A lack of experimental data illustrating the effect of composition, particularly in respect to impurities, on the mechanical properties and corrosion resistance of aluminum-alloy die castings induced the authors and their associates to undertake a limited study of these relations. A number of commercial alloys and several experimental variations of a commercial alloy were used for the investigation. Mechanical property, growth, steam, paraffin, salt spray and atmospheric exposure tests were employed. This paper deals with the more accelerated tests and the results they have produced. It is concluded that a high-silicon alloy with all impurities except iron strictly limited to small amounts will develop an excellent resistance to corrosion and retain satisfactory mechanical properties and casting characteristics. As a direct result of this investigation an alloy of this character with superior corrosion resistance is now available commercially. In general, copper increases the strength and decreases the elongation and corrosion resistance. Tin reduces the mechanical properties and the resistance to corrosion. Iron reduces the elongation and, if excessively high, may adversely affect the tensile strength. Even excessively high iron contents do not affect the corrosion resistance, which is fortunate for the die caster as it is this element that is the most difficult to control. Nickel and zinc in limited amounts do not seem to affect the properties or corrosion resistance of at least the high-silicon alloy. Growth tests have confirmed the previous common belief that dimensional changes under either dry or wet conditions at 100" C. are too small to be of practical importance. Introduction The technical literature contains numerous papers describing die castings, their production, compositions and uses, but nearly all of these

Jan 1, 1935

By J. J. Bowman, E. H. Dix

A lack of experimental data illustrating the effect of composition, particularly in respect to impurities, on the mechanical properties and corrosion resistance of aluminum-alloy die castings induced the authors and their associates to undertake a limited study of these relations. A number of commercial alloys and several experimental variations of a commercial alloy were used for the investigation. Mechanical property, growth, steam, paraffin, salt spray and atmospheric exposure tests were employed. This paper deals with the more accelerated tests and the results they have produced. It is concluded that a high-silicon alloy with all impurities except iron strictly limited to small amounts will develop an excellent resistance to corrosion and retain satisfactory mechanical properties and casting characteristics. As a direct result of this investigation an alloy of this character with superior corrosion resistance is now available commercially. In general, copper increases the strength and decreases the elongation and corrosion resistance. Tin reduces the mechanical properties and the resistance to corrosion. Iron reduces the elongation and, if excessively high, may adversely affect the tensile strength. Even excessively high iron contents do not affect the corrosion resistance, which is fortunate for the die caster as it is this element that is the most difficult to control. Nickel and zinc in limited amounts do not seem to affect the properties or corrosion resistance of at least the high-silicon alloy. Growth tests have confirmed the previous common belief that dimensional changes under either dry or wet conditions at 100" C. are too small to be of practical importance. Introduction The technical literature contains numerous papers describing die castings, their production, compositions and uses, but nearly all of these

Jan 1, 1935

By Robert E. Sorenson

EXPLORATION for deep-seated orebodies in the Silver Belt area of the Coeur d'Alene mining district is complicated by meager surface expressions of diagnostic criteria, lack of knowledge of the significance of specific alteration phenomena, and the great expense involved in the exploration for ore shoots, the tops of which often occur near sea level elevation or below and as much as 4000 ft or more below the surface. Except for the early studies of Ransome and Calkins in 1903 and 1904,[1] little geological work was done in the Coeur d'Alene district for many years, and it is only during the last 15 to 20 years that complete and careful geological mapping has been applied to most of the mines in the area. Much early information, which now would prove invaluable, is lost in hundreds of miles of caved and inaccessible mine openings not mapped by mining geologists. In more recent years mining geology has become a tool of greater use in the district, and some measurable progress is being made in the accumulation of observations that are adding gradually to the knowledge of ore deposits in the district.

Jan 7, 1951

By Major William R. King U. S. Engineer

My attention was drawn to this subject just twenty years ago this month, when I was detailed to rebuild one of the bridges in Richmond that had been burned during the evacuation. We took pos

Jan 1, 1886

By Hugh P. Tiemann

The desirability of employing the centigrade scale for the measurement of temperatures is becoming more and more recognized in this country, particularly in view of the fact that this scale is used almost exclusively in technical papers and publications—exclusively in those published in French or German. There are, however, a large number of factories and laboratories which still employ the Fahrenheit scale. It therefore frequently becomes necessary to convert one into the other and the accompanying chart (Fig. I) has been found very convenient for this purpose. The formulas for conversion follow: (1) °F. = 9o /5+ 32 (2) oC = 5 (oF - 32 ) (1) 100° C X 9 900/5 =180 .'. 180 + 32 = 212° F. 5 (2) 5 (212° F - 32) = 5 X 180 =100o C 9 9

Jan 1, 1916

By George Krauss, M. Cohen

The reverse martensitic transfomzation (i.e., the conversion of martensite to austenite on heating) was investigated in Fe-Ni alloys containing 30.5 to 33.5 wt pct Ni. The reversed austenite was found to be sufficiently distorted to exhibit marked differences in mechanical properties and to undergo recovery and re crystallization on further heating. In particular, the yield strength of the reversed austenite was as much as 2.5 times higher than that of the virgin austenite: with five cycles of the direct and reverse martensitic transformation, the yield strength was 2.6 times higher. There was an accompanying decrease in strain-hardening capacity and in stable ductility or uniform elongation. The recrystallization was observed to follow sigmoidal kinetics, but was characterized by an abnormal1y large temperature dependence which was evidently due to carbon segregation at the migrating grain boundaries. Upon recrystallization, the strength Properties reverted to those of the virgin austenite, but the ductility did not fully recover until the annealing temperature was further raised to dissipate the carbon segregation at the grain boundaries. The transformation of reversed austenite to produce second-generation martensite resulted in an unusually imperfect structure, thereby leaditg to additional strengthening. Horlleuer, the martensitic phase was much less responsive in this respect than was the austenite. MOST martensitic transformations are capable of undergoing a reverse transformation back to the austenitic phase on heating.&apos; This reaction, like the direct transformation to martensite on cooling, is usually athermal. In analogy with the Ms andMf temperatures for the martensitic transformation (where M, > Mf), the reverse transformation is characterized by the As andAf temperatures (where As<Af). It is well-known that the finish (Af) of the martensite-to-austenite reaction on heating may occur at a temperature where austenite is not stable relative to other phases in the equilibrium diagram.&apos; Reverse martensitic transformations have been found to influence the properties of the parent austenitic phase in a number of ferrous alloys. The austenite thus produced after one or more reversals is significantly altered in strength, microstruc-ture, diffusivity, and annealing characteristics compared to well-annealed, virgin austenite. The first detailed observations of such phenomena were made by Wasserman3 on an Fe-30 wt pct alloy. He found that the reversed austenite (i.e., austenite formed by the reverse martensitic transformation) was much stronger than the original austenite, and the second-generation martensite (i.e., martensite produced from the reversed austenite) was somewhat stronger than the first-generation martensite. On heating the reversed austenite, recrystallization occurred in a manner similar to that of a cold-worked metal; the Laue spots sharpened and the strength decreased.4 In recent years, Russian workers have shown considerable interest in these reverse martensitic transformations. Most of such investigations5-10 have been concerned with the stabilization of reversed austenite relative to subsequent martensitic transformation, and because of its unusual nature, this phenomenon will be discussed in detail elsewhere." On the other hand, the annealing behavior of reversed austenite and the attendant variation in properties have received little attention beyond the experiments of Wasserman.3,4 Gridnev eta1.,8 in one of the few such studies. followed the hardness change of reversed austenite as a function of time at three annealing temperatures. The marked strengthening of austenite achieved by the reverse martensitic transformation has been referred to as "transformation strengthening" by Wasserman3,4 and as "phase hardening" by Malyshev et a1.7,9,10 to differentiate it from hardening produced by cold working. Both groups of investigators noted that further strengthening of the austenite could be attained by repeated or cyclic transformations, but the first cycle resulted in the most pronounced effect. Evidence of the altered microstructure of reversed austenite has been reported by Maximova and Nikonorova6 and by Edmonson and KO.12 The former found that reversed austenite was much more sensitive to etching than the original austenite, and the latter authors observed a (&apos;ghost" structure resembling martensite in certain areas of the reversed austenite. Enhancement of the self-diffusion rate in reversed

Jan 1, 1962

By John D. Price

R. W. Campbell (Jones and Laughlin Steel Carp., Pittsburgh)—As usual John Price has presented an excellent paper. I know of no one who has devoted more time and conscientious thought to this subject than he has, and his efforts have produced scientific data and conclusions of real value. Results of similar studies made by the Jones and Laughlin Steel Corp. on the blending of Pennsylvania coals may be of interest. During 1935 the late F. W. Wagner and the present writer developed an empirical physical fuel value formula for evaluating the combined physical tests of metallurgical coke, see Table IV. In the development of the formula, the tumbler test, shatter test, screen test, and porosity of coke have been taken into consideration. Each of these tests brings out some physical property not expressed by the others, and in estimation of the importance of these tests as a medium for evaluating coke for the blast furnace, their worth has been graded as follows: It was thought that some additional penalty should be applied to cokes that do not show a uniform screen size, assuming that coke larger than 4 in. was not desirable and that this size was an indication of irregular size. Therefore the screen test factor is further corrected by applying a penalty of 1 pct for each 1 pct material greater than 4-in. size as shown by the screen test. The physical fitness of coke for blast furnace use depends upon four fundamental characteristics: l—gen-era1 strength, as indicated by the shatter test; 2— abradability, or the resistance of cell walls to reduction in size by attrition, as indicated by the tumbler test; 3—porosity; and 4—size and uniformity. Each of these characteristics is not of equal importance, but surely, in an attempt to determine an accurate physical value, the individual value of each should be taken into consideration. The formula is used as a yardstick, so to speak, in determining variations in the normal production of metallurgical coke and in making comparisons between normal coke and experimental blends with other coals. Table IV gives results of coking tests on raw and washed high volatile coals and these same coals with blends of coke breeze, anthracite coal, char and low volatile coals, all from Pennsylvania. The table also gives the source of the coals and coke breeze, as well as their proximate analyses. It will be noted that the washing of the raw high volatile coal increased the physical fuel value from 26.17 to 39.16, showing the effect of removing shale and slate which produces a detrimental fracturing and weakening of the coke. It is a well known fact that many Pennsylvania high volatile coals contain an excess of resinous material or binder which has a tendency to weaken the coke, owing to its high evolution of gases during carbonization. Tests were therefore made with coke breeze, an inert material, in an attempt to alleviate this condition. Blends of washed coal with 5 pct and 7.5 pct coke breeze collected from the coke plant quenching sump (82.9 pct through 1/8-in. screen) resulted in cokes with a physical fuel value of 20.75 and 16.73 respectively, lower than results obtained from 100 pct raw high volatile coal. It will be noted that the percentage of + 4-in. coke increased but that the tumbler test was very low. Undoubtedly better results could have been obtained if the coke breeze could have been crushed extremely fine. During World War II the government asked the coking industry to consider the use of anthracite coal as a substitute for high quality low volatile coal, which was extremely scarce at the time. The next series of tests was made with blends of raw and washed high volatile coals and 5, 10, and 15 pct Pennsylvania No. 5 buckwheat anthracite (100 pct through l/8-in. screen). It was necessary to use some raw high volatile coal in these blends because of insufficient washer capacity at the time. It will be noted that the physical fuel values

Jan 1, 1954

By E. P. Pfleider

Important economic planning by industries, companies, financial firms and governments is predicated on estimates of future growth potential. Prior to the passage of the Taconite Amendment by the people of the State in November 1964, various admittedly conservative forecasts were made of the future of Minnesota&apos;s iron ore industry. Since that date, 3 new taconite plants are under construction, 2 are being expanded, one has just gone "on stream," and a seventh is in the design stage. These plants have a total capacity of about 35 million tons of pellets annually. The pessimism of 1964 today is being replaced by unbounded optimism. In the light of such recent developments, it becomes essential to update forecasts related to production, employment and capital investments. New projections show 50 to 58 million tons of pellet production from Minnesota by 1975. This tonnage, together with some 6 to 8 million of natural ores, should provide an annual full-time employment of 15,000 by the mining companies, plus 700 in related railroad and power producing activities and 1000 in plant construction. Total capital investment in new plants should reach $1.5 billion by 1975 and $2 billion by 1990. These current estimates indicate that the conservative goals as set in 1964 for the year 1990 should actually be achieved by 1975 or 1980. BACKGROUND Various forecasts1,2,3 have been made of the future consumption and production of iron ores within the United States. The most recent of these is by Harrison,1 delivered at the American Mining Congress meeting in Las Vegas in October. His estimates reflect the latest iron ore developments on a world wide front as well as the accelerating trend toward pellets. Minnesota&apos;s Natural Resources council prepared a detailed report in 1964 outlining the various factors that affect the future of Minnesota&apos;s iron ore industry. It presented estimates predicated on the

Jan 1, 1967

By Victor J. Miller

The Northeast Tripp Slide is one of the larger slope failures that can be attributed to open pit mining. It is a 11.7 million cubic meter (15.3 x l0 6 yd3) wedge failure created by two thick gouge-filled fault zones whose intersection plunges into the Tripp pit at 13°. One unique aspect of this failure is that the slide is now stable despite having moved an estimated 8.5m (28 ft.) towards the pit and having reached a maximum overall velocity of 2lmmlday (0.07 ft/day). The slide started to fail in 1968, accelerated until mining in the slide&apos;s toe area was halted in April 1970, then began to decelerate. With the cessation of mining in the toe area, rubblized rock sloughed into the pit bottom which added weight to the failures toe constraints and began the stabilization process. Measurements from a network of survey stations revealed a correlation between the slide&apos;s velocity and heavy precipitation. Runoff water accumulating in the tension cracks is believed responsible for this correlation. Moreover, the survey net measurements showed that during the failure&apos;s last stage the vertical component of the slide&apos;s movement greatly increased. It is proposed that this settling was caused by plastic-like flowage of the clay gouge underlying the failure The fault zone&apos;s effective shear strength was estimated by a back- analysis on the wedge&apos;s geometry and by performing direct shear tests. The tests, performed on cores taken from samples that were collected on the failure, yielded a residual shear strength of: cohesion 0.61 kg/cm2 (8.7 lb/in2), and a friction angle of 9.6°. This residual shear strength was near1y equal to the back-calculated strength indicating that the controlling fault&apos;s effective strength was essentially the same as the residual shear strength of the gouge filling

Jan 1, 1983

By AIME AIME

The following abstract of the minutes of the final Adjourned Annual Business Meeting, held Nov. 12, 1912, in the office of the Institute, 29 West 39th Street, New York City, is here presented for the information of the membership at large. On the announcement by the Secretary that there was a quorum present, President James F. Kemp called the meeting to order. The minutes of the Adjourned Annual Business Meeting of Oct. 7, 1912, were read and approved. (Sec p. xi,Bulletin No. 71, November). Prof. Jos. W. Richards, in behalf of the Special Committee of the Board of Directors and the Council (Messrs. Richards, Kirchhoff, and Rand), withdrew the two proposed amendments to the Constitution offered by the said Committee at the Adjourned Annual Business Meeting of Oct. 7, 1912. (See Bulletin. No. 70, October, 1912, p. vi., and Circular Announcement No. 8, Oct. 15, 1912, p. 15.) Professor Richards presented a syllabus of the proposed amendments to the Constitution and By-Laws prepared by the Special Committee. Several members present discussed various sections of the proposed Constitution, and the Committee advised that the suggestions would he duly considered before submitting the final document, which would be duly presented and sent to the membership at large at least 30 days before the next Annual Business Meeting, Feb. 18, 1913. Professor Richards presented a resolution, seconded by Mr. Kirchhoff, making a change in the present Certificate of Incorporation, so that it would conform to the proposed changes in the Constitution and By-Laws; said resolution was unanimously adopted. Professor Richards presented another amendment to the Constitution, which had been purposely omitted from the printed list, but had been requested by many members, namely, the creation of a " Class of Fellows." This question was freely discussed at the Cleveland meeting (see Bulletin No. 71, November, 1912, p. 1348), and in view of the diversity of opinion it was-decided to present it in separate form for separate action of the membership at large at the Annual Business Meeting, Feb. 18, 1913. In answer to question, the President announced that the proposed amendments to the Constitution and By-Laws presented by Messrs. Corning and Stone at the Adjourned Annual Business Meeting, Oct. 7, 1912, and published in Circular Announcement No. 8, Oct. 15, 1912, were still on record. Professor Richards presented a syllabus of the proposed amendments to the By-Laws, and several sections were discused by members present, but no action of record was taken. Mr. Charles F. Rand read a letter from Mr. L. K. Armstrong, Sec-retary of the Spokane Local Section of the Institute, referring to the proposed amendments to the Constitution, and he announced that many of Mr. Armstrong&apos;s suggestions were, in one form or another, already incorporated in the proposed amendments submitted by the Special Committee. A special vote of thanks was passed to Dr. Albert R. Ledoux for the valuable assistance rendered by him to the Special Committee in the preparation of the proposed amendments to the Constitution and By-Laws.

Dec 1, 1912

By Eugene McAuliffe

AS anthracite is no longer used to a marked extent by the rail- ways of the United States (1,513,000 tons in 1933), that portion of the mining industry engaged in the production of bituminous coal is, and will continue to be, the one chiefly concerned with the future use of its product by the railways. In a period such as the present, when all enter- prise is unsettled, when fundamental principles of industrial management and control are being swept aside or else changed overnight, it is difficult to predict what will happen. The relation between the total production of bituminous coal and the volume consumed by the steam rail- ways of the United States, Classes I,

Jan 1, 1936

MONDAY, FEB. 17 9.00 A.M. to 9.00 P.M. Registration at Institute Headquarters. 9.00 A.M. Meeting of Committee on Development of the Activities of the Institute, Room 905, 9th Floor. 10.00 A.M. Simultaneous Sessions of Institute of Metals Division, Room 2, 5th floor. Industrial Organization, Room 1, 5th Floor. 12.30 P.M. Luncheon at Headquarters, 5th Floor. 2.00 P.M. to 4.25 P.M. Simultaneous Sessions of Institute of Metals Division, Room 2, 5th Floor. Industrial Organization, Room 1, 5th Floor. Petroleum and Gas, Room 905, .9th Floor. 2.30 P.M. Sightseeing trip by automobile for the ladies. Among the points visited will be: The American Museum of Natural History. The Episcopal Cathedral of St. John the Devine. The Spanish Museum. The American Geographical Society. The American Numismatic Society. The visits will be followed by Tea. 4.30 P.M. Memorial Service to Dr. Rossiter W. Raymond, Auditorium. 8.30 P.M. Smoker, 5th.floor.

Jan 2, 1919

By M. E. Grimes

A method of predicting uranium extraction rate in underground bacterial leaching of as-blasted ore has been developed. The method is based on the hypothesis that extraction is directly proportional to the volume of a piece of ore that is penetrated by the leaching agent, and that each piece of ore, regardless of size, has been penetrated radially from the external surface to the same depth at a given leaching time. Consequently, given an initial size and assay distribution, extraction should be predictable for a given penetration. Two laboratory bacterial leaching tests under simulated stope leaching conditions were carried out for a periods of 89 and 96 weeks. On completion, the residual ore was screened and analyzed. The information so obtained was employed to provide an elapsed time base for the penetration model, from which predictions of future extraction were made. The finding of solubilized uranium trapped within apparently sol id ore pieces was unexpected. However, it is not recoverable except after crushing, and hence does not affect calculations of underground leaching .

Jan 1, 1974

By E. J. Rapperport, M. F. Smith

A presentation of the W-Ru constitution diagram is given. Techniques utilized in the determination of phase boundary values include electron micro-probe analysis of two-phased alloys and diffusion couples, as well as normal metallographic and X-ray methods. The primary features of the diagram are: 1) a terminal solid solution of ruthenium in tungsten with a maximum solubility of 23 at. pct Ru at 2300°C; 2) a terminal solid solution of tungsten in ruthenium with a maximum solubility of 48 at. pct W at 2205°C; 3) a o phase of maximum breadth about 6 at. pct based on the composition W3Ru2 which forms peritectically from the melt at 2300°C, and which decomposes eutectoidally at 1667 °C to form a twigs ten and 0 ruthenium; 4) a eutectic at 45 at. pct Ru and 2205°C with the products being o plus ß ruthenium. THE W-Ru diagram has previously been studied only in a cursory fashion. Raub and alter&apos; obtained a 1400°C isotherm in which they observed no intermediate phases, and on which they established the limits of solubility as 36.5 at. pct W in ruthenium and about 1.5 at. pct Ru in tungsten. In addition, Obrowski2 found a o phase forming peritectically from the melt and existing only above 1650°C. Below this temperature the phase was presumed to decompose eutectoidally. The present work finds the diagram as given in Fig. 1. I) EXPERIMENTAL PROCEDURE The materials used for alloy preparation in determining the W-Ru constitution diagram were 99.9 pct pure ruthenium powder supplied by Baker Chemical Co., and 99.9 pct pure tungsten powder from General Electric Co. Typical analyses of these elements are given in Table I. Initial alloys at 10 at. pct intervals were prepared from the metal powders by the following method. Powders sufficient for 25 g of the alloys were weighed out with an accuracy of 0.1 mg and blended mechanically. After blending, the powders were compacted, in a steel die, at approximately 30,000 psi. The compacts were sintered in an electric vacuum furnace in order to remove adsorbed gases and to achieve partial densification prior to arc-melting. Vacua of 10-4 mm Hg or less were maintained in sintering as the furnace temperature was raised to approximately 2000°C. Sintering times ranged from 10 to 20 hr. The sintered compacts were arc-melted under a protective atmosphere of purified helium. Melting was conducted on a water-cooled copper hearth, utilizing a nonconsumable tungsten electrode. In the melting process, each alloy was turned over and re-melted on opposite sides from four to six times to ensure complete melting and to eliminate gross in-homogeneities. The arc-melter used had a vacuum capability of 5 X 10-6 mm Hg, and a leak rate of about 20 -liters per hr. Chemical analysis techniques for refractory metal-platinum group metal combinations are not well-established; therefore, composition control and determination depended principally upon weight-loss observations and calculations. This consisted in weighing each alloy after sintering and after arc-melting, and calculating the maximum and minimum composition values, assuming the total weight losses to be first all tungsten, and then all ruthenium. Since composition uncertainty was directly related to weight loss, care was taken to minimize losses in handling, compacting, and melting. Prior to homogenization and equilibration the as-arc-melted alloys were analyzed in several

Jan 1, 1964

By G. W. Elger, H. E. Bell, J. E. Tress, J. B. Wright

This paper describes laboratory techniques and subsequent results of US Bureau of Mines (USBM) research to produce chlorination-grade feed- stock from an abundant, low-grade, domestic, rock ilmenite ore. The research is part of the Bureau effort to devise technology that may help decrease US dependence on imported raw materials. A rock ilmenite containing about 46 wt % TiO2 was smelted in an electric arc furnace with coke, wood-chips, and Na2CO3 to separate most of the iron as pig iron and to form a low-iron, titanium-enriched slug. The slug was ground, pelletized, oxidized, and then sulfated with mixtures of SO2 and air in a continuous 4.5- to 9.1-kg/h (10- to 20-lb per hour) apparatus at 1023° to 122J0 K (1380° to 1740° F). The sulfated slug, containing 60% to 65% TiOb, was reground and leached in water at ambient temperature to decrease the combined levels of the troublesome calcium, magnesium, and manganese impurities from 7.0 to 1.7 wt 70. The final product was upgraded to about 8.4 wt % TiO2. This material is potentially suitable for chlorination in a fluidized bed reactor. The most favorable results were achieved with leached slug sulfated at a feed rate of 4.5 kg/h (10 lb per hour) and at temperatures of 1073° to 1123° K (1470° to 1560&apos; F).

Jan 1, 1986

[MINING AND EXPLORATION DIVISION Established as Mining, Geology and Geophysics Division, Sept. 27, 1949 Name changed February 19, 1958. Lyman H. Hart, Chairman Robert J. Lacy, Assistant Chairman Vice Chairmen: John C. Wangaard, Membership J. M. Ehrhorn, Program John G. Hall, Publications C. E. Nelson, Secretary American, Smelting and Refining Co. 120 Broadway New York 5, New York Editor, Rock-in-the-Box: J. W. Chandler.]

Jan 1, 1961

By C. Chiou, D. P. Seraphim

The effect of clustering on the superconducting properties of Al-Zn alloys has been studied by the ballistic induction techniques. The superconducting critical temperature, T,, changes when zinc-rich clusters are formed. The change in T, depends on the concentration and may be positive or negative, but always correlates with an effective decrease in the solute concentration of the alloy. Reversion after clustering effectively returns a 5 at. pct Zn alloy to the quenched state. These methods might be use&lly extended to the Al-Mg system, where X-ray data are difficult to obtain. In very dilute Al-Zn alloys, as in other tin,&apos; indium, aluminum,2 or tantalums base solid solutions, there is a decrease in the superconducting critical temperature, Tc, roughly proportional to the temperature independent resistivity, i.e., -0.2°K per pS2cm. With increasing solute concentration, the T, generally reaches a minimum and then increases4 to a value well above that for the pure solvent. The change of T, with solute concentration follows an empirical formulation involving two constants which correlate with the scattering cross section of the impurities. As will be shown below, the Al-Zn alloys more concentrated than 1or2at. pct do not follow the empiricism, probably because they are unstable even when rapidly quenched.5 However, it seems possible to study at least the later stages of solute clustering by precise measurements of the 1&apos;, following various thermal treatments. A few experiments on quenched alloys, aged alloys, and tests on reversion are reported here. The heat treatments selected for obtaining the quenched and aged states were mainly deduced from the work of Dash and Fine.6 For the quenched state, specimens were homogenized at 480°C, quenched to -160°C, and immediately transferred and mounted in liquid nitrogen. Measurements on the superconducting properties and residual resistivities were then made at helium temperatures, after which the specimens were aged at room temperature for 3 to 5 hr, i.e., much longer than the time required for clustering to be essentially completed. The superconducting properties and residual resistivities were once again examined. To reach the reverted state of the A1-5at. pct Zn alloy, the aged specimen was heated for 5 min at 200°C and then tested as above.

Jan 1, 1963

By Kenneth A. Gutschick, Robert S. Boynton

Lime has become a general and loosely used term to denote almost any kind of calcareous material or finely divided form of limestone or dolomite, as well as burned forms of lime. However, according to Webster, lime is only calcined limestone (known as quicklime, unslaked lime, or calcium oxide). It also embraces the secondary product of quicklime, i.e., hydrated lime or slaked lime (calcium hydroxide). There are two basic types of limestone used for lime manufacture-high calcium and high magnesium (dolomitic). The dolomitic quicklimes and hydrated limes correspond to their "high calcium" counterparts. The only difference is that the dolomitic types are a combination of the elements calcium and magnesium, in varying percents, whereas high calicum limes contain less than 5% MgO down to 1/2%. In either case a pure form of limestone of at least 97% combined carbonate content is needed to make salable lime, barring a few exceptions. The calcination of both types is diagrammed chemically as follows: [ ] In the foregoing reversible reactions the limestone is burned (calcined) in lime kilns, with the carbon dioxide content of the stone expelled as a gas. The weight loss during calcination of pure high calcium limestone is 44%; with equimolecular dolomitic limestone, the weight loss is 48%. Since lime has a strong affinity for CO_, particularly if moisture is present, it will readily revert to its original carbonate form. This occurs when quicklime "air-slakes" and adsorbs CO.. from the air. Thus, quicklime is perishable and should be stored in dry, water-tight areas. Depending upon the type of kiln used and the physical structure of the stone, the size of the quicklime may range from sandlike granules to 8 in. lumps. However, pebble sizes ranging from 1/4 in. to 2 in. are the most common. Screened quicklime fines are also com¬pressed (pelletized) into 1 in. pellets. For some purposes ground or pulverized forms of quicklime are used, ranging from No. 10 mesh to dust. Generally a pebble of quicklime is about the same size as the pebble of limestone before calcination (perhaps shrinking slightly). A more stable form of lime is hydrated lime. This is obtained by adding water to quicklime, slaking it into a dry, fine, subsieve size white powder. Because its affinity for moisture has been satisfied, it is not vulnerable to further moisture like quicklime. However, it has the same strong affinity for CO_. The following reversible chemical reactions illustrate how hydrated lime when heated (or dehydrated) can revert to the original oxide form:

Jan 1, 1975

By Wilhelm Borchers

IN all special branches of the chemical and metallurgical industries, in which large electric furnaces became necessary for carrying out new processes or for the improvement of old ones, the development of the electric furnaces took place on much the same lines. The endeavors to make a success of a new idea brought forth many ingenious designs, which, however, almost without exception, furnished the proof that the safest and shortest way to practical success is the utmost simplicity of construction of the necessary apparatus. Our knowledge of the qualities of materials for building electric furnaces and of the constituents of the furnace-charges, especially their electric conductivity and their chemical affinity . towards one another at high temperatures, is still far from being complete, and from this fact we must conclude that the smaller the number of elements in the construction of a furnace, the fewer the number of unreliable factors both in the construction and in the operation of the electric furnace. This conclusion deserves special attention when an electric furnace for making steel has to be chosen from the constantly growing number of inventions, inasmuch as the chief con¬stituent of steel, the element iron, is a substance which in its liquid phase has so great an affinity fir those elements which are to be removed from the charge, that it is very difficult to comply with the following conditions: 1, to beat the refining-slag to the highest point of its chemical activity ; to prevent the iron from entering the slaw, or, where this cannot be done, to make it enter so that it finally appears in the end-product

Jan 1, 1910

By J. S. Owens, R. W. Marsden, J. W. Emanuelson, R. F. Werner, N. E. Walker

The iron ores of the Mesabi Range occur in a 340 to 750-foot thick, Precambrian cherty iron formation termed "taconite." For about 65 years, extensive natural iron ore bodies were mined, and the ores either shipped as a direct ore or processed by gravity methods to a shipping grade iron ore. Since 1956, magnetite taconite ores, occurring in magnetite-rich horizons in the Biwabik iron formation, have been commercially concentrated and agglomerated. The transition from natural ores to concentrating-grade ores is progressing rapidly so that, in the near future, a major percentage of the iron ore shipped from the Mesabi Range will be as iron ore pellets produced from taconite. Natural iron ores of the Mesabi Range occur in the Biwabik formation as trough ore bodies in elongated channels and as irregular and tabular deposits in fractured areas associated with faults and folds. Ore bodies range in size from a few thousand tons to hundreds of millions of tons and may occur in any part of the iron formation. In some areas of strong ore development, ore was formed from the hanging-wall argillite to the footwall quartzite. The natural ores and beneficiating-grade natural crude ores were formed by the oxidation of the iron minerals, magnetite, greenalite, stilpnomelane, minnesotaite, and siderite, to hematite and goethite and by the removal of much of the silica in the cherty quartz and in the associated silicates by leaching. The ores are believed to have formed by the oxidizing and leaching action of surface waters. Magnetite taconite ores occur as stratigraphic zones in the Biwabik formation where it contains sufficient magnetite to be concentrated profitably, by magnetic methods, to give a magnetite concentrate that is agglomerated into a high quality product. Unoxidized taconite has an extensive distribution away from and between channels of oxidation and leaching but only a part of the unoxidized taconite is of ore grade. Two general types of magnetite taconite ore occur: ( 1) magnetite taconite of the Main Mesabi Range, generally west of Mesaba, which is composed of magnetite associated with cherty quartz, greenalite, stilpnomelane, minnesotaite, and carbonates and (2) magnetite taconite of the Eastern Mesabi, generally east of Mesaba, composed of magnetite associated with quartz, cummingtonite, actinolite, ferrohypersthene, hedenbergite, fayalite, hornblende, pyroxene, garnet, and biotite. The Mesabi taconite is a metasediment derived from an iron- and silica-rich chemical sediment that has been regionally metamorphosed and, on the eastern end, additionally metamorphosed by the Duluth Gabbro Complex.

Jan 1, 1968