By D. W. Hoey

Eight years use of the ISA Process is reviewed and current design and operations described. Nodern Technology used for impurity control and disposal as well as the use of mechanised electrode handling equipment, cell voltage monitoring, cell insulation and an efficient contact bar system are described. Improvements achieved in terms of energy usage and plant productivity are detailed.

Jan 1, 1987

By Yutaka Shiraishi

Two methods were developed to measure the viscosity of the slag from the glassy to the liquid states in an ascending temperature process. The first method employs rotating parallel plates within which is placed a solid cylindrical sample in line with a sphere. The second method uses a tube which is pushed into a sample held in a rotating crucible. Both methods were tested using standard glasses, including boron trioxide and NBS standard glass #711. The main difference between these two methods is in sample preparation. Comparative measurements between two methods were performed using a sodium boro-disilicate glass containing 5%mol of alumina. The results showed good agreement in the mid-range of glassy viscosities, 105 to 107 Pa.s. In the liquid state, there were no significant differences between the two methods.

Jan 1, 2003

By Carl C. Nesbitt

A study was conducted to examine the treatment of metal-bearing effluents by precipitating the metals as sulfides and simultaneously collecting the particles by flotation. The precipitant was hydrogen sulfide gas which was introduced into a bench-scale column cell with air. The study included experiments of various flotation reagents and column configurations in treating solutions containing dissolved copper, lead, mercury, iron, zinc and cadmium. An acidic laboratory waste from a local copper operation was used to test the column with a solution containing several metals and arsenic. Precipitates were observed to form at the gas/liquid interface when the gas mixtures were rich in H2S. Copper, mercury, lead, and cadmium were precipitated from solution as sulfides to concentrations near detection limits. The flotation of these precipitates was enhanced with small amounts of S-7151 promoter from American Cyanamide Company and Dowfroth 1263 mixed with the feed. The recovery of the precipitates in this manner produced a smaller volume slurry which was easier to dewatering than a slurry produced by conventional precipitation techniques. The low pH and high oxidation-reduction potential in the cell from H2S addition was not conducive to form precipitates of iron, zinc or arsenic. However, these ions were precipitated as sulfides by raising the pH of the column discharge.

Jan 1, 1994

By W. F. Ranson, R. C. Progelhof

"I. THE PROBLEM: MANUFACTURING PRODUCTIVITYThe 1985 President's Commission [I] on Industrial Competitiveness found compelling evidence of the declining economic position of the United States in world markets. The annual rate of increase in the United States productivity is approximately one-seventh that of our major trading partners over the last decade: profit levels in manufacturing investments are below those of the mid-1960's; an increasingly negative trade balance since 1971; and a sharp decline in the United States share of world trade in manufactured goods for more than two decades. A particularly dramatic example of the shifting economic balance is the fact that Japanese productivity growth has been five times greater than that of this country since 1960. In face, Japan's productivity now exceeds that of the United States in such critical industries as steel, transportation equipment, electronics and electrical machinery.American employees have experienced the competitive consequences of this nation's lagging industrial performance. Between 1980 and 1984 alone, the population of non-farm employees engaged in manufacturing dropped from 22.4% to 20.6%. This reduction in manufacturing must be arrested.Commissions RecommendationsThe comprehensive set of recommendations offered by the President's Commission recognized the nation's ""key competitive advantages"", technology and human resources, and calls for their strengthening. Particular emphasis is placed on manufacturing technology and the fact that this country does not translate research into new technologies rapidly and fully.""Perhaps the most glaring deficiency in America's technological capabilities has been our failure to devote enough attention to manufacturing or 'process' technology. It does us little good to design state-of-the-art products if within a short time our foreign competitors can manufacture them more cheaply. The United States has failed to apply its own technologies to manufacturing. Robotics automation and statistical quality control were all first developed in the United States but in recent years they have been more effectively applied elsewhere""."

Jan 1, 1988

By R. W. Lee

The first prototype plant using the Imperial Smelting Process commenced operation in 1950. It is timely therefore to review the developments that have occurred with the process over the past half-century. A major advantage claimed initially for the process was its ability simultaneously to recover zinc and lead from bulk concentrates. This has remained a fundamental advantage, but it has been extended by the increasing treatment of secondary materials containing zinc and lead. This has been facilitated by the development of hot briquetting and tuyere injection. These techniques and their impact on the technology of the operation will be described. The other major advantage claimed for the process was its potential to achieve new levels of productivity in the pyrometallurgical smelting of zinc. This has been realised with operating furnaces producing up to 400 t/d of zinc. The technical developments that have enabled this scale of operation will be reviewed.

Jan 1, 2000

By John M. Rapkoch

In the continuing search for copper matte converting methods, commercially available and feasible choices remain Peirce-Smith Converters, Hoboken Converters, Mitsubishi Converting, Ausmelt converting, and Outokumpu/Kennecott Solid Matte Oxygen Converting (?Flash Converting?). While each alternative improves on Peirce-Smith Converters? limited fugitive gas capturing capability, the Peirce-Smith Converter is relatively easy and economic to operate and has an unmatched ability to accept valuable but difficult-to-handle material such as scrap anodes and purchased scrap copper. Recent experience with designing, building, and starting up an ISASMELT facility, applied in primary smelting of copper concentrates, has led the authors to speculate on how suitable the ISASMELT process would be for copper converting, given its low fugitive gas release and its ability to accept a variety of feed types. This paper reviews the potential metallurgical challenges posed by converting copper matte in an ISASMELT vessel and considers possible engineering and design challenges posed by the inclusion of this technology into a new or refurbished copper smelter.

Jan 1, 2006

By W. Drummond

The cooling of smelter gases by air dilution, adiabatic evaporative cooling and indirect heat exchange is discussed with reference to the process, to the subsequent cleaning of the gas. and to the use of the heat extracted from the gas. The method of reducing the effect of acidic sulphide formation on the corrosive properties of the gas and the dust and the development of surface cleaning mechanisms?are discussed. The development of indirect recuperators using air, water or steam cooling, made possible by the control of surface fouling is traced. The application of the modern Waste Heat Boiler to the new sulphide smelting processes is discussed with respect to the natural and forced circulation concepts. Case histories are presented to illustrate mistakes made with respect to designs produced without recourse to sensitivity analysis and without an appreciation of "worst process? conditions".

Jan 1, 1992

By G. A. Brooks

Reactive ball milling has been proposed as a new route for producing carbides from oxides through carbothcrmic reduction. It is claimed that through milling oxide and graphite powders to the nanoscale, amorphous materials with very high reactivity are formed, that allows for easy transformation of the starting material to another in a subsequent thermal process. Thermodynamic analysis of this proposed process suggests that unless particle sizes are reduced to below 10nm, then reduction in size alone cannot explain a change in the stability of oxides. Even with nanometer scale powders, the products formed need to have a lower total surface energy than the reactants before a chemical change will occur. A model developed by Bhattacharya and Arzt for predicting localized temperature changes based on milling conditions suggest that temperarure rises less than 400 K will be achieved in laboratory conditions. The present calculations suggest that nanometer scale powders formed through high speed ball milling (>10 mls) may have undergone a process analogous to melting and quenching. Further work is required to fully distinguish these features.

Jan 1, 2003

By Takashi Fujii

In the OG (Osaka Gas) process which includes a fusion process of sewage disposal sludge in coke bed knowledge of molten and fluid properties of the sludge are most important to controll the process in good condition. Thus, the softening and melting temperatures and viscosity were measured by the sessile drop technique and a rotating viscometer. Obtained results are summarized as follows: Melting character of sludge slag is varied according to their composition, but closely related to CaO/SiO2 ratio in ordinary sludge and to CaO/(Cr2O3,+Al2O3+P2O5) ratio in Cr2O3 containing sludge. Fluid property of sludge slag has a correlation with optical basicity or Riboud parameter, However, the correlation is poorer than that of metallurgical slags. Especially, chromium oxide containing sludge shows high viscosity and behaves somewhat different manner from ordinary sludge.

Jan 1, 1992

By Jeffrey Shepherd, Scott R. Smith, Eduard Guerra

"Electrochemical and spectroscopic evidence for the dissolution of a Au electrode by meso-2,3- dimercaptosuccinic acid (DMSA) from an acidic LiCl04 electrolyte is presented. Near the potential of zero charge, DMSA was determined to form a stable layer on the metal surface but at more anodic polarizations, DMSA was displaced from the metal through an oxidative process. The anodic displacement of the layer from the electrode resulted in a small amount of Au that was detected in the electrolyte using atomic absorption analysis. The extent of Au dissolution, was monitored while holding the potential of the electrode for 24 hours at the thermodynamic Eo/H,O in LiCl04 electrolytes containing 10 mM DMSA. This routine resulted in detectable quantities of a soluble Au-DMSA complex in the electrolyte and the greatest leaching was observed at a pH = 2.0. At room temperature, the leaching rate was stable at 10.9 µg cm·2 hr·' however, upon increasing the temperature to 50.0°C, the rate of Au dissolution increased yielding an average rate of extraction of 40.1 µg cm·2 hr- 1. Interestingly, after the first 12 hours of leaching at 50.0°C, the leaching current decreased dramatically suggesting surface passivation which prevented further Au extraction. The implications of this process in the industrial leaching of Au will be discussed.IntroductionThe use of cyanide in the industrial process of leaching Au from ores has raised concerns regarding both operational safety and environmental issues surrounding the disposal of spent leaching eftluents in tailings ponds. Depending on the chemical nature of the processed ore, the spent solutions that are released into the tailings ponds can contain toxic cyanide, either dissolved or complexed with different metals and may pose serious risk to wildlife as well as freshwater contamination to nearby water systems. Because of these issues, some recent studies have focused on the exploration of more environmentally-friendly molecules to selectively leach Au with appropriate kinetics. However, to effectively leach Au into an aqueous solution, a suitable ligand that reacts to form a stable chemical bond with Au is needed to form soluble Au complexes that can be later recovered [I]. Recently several sulfur bearing alternatives have been shown to leach significant quantities of Au in aqueous solutions. These include thiourea [2], thiocyanate [3], and thiosulphate [4]. However, alkylthiols are also known to quickly form a stable covalent Au-S bond [5], but have been relatively understudied in term of their ability to leach Au in solution, even though some short chain thiols are water soluble and relatively nontoxic."

Jan 1, 2012

By Toshiro Kuji, Masakazu Fujita, Tetsuji Saito

"The magnetic properties of the magnetic materials were deeply dependent on the microstructures. In this study, the novel technique to produce the desired microstructures in a controlled manner was proposed. The technique consisted of the production of the amorphous alloys and the control of the crystallization process. The technique was applied to improve the magnetic properties of Nd-Fe-B permanent magnets. The microstructural control of the magnets exhibited the excellently high energy-products of higher than 430 kJm-1. The relationship between the magnetic properties and the microstructures of the Nd-Fe-B permanent magnets was discussed.IntroductionThe intrinsic properties of the materials are basically determined by the properties of the constituent elements or the compounds. However, it is often noticed the difference between the observed properties and the theoretical values expected from the intrinsic properties of the materials. This indicates that the observed properties of the materials are determined not only by the properties of the constituent elements. In other words, the observed properties of the materials are also strongly dependent on the morphology of materials. This means that the microstructural control may creates a great improvement of the properties of materials.In Nd-Fe-B permanent magnets, the superiority arises from the uniaxial intermetallic Nd2Fe14B compound which has a large saturation magnetization and a high anisotropy field [1,2]. The magnetic properties of the Nd-Fe-B permanent magnets are dependent on the microstructure, that is, the size, shape and degree of the crystallographic alignment of the Nd2Fe14B phase. Currently, the Nd-Fe-B permanent magnets have been produced by either sintering or melt-spinning [3,4]. In the sintered magnets, alignment of the Nd2Fe14B phase is achieved by the prior green compaction of the crushed ingot powders in an applied magnetic field [3]. In the melt-spinning approach, alignment of the Nd2Fe14B phase is achieved by hot deformation [5]. Amorphous melt-spun ribbons are comminuted and then are consolidated into bulk form by hot pressing before hot deformation. As-hot-pressed magnets have randomly oriented Nd2Fe1~ grains [6]. Subsequent die upsetting of as-hot-pressed magnets gives rise to the crystallographic alignment of the Nd2Fe14B phase."

Jan 1, 1998

By Taner Kavas

The refractory bricks of a rotary cement furnace containing of alumina and magnesium chromite were studied in order to determine whether they could be used in the concrete production as aggregates. Three mortars were prepared by mixing 1 part cement, 3 part aggregate materials, 0.5 part water by weight and mechanical, chemical, thermomechanical and microstructural characteristics were evaluated. The compressive and bending strength of samples were determined after 2 and 28 days curing. Resistance to chemicals were established by calculating the weight gain of mortars stored in 2 % HCl solution for 1 h and 24 h. Thermomechanical characteristics were determined by measuring the compressive strength of heat treated specimens at temperatures of 400 °C, 600 °C and 800 °C. Consequently, magnesium chromite containing waste brick aggregates have given the best results.

Jan 1, 2006

By Alessandra Bonoli, Garfìm Marianna

"Construction and demolition waste (CDW) is no dangerous material resulting from construction, and demolition of houses, large building structures, roads, bridges, piers, and dams. It is possible to recycle these materials, to reduce environmental impacts, and to reuse them in construction sector. To evaluate in a correct way the possibility to reuse this material it is important to lead laboratory tests to assess the proprieties and quality characteristics. European, Italian and British ad hoc Committees had elaborated specific Standards, to evaluate Geometrical, Physical, and Chemical requirements of recycled materials. A research was carried on to define the guidelines for laboratory tests, their suggested values and quality standards. The Construction and Demolition Waste Construction and demolition waste (CDW) is no dangerous, uncontaminated material resulting from construction, renovation, repair, and demolition of houses, large building structures, roads, bridges, piers, and dams. CDW waste is made up of wood, steel, concrete, gypsum, masonry, railway ties, roofing materials, carpeting, insulation, plaster, metal, and asphalt, and all waste included in CER Code 17. In particular Demolition wastes are defined as materials resulting from the demolition, instead Construction wastes are defined as waste materials resulting during construction process or in pre-manufacturing construction industry. Environmental problems In a lot of cases Construction and Demolition Waste materials were discharged in landfills, these are filling up with CDW and others, and some of them will close in the near future. In addition, illegal dumping of CDW debris can result in future health risks, decreased property values, cleanup costs and enviromental problems. The typical environmental impacts generated by CDW dumps are: 1- Dust problem, which causes air pollution, as will as forming dirty areas. 2- Uncontrolled locations, that will encourage the disposal of other waste types with the usual construction wastes leading to an environmental disaster. 3- The degradation and deterioration of the coastal lands and the natural protectorates. 4- The loss of aesthetic features. 5- Occupation of large areas, causing extra hauling costs. Therefore, it is wise to find other alternatives, like reuse or recycling, other than landfilling CDW debris or illegal dumps, because a proper management and the reduction of CDW amount can save money, conserve resources, and preserve the environment."

Jan 1, 2008

By W. Drummond

The cooling of smelter gases by air dilution, adiabatic evaporative cooling and indirect heat exchange is discussed with reference to the ,process, to the subsequent cleaning of the gas and to the use of the heat extracted from the gas. The method of reducing the effect of acidic ,sulphide formation on the corrosive properties of the gas and the dust and the development of surface cleaning mechanisms are discussed. The development of indirect recuperators using air, water or steam cooling, made 'possible by the control of surface fouling is traced. The application of the modern Waste Heat Boiler to the new sulphide smelting processes is discussed with respect to the natural and forced circulation concepts. Case histories are presented to illustrate mistakes made with respect to designs produced without recourse to sensitivity analysis and without an appreciation of "worst process conditions".

Jan 1, 1992

By Germán Richter a

To comply with the chilean air quality regulation requirements, the Hernan Videla Lira Smelter which is a custom smelter having to cope with a wide variety of concentrates, has developed a two-step modernization plan. The main steps are: - A second acid plant of 80,000 Nm3/hr to be operating at the end of 1996. This will increase the sulphur capture from 43% to 701/o in association with the replacement of the Hoboken converter by a second PS-converter to reduce the operation problems resulting from the treating of high garde matte. - Oxygen enrichment, is going to be incorporated in 1998 in the Teniente Converter and PS-converters in association with tuyere injection of dry concentrates, increasing the sulphur capture to 90 - 93% of sulphur inputs. By this program, sulphur emissions will be decreased from 40,000 tpy today to less than 8,000 tpy and in this way to carry out the environmental regulations.

Jan 1, 1996

By Chi-Ming Chang

Alloy powders are commonly used in the purification of zinc sulfate solutions for use in standard electrowinning practice. The primary goal of this research was to study the use of zinc-lead alloys for similar reactions in the galvanic stripping of impurities from organic solutions. The effects of various parameters on the electrochemical behavior of commercially produced zinc-lead alloy powders were determined. A qualitative evaluation and summary of the influence of the more pertinent parameters on iron removal from di-(2-ethylhexyl) phosphoric acid (D2EHPA) by galvanic stripping is given. Water concentration, oxygen content and reaction temperature were the principal factors affecting the reaction rate and process efficiency. Activation energies were also calculated and indicated that the reaction changes from chemical to diffusion control .with increasing temperature in the range of 35" to 45°C. The results showed that zinc-lead alloy gave faster reaction rates with less sensitivity to process variables than SHG zinc as a reducing agent for galvanic stripping. The role of lead could be as cathodic sites for the reaction which enhances the zinc dissolution or anodic half reaction. The morphology of the zinc-lead alloy surfaces, before and after the reactions, supports this assumption.

Jan 1, 1998

By M. J. King

The Chino Smelter embarked on a program to reduce smelter emissions. Fugitive sulfur dioxide and particulate emissions were reduced by (i) removing the flash furnace settling chamber and (ii) installing a baghouse, to treat converter secondary emissions. Neutralization plant capacity was increased, to accommodate increased flow from the flash furnace off-gas cleaning system and to reduce costs.

Jan 1, 1998

By Min Zhu, Yu Ji, An-chao Ren

"After being welded in the weld plant, the 100-meter heavy rails with the specification of 60kg/m are found broken during the straightening process in four planes. Failure analysis is made using the optical microscope and SEM with the result showing that the broken rail contains the imperfection of protrusion which exists at the edge of rail foot, about 1 00mm away from the rail end. When the protrusion is peeled off by deseamer from rail surface, cold scratch is generated which causes the rail to be broken during the subsequent straightening process. By adjusting the roll diameter differences between top and bottom roll of universal finishing mill and the height of pass line, it is possible to maintain the rails flat when leaving the mill. This prevents the upsweep and downsweep phenomena and, thus, the imperfection of protrusion can be eliminated. IntroductionThe development of rail transit worldwide has entered into a new era since the 1960s. The hi-tech rail transit system has gradually gained recognition over the world. In particular, the emergence of new-type passenger trains represented by TGV of France, ICE of Germany and Shinkansen of Japan and heavy haul trains as well, has revealed the charming way and more prosperous future of the modern and hi-tech rail transit system to the people all over the world. It should be pointed out that rail transit system is still the most effective solution to traffic jams among urban cities and in the central cities during the 21 '1 century, especially high-speed railway and subway which take overwhelming advantages over air transport, marine transport and road transport in terms of high speed, high efficiency, safety, comfort, environment protection and high flow. With the trend of increasing speed and heavier load of trains, higher product quality of rails is demanded. The rails for passenger dedicated lines require high cleanness, high accuracy in size, high flatness, high surface quality and large size (100-meter fixed length). The rail quality has direct influence on the operating performance of rail and railway traffic safety. The 100-meter heavy rails with the specification of 60kg/m are broken subject to the straightening process in four planes after being welded in the weld plant. This paper analyzes the reason for rails being broken and provides the theoretical proof for determining the rolling process."

Jan 1, 2013

By Li. Jiarong, Zuojian Liang, Qingyan Xu, Baicheng Liu, Shizhong Liu, Hailong Yuan

Single crystal solidification of turbine blades is a key technology for the production of reliable and high efficiency gas turbines. The solidification process of single crystal investment castings causes a number of problems that have to be solved such as the increase of casting defects and complexity of production process. Computer modeling and simulation is helpful to predict the defects and improve the process design. In the paper, a mathematical model for three dimensional simulation of solidification and single crystal growth of investment castings was developed based on CA, mechanism of crystal growth and basic transfer equations such as heat, mass transfer equations. Many factors including constitutional undercooling, curvature undercooling and anisotropy, which had vital influences on microstructure evolution, were considered in the model. Temperature, crystal growth interface and structure defects of investment castings of single crystal superalloy were investigated at withdrawal rates of 4.5mm/min and 7mm/min. Simulated results showed that microstructure evolution and structure defects were predicted reasonably and calculated results were coincident with experimental ones. The study indicated that three dimensional solidification simulation technique is a powerful tool for understanding the fundamental of solidification and the formation of structure defects in single crystal investment castings and finally for optimizing process design.

Jan 1, 2004

By B. Q. Li, S. P. Song

"This paper describes an on-going research on developing coupled boundary element and finite element algorithms for the solution of thermal and electrodynamic problems relating to materials processing. The coupled methods are uniquely suitable for field problems involving composite regions, in which detailed information on field distributions within one particular region is of more interest and yet the solution can be obtained only if the effects of other regions are all considered. Problems of this type include heat transfer in multiple regions and also magnetic induction involving an infinite boundary. The hybrid boundary and finite element formulation, algorithm development and the applications are discussed. Two examples are given to demonstrate the capability and accuracy of the coupled algorithm for heat transfer problems. Various treatments of corner discontinuity are discussed. It is found that the double flux treatment is an ideal choice amongst those tested as it is easy to implement and also gives the most accurate solution. 1. INTRODUCTIONElectrodynamic and transport problems occur frequently in materials processing systems. Accurate solution of these problems is of great importance not only for our fundamental understanding of physical principles governing these phenomena in the processing systems but also for optimization of the existing processes as well as development of new processes. For this purpose, many numerical algorithms have been developed. These computational schemes in general can be classified into three categories, that is, the finite element and finite difference schemes and the boundary element scheme. The former two are domain based numerical algorithms while the latter the boundary-based algorithm.The finite element method, which is based on the variational calculus, is a very useful and yet popular engineering numerical method for boundary value problems defined over irregular boundaries. The use of the method requires the discretization of the entire domain. It can be applied to solve both linear and nonlinear problems, but is particularly powerful for nonlinear problems that involve the field variables defined within the computational domain. On the other hand, the boundary element method, with its root in the Green's function method, is very efficient for linear boundary value problems or nonlinear problems that involve field variables only along the boundaries. The primary advantage of the boundary element method lies in the fact that only the boundaries of the computational domain need to be discretized, and hence the dimension of the problem is reduced by one, compared with the finite element method."

Jan 1, 1994