By Terence Makanyire, Animesh Jha

The dissolution and chemical properties of vanadium, zirconium, and niobium in rutile lattice are analyzed by comparing the octahedral site preference energies, with respect to Ti4+ ion in the solvent phase. The oxides are often present in rutile lattice and interfere in achieving the quality of pigment grade TiO2 due to favourable Gibbs energy for dissolution in the solvent rutile matrix. Binary mixtures of V2O5 { TiO2; Nb2O5 { TiO2 and ZrO2 { TiO2 with compositions of 80, 85, 90, 95 and 97 wt% TiO2 were made, pelletized and sintered at 1100 °C for 24 hours. The solidsolution mixtures were then cooled and leached in 2M NaOH for 3 hours at 60 °C. Phase and lattice parameter characterizations, and microstructural and compositional analyses were then carried out using X-ray diraction and SEM/EDX, respectively. The leachates were analysed by Atomic Absorption Spectroscopy (AAS), using which the solute dissolution model for oxides were investigated.

Jan 1, 2014

By Jianguo Yin, Wenqiang Yang, Xiaoli Yuan, Juan An, Wentang Xia

Low grade iron ore with phosphorus (LGIOWP), a raw and wasted industrial solid material was used as an adsorbent to remove Pb(II) from wastewater. The effects of initial pH value, adsorptive time, initial Pb(II) concentration, adsorptive temperature and LGIOWP dosage on the Pb(II) removal efficiency were studied. The results show that the Pb(II) removal efficiencies exceed 99.4% and Pb(II) concentrations are less than 0.30 mg/L under the conditions of pH value 7.0, adsorptive temperature 50 oC, adsorptive time 30 min, initial Pb(II) concentration 100 mg/L, particle size <0.25 mm, adsorbent dosage 5 g/L and stirring speed 260 r/min. After Pb(II) removal reaction, the Pb(II) concentrations of wastewater completely accord with the requirement of national discharge standards of pollutants from lead and zinc industries (GB 25466-2010) (TPb= 0.5 mg/L) in China. Therefore, it can be concluded that LGIOWP is a new low-cost adsorbent which is suitable for the adsorption of Pb(II) from wastewater.

Jan 1, 2015

By Hassan Saalman, Mahmoud Mahmoud, Omneya El Hussaini

The Ferruginous sandstone ore was obtained from Ramlet Hemeyir area, Southwestern Sinai, Egypt, was found to contain 10% rare earth elements (REE). A representative sample has been subjected to sulfuric acid agitation leaching. About 93% of the REE content was released by mixing the ground sample to -100 mesh with concentrated H2SO4 at solid/liquid (S/L) ratio of 1/2 for 5h at a temperature ranged from 250 to 300o C. The REE was precipitated from the prepared sulfate leach liquor of pH 1.0 by adding 35% oxalic acid at 25o C. The precipitation yielded 98% REE. For selective separation of yttrium, the rare earth cake was leached with 31.5% nitric acid. Next, the aqueous solution was contacted with di-(2-ethylhexyl) phosphoric acid (D2EHPA) where 98% yttrium extraction was achieved. Stripping was done with hot H2O (80o C). Finally, a precipitation with oxalic acid was done followed by ignition at 950o C. A yield of 95% yttrium oxide was produced.

Jan 1, 2014

In low carbon TRIP steels, the formation of carbide-free bainitic ferrite is crucial for the stabilization of austenite. Based on experimental investigations modeling the bainite reaction is examined adopting diffusional and displacive mechanisms, as well as the semi-empirical JMAK approach. Transformation tests were carried out to study the isothermal austenite decomposition into bainitic ferrite for a model steel containing 0.6wt%C, 1.5wt%Mm and 1.5wt%Si which replicates the composition of remaining austenite at the start of the bainite reaction in a classical C-Mn-Si TRIP steel. In the diffusional approach, classical nucleation theory is employed and subsequent growth of bainite plates is modeled using the Zener-Hillert theory. In the displacive approach, the autocatalytic nucleation of bairtite plates is assumed to be rate controlling. The predictive capability of all models is evaluated for temperature ranges where different morphologies of bainitic ferrite have been detected, The shortcomings and inherent challenges associated with either of these modeling approaches will be delineated.

Jan 1, 2003

By E. V. Verhoef

The proposed EU directive on the restriction of the use of certain hazardous substances in electrical and electronic equipment promotes the substitution of lead in consumer electronics to reduce emissions from lead in the end of life phase. In this paper, the consequences of substituting lead in solders is assessed using the Eco-lndicator-99 method for the examples. The base metal production system is considered as an interconnected network modeled dynamically in Simulink 4 and Matlab 6 (Mathworks Inc 2000), where the recovery and production of metal components of the assessed product partially overlap. This approach requires global modeling of metal production processes and mass balances and resulting allocation choices. It also reveals the susceptibility of LeA scores to different choices in the modeling and data availability and uncertainty. Besides the comparison between lead-free and lead-containing solders, other side effects are revealed. Lead is carrier material for the recycling and production of many co-elements in the interconnected production and recovery system. Substitution may have adverse effects such as temporary shortages of other connected metals that are often not considered in normal LeA assessments, thus leading to erroneous results. The suggested approach provides directions for including these external effects and for further assessment of the environmental effects of substituting lead. This paper shows that in order to assess the environmental aspects of metallurgy, dynamic modeling of the total system is required based on the fundamental thermodynamics in each metallurgical reactor, the basis of this dynamic model. With this the true environmental impact of metallurgy can be explained. In the case of lead free solder, it is shown that the mining of substitutes has a very much larger impact.

Jan 1, 2003

By E. V. Verhoej

The proposed EU directive on the restriction of the use of certain hazardous substances in electrical and electronic equipment promotes the substitution of lead in consumer electronics to reduce emissions from lead in the end of life phase. In this paper, the consequences of substituting lead in solders is assessed using the Eco-Indicator-99 method for the examples. The base metal production system is considered as an interconnected network modeled dynamically in Simulink 4 and Matlab 6 (Mathworks Inc 2000), where the recovery and production of metal components of the assessed product partially overlap. This approach requires global modeling of metal production processes and mass balances and resulting allocation choices. It also reveals the susceptibility of LCA scores to different choices in the modeling and data availability and uncertainty. Besides the comparison between lead-free and lead-containing solders, other side effects are revealed. Lead is carrier material for the recycling and production of many co-elements in the interconnected production and recovery system. Substitution may have adverse effects such as temporary shortages of other connected metals that are often not considered in normal LCA assessments, thus leading to erroneous results. The suggested approach provides directions for including these extemal effects and for further assessment of the environmental effects of substituting lead. This paper shows that in order to assess the environmental aspects of metallurgy, dynamic modeling of the total system is required based on the fundamental thermodynamics in each metallurgical reactor, the basis of this dynamic model. With this the true environmental impact of metallurgy can be explained. In the case of lead free solder, it is shown that the mining of substitutes has a very much larger impact.

Jan 1, 2003

By R. C. Hubli

Copper (II) chloride has proven to be an efficient lixiviant for copper sulphide ores and secondary sources of copper such as scrap. Nickel sulphides are generally associated with copper ores and copper-nickel matte is an intermediate product of processing mixed sulphides. While the copper species in aqueous chloride media are present as chlorocomplexes, the presence of nickel as Ni++ offers effective separation between the two by solvent extraction techniques. Oxidation of millerite by cupric chloride in sodium chloride solutions has been studied as a function of rate of agitation, leaching time, temperature, acid concentration and total initial cupric concentration. The reaction has a 1/2 order of dependence on initial cupric concentration in the range of 0.0 to 0.5M. The activation energy for the temperature range 333 -363 K has been found to be 59.2 kJ/mol with chemical reaction at the unreacted mineral surface as the rate controlling step. The rate expression, according to the shrinking-core model, for initial cupric concentrations between 0.0 to O.5M, is evaluated as

Jan 1, 1996

By Laila A. Guirguis

Impurities are removed from crude phosphoric acid (57.75% P2O5) with a mixture of low and high molecular weight alcohols, one of which is hydrophilic and the other is hydrophobic i.e. methanol and hexanol. In a single stage, the phosphate values segregate to the high molecular weight alcohol fraction and the impurities segregate to the low molecular weight alcohol fraction. The optimum ratio for the extraction is found to be 0.5 part methanol, one part impure acid and four parts hexanol where an extraction percent of more than 95% is achieved. Re-extraction of the phosphate value from the solvent is obtained by 6% phosphoric acid and the different factors affecting the re-extraction process have been studied. Finally, the purified acid is concentrated under reduced pressure and passed through activated carbon column, whereas the alcohols are re-circulated. The produced phosphoric acid was found to be in good match with the international specifications of food grade quality acid. A technological flow sheet is elucidated.

Jan 1, 2006

By R. M. Luna-Sánchez

Electrochemical studies, particularly Evans? diagrams, have been employed in hydrometallurgy to simulate and explain the redox phenomena that take place at mineral and metal surfaces during operations such as leaching and cementation. However, despite their utility, in some cases, the combination of the cathodic and anodic branches, determined separately, does not reproduce the chemical environment present when both processes occur simultaneously on a specific surface. In the present paper, limitations of Evans? diagrams are analyzed through two examples: silver sulfide cyanidation and gold cementation on zinc. In both cases, the surface kinetics are sensitive to the local pH and cyanide levels. When the electrochemical oxidation of silver sulfide or the reduction of gold are performed in the absence of its corresponding redox reaction, the local pH obtained does not simulate the real situation and the combined reaction kinetics may be very different from those determined from the Evans? diagrams.

Jan 1, 2003

By Yu. A. Grinin, Yu. A. Sannikov, M. A. Lyamina, V. A. Shumskij, L. V. Slobodkin, N. N. Ushakov

This manuscript describes the Kivcet treatment of lead-bearing materials having high contents of copper and zinc. The tests were carried out on bulk concentrates from the Zyrianovsk Mining and Concentrating complex, "Kazzinc" JSC (Kazakhstan) with the following composition: Pb 37.6%, Cu 10.4% and Zn 6.8%. Two properties of the concentrate were under investigation: their calorific value and their desulphurization rate. By adding flux, the charge properties were brought close to the properties of high-grade lead sulphide concentrate. The charge was melted with high productivity. To ensure high copper recovery, Waelz residue was added to the charge. The residue contained more than 20% carbon and about 30% iron metal. The residue was partially replaced by coke that facilitates high copper recovery into the matte. The smelting achieved a production rate of 20 t/h with one burner. Lead recovery into the lead bullion was 88.8%; copper recovery into matte was 92.3%; zinc recovery into slag was 75.5%; and zinc recovery into the fume was 5.1%.

Jan 1, 2000

By Tae-Hyun Kim, Shun Myung Shin, Jin-gu Kang, Jeong-Soo Sohn

We investigated about synthesis of Mn-Zn ferrite with spinel structure using sulfuric acid leaching solution of mixed spent zinc-carbon batteries and spent alkaline batteries. The waste batteries were prepared by physical treatment such as crushing, magnetic separation, and screening. After screening, the crushed batteries were separated to +8 mesh and -8 mesh powder. Among these, under 8 mesh powder was selected for leaching test. The leaching test was investigated at 2 M H2SO4, 4 vol.% H2O2, reaction temperature 60 ?, agitation speed 250 rpm, solid/liquid ratio 50 g/ 500 ml, reaction time 1 h. The leaching efficiency of zinc, manganese and iron were 99.0%, 98.9%, 58.5%, respectively. For co-precipitation of zinc, manganese and iron, 5M NaOH solution was used for pH control. Then in order to synthesize Mn-Zn ferrite powder, it was investigated according to reaction temperature, agitation speed and O2 partial pressure. We could synthesize about 20 nm of Mn-Zn ferrite with spinel structure.

Jan 1, 2008

By V. L. Stolyarova

As part of an effort to develop the fluoride electrolysis route for the production of rare earth metals and alloys, a study of the thermodynamic properties of DyF3 has been carried out by Knudsen cell mass spectrometry. A quadrupole mass spectrometer QMS 420 was used in conjunction with the Knudsen cell arrangement. The experiments were carried out in the temperature range 1280-1440 K. Vaporization was carried out from platinum, molybdenum and tantalum cells. The Dy*, DyF+, DyF2+ fragment ions and the DyF3 parent ion were identified in the mass spectrum of the DyF3 vapour. The DyF, vapour pressure was obtained by the complete isothermal vaporizadon method as well as the ion current comparison method, and the enthalpy of sublimation of DyF3 was evaluated. From the DyF3 vapour pressure data obtained at different temperatures, the enthalpies of formation of DyF3 in the gaseous as well as condensed phases have been evaluated. The experimental data are compared with the thermodynamic information available in literature.

Jan 1, 1995

By Jorge Alberto Soares Tenório, Denise Crocce Romano Espinosa, Luciana Harue Yamane

"The present work investigated the effect of inoculums volume on bioleaching to recover metals from printed circuit boards using Acidithiobacillus ferrooxidans-LR. Printed circuit boards from obsolete computers were mechanically processed by comminution followed by magnetic separation, and the obtained non-magnetic fraction was used in the bioleaching experiments. A shake-flask study was carried out on the non-magnetic fraction samples using a rotary shaker at 30°C, 170 rpm and different volumes of oxidized culture solution as inoculums (%v/v): 5, 10, 20, 30, 40, 50 e 60. The oxidized culture solution was prepared inoculating pre-adapted bacteria Acidithiobacillus ferrooxidans-LR (5%v/v) in 200mL T&K medium. Leaching in acidic ferric sulphate was also performerd. The analyzed parameters were pH, ferrous iron concentration and metals analysis (AAS). The results showed that using 10%v/v of inoculums were extracted 99,2% of copper and 60% of aluminum by bioleaching. Zinc, lead and tin extraction were not influenced by bacterial leaching and extractions rate were obtained by chemical leaching promoted by acid medium. Ferric iron leaching extracted less copper (35%) than bioleaching. SEM analysis shown surface difference between samples of non-magnetic fraction before treatment and after bioleaching, showing corrosion pits formed by the bacteria contact.IntroductionWaste of electrical and electronic equipments (WEEE) has been target of discussion due to environmental, political and economical issues involved. Around 17 million of computers are discarded annually in the world due to malfunctioning equipment or because technologies become obsolete [1,2]. In contrast, only the central processing unit (CPU) of computers weights around 3kg. From this data, it can be calculated that 51 million kilograms of CPU waste are discarded yearly. This calculation was performed considering only the CPUs, disregarding the cathode ray tubes and liquid crystal displays of monitors [3,4]. Because of the amount that has been accumulated, e-waste has become a global problem but also can be an alternative source to recover valuable materials [5,6]."

Jan 1, 2012

By Marisa Di Sabatino, Michael Phan Knudson, Mari Juel, Eivind Øvrelid

"A p-type Czochralski silicon ingot doped with boron was characterized for resistivity, minority carrier lifetime, interstitial oxygen, and metallic impurities. Analyses show a peak in resistivity and a dip in lifetime both occur 5 cm from the top of the ingot crown. This peak in resistivity deviates from the expected trend based on Scheil's equation for boron distribution. High concentration of interstitial oxygen in this area suggests that other oxygen-related defects, such as thermal donors and precipitates, may also be present here, and the observed peak in resistivity and dip in lifetime could be attributed to such defects. The low lifetime of 15-30 µs at minority carrier density of 7.5 x 1014 cm-3 is likely due to copper contamination.IntroductionSolar energy resources vastly exceed all other alternative energy resources, ensuring that solar power must play a crucial role in the evolving energy market. The economic viability of solar power in competition with other energy resources depends upon finding efficient, cost-effective, reliable, and controlled methods for solar cell production. In this regard, minimizing waste (such as material with unsuitable electrical properties that hinder solar cell performance) is a vital component of making solar cell manufacturing cost-effective. Impurities affect electrical properties of solar cell silicon in different ways (i.e. [1, 2, 3, 4, 5, 6]). In this work we focus on the role of oxygen and metallic impurities. Understanding oxygen impurities in silicon is critical to solar cell development because oxygen has been attributed with influencing critical electrical properties including resistivity and minority carrier lifetime and thereby potentially hindering solar cell performance or rendering material unsuitable for solar cells.[1, 2] Furthermore, oxygen is a common impurity in the standard type of solar cell silicon, Czochralski (CZ) silicon, due to diffusion of oxygen from the silica crucible into the melt during crystallization. [7] This study investigates the effects oxygen impurities have on the electrical properties of p-type CZ silicon."

Jan 1, 2013

By De-qing Zhu, Zi-fu Gao, Jian Pan

"In order to produce high quality metalized products and prevent from burden cohesion during pre-reduction, self-fluxed pellets were made for COREX process in the paper. The effects of reduction temperature and reducing gas composition on pre-reduction behaviors of self-fluxed pellets are studied. The results show that the prereduced pellets have poor quality and deposited carbon appears when the reduction temperature is between 600°C and 700°C. The metallization rate, reduction degree and compressive strength of prereduced pellets are promoted by the elevating reduction temperature and mole fraction of H2. Pellets reduced by pure H2 at 800°C have high metallization rate (96.2%), reduction degree (99.4%) and compressive strength (960N/pellet). In all tests, self-fluxed pellets display normal swelling (RSI<l5%) behavior which reveals that self-fluxed pellets are suitable for COREX process. Increasing reduction temperature and mole fraction ofH2 in reducing gas is benefit for pre-reduction of pellets.IntroductionCompared with Blast Furnace, the COREX process has advantages of short flow sheet, using non-coke coal and high-energy utilization. Acidic pellets and lump ores are the chief iron- bearing burden for COREX process which could lead to low melting point substance appearing in per-reduction process. In addition, the acidic hematite pellets tend to swell during the reduction [1-3]. This will result in decreasing compressive strength of pellets, burden cohesion, bad air permeability and poor work status in shaft furnace. Adding carbonate flux could restrain burden bonding to some extent in actual production, but decomposition of carbonate flux increases energy consumption. Worse still, weak reduction potential is unfavorable to iron material reduction [ 4, 5]."

Jan 1, 2013

By Xuemei Zheng, Aiyuan Ma, Jing Li, Jinhui Peng, Shaohua Yin, Libo Zhang

Zinc recovery from zinc oxide flue dust (ZOFD) by ultrasound enhanced neutral leaching process was investigated. In this study, the effects of leaching temperature, liquid/solid ratio, leaching time and ultrasound power were studied, and the conventional leaching experiments were also performed. The experimental results showed that the leaching time was greatly shortened and the leaching rate of zinc was effectively improved by the assistance of ultrasound. The optimum conditions of ultrasound-assisted leaching were determined as leaching time 20 min, temperature 35℃, and the liquid/solid ratio of 5. Under these conditions, the leaching rate of zinc was close to 80% as the ultrasound power of 540W, which was increased by 7% or so, in comparison with that of conventional leaching process.

Jan 1, 2015

By Ping Long, Bin Yang, Jian Wu, Xiumin Chen, Wenli Zhang

In this study, the analysis method of trace element in pure indium using glow discharge mass spectrometry (GD-MS) has been established by correcting the analysis result, which was obtained from non-standard quantitative method of GD-MS. The effect of instrument operating parameters, the resolution and isotopes and the pre-sputtering time on the determination results were investigated respectively. The optimized operating parameters of the instrument were obtained as follows: the discharge current was 37.5mA and discharge airflow was 475ml/min. Mass spectral interferences have been eliminated using selected resolution and isotope. The pre-sputtering time was 30 min. 4 trace elements in two pure samples were determined for 6 times. The RSD were less than 20%. The content of trace elements in indium samples was determined by GD-MS and Chemical Analysis Method of Indium which is tested by inductively coupled plasma atomic emission spectrometry, respectively. The results were consistent with each other.

Jan 1, 2016

By Anjan Kumari, B. K. Soni, Manis Kumar Jha, A. Vidyadhar, Vinod Kumar

"In the present paper, recovery of valuable metals from the poly-cracked ash obtained by pyrolysis of discarded PCBs has been studied following physical beneficiation and a hydrometallurgical process alternate to smelting. The ash is subjected to comminution for the separation of metallic components from non-metallic fractions by scrubbing, tabling and froth flotation which enriched the metal in the concentrate -97% which was further screened to separate high and low metal concentrate. The finer fraction containing -12% metallic value was leached in acidic solution. Almost all (Cu, Pb, Fe, etc) were leached in 4M HN03 at 90°C in 75 min at a pulp density 100 g/L. The characterization of both ash and residues were made by XRD, EPMA, EDS, etc. to validate the experimental results. The metals from the leach liquor could be recovered/separated using solvent extraction techniques which can further be processed to get pure metal salts/ sheets.IntroductionPrinted circuit boards (PCBs) are an essential component of electrical and electronic equipments (EEEs) as it plays an important role during operation of these devices. The world market of PCBs has reached nearly $60 billion in 2012, with 1.7 percent real growth over 2011 [1]. The diverse technology-driven global market is expected to grow at an average annual rate of 5% by 2014 [2]. The waste EEEs are generated due to replacement of obsolete equipments with modem ones and thus their demand is also increasing rapidly [3]. The discarded e-wastes are being piled up as landfills which affect the environment and cause health threats to living organisms, if not disposed of properly. These e-wastes contain metals some of which are precious, few are hazardous and others as valuable."

Jan 1, 2014

By Guohua Bai, Mingjun Rao, Jianchen Lim, Guanghui Li, Tao Jiang

"By using thermogravimetry, optical microscope and chemical phase analysis, the solid-state reduction of carbon-burdened chromite pellets in the absence and presence of additives were investigated. The effects of reduction temperature, reduction time and additives on the metallization of chromite pellet were studied. The results indicate that the pre-reduction ratio of carbon-burdened chromite pellets is improved with the increase of reduction temperature and the addition of additives. The metallization of chromium is increased from 63.9% to 92.8% at 1300 °C for 4h with the addition of 2 wt.% of sodium borate. Investigation suggests that the reduction of carbon-burdened chromite pellets is diffusion controlled. The apparent activation energy without additive is 192.1 kJ/mol, while it decreases to 170.4 kJ/mol in the present sodium borate.IntroductionFerrochrome is used to produce high strength, corrosion resistant, wear-resisting, high temperature resistant and oxidation resistant special steels, and it is becoming one of the most important alloy materials for the production of stainless and high alloying ferritic steels [1-5]. Demand for ferrochrome is steadily on the rise due to the growth of stainless steel industry. Nowadays, more than 80% of the world's ferrochrome is utilized in the production of stainless steel [6-7].Ferrochrome is mainly produced in submerged-arc furnaces (SAF) with chromite lump ore. However, lump ore merely accounts for 20% of the chromite ore output, while fine ore (< 8 mm) accounts for about 80% [8]. Therefore, agglomeration of chromite fine ore is necessary before charging into SAF."

Jan 1, 2011

By Hu Long

Pyrite, as the host mineral in refractory gold ores and concentrates, has been treated by pressure oxidation in sulfuric acid solutions at temperatures above 180°C to liberate gold prior to cyanidation since the 1980&apos;s. However, no data is available on the kinetics of pyrite during acid pressure oxidation over the temperature range of 180 to 230°C which is the range employed by most commercial plants. The dissolution of pyrite (FeS,) in sulfuric acid solution under oxygen pressure was investigated at temperatures ranging from 170 to 230°C. The effects of temperature, particle size, agitation speed, oxygen partial pressure, and pulp density were evaluated. The effects of foreign ion addition and the concentration of sulfuric acid were also examined. The apparent activation energy was estimated to be 42.6 kJ/mol in the temperature range 170 to 230°C. The reaction orders with respect to particle size and oxygen partial pressure were found to be -1.5 and 0.5 at 210°C, respectively. Experimental evidence suggests that the kinetics are limited by the surface chemical reaction initially, and then also to some extent by the diffusion of ferrous ions away from the particle surface.

Jan 1, 1999