By S Bankoff

INCE1 proposed that electrostatic attraction between oppositely charged particles was responsible for slime-coating. Del Giudice2 postulated the metathetic formation of a cementing compound. Wark3 suggested that prevention of slime-coating was related to peptization of the slime. [ ] In the experiments of Table I the technique employed was essentially that of del Giudice, with the difference that the particle was examined under a film of water rather than dry.4 In general, the polished particle was agitated for 2 min. in a pulp consisting of 12.5 grams of the slime (-200 mesh) and 50 c.c. of distilled water, washed in three baths of distilled water, and examined at 220 diameters with the Leitz Ultropak. Observations of Brownian movement were made at 850 diameters with dark-field illumination. Several of these experiments do not jibe with the metathesis theory. According to published solubilities,5,6 the lead salts of the anions in experiments c through g are more insoluble than lead carbonate, there- [ ] fore should prevent the formation of lead carbonate on the galena surface. In experiment i the calcium oxalate, which presumably was on the calcite surfaces, should have permitted the formation of a lead carbonate cement by virtue of its greater solubility. Experiments j through m show that the addition of lime accelerates the deposition of quartz onto a galena surface. The writer is unable to postulate a satisfactory cementing compound, according to the metathesis theory, to explain this effect. These experiments led to the conclusion that the metathetic formation of a cement-

Jan 1, 1941

By H. E. Cline

Mechanical properties of the eutectic between CoAl and cobalt were measured over a range of- temnperatures and strain rates for a variety of microstructures produced by directional solidification and by thermo-mechanical processing. Directional solidification led to rodlike, lamellar, and irregular microstructures. The unusually high volume fraction of the cobalt-rich rods and the lurge spacing of the rods were explained by the phase diagram. The hot-worked structure consisted of fibers of COAL in a cobalt-rich matrix. The roonl- tevlperature strength of the uvrought material increased with decreasing grain size but the 1000°C strength decreased with decreasing pain size. At high temperatures the directionally solidified tnaterial was stronger and less strain-rate-sensitice than the hot-rolled material. The fine-grained hot-worked ma-terial became superplastic at high temperatures, with tensile elongations greater than 850 pct, while at root temperature this material was ductile and impact-resistant because of the ductile matrix. Fracture occurred in the directionally solidified material at elevated temperatures by inter phase separation and at roorn temperature by cracks in the intermetallic phase. Growth of these cracks was impeded by the ductile cobalt-rich phase. It was found that the CoAl intermetallic remains ordered at elevated temperatures. DIRECTIONAL solidification of eutectic alloys has been used to produce structures consisting of parallel rods or lamellae. Although the spacing of the phases depends on the growth rate, it has been observed to be of the order of 1 µ in many eutectics. A strong intermetallic phase has been used to reinforce a ductile matrix in the rod eutectic A1-Al3Ni and the lamellar eutectic Al-Al2cu.1 The microstructure of the eutectics A1-A13Ni and A1-A12Cu remained aligned after samples of these alloys were exposed to temperatures just below their melting points for long times. Stability of the microstructure at elevated temperatures makes directionally solidified eutectics a candidate for high-temperature applications. Recently Thompson4 has developed the Ni-NiMo eutectic containing 40 pct NiMo lamellae, giving a tensile strength superior to nickel-base superalloys. Unfortunately, this eutectic oxidizes rapidly at elevated temperatures. By mechanically processing a two-phase structure, one may reach strengths as high as 700,000 psi, as demonstrated by drawn pearlite.5 In this case the strengthening mechanism was thought to be related to the fine substructure formed during deformation.5 However, a heavily worked structure may recrystallize and coarsen at elevated temperatures. Some worked eutectics such as Al-Al2Cu,6 Pb-Sn,7 and Sn-Bi7 have shown unusually large elongations in tension when tested at elevated temperatures. This phenomenon of large extension, called "superplasticity", was related to the fine grain size of wrought two-phase alloys at elevated temperatures. A mode of deformation of "superplastic" material has been shown to be grain boundary sliding,' which has also been observed during creep of polycrystalline materials.9 The Co-A1 system was chosen for this investigation after examining the phase diagrams of binary eutectics." The high melting point of 1400°C, the aluminum content which was expected to give oxidation resistance, and the properties of the intermetallic CoAl were the chief factors influencing this choice. This eutectic consists of a mixture of the intermetallic CoAl and a cobalt-rich solid solution. The intermetallic CoAl has a large range of solubility and a CsCl structure." From the similarity between CoAl and NiAl one would expect CoAl to be ordered at elevated temperatures; however, specific heat measurements" show a transition at 800°C. West-brookL2 has measured the hot hardness of CoAl and found a rapid decrease in hardness above 600°C. The tensile properties and stress rupture properties of as-cast CoAl-Co eutectic were measured by Ashbrook and wallace13 who report a room-temperature tensile elongation of less than 1 pct. I) EXPERIMENTAL A) Sample Preparation. Experimental materials were prepared by directional solidification, by hot working, and by powder processing. The starting materials were electrolytic 99.9 pct pure cobalt and 99.99 pct pure aluminum. 1) Directional Solidification. A vertical Bridgman apparatus heated by induction was used to directionally solidify cylindrical ingots $ in. in diam and 5 in. long. The apparatus was first evacuated and then an argon atmosphere was introduced to retard evaporation. The ingots were contained in an alumina crucible inside a graphite susceptor that rested on a movable water-cooled base. The base was lowered out of the induction coil at a constant rate. Eight of the ingots were solidified using a drive rate of 2.5 cm per hr, two of the ingots at 1.2 cm per hr, and one ingot at 10 cm per hr. The eutectic composition Co 10 wt pct A1 was used in all but one ingot which had the composition of the stoichiometric CoAl intermetallic, Co 32 wt pct Al. 2) Mechanical Processing. At 1000°C the eutectic Co 10 wt pct A1 is a mixture of an intermetallic phase, Co 21 wt pct Al, and a cobalt-rich phase, Co 5 wt pct Al.10 These phases differ from the stoichiometric CO 32 wt pct A1 and pure cobalt because of the large solubility of this eutectic at elevated temperatures." Four rectangular slab ingots, 4 by 1 by 12 in. high, of Co 10 wt pct Al, Co 5 wt pct Al, Co 21 wt pct Al, and Co 32 wt pct A1 were cast for hot rolling. The cobalt was first vacuum-melted, H2-treated for 20 min,

Jan 1, 1968

By B. C. Allen

The interface energies of chronzium, molybdenunz. hugsten, and their solid-solution alloys Cv-35Re, MO-33Re, and UJ-25Re were studied at 0.6 to 1.0 of the absolllte liquidus ter)zpe,vature using fiz&apos;e )izethods. Liquid surface tension, yv , was deter mined clsing the pendant-drop and drop-weight methods. Results are, respectizlely, 1700, 2370, and 2480 +100 dynes per ct for the rhernium -containing alloys and essentially the same as tlwse reported for liquid chro)riln, trolybdenum, and tungsten. Average solid slrjace energy, rsv< xias ))zeasured using tlre fiber-extetlsion method. The ratio of ysS, the acerage high-angle grain-boundary energy, to ySV cclas jolnd fronz grain-bolzdary grooue angles fort)zed at the surface in an inert atrfizosphere. Absolllte iute?:face energies were deterawined using ?nultip/rase equilibria involzing suitable liquids of known surface tension (tin, silver). Interpretation of the experimented results in view of pvobable tenzperatzcre, orientation, and purity effects giz,e the follouling approximations in ergs per sq ctn: ysv (i2lo. Mo-33Re) - 2100, ySS (Mo, Mo-33Re) - 800, rr (defornzation twins in MO-33Re at 1200"C) - 800. ysV (Cr. Cr-35Re) - 2400. YSS (CY, Cr-35Re) - 1000. Probably Ylv- YSV- 2500 for tungsten and W-25Re, giving yss (It&apos;, W-25Re) - 900. The interface energies of solid and liqid ch?&apos;omiu?.z, nolybdenu?rr, and tungsten are not geatly aff&apos;ected by rhenium and therefore are not a ttlajor factor in the ductili zing rhenium effect in Croup VI-A metals. THE interface energies of the refractory Group VI-A metals, chromium, molybdenum, and tungsten, are not well-established. The objective of this investigation was to study the liquid surface tension, solid surface energy, and grain-boundary energy of these metals and compare them to those found for the bcc solid-solution alloys, Cr-35e,&apos; 0-33e,&apos; and -25e. Five techniques were used to measure interface energies in high-purity polycrystal rod, wire, and sheet at 0.6 to 1.0 of the absolute liquidus temperature. The alloys were chosen to see if there was any connection between interface-energy behavior and the ductilizing rhenium effecL4j5 EXPERIMENTAL WORK Materials. A description of the materials used is presented in Table I. Chromium rod was prepared by arc melting iodide process crystals supplied by Chromallo Cor., hot extruding, and warm swaging to 0.63-cm-diam rod.6 The sheet was prepared by rolling as-extruded rod to 95 pct reduction in area from a hydrogen furnace at 800" to 900°C and surface grinding off 0.02 cm from each face. Cr-35Re rod was prepared by arc melting sintered rhenium powder and iodide chromium crystals, warm rod rolling to 50 pct reduction in area in cans, and swaging to 60 pct reduction in area at 1100" to 1200°C. Some of the rod was warm-rolled to sheet and then surface-ground. Portions of swaged chromium and Cr-35Re were further reduced by swaging and drawing to 0.013-cm-diam wire by the General Electric Co. Mo-33Re and W-25Re rod, sheet, and wire were provided by Chase Brass and Copper Co. The molybdenum sheet consisted of two lots, both essentially the same except for the carbon content. Liquid Surface Tension. The liquid surface tension of Cr-35Re, Mo-33Re, and W-25Re was measured by a combination of pendant-drop and drop-weight methods using techniques already decribed." Following out-gassing, molten drops were formed on the ends of centerless-ground Mo-33Re and W-25Re rods by electron bombardment at 5 x 106 mm. Similar drops were formed on outgassed Cr-35Re rods by induction heating under 1 atm of 99.995 pct Ar. Solid Surface Energy. Solid surface energy was measured by conducting microcreep experiments on molybdenum, Mo-33Re, chromium, and Cr-35Re wires at 2350°, 2306, 1550°, and 180O°C, respectively. In preparation, gage marks -2.5 cm apart and -0.001 cm deep were circumferentially scribed on the wire with a razor blade. Weights of the wire material were then attached. Five to seven reasonably straight wires were hung in a container made out of the wire material. The free end was placed through a small hole in the removable top and secured by bending a small portion 90 deg. The containers not only tended to provide vapor-solid equilibrium for the wires but also protected them from gaseous impurities. They were nominally 2.5 cm in diam by 5 cm high and were made from extruded chromium rod, Cr-35Re arc casting, molybdenum bar stock, or welded Mo-33Re sheet. After deg re as ing, the assembly was outgassed at a relatively low temperature to 2 x 10"5 mm and then recrystallized 2 to 8 hr at the creep temperature in a rhenium-element resistance furnace. The static argon atmosphere was gettered by tantalum radiation shielding. Specimen temperature was measured optically to 25"C using calibration with known melting points and blackbody conditions. The wires generally developed a stable bamboo-type structure according to Fig, l(b), (c), and (d) and retained their gage marks [upper portion of Fig. l(d)]. One or two of the weights were clipped off to provide a low load for the creep anneal. To minimize the possibility of bending or breakage, the wires remained attached to the top of the annealing container which was held to keep the wires vertical. The distance between gage marks was

Jan 1, 1967

By J. W. Cuthbertson, R. A. Cresswell

THE constitution of Cu-rich alloys with 1.5 to 13.5 pct Sn and 0.25 to 3.0 pct Be and the precipitation-hardening characteristics of alloys with 1.5 to 13.5 pct Sn and 0.25 to 1.0 pct Be have been examined. The hardness and tensile strength of the alloys examined increase markedly after solution treatment at 700°C followed by heat treatment at temperatures between 200" and 450°C. By a combination of cold work and heat treatment, hardness values similar to those exhibited by commercial Be-Cu alloys containing 2.25 pct Be can be obtained with ternary alloys containing 9 pct Sn and 0.75 pct Be and containing 10 pct Sn and 0.5 pct Be. Marked hardening effects occur with alloys containing even less beryllium. By heat treatment alone, a hardness value of 310 diamond pyramid hardness can be obtained from an alloy containing 10 pct Sn and 0.75 pct Be. Preliminary tensile tests have shown that an ultimate tensile strength of 110,000 psi with an elongation of 23 pct is obtainable by precipitation hardening an alloy with 8 pct Sn and 0.75 pct Be. The precipitation-hardening process has been followed microscopically for certain alloys and the inference is that, while the initial hardening effect is probably explained by the precipitation of the ß phase of the Cu-Be system, further hardening, proceeding at a much slower rate, also occurs, apparently as a result of precipitation of phases of the Cu-Sn system, particularly precipitation of the 6 phase at temperatures below 350". The presence of the e phase of the Cu-Sn system in certain alloys at temperatures below 350°C has been confirmed. Tin-bronzes are widely used in engineering applications where a combination of high strength and good resistance to corrosion is wanted. The maximum strength is induced in these alloys by cold working, and it would be an advantage for many purposes if high strength could be achieved alternatively by an age-hardening process. While Cu-Sn alloys have a good fatigue resistance they can be surpassed in this respect by Cu-Be, but the use of the latter alloy is limited by its high cost. If, by adding beryllium to tin-bronze, the properties of the respective binary alloys could to some extent be combined, a most attractive alloy should result. As pointed out by Raynor,¹ beryllium is on the borderline of the zone of favorable size factors for copper, and the solid solubility of beryllium in copper is consequently much more restricted than if the size factor were strongly favorable. The size factor is sufficiently favorable, however, to permit an increase in solid solubility with rise in temperature, and there is thus a composition range in which CU- Be alloys are susceptible to hardening by precipitation heat treatment. Although the a phase of the Cu-Sn system is similarly susceptible to precipitation treatment, the time necessary to establish equilibrium in commercial alloys of this type is usually so great that age hardening becomes impracticable. The addition of beryllium to Cu-Sn alloys would appear to offer a means of conferring on the latter useful age-hardening properties. Masing and Dahl² and others have, in fact, shown that the addition of beryllium to Cu-Sn a solid solutions renders these alloys susceptible to precipitation hardening and after such hardening confers on them an encouraging improvement in physical properties. If this improvement could be achieved by the addition of substantially smaller amounts of beryllium than are customarily found in binary Cu-Be alloys, the ternary alloys should possess economic advantages which might make them more attractive than the binary alloy for some applications. Binary Systems Copper-Tin: The constitution of these alloys is now reasonably well known and is summarized in the equilibrium diagram published by Raynor.³ The following observations, due to Raynor,¹ on the structure of those phases of the Cu-Sn system that are likely to be found in the ternary alloy system will facilitate the subsequent discussion on the examination of that system. The ß phase is an electron compound at the electron-atom ratio 3:2 and has a body-centered cubic crystal structure. This phase is stable only down to 586°C, at which temperature it decomposes eutectoidally into the a and y phases. The y phase has a structure that is also based on the cubic system. This phase is stable down to 520°C, at which temperature it decomposes eutectoidally into the a and d phases. The d phase is an electron compound (Cu³¹Sn8) which has a crystal structure analogous to that of 7 brass. This phase is stable from 590" to 350°C; on prolonged annealing at the latter temperature it breaks down into a mixture of the a and E phases. The e phase is an electron compound (Cu³Sn) having the electron-atom ratio 7:4. Its structure may be regarded as a superlattice based on the close-packed hexagonal system. This phase is stable from 676°C to room temperature. The primary solid solubility of tin in copper increases to a maximum of 15.8 pct as the temperature falls from that of the peritectic reaction to 586°C. The solid solubility remains constant from 586" to 520°C. At lower temperatures the solubility decreases progressively. Below 350°C the fall in solubility is pronounced and is associated with the precipitation of the e phase. This precipitation is very sluggish and does not normally occur under service conditions. Copper-Beryllium: The Cu-Be system has been investigated by Borchers&apos; and others. Raynor5 summarized the present state of information on it.

Jan 1, 1952

By David L. Holt

The contribution of grain boundary shear to total elongation, CS/E&apos;, has been measured in an Al-Zn eu-tectoid alloy that was quenched from above the invariant temperature, then annealed at 250° C to a grain size of&apos; 1.8 p. At 250°C, ks/E&apos; is low at both high and low strain rates, but reaches a maximum, estimated as 60 pct at an intermediate rate of 5 X 10 per rnin. Rate sensitivity, as measured by the index m = a log a/a log E&apos;, follows the same trend, and furthermore the maximum values of m and -cur at approximately the same strain rate. This result, combined with the metallographic observation that boundary migration enhances boundary shearing, is interpreted as supporting a previous suggestion that the high rate sensitivity characterizing super-plasticity is the result of combined boundary shearing and migration. It is suggested that the latter event relieves stress concentrations at triple points, and smoothes boundaries so that stress is governed largely by a viscous boundary shear. GrAIN boundary shear has been considered in relation to superplasticity in several recent papers.&apos; The problem has been to explain the high strain rate sensitivity of flow stress, and the variation of rate sensitivity with strain rate (E&apos;) and grain size (L). The requirements for superplasticity, small L and high T, suggest the reasonableness of an approach to high rate sensitivity involving grain boundary shear. Further support came from experiments on the A1-Cu eutectic alloy,&apos; where it was found that strain rate sensitivity of cast material annealed to produce an equiaxed, micron-size grain is always low; taking as an index of rate sensitivity m = a log a/a log <, m < 0.3. However, m in hot-worked alloy of comparable grain size can be as high as 0.7. In the cast and annealed material, each phase is a single crystal, the only boundaries are interphase boundaries, and it is, consequently, geometrically impossible for boundary shear to contribute to deformation in any major way. Other observations (for hot-worked material) were a-L at constant (low) strain rates and indications that the rate of recrystallization was enhanced as strain rate increased. As a result of this work, it was proposed that high rate sensitivity arises from a deformation mode of boundary shear associated with boundary migration. Migration serves to relieve stress concentrations at triple points, and smoothes boundaries so that they assume properties of fluid films. On the other hand, the low rate sensitivity observed at high and low strain rates reflects deformation of bulk material. Measurement of the variation of grain boundary shear with strain rate and m have not yet been made. Such measurements are important, especially in view of a proposal, differing in detail from the above, that high m arises merely from a transition between a grain boundary shear mode of deformation at low rates to a transgranular mode at high rates.2&apos;4 In the present work, the contribution of boundary shear to total deformation is measured and in addition metallographic observations are made on surfaces of deformed specimens to look at the interaction between boundary shear and migration. The Al-Zn eutectoid alloy was chosen for its homogeneous, fine-grained structure, which is obtained readily without hot-working. It has also been the subject of a previous phenom-enologically directed study. EXPERIMENTAL Material. Compression specimens, cross section 4 by + in., length \ in., were machined from a sand-cast ingot of composition 77.5 wt pct Zn, 22.5 wt pct Al. (The melt was prepared from 99.9 pct Zn and 99.99 pct Al.) After homogenization at 375°C for 50 hr, the specimens were quenched in brine and removed before the heat evolution that accompanies de -composition of the high-temperature phase.5&apos;6 The resulting microstructure, see Fig. l(a), was too fine for grain boundary sliding to be easily studied; coarser structures were obtained by annealing for various times at 2 50°C. Annealing was terminated by a brine quench. Final average intercept lengths between all grain boundaries (both interphase and those lying in a phase), L, were: 0.5 p [annealed for 15 min, Fig. (a)], 0.8, 1.1, and 1.8 p [Fig. l(b)l. Testing Procedure. An Instron machine was used for most of the compressive deformation. Tests were of two types: those in which crosshead velocity was changed in steps to measure m as a function of strain rate15 and tests at constant velocity to a fixed (engineering) strain of -0.2 (20 pct). Stress reached a steady-state value (a) which was plotted, on a logarithmic scale, against log strain rate (E&apos;). An alternate and equivalent evaluation of m was to take the slope of the log o vs log 6 curve. Time at temperature before testing was 15 min. Strain rates covered by the Instron (4 x lo-&apos; to 4 x 10&apos; per min) were insufficient; at a higher rate of 5 x lo2 per min a gas-operated testing machine was used, the gas driving a piston to compress the specimen at a controlled velocity.&apos; To obtain points on the log a vs log E&apos; curve at low rates, specimens were compressed by a dead weight. strain rate was an average value computed by dividing strain at the end of test by loading time. In some tests strain was measured at fractions of the loading time; creep rate was found to be reasonably constant.

Jan 1, 1969

By R. D. Lord

The search for the best practical means of storing sulfide bearing tailings, where there is no residual excess of carbonate material is discussed in this paper• Usually the sulfide content decomposes, with the aid of bacterial action, and the resulting sulfuric acid escapes, along with any heavy-metal solutes, through embankments that are usually porous to some degree• The problem is typified in the tailings of the uranium operations of Elliot Lake, Ont., where mining started some 20 years ago• The approach to tailings disposal paralleled the practice for other hydrometallurgical plants treating gold and base-metal ores• Impoundment areas were designed to retain solids, and a clear and neutral overflow was considered satisfactory practice• Now experience has shown that these areas, some of which have been idle for over a dozen years, release acids in seepage and overflows to an unacceptable degree• To protect natural water courses, neutralizing plants are operated wherever required• Lime slurry is fed continuously into the tailings outflows in a quantity sufficient to raise the pH to 8•5 and precipitate heavy metals that may be in solution• The objection to this procedure is that the plants will require servicing indefinitely, unless a better remedy is found• The problem differs only slightly from that common to base-metal concentrators in that here the ore has been leached with sulfuric acid for the recovery of uranium• Any native content of calcareous material has been digested, and only that added for final neutralization is available to maintain a pH unfavorable to bacterial activity• Chemical oxidation slowly lowers the pH and when this reaches a level of 4•5 or less, bacteria become active and greatly accelerate the formation of acid. The bacterial process is probably at least ten times as fast as the chemical oxidation• Location and Processing The operations referred to, uranium and one copper mine, are located at approximately 46°N and 82°W longitude• This is typical Canadian Shield country, a land of lakes, deeply glaciated and rocky, with sparse soil which supports mixed forest cover• Drainage is to Lake Huron, 25 miles to the south• Average temperature is 45°F, ranging from -40° to +95°F• Annual precipitation is 38 in•, about half of which is snow• The ore is Precambrian, quartz-pebble conglomerate, with mineralization in the matrix• From 5 to 10% pyrite is present• All known means of pre-concentration have been tested, but a bulk sulfuric acid leach has proved the most efficient. Tailings have from the outset been neutralized before release• Current practice is to add ground limestone to bring the pH to 4•5, and then lime to raise the value to 10•5• Environmental regulations have recently been increased and the foregoing meets the new standards• Separate measures are taken to precipitate radium• Remedial Measures Since the outstanding environmental problem is the oxidation of pyrite by bacterial action, the solution is to contain the products, or arrest the process• Given the ambient temperature, favorable half of the time, four items are essential to the activity• 1) Pyrite• 2) Moisture pH < 4•5. 3) Oxygen• 4) Bacteria• Removing any one of these out of the range of tolerance will bring the reactions under control• A variety of proposals considered, and a number tested for the arrest of the process, are: (a) render embankments impermeable, (b) provide an impermeable cover, (c) cover with an oxygen absorbing layer, (d) provide a vegetative cover, (e) flood the site, (f) remove pyrite from current tailings, (g) add excess limestone to current tailings, (h) poison the bacteria• Bank Seal-On existing impoundment areas, where the embankments are several thousand yards in length, it is believed that any program of injecting sealants can have small chance of success• However, a moisture barrier is an indicated specification for future construction, and this can be highly expensive• Surface Seal-Depending on the configuration of the deposit, the downward travel of water should be prevented, and oxygen excluded• Burying a plastic membrane just below the surface has been considered, as has the application of a liquid sealant that would penetrate the surface. The objection to these remedies is the excessive cost of dealing with large areas and the expectation of only temporary benefit as a result• Frost penetration is over 4 ft, and frost action breaks up asphalt paving and all but heavy concrete in a few years• Organic Layer-An oxygen-absorbing layer, such as bark fines from paper mills has been proposed as a surface treatment• Cultivated into the tailings such material might be expected to arrest subsurface oxidation for some years• Estimates are 100 tons per acre of bark fines, or 35 tons per acre of sawdust, and these enormous quantities do not so far give assurance of providing a long-term remedy• Vegatative Cover-Several obvious benefits would result from a good growth of grass or other vegetation on abandoned tailings• While restoring the natural green of the tract the growth would prevent wind-blown dust and reduce erosion• Subsurface oxidation should be reduced, as well as the upward movement of ground moisture as occurs in dry weather. To this end, considerable research and field testing has been carried out to arrive at a formula - a prescription which will provide a self-sustaining growth on the tailings surface, or at least one that would survive with reasonable maintenance attention. Many test plots have been run with different combinations of surface treatment and seed mixtures. Generally, by addition and close cultivation of limestone, lime, and fertilizers, technical success has been demonstrated• Plants with a high tolerance for acid soil seem the more hardy, and a pH above 3 is indicated so that nutrients can be absorbed• Recommendations are for 12 to 15 tons of

Jan 1, 1977

By C. G., Fink

The dissolution of gold by cyanide solutions was studied by determining the time required for the solvents to dissolve gold leaf. Minute traces, even 0.5 ppm, of sulphide ion retard the dissolution of gold, and this behavior cannot be accounted for by the presently accepted hypotheses involving oxygen-depletion or thiocyanate formation. On the other hand, traces of the salts of lead, bismuth, mercury, and thallium considerably accelerate the dissolution. The beneficial effect of lead is dependent upon the pH and cyanide ion concentration of the solution.

Jan 1, 1950

Mounting pressures to increase efficiency and yield, conserve energy, or minimize pollution have all taken their toll on the minerals industry. As management and technical personnel take a harder look at their operations for ways to shave cents off operating costs or to squeeze a bit more productivity out of existing equipment, instrumentation often comes up as the most effective answer. When Amax Lead installed an automatic grind control system in its Buick mill, ore throughput increased by 3 to 5%. Mill operators calculate that the initial investment is returned to them several times annually.

Jan 2, 1978

By C. G. Palagi, S. S. Stillar

The C. E. Weed concentrator treats 51,000 tons per day of 0.5% to 0.7% copper ore received from the Berkeley Pit, the Continental East Pit and the Butte underground mines. Improved operating techniques and conversion from semi-autogenous secondary grinding to ball milling have increased tonnage from an original design of 42,000 tpd. Separate treatment of sands and slimes, with recovery of soluble copper from the slimes, has increased total copper recovery. Concentrator tailings are pumped 600 vertical feet and 20,000 horizontal feet for disposal.

Jan 1, 1976

By Phillip E. Butler

The Pennsylvania Dept. of Transportation is actively engaged in the utilization of coal mine refuse in the construction of highway embankments. Long-held objections for utilization are invalidated by research, laboratory data, and construction performance. Laboratory, engineering, construction, and environmental impact analyses are presented from the construction of the Cross Valley Expressway embankment at Forty Fort, Luzerne County, Pa. Comparisons of laboratory data and construction measurements are given. The refuse embankment is the first of its size in Pennsylvania, and possibly the U. S., covering 1.5 million cu yd.

Jan 1, 1977

By C. Hirayama

THIS investigation was undertaken to determine some of the factors contributing to the embrittle-ment of glass-coated silver wire on heat treatment. The materials used in this investigation were 22 and 23 AWG silver wires obtained from Handy and Harman as "fine quality, soft temper." A wet analysis of one sample showed 99.8 pct Ag. The 23-gage wire was covered with a double layer (2.5 mils thick) of electrical grade fiber glass (aluminum borosilicate glass containing a relatively high concentration of calcium, and a very small amount of

Jan 1, 1960

CHEMICAL PRECIPITATION U.S. 4,067,789 - Removal of soluble manganous ions from a zinc sulfate solution formed by leaching roasted zinc sulfide ore with spent electrolyte. An excess of ammonium persulfate or like oxidant is added to the leach solution to convert manganese to insoluble, filterable gamma-manganese dioxide, and the precipitate separated from the solution by filtration. L. Harris and A. K. Hanson, Jr., assigned to Newmont Exploration Ltd. Jan. 10, 1978. 11 pp. (204-119). Filed: 5-3-76 (682.442). (Drawing on page 67.)

Jan 1, 1979

By Archer E. Wheeler

IN the copper industry, the year 1942 was one of striving for larger tonnage and increased production. The demands of the war program placed copper high in the list of strategic metals and the Government encouraged production by offering a premium of 5c. per pound for copper output in excess of the 1941 quotas. This had the effect of increasing the tempo of existing operations and also of initiating a number of projects which will eventually result in production from sources not hitherto exploited. No radically new methods of copper reduction were reported.

Jan 1, 1943

By Milton E. Wadsworth, J. Brent Hiskey

Galvanic interaction between particulate chalcopyrite (CuFeS2) and copper results in the rapid conversion of chalcopyrite to chalcocite. The effects of temperature, surface area, concentration of sulfuric acid and agitation were systematically evaluated. The kinetics were found to be controlled by a steady-state current flow controlled by the effective anodic and cathodic surface areas involved in the galvanic couple. The experimental activation energy was 11.5 and stoichiometric data and reaction products have been characterized. The overall kinetic system has been evaluated based upon an electrochemical model.

Jan 1, 1974

ONE HUNDRED AND FOURTEENTH MEETING OF THE INSTITUTE, MONDAY, FEBRUARY 19, TO THURSDAY, FEBRUARY 22, INCLUSIVE, 1917 Committee on Arrangements DAVID H. BROWNE, Chairman LAWRENCE ADDICKS Louts D. HUNTOON E. MALTBY SHIPP PERCY E. BARBOUR H.A. MEGRAW BRADLEY STOUGHTON GEORGE D. BARROW _ THOMAS T. READ EDWARD B. STURGIS KARL EILERS BURR A. ROBINSON ARTHUR L. WALKER F. T. RUBIDGE Summarized Program MONDAY, FEBRUARY 19 9:00 a.m. to 5.00 p.m. Registration at Institute Headquarters. , 10.00 a.m. Simultaneous Sessions on Geology and on Metallography.

Jan 2, 1917

By C. G. Fink, G. L. Putnam

The dissolution of gold by cyanide solutions was studied by determining the time required for the solvents to dissolve gold leaf. Minute traces, even 0.5 ppm, of sulphide ion retard the dissolution of gold, and this behavior cannot be accounted for by the presently accepted hypotheses involving oxygen-depletion or thiocyanate formation. On the other hand, traces of the salts of lead, bismuth, mercury, and thallium considerably accelerate the dissolution. The beneficial effect of lead is dependent upon the pH and cyanide ion concentration of the solution.

Jan 9, 1950

By W. J. Babyak, J. M. Sheehan, H. W. Paxton

THE- solubility of hydrogen and deuterium in solid niobium up to I-atm pressure has been established bv a number of workers.1-5 X-ray examination at room temperature of specimens reacted in hydrogen at high temperatures from 300° to 1000°C shows the presence of two phases—a bcc phase (a) based on the niobium lattice and with an u0, increasing from 3.30A for Nb to 3.32Afor NbHo.L, and an orthorhombic phase6n = 4.84A, h=4.90A, c =

Jan 1, 1960

By Robert Keeney

IMPORTANT recent developments in the melting and annealing of non-ferrous metals include: 1. Melting of nickel silver in the vertical ring induction furnace. 2. Electric melting of stereotype metal. 3. The rotary-drum gas-fired brass melting furnace. 4. The low-frequency coreless induction furnace. 5. Finishing annealing of brass sheets with city gas1 replacing wood. -in the large brass-rolling mill. 6. Electric annealing of brass and copper tubing and sheets. 7. Replacement of oil by gas and electricity in the annealing of nickel-silver shells and stampings.

Jan 1, 1930

By Herbert Herman, M. E. Fine

THE first decomposition product of a supersaturated aluminum-rich A1-Ag alloy at low tempera- tures is Guinier-Preston zones.&apos;-, The zones are ideal and each consists of a spherical shaped silver-rich cluster about 16 A in diam syrounded by a silver-poor shell approximately 72A in diam.&apos; The composition of the two regions is not known with certainty., After quenching from the solution anneal, these zones form rapidly on aging at temperatures as low as -30°C.5 The rate of zone formation increases with aging temperature; the activation

Jan 1, 1961

By John Marshall

THE purpose of this paper is to present to the profession data and experience obtained over a period of 5 years in the operation of 87 shaker-conveyor units, and the production of 2,169,638 tons of run-of-mine anthracite coal. The data are not generally available and should be of interest to those concerned with the operation of anthracite and bitu-minous mines. To simplify comparison, a ton of 2000 lb. of raw run-of-mine coal has been used as the production unit throughout this paper.

Jan 1, 1940