By Baohua Li, Yanhui Liu, Shengping Li, Xuewei Lv, Yun Chen

There are almost ten billion tons of vanadium-bearing titanomagnetite in Panzhihua-Xichang area. However, iron ores in Hongge, which has the most abundant reserves in the four mine areas in Panzhihua, have not been utilized sufficiently so far. The reason behind this is the relatively high Cr2O3 in the ores (0.49 %~0.82 %), that due to its high melting temperature will negatively influence the blast furnace reduction and slagging process. Therefore, in the blast furnace process, Cr is hope to be reduced into molten iron, which can reduce slag viscosity problems. Slag iron reduction experiments were conducted to quantify the Cr reduction. Experimental results shows that with the increase of TiO2, the content of Cr in the hot metal is decreased when balanced. And during the initial stage of the reduction reaction, the reaction kinetic model is a first-order reaction.

Jan 1, 2016

By Liangju He, Peixuan Ouyang, Peijie Li

Single-pulse laser ablation of aluminum and titanium alloys under glass confinement is investigated. Processing parameters such as laser intensity and gap width between targets and glass are varied. Surface morphologies and crater profiles of the alloys after laser ablation are studied by SEM and white-light interferometric microscope, respectively. The effects of gap width and laser intensity on surface morphologies and crater profiles of targets are systematically analyzed. In addition, the generation of porous surface structures in Ti target is regarded as the result of phase explosion in the molten surface layer of targets and the thermodynamic condition in our experiment for phase explosion is evaluated.

Jan 1, 2016

By Guangliang Wu, Dongchang Huang, Xinbin Liu

Oxidation Kinetics of SPHC was analyzed by TGA, and the curve of oxidation weight gain with different temperature was acquired. It is found that, when the oxidation temperature is between 500 and 600 , all the curves are linear; when the oxidation temperature is above 700 , the curves are close to parabolic. At the temperature of 900 , the oxidation weight gain increases dramatically. The TGA results indicate that the activation energy of SPHC steel is 146.19 kJ/mol at the temperature of 500 900 , and an oxidation kinetic model was set up for variable temperature. Based on the temperature change during rolling process, numerical simulation of oxide scales evolution was carried out for SPHC steel, and the simulation result agreed well with measured ones. It can provide a basis for estimating the scale growth and controlling the temperature on site.

Jan 1, 2016

By Jiang Diao, Yong Qiao, Xuan Liu, Tao Zhang, Bing Xie

Adding CaO into the vanadium extraction converter is an effective way to decrease the dephosphorization burden in subsequent steelmaking process. The crystallisation process of spinel is one of the most decisive factors in the subsequent extraction. The theoretical calculation results show that the temperature of the peak total crystallization rate will decrease 5K with basicity increasing 0.1. The relation between cooling conditions and grain size of spinels is also discussed. It is found that low cooling rate and high basicity benefit spinel crystal growth. And the non-isothermal crystallization kinetics results indicated that the restriction factors of spinel growth is that solid crystals accept new components from liquid-solid interfacial. While the sample was cooled down to 1250 (1523K) at cooling rate of 5K/min, the crystal growth is consistent with Ostwald coarsening grew up law, and controlled by diffusion of particle.

Jan 1, 2016

By Anja Pfennig, Thomas Böllinghaus, Marcus Wolf

During CCS components are exposed to a corrosive environment and mechanical stress which results in corrosion fatigue and is inevitably followed by the lifetime reduction of these components. The lifetime reduction of the cyclically loaded high alloyed stainless injectionpipe steel AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2- saturated hot thermal water is demonstrated in in-situ-laboratory experiments (T = 60 °C, brine: Stuttgart Aquifer, flow rate: 30 l/h, CO2) in an environment similar to the on-shore CCS-site in the Northern German Bassin. In-situ tension-compression experiments were established simultaneously along with electrochemical measurements using a newly designed corrosion chamber in a resonant testing machine at a frequency as low as 30 – 40 Hz. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h. S-N plots, micrographic analysis and surface analysis of the fracture surface are demonstrated. X46Cr13 (surface roughness Rz = 4) reached the maximum number of cycles (12.5 x 106) at stress amplitude of 173 MPa producing a low scatter range of 1:3.5. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists. Pit corrosion prior to crack initiation may be identified as failure cause.

Jan 1, 2016

By Tianzu Yang, Weifeng Liu, Lin Chen, Wei Chen, DUCHAO ZHANG

Ni-M (Metal=Cu, Fe, Co, Mn, Zn, Cr) aerogel catalysts were tested for CH4 oxy-CO2 reforming. It was found that the Ni-Co bimetallic aerogel catalyst had the highest activity and stability in methane oxy-CO2 reforming among all the Ni-M aerogel catalysts. It exhibited a steady activity of 79 % (in terms of CH4 conversion) at 750 oC, which is the highest activity under a similar reaction condition as compared with those published in literature. Characterizations for the reduced catalysts indicated the formation of Ni-Co alloy, while other transition metals separated from Ni during the reduction process. Therefore, the active species in the Ni-Co bimetallic catalyst showed a stronger interaction than those in other Ni-M catalysts, which might be one of the main reasons for the better catalytic performance of the catalyst.

Jan 1, 2016

By Xiancong Zhao, Hao Bai, Qi Shi, Zhancheng Guo

Reducing electricity cost is important for energy intensive industries such as the iron and steel industry. With the implementation of time-of-use (TOU) electricity price, plenty of attention has been paid to the optimal management of byproduct gases. The time-of-use (TOU) electricity price is the practice of implementing different prices for different times of use. It is possible to reduce electricity cost by adjusting the amount of product gases stored or used for power generation throughout the day. In this paper, a novel mixed integer linear programming (MILP) model concerning the TOU electricity price is proposed to optimize byproduct gas use. Compared with previous models, this model considers the optimal load shift between gasholders and boilers under TOU electricity price. The case study of a steel plant demonstrates that the electricity purchase cost can be reduced by more than 30% after optimization.

Jan 1, 2016

By Linfeng Zhou, Rong Sun, Guanghui Li, Zhiwei Peng, Tao Jiang

Dust, or airborne particulate matter, from metal smelting can be either mechanically or thermally generated and it negatively affects the indoor air quality as well as the fugitive emissions from the plant. The thermally generated dust is often referred to as fume and it is typically generated whenever liquid metal comes into contact with air. For practical reasons, such as vehicle access, etc. it is often difficult to collect 100% of the fume. It is therefore highly desirable to develop processes and optimize operational procedures so that fuming can be kept to a minimum. In this series of experiments, the mechanism of active oxidation and fume formation from liquid silicomanganese under an impinging air jet in the temperature range 1400-1600°C has been explored. Characteristic properties of the fume have been established; particle diameter, shape, size distribution, and elemental composition are reported. The oxidation process is described in terms of vaporization, oxidation and agglomeration. In the boundary layer, two competing mechanisms seem to be operative in parallel: a direct oxidation of Mn vapor, and a two-step oxidation of silicon. The thermodynamic and kinetic conditions governing the two mechanisms are discussed.

Jan 1, 2016

By Zhanjun Wang, Yongqi Sun, Mei Zhang, Zuotai Zhang, Min Guo

The role of fluorine on the viscous and crystallization behavior of CaO-SiO2-MgO-Al2O3-FetO-P2O5-(CaF2) slags were explored using the rotating cylinder method, non-isothermal differential scanning calorimeter (DSC), X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. It was found that the viscosity slightly decreased with increasing CaF2 content. It was also found that CaF2 addition can promote the primary phase transformed from MgFe2O4 spinel to Ca3(PO4)F, which was beneficial to the enrichment of phosphorus. Additionally, the structure of the slags explained by X-ray photoelectron spectroscopy (XPS) and magic angular spinning nuclear magnetic resonance (MAS-NMR) were further analyzed, which was well in accordance with the above analysis.

Jan 1, 2016

By Mike Johnson, Niels Verbaan, David Dreisinger

The Search Minerals Foxtrot project in Labrador is a surface deposit enriched in the highly sought after heavy rare earth elements. Early metallurgical work investigated beneficiation of the rare earth content of the Foxtrot resource using flotation, gravity separation and magnetic separation. The concentrate was then processed by acid baking and water leaching to produce a REE leachate for purification and recovery. The Search Minerals Direct Extraction Process was developed through bypassing the beneficiation process and directly acid treating a coarse crushed ore material prior to water leaching. The result is a simple, low risk technical process for direct recovery. Concurrently, the treatment of the water leach solution was modified to produce a high grade (98.9% total rare earth oxide) product for refining.

Jan 1, 2016

By Yousef Mohassab, Hong Yong Sohn, Mohamed Elzohiery

As part of the development of a novel flash ironmaking process at the University of Utah, a labscale flash reactor was used to produce iron directly from iron oxide concentrate. This work tested the feasibility of the novel flash ironmaking process using the partial combustion of hydrogen as fuel and reductant. In this flash reactor, the energy required to reduce concentrate particles was obtained from the internal combustion of hydrogen and oxygen with complementary energy from electrical resistance heating to compensate for the heat loss. After the reaction shaft was electrically pre-heated, hydrogen and oxygen streams produced a non-premixed flame inside the reaction shaft. Various conditions such as flame configuration, flame power, positions of concentrate feeding ports, excess hydrogen amount and residence time were tested. More than 90% reduction of magnetite or hematite was achieved at temperatures as low as 1175 oC with < 100% excess hydrogen in <10 s of residence time.

Jan 1, 2016

By Shenghui Guo, Jianbo Lan, Hongying Xia, Jinhui Peng, Lihua Zhang, Libo Zhang

Spent Hawaii nut shell was converted into a high-quality activated carbon via steam physical activation. Analysis of the experiment including activation temperature, activation duration, steam flow rate on the adsorption capability and yield of activated carbon were identified. Response surface methodology showed that the activation temperature was identified as 866 , an activation duration of 36 min and a steam flow rate of 2.5mL/min with the methylene blue adsorption number of 195 mg/g and yield of 77.75%. The key parameters that characterize quality of the activated carbon such as the BET surface area, total pore volume and average pore diameter were estimated to be 1125m2 /g, 0.94mL/g and 5.21 nm, respectively. Additionally, by the SEM analyses of char and activated carbon, the surface of activated carbon has large number of pores of irregular and heterogeneous morphology.

Jan 1, 2016

By Huimin Lu, Zegao Sun, Zhijiang Gao

The traditional Ti6Al4V alloys were obtained by the smelting reduction of V-Ti bearing beach placer by rotary hearth furnace and aluminothermic reaction in laboratory. First, it gets he lp from combined rotary hearth furnace and grinding magnetic separation process to prepare titanium slag containing vanadium. In this study, a neural network model was used. The comparisons between experiment results and neural network simulation results show that genetic algorithm (GA)-based on back propagation (BP) method can predict the degree of reduction and separation of iron and slag with higher prediction accuracy. Then by aluminothermic reaction process, the optimized process parameters for Ti-V-Al alloys were searched. Al can deoxidize metal V and Ti from the metal oxides of artificial rutile containing vanadium. Finally, traditional Ti6Al4V alloy can be obtained by remelt and adjust the constituents.

Jan 1, 2016

By Teruhisa HORITA

The durability of SOFCs is one of the critical issues to realize the SOFC systems. In order to improve the durability, a precise degradation mechanism should be clarified at the different functional ceramic interfaces in SOFC cells and stacks. This paper reviews the improvement of SOFC durability by the mass transport analysis especially at cathode/interlayer/electrolyte interfaces. We have made a precise analysis on the reaction of cathode with impurities. Especially at the (La,Sr)(Co,Fe)O3/CeO2/ZrO2 interfaces, a significant amount of SrCrO4 and SrSO4 were observed at the (La,Sr)(Co,Fe)O3 surface as well as inside the (La,Sr)(Co,Fe)O3 cathode, which suggested some process occurred for both poisoning. Possible degradation mechanisms were proposed based on the observation data.

Jan 1, 2016

By Caryn Wendt, Donna Post Guillen, Armando McDonald, Erik R. Coats, Chaston Ellis, Kevin Feris

Dairy operations constitute ~2.5% of annual U.S. greenhouse gas (GHG) emissions, making dairies one of the largest sources of industrial GHG emissions. We are developing a novel, integrated system to achieve a net reduction in dairy GHGs while producing value-added materials and products. This integrated manure-to-commodities system converts dairy manure to bioenergy, sequesters carbon by converting volatile fatty acid-rich fermenter supernatant to bioplastics, and utilizes anaerobic digester (AD) and polyhydroxyalkanoate (PHA) reactor effluents to produce algae that can be harvested and internally recycled to enhance PHA production and sequester carbon. A decision-making tool is being developed for the integrated system that quantifies net GHG reduction, carbon sequestration, nutrient management and economics.

Jan 1, 2016

By Zhengjie Chen, Wenhui Ma, Jijun Wu, Kuixian Wei

The gasification reactivity of PC (petroleum coke), strengthened by addition of different potassium carbonate proportions using different grinding medium, was investigated by using thermogravimetric analysis (TGA). Results showed that the gasification reactivity of PC not only increased with the increase of catalyst-loaded, but also showed the effective improvement by anhydrous alcohol. The PC was mixed with potassium carbonate [K2CO3] catalyst at 0.5%, 0.8%, 1.0% and 1.5%, and then ground wet with distilled water. The CO2-gasification rate of PC was only 77.35%, 80.55%, 84.07% and 85.88% under the gasification temperature 1100 °C and holding time 120 min, at different K2CO3 respectively. However, when the PC was ground in anhydrous alcohol at the same condition of catalyst-loading, the gasification rate of PC reached 95.43%, 96.63%, 95.50% and 95.61% at the holding time of 108 min, 101 min, 74 min and 35 min, respectively. It was shown by FTIR, SEM and EDX determinations that the anhydrous alcohol used as the grinding medium can further improve the gasification reactivity of PC when compared with the distilled water.

Jan 1, 2016

By Shengqin Zhang, Yousef Mohassab, Feng Chen, Hong Yong Sohn, Mohamed Elzohiery, Amr Abdelghany

A novel ironmaking process is under development at the University of Utah aimed at producing iron directly from iron oxide concentrate in a flash reactor. This process will reduce hazardous emissions and save energy. The kinetics of magnetite reduction with hydrogen was previously investigated in our laboratory in the temperature range 1150 to 1400 oC at large temperature increments (~100 oC increments). Due to the significant melting that occurs above 1350 oC, the reduction kinetics was measured and analyzed in two distinct temperature ranges of 1150 to 1350 oC and 1350 to 1600 oC (~50 oC increments). Experiments were performed using magnetite concentrate particles of different sizes under various hydrogen partial pressures and residence times. Reduction degrees of more than 90 % were achieved in a few seconds at temperatures as low as 1250 ºC. Different rate expressions were needed to obtain reliable agreement with experimental data.

Jan 1, 2016

By Adegbenjo Adewale Oladapo, Ibitoye Simeon Ademola, Ladiipo Olufemi Akinbiyi, Adegbola Adekunle Amos, Adeboje Taiwo Bode, Raji Fatai Olasunkanmi

The combined effects of the addition of Silicon (Si) as alloying element and low temperature annealing on the tensile properties of 70/30 brass with Nickel (Ni) and Iron (Fe) contaminants is investigated in this paper. Melts of cartridge brass were made to which 0, 0.5, 1, 2, 3 and 4 wt % of Si was added. These were sand cast into rods of 600 mm by 10 mm diameter and were thereafter machined into standard tensile test samples. Some of these samples were annealed in a muffle furnace at temperatures of 250, 300, 350, 400 and 450 oC respectively and the others were used as control. Subsequently, all the heat treated and non heat treated samples were subjected to tensile tests on a Hounsfield Extensometer and the load – extension plots retrieved were analyzed. Microstructural characterizations of the samples were carried out using Accu-Scope Optical Microscope. The results showed that cartridge brasses subjected to alloying and annealing treatments had improved tensile and yield strengths. However, the tensile properties were increased and maintained within acceptable limits at stress relieve annealing temperatures.

Jan 1, 2015

By Junfu Chen, Jiann-Yang Hwang, Yong Zhou, Lijun Lu, Likun Lia, Jixiong Liu

The sheet-like NiS-ZnS heterostructured composites were prepared by the microwave hydrothermal. The fabrication of the heterojunctions broadened the range of light response of ZnS. The photoexcited electrons of ZnS migrated to the redox potential of NiS/Ni2S under visible light irradiation, which can facilitate the effective separation of photogenerated electrons and holes in space. The visible photocatalytic activity towards hydrogen production for NiS/ZnS nanosheet heterostructed composites without co-catalyst achieved 0.28 mmol h–1, and the quantum efficiency was up to 18.6% under the wavelength with 420 nm visible light irradiation.

Jan 1, 2015

By S. Yin, A. Bogno, H. Henein, P. Natzke

Impulse Atomization (IA) (a single fluid atomization technique) was used to rapidly solidify Al- 4.5wt%Cu and Al-4.5wt%Cu-0.4wt%Sc under argon atmosphere. In addition to the IA-generated droplets, the same technique was used to produce strips by Spray Deposition (SD) of the same alloys on a copper substrate with and without oil coating. The rapid solidification microstructures were analyzed using Scanning Electron Microscopy (SEM). From the SEM images, the amount of eutectic and the secondary dendrite arm spacing (SDAS) were measured. These SDAS results lead to the estimation of cooling rate. The eutectic fraction coupled with the metastable extension of the solidus and liquidus lines of Al-Cu (Sc) phase diagram lead to the estimation of primary and eutectic undercoolings. A comparison of the solidification path of the droplets and the strips was done as well as the analysis of the effects of scandium.

Jan 1, 2015