up section provided an output voltage proportional to the intensity of the standing wave. This output voltage was monitored on an oscilloscope and the ultrasonic system was tuned to resonance by varying the frequency until the output signal was a maximum amplitude. The amplitude of the output signal was maintained constant throughout the diffusion anneal. A split cylindrical stainless-steel chamber, which was purged with argon prior to and during the runs, was placed around the specimen. The chamber in turn was surrounded by a movable furnace whose temperature could be controlled to 7C. Heat exchangers were used to cool the driver, follow-up section, and ultrasonic transducer. Great care was taken to obtain the true specimen temperature in all cases. Several different methods were tried; the most successful was that in which the thermocouple was held in contact with the midlength of the specimen by means of an asbestos insulating pad and wire straps. In the case of zinc, single-crystal specimens of 99.999 pct purity were used. The samples were 0.25 by 0.25 in. square and of the proper length for resonance, that is 1.1 in. long with the c axis parallel to the long dimension of the specimen for the case of diffusion perpendicular to the c axis and ultrasonic motion parallel to the c axis, and 1.9 in. long with the c axis perpendicular to the long dimension of the specimen for the case of diffusion parallel to the c axis and ultrasonic motion perpendicular to the c axis. In each case, one of the rectangular faces was electroplated with a thin film of zinc containing Zn The constant pressure used to clamp the specimen in place in the ultrasonic system caused some deformation in some of the samples. For these samples the deformation was concentrated in either end of the specimen; thus, for all samples (both zinc and nickel) the center in. was cut from the specimen after the diffusion anneal to be used for sectioning and counting. The nickel single-crystal samples, of 99.999 pct purity, were used in the form of rods 0.25 by 0.187 by 2.07 in. long with the (100) direction parallel to the rod axis. The polycrystalline nickel samples of 99.97 pct purity had an average grain diameter of 0.007 in. and were used in the form of rods 0.25 by 0.125 by 1.87 in. long. The direction of ultrasonic motion was parallel to (100) direction (bar axis) for the single-cqstal samples and parallel to the bar axis for the polycrystalline specimens. A thin film of c14 suspended in methanol was applied to the diffusing face of the specimen. Two specimens were butted together lengthwise for each diffusion anneal to minimize oxidation. After diffusion, a precision lapping device similar to the one described by Goldstein7 and a radiation detector were used to obtain a plot of specific activity vs penetration distance for each specimen. (A scintil-

Jan 1, 1969

By Karl A. Bauer, Cornelis Bezemer

The deposition of calcium carbonate scale on surface and subsurface production equipment creates an operation problem in many oil fields. The formation water in which the carbonate-scale-forming components are initially dissolved becomes supersaturated with calcium carbonate as a result of the drop in pressure during production. The continuous flow of a supersaturated solution through the production equipment results in the growth of a dense layer of calcium-carbonate crystals. For a scale layer to be built up, the supersaturated formation water should contact the walls of the production equipment. The tendency for scale to be deposited, therefore, will be low, if the crude has a low water cut and if the water is finely dispersed in the oil. A scale problem will occur, if at a high water cut part of the water is present as free water. The rate of scale deposition will then be approximately proportional to the rate of free water production. Depending upon where the formation water becomes supersaturated, scale may be deposited in the flow line only, in both flow line and tubing, and in some cases even in the perforations and in the formation near the wellbore. In the South Sumatran fields (Indonesia) the main difficulties encountered due to the deposition of calcium-carbonate scale have been restriction of flow through tubings and flow lines, wear and abrasion of plungers and liners, and stuck plungers or wellhead valves. So far, the only methods of combating the *Presently associated with Brunei Shell Petroleum Co., Ltd.. Seria. scale problem have been routine acidizing and additional well pulling. As for the pumping wells, it was estimated that some 50 percent of the total well-pulling effort was directly attributable to scale deposition. The most promising alternative was to prevent the deposition of calcium carbonate scale by means of chemicals. Inorganic polyphosphates such as sodium hexametaphosphate and trisodium polyphosphate are known to retard the formation of scale by the "threshold action". They are adsorbed on specific faces of the crystal nuclei and thus prevent crystal growth, thereby stabilizing supersaturation. Polyphosphates are effective at very low concentrations ( a few ppm), and far less than stoichiometric quantities are required to keep the scaling ions in solution. Recent investigations on barium sulfate scale1 have confirmed this mechanism. The types of polyphosphate mentioned can be applied as concentrated aqueous solutions either squeezed into the formation, lubricated down the annulus or injected via macaroni string. Several squeeze jobs with polyphosphate solutions have been carried out in the South Sumatran fields, however, with disappointing results. Lubrication down the annulus and injection through a macaroni string were not considered attractive in this area because of the kind of equipment and the degree of supervision these techniques require. Polyphosphates are also available in a granular, glassy form, which, in contrast with the readily soluble types already mentioned, show an extremely low

Jan 1, 1970

By M. Prats

Most of the information available on the heat efficiency of hot fluid injection processes, both water and steam, has been obtained from calculated temperature distributions in the pay zone and adjacent formations. The usual approach has been to write the heat balance equations in terms of the temperatures, and then to introduce whatever simplifications are necessary to help obtain an analytical or a numerical solution. In either case, the assumption has often been made that the vertical thermal conductivity in the flooded interval is infinite, so that the temperatures within the flooded interval are then independent of vertical position. Because it was first made by Lauwerier,l and has been used extensively since, this assumption will be referred to as the Lauwerier assumption. Excellent reviews of the literature on the heat efficiency of hot fluid injection processes have been given by Spillette,2 Flock et al.,3 and Ramney.4 Of course, the most significant contributions take into account the effect of a finite vertical thermal conductivity on the vertical temperature profile. The most general analytic expression for the heat efficiency of a hot fluid injection process is that of Antimirov5 who considers injection of a heated incompressible fluid into a reservoir through an arbitrary number of wells. The rate of heat injection into the reservoir, as well as the injection temperature, is an arbitrary function of time. The geometry of the horizontal flow is arbitrary, although the reservoir is considered to be of uniform thickness and properties and to be of infinite areal extent. Heat transfer within the reservoir is by horizontal convection and conduc- tion, and by vertical conduction. In the formations adjacent to the flooded interval, heat transfer is by conduction in any direction. Thus, the available expression for the heat efficiency due to hot water injection has been developed for rather general conditions. This degree of applicability has not been obtained for other thermal recovery processes. By making the Lauwerier assumption we have been able to obtain expressions for the heat efficiency that are essentially independent of the thermal recovery process, be it steam, hot-water, or underground combustion. Clearly, then, the approach followed here is more restrictive than that of Antimirov5 in that it uses the Lauwerier assumption. At the same time less restrictive assumptions are made about the horizontal heat transfer mechanisms, either in the flooded interval or in the formations adjacent to it. The main difference between our approach and that of other investigators is that the heat balance in the pay zone is expressed for the pay zone as a whole rather than for a volume element within it. The Lauwerier assumption is introduced after the problem is developed along these lines as far as possible. The details of the development of the heat efficiency are given in the Appendix, while the main features of the model are discussed in the next section. Results and their implications are discussed later in a separate section. The Model Certain assumptions have been made to determine

Jan 1, 1970

By Mehmet Guney

At the Armatcuk mine in Turkey, various modifications of sublevel methods have been tried during the last decade in an effort to eliminate gob fires, dangers from roof falls, and surface subsidence, and also to increase extraction efficiency. From the experience thus gained, it was decided that the most likely system to give maximum benefits, considering the existing geological conditions and coa1-seam characteristics, was hydraulic stowing. This paper examines trends in the working techniques of hydraulic stowing and discusses the favorable results and technical problems that the method produced at Armutcuk. The Armutcuk mine, a subsidiary of Eregli Coal Mines (EKI), produces 1300 tons of run-of-mine coal daily from thick (about 10-90 ft) and highly dipping (about 50-90°) coal seams. The coal is highly volatile with good coking properties that make it highly suitable for industrial use. Most of this coal is used in the iron and steel industry at Eregli on the Black Sea coast. Complete recovery of the coal is of vital importance to industrial development and progress. Initial coal extraction was carried out by means of a sublevel mining system modified to accommodate local geological conditions and coal seam characteristics. This method is similar to that employed in metalliferous mines. Several problems arose from the application of the method, one of them being the prevalence of gob fires which caused periodic shutdowns in some sections. To achieve maximum coal extraction with minimum dilution, to eliminate gob fires and surface subsidence, and to reduce fatal accident rates, a decision was taken to change from this method to a hydraulic stowing system. The pres- ence of large deposits of conglomerate and sandstone on the surface contributed to the decision to employ this new method. Although hydraulic stowing practices have been carried out in America and Germany, Upper Silesia may, so far as coal is concerned, be considered the birthplace of the method. Here the process was adapted to thick coal seams on a large scale to reduce dangers from gob fires and damage from surface subsidence. Today, the mining system is not only widely used in the coal mines of France, the Saar, India and Poland, but has also been successfully applied to the iron ore and potassium salt mines in Russia and Germany. LOCATION AND HISTORY The Kandilli-Armutcuk coal field, the most western outcrop of the North Anatolian coal basin, extends for five miles along the Black Sea coast (Fig. 1). The Armutcuk Mine is situated on the southern boundary of the coal field about 40 miles from Zonguldak and about 12 miles from Eregli. The history of coal mining in the North Anatolian coal basin goes back more than a century. Mining commenced on a small scale in the Kandilli-Armutcuk coal field in the late 1880&apos;s, and from this time until nationalization in 1940 the mines were operated by private Turkish and foreign interests. In 1940, Eregli Coal Mines was established to takeover the management of these enterprises. The Armutcuk Mine was developed for the first time in the mid-1940&apos;s. Since then it has been in continuous production and it now produces an annual 440,000-ton run-of-mine output from which 320.000 tons of salable coal is obtained. MINE GEOLOGY The carboniferous inlier of the Kandilli-Armutcuk coal field crops out over an area about three miles long and one mile wide. The major part of the inlier consists of the Namurian formation with only a relatively small area of Westfalian-A visible on the surface (Fig. 2). The Namurian formation, which has no exploitable coal seams in the Armutcuk Mine, consists mostly of arkose sandstones and black shales often having

Jan 1, 1969

By R. M. Hays

At the present time, oxidized taconite and semitaconite are not processed on the Mesabi Range except in vely limited tonnages. However, it is estimated that by 1990 shipments from the Range will approach 75 million tons of iron ore per year. To achieve this and future production, either additional magnetic taconite reserves must be proven or oxidized taconite and semitaconite must be processed. One beneficiation process which uses high-intensity magnetic separation and flotation for concentrating oxidized taconite and semitaconite is described. Detailed metallurgical results are given and an economic evaluation of the process is presented with comparison to other processes. The results of the present study indicate that the high-intensity magnetic separation and flotation process appears nearer commercialization for the processing of Mesabi Range semitaconite. The disadvantages of the process are nearer solution and are being solved by well-defined programs. During the twentieth century, the Mesabi Range in northeastern Minnesota has been the main source of iron ore for American steel mills. The Mesabi Range, which is about 120 miles long and up to 3 miles wide, is the pre-glacial outcrop of a group of sedimentary iron-bearing rocks known as the Biwabik formation. The formation, which is 200 to 650 ft thick and dips 50 to 10° to the southeast, is divided into four stratigraphic units. From top to bottom, these are the Upper Slaty, Upper Cherty, Lower Slaty, and Lower Cherty. Since its deposition in Precambrian time, most of the original Biwabik formation has been subject to alteration. Thus, although the iron content of the original formation was quite uniform, major variations in mineral composition now occur both laterally along the length of the formation and vertically within its units. Details of the mineralogical variations in the Biwabik formation have been described by Wolff,&apos; Gruner, 2 and White.3 The unaltered portion of the Biwabik formation includes the magnetite taconites which are being commercially processed by Reserve Mining, Erie Mining, Eveleth Taconite, National Steel, Butler Taconite, and U.S. Steel. These six operations have a capacity of 32 million tons of iron ore pellets per year and have produced approximately 170milion tons of pellets since 1956. Capacity for another 30 million tons of pellets per year is being considered by the industry for the next ten years. This increase will be obtained by constructing new plants and by expanding present operations. Thus, by ! 978, it is estimated that approximately 60 million tons of iron ore vellets will be produced each vear from the magnetite taconites of the Biwabik formation. The portions of the Biwabik formation subjected to intense alteration resulted in direct shipping, wash, and heavy-media ores. Since 1892, 1.8 billion tons of direct shipping ore have been shipped from the Mesabi Range. This ore has been the major source of iron ore for American steel mills. In 1967, about 11 million tons of direct shipping ore and 13 million tons of wash, jig, heavy-media, and other gravity concentrates were shipped from the Mesabi Range.4 These products generally have poorer physical and chemical properties than the iron pellets produced from magnetic taconite. It is predicted that the shipment of these materials will decrease from 24 million tons in 1967 to 6 to 8 million tons in 1975.&apos; This decrease will

Jan 1, 1970

By R. J. Blackwell, J. R. Rayne, W. M. Terry

This paper presents results of an experimental investigation of factors that control the efficiency with which oil is displaced from porous media by a miscible fluid. The study was made to elucidate the relevant processes both on microscopic level (within individual or between neighboring pore spaces) and on macroscopic level (within a large sand body). Mixing of miscible fluids on the microscopic level was studied in sand-packed tubes. It was found that molecular diffusion is the dominant dispersion mechanism for reservoir conditions of rate, length and pore sizes. Macroscopic channeling was studied for various mobility ratios in reservoir mode1s scaled to relate viscous, gravitational, and diffusional forces. The formation of channels was due to viscous firzgering, gravity segregation and variations in permeability. With adverse mobility ratios, it was found for reservoirs of realistic widths that diffusion will not be effective in preventing the formation and growth of fingers, even in homogeneous sands. At sufficiently low rates channeling was eliminated by gravity segregation in tilted reservoirs. The dependence of recovery on mobility ratio, length-to-width ratio, flow rate and angle of dip is presented. INTRODUCTION Oil recovery by solvent flooding is finding increasing application in the field. While the process promises high recoveries from the region swept by solvent, under adverse conditions only a small fraction of the reservoir volume may be swept at the time solvent breaks through to the producing well. Further, the high cost of the solvent encourages its use only as a bank whose size must be kept at a minimum. Thus, two important questions arise: (1) what fraction of the reservoir can be swept, practically, by solvent? and (2) what is the minimum size solvent bank that can be used to carry out the displacement? The answers to these questions require knowledge of both macroscopic channeling processes and microscopic mixing processes. The studies described here were carried out to gain this knowledge. Microscopic mechanisms which cause mixing will be discussed first, because an understanding of these mechanisms is necessary for proper interpretation of the experimental work on channeling described later. INVESTIGATION OF MICROSCOPIC DISPLACEMENT PHENOMENA FOR MISCIBLE FLUIDS The questions to be resolved concerning microscopic displacement behavior are: (1) how much mixing occurs between oil and solvent in the direction of flow? and (2) does the solvent completely flush the oil from the pore spaces in the region invaded by solvent? The classic work of Sir Geoffrey Taylor&apos; and its extension by Aris2 have shown that it is possible from theory to describe the amount of mixing in single straight capillaries when solvent displaces a fluid of equal viscosity and equal density. Aris showed that the lengths of the mixing zones, 81, corresponding to the 10 per cent and 90 per cent concentration levels of the solvent can be calculated from the formula, 81 = 3.62 \/Kt, .........(1) where 8l is the length of the mixing zone, cm; t is the time, sec; and K is the effective dispersion coefficient, cm2/sec, given by K/D = 1 + (1/48) (au/D)2......(2) where a is the radius of the capillary, cm; D is the molecular diffusivity, cm2/sec; u is the average velocity

By F. J. Plecity, J. T. Michalak, W. C. Leslie

Isothermal recrystallization and grain growth in zone- and vacuum-melted irons and Fe-Mn alloys, up to 0.60 pct Mn, were studied in the range 480° to 650° C, after 60 pct cold reduction. In initial stages, rate of grain growth and rate of recrystallization of iron decrease with time. The recrystallization is typical of a growth-controlled process, and rate of growth is determined by the extent of recovery. Mn decreases rates of growth and of recrystallizatzon. The recrystallization process changes at about 0.30 pct Mn and nucleation may become time-depetzdet~t. In recent years, considerable effort has been expended in determining the effects of solute elements on recrystallization and boundary migration in fcc metals. The results have indicated that the effects produced by single solute additions are dependent upon both the element added and its concentration.&apos;-&apos; In contrast, there have been very few attempts to determine the characteristics of recrystallization and boundary migration in high-purity bcc metals, especially after heavy deformation, and the effects thereon of single solute elements.9-11 This study was undertaken to determine the recrystallization characteristics of various "high-purity" irons and the effects of manganese additions at two levels of base purity. It was hoped that the information obtained would improve our understanding of the recrystallization of pure metals and aid in formulating a theory for the effect of solute elements. The interest was not entirely academic, for the annealing of low-carbon steels, which is of very great commercial importance, is but poorly understood. MATERIALS The compositions of the irons and iron-manganese alloys used are listed in Table I. The zone-melted iron and Fe-Mn alloys were made by Battelle Memorial Institute. Iron S-1 was arc-melted in a water-cooled steel mold in an argon atmosphere. The ingot was forged into a bar, then given two horizontal zone-refining passes in an alumina boat. Iron V-4 was treated in a similar manner, but was not zone-refined. The iron for the zone-melted Fe-Mn alloys was induction melted in vacuum in MgO crucibles and cast into alumina molds. The ingots were forged into bars, machined to shape, and a groove milled down one side of each. The best available electrolytic Mn was placed in the grooves, and the bars were zone melted. The vacuum-melted Fe-Mn alloys were induction melted in this Laboratory in MgO crucibles and poured into cast-iron molds. Iron V-5 was purchased from National Research Corp. in the form of a small vacuum-cast ingot. The low-carbon steel was made by induction melting in air at the U.S. Steel Corp. Applied Research Laboratory. The history of the materials prior to the final cold reduction differed; these details are given in the Appendix. The penultimate grain size of the principal materials was kept in the range ASTM 2 to 4, except for the low-carbon steel. PROCEDURES The cold work prior to the final recrystallization anneal was kept constant at 60 pct. It is known that rolling procedure can influence the kinetics of recrystallization of ironI2; therefore, all specimens were rolled in one direction only, between clean,

Jan 1, 1962

By F. G. Jaicks

RECOGNITION of the benefits to be gained from the continuous casting of molten steel into finished or semifinished products has been given by scientific minds since the very beginnings of steel plant technology. In fact, Sir Henry Bessemer is credited with the first of a long list of patents&apos; issued by the U. S. Patent Office for a process which would accomplish this desirable end. None of these early ideas attained practical success and, as a result, the conventional method of teeming into ingot molds became an integral part of modern steelmaking operations. This procedure, although refined to keep pace with the changes which have come about in steelmaking and finishing facilities, is recognized to have inherent shortcomings which adversely affect manufacturing costs and steel quality. Interest in the continuous casting of steel persists because the process is directed toward avoiding some obvious weaknesses of conventional ingot casting. It has been recognized that should it be possible to substitute any of the continuous casting techniques under current development for ingot casting, it would no longer be necessary to make large capital investments in primary rolling equipment, the sole purpose of which is to reduce ingot castings to a form rollable on finishing mills. The results reported in the continuous casting of non-ferrous metals and specialty steels indicate that in addition to avoiding the primary rolling mills there is some basis for expecting significant improvements in yield, surface, and internal quality. Recognizing the shortcomings of the conventional procedures, the Inland Steel Co., in cooperation with Atlas Steels Ltd. and the Freyn Dept. of the Kop- pers Co. Inc., embarked upon a program to evaluate certain aspects of continuous casting in order to determine whether the process could be applied practically to an existing integrated steel plant producing &apos;large tonnages of carbon steels. TO assist in this evaluation a study was carried out in which several types of low carbon steel were continuously cast in an existing machine. It is the purpose of this paper to review some of the results obtained in the casting studies and to interpret the information that was obtained so as to indicate factors that must be considered in assessing operating limitations and plant capacities. Despite the early interest in the continuous casting of steel, the actual application to the steel industry is relatively recent. At present, there are about 25 operating plants casting steel, most of which have been built in the past decade. None of these plants could be classified as large in terms of the tonnages that are being processed by the major integrated steel plants. In contrast to the situation in the steel industry, there has been widespread adoption of the continuous process in the casting of nonferrous alloys, particularly aluminum and copper. As a result, much of the basic information that was required to apply the process to steel was developed in the nonferrous industries. In this respect, a most important contribution was the development of the Junghans2 system, which was initially designed for the casting of nonferrous metals and later applied to the casting of steel. Alternative methods for casting have also been proposed by Babcock and Wilcox Tube Co.,&apos;" the British Iron and Steel Research Association,5 and the Gebruder Bohler A. G.13 Each of these methods is now being used successfully for the casting of special steels in small experimental plants or in modest sized commercial steelworks. The Original Junghans process was first developcd in Germany. Further application of the process has been made by Rossi in other countries.&apos;*&apos; The experi-

Jan 1, 1958

By D. H. Forbes, I. B. Cadoff, H. M. Manasevit

Single-crystal silicon films have been obtained on several natural crystal faces of BeO using the thermal decomposition of silane and the hydrogen reduction of silicon tetrachloride. From an analysis of X-ray diffraction data it was determined that the following film-substrate orientation relationships exist: (111) Si 11(0001) BeO, (111) Si 11(1011) BeO, (100) Si 11f1010) BeO. and (110) Si 11(1010) BeO. An analysis of the crystallographic relationships between the film and substrate indicates that a match occurs between the silicon atoms in the film and the berylliuni ion sites in the substrate. This correspondence is in agreement with previous work on the deposition of silicon on sapphire.1-3 silicon on spinel: and tungsten on sapphire. The high resistivity, thermal conductivity, and radiation resistance of beryllium oxide make it an important substrate material for the deposition of thin films of silicon or other semiconductors. The importance of semiconductor-insulator composites to the field of integrated microelectronics has been well-documented in the case of silicon on sapphire.&apos;-&apos; The successful growth of large-area single-crystal silicon on an insulator, sapphire, was first reported in 1963.1,2 Since that time studies have been made of the crystallographic relationships between the deposited film and the sapphire substrate. On the basis of the observed relationships, a model has been proposed relative to the crystallographic requirements for epitaxy between the semiconductor film and the metal oxide substrate.3 It is proposed in this model that epitaxy is the result of a match between atoms of the deposited film and the metal ion sites of the substrate plane. This match is not limited to a 1 to 1 correspondence between sites in the two lattices. Sub- sequent studies of the deposition of silicon on spinel4 and tungsten on sapphire5 have yielded data which support this model. On the basis of this previous work it was felt that silicon on BeO should also fit this model. In the present study, the choice of substrate orientation was limited to the natural faces of synthetic BeO crystals. Of the faces available, the (0001) plane seemed the most favorable for epitaxial growth. EXPERIMENTAL PROCEDURE Silicon films were deposited from silane and silicon tetrachloride in the apparatus shown in Fig. 1. The hydrogen ambient gas was purified by passage either through a DEOXO unit, molecular sieves, and a liquid nitrogen cold trap, or through a heated Pd-Ag thimble. The gas was then mixed with the silicon source materiai and passed over the substrate which lies on a spacer above an inductively heated silicon pedestal. The following deposition conditions were used: a hydrogen flow rate of 3 liters per min with silane and silicon tetrachloride concentrations of 0.2 mole pct and a pedestal temperature of 1175" * 5°C as observed with an optical pyrometer assuming an emissivity of 1.0. Deposition was preceded by a 15- to 30-min hydrogen-etch period conducted at a temperature of 1275°C (obs). Adherent silicon films from 2 to 10 u were grown on the various BeO faces. The substrates were synthetically grown beryllium oxide single crystals ranging from 5 to 10 mm in

Jan 1, 1967

By F. V. Lenel, G. S. Ansell

The creep behavior of an aluminum -aluminum oxide alloy, A T 400, fabricated by compacting an atomized aluminum powder, extruding the compact, cold working, and recrystallizing the extrusion, was investigated. This alloy has a dispersion spacing of 1 . Previously Ansell and Weertman determined the steady-state creep rate of a recrystallized aluminum-aluminum oxide SAP-type alloy, MD 2100, with a 0.48-p dispersion. This alloy was found to have a steady-state creep rate of less than 10-6 min-1, too small to be measured accurately. By employing a more sensitive method of measuring creep rate, it was possible to determine the steady-state creep rate of AT 400 alloy, which is somewhat faster than that of MD 2100, at a series of temperature and applied stresses. Above a stress of Burger&apos;s vector, A = dispersion spacing, u = is a shear modulus) the rate follms an equation of the type: Steady-state creep rate K = A exp. where A is a constant, Q is the activation energy for sey-diffusion, and is the applied stress. At stresses lower than the steady-state creep rate drops off sharply and is no longer in agreement with this equation. This behavior is in good agreement with that predicted by the model for dispersion strengthened alloys in the stress and temperature range investigated. The absolute value of the creep rate is, however, four orders of magnitude lower than that predicted if the normal number of active dislocation sources are assumed to be present. It is concluded that in this SAP-type alloy the usual three-dimensional dislocation network is not present. Instead, short dislocation segments extending from one dispersed particle and terminating at a neighboring particle may act as dislocation sources. With this provision the creep model proposed by Ansell and Weertman reasonably accounts for the creep behavior which was observed. RECENTLY, Ansell and Weertman1 proposed a dislocation model from which they derived creep equations to describe the steady-state creep behavior of dispersion - strengthened alloys. Following Schoeck,2 they assumed that the rate controlling process for steady-state creep is the climb of dislocations over the dispersed particles. In order to verify their creep model, Ansell and Weertman determined the steady-state creep behavior of an aluminum-aluminum oxide SAP-type alloy, MD-2100, in both the fine-grained as-extruded, and coarse-grained recrystallized conditions. Since the grain size was the order of the dispersion-spacing, their model was not applicable for the as-ex- truded alloy. It should, however, be applicable to the coarse-grained recrystallized alloy. The results they obtained were rather unexpected. No meas-ureable steady-state creep was observed for the recrystallized MD-2100 alloy. If their model is correct, and if the second-phase particles act solely to hinder dislocation motion, then some measureable steady-state creep would have been expected. On this basis, they postulated that, in this SAP-type alloy, the main effect of the fine dispersion was to inactivate dislocation sources rather than to hinder the movement of dislocations. In order to understand more fully this unusual creep behavior, and to determine the validity of the model proposed,&apos; the steady-state creep behavior of an aluminum-aluminum oxide recrystallized SAP-type alloy, with a somewhat coarser dispersion spacing, was investigated. The results of this study are presented in this paper.

Jan 1, 1962

By E. E. Wahlstrom

The Harold D. Roberts tunnel, in Summit and Park Counties, Colorado, is a concrete-lined pressure tunnel finished to a circular cross section of 10.25 ft diam. The tunnel is 23.3 miles long and is designed to transport water for domestic use by the City and County of Denver from reservoir storage at Dillon to a tributary of the South Platte River at Grant. The tunnel passes beneath the Continental Divide at the crest of the Front Range and intersects rocks of diverse types and origins and geologic structures of extreme complexity. Geologic investigations preceded and were continued during construction and contributed materially to the safe and economical advance of the tunnel headings. Geological data obtained and evaluated during construction include plans and sections on a scale of 1 in. to 50 ft, rock temperatures at 2000-ft intervals, records of progress related to geology, records of ground-water conditions, summaries of the use of steel and timber supports, and summaries of grouting operations. Adverse conditions required use of steel and timber supports for 71.74% of the total length of the tunnel. Most supported sections reached a condition of equilibrium within a few hours to a few months after being excavated, and the concrete lining serves chiefly to provide an additional safety factor and to provide necessary hydraulic characteristics to the tunnel. Efforts to attain a maximum rate of advance of the tunnel headings necessitated use of more steel and timber supports than would have been required in a less accelerated tunneling operation. This report summarizes geologic investigations prior to and during construction of the Harold D. Roberts tunnel in Summit and Park Counties, Colorado (Fig. 1) and analyzes the tunneling operation as it is related to the various kinds of geologic conditions encountered in the tunnel. The tunnel is concrete lined to a circular cross section of 10.25 ft and is designed to transport 788 sec ft from reservoir storage at Dillon 23.3 miles along a dog-leg course passing under the Continental Divide to outlet and control works at Grant, Colo. The primary purpose of the tunnel is to augment the domestic water supply of the City and County of Denver, but plans include provisions for power generation at the outlet portal at a future date. Location of the tunnel was made after extensive preliminary geologic and engineering investigations by the Board of Water Commissioners of the City and County of Denver, and the U.S. Bureau of Reclamation. In 1946 the Board of Water Commissioners started tunnel driving on a limited scale from the east (outlet) portal and by 1955 had completed 9986 ft of tunnel. An urgent need for additional sources of water supply required acceleration of the tunneling operation, and, in 1955, Tipton and Kalmbach Inc. of Denver were assigned the responsibility of reviewing the project and preparing plans and specifications for the tunnel and appurtenant features. Additional geologic studies were made, and the geology of several possible alternate tunnel lines were compared before determining that the tunnel should be driven along the course previously adopted by the Board of Water Commissioners. On July 12, 1956, a contract for construction was awarded to Blue River Constructors Inc., a combine

Jan 1, 1962

DEVELOPMENT of a chemical process for the extraction of pure metals from mill concentrates or metal scrap has progressed beyond the pilot plant stage and may prove an important adjunct to present smelting and refining methods if initial commercial operations prove economically successful. Developed by the Chemical Construction Corp., the new process involves the treatment of oxide and sulphide ore concentrates by chemical methods, instead of the usual smelting and refining techniques. Several of the many applications are now scheduled for commercial use. Refiners using the new process will prepare ore concentrates by standard flotation methods, introduce the concentrate as a slurry into an autoclave along with water and an acid or ammonia. From the resulting leach solution, recovery of individual metals is made by use of suitable reducing agents. By varying conditions during treatment, different metals in the ore are produced separately as pure powders, which may be pressed into forms ready to market, or in the case of copper, extruded as rods or pipe. The reagents are generally recovered. By manipulating the variables during reduction, selective separation of nickel, and/or cobalt, and/or copper can be made simultaneously. The separation is a continuous operation. Low metal prices are not immediately in view because of the tremendous demand at this time. However, reduced metallurgical treatment costs will allow economical mining of orebodies with lower metal content, permitting increased production to meet demand. Although the practical horizon for use of the new process appears to be limitless, one factor may enter into its employment. Just how low grade a concentrate can be economically used is unknown. In addition, for present practical considerations, only metal below zinc in the electromotive series may be processed. Each commercial application requires specific technique adaptation and pilot-plant data for engineering design. A nickel-cobalt-copper process has been researched and piloted in collaboration with Sherritt Gordon Mines, Ltd., for the firm&apos;s Lynn Lake properties. In addition, processes were tailored for cobalt concentrates of Howe Sound Mining Co., and National Lead Co., in view of the urgent need for this specific metal. Major General William N. Porter, president of Chemical Construction, says of the new process, "piloting experience has shown that production cost, from ore concentrates to pure metals should be considerably below current costs." Other savings may be realized by cutting transportation and personnel costs, and by reducing the time lag between mining and pure metal from months to a matter of hours. First commercial use of the process will start sometime this summer. Chemico is slated to finish building a $2.5 million cobalt refinery for Howe Sound Mining near Salt Lake City. The plant is expected to raise world cobalt production by 40 pct. The plant will process 35 tons of 20 pct cobalt concentrates from Howe Sound&apos;s Blackbird mine near Cobalt, Idaho, daily. Yearly production is expected to reach 2000 tons of pure metal, about one half of U. S. consumption in 1950. Steps in the Howe Sound application of the process are: 1. Acid oxidation leach. 2. Filtration (residues thrown away are insoluble compounds-gangue, iron, arsenic). 3. Cementation (for Cu removal because Cu content is too low for recovery). 4. Reduction from ammoniacal solution. 5. Separation of Co and Ni as mixed metals (95 pct Co and 5 pct Ni). 6. Recovery of ammonium sulphate. Under construction at the Fredericktown, Mo., mine of National Lead is a $5 million refinery sched- [ ]

Jan 1, 1952

By W. J. Helfrich, C. L. Sollenberger

Many present direct reduction processes utilize iron ore concentrates for the production of sponge iron and the sponge iron is usually preferred as an agglomerate. Pelletizing a high grade iron oxide concentrate prior to reduction is a simple approach to the high capacity production of a uniform and agglomerated sponge iron product. The present paper describes the effect of different atmospheres and physical characteristics on the reduction of pelletized iron oxide concentrates. The kinetics of iron oxide reduction have been I studied by numerous investigators1-4 and a rate equation for the hydrogen reduction of hematite and magnetite has been proposed. Mc Kewan&apos; obtained kinetic data for the reduction of hematite spheres sintered at 13&apos;70°C (2498&apos;F&apos;). The kinetics of magnetite reduction was studied by Quets. He compacted the oxide at a pressure of 1 ton per sq cm and sintered the specimens to densities of 95 to 96 pct of theoretical. These studies demonstrated that the reduction of iron oxide is a topochemical process and that the rate of reduction is proportional to the receding surface area of remaining iron oxide. Thus, the measurement of the kinetics of iron oxide reduction depends upon the development of a measurable and well defined interface between metal and reacting oxide. It is evident that the reduction rate will be constant only when the rate of formation of the reaction product layer is constant. It was recognized by Joseph&apos; and Edstrom&apos; that the physical character of the oxide will determine the configuration of the interface between oxide and metal. The reduction of oxides which exhibit few pores or no interconnected pores should proceed by topochemical processes. However, if a massive or dense crystalline ore cracks during the reduction of the oxide, thus allowing the reduction to Proceed away from a well defined oxide/metal interface, then the observed reduction rate will vary or change during reduction. From a process standpoint, it would be difficult to apply absolute reduction rates determined for crystalline or nonporous iron oxide to the direct reduction of a porous pellet of iron ore concentrate. Most present direct reduction processes are attempts to utilize iron ore concentraates in the production of sponge iron. The sponge iron is usually preferred in an agglomerated form for subsequent melting practices. Pelletizing a high grade iron oxide concentrate prior to reduction is a simple approach to the high capacity production of a uniform and agglomerated sponge iron product. One process for preparing such a product has already been de-scribed. This paper describes the effect of different atmospheres and physical characteristics on the reduction of pelletized iron oxide concentrates. ORE CONCENTRATES STUDIED A magnetite concentrate from Reserve Mining Co. and a hematite concentrate from U.S. Steel Corp. were used in preparing pellets for these experiments. A head analysis of these concentrates is given in Table I. To compare the reduction rates of pelletized concentrates, it was necessary that each pellet contain equal amounts of oxygen which could be removed by reduction, regardless of the oxidation state, i.e., Fez% or Fe304. Also, because of the difficulty in preparing spherical pellets of uniform size, weight, density, and porosity for experimental purposes, pellets of a cylindrical shape were formed in a press.

Jan 1, 1961

By William E. Galloway, Gary E. Smith, Christopher D. Henry

INTRODUCTION Studies relating to the Oakville aquifer as presented in this report and by Henry et al. (this volume), are part of a larger , comprehensive examination of regional and local stratigraphic, hydro- geologic, and geochemical parameters within the Oakville Formation recently completed by the Bureau of Economic Geology. The Oakville serves both as a major Gulf Coast aquifer and an important uranium host (Fig. 1). Regional and local controls on hydrodynamics and hydrochemistry have important implications for hydrochemical exploration, the establishment of premining baseline parameters, and the design of post mining restoration procedures. Investigations of the Oakville Formation were de- signed for the purpose of determining the response of the aquifer to uranium extraction and were funded by the U.S. Environmental Protection Agency under grant numbers R-805357-01 and R-805357-02. Physical Stratigraphy Physical stratigraphic analysis shows that the Oakville Sandstone, a lithostratigraphic unit deposited by a major coastal-plain f luvial system, consists of five mappable, component depositional elements (Figs. 2 and 3). Each major component element is the product of one or more rivers traversing the Miocene coastal plain. In turn, each river possessed a unique sediment load, discharge characteristics, and source terrane. Consequently, each element exhibits distinguishing geometric and compositional parameters that potentially influence the flux and hydrochemical evolution of contained ground waters (Galloway, Henry, and Smith, in preparation). The Oakvil le Sandstone, as mapped and interpreted as a lithostratigraphic unit in the study area, corresponds closely to the Jasper aquifer system, an equally well-defined Gulf Coastal Plain hydrogeologic unit (Baker, 1978). Principal surrounding hydrogeologic units include the underlying Catahoula confining system, the Jasper aquifer system itself, and the overlying Burkeville confining system (lower Fleming mudstones). The Evangeline aquifer system includes much of the Fleming Formation. The Jasper aquifer system is bounded above and below by relatively less transmissive, finer grained confining systems, although absolute transmissivity varies greatly within both the Jasper and confining units. Lithostratigraphic and hydrogeologic boundaries coincide almost exactly within the Hebbronville flu- vial axis (Fig. 3). Correspondence of geologic and hydrostratigraphic boundaries is good within the George West axis; farther to the northeast the correlation of the Jasper aquifer with units mapped as Oakville Formation diverges to varying degrees. A complete analysis of these trends and a study of the depositional facies comprising the Oakvillle are included in Galloway, Henry, and Smith (in preparation). REGIONAL HYDROGEOLOGY The stratigraphic, compositional, and structural framework of the Oakville Formation and the mosaic of interrelated depositional facies that are combined in this framework play a key role in defining the hydrogeology of the Oakville. Furthermore, a combination of climate and hydrogeology, as well as past and present socioeconomic conditions, has determined water and land use patterns within the region of Oakville outcrop. Utilization of Oakville Ground Water Stratigraphic control for determining which wells produce ground water from the Oakville aquifer was established by preparing structural and isopach maps of the Oakville Formation using regional electric log cross sections. Surface elevation and screened interval data (or total well depth, if open-hole completion techniques were used) from each water well, combined with the stratigraphic data, allowed accurate assessment of the producing aquifer for individual wells. Information on well and screen depths, water levels, and usage of water from

Jan 1, 1980

By J. E. 214-000-000-010 Warren, M. R. J. Wyllie, T. Meidav, L. Scharon, R. Uhley, A. J. deWitte

By considering the stoichiometry of the underground combustion process, an equrztion was derived relating the point velocity of the combustion front as a function of the air flux, fuel content, efficiency&apos; of oxygen uitilization, hydrogen:carbon ratio, and ratio of carbon dioxide In carbon monoxide produced. In addition, an equation for cnlcrllating the amount of injected air necessary 10 produce the oil from I Cu. ft of reservoir space was derived. This equation has a direct bearing on evaluating compression costs for the process. Values calculated from these equations are in good agreement with experimentnlly obscrvcd values obtained from laborator) tube runs reported in the literature. The equations are also u\eful for atlcrlyzinf: experinlental data for inconsistencie.r.. I NTRODUCTION The injection of energy in the form of heat into an oil-bearing formation as a means of increasing the recovery of oil has been the subject of much discussion and experimentation as far back as 1920. The ideas have ranged from the injection of steam to the direct use of electricity as a means of getting thermal energy into a formation. However, most laboratory and field studies have been confined to the process whereby a portion of the crude in the reservoir is burned to generate the necessary heat to increase the mobility of the oil by reducing its viscosity. A recent paper by W. L. Martin, et al.&apos;, described the results of a number of laboratory experiments in which the combustion process was studied in a sandpack. Studies such as this indicate that with the temperatures involved, the oil is partially coked in this process and it is this coke which provides the fuel for combustion. The combustion of this residual coke can be analyzed theoretically by applying simple stoich-iometric principles to the combustion process. It is the purpose of this paper to compare the results reported in these experiments with those obtained from theoretical considerations. The variables studied by Martin, et al, among others, include combustion front velocity, air flux, oxygen utilization, fuel concentration, ratio of carbon dioxide and carbon monoxide in combustion gases, and the hydrogen:carbon ratio of the residual fuel. All these variables come into consideration when the stoichiometry of the combustion process is studied. The experimental conditions and results are tabulated in Tables 3 and 4 of Ref. 1. For purposes of comparison with calculated results, it was necessary to change the units of a number of the variables. UNDERGROUND COMBUSTION STOICHIOMETRY The combustion or oxidation of the carbonaceous residue or "coke" on the sand can be described in terms of the equation: where n is atomic ratio of hydrogen to carbon, m is ratio of moles of CO2 to CO produced, and CH. is taken as the unit molecular weight, realizing that actually the coke has a large range of high molecular weights. Assuming that all the fuel laid down in the sand is burned, the ratio of moles of oxygen consumed to moles of coke can be written as follows. Moles 0MolesMolescoke In terms of moles O2 per pound of coke, where 12 + n is the molecular weight in pounds per mole. If the 0, consumed is measured in standard cubic feet (60°F and 1 atm) and the coke in pounds per cubic foot of formation, 2, then: