By G. F. Leaming

The paper by R.V. Ramani and R.J. Sweigard is a wonderful description of the labyrinthine web that has been spun about the mining industry by energetic bureaucrats and politicians over the past 50 years. The remedy for the problem, however, is not more of the same, but less. That may be difficult for the industry to achieve, for it is not a technical solution but a political one. And the current fervor for more detailed planning at all levels of government and private enterprise has become deeply ingrained. The authors recommend the provision of more information about mining and mineral resources to "macro" (i.e., government) land use planners. They apparently overlook, however, the already strong tendency on the part of most government land use planners to consider themselves omniscient. Thus, giving them more information about the technical problems of mining will only make them want to get more and more involved in the "micro" (private, site specific) mine development and production plans of the individual mining firm. In fact, this has already happened at all levels of jurisdiction from municipal to federal government. Examples are legion. The most effective way to ameliorate the adverse impacts of government land use planning on existing and potential mining operations is to: (1) introduce greater flexibility in the definition of land use zones by local and state governments; (2) adopt realistic and relevant ambient environmental performance standards in governing relationships between mineral land uses and concurrent or subsequent nonmining land uses; (3) allow greater leeway for economic considerations in land use decisions in contrast to the explicit legalistic approach now in vogue; (4) recognize that all minerals are not the same and that sand and gravel mining should not be treated the same as underground metal mining, coal stripping, oil field production, or in situ leaching; and (5) eliminate the notion that mining operators should be responsible for determining in detail the use of land by subsequent owners of mined land. This last bit of conventional ethic really makes no more sense than requiring the builders of every shopping center or government office complex to provide detailed plans for the use of that land when its use for shopping or government is ended. Did the builder of Ebbetts Field plan for Brooklyn after the Dodgers went to Los Angeles? Should the developer of the Bingham Pit plan for suburban Salt Lake City after the copper mining goes to Chile? The nation's mining industry must address these questions before further bankrupting itself to provide more data to planners and spending thousands of dollars per acre to create land that when reclaimed is worth only a few hundred dollars per acre. ? Reply by R.V. Ramani and R.J. Sweigard We thank Mr. Learning for his valuable contribution. His views on the problems of land use planning and mineral resources are most welcome additions to our paper. As the title indicates, our paper was more concerned with the impacts of land use planning on mineral resource conservation than with the details of the planning process. On the whole, his five recommendations would be helpful for mineral resource conservation. However, we would suggest that the argument he presents for his final recommendation does not address the differences between mining as a land use and commercial or institutional uses. We believe that this difference is the crux of the issue. We share Mr. Learning's desire to ameliorate the adverse impacts of land use planning. Possibly the most detrimental impact is the loss of mineral resources. Any development, whether mineral or community, that does not give proper consideration to other resources can result in permanent loss or sterilization of resources. With proper planning, some of these losses can be avoided. As our paper indicated, one factor that limits the consideration of mineral resources, and ultimately leads to their sterilization, is the generally inadequate levels of resource characterization and understanding of the unique nature of mineral resources and mining operations. The last point raised by Mr. Learning is also important. In terms of reclamation and land use planning in mining districts, we certainly do not advocate spending more than what the results are worth. The main thrust of the paper was to explore the avenues for conserving the mineral resources so that, at some appropriate time, the issue of mining and reclamation can still be addressed. ?

Jan 1, 1986

By C. G. Dunn, M. Sharp

IN twinned crystals of the face-centered cubic metals the lattice of one twin is a mirror image of the other in a common twin boundary. When several twins appear within large grain in a sheet specimen, the twin one boundaries form a set of lines at the surface of the specimen which coincide with (111) planes of the large grain. Furthermore, for twins of the same orientation, these lines are parallel. Generally, the presence of identically oriented regions with straight parallel boundaries coinciding with a (111) plane of the surrounding crystal is strong evidence for identifying the island regions as twins of the parent crystal. However, Fig. 1, which shows the macrostructure of a large grain of copper with island regions that satisfy these conditions. is not an illustration of (111) twins. Since the reverse side of the specimen has much the same appearance, it was thought at first that these regions, which appear dark in the macrograph, actually were twins. According to X-ray data, however, these regions are second-order twins of the large crystal. With regard to their formation, these second-order twins formed by secondary recrystallization in a cube texture matrix. Growth occurred in the direction of the arrow (see Fig. 1) as the specimen moved slowly into a gradient temperature furnace as described previously.' Nucleation of the second-order twins occurred, therefore, on the ends facing opposite the arrow. If the origin of the second-order twins were due to repeated twinning, some first-order twin structure should be visible on these ends. This proved to be the case, as very small twins were readily found with the aid of a microscope, and probably could have been seen, in some instances, under ideal lighting conditions without aid of a microscope. Fig. 2 shows a cross-section view taken perpendicular to both the surface and the (111) trace of the parent crystal (visible as a straight boundary in Fig. 1) at the beginning point of growth of a second-order twin and where one first-order twin was relatively thick. In the micrograph, A is the large parent grain; B is the first-order twin of A; and C, which is a first-order twin of B; is a second-order twin of A. Between A and B and between B and C the major straight portions are traces of common (111) twin boundaries. The straight portion of boundary between A and C, however, is not a common crystallographic plane to the two lattices; it is a (111) plane of A and a (115) plane of C. Without considering the mechanism of twinning itself, the origin of the second-order twins may be accounted for in terms of repeated twinning and special growth characteristics. After each nucleation, a selective growth process can be thought of as favoring growth of the first-order twin in local spots only and favoring growth of the second-order twin to an extent comparable with that of the parent grain over relatively large areas in a way similar to that described for twinning in aluminum.' It has already been pointed out that the boundary between the large grain (A) and the second-order twin (C), which is responsible for the straight boundary portions in Fig. 1, involves a (111) plane of A and a (115) plane of C. The same combination of planes is not only possible in first-order twins, but actually appears quite frequently.3 Their prevalence in first-order twins and their presence here in second-order twins, together with the necessary occurrence of a large number of common lattice sites at the boundary, is an indication that this combination produces an "energy cusp"' boundary. (Energy cusp boundaries have been described by Shockley and Read.") The configuration of atoms near a {Ill), (115) boundary in first-order twins is of course different from the configuration near the same type of boundary in second-order twins. References 1 M. Sharp and C. G. Dunn: Secondary Recrystallization Texture in Copper. Journal of Metals (January 1952) Trans. AIME, p. 42. 2W. G. Burgers and W. May: Stimulated Crystals and Twinning in Recrystallized Aluminum. Recueil des travaux chimiques des Pays-Bas (1945) 64, p. 5. aD. Whitwham, M. Mouflard, and P. Lacombe: Discussion of W. C. Ellis and R. G. Treuting, "Atomic Relationships in the Cubic Twinned State." Trans. AIME (1951) 191, p. 1070; Journal of Metals (October 1951). 4 W. Shockley and W. T. Read: Dislocation Models of Crystal Grain Boundaries. Physical Review (1950) 78, p. 275.

Jan 1, 1953

By R. E. Miner, J. K. Jackson, T. L. Wilson

A study has been made of the transformation kintetics and morphology in gas-quenched Fe-5 pct Ni alloys. Massive ferrite or nlurtensite was found to form at temperatures in agreement with earlier results. Surface Preparation appeared to have the greatest effect in determining the type of transformation Product formed. Grain size change, subgrain morphology, and dislocation densities of massive ferrite were essen-tinlly invariant functions of cooling rate. The mar-tens~tic structures were typical of transformation in austenite grains of the order of the sample thickness. BY introducing the idea of a massive transformation in dilute iron-base alloys, Gilbert and Owen in 1962 served to stimulate a closer inspection of phase transformations in ferrous systems.' A wealth of literature has followed concerned with the morphology,2-5 transformation mode,2'3'6-8 and thermodynamics of transformations.2,5,9 interesting controversies have resulted from the experimental observations; closer attention has been paid to the definition of massive transformations and still to be resolved is the Ms temperature of pure iron. The purpose of this note is to report some observations made in a detailed kinetic and metallographic examination of the transformations that occur in gas quenched Fe-5 pct Ni. The results are pertinent to the Ms extrapolations that have been made for pure iron and the observed substructure of massively transformed alloys. PROCEDURE The material used in this investigation was cast as a 5 lb vacuum induction melted, carbon deoxidized heat. The ingot was hot worked to a strip 0.10 in. thick, decarburized, and cold rolled to final thickness. Specimens were punched to sample shape and decarburized in wet hydrogen at 600°C. The chemistry of test specimens is indicated in Table I. Samples 1 by $ in., by thickness were resistance heated and rapidly cooled in an apparatus as illustrated in Fig. 1. Similar helium quenching apparatuses have been described previously;2,6'10 the distinguishing feature of this apparatus is the nozzle geometry. Twin nozzles with three convergent-divergent, sonic ports were mounted perpendicular to the specimen for quenching purposes. The specimen temperature was monitored with an intrinsic 3 mil chromel-alumel thermocouple spot welded to the specimen and con- nected to an oscilloscope. A single switch stopped the current flow through the specimen, opened a gas flow solenoid valve, and initiated an oscilloscope sweep. Cooling rates were read directly from a photograph of the oscilloscope trace and the quenching rates quoted later were made at a point immediately prior to transformation on the trace. All quenching studies were conducted either under a vacuum of 10"-5 torr or a helium atmosphere. The sample geometry was chosen large enough to permit optical and electron microscopy to be performed on samples. The samples were electropolished for both types of examination in a perchloric-acetic solution. Electron microscopy was conducted on a HU 11A microscope operated at 100 kv. Dislocation densities were determined at the same general operating reflection (110) on foils thick enough to produce Kikuchi patterns. RESULTS AND DISCUSSION Transformation Temperature Observations and OD-tical Microscopy. The quenching results of this study are illustrated in Fig. -2(a). Samples which were treated in the as-decarburized condition transformed in a manner similar to that reported previously—a decrease in transformation temperature occurred as the quenching rate increased until a plateau region was reached. Within the scatter of the results obtained here, there was no break in the transformation temperature-quenching rate plot. This suggests no change in transformation mode. Further metallographic examination confirmed this observation. A martensitic transformation was obtained for similarly treated samples except that the surface was first electropolished. The Ms temperature was approximately 85°C below the plateau determined for the unpolished samples and cooling rates as slow as 2000°C per sec were adequate for producing marten-site. The transformation temperatures are in gen- / STRIP SAMPLE / COPPER I SAX/-/}' / CONNECTOR-----A f, SON|C poRTS AC LEADS 3j ]j"I rofe[ \ Mf/yinK/iKj''^ THERMOCOUPLE X-(^—iie"s*c? ' LEADS 1 INCH Fig. 1-—Schematic scction of gas quenching apparatus

Jan 1, 1970

By E. S. Anolick, Joseph Singer

The magnetic after-effect, in the form of time decay of permeability (l/µ), has been used to obtain independent data on the solubility of' carbon in pure iron. The results differ slightly from the solubilities obtained through internal -friction experiments. The mechanism of the time decay being the magnetic analogue of internal friction, it appears necessary to explain the observed discrepancies, and some suggestions are made. THE purpose of this work was to establish the reliability of the time decay of permeability as a measure of dissolved interstitial in the body-centered-cubic lattice, and further, to establish techniques suitable for such measurements with samples of a form convenient for various other measurements. This particular sample form was the "epstein" strip, i.e., 25 cm by 3 cm by 0.035 cms. While the general conclusions are not limited by this geometry, there are two aspects of the samples that may be relevant: a) texture, and b) grain size, which ranged generally from 1 to 10 mm. Effects due to these two possible parameters were thought to be small and were not investigated. Calibrating the time decay technique and the other experimental procedures by measuring the solubility of carbon in pure iron suggested itself because of the accumulation of data on this subject through the related technique of the internal friction'; The essentials of this report have been published in a somewhat condensed form.5 Since then some additional data have been taken. It is the purpose of this paper to add these data and to provide more complete description of the experimental techniques than was possible then. The time decay of permeability is a form of the magnetic after-effect.6,7 Permeability is measured immediately after demagnetization (µº) and also long after (µ8). The time decay, ?(l/µ), is the difference 1/µ8 - 1/µ0 and has been considered to be proportional to the concentration of a dissolved interstitial6,8,9,12 The relaxation time! 7, is characteristic of a particular diffusion, and affects the permeability as follows: where he being the activation energy for diffusion of the interstitial. Reference is made to the works of snoek6 and Neel7 for a complete discussion. A brief exposition of the principal ideas may be in order here, as follows. On the basis of the simplest model, resistance against domain wall motion increases with time after demagnetization due to the diffusion of interstitials to preferred sites created by the magnetostrictive tetragonolization under the strong magnetic field. Thus permeability, measured with a small field after the abrupt removal of the large field, will continuously fall with the process of diffusion of the interstitials, and the total "time decay" (or "time decrease") should be proportional to the amount of interstitial in solid solution. In the present report, use is made only of the total time decay rather than of the nature of the progress of the decay; the only problem involved in this approach is the need for assurance that only one interstitial is contributing to the effect as used. It is felt that the special use made here of the total time decay warrants the conclusions. Other work has been going on elsewhere on the detailed study of the nature of the time decay.8'9 EXPERIMENTAL A) Materials—12-lb ingots were made in a vacuum furnace from high-purity iron and by a series of hot and warm reductions were brought down to 14-mil strip. This was cut into 25-cm epsteins. The pure iron was decarburized at 750 °C by hydrogen. The time decay measurement for the decarburized iron (see below) indicated a satisfactorily low starting level of interstitials. Grain growth to grain sizes of 1 to 10 mm was produced in the pure iron by a 700" anneal in hydrogen after a critical reduction of about 7 pct as suggested by previous trials. No measurement of texture in the pure iron was made. The grain size was taken to be large enough to be beyond any sharply critical size regarding solubility. B) Infusion of Carbon—Since the permeability measurement required about two dozen epsteins, a special method of carbon infusion had to be developed to ensure homogeneity of infused carbon. This was accomplished by setting the samples edgewise in a

Jan 1, 1961

By M. D. Hassialis, C. G. Myer

THE nature of a collector-coated mineral surface has been the subject of some experimentation and much speculation. Various aspects of the problem have been isolated and studied; it is probable, however, that there exist aspects as yet unrecognized, which are needed for a complete description of the system. The recognized elements of the problem are: 1—The nature of the chemical units comprising the film and the nature of the forces holding these chemical units to the mineral surface; 2—The orientation of the chemical units at the surface; and 3—The disposition of the collector units at the mineral surface. This report touches upon all three aspects of the broad problem; it deals, however, with a new and heretofore unrecognized element—the mobility of the collector units in the two dimensions of the solid-liquid interface. Regardless of the viewpoint adopted as to whether the chemical units comprising the collector film are collector ions or molecules, held either by chemical or physical forces, the writers on flotation theory are in apparent agreement as to the orientation of the chemical units at the mineral surface. Wark and Cox' showed that the contact angle at a stable collector-coated surface in a constant chemical environment is independent of the nature of the mineral and of any resurfacing agent; it depends solely upon the collector used. They showed further that the value of the contact angle increases with the number of carbon atoms in a homologous series of compounds. Taggart, Taylor, and Knoll2 postulated that the collector ion is oriented with the chemically reactive, polar end toward the mineral surface and the non-polar, hydrocarbon-like end toward the liquid phase. In support thereof they cited the abstraction of p-p1 dihydroxydiphenylthiourea and of glycol xanthate8 by galena without a concomitant increase in the contact angle above that of clean galena. It was argued that in these cases the water-repellent layer which normally would be presented to the liquid phase owing to the orientation of the collector ions is overlain by a layer of water-avid groups, the hydroxyl groups. Implicit is the analogous orientation exhibited by a monomolecular layer of an insoluble substance at an air-water interface. It should be pointed out that these facts also are consistent with the concept that the collector units be flat on the surface of the mineral and that the response of the surface to an air bubble is determined by the ratio of the area covered by water-avid groups to the area covered by water-repellent groups; the areas being weighted according to the relative watef-avidity or water-repellency of the groups involved. The disposition of the chemical units of the collector film at the mineral surface has not received the attention it merits. Taggart4 concluded from the observed stoichiometry of the ions entering and leaving a surface that the stoichiometry is obeyed in detail at the surface of the mineral. Thus, in the case of xanthate-coated galena, pairs of xanthate ions are attached to surface lead ions. In the case of chemisorption, Gaudin and Preller postulated an agreement between the atoms or ions of the substratum (the mineral surface) with those of the superstratum (collector film); in the case of the physical adsorption their position is not clear. In one place they state "the first type (physical adsorption) does not require any agreement between the atoms or ions of the substratum with that of the superstratum" and in another place that "It seems, in fact, as though some slight influence of the substratum is formed even in physical adsorption." The present work shows that in some cases of chemisorption the chemical units of the collector film are in constant surface-bound motion and may not be assigned to any site of the surface, hence there is no permanent association between the chemical units of the film and the atoms or ions of the solid. The physical property of the collector film that is of paramount importance is its surface energy. Although this property is not susceptible to direct experimental determination, the related contact angle is. Much of the knowledge of the properties of a collector film derives (by deductive and inductive reasoning) from the behavior of an air bubble thereat

Jan 1, 1952

By Louis A. Panek

INTRODUCTION AND SUMMARY With respect to the geomechanics aspects, the primary technical objectives in mining by an undercut-cave method are to achieve a controlled, sustained caving of the mineral body and to remove the fragmented ore with a minimum of dilution from surrounding unmineralized rock, while maintaining stability or control of the rock structure around the access openings. The structurally ideal ore body probably does not exist. If the rock mass is so weak as to cave on a short span, it may tend to be too sticky for easy drawing and handling, or create special problems in regard to support of the access openings. If the ore is strong, caving may be difficult and the caved fragments may be of such a large size as to require special equipment for transferring the ore from the caved zone. Given enough time and money to generate data and conduct trials, engineering and ingenuity can devise an appropriate combination of mine layout, sequence of extraction, and mechanical equipment to achieve a technically successful caving extraction operation to meet the foregoing requirements in many types of deposits. The large capital investment involved, however, reduces the freedom to make major changes once the mine development is well under- way, and the penalties for failure to accurately anticipate operating conditions militate against selecting any but the most obvious candidates for mining by an undercut-cave method. The demonstrated capability to extract large, deep, economically marginal deposits by this low-cost, high-volume method of mining provides an incentive to develop a rationale for predicting the cavability and stability characteristics of a deposit prior to mining, so that the undercut-cave method may be extended to a much wider range of mineral deposit characteristics. The ultimate goal is to establish as explicitly as possible the quantitative interrelationships between the measured rock-mass characteristics, the caving span, the size distribution of caved ore fragments, and the sizes and locations of stable access openings. Lacking an understanding of these relation- ships, a designer may readily change some factor in the wrong direction (e.g., excessively reduce the distance between the extraction level and the undercut to increase the convenience of operations for the undercutting crew, increasing the frequency of repairs to the extraction-level support system) or create unnecessary problems elsewhere in the system by introducing a design change that can achieve only minimal improvement in the factor of direct interest (e.g., unnecessarily complicate the ore-transfer system by changing the orientations of the openings, with- out succeeding in the objective of improving the ground support conditions). Although successful predesign is the prime objective, subsequent modifications in mine lay- out and sequence of extraction operations are inevitable. In developing the modified solution, systematic experimentation based on an understanding of the underlying structural relationships, coupled with monitoring measurements of selected diagnostic structural-behavior parameters, can achieve an acceptable solution in a minimum number of steps, which is far superior to the typical operational trial-and-error approach, in view of the cost of implementing each successive change. Since a drill-core sample of ore rock from a successful undercut-cave operation may exhibit a uniaxial crushing strength in excess of 100 MPa, the caving of such a rock mass is now commonly believed to be ascribable to the presence of discontinuities such as joints or fractures throughout the ore body. An essential part of the present investigation was therefore to characterize the natural discontinuities at each of the test sites by measuring their attitudes and spacings. The term "fracture" is used herein in a general sense to include any planar discontinuity without implication as to its suggested mode of origin. Most, but not all, of the fractures are properly termed joints. As a point of departure we may consider the possibility that the rock mass is transected by three families of joints, each family possessing a distinct orientation, such that parallelepipeds of intact rock are delineated by the jointing. Even if cementation is absent between adjoining parallelepipeds, the undercutting of the rock mass will not necessarily initiate sustained caving--owing to the all-around confinement, an arch may tend to stabilize over the undercut unless prevented from doing so by the failures of key blocks of intact rock. Thus, although the jointing can be assumed to weaken the rock mass, creating preferred directions of

Jan 1, 1981

By E. Wainer, K. D. Burnham

A wet beneficiation technique for producing wollas-tonite from its ore in high yield and purity has been evaluated in a pilot plant operation at the rate of 75 tons per month. Finely crushed, unsized wollastonite ore mixed with water is passed through a high in tensity oscillating wet magnetic separator of unique design and in a single pass over 90% of the wolla-stonite exhibiting a crystal purity of 99.8% is obtained irrespective of size of feed fraction. Thereafter, the material is processed by closed cycle standard wet milling and classification techniques to yield a 1µ size product, though any mesh size up to and including 50 mesh may be obtained, if desired. Costs appear to be significantly lower than those available from dry processed techniques. Wollas tonite made by this unusual wet process appears to have potential utility in the following fields: ceramics, paints, plastics, paper, organic finishes, reinforcement of portland cement items, controlled porosity refractory ceramic foams, cinder and concrete block paint, and the like. The 1µ and certain chemically processed varieties of wollastonite may have unusual utility in the paper industry both as a filler and as a coating material and in the organic finish industry. Extensive deposits of wollastonite ore equivalent to an average tenor of 50% to 60% of this latter mineral in easily separable form exists in and around Essex County in northern New York State in reserves of the order of several tens of millions of tons. While important portions of these deposits are susceptible to open pit mining techniques, one operation near Wills-boro, N.Y., involves tunnel mining and dry milling and beneficiation techniques. This mill and tunnel mine is presently being operated by The Cabot Corp. and a variety of particle sizes are now sold into markets in the ceramic, paint, plastic finish, floor tile and in similar fields in substantial tonnages on a repetitive basis. Serious investigation and study over the past several years has indicated that, outside of the obvious economies of open pit techniques for mining purposes, wet beneficiation and milling procedures applied to the ore not only represent a potential for greater economies in the production of a superfine finished product but yields products of improved properties exhibiting increased market potential which may not be available from the dry ground product. The Lewis and Deerhead deposits, controlled by the Adirondack Development Corp., appear to be identical to the Wilisboro deposit. Utilizing ore taken from the Lewis and Deerhead deposits, a pilot plant process for the wet beneficiation, milling and classifying of wollastonite ore has been operated for several months. After scalping a marketable garnet product from a minus 16 mesh dry crushed feed on a high intensity roll magnet the balance of the material is then roll crushed in a closed cycle until it will pass a 50 mesh screen. The product constitutes the feed of the wet magnetic separator. The heart of the new beneficiation process is a cyclically operated wet magnetic separator which exhibits the unique feature that unsized feed is easily handled. Product yields of higher purity are equal to that obtained with dry magnetic separations which use closely sized dry ore and multiple passes, but only produce wollastonite of about 98% mineral purity as determined by sink float techniques. It was anticipated that the wet processing through the grinding, milling and classification stage would yield a low cost 1µ ground product which should make available greatly increased applications for the mineral beyond those presently enjoyed. The improved purity was also expected to provide coarser sizes which might be utilized as a raw material for chemical modification which again would expand the uses of wollastonite. The evidence thus far collected appears to indicate that this premise may be expected to be fulfilled. There are on the surface of wollastonite particle sites at which cheinical reactions may occur1. It is believed that wet ground material provides a better base which will allow wollastonite a deeper entree into the field of chemical raw materials. Wet ground at 20µ and finer permits with certainty a number of chemical reactions, some of which are mentioned later in this article. While well crystallized wollastonite makes up the majority of the ore, the balance consists mainly of very weakly magnetic diopside of the hedenbergite-

Jan 1, 1965

By Y. C. Liu, W. R. Hibbard

Based on pole figure data and microstructural observations, the re-crystallization orientation found in a copper strip previously cold-rolled 99.5 pct from a single crystal with an initial (110) [112] orientation may be described as: a 30° rotation, clockwise and counterclockwise, about octahedral poles of the cold-rolled texture such that all four poles function at a low annealing temperature (400°C) and only three of them function at high temperatures (500' to 1050°C). The relative intensity of deformation stresses on various slip planes can be correlated with the choice of poles affecting the rotations found in the recrystallized orientations. ROTATIONAL reorientation about the poles of densely packed crystallographic planes is an important characteristic of secondary recrystallization" in face-centered cubic metals. Some evidence has also been interpreted to show that such a rotational relationship also exists in the primary recrys-tallization process." In an investigation of the crystallographic relationships in the recrystallization process, several aspects of the experimental procedure should be considered. With cold-rolled poly-crystalline metal as the initial material, pole figure analysis leaves many ambiguities as to whether or not simple indices can be assigned to adequately represent its orientation. The rolling texture does not consist of a single texture. Minor deformation textures are usually present. In all cases, twin textures are present. The presence of both minor and twin deformation textures influences the recrystallization texture. In order to study the recrystallization mechanism, a more precise knowledge of the history of the material before recrystallization is necessary. Tensile deformation of a single crystal usually produces residual stresses which are concentrated at slip bands. Since the exact nature and orientation of these potential nuclei sites cannot be experimentally evaluated, the tensile deformation of a single crystal was not considered adequate. From the work done by Barrett and Steadman6 n copper, it appeared that cold rolling of a single-crystal specimen with an initial (110) [112] orientation would yield a specimen which fulfills the conditions required for the present investigation, namely a highly preferred single rolling texture with relatively homogeneous stress distribution. By investigating the recrystallization texture of this material, additional details of reorientation during recrystallization might be obtained. The purpose of this paper is to describe such an investigation. Experimental Procedure Copper used in the present investigation was cathode sheet with a purity of 99.94 to 99.97 pct. A copper single-crystal specimen, 1.15x0.8720x0.5322 in. (thickness) was cut from a cylindrical crystal which was grown in a Bridgman furnace.' The cutting was accomplished on a horizontal milling machine operated at a very slow speed to obtain a (110) plane in the rolling plane and a [112] direction in the rolling direction. The disturbed surface was removed by electrolytic polishing in dilute orthophos-phoric acid (H3PO4) with a specific gravity of 1.14, and a current density of about 1 to 2 amp per sq cm. A 3-min polishing was needed to eliminate the disturbed surface causing Debye-Scherrer rings and a 45-min polish produced a surface which yielded sharp rounded Laue spots. It was estimated that about 1/16 in. of metal was removed from the original cut surface. The final orientation of this specimen before rolling was about 2" from the (110) plane in the rolling plane with a [112] direction aligned in the rolling direction. It is possible that a small amount of strain was still present in the cube despite the fact that the Laue spots seemed very sharp. It is doubtful, however, that this would be an important factor after a subsequent rolling reduction of 99.5 pct. This copper specimen was rolled on a laboratory rolling mill with two highly polished rolls 37/8 in. in diam in the following manner: 0.010 in. per pass to 50 pct reduction, 0.005 in. to 70 pct, 0.002 in. to 85 pct and, finally, 0.001 in. per pass to a 99.5 pct reduction. Specimens, about 1 in. sq with the rolling edges intact, were cut from the rolled strip by the electrolytic method previously described, after the strip

Jan 1, 1954

By W. D. Robertson, E. G. Grenier, V. F. Nole

The electrical, mechanical, and corrosion cracking properties of an age-hardenable Cu-Ni-Si alloy have been studied over a range of time, temperature, and deformation states for the purpose of determining the relationship between the properties and the structural state. The precifitate has been identi3ed as and the sites of preferred precipitation have been located by electron microscope studies of the structures developed by various combinations of heat treatment and plastic deformation. An extreme form of deformation banding has been observed in the aged alloy that results in high strain concentration in bands lying parallel to {111} planes. These bands are the structural paths along which transcrys-talline cracks propagate in the deformed alloy. The observations provide a basis for a general mechanism of transgranu-lar corrosion cracking of face-centered cubic alloys in terms of stacking fault probability. AMONG the age-hardening copper alloys the copper-nickel-silicon (Silnic Bronze) type is outstanding in exhibiting a high strength combined with a considerable capacity for cold working, a relatively high conductivity, and a low to negligible susceptibility to stress corrosion cracking. It is not a new alloy and it has been the subject of a number of investigations,1-5 which were made primarily to establish practical composition and heat treatment limits. The structural characteristics of the aging processes in this alloy have not previously been studied in detail. This particular investigation was undertaken to explore, in detail, and over a wide range of conditions, the properties obtainable by various combinations of working and heat treatment and to correlate structural changes with the observed mechanical, electrical and corrosion properties. MATERIAL AND PROCESSING Eight different commercial heats of the alloy were made and used in the investigation. The range of composition among the eight heats is shown in Table I. Billets, 8 by 24 in., were cast into water-cooled molds, extruded to 1.687-in. rod, and quenched in water after extrusion. Extruded material was rod rolled to 0.750 in., annealed at 1450° F for 2.5 hr, and quenched in water. Subsequent working operations were performed by tandem rolling to various sizes depending on the degree of reduction required. Final cold-working operations were performed by drawing to a uniform size of 0.187 in. diam and straightening by a roller straightening machine (Lewis). The combinations of heat treatment, working and aging that were investigated are summarized in Table 11; the various treatments were performed in the order given in each row of the table, and they will be subsequently identified by the symbols shown in the first column. SOLUTION TREATMENT All material investigated in the cold-worked condition, or cold worked prior to aging, was solution

Jan 1, 1962

By Leonard H. Goldman, Harold E. Marr

The PGT uranium assay probe is a borehole tool developed by Princeton Gamma-Tech over the last several years. It has the ability to do an in-situ assay of uranium in the presence of any amount of disequilibrium. It has some advantages over coring including cost, speed of analysis, and accuracy. In this paper we would like to give a brief description of the measurement and then show some sample logs from South Texas. Uranium exploration and development is carried out primarily by gamma logging since uranium daughters are prolific emitters of gamma rays. The conventional gross gamma tool for uranium logging is limited in value because of the inability of this tool to distinguish uranium from its daughters and other naturally occurring radioisotopes, such as potassium and thorium. This problem becomes severe in cases of disequilibrium. Disequilibrium, in a geological context, is defined as the condition when the gamma radiations from the daughter products are being emitted in a location different from that of the parent uranium. In the decay chain of uranium almost all the gamma radiation emitted in the entire chain comes from the daughter product, bismuth-214. Bismuth-214 is separated from uranium by several long-lived isotopes that are chemically active and have different physical properties, often resulting in shifts in the location of bismuth- 214 relative to the parent uranium. In the United States orebodies exhibiting disequilibrium are a common occurrence and the use of a gross gamma log to delineate uranium orebodies can lead to errors. At present the solution to the disequilibrium problem is extensive coring followed by chemical analyses of the cores. There are several drawbacks in using this technique. First is the high cost of coring, the second is the fact that no results are available for days, or typically, weeks after the drilling is done. Thus for development work, coring and drilling must be done on a grid basis and many additional holes are cored to ensure that the entire orebody is mapped. Another disadvantage to cores is the fact that a small volume is sampled, the volume of the core itself. This leads to problems in the mapping out of the orebody when the ore de- posit is not very homogeneous. The PGT probe described in this paper is a new solution to the disequilibrium problem. Basically, the probe measures radiations that come almost directly from uranium itself. The first daughter of uranium, which is protactinium-234 (Pa-234), is only separated from uranium by a 24-day half-life and no disequilibrium problems build up in such a short time. The PGT probe measures the intensity of a one MeV gamma line emitted by Pa-234 and, using this information, calculates the concentration of uranium. The PGT probe is 24" in diameter and 12 feet long. The probe contains a microprocessor which passes the information to a larger minicomputer in the truck. All data is analyzed on site, and the results from a high speed printer are presented to the geologist. Data is also available on 9- track IBM compatible tape for further processing. The PGT probe output is linear with uranium concentration. The only correction factor is for borehole size, and that only becomes important in boreholes bigger than seven inches in diameter. Dead time is compensated in the probe itself and no problems have been encountered in ore zones up to several percent UjO8. In addition to the uranium assay, a conventional gross gamma log is plotted alongside. Grade thicknesses for zones above cutoff are calculated as well as disequilibrium factors. COMPARISONS During its commercial operation PGT logged a series of 18 holes that had been cored and assayed. All of the holes in this series were logged in normal operation by regular field operators. The time to log each hole was generally under an hour, and in typical operation a PGT logging truck will do between 7 and 8 holes a day. The results of the comparison of the PGT and the core assays are presented in a series of figures showing plots of the PGT assay, core analysis and gross gamma measurements. The first three figures show individual holes with the gross gamma plotted along with the core and the PGT assays. All three logs were from holes on the reduced side of a rollfront deposit in South Texas. In Figure 1 we see the two wings of the roll- front at 143 ft and 150 ft separated by a barren zone. The wings are well defined both by the PGT assay and the core. There is approximately a one foot shift which can be attributed to drilling errors. The gross gamma is showing a rather severe discrepancy, being considerably lower and not showing the barren zone. The grade thickness calcula-

Jan 1, 1980

By I. S. Levy, J. L. Brimhall, B. Mastel

Specimens of' Hastelloy X-280, a low-cobalt version of the solid-solution- hardened nickel-base alloy Hastelloy X, were given a series of thermomechanical treatttzents. They were then Lensile-tested at room temperature and 1350°F. The Microstructures of the specimens tested at 1350°F were studied by electron Microscopy. Microscopy showed that dislocation tangling, caused by the cold working, mas still in evidence after aging-for 24 hr to temperatures as high as 1550oF. (Cr, Mo)23 C6, (Fe, Mo)6 C'. as well us an unidentifiable phase precipitale due to the combination of the thermomechanical treatments and subsequent tensile strain. The room -temperature and 1350°F tensile properties show a general increase ill strength and decreccse in ductility with increusing cold-work level. This is due to the dislocation taangling-. PerLurbatiot~s to this general trend occur- due to solid-solution weakening at the higher cold-work levels as a direct result of the preciplitation reactions. THE requirements for corrosion resistance and high-temperature strength place nickel-base alloys among the more promising materials for advanced nuclear reactor applications. However, when these alloys are irradiated at service temperatures, they generally suffer severe embrittlement'" and reduction in rupture life.3 Certain experimental treatments resulted in improvements in the tensile and stress-rupture properties of Hastelloy X-280, a solution-hardened nickel-base alloy.' To provide a basis for understanding these improvements, unirradiated tensile specimens were examined by electron microscopy. The results are reported in this paper. EXPERIMENTAL DETAILS Material. Hastelloy X-280, a low-cobalt version of Hastelloy X, is a member of the solution-hardened class of nickel-base alloys. The Hastelloy X-280 was obtained from 4- and 1-in: thick plates in the mill -annealed condition. Table I gives the chemical composition of the material as reported by the National Spectrographic Laboratories. ~x~erimental Treatments. Plates of suitable size, 12 by 3 by 1 in., or by + in., were cut under a water jet from the stock material and examined ultrasonic -ally for homogeneity of grain size and absence of voids. The acceptable plates were solution-treated at 2150°Ffor 1 hr and air-cooled. These plates were then reduced in thickness by cold rolling 0, 10, 15: or 20 pct along the original rolling direction. The plates were machined into buttonhead tensile specimens with a gage diameter of 0.125 in., with a gage length of 1.125 in., and with their tensile axes parallel to the rolling direction. The specimens were examined for quality of finish with a penetrant dye, ultra son ically checked for voids, and finally given a dimensional tolerance check with an optical comparator. The acceptable specimens were aged for 24 hr at either 1000" or 1500 F and air-cooled. These specimens were then held at 540°F in a water loop for approximately 18 days to qualify as controls for similar specimens irradiated under the same conditions of time, temperature, water chemistry, and flow rate. Table U summarizes the treatments. These treatments were investigated to establish whether prior precipitation and stabilization of carbide phases at strain sites within the matrix could reduce the amount of carbides available for precipitation at grain boundaries during service. Tensile-Test Conditions. Specimens were tested to fracture at room temperature or 1350 F in air on an Instron tensile-testing machine at a crosshead speed of 0.05 in. per min. The time for the furnace to reach equilibrium at 1350°F was approximately 30 min; soak time prior to testing was 15 min; and test duration was approximately 5 min.

Jan 1, 1968

By R. I. Lahring, C. G. Inks

A surfactant waterflood, using a block copolymer of ethylene and propylene oxide (PLURONIC L64*), wa., started in 1956 in Kansas to determine the commercial feasibility of such a process. The production formation was the Bartlesville sand at a depth of 1,400 ft. Leares in the test area had attained both primary and secondary production peaks, and were on a normal decline when the tests were initiated. The injection wells were taking water at a reasonable pressure and none of the operating conditions were particularly unusual. The leases were selected primarily because of normal operating conditions, and not because of any serious problems demanding remedie>,. Oil production and water injection data were recorded during the 10-year test period, and their compilation indicates that the surfactant resulted in an increase of about 9 percent in secondary oil production. Other benefits derived from the surfactant injection were lower injection pressure that resulted in reduced power consumption and reduced erosion of the pumps; and lower calcium scale buildup. These fringe benefits more than offset the cost of the surfactant used. Introduction During the past several decades, considerable research has been carried out on secondary recovery of crude oil that remains in the producing formation despite the most efficient, current primary production practices. Methods are constantly sought of increasing recovery of oil, while at the same time improving the economic efficiency of operations. One method that has received intensive study over the years is the use of a surfactant as a waterflood additive. Laboratory tests show conclusively that dilute solutions of surfactants remove considerably more oil from uncon-solidated sand cores than does water alone.'- The loss of surfactant by adsorption at solid-liquid interfaces has caused serious doubt that surfactants can be used economically as waterflooding additives. This is especially true with anionic and cationic surfactants, and to a lesser extent with nonionic surfactants. This work was undertaken to determine the effectiveness in increasing oil production by injecting water containing small quantities of a nonionic surfactant. The surfactant selected was PLURONIC L64*, a block copolymer based on ethylene and propylene oxide, having the following structure The selection of the test site, a typical shoe-string sandstone type of field located at Batesville pool, Toronto District of Woodson County, Kans., was made because of its normal primary and secondary recovery operating conditions, and not because of any serious operating problems. When the tests were begun, the field was experiencing the customary post-peak production decline of a waterflood. Using for the tests a field that was on a normal production decline, while maintaining constant all variables other than the addition of the surfactant. was of varamount importance if success or failure was to be attributed to a particular cause. It was reasoned that if a surfactant was added to the injection waters and nothing else was done to influence the oil production or injection of water, the effects of the surfactant on the flood could be determined precisely. Production History The first well in the tested field was drilled in 1935. Gas repressurization began immediately, but it was not until Aug., 1938, that the major portion of the field was developed. During the period of repressurization, 1,700 MMcf of gas was injected. As can be seen from the curves of Fig. 1, the production peak from gas injection was attained in 1937 and a normal production decline followed. Early in 1942, water injection wells were drilled and injection of water Was initiated. The amount of water injected increased as more injection wells were drilled until a peak injection rate of 2,700 BID was reached in

Jan 1, 1969

By L. F. Coffin

Monotonic tension and controlled cyclic-strain tests have been conducted on an annealed steel at various strain rates and temperatures in the weep range. Evidence of a strain-induced precipitate reaction abozle 500°C was determined from pronounced cyclic-hardening effects, increase inflow stress, inter granular fracture, drastic decrease in low-cycle fatigue resistance, and loss in tensile fracture ductility, as well as through electron-microscopy examination. It was found that strain rate as well as temperature had a pronounced effect on these observations. A parameter of the form P = T(7.95 - log ip) was determined, which was directly related to the ductility, defined either as the true strain at fracture in the case of simple tension, or as 2N 1/2 ? E p in the case of cyclic plastic strain. A highly satisfactory comparison of the cyclic life as measured and as computed from the ductility predicted by this parameter was obtained for a range of temperatures from 400° to 650°C and for crosshead speeds of 0.002 to 0.2 in. per min. MANY metals subjected to sustained loading at elevated temperatures derive resistance to creep from solid-state reactions of various alloying constituents. These reactions can be many and varied, and occur as a consequence of time and temperature according to reaction-rate principles. Strong evidence exists that many of these reactions are influenced by plastic strain, the argument being put forth that dislocations act as sites for nucleation and growth for the new phase.' Many examples can be cited where plastic strain during transformation influences the structure, and as a consequence affects the properties.2 The low-alloy steels serve as particularly good examples for investigating the effect which aging reactions have on resulting properties. Alloying elements such as carbon and nitrogen, and carbide formers such as manganese, chromium, molybdenum, and so forth, can, by the particular aging reaction which occurs, produce strengthening effects at various temperatures, and so endow strength to the alloy over a broad range of temperatures. These effects have been systematically studied by Glen both during creep3 and for constant strain-rate tension testing.4,5 The work of Glen is of considerable interest in connection with the present study, particularly in regard to the effect of various alloying additions on the true stress-strain curve and on fracture ductility at various elevated temperatures. He has shown that strain-age hardening occurred during plastic straining, which was quite specific both to the temperature of the test and to the alloying element involved. When strain-age hardening was noted at a particular temperature, a .minimum in reduction of area was also obtained. Provided the temperature for the minimum reduction of area exceeded 300°C, all minimum ductility fractures were found to be inter-crystalline in nature. For carbon steels containing molybdenum, two minima in reduction of area were noted, one occurring at 200° to 250°C, the precise temperature depending on the percentage of molyb-

Jan 1, 1964

By W. M. McKewan

Magnetite pellets were reduced in flowing hydrogen at pressures up to 40 atm over a temperature range of 350° to 500°C. The rate of weight loss of oxygen per unit area of the reaction surface was found to be constant with time at each temperature and pressure. The reaction rate was found to be directly proportional to hydrogen pressure up to 1 atm and to approach a maximum rate at high pressures. The results can be explained by considering the reaction surface to be sparsely occupied by adsorbed hydrogen at low pressures and saturated at high pressures. PREVIOUS investigation1,2 have shown that the reduction of iron oxides in hydrogen is controlled at the reaction interface. Under fixed conditions of temperature, hydrogen pressure, and gas composition, the reduction rate is constant with time, per unit surface area of residual oxide, and is directly proportional to the hydrogen pressure up to one atmosphere. The reduction rate of a sphere of iron oxide can be described3 by the following equation which takes into account the changing reaction surface area: where ro and do are the initial radius and density of the sphere; t is time; R is the fractional reduction; and R, is the reduction rate constant with units mass per area per time. The quantityis actually the fractional thickness of the reduced layer in terms of fractional reduction R. It was found in a previous investigation2 of the reduction of magnetite pellets in H2-H,O-N, mixtures, that the reaction rate was directly proportional to the hydrogen partial pressure up to 1 atm at a constant ratio of water vapor to hydrogen. Water vapor poisoned the oxide surface by an oxidizing reaction and markedly slowed the reduction. The enthalpy of activation was found to be + 13,600 cal per mole. It was also found that the magnetite reduced to meta-stable wüstite before proceeding to iron metal. The following equation was derived from absolute reaction-rate theory4,8 to expfain the experimental data: where Ro is the reduction rate in mg cm-2 min-'; KO contains the conversion units; Ph2 and PH2O are the hydrogen and water vapor partial pressures in atmospheres; Ke is the equilibrium constant for the Fe,O,/FeO equilibrium; Kp is the equilibrium constant for the poisoning reaction of water vapor; L is the total number of active sites; k and h are Boltzmann's and Planck's constants; and AF is the free energy of activation. Tenenbaum zind Joseph5 studied the reduction of iron ore by hydrogen at pressures over 1 atm. They showed that increasing the hydrogen pressure materially increased the rate of reduction. This is in accordance with the work of Diepschlag,6 who found that the rate of reduction of iron ores by either carbon monoxide or hydrogen was much greater at higher pressures. He used pressures as high as 7 atm. In order to further understand the mechanism of the reduction of iron oxide by hydrogen it was decided to study the effect of increasing the hydrogen pressure on rebduction rates of magnetite pellets. EXPERIMENTAL PROCEDURE The dense magnetite pellets used in these experiments were made in the following manner. Reagent-grade ferric oxide was moistened with water and hand-rolled into spherical pellets. The pellets were heated slowly to 550°C in an atmosphere of 10 pct H2-90 pct CO, and held for 1 hr. They were then heated slowly to 1370°C in an atmosphere of 2 pct H2-98 pct CO, then cooled slowly in the same atmosphere. The sintered pellets were crystalline magnetite with an apparent density of about 4.9 gm per cm3. They were about 0.9 cm in diam. The porosity of the pellets, which was discontinuous in nature, was akrout 6 pct. The pellets were suspended from a quartz spring balance in a vertical tube furnace. The equipment is shown in Fig. 1. Essentially the furnace consists of a 12-in. OD stainless steel outer shell and a 3-in. ID inconel inner shell. The kanthal wound 22 in. long, 1 1/2, in. ID alumina reaction tube is inside the inconel inner shell. Prepurified hydrogen sweeps the reaction tube to remove the water vapor formed during the reaction. The hydrogen is static in the rest of the furnace. The sample is placed at the bottom of the furnace in a nickel wire mesh basket suspended by nickel wire from the quartz spring. The furnace is then sealed, evacuated, and refilled with argon several times to remove all traces of oxygen. It is then evacuated, filled with

Jan 1, 1962

By J. E. McDonald, J. G. Eberhart

A model is discussed from which the work of adhcslon .tor liquid transition metals on aluminum oxide surfaces can he calculated, A close-packed (00011 oxygen surface on A12O3 is assumed with two different types of surface sites: one type involving metal-oxygen bonds and the other man der Waals into actions. The work of adhesion is thus expressed as the sum of these two bonsding free energies. Calculated works of adhesion for nickel, titanium, chromium, and zirconium on sapphire agree well with the experimentally determined quantities. The model is extentled to the calculation of the work of adhesion and shear stress required to remove a thin metal film from a sapphire substrate and is in good agreement with experimental values. The obsewed dependence of the work of adhesion on the free energy of oxide formation of the metal is shown to also provide an interpretation of the tittle dependence of thin-film adhesion. THIS paper presents a model for the type of bonding which occurs across a metal-A12O3 interface. The model is used to explain the results of two types of experiments in which such an interface exists: 1) the adhesion of thin metal films on Al2O3 substrates and 2) the wetting of A12O3 by liquid metal drops. The adhesion of thin films to various substrates has been the subject of a variety of investigations.'-' Benjamin and weaver3 and Bowie,6 using the scratch test developed by Heavens,10 studied the adhesion of metallic films to glass substrates. Their observations for noble-metal film adhesion agree well with an adhesion model involving a van der Waals type of bonding between the film and the substrate. For films of metals whose free energy of oxide formation. ?F°f, has a negative value. Benjamin and weaver3 and Bowie6 found a time-dependent adhesion with an initial value that can be interpreted in terms of van der Waals interactions but a larger terminal value which was related to ?F°f, Karnow-sky and Estill7 deposited films on sapphire at elevated temperatures and noticed no time dependence of film adhesion but a similar correlation with ?F°f. Because of the kinetic problems associated with thin-film adhesion it is desirable to examine adhesion in an equilibrium system. The wetting behavior of liquid-metal drops on Al2O3 provides such a system. Systems of this metal-ceramic type have been studied extensively.11 Humenik and Kingeryl2 have measured the wetting of A12O3 (and other substrates) by several metals and have pointed out that the wetting ability of these metals increases with increasing values of -?F°f. It is thus seen that thin-film adhesion and metal wetting on A12O3 are both related to the tendency of the metal to react with the surface oxide ions of the Al2O3 substrate and, because of this, both phenomena should be explainable by an appropriate model for the metal-Al2O3 interfacial bonding. In the sections that follow, wetting and adhesion data on A2O3 are reviewed and a model is presented by which these phenomena can be interpreted. ANALYSIS OF WETTING EXPERIMENTS In an equilibrium system involving a liquid-metal drop on a solid Al2O3 substrate, the work of adhesion, WAD, is defined by the Dupre, equation as WAD = ?s + ?L -?sL [1] where ?s and ?L are the surface free energies of the solid substrate and the liquid drop, respectively, and ?sL is the interfacial free energy. The work of adhesion is the work required to separate a unit area of the solid-liquid interface into two surfaces. The work of adhesion is usually determined from a sessile-drop experiment in which yL and the contact angle, ?, are measured. The Young-Dupr6 equation is then used to calculate WAD Wad = ?L (1+ cos ?) [2] The literature of this subject has been examined and Table I shows work of adhesion data for various liquid metals as measured on A12O3 substrates. The standard free energy of oxide formation of the metal at the temperature of the wetting experiment, ?F°f . is also tabulated in kcal per g-atom of oxygen. The data is grouped according to the gaseous atmos-

Jan 1, 1965

By M. J. Marcinkowski, A. S. Sastri

A detailed compressive stress-strain analysis and transmission electron microscopy investigation has been made of the deformation behavior occurring in a 50 at. pct Ni-Ti (hypoeutectoid) alloy and a 54.5 at. pct Ni-Ti (hypereutectoid) alloy. In the case of the hypoeutectoid alloy, three stages of work hardening are observed. Stage I occurs at a very low stress and is associated with plastic deformation via martensite formation. Stage 11 is characterized by very rapid work hardening and is due to difficulties in causing further deformation in the fine martensite aggregate produced in Stage I. Stage III which occurs at very high stress levels is characterized by smaller work hardening rates and is due to the plastic deformation arising from alternate reconversions of the original martensites to martensites of varying orientation. Rapid quenching of the hypereutectoid alloy leads to very high yield strengths and is related to a fine precipitate dispersion that such treatment brings about. The present investigation represents the final phase of a three-part study directed toward an understanding of the solid-state transformations in near equi-atomic Ni-Ti alloys as well as the deformation mechanisms associated with these alloys. In the first part,"2 to be henceforth referred to as I, it was found that alternate simple shears on {112} planes and in (111) directions convert the parent B2 structure in the equiatomic NiTi alloy into two distinct close-packed monoclinic martensites. All of the marten-sites were of this type, whether they were formed by cooling or by plastic deformation, whether induced to form in bulk samples or in thin foils, or whether examined in the electron microscope at room temperature or below. On the other hand, in the second part of this investigation,3 to be reffered to as 11, it was shown that upon slow cooling to about 640°C. alloys in the neighborhood of NiTi which possess the B2 structure transform eutectoidally into their equilibrium phases Ti2Ni and TiNi3. However, preceding the formation of these equilibrium phases a series of metastable intermediate phases are formed. This paper will set as its goal the elucidation of the remarkable deformation behavior exhibited by NiTi. In particular, Buehler and Wiley4 have found equiatomic NiTi to be surprisingly soft, while Buehler et al.5 have shown this alloy to possess a memory effect: i.e., upon bending at room temperature it will revert to its original shape when heated to above about 50°C. In I it was shown that NiTi was soft in the sense that the yield stress was low; nevertheless, the alloy work-hardened at an extremely rapid rate to very high stress levels. On the other hand, the hypereutectoid alloys with somewhat higher nickel, say 54.5 at. pct (60 wt pct) have enormously increased yield strengths compared to those of the equiatomic alloys. In order to determine the atomistic processes giving rise to the above behavior, it was decided to examine samples that were wafered from bulk specimens deformed in compression to various strains using the techniques of transmission electron microscopy. EXPERIMENTAL TECHNIQUE All of the alloys used in the present investigation contained either 50 at. pct Ni (55.06 wt pct) or 54.5 at. pct Ni (60 wt pct) and were arc-melted in the form of a finger using the same techniques described in I and II. The finger was capsulated in a stainless-steel jacket and swaged at 850°C into rods. Compression specimens 0.300 in, long and 0.200 in. in diam were machined from these rods. In order to completely re-crystallize the samples and remove residual stresses, all of them were capsulated in evacuated quartz, annealed for 1/2 at 1050°C. and then furnace-cooled. Compression tests were carried out in an Instron tensile testing machine covering a range of temperatures from —196° to 200°C using procedures described previously.6'7 In all cases crosshead speed was 0.02 in. per min. Wafers 0.015 in. thick were spark-cut from the cylindrical samples at 45 deg to the compression axes after they had been deformed to the desired strain. These specimens were then spark-planed to about 0.005 in. and then electrochemically thinned for examination by transmission electron microscopy as described in I.

Jan 1, 1969

By F. Weinberg

The relative concentration of 1" at grain boundaries in controlled orientation bicrystals has been examined by autoradiographic techniques, and by activity measurements of grain boundary surfaces exposed by preferential ,melting. The autoradio-graphs indicate that thallium is concentrated at grain boundaries in as-grown bicrystals, but not in zcell-annealed bicrystals. They also indicate that the solute concentration and the distribution on as-grown bicrystal surfaces are markedly different than that of the bulk material. The boundary surface measurements are in agreement with the autovadiographic evidence. On the basis of these measurements, as-grown bicrystals containing approximately 100 ppm of Tl, solidified at rates between 5 and 30 cm per hr and with tilt boundaries greater than 10 deg, exhibited grain boundary segregation equivalent to roughly 10 atomic planes of pure solute. Higher solute concentrations (equivalent to 140 atomic planes of pure solute) were obtained in bicrystals solidified slowly (0.6 cm per hr); slightly higher values were obtained in specimens containing a large angle nantilt boundary. Annealing for various times over a range of temperatures eliminated grain boundary segregation within the experimental uncertainty of the results (equivalent to 1 atomic Plane of pure thallium at the boundary). The results for the as-grown bicrystals can be qualitatively accounted for by assuming the presence of a groove on the solid-1iq;id interface, at the grain boundary. SOLUTE segregation at grain boundaries may be considered in two parts, namely, nonequilibrium segregation associated with the solidification process, and equilibrium segregation in fully annealed materials.' There is much indirect evidence for nonequilibrium segregation, based on preferential etching at grain boundaries and the mechanical properties of as-cast alloys. In addition, some direct observations have been reported in which radioactive tracers were used as solute additions and segregation detected at the grain boundaries by autoradiographic techniques. However, there is little detailed quantitative data on solute concentrations related to grain boundaries, particularly for different freezing conditions and grain boundary configurations. Equilibrium segregation at grain boundaries has been considered both theoretically and experimentally. cean' has made an estimate of the maximum equilibrium solute concentration that might be expected at a grain boundary, based on the lattice distortions in the boundary region. He arrived at a concentration which was equivalent t a monatomic layer of pure solute. A similar value, based on thermodynamic arguments, was calculated by Cahn and Hilliard for the segregation of phosphorus in iron. Experimentally, much higher values of solute concentration at grain boundaries have been reported recently by both Inman and iler' for phosphorus in iron, and Ainslie et 1.' for sulfur in iron. They observed concentrations equivalent to as much as 20 to 100 atomic layers of pure solute at the grain boundaries. However, in both cases it was shown that the observed segregation was not due solely to equilibrium segregation at the grain boundary. In the former case, precipitation effectss due to trace impurities in the material were believed to account for the large amount of solute present at the grain boundary. In the latter case it was shown that a high density of dislocations in the boundary region could provide a large number of additional sites for solute atoms, other than at the grain boundary. Thomas and chalmera have reported on the equilibrium segregation of po210 in grain boundaries of Pb-5 pct Bi alloys. Using autoradiographic techniques, they observed a concentration of polonium along the boundary trace on the surface of annealed bicrystal specimens grown from the melt. The concentration only appeared after annealing, and varied with boundary angle, increasing as the boundary angle increased. Their conclusions have been questioned by Ward," who pointed out that the segregation they observed along the boundary trace was much too wide to be compatible with the usual concepts of the thickness of a grain boundary of several lattice spacings. Also, Maroun et al.,l1 with specimens similar to those of Thomas and Chalmers, found that segregation could only be detected on the specimen surface, suggesting that Thomas and Chalmers' results were associated with an oxidation effect of polonium, and not equilibrium segregation. Thomas and Chalmers replied12 that they did observed segregation at the grain boundary in the bulk material and suggested further experiments were necessary to resolve the difference. The purpose of the present investigation was to examine both nonequilibrium and equilibrium grain boundary segregation in melt grown bicrystal specimens as a function of boundary angle, growth rate, and solute concentration, and to de-

Jan 1, 1963

By David D. Rabb

Leaching or solution mining, a relatively simple and economical process for beneficiating metallic ores, is likely to find increasing application in the treatment of low-grade ores that are impractical to mine by any other means. This process may be carried out in two different ways: 1) dump leaching, where the ore is moved from its original location to be leached at another site; and 2) In-situ leaching, where the ore is leached in place by introducing the leach solution at the top, letting it flow down through the ore under gravity, and then recovering it plus the dissolved metals it contains. Whichever leaching method is used, it is almost always necessary to break up the ore before leaching. In this paper a study is reported which indicates that rock broken by an explosion-in particular, an underground nuclear explosion-is significantly more amenable to leaching then is rock broken by other methods. These results suggest that the leaching speed and efficiency could be increased by nuclear fracturing of the ore. Not only would the leach time be shortened, but the resulting increase in strength or richness of the solutions would decrease plant installation expense as well as reduce pumping and processing costs. A considerable fund of experience has been accumulated in the course of several hundred experimental underground nuclear explosions, so that the gross results of any given nuclear explosion can now be predicted with a fair degree of confidence.' From this knowledge it seems clear that, under the proper conditions, large ore bodies can be fractured much more economically-macroscopically speaking-by nuclear explosions than by other methods. The present study concentrates on smaller scale effects that is, the cracks in the chunks of rock broken by the explosion-and shows that here too, in the microscopic domain, there are important advantages to nuclear fracturing. The intense shock produced by the very fast acting, high-brisance nuclear explosive fractures the rock in a way that should significantly improve its leachability. Experimental Procedure This study compared rocks broken by nuclear explosives with rocks produced by conventional mining, quarrying, or core drilling. The test samples, granite chunks 6 to 8 in. on a side, plus core sections, came from the area of the Hardhat*2 nuclear explosion and were taken both before and after the explosion. For comparison, several samples of quarried granite were obtained from a local gravestone monument company. The general procedure was to soak the test samples in leaching solution and then determine the extent of penetration. A standard commercial copper leaching solution was used (10 gpl Cu, 10 gpl H2SO4, 5 gpl ferric Fe, 15 gpl total Fe, pH about 1.5), to which a water-soluble penetrant dye, Zyglo 1-c, had been added. Details of the procedure were as follows: 1) Sample leached in solution containing Zyglo penetrant dye. 2) Washed with water. 3) Air-dried. 4) Cut with granite wire saw. 5) One face polished with granite monument polish. 6) Sent directly to be photographed, or heated at 110°C for 2 hr and then sent to be photographed. 7) Photographed under ultraviolet light to show crack patterns. Results After 10 days of leaching at 70-75°F, the samples were removed from the solution, washed, dried, and cut in half with a granite wire saw to study the penetration of the leach solution. Since the Zyglo dye in the leach is visible under ultraviolet light, the degree of penetration of the leach (and hence the cracks in the samples) can be studied on photographs of the crosscut samples made under ultraviolet light. The photos in [Fig. 1] show how the leach solution penetrated various representative samples. Of the 71 rock samples examined, fractures were most frequent and prominent in samples from the rubble produced by the nuclear explosion [(Fig. 1D)]. Fracturing was less apparent in shaft-mined rock [(Fig. 1B)], still less evident in drift-mined rock [(Fig. 1C)], and practically nonexistent in cored or quarried specimens [(Fig. 1A)]. The samples in [Fig. lA-C] were from the same general area as the nuclear explosion, but they were obtained before the explosion. Results of the crack studies are summarized in [Table 1]. The Zyglo-treated leach solution penetrated the test samples at the rate of about 1/2 mm during the first hour, 1 mm by the end of 4 hr, 2 to 3 mm in 12 hr, and 4 to 6 mm in 10 days, showing a progressively slower rate with time.

Jan 1, 1972

By G. H. Bishop

The kinetics of the inter granular penetration and embrittlement of [100] tilt boundaries in 99.998 pct pure nickel upon exposure to bismuth-rich Ni-Bi liquids have been determined in the temperature range from 700° to 900°C. The kinetics of penetration are parabolic in time at constant temperature over most of the temperature range. In a series of 43-deg bicrystals the rate of penetration is anisotropic with respect to the direction of penetration into the grain boundaries. In lower-angle bicrystals the penetration rate is isotropic. The rate of penetration decreases with tilt angle at 700°C. The activation energy for penetration in the 43-deg bicrystals is 42 kcal per g-atom independent of direction. It is concluded that the intergranular penetration and embrittlement in the presence of the liquid proceeds by a grain boundary diffusion process and not by the intrusion of a liquid film. This was confirmed by a determination that the kinetics of penetration and embrittlement were the same in the 43-deg bicrystals upon exposure to bismuth vapor under conditions such that no bulk liquid phase would be thermodynamically stable. WhEN solid metals are exposed to a corrosive liquid-metal environment, the grain boundaries are sites of preferential attack. Depending on the temperature, the composition of the liquid, and the composition, structure, and state of stress of the solid, a number of modes of attack are possible. This paper reports a study of the kinetics of intergranular penetration and embrittlement of high-purity nickel bicrystals upon exposure to bismuth which, together with an earlier study by Cheney, Hochgraf, and Spencer,&apos; demonstrates that there are at least two modes of intergranular attack possible in the Ni-Bi system. In the study by Cheney et al., columnar-grain specimens of 99.5 pct pure nickel were exposed to liquid bismuth presaturated with nickel in the temperature range 670" to 1050°C. They found that the majority of the boundaries, which were predominantely high-angle boundaries, were penetrated by capillary liquid films, the attack proceeding by a process which will be termed grain boundary wetting. This process occurs in a stress-free solid when twice the liquid-solid surface tension is less than the surface tension of the grain boundary,* i.e., when 2yLs < YGB In this case the penetration of the grain boundary by the liquid occurs at a relatively rapid rate, resulting in the severe embrittlement of a polycrystalline solid. Grain boundary wetting is a common mode of intergranular attack in systems in which the lower melting component is relatively insoluble in the solid, but the solid has an appreciable solubility in the liquid, for example, the Ni-Bi system, Fig. 1. In systems of this type at temperatures above the range of stability of any intermetallic phases, once the liquid is saturated with respect to the solid so that no gross solution occurs, chemical gradients are small, and surface tensions become major driving forces for attack, provided the solid is stress-free. The results of Cheney et al. appear to be typical of those encountered when grain boundary wetting occurs.&apos; Capillary films were observed in the boundaries after quenching from the exposure temperature. The mean depth of penetration increased linearly with time, and the activation energy for the process was found to be 22 kcal per g-atom. In a study of the Cu-Bi system Yukawa and sinott4 found that the depth of penetration of bismuth into high-purity copper bicrystals of orientations from 22 to 63 deg of tilt about (100) at 649°C ranged from 0.05 to 0.25 in. after a 12-hr anneal. This corresponds to a linear rate of 6 to 15 X 10~6 cm per sec. At the same reduced temperature of 0.68 the rate for the Ni-Bi system&apos; was 7 x lo-&apos; cm per sec. In another study of the Cu-Bi system, Scheil and schess15 determined the kinetics of grain boundary wetting in hot-worked commercial rod. While there were several complicating factors present in this study, there is general agreement with the above results. The kinetics of penetration were linear, the activation energy was 20 kcal per g-atom, and at 650°C the rate of wetting was 2 to 5 x 10-6 cm per sec. The rate of wetting in the A1-Ga system6 is somewhat

Jan 1, 1969

By D. E. Spiller

Introduction Precious metals recovery from ore can generally be accomplished using gravity concentration, flotation, and/or hydrometallurgical (leaching) techniques. The objective of this paper is to show why gravity concentration can be an important part of recovery systems that employ leaching as the primary unit operation. A brief discussion of modem gravity concentration equipment is also presented. Discussion Gravity concentration of ores has generated increasing interest in recent years. Reasons for this interest include: • Gravity concentration is environmentally attractive. There is little or no use of reagents. Hence, it is relatively nonpolluting. • The cost of cyanide has continued to increase. Therefore, cost savings may be realized whenever leaching feed tonnage can be reduced by preconcentration. • Compared to flotation and leaching, gravity equipment costs are low per processed ton. Field installation costs for gravity circuits usually are less because many&apos; units are supplied as self-contained modules. Also, the cost required to supply services, particularly power, to a gravity plant site are also less. In situations where preconcentration at coarse particle size is applicable, significant grinding equipment savings may be possible. • Gravity circuit operating costs are also relatively low compared to typical flotation and leaching circuits. Reagents, power, maintenance, and manpower savings in a well-engineered gravity plant may be realized. Again, if grinding is reduced, significant power and steel (media and liners) savings are possible. •In recent years, more efficient gravity concentrating devices have been developed. Benefits to Precious Metal Leaching Gravity beneficiation can complement precious metal leaching in two ways. First, the recovery of coarse liberated values before leaching may reduce leach time requirements and may reduce reagent consumption. Second, gravity preconcentration can reduce the size of a leach plant by decreasing the quantity of material to be leached. Coarse gold and silver have been shown to leach rather slowly. Kameda (1949) and Habashi (1967) have investigated the kinetics of cyanide leaching systems. They concur that in a heterogeneous reaction, the rate of gold and silver dissolution is directly proportional to the surface area. Thus, the instantaneous rate of dissolution for spherical 0.37 mm (400 mesh) gold is theoretically -25 times faster than for the same amount of gold at .841 mm (20 mesh), based on data from Fuerstenau, Chander, and Abouzeid (1979). Conversely, coarse liberated, +.841 mm (20 mesh), gold is more readily recovered by gravity concentration than is fine, -.037 mm (400 mesh) gold. Therefore, it is apparent that the two recovery systems complement one another. Figure 1 data demonstrates the potential synergism. A sample of - 3.327 mm (6 mesh) Nevada gold-bearing ore was cyanide leached using conventional bottle-roll test procedures. Gold extraction was determined as a function of leaching time. A second sample split from the same leach feed material was hand jigged to remove a coarse heavy mineral fraction, including virtually all of the +.210 mm (65 mesh) liberated free gold. This second sample, with the coarse gold and heavy minerals removed, was subjected to an identical cyanide leach procedure. Figure 1 presents the resulting comparative extraction data. Note that the percent gold extraction for the sample containing no +.210 mm (65 mesh) free gold includes the coarse gold recovered by gravity. The data show that the sample containing coarse gold required about 72 hours of leaching time to achieve 80% extraction. This compared to about 22 hours of leaching time for 80% gold recovery from the sample that contained only -.210 mm (65 mesh) free gold. Thus, there was a 69% reduction in leaching time. The improved extraction data is not wholly attributable to coarse gold removal, but rather it was the combination of gold removal and rejection of other heavy mineral cyanide consumers or leach retardants. Further investigation was not warranted at this time. Preconcentration is the second manner in which leaching systems can benefit from gravity concentration. The premise is that preconcentration can reduce the quantity of leach feed, which, in turn, may reduce leaching costs. Figure 2 presents preliminary data developed by CSMRI for US Minerals Exploration (USMX). Centennial Exploration Inc., in agreement with USMX, is proceeding with evaluations to determine the suitability of various processing schemes for recovery of gold values from the Montana Tunnels property. The data shows how the ore can be preconcentrated by gravity techniques to result in a reduced feed tonnage to secondary extraction techniques, presumably flotation or cyanide leaching. Testing has shown that Reichert cones, followed by treating the cone concentrate on spirals, can deliver about 88% gold recovery in about 13% weight, that is, 87% weight rejection. Consequently, fine grinding and reagent costs are attributable to only 13% of the plant feed rate. Cost data is not yet available, but the potential exists for significant cost savings.

Jan 1, 1985