By George Comstock

IT seems a common opinion among metallographists that all light-gray inclusions seen with the microscope in polished sections of steel are manganese sulphide. Examples of this belief are continually appearing, as for instance in the paper by Dr. Henry Fay on manganese sulphide as a source of danger in steel rails,1 and in Lieutenant-Commander Cook's paper on Metallography of Steel for U S. Naval Ordnance.2 Slate FIG. 1-TRANSVERSE VIEW OF THE EDGE OF A SMALL HOT-ROLLED STEEL ROD. ETCHED WITH PICRIC ACID. X 200. colored inclusions are considered to be silicates, and dove-gray inclusions, manganese sulphide. To show the danger in the latter unqualified assumption, it should be sufficient to examine the edge of any piece of steel that is covered with a fairly thick scale, and that has been polished in such a way as to prevent the scale from breaking away entirely below the polished surface. This can be done by protecting the scaled edge of

Jan 12, 1916

By D. F. Hewett

CONTENTS PAGE Introduction 1 Geologic features of eastern Oregon 2 Geology of the Sumpter quadrangle 2 Rocks older than the ore deposits 3 Rocks younger than the ore deposits 8 Lodes of the Sumpter quadrangle 8 Areal distribution 8 Geologic distribution 9 Major features of the veins 9 Mineralogy and texture of the veins 13 Ore deposits zonally disposed around the Bald Mountain batholith . . . . 13 Summary of mineralogy and texture 32 Zonal relations 33 Ore deposits zonally disposed around Greenhorn Mountain batholith . . . 36 Zonal relations 37 Relation of textural features to zonal arrangement of veins 37 Summary of zonal relations 38 Comparison with similar districts 39 Outlook for the district 40 INTRODUCTION IN an earlier report on the Sumpter quadrangle1 it was briefly stated that the quartz lodes of that region might be separated into several groups or belts on the basis of the kind and abundance of the minerals of which they are composed, and that these belts were disposed as areal zones around the principal intrusive mass of the region. When the opportunity to revisit the region was offered in 1929, as a result of a cooperative agreement between the State Mining Board of Oregon and the United States Geological Survey, it seemed advisable to pay particular attention to this feature of the lodes, in the hope that if the idea of zonal relations was confirmed it might serve as a guide in exploitation.

Jan 1, 1931

By Charles W. Merrill

Obsolescence in the mineral world is virtually nonexistent if the term is taken to mean that a mineral commodity, once established in commerce and industry, subsequently has fallen into disuse. We are living in an age of minerals. Each generation puts an increasing array of mineral-based commodities, in larger quantities, to more uses than ever before. Bastnasite, a museum mineral and a collector's item a few years ago, is now produced in quantity at Mountain Pass, Calif. Uranium, a minor byproduct of vanadium mining in the Rocky Mountain plateau area before World War 11, has grown to be a leading mineral product in several western States. And finally the total quantity and value of minerals both in the United States and in the World establish new records almost yearly. Surely the mineral industry as a whole is not obsolescent in our economy. Nevertheless, there are particular uses for particular minerals that are obsolescent and some applications have been supplanted entirely. Tin does not occupy the prominent place in foil manufacture that it once did, and the schoolboy's slate left most classrooms before the oldest of us were born.

Jan 9, 1964

By M. R. Pickus, I. W. Pickus

ORDINARILY age-hardening is thought of as being associated with a limited solubility of one metal in another. Much less has been written about the type of age-hardening that attends the formation of superstructures. Solid solutions generally have a disordered or random arrangement of atoms; that is to say, in a unit cell, such as that of the face-centered cubic lattice, there is no distinction between atomic sites. Atoms of a given metal may occupy cube corners or face centers. Under certain conditions, however, some alloys develop what is known as an ordered structure. In this case, cube corners would be occupied by only one type of atom and face centers by another type, Associated with this ordering process are many interesting changes in physical and electrical properties. Moreover, in many instances the alloys become susceptible to age-hardening. From the evidence now to be described, it appears that age-hardening in 14-carat gold alloys is due to the formation of both a super-structure and a precipitate. Alloys of the metals gold, silver and copper were known in antiquity. The available knowledge regarding their constitution has been ably summarized and extended by Sterner-Rainer,1 Janecke,2 Carter,3 Wise,4 and Coleman.5 Despite the long familiarity with these alloys and the numerous investigations of their properties that have been made, there is still much that remains unexplained. It has been known for a long time that the hardness of these alloys is closely related to the rate of cooling, Similar changes have been observed in the binary gold-copper system,6 one alloy of which corresponding to the formula Cu3Au, has been the subject of a careful and competent report by the English investigators, Sykes and Evans.7 They have established the fact that the shift of atoms from the ordered to the disordered condition takes place in some critical temperature range. At temperatures above the critical range the structure is random, and at temperatures below it the structure is ordered. No difference between these two structures is revealed by the microscope. Both have a face-centered cubic lattice and complete solubility, so that there is no evidence to suggest that the changes in properties are associated with a phase change, The more slowly the alloy is cooled, the higher is the degree to which the ordering process proceeds and the more marked is the increase in hardness. As experimental data were accumulated on 14-carat gold alloys, several contradictions arose. Certain observations tended to confirm the existence of a superstructure, while other observations seemed to be inconsistent with such a transformation. PRESENT INVESTIGATION As a focal point about which to develop this subject, it is expedient to consider first

Jan 1, 1943

By W. H. Boyer, J. W. Gabelman

The concept of metal zoning has long been recognized (Spurr, 1907, 1923; Emmons, 1924, 1926; Lindgren, 1933; Rateman, 1950), although it has been considered indistinct for most epithermal districts. The geometric relation of barren zones of hydrother-mally altered rock to ore deposits was emphasized in the work of Lovering (1941, 1949, 1950), Sales and Meyer (1948, 1949, 19501, Burbank (1941, 1950), Schwartz (1939, 1950), and Kerr (1947). Lovering (op. cit.) and Sales and Meyer (op. cit.) emphasized the consistent presence of barren alteration envelopes enclosing individual ore bodies, particularly of the vein type. Schwartz (1950) noted a difference between the distribution of alteration zones described by Lovering and by Sales and Meyer, as compared with those associated with the porphyry copper deposits of the Southwest. The disseminated deposits of the Southwest usually occur within large bodies of altered rock whereas most veins do not. In the following discussion the mineralization process is conceived of consisting of two distinct phases: pre-ore nonmetallic alteration and metallization. In the present investigation the position, size, and shape of all known hydro thermally altered areas and the position, size, and metal type of all known ore deposits were plotted on base maps of southwestern and west-central Colorado (Figure 1). The maps indicate a generally consistent geometric relation between altered and metallized areas. The addition of alteration to the pattern of metal deposits establishes a temperature zoning pattern of much greater clarity than that formed by the epithermal metal deposits alone, and allows a more precise definition of mineral belts. The center of strongest mineralization is indicated to be the area of greatest barren alteration, and metal deposits are grouped about it both under structural control and crudely in response to temperature zoning. The combination of an area of strong alteration and associated marginal clusters of metal deposits is defined as a mineral district. The strong similarity in individual deposits, in groups of different types of deposits, and in the alteration-metallization relation in districts throughout the region implies that a single metallogenic province is represented in southwestern and west-central Colorado. The occurrence of deposits in Tertiary voi-canics indicates a late Tertiary metallogenic epoci., although an early Tertiary epoch is known locally as at Ouray. Patterns formed by mineral districts can be

Jan 1, 1961

By W. L. Saunders

WHEN work was begun in September, 1910, on the rock excavation for the foundation of the gigantic dam at Valhalla, N. Y., which is to convert Kensico lake into an important storage reservoir of the Catskill Aqueduct system, one of the first steps taken by the contractor, H. S. Kerbaugh, Inc., was the development of a quarry to supply the stone needed in the construction work.The importance of a bountiful supply of suitable rock in an accessible location is apparent when it is considered that nearly a million cubic yards of cyclopean masonry will be contained in the completed structure, not to mention dimension and facing stones, concrete blocks, and mass concrete. The dam structure will be over 1800 ft. long and about 170 ft. above the present river bed. However, for a distance of some 800 ft., it will be carried down to solid ledge rock, which will make the finished structure about 300 ft. in maximum height. It will be about 200 ft. thick at the base and directly beneath the coping it will be 28 ft. thick. This dam will raise the reservoir surface 110 ft. above old Kensico lake. The reservoir capacity will be 29,000,000,000 gal.-equal to New York's total needs for over two months. The contract price for this work is nearly $8,000,000 and is second only in amount to the cost, over $12,600,000, of the Ashokan Reservoir work. Fig. 1 is a view of the dam site.

Jan 2, 1914

By C. F. Weinaug, R. W. Farley, J. F. Wolfe

A rapid, accurate method for predicting the dew points of gas condensate systems and their subsequent normal and retrograde phase behavior with pressure decline has been developed. The method predicts dewpoint pressure, volume percent liquid, condensate content of produced gas, and the liquid and gas compositions at pressures below the dewpoint pressure. Use of a modified form of the BWR equation of state, which was established by regression calculations on experimental data from several gas condensates, provides depletion behavior predictions that are significantly improved over predictions using K-values based on convergence pressures and Standing's correlation for density. INTRODUCTION Prediction of complex hydrocarbon-mixture thermodynamics is fundamental to reservoir and gas process engineering. In particular, accurate descriptions of phase behavior are needed to plan production operations for gas-condensate reservoirs. Although analysis of reservoir behavior during producing and cycling operations can be made for simple reservoir models, extensions of these studies to more complex reservoir systems are still difficult, both with regard to numerical techniques and the phase behavior of the fluids. This report presents a mathematical method for handling the complex phase relationships encountered in retrograde condensates; it represents an advance in reservoir behavior technology in that it will aid the development of closed-form mathematical representations of total production systems. A typical phase diagram for a complex hydrocarbon mixture is shown in Fig. 1. When the reservoir temperature T, is higher than the critical temperature Tc, and lower than the critical-condensation temperature Tct' the mixture is a gas condensate. Decreasing the pressure on a condensate while maintaining nearly constant temperature will result in two phases forming at the dew point. Further decrease in pressure will cause additional liquids to be formed. This phenomenon is called retrograde condensation. As pressure continues to decrease, normal phase behavior regions are encountered (liquid vaporizes as the pressure decreases) until the low-pressure dew point is encountered. When a gas-condensate reservoir is produced, gas is withdrawn and the volume of fluids in the reservoir remains nearly constant as the pressure declines. Heavier components tend to accumulate in the liquid phase as a result of retrograde condensation, while lighter components tend to concentrate in the vapor phase. Thus, as the gas is produced the composition of the gas and the condensate

Jan 1, 1970

By Edward Capillon

THE problem of scrap is probably of greater importance inn the production of gold, silver and other precious metal alloys than is the case for base metals and alloys. Remelting of gold and silver scrap in the shop is always a costly process because it involves losses by oxidation of the base metals in the alloy with a consequent increase in the percentage of precious metal. This is most marked in the case of alloys containing the low-boiling and easily oxidized metals zinc and cadmium. Since it is. not generally feasible to assay every shop remelt it follows that the possibilities of lost values are large. So-called rolled gold and silver plate is made by soldering or welding the precious metal alloys onto base, metal. Such plate when defective must be sent to the refinery to recover the gold and silver values, thereby involving additional expense in the form of refining charges. It is obvious therefore that gold and silver alloy scrap is an important item in manufacturing cost and must be reduced to a minimum. The amount of scrap resulting from poor metal will depend on a number of factors in the manufacturing operations, not least among which is the melting and casting practice. The notes which follow are a summary of experiments performed at various times to determine what variables in melting and casting are influential in the production of sound alloys.

Jan 1, 1930

By R. W. Smith

Many industries such as the cement industry handle large quantities of limestone and clay slurries. However, at present very little is known about the flow properties, such as friction loss due to flow of slurries in pipelines. This lack of knowledge has made it often very difficult to calculate the total dynamic head of a proposed slurry handling system, and therefore has often made the selection of correct size slurry handling equipment difficult. Because of lack of knowledge about slurry flow a study of slurry flow theory has been made at the Portland Cement Association's Research and Development Laboratory with the idea of developing a method whereby friction losses due to slurry flow may be predicted for any size pipeline. The flow equations developed have been checked by pilot plant size equipment. DERIVATION OF FLOW EQUATIONS It has been known for some time that limestone and clay slurries handled in cement plants do not flow in the same manner as a Newtonian fluid such as water. When a Newtonian fluid flows the shear stress at any flow velocity is proportional to the rate of shear. This phenomenon can be illustrated by a line (Figure 1). The viscosity of the fluid is the slope of the curve. Thus, the flow properties of the material may be characterized by a single materials constant: viscosity. When a non-Newtonian fluid with the type of characteristics exhibited by limestone and clay slurr-ries flow, a similar curve can be constructed (Figure 2). This graph is a shear diagram of a Bingham plastic non-Newtonian fluid. It should be noted that with the Bingham(1) plastic type of flow viscosity, the slope of the curve, is still an important materials constant. In addition, however, there is another materials constant, namely the yield stress of the material. One way to visualize this constant is to consider it as the amount of energy that must be put into a Bingham plastic material to start it flowing.

Jan 1, 1961

By Job Goostray

IN THIS paper, as in so many other discussions of historical nature, there is little chance for original material and much has had to be rewritten from older papers, documents, accounts, reports, and the like, some of which are of doubtful authorship or contain conflicting statistics. Fully aware of these little historical pitfalls, the authors have tried to quote the origin where possible, and also to seek further confirmation when the statement warranted it, but cannot assume responsibility for certain facts and dates. The Encyclopedia Britannica was frequently consulted. The authors wish to acknowledge assistance from MacKintosh-Hemphill Co.-formerly the Fort Pitt Works-and also from officials of the Watertown Arsenal who loaned valuable books and gave much necessary information. They are particularly indebted to Colonel Dixon of that institution. The data on modern guns were furnished by Mr. F. Brauer of the Watertown Arsenal; Mr. H. S. Chaffee assisted by obtaining records and data of work carried on by the Builders' Iron Foundry of Providence, R. I.

Jan 3, 1925

By C. F. Lucks, W. D. Wood, H. W. Deem

Electrical ad thermal-conductivity measurements have been made on titanium and 6 titanium alloys. The following expression was derived for calculating thermal conductivity from electrical conductivity: K = 0.626 s T x 10-8 + 0.00497 where K = thermal conductivity, cal sec-1 cm-2 cm0C-1 s = electrical conductivity, ohm-]cm-1 T = temperature, deg Kelvin This expression gives calculated thermal conductivities that are not in error by more than 10 pct from the experimental values for A-55 titanium and the 6 alloys measured; namely, A-110AT, C-110M, C-130AM, Ti-6A1-4V, Ti-140A, and Ti-155A, which are representative of the presently available commercial a and a-ß titanium alloys. THERMAL conduction in a gas, liquid, or amorphous solid is accomplished by energy diffusion from molecule to molecule, a relatively slow process. For this reason, such materials have a low thermal conductivity. When a material is crystalline, there is in addition a heat transfer by a vibratory motion of the crystal lattice. It is the contribution of this lattice conduction that makes a crystal a much better conductor than a gas, liquid, or amorphous solid. Lattice conduction, however, does not account for the relatively enormous thermal conductivity of a metal. This is explained by the freedom of movement of valence electrons. These valence electrons drift in a metal in a direction toward a drop in electrical potential and, to a lesser degree, in the direction of a temperature drop in the metal. Since both the electrical and thermal conductivities of a metal depend upon the presence of free electrons, there should be some relatively simple relation between the two. Wiedemann and Franz in 1653 first discovered an approximate empirical relation between the electrical and thermal conductivities of metals at the same temperature. This ratio varies appreciably with temperature, and Lorenz later showed that by adding a temperature factor to the Wiedemann-Franz ratio the value of K/(s T) is constant, where K is the thermal conductivity, a the electrical conductivity, and T the absolute temperature. This Lorenz constant shows a greater variation for alloys than it does for pure metals, the ratio increasing slightly as the proportion of alloying elements increases. It has been found that a closer correlation between electrical conductivity and thermal conductivity can be obtained by means of an equation of the form K - A s T + B [1] where A and B are constants. In this equation the term AsT is the contribution of electronic conduction and B is the contribution of lattice conduction to the total thermal conductivity. EXPERIMENTAL MEASUREMENTS Electrical-resistivity and thermal-conductivity measurements on titanium and 6 titanium alloys serve as the basis for determining an equation of the K = AsT + B type for titanium alloys. Specimens—Table I shows nominal compositions of the 7 metals on which electrical and thermal conductivities were measured. The electrical and thermal-conductivity specimens for each alloy were taken from stock of the same heat and usually from adjacent sections of the same bar. All of the metals measured were in a mill-annealed condition. Methods—Electrical-resistivity measurements

Jan 1, 1959

By . M. Muskat

A THEORETICAL consideration of the mechanics of various water-flooding systems with the viewpoint of comparing their relative merits involves the study of two fundamental properties of such systems. On the one hand, it is important to determine the efficiency of the flood as measured by the percentage of the total area that is swept out by the encroaching water before water actually reaches the output wells. This is really a measure of the regional tendency of the water to "bypass" the oil. On the other hand, the various systems must be compared from the viewpoint of their resistances which determine the rate of fluid production obtainable for given pressures maintained at the water input wells. The first of these questions has been studied and very definite answers have been obtained by means of simple electrolytic models.1 These models showed that, in an ideal system, the percentages of the areas flooded out before water reaches the output wells are about 57 per cent for the direct line-drive flood (the input and output wells being equally spaced and placed in alternate parallel lines), 74 per cent for the regular five-spot network, and 79 per cent for the seven-spot network. With respect to the efficiency of the usual flooding arrangements, they are, therefore, given quite accurately by the above numbers. With regard to the resistances of the flooding networks, electrical conduction models have also been used successfully2 and are well adapted to the problem of determining experimentally the pressure distribution and streamlines, or over-all resistances of specific flooding networks. However, such models do not permit readily a study of the effect of changing dimensions or configuration within a network, since a new model must be made up for each set of dimensions considered.

Jan 1, 1933

By F. Haessner, M. Wilkens, U. Jakubowski

ThOUGH at present there is a wide range of possibilities for the quantitative determination of preferred orientations, pole figures of identical specimen material have not been determined by different methods as yet.''' In this paper a comparison of (Ill), (200), and (220) pole figures is presented which were obtained from a 95 pct cold-rolled high-purity cop- per sheet (99.9998 pct Cu), by three different methods. The three methods are: a) The combined X-ray reflection-transmission technique of plane samples by schulz3 and Decker, Asp, and Harker. 4 A Siemens texture goniometer was used. The experimental details are described elsewhere. 6 b) The X-ray reflection technique of spherical samples by Jetter and Boric.' A Siemens texture goniometer with some modifications was used. The samples were prepared by sticking 140 polished sheets together with an adhesive and machining a sphere (20 mm diam).* Additional

Jan 1, 1967

By Charles S. Barrett

NUMEROUS determinations1-7 of the tex-ture of cold-rolled polycrystalline iron, steel, and ferritic alloys have been made with good agreement among the various observers as to the principal features of the texture common to all, but there has been no adequate explanation of the texture in terms of the behavior of individual grains. This study presents an explanation of the texture based on the observed rotation of single crystals when deformed in a manner similar to a grain in the aggregate, a method we have found useful in leading to a better understanding of compression and tension textures;8,9,10 in particular, the aim has been to determine experimentally the end orientations of rolled single crystals of iron. These are discussed in connection with the point of view of Wever1 and of Boas and Schmid2 that the rolling texture is a simple compression texture (compression normal to the rolling plane) superimposed on a simple tension texture (tension in the roll-ing direction), and the point of view of Kurdjumow and Sachs3 that three ideal end orientations exist.

Jan 1, 1940

By O. E. Palasvirta

Several drum-type, low-intensity dry magnetic separators have recently been described 1,2,3,4 all of which share at least two generic similarities. The magnet consists of a multiplicity of poles of alternating polarity and, the speed of the drum shell, relatiw to the magnet, is such that the magnetics are agitated through rotation of the magnetic particles around their individual axes. The speed of the drum relative to the magnet (differential speed) determines the frequency of the field reversals. For effective agitation this frequency generally has to be above a specific value, which varies according to the mean particle size of the magnetics. With separators of small diameter, say less than 11/2 ft., a sufficient differential speed for treatment of fine magnetite can be attained only by rotating both the magnet and the drum separately; separators of large diameter may attain sufficiently high differential speeds with stationary magnets. Separators of large diameter thus have the advantage of simplicity of design. The capacity of a separator of this type is directly proportional to the speed of the shell. As the centrifugal force opposing the magnetic force increases at a slower rate than the peripheral speed of the shell when drum diameter is increased, large drums can be operated with higher peripheral speeds. Thus they have a higher capacity than smaller drums. Separation is also a statistical phenomenon, i.e. the grade of concentrate improves as the number of agitations or rotations of the magnetic particles per separation increases. As separators of large diameter have space for a large number of magnets they are best suited for production of optimum grade concentrate. The statements above are general clues For separator design. In the following an expression IS derived showing a more exact relationship between the pertinent separator variables. As both magnetic attraction and centrifugal forces are directly proportional to the volume of the affected bodies, complications in mathematical analysis, arising from variable particle size, are avoided by considering the force per unit volume of affected material. For the magnetic force per unit volume Runolinna (3) gives the following equation: V " 1 + N(ur, - 1) uo dr (1) where ur and uo stand for the relative permeability and the permeability of vacuum, respectively, N is the demagnetization factor, B the intensity of the magnetic field, and r the distance from the face of the magnetic pole. The permeability of a specific magnetite ore can generally be considered as a constant. For ground, liberated material N can also be treated as a constant, and the first simplification can be made by writing ur-1 1=k1. 1 + N(ur - 1) uD k1. Fig. 1 shows the field intensity curves for two U-magnets of different size, but of roughly similar geometry of cross-section as plotted against the distance from the plane of the pole faces. The curves

Jan 1, 1961

By M. M. Singh, J. W. Brown

Three rocks of highly varied physical properties are selected for the first reported experimental study concerning microseismic activity of rock under tension to determine the effects of static fatigue, loading rate, repeated loading and rock anistropy compared to compression and bending loads. The microseismic method of detecting rock under deformation may be a great potential tool in surveillance and location in situ of dangerously stressed strata, as well as predicting rock failures. Noises emitted under load or the rate of energy (energy of noise pulses generated per unit time) are computed for varying conditions. The tests are conducted at constant load on a dead weight loading machine to eliminate all possible extraneous noises — an indispensable precaution — at various load levels. Experimental results are reported including the relation of total energy emitted to tensile strength of rock and the possibility of simulating a phenomenological model for microseismic activity. Plots of some of the experiments are included. INTRODUCTION Rock failure, whether on a large scale faulting in the earth's crust and rock bursts in mines, or on small scale ruptures of laboratory test specimens, generates transient vibrations in the rock mass. Mechanisms of intermittent deformation, such as twinning and cracking through and between mineral grains, also produce similar vibrations, but of very small amplitude. Such vibrations from both deformation and failure are referred to as microseismic activity, rock noise, or occasionally seismo-acoustical activity. An individual rock noise is sometimes

Jan 1, 1967

By B. Wilshire, P. W. Davis

It has been shown that grain-boundary migration during high-temperature creep can reduce or even prevent the formation of intercrystalline voids, giving a considerable increase in ductility.' A similar observation has been made in a recent investigation of the creep properties of various grades of nickel and nickel alloys. The results can be illustrated by the observations made on: a) Pure vacuum-cast nickel (99.993 pct Ni) b) Impure vacuum-cast nickel (99.97 pct Ni) c) Pure nickel containing internal voids (produced by a process of intering). d) A substitutional solid solution alloy of pure nickel containing 1.16 pct Sn. All the materials were given a high-temperature anneal (>850°C) to produce a stable grain size of 7 to 10 grains per linear mm. The apparatus and techniques used to obtain the present results have been described elsewhere.' In this series, grain growth was observed only in the highest-purity, vacuum-cast metal. Thus we may consider that in the other materials grain-boundary migration was prevented by either preexisting voids or solute atoms. The effect of migration on the creep ductility of the above materials can be seen from Fig. 1, which

Jan 1, 1962

By A. S. Argon, G. East

From their study of the anisotropy of grain boundary mobility in aluminum, the authors conclude that tilt boundaries have a higher mobility than twist boundaries because the atomic misfit at the pure-twist boundary is relatively small compared to the misfit at a tilt boundary for a given amount of misorientation. If this is true, then one would expect a twist boundary to have a lower grain boundary energy than the corresponding tilt boundary. Fig. 6, taken from the work of Gjostein and Rhines,10 shows that this is indeed the case for [001]-cu tilt and twist boundaries in the high-angle region, thus lending support to the authors' conclusion.

Jan 1, 1968

By G. Beghi, G. Piatti

THE authors examined the problem of the gradual transformation of Al2O3 from the transition phases normally encountered in SAP (r -x-n)1-3 to the stable a phase. This phenomenon is well-known at temperatures above the melting point of aluminum,3"6 whereas in this paper the transformation was studied at temperatures lower than the melting point of the aluminum matrix.

Jan 1, 1967

By W. A. Burns

Vertical flow is an important mechanism in many petroleum reservoirs. Yet no adequate method has heretofore been proposed for determining the in-situ vertical permeability in a reasonable length of time. Core measurements of vertical permeability do not necessarily represent effective in-situ values. Cores may be representative of only localized pockets of high or low permeability, and total reliance on cores might cause one to overlook the presence of vertical fractures altogether. Conventional single-well tests, interference tests, and pulse tests commonly are used to determine horizontal transmissibility, khh/u, but generally are not designed to measure vertical trans-missibility or other groups containing vertical permeability, ku. A new well test described here provides a measure of in-situ vertical permeability as well as the previously measurable horizontal permeability. This "vertical test" determines the vertical diffusivity, kv/gcu, and horizontal transmissibility, khd1/u (where dl is the length of injection or production perforations). The test is basically a short-term interference or pulse test normally lasting less than a day. Conventional down-hole equipment is used between two isolated sets of perforations in the same well, as shown in Fig. 1. A "layer-cake" description of a reservoir can be obtained by running two or more vertical tests in the same well, each over different vertical intervals. Each test can be analyzed for the effective vertical and horizontal properties of the interval tested. In addition, a vertical well test can determine the effective- ness of a shale barrier or tight zone by testing across it. Field use to date of vertical testing has confirmed its utility in reservoir description. Mathematical Basis Interpretation of vertical tests for ku and kh is based on comparison of measured pressure response with computer-generated response. Pressure behavior during a vertical test in a homogeneous, anisotropic, infinite-acting reservoir (infinite in radial extent and bounded in both directions vertically) is given by the diffusion equation for slightly compressible fluids with negligible gravity effects.l A schematic diagram of the problem is presented in Fig. 2, and an analytic solution, based on the image

Jan 1, 1970