By Selvin Yesilay, Munevver Caki, Canbora Bayraktar, Bekir Karasu, Rahmi Imrak

"In this study, the utilization capability of the solid wastes taken from a commercial roof tile and brick factory in Eskisehir of Turkiye has been investigated in the production of stoneware bodies which can be formed by slip casting. At the first stage, X-ray fluorescent (XRF) and X-ray difractometer (XRD) analyses of the wastes were performed. Depending upon the results, a body recipe with an optimum casting concentration was adjusted. The bodies obtained from prepared slips were fired at 1160 oC as glazed and unglazed forms. Then, they were undergone certain tests in order to determine their firing shrinkage values, water absorption levels and optical parameters. To establish what kind of phase formations occurred after firing as a result of waste incorporations into bodies XRD analysis was conducted. Additionally, effects of such a compositional modification on the microstructure of the bodies were examined by a scanning electron microscope (SEM). Consequently, it was concluded that fired roof tile and brick wastes could be evaluated in both glazed and unglazed stoneware bodies. Introduction Stoneware is the general name applied to many wares fired between 1150 and 1300 °C. It has a different and denser structure than those of ceramics produced at lower temperatures. Fired stoneware possesses a lower water absorption value. When matured at a high temperature, it gives a possibility for the use of feldspar as a main ingredient [1-2]. Colors of stoneware can be brown, red, white and most of the times beige. Firing usually takes place in oxidation atmosphere but also reduction can be rarely used. This naturally has an effect on the body colors [3]. Earth, which contains clay minerals, becomes plastic mud when mixed with water, has a capability to be easily shaped and can be hardened without cracking if fired at 900-1000 °C, is referred as one of the brick and tile raw materials [4]. Natural and aesthetic appearances of buildings obtained with brick and tile products, which make them preferable especially for construction sector, are of importance. Because clays being main raw material of that type of productions generally do not exist as pure materials in nature, their usability depends on their mineralogy and impurities they contain [5]."

Jan 1, 2008

By Kenji Monden

"In order to obtain basic data for the development of highly thermally conductive composite materials, the thermal conductivity of a resin composite material with an Aluminum Nitride filler was assessed. Several different measurement techniques such as the xenon flash and the temperature wave thermometric analysis method were employed to gather data on these composites. An excellent match between theoretical and experimental data was achieved by employing a predictive expression that takes into account the effect of percolation on thermal conductivity.IntroductionA thermal solution composite is made by incorporating dense inorganic fillers with high thermal conductivity into a resin. Because the composite materials have high thermal conductivities, they have been used in electrical products that generate excessive thermal energy during operation, such as inverters, amplifiers and motor drivers. They function as electrically insulating and thermally conducting parts of the electric modules. As the uses of thermal solutions are expanded, composites of higher thermal conductivities will be required. The aim of this work was to investigate, evaluate, and try to predict the influence of key parameters on thermal conductivity and diffusivity. This was achieved by analyzing the effect of both volume fraction and shape of Aluminum Nitride ceramic fillers and measuring the thermal conductivity. In addition, the influence of percolation on thermal conductivity is considered. The thermal conductivity of the composites is discussed by employing a predictive equation using literature data of thermal conductivities for both the filler and resin. As well as thermal conductivity measurements the effect of volume fraction of the filler was also explored.ExperimentalSpecimen PreparationThe composite samples were prepared from silicone resin and Aluminum Nitride (AlN) fillers. The AlN fillers with an average particle size of 20 µm are shown in Figure 1. The mean diameters of the AlN particles used are given in Table I. For comparison the AlN fillers with an average particle size of 5 µm are shown in Figure 2. A planetary centrifugal mixer was used for simultaneously dispersing the components uniformly and de-aerating the mixture. After mixing, these materials were placed in a silicone rubber case and cured at 150 °C for 1 hour."

Jan 1, 2013

By G Hope, C Young, R. N. Gow

"The presence of enargite (Cu3AsS4) is problematic in gold processing as it is refractory, increasing cyanide and oxygen consumption, and enviromnentally hazardous. Selective leaching and treatment of the arsenic would prove advantageous to conventional gold leaching methods. The reactivity of enargite samples from Montana, US and Quiruvilca, Peru were studied under alkaline conditions, pH range of 8-13, using a cyclic voltammetry corrosion cell setup. Raman spectra of the surface were taken during and after cycling to compare surface species against theoretical predominance diagrams. Under slightly oxidizing conditions, covellite (CuS) peaks were found on the surface in a short matter of time, above - 200m V vs SHE for pH 9-13, suggesting arsenic leaching, but for longer conditioning times, elemental sulfur peaks were also found, which created a passivating surface layer. By operating above pH 12, under reducing conditions, ~-500mV vs SHE, arsenic can be leached as a thioarsenate (AsS4-xOx3-), without sulfur formation.IntroductionEnviromnental limitations on pyrometallurgical processing of arsenic has pushed the desire to process enargite-, Cu3AsS4, bearing concentrates towards a hydrometallurgical solution. Attempts to process can be broken down into two categories - the co-dissolution of arsenic and copper under acidic conditions or the selective leaching of arsenic under basic conditions. The selective leaching of arsenic would preferably leave behind a chalcocite, Cu2S, or covellite, CuS, phase that would be more amenable to conventional processing methods of the copper and gold industries. These methods employ bi- or poly-sulfides to leach arsenic as Assl· [1-4], hypochlorite leaching [5-7], ammoniacal leaching [8] or fine grinding to mechanically activate the enargite surface and increase normally slow reaction kinetics[9]. This study looked into the surface formations of an enargite electrode under alkaline conditions, in a pH range from 8-13, as it cycled from -1000 mV to 1000 mV vs SHE. The understanding of the formations and under what conditions they form will be helpful in further development of any of the aforementioned processes."

Jan 1, 2012

By Beatriz Ribeiro Nogueira, Vijaya Kumar Rangari, Esperidiana A. B. Moura, Anne Chinellat, Arifa Parveen, Angel Visentim Ortiz

"Composite consisting of ethylene vinyl alcohol (EVOH) with short piassava fibers were prepared by extrusion process and their thermal and morphological behavior were investigated. The EVOH reinforced with 5 and 10 % of pi as sa va (Attaleafunifera Mart) fiber particle, based on the percentage weight ratio (wt %), untreated and treated with a commercial silane coupling agent, were prepared and the influence of fiber loading and the effect of chemical treatment on their thermal and morphological behavior were evaluated by SEM, DSC and TG analyses. Melt flow index (MFI) of the composites have been determined to evaluate the effects of fiber reinforcement on dynamic viscoelastic melt of the EVOH. In addition, piassava fibers characterization by SEM, FTIR, and organic and inorganic composition have also been carried out. The SEM results of the composites showed surface micrographs without microvoids and a good distribution, dispersion and compatibility between the fillers and the EVOH matrix. Concerning the piassava fibers characterization, the results showed that piassava has higher lignin content than cellulose and hemicelluloses, and around 0.7 % of ash with 52 % of silica (Si02). This high concentration of silica is consistent with the SEM analysis of the fiber that showed a large amount of ""silica rings"" encrusted on their surface.IntroductionLately, great worldwide interest has arisen in developing new technologies that enable the use of products with less environmental impact. Effort has been put into seeking natural modifier applications, particularly regarding the use of natural fibers. Special attention has been given to the use of natural vegetable fibers, because of the huge variety of species available. Such vegetable fibers are usually referred to as lignocellulosic materials [1]. This work evaluated the effects of piassava (Attalea funifera Mart.) fiber incorporation in an ethylene and vinyl alcohol copolymer (EVOH). The EVOH belongs to a family of copolymers with excellent gas barrier properties and resistance to organic compounds, which allow its application in different segments, from food packaging to gas tanks. However, EVOH is very sensitive to moisture, and in conditions of high humidity its gas barrier properties, thermal and mechanical properties are affected."

Jan 1, 2012

By Guo-hua Bai, Hong-jing Yuan, Qian Li, Yong-bin Yang, Tao Jiang, Yan Zhang

"The effect of different additives on the bio-oxidation of arsenic-bearing gold ores has been carried out to solve the problems such as long period of leaching, low oxidation rate. The oxidants strengthen the cathodic reaction and thus improve the leaching rate by the increase of electron transfer. Meanwhile, silver catalysis is also effective for the decomposition of arsenicbearing gold ores due to the strengthening of anode reaction. Co-intensification by oxidants and Ag (I) is more efficient to the bio-leaching and the conversion of As (III) because the anode and cathodic reaction of biological oxidation of sulphide ores were both strengthened. The leaching rate reached to 63.94% after bio-leaching 13days by co-intensification of Ag (I) and Fe(III).IntroductionWith the worsening global ecological problems and the gradual exhaustion of available gold resources, metallurgical technology of refractory gold ore has received more and more attention and become possible due to its good advantage of the economic effects and negative effects to the environment. Refractory gold ore, the direct cyanide leaching rate of that is defined as less than 70%, has become an important raw material in gold extraction industry, in which sulfide bearing gold ore represents a large proportion, pyrite and arsenopyrite (FeAsS) is a common gold-bearing mineral. Since the gold is often encapsulated in the crystal lattice of these minerals, destruction or alteration of the ore to liberate the submicron and/or structurally bond gold is necessary[l]. Even if the ultrafine grinding approach also is generally not sufficient for these refractory ores and additional techniques like roasting, pressure oxidation and bacterial oxidation are used to liberate the gold [2]. In the three pretreatment processes, bacterial oxidation is characterized by its new ideas, low cost, no pollution, simple equipment and operation, high leaching index and become the most promising process which has received much attention over time [3-5]. But its further application is limited by some of its own shortcomings, such as long pretreatment time and the toxic effects of arsenic to bacteria on bio-leaching limit."

Jan 1, 2013

By Shuo Wang, Yu Wang, Bing Xie, Rui Tang, Hong-Yi Li, Kun Wen

"During present converter vanadium extraction process, phosphorus could not be removed from hot metal due to absence of CaO in slag though it is an efficient way for vanadium extraction. In order to improve the phosphorus remove and produce CaO-containing vanadium slag, which could be directly used in subsequent roasting process, during the converter vanadium extraction process, lime dissolution in FeOx-Si02-V203-Ti02 slag was investigated by using a rotating cylinder technique and the slag-lime interface was characterized by SEM/EDS. Results showed that changes in the slag chemistry and phase compositions during the lime dissolution process were similar to that in CaO-Si02-FeOx based slag during the BOF process. The V and Ti in the slag were expected to diffuse into the lattice of2CaO·Si02 solid solution, which formed a rather thinner layer in thickness at the slag-lime interface than that in BOF process, leading to improvement of lime dissolution in the slag.IntroductionVanadium is important material that widely applied in industries. The traditional technique to extract vanadium was to leach vanadium after sodium salt roasting. However, the sodium salt roasting process has several problems including lower yielding rate[!] and environmental pollution[2]. Therefore, the more environment-friendly technique of calcium roasting[3-4] was proposed. In order to increase roasting efficiency of vanadium slag, it is essential to study the dissolution/reaction mechanism between lime and vanadium slag. Many investigations about the dissolution reaction of lime in molten slag have been carried out from the standpoints of rapid slagging to De-Pin steelmaking process[5-6]. However, their studies were focused on BOF slag and the reaction mechanism between solid lime and slag containing vanadium has not been reported yet. In present work, the dissolution process was studied with rotating cylinder technique and the reaction interfaces were observed and analyzed by SEM/EDS to elucidate the dissolution mechanism of lime in vanadium slag. This work was supported by National Natural Science Foundation of China No. 51090382."

Jan 1, 2013

By Alessandra Bonoli, Garfìm Marianna

"Construction and demolition waste (CDW) is no dangerous material resulting from construction, and demolition of houses, large building structures, roads, bridges, piers, and dams. It is possible to recycle these materials, to reduce environmental impacts, and to reuse them in construction sector. To evaluate in a correct way the possibility to reuse this material it is important to lead laboratory tests to assess the proprieties and quality characteristics. European, Italian and British ad hoc Committees had elaborated specific Standards, to evaluate Geometrical, Physical, and Chemical requirements of recycled materials. A research was carried on to define the guidelines for laboratory tests, their suggested values and quality standards. The Construction and Demolition Waste Construction and demolition waste (CDW) is no dangerous, uncontaminated material resulting from construction, renovation, repair, and demolition of houses, large building structures, roads, bridges, piers, and dams. CDW waste is made up of wood, steel, concrete, gypsum, masonry, railway ties, roofing materials, carpeting, insulation, plaster, metal, and asphalt, and all waste included in CER Code 17. In particular Demolition wastes are defined as materials resulting from the demolition, instead Construction wastes are defined as waste materials resulting during construction process or in pre-manufacturing construction industry. Environmental problems In a lot of cases Construction and Demolition Waste materials were discharged in landfills, these are filling up with CDW and others, and some of them will close in the near future. In addition, illegal dumping of CDW debris can result in future health risks, decreased property values, cleanup costs and enviromental problems. The typical environmental impacts generated by CDW dumps are: 1- Dust problem, which causes air pollution, as will as forming dirty areas. 2- Uncontrolled locations, that will encourage the disposal of other waste types with the usual construction wastes leading to an environmental disaster. 3- The degradation and deterioration of the coastal lands and the natural protectorates. 4- The loss of aesthetic features. 5- Occupation of large areas, causing extra hauling costs. Therefore, it is wise to find other alternatives, like reuse or recycling, other than landfilling CDW debris or illegal dumps, because a proper management and the reduction of CDW amount can save money, conserve resources, and preserve the environment."

Jan 1, 2008

By W. E. Wallace

Rare earth elements combine with most, of the metallic elements. As early as 1971 over a thousand intermetallics had been identified and described(1) From a magnetics viewpoint, systems involving. the d-transition metals Fe, Co and Ni are particularly interesting. In these systems there are at least four significant interactions: R-R exchange (R - a rare earth), R-T exchange (T = a transition metal), R-R exchange and the crystal field interaction acting upon the. rare earth ion. There is complex interplay between these interactions leading to bewildering variety in their magnetic behavior., Because of this and in view of the commercial significance of some rare earth intermetallics, studies of these systems has been an unusually active area of inquiry for the past two or three decades. The large magnetic moment of many of the rare earths, viz., 10 µB per atom for Dy and Ho, 9 1B for Tb and Er, etc., attracted, attention many years ago to the rare earths as potential ingredients for alloys to be used in permanent magnet fabrication. The utility of a permanent magnet in high perform¬ance devices (travelling wave tubes, voice coil motors, brushless motors, etc.) is in large measure determined by its maximum energy product, (BH)max. [(BH)max is the maximum value of B (magnetic induction) and H in the 2nd quadrant of the hysteresis loop.] Enhanced atomic moment in princple can lead to increased B and a large maximum energy product. Until about 1970 the largest (BH)max value known was about 5 MGOe(mega-gauss Oersted). This was for A1NiCo - an alloy involving Al, Ni and Co. It was recognized that the rare-earths had the potential for much higher energy product; in the case of Dy the theoretical energy product is about 35.0 MGOe., 70 times that of Alnico. (Needless to say, this theoretical value has never been achieved.) Large-scale efforts began about 30 years ago to synthesize magnetic materials containing rare earths and which would be suitable for permanent magnet fabrication. It was recognized by Strnat(2) et al. that a material to, be useful in high energy magnet fabrication would have to satisfy three. criteria:

Jan 1, 1992

By Wankun Wang, Shixing Wang, Jinhui Peng, Zebiao Zhang

"Germanium leaching from germanium dust and fume was carried out using sulphuric acid. Response surface methodology (RSM), based on a five level, four variable central composite design (CCD), was employed to obtain the best possible combination of liquid/solid ratio (Xi: 2-10), leaching time (X2: 1-5 h), sulphuric acid concentration (X3:3.15-15.75mol/L) and leaching temperature (X4:50-90 *C) for germanium leaching. The obtained experimental data were fit to a one-order polynomial equation using multiple regression analysis and also analyzed by analysis of variance (ANOVA). The 3-D response surface plot and the contour plot derived from the mathematical models were applied to determine the optimal conditions. The optimum extraction conditions were: liquid/solid ratio of 10, leaching time of 1 h, sulphuric acid concentration of 15.75 mol/L, and leaching temperature of 87.8 'C. Under these conditions, the germanium leaching extent was 65.14%, which is in close agreement with the value predicted by the model. The samples were characterized before and after leaching using X-ray diffraction (XRD).IntroductionResponse surface methodology (RSM) is one of the relevant multivariate techniques which can deal with multivariant experimental design strategy, statistical modeling and process optimization [1-15]. It is used to examine the relationship between one or more response variables and a set of quantitative experimental variables or factors. This method is often employed after the vital controllable factors are identified. It is also used to find the factor settings that optimize the response. Designs of this type are usually chosen when a curvature in the response surface is suspected [6], The process optimization of the sulphuric acid leaching of germanium from germanium dust and fume has not been reported in the literature. Hence the present work intends to assess the effects of variables such as liquid/solid ratio, leaching time, sulphuric acid concentration and leaching temperature and to identify the optimum conditions using RSM. The characteristics of sample before and after leaching are assessed using the advanced analytical instruments such as X-ray diffraction (XRD)."

Jan 1, 2012

By Antonio de Ita, Isaias Hilerio, Miguel Barron

"The influence of an unconventional lance with a central nozzle on the multiphase fluid flow in a steelmaking converter is studied in this work by means of computer simulations. The lance has four peripheral supersonic nozzles and a vertical central nozzle. Besides, the oxygen flow in the central nozzle is considered independent from the main oxygen supply. Transient two-dimensional numerical simulations were carried out considering just molten steel and gaseous oxygen as the existing phases. Numerical results show that bath agitation and droplet generation are enhanced as a result of the central nozzle. However, the performance of this lance strongly depends on the distance of the lance tip to the molten steel surface and the velocity of the oxygen jet.IntroductionCurrently, two thirds of the world crude steel is produced through the steelmaking oxygen converter [1]. Given the unquestionable economic importance of this technology, any improvement or optimization proposal is welcome. In the majority of current oxygen converters a top oxygen supersonic jet is blown onto the molten steel through a water-cooled lance to eliminate by oxidation some impurities such as carbon and phosphorus. Conventional lances have inclined peripheral nozzles whose number depends on the converter capacity. During the process, a large amount of gases evolves, forming metal droplets and a metal-slag-gas emulsion [2]. The droplets and the resultant emulsion increase the reaction interfacial area, promoting in this way carbon removal and dephosphorization of the molten steel bath [3]. However, during the blowing stage, the emulsion rises towards the lance and converter mouth and frequently forms layers which accumulate in the lance, reducing the life of the lance tip [4, 5]. It is possible that some freezing of the molten metal occurs due to the low oxygen injection temperature, however there are no reports on this. Besides, frequently undesirable operating phenomena such as spitting and slopping may arise as a result of inappropriate blowing practices or bad lance design. In the oxygen steelmaking industry, novel lances design are needed in order to enhance the decaburization rate and the slag formation and, at the same time, preventing operating practices that decrease productivity and move away the shop from safety standards."

Jan 1, 2012

By Michael Heximer, Dominic Verfielst, Timothy Moore

"Teck's Trail Operations recently installed new pressure filters in the cold stage purification step in the zinc leaching plant. Alloy 2205 duplex stainless steel was chosen as the material of construction as it was in use in the hot stage purification operation. Within a year of commissioning, an unacceptably high rate (greater than 1 mm/y) of corrosion was observed on the weld heat affected zone (HAZ). Laboratory and field tests were conducted to establish the conditions under which the corrosion was occurring. The tests isolated the aggressive conditions to a unique combination of materials present during the filter regeneration stage. Furthermore, the change of the duplex grain structure of the alloy during welding resulted in the HAZ being more susceptible to the corrosive environment. A new material of construction was recommended as a result of the investigation.IntroductionThe sulphide leaching plant uses four horizontal tank pressure leaf filters to remove solids precipitated in the cold stage electrolyte purification process. The current filters were installed in 2007, and replaced a bank of filter presses. The material of construction for the filters - alloy 2205 duplex stainless steel - was selected based on its successful use in similar service areas of the leaching plant. However, within the first year, unexpected and rapid corrosion of the filter tank material was observed. Although moderate general corrosion was noted throughout the filters, the attack was particularly aggressive in the areas where intense heat was applied during fabrication, observed at the HAZs caused by welding, and on the exposed edge grain of the duplex plates. On the inaugural annual inspection of the filters in the first year of operation, a corrosion penetration rate of 1.0 to 1.5 mm/y was observed at the HAZs. The parent plate of the pressure tank was a minimum of 6 mm, with a minimum allowable thickness of 3 mm under the ASME pressure tank design rules. Therefore, the projected useful life of the filters could then be roughly calculated to be two to three years. Urgent action was required to understand and correct this problem."

Jan 1, 2012

By G. Johnston, J. Greenly, R. G. Buchheit, D. C. McIntyre, R. Muenchausen, D. J. Rej, R W. Stinnett

"Rapid thermal treatment of materials using high energy, high flux, pulsed ion beams can produce modified surface layers with unique microstrutures and properties. High energy ions loose their energy during the slowing down process in the workpiece and thus deposit their energy continuously over a depth of a few microns. The deposition of energy can lead to melting and in some causes ablation of the heated layer. Because the pulse duration of the ion beams is typically only 50-200 ns, steep thermal gradients generated during heating facilitate rapid cooling (107K/sec-108K/sec) of the treated layer by thermal diffusion into the underlying material. Rapid heating and cooling of materials can generate surface layers with non-equilibrium amorphous or nano-crystalline microstructures that exhibit increased hardness, wear resistance, and corrosion resistance. Pulsed ion beam treatment can also lead to surface smoothening or can be used to mix thin « 1 11m thick) coatings into underlying substrates. Pulsed ion beams can be generated using existing ""flashover"" ion source technology which is capable of producing single shot, mixed C, H, and O ion beams with beam cross sections of approximately 100 cm2 and energy fluxes up to 100 J/ cm2. Recent advances in repetitive high energy pulsed power technology and development of magnetically confined anode plasma ion sources have facilitated the development of ion beam systems that generate single species beams that pulse continuously at 120 shots/second. These capabilities will allow rapid treatment of large surface area workpieces at low cost.IntroductionThe rapid solidification of liquid materials can create unique materials and material microstructures that often have properties that can lead to enhanced performance. Rapid solidification processing of the surfaces of materials using continuous and pulsed laser beams (laser glazing) has been explored for over 20 years (1-5). Advances in high energy, pulsed electron and ion beam technologies over the past decade have provided rapid thermal treatment techniques that may be less expensive to impliment than laser surface treatment for many surface modification applications (6). High energy pulsed ion beams have recently been used to harden aluminum(7), copper(8) and tool steel surfaces (6,9), increase corrosion resistance of Al alloys (6), mix coatings into underlying substrates (10), and create amorphous films (11,12)."

Jan 1, 1994

By Bing Hu, Zhu-Cheng Huang, Guang-Bin Xia, Hu Peng, Hua Wang

"The temperature rising characteristics and reaction of the reduction of iron oxide pellets with anthracite fines were studied using a MW-L0316V microwave oven and Leica-DM-RXP polarizing microscope. The results show that iron oxide pellets and anthracite fines have good microwave absorbing properties, and high temperature and reducing atmosphere in a relatively short time for reduction of iron oxide pellets can be achieved. The reduction reaction, which follows the unreacted core model, is rapid and the metallization increases from 13.41% to 56.57% as the reduction end point temperature increases from 850oC to 950oC. The iron is formed, fine grain crystals of iron are transferred and the contraction of metal phase occurs firstly at the surface of pellets, which hinders the reduction reaction at the center of pellets. The rate of reduction reaction increases slowly as the reduction end point temperature increases from 950oC to 1050oC.IntroductionIron ore direct reduction can be divided into gas-based reduction and coal-based reduction. Owing to the effect of the resource and the related economic benefits [1, 2, 3, and 4], the development of gas-based direct reduction technology is restricted, but the development of coal-based direct reduction supported by the relevant industrial policy has very good prospects for application.As a source of clean energy, in China microwaves have been applied in many fields [5, 6, and 7]. Chen Jin studied the reduction of carbon pellets under microwaves, and has made some progress on reduction kinetics and reaction mechanisms. Other countries also have related research in this field [8 - 15], for example, Kotaro Ishizaki and Kazuhiro Nagata have done research on the reduction reaction of carbon magnetite heated by microwaves. The research shows that Fe3O4 is deoxidized to FeO at about 800oC, and FeO is deoxidized to Fe at 1000oC-1025oC. Due to the very good heat absorbing properties of iron oxide pellets and anthracite fines, the selective and rapid heating of microwaves can rapidly raise the temperature of pellets and anthracite, and the iron oxide pellets can be rapidly reduced. In order to provide enough theoretical basis for direct reduction by microwave heating, this paper studies the temperature rising characteristics, behavior of the reduction reaction and the changes of the iron oxide pellets and anthracite in the microwave field."

Jan 1, 2011

By L. Katgerman, R. Van Toi, H. E. A. Van den Akker

"Mould filling simulations are powerful tools for optimizing the characteristics of castings. The robustness of calculational methods for mould filling simulations is generally tested in simple geometries. While a vertical plate has been used often for validation studies, this paper aims at mould filling simulations of a horizontal thin wall casting. Such castings exhibit a strong interaction between heat transfer (solidification), surface tension and gravitational force.The results are presented of a study to validate numerical simulations of mould filling phenomena in a thin wall horizontal casting. Solidification during mould filling is studied computationally. Velocities are measured using Particle Image Velocimetry.INTRODUCTIONIn foundry practice Computational Fluid Dynamics (CFD) is being considered a promising tool to arrive at a better understanding of casting defects introduced during the mould filling period of a casting. The use of CFD is believed to be advantageous in predicting possible defect locations, pouring times, and the lowest possible casting temperature without the risk of cold shuts. In addition, CFD may be used to optimize pouring system geometries [1,2]. As opposed to experimental studies in, e.g., cold water models, CFD allows for the flexible modification of the casting geometry and the pouring system, and for the inclusion of physical effects such as solidification and heat transfer. Thus, a proper use of CFD may lead to a reduction of the casting rejection rate without expensive trial-and-error procedures, and to a decrease of production costs in foundries. Mould filling simulations take a special place in CFD, because a free surface tracking algorithm is required. Over the past decade methods, MAC [3] and SOLAVOF [4], have been extended to 3-D. The robustness of computational methods for mould filling simulations is generally tested in simple geometries [5,6]. While a vertical plate has been used often for validation studies, this paper concentrates at mould filling simulations of a horizontal thin wall casting. Thin wall horizontal castings exhibit a strong interaction between heat transfer (solidification), surfaces tension and gravitational force. The gravitational force in this setting is orthogonal to the plane of flow and has therefore no influence on the shape of the free surface in the plane of flow. Mould filling numerical methods and algorithms have been recently reviewed by Chen et al.[7]."

Jan 1, 1999

By Ana P. Paiva, Marc F. Comella, Sandra S. Reis, Joao N. Reis, M. Soledade Santos

"In this work, the influence of the malonamide structure, acidity of the aqueous phase and diluent on the equilibrium interfacial tension (IT) of N,N'-dimethyl-N,N'-diphenylmalonamide (DMDPHMA) and N,N'-dimethyl-N,N'-dicyclohexylmalonamide (DMDCHMA) in 1,2- dichloroethane (1,2-DCE), and DMDCHMA in toluene, with aqueous HCl, were investigated. IT isotherms were determined using the Du N ouy ring method. Densities of the organic phases were determined, and used to screen solute-diluent interactions. Formation of third phases was never observed; furthermore, ITs increase with the phase separation period, constant values being obtained for separation periods larger than 1000 seconds. Each malonamide interfacial efficiency at the oil/water interface is interpreted in terms of malonamide basicity, diluent polarity and malonamide - hydrochloric acid- diluent interfacial interactions.IntroductionFor several years now, N,N'-tetrasubstituted malonamide derivatives have been extensively investigated as liquid-liquid extraction agents since they were first proposed as the organic components of the DIAMEX process, with the aim of advantageously replacing tributylphosphate in PUREX [1]. Therefore, a significant part of research studies with malonamides appearing in the literature deal with the extraction of major and minor actinides in real or simulated spent nuclear fuels in nitric acid solutions [2]. Under typical experimental process conditions, the tendency shown by some N,N'-tetrasubstituted malonamide derivatives to aggregate in the organic phase, leading in a few cases to the formation of undesirable third phases, has been remarked and consequently thoroughly investigated [3, 4]. The increasing use of chloride streams as hydrometallurgical aqueous feeds is becoming a reality, and this fact is obviously deeply founded on an extensive research carried out to recover value-adding metals from these media. Following this trend, a number of N,N'-tetrasubstituted malonamides have already been screened for the recovery of iron(III) [5, 6] and platinum-group metals [7] from hydrochloric acid solutions. The results obtained are quite promising either in terms of total metal ion recoveries or selectivity patterns achieved. The formation of a third phase when iron(III) was extracted by the tested N,N'-tetrasubstituted malonamide derivatives has never been observed under the adopted experimental conditions, and the extraction data collected would need to be reinterpreted accordingly if any aggregation phenomena involving the considered extraction systems were to take place."

Jan 1, 2011

By A. M. Blount

In 1983, a final ruling of the U.S. Occupational Health and Safety Administration (OSHA) specified that chemicals containing >0.1 % of a carcinogenic substance or > 1 % of a substance hazardous to health must be labelled. Amphiboles of the fibrous or asbestos-type must be quantified at levels of 0. I % whereas the status of non-fibrous types is not finally determined at this time. Tremolite and actinolite can possibly be measured to 0.1 % by XRD, but anthophyllite cannot be so measured. Recently the International Agency for Cancer Research (IARC) has designated quartz as a suspected carcinogen, and its quantity must be measured to the 0.1 % level. Thus, it has become Increasingly important to be able to detect and quantify minerals in bulk samples down to low or "trace" levels. It has been found that minerals needing to be quantified can often be concentrated by microcentrifuge and counted by means of polarized-light microscopy. For example, amphiboles in talc samples can be separated by using a heavy liquid (thallium formate-malonate) of density 2.810. Talc floats, and amphiboles sink. After centrifuging, the denser particles are removed from the bottom with a Pasteur pipette and placed in a clean centrifuge tube. Distilled water is added to the tube containing the denser minerals and the tube centrifuged again. After several washings with distilled water, the sample is removed along with a drop of water to a clean glass slide. A drop of 1 .584 refractive index liquid and a cover glass are placed over the dried sample. The slide is scanned for particles greater than 5 um in length and having an aspect ratio greater than 1:3. These are checked for refractive index, sign of elongation and extinction angle to differentiate them from talc particles on edge and other minerals. Amphiboles have all indices greater than 1.584, and talc has all indices equal to or lower than this value. Alternately the heavies at the bottom of the centrifuge tube can be filtered through a nucleopore filter. After the filter has been washed with distilled water and dried, a 1.584 refractive index liquid renders the filter transparent in two of the four extinction positions so that a count of amphibole particles can be made directly on the filter. The refractive index-density method which is so useful for talc powders should be equally useful for other nonsoluble industrial minerals.

Jan 1, 1989

By Teruo Bitoh, Shogo Izumi

"The effect of B203 flux melting on the structure and the soft magnetic properties of the (Feo.1sBo.20Sio.os)96Nb4 bulk metallic glasses prepared by casting has been investigated. The ringshaped bulk specimens were prepared by the B203 flux melting and copper mold casting. It was confirmed that the flux melting promotes the precipitation of the a-Fe(-Si) and Fe2B phases in the central region of the specimens. The ring-shaped bulk specimens show a flat hysteresis curve, indicating a good linear relationship between the magnetic induction and the applied magnetic field. These results show that it is possible to develop a new soft magnetic material that exhibits constant permeability, which is necessary for producing inductors and choke coils.IntroductionSince the success of forming Fe-based bulk metallic glasses (BMGs) with good soft magnetic properties, great attention has been developed to synthesis and properties of the BMGs [l, 2]. The BMGs have high glass-forming ability (GFA) and, therefore, they can be used to prepare bulk amorphous alloys with a thickness of the order of a few millimeters by casting. The soft magnetic properties of Fe-based BMGs are better than those of ordinary amorphous alloys; therefore, these BMGs have wider applications as soft magnetic materials [3-5]. It is often required for soft magnetic materials that the shape of the hysteresis curve is changed according to the demands of applications. For example, materials with ""flat hysteresis curves,"" which means the magnetic flux density (B) and the applied magnetic field (H) show a linear relationship up to rather high magnetic field, are necessary for producing inductors and choke coils. Flat hysteresis curves can be easily achieved by creating an air gap in the magnetic path. However, magnetic flux leakage generated in the air gap inhibits high-density packing of the electronic components. In order to achieve flat hysteresis curves without creating an air gap, Fe-based ordinary amorphous alloys are subjected to crystallization by annealing and transformed into thin surface layers of a-Fe; the crystallization results in the compression of the remained amorphous phase [6]. Another way to achieve flat hysteresis curves is the formation of secondary phase (such as Fe2B) that act as pinning site of magnetic domain wall displacements [7]."

Jan 1, 2013

By Yasuhiro Konishi, Yoshiyuki Noda

"This paper describes a new processing of rare-earth oxide precursor, in which rare-earth carbonate powders are precipitated directly from emulsions of rare-earth loaded carboxylate solutions, using CO2 gas and water. This synthetic route of rare earth carbonate is a combined process of the stripping and precipitation stages in a conventional solvent extraction. Using this technique, lanthanum carbonate and yttrium carbonate were prepared at temperatures of 10 to 80°C and CO2 pressures of 0.1 to 3.0 MPa for 120 min. The rates of carbonate precipitation in a batch autoclave were sensitive to processing parameters such as CO2 pressure, temperature, and organic-phase composition. The particle size distributions of the carbonate powders were markedly dependent on temperature and C02 pressure.IntroductionSolvent extraction is the most appropriate commercial technology for separation and purification of rare earths. In typical commercial processes, the rare earths are stripped from loaded solvent extractants using aqueous solutions of mineral acid. After adjusting the pH of the aqueous strip solution, the rare earths are precipitated as insoluble powders of oxalates or carbonates, from which oxides can be produced by calcination. Such conventional processing can be simplified when the stripping and precipitation stages are combined by emulsifying rare-earth loaded solvent extractant with aqueous oxalic acid solution. It is likely that the single-stage precipitation stripping results in a marked decline in the consumed amounts of precipitating and neutralizing agents, thereby saving on both running and capital costs.Yoon and Doyle1) first demonstrated that oxalate powders of lanthanum and yttrium are directly precipitated from rare-earth loaded carboxylic acid solvent extractant when contacted with aqueous oxalic acid solution at ambient temperature and atmospheric pressure. Yttrium oxalate pow4ers were also prepared by precipitation stripping of di-(2 ethylhexyl) phosphoric acid. (D2EHPA) extractant using oxalic acid-hydrochloric acid solutions. 2) Moreover, neodymium oxalates were directly precipitated from organic solutions of tertiary aliphatic monocarboxylic acid and 2-ethylhexyl phosphonic acid mono-2- ethylhexyl ester using aqueous oxalic acid solutions, and powder characteristics of the resulting oxalates were compared with those of powders by the conventional solvent extraction routes. 3 • 4) Recently, attention has been directed towards the influence of processing parameters on the particle size distributions of yttrium oxalate precipitates. 5)"

Jan 1, 2000

By Toshiro Kuji, Masakazu Fujita, Tetsuji Saito

"The magnetic properties of the magnetic materials were deeply dependent on the microstructures. In this study, the novel technique to produce the desired microstructures in a controlled manner was proposed. The technique consisted of the production of the amorphous alloys and the control of the crystallization process. The technique was applied to improve the magnetic properties of Nd-Fe-B permanent magnets. The microstructural control of the magnets exhibited the excellently high energy-products of higher than 430 kJm-1. The relationship between the magnetic properties and the microstructures of the Nd-Fe-B permanent magnets was discussed.IntroductionThe intrinsic properties of the materials are basically determined by the properties of the constituent elements or the compounds. However, it is often noticed the difference between the observed properties and the theoretical values expected from the intrinsic properties of the materials. This indicates that the observed properties of the materials are determined not only by the properties of the constituent elements. In other words, the observed properties of the materials are also strongly dependent on the morphology of materials. This means that the microstructural control may creates a great improvement of the properties of materials.In Nd-Fe-B permanent magnets, the superiority arises from the uniaxial intermetallic Nd2Fe14B compound which has a large saturation magnetization and a high anisotropy field [1,2]. The magnetic properties of the Nd-Fe-B permanent magnets are dependent on the microstructure, that is, the size, shape and degree of the crystallographic alignment of the Nd2Fe14B phase. Currently, the Nd-Fe-B permanent magnets have been produced by either sintering or melt-spinning [3,4]. In the sintered magnets, alignment of the Nd2Fe14B phase is achieved by the prior green compaction of the crushed ingot powders in an applied magnetic field [3]. In the melt-spinning approach, alignment of the Nd2Fe14B phase is achieved by hot deformation [5]. Amorphous melt-spun ribbons are comminuted and then are consolidated into bulk form by hot pressing before hot deformation. As-hot-pressed magnets have randomly oriented Nd2Fe1~ grains [6]. Subsequent die upsetting of as-hot-pressed magnets gives rise to the crystallographic alignment of the Nd2Fe14B phase."

Jan 1, 1998

By S. V. Ketov, V. P. Menushenkov, V. S. Shubakov

"The glass samples were obtained by melting of the oxides mixture SrO-Fe2O3-B2O3(Al2O3) at 1200-1250°C with subsequent quenching of the melt on quickly rotating steel roller. Submicronsized Sr(Fe,Al)12O19 particles were formed in glass-ceramic matrix during the crystallization aging of glass. The aging temperature Tag varied in the range 650-950°C. The submicron-sized hexaferrite powder was obtained by removing of the matrix phases using etching. The samples were characterized by X-ray diffraction, scamiing electron microscopy and magnetization measurements. The glass-ceramic material exhibits very high coercivity value up to 10 kOe. The samples of magnets were obtained by pressing of the hexaferrite powder at RT and subsequent aging in the range 900-1200°C. The aged samples exhibit coercivity value up to 8 kOe.IntroductionStrontium M-type hexaferrites have been widely used in technology and industry mainly for production of permanent magnets owing to their appropriate magnetic properties, chemical stability and low cost [1,2]. The SrFe12019-based compounds are characterized by high magnetocrystalline anisotropy and single easy magnetization axis. The highest coercivity is received for monodomain, defect-free single crystal particles with size D - 100 mn. Finely grained strontium hexaferrite prepared by chemical methods such as sol-gel pyrolysis and oxide glass crystallization exhibits high coercivity up to 6-8 kOe [3-5]. Owing to the partial substitution of Al for Fe in the strontium hexaferrite leading to the increase in the magnetic anisotropy field Ha=2Ki/M,, the increase in the coercivity may be received [6]. The notable results were achieved using the SrO-Fe2O3-AlzO3-B2O3 glass crystallization and formation of perfect submicron crystals of alumina-doped hexaferrite [ 6, 7]. The coercive force of glassceramics reached values of up to 10 kOe. Hexaferrite particles are well faceted and have the shape ofhexagonal bipyramids with truncated vertexes [7].In the present paper, we report results of our investigation into the SrO-Fe2O3-B2O3(Al2O3) glass crystallization, hexaferrite powders and permanent magnets, which were prepared by pressing submicron-sized hexaferrite powders at RT and subsequent sintering at 900-1200°C."

Jan 1, 2012