A modified Cuprex Metal Extraction Process (CMEP) leach process was used to extract Cu. Ni and Co from a complex sulphide concentrate. The standard leach was modified to a two-stage countercurrent leach which provided emf control of the copper SX feed and minimized iron dissolution. A flowsheet was developed to recover the base metals and silver from the leach solution and gold and platinum group metals from the leach residue which was predominantly elemental sulphur. Techniques required to maintain an iron balance in the system including pressure oxidation and solvent extraction are described.

Jan 1, 1996

By Zhengjie Chen, Wenhui Ma, Jijun Wu, Kuixian Wei

The gasification reactivity of PC (petroleum coke), strengthened by addition of different potassium carbonate proportions using different grinding medium, was investigated by using thermogravimetric analysis (TGA). Results showed that the gasification reactivity of PC not only increased with the increase of catalyst-loaded, but also showed the effective improvement by anhydrous alcohol. The PC was mixed with potassium carbonate [K2CO3] catalyst at 0.5%, 0.8%, 1.0% and 1.5%, and then ground wet with distilled water. The CO2-gasification rate of PC was only 77.35%, 80.55%, 84.07% and 85.88% under the gasification temperature 1100 °C and holding time 120 min, at different K2CO3 respectively. However, when the PC was ground in anhydrous alcohol at the same condition of catalyst-loading, the gasification rate of PC reached 95.43%, 96.63%, 95.50% and 95.61% at the holding time of 108 min, 101 min, 74 min and 35 min, respectively. It was shown by FTIR, SEM and EDX determinations that the anhydrous alcohol used as the grinding medium can further improve the gasification reactivity of PC when compared with the distilled water.

Jan 1, 2016

By Lucas L. da Costa, Sergio N. Monteiro, Romulo L. Loiola, Tammy G. Rodrigues Portela

"The fibers extracted from the petiole of the buriti palm tree are relatively strong as compared to other lignocelluloses fibers, with a potential for composite reinforcement. In this work, polyester matrix composites incorporated with these fibers were investigated for their flexural behavior. Specimens with up to 40% in volume of continuous and aligned buriti petiole fibers were bendtested until rupture. The results showed an increase in both the composite mechanical strength and the stiffness with incorporation of these fibers. A fractograph analysis by SEM disclosed a moderate adhesion mechanism between the buriti petiole fiber and the polyester matrix. This mechanism is apparently responsible for the improved performance of the composites.IntroductionIn recent years, the substitution of energy-intensive synthetic materials for natural ones is being considered in many industrial sectors including automobile, packing and textile [1]. A typical case is that of natural fibers, mainly those obtained from cellulose-based plants also known as lignocelluloses fibers. They have being investigated in the past two decades, aiming to replace synthetic fibers, particularly the glass fiber, commonly used as polymer composite reinforcement [2-8]. From the engineering point of view, lignocellulosic fibers present today important environmental, economical, societal and technological advantages already discussed [7-8]. Moreover, several lignocellulosic fibers are known since the beginning of our civilization and still cultivated or naturally extracted all over temperate and tropical regions of the world. According to Kalia et al [1 ], these fibers can be classified by their origin, as shown in Table 1."

Jan 1, 2011

By Achilles J. B. Dutra, Carlos M. Juarez

"The use of thiourea as a gold leaching reagent has been extensively studied by many researchers, and it has proved to be promising for some cases as refractory ores. Otherwise, the recovery of gold from these solutions did not receive so much attention. In this paper the electrowinning of gold in acidic thiourea solutions was studied by voltarnmetry and chronopotentiometry. An adsorption step was detected prior to Au(I) reduction and the diffusion coefficients at 25°C for Au-TU complex and FD were found to be 1.00 x 10.5 cm2 S-I and 1.98 x 10-5 cm2 S-I respectively. At -0.350 V (SCE) a passivation probably due to TU adsorption was observed. For higher overpotentials hydrogen evolution was the main reaction.IntroductionThe use of acidic thiourea solutions for the extraction of gold and silver has shown to be a promising alternative to the traditional process of cyanidation, specially for certain refractory ores (1-3) and electronic scrap (4). In some cases, the industrial scale was reached (1,5). The thiourea leaching of precious metals presents advantages over cyanidation, as faster kinetics, lower toxicity and lower sensibility to base metals; however the costs due to high thiourea consumption impairs its use.The majority of the publications on thiourea processing of gold is on leaching. Many are review papers (5-7). Recently, the adsorption and desorption of the gold-thiourea complex on activated carbon and ion exchange resins have been studied (8-11).Little research has been done on the electrowinning of gold from acidic thiourea solutions, most of it has been carried on the seventies and beginning of the eighties in the former USSR (12-17) and concerned the eletrolytic extraction of gold in tridimensional cathode cells.The present paper concerns the cathodic behavior of the gold-thiourea complex in the presence of formamidine disulfide in order to provide information on the electrowinning of gold from solutions obtained directly from leaching or from an elution process."

Jan 1, 1997

By P. M. Tyroler

Inco operates a hydrometallurgical plant to treat the residue from the pressure carbonylation process. The main constituent in the residue is cop¬per. The residue is leached under pressure in an acid sulphate solution in two stages and the copper is recovered via electrowinning. The electrowinning tankhouse is fully integrated into the overall plant flowsheet as spent elect¬rolyte is required in upstream leaching steps. In recent years, the amount of residue had increased and copper removal capacity became the rate limiting factor for the entire plant. Consequently, a major program was undertaken to upgrade the tankhouse with regards to capacity, efficiency, cathode quality, working environment and structual integrity and appearance. This paper will describe current facilities and operation, and detail progress in our up¬grading efforts.

Jan 1, 1987

By Saskia Duyvesteyn

Small ion-exchange resin particles provide faster mass transport than conventional-sized beads. Unfortunately, high pressures are needed to pump solutions through columns containing small resin particles. It is preferable to disperse fine resins in the solution being treated. Screens have been used to separate the resin from the solution, but screens do not retain fines created by attrition of the resin particles. We have developed a separation process based on flotation, which relies on the surface characteristics of the resin, instead of size. The resin is conditioned with a surfactant before dispersing it in the solution to be treated; this increases the hydrophobicity of the resin sufficiently for froth flotation, without introducing surfactant directly into the solution. The surfactant adsorbed on the resin surface does not appear to impair the kinetics of metal ion removal. A flowsheet for an effluent treatment process is proposed; other applications are clearly possible.

Jan 1, 1998

By James M. Fragomeni

"The mechanical behavior of an Al-Li alloy was studied and related to the extrusion processing parameters, the plastic metal flow during defonnation, the anisotropy, and the microstructure. The extrusion temperatures, strain rates, extrusion ratios, billet temperatures, and extrusion geometries were varied during processing and correlated with the microstructure and properties. The extrusion processing variables were related to the mechariicar behavior, anisotropy, and microstructure through the ZenerHollomon parameter i.e., the temperature compensated strain rate. Based on optical and electron microscopy studies it was found that regardless of the extrusion conditions, the various microstructures for the most part were unrecrystallized for both the as-extruded and the solution heat-treated conditions. Smaller grain sizes were correlated to larger Zener-Hollomon parameters. The extrusion temperature and ratio did not significantly affect the strength or ductility as did the section geometry, which had a large affect on these mechanical properties. The anisotropy of the properties varied substantially when comparing the extruded longitudinal versus transverse grain orientations.IntroductionThe extrusion process also has a substantial influence on: the microsfructure and mechanical properties of a material that is Athens, Ohio, 45701 fonned The plastic defonnation that occurs during the extrusion process alters the grain size, crystallographic texture, anisotropy, subgrain size, dislocation density and various other microstructural features. Often the material being extruded is not homogeneous, therefore variations in the microstructure and properties occur across the cross-section of the final extruded product. The mechanical properties and microstructure can also vary with length since it is hard to maintain a constant temperature throughout the extrusion process. The extrusion temperature often varies from the heat generated during the extrusion process. The demonstration material that was extruded for this .study was an aluminum alloy containing 2.6wt, % lithium and 0.09wt.% zirconium. This alloy was strengthened by heat treatment causing nucleation, growth, and coarsening of coherent metastable o' (Al3Li) precipitates in the microstructure. The ? precipitates which are a consequence 9f artificially aging the AlLi alloy, are spherical, ordered, and coherent with the aluminum matrix and impede the dislocation glide inotion during plastic defonnation. Theo particles grow homogeneously in the matrix, and have the Cu3Au (L 12)"" superlattice crystal structure. Aluminum-lithium alloys are used primarily for aerospace structural applications since they have attractive properties such as a lower density and higher elastic modulus than conventional 2XXX and 7XXX alloys."

Jan 1, 2000

By P. N. Anyalebechi

The effects of Si (0.19-0.52 wI. %), Fe (0.20 wI. %-0.44 wI. %), and Cr (0-0.10 wI.%) on the response of ingots of aluminum alloy 3004 solidified at different rates (O.IO°C/s to 30°C/s), to homogenization heat treatment have been investigated. Response to homogenization was determined by quantifying the following microstructural parameters: (i) amount of Mn retained in solid solution; (ii) types, relative amounts, sizes, size distributions, shapes, and chemical compositions of second phases; (iii) extent of the alpha-transformation (i.e., AI6(Fe,Mn) --7 (XAI12( Fe,MnhSi) reaction; (iv) dispersoid formation; and (v) alleviation of dendritic microsegregation. Of the three alloying elements investigated, Si had the greatest effect on the response of aluminum alloy 3004 to heat treatment. Increase in Si content, fineness of cast microstructure, and homogenization temperature facilitated alpha-transformation reaction, dissolution of Mg2Si, loss of Mn supersaturation, and formation of AldFe,Mn)3Si and Mg2Si dispersoids.

Jan 1, 2008

By A. M. T. S. Bandara

The solubility of rare earth (RE) salts in aqueous solutions depends on many factors including the type of cations and anions in solution, their concentrations, temperature and the type of solid precipitated. Experiments were conducted using anhydrous La2(SO4)3 and Ce2(SO4)3⋅8H2O as solids and lanthanum(III) perchlorate prepared by dissolving La2O3 in HClO4 solutions as RE-sources. Solutions of H2SO4, H3PO4 and their mixtures in the presence or absence of Na+, Ca2+, Fe(III) or Al(III) as perchlorates served as test solutions. Saturated solutions and precipitated solids were assayed and characterized using standard techniques to show that the La(III) and Ce(III) ions precipitate as hydrated sulphates, phosphates or double salts with sodium, depending upon the solution composition. The change in solubility of RE-salts with solution composition and temperature is the result of the composite effect of changes in solubility products (pKSP) of salts, pKa of acids and other equilibrium constants for ion-association.

By Carl C. Nesbitt

A process has been developed to recover and recycle metals from wastes of brass foundries which contain copper, zinc and lead in various quantities. Tests were conducted to evaluate several leachants, including sulfuric acid, ammonia, hydrochloric acid, cyanide and acetic acid, and to determine the optimum leaching conditions, such as air flow rate, initial copper ion concentration, temperature, and agitation strength. Sulfuric acid containing copper sulfate with dissolved oxygen is the most successful leachant. More than 99% of the copper and zinc originally present in the waste was dissolved, while only 0.5% of the lead entered the solution after 14 hours of leaching. The leaching mechanisms of copper, zinc, and lead are proposed. The copper and zinc can be recovered from the solution by electrolytic processing. The unleached residue may be converted to a lead carbonate which can be converted to litharge at 400-450°C and to massicot at temperature above 500°C by calcination.

Jan 1, 1995

By Katsumi Ogi, Hiroto Uchida, Masamitsu Sato, Atsushi Itsuki

"(BTMSE)Ag(hfac) (BTMSE = trans-bis(trimethylsilyl)ethene) was chosen as a suitable precursor for the XeCl laser (308nm) MOCVD of Ag. Iso-propanol solution of (BTMSE)Ag(hfac) was used as a liquid source for the liquid delivery method, high deposition rate 9nm/min at substrate temperatures of 100°C and 120°C were obtained at the vaporizer temperature of 90°C. This deposition rate is three times faster than by conventional bubbling method and life of the source and reproducibility of the deposition were also improved. Electric resistivities of the laser deposited film shows significantly low resistivity of 10-6Q-cm compared to 1 o-3Q-cm of thermal MOCVD film. These results indicates that the laser MOCVD is one of the effective method for the preparation of the high quality silver film.IntroductionSilver films are a potentially important metallization material in electronic and photonic devises due to their lowest resistivity (1.6µ0-cm) among the metals, high optical reflectance and chemical stability. The MOCVD technique has advantages to sputtering or evaporation in the point of conformal growth and better coverage on sharp steps and narrow gaps[l-2]. For MOCVD application, silver precursors must have sufficient vapor pressure without decomposition at their evaporation temperature. To achieve stable precursor gas supply, liquid delivery of precursor material is promising[3-4] especially for materials that have not enough heat stability and high vapor pressure like silver complexes[S-10]. Several new silver complexes for MOCVD and UV irradiation effect to their MOCVD silver film quality were reported by same authors[5]. In this paper new solvent system for liquid delivery system of silver MOCVD were investigated to suite XeCl(308nm) laser MOCVD application."

Jan 1, 1998

By Chikabumi Yamauchi

The comprehensive scientific development of conventional industrial technologies stimulates the creation of new ones in the next generation. Prof. Akira Yazawa has just accomplished such an important work in the non-ferrous pyrometallurgical field. The results of his successful research are immortal. The research group of the author has conducted since 1985 fundamental studies on the application of sodium carbonate slag to copper fire refining. In the present paper, a calculation method for the distribution ratios of impurity elements between sodium carbonate slag and molten copper will be shown. The specific treatment by sodium carbonate slag will also be presented as an effective way for reducing each impurity content in the molten copper to 0.1 mass ppm, which is the level required for the production of high purity copper. The thinking-out of this evaluation method gets a hint from the Equation (2) in the text which was proposed by Prof. Akira Yazawa.

Jan 1, 2003

By H. Conrad, K. Jung

"The effect of an external electric field E=5(+) kV/cm applied during the solution heat treatment at 500°-550°C of three commercial Al-Mg-Si alloys (AA6061, AA6022 and AA61l1) on the asquenched resistivity Pw and hardness H.,NULL, w was investigated. It was found that the field gave a significant increase in Pw and in Hv,w, for AA6022 and AA6111, but had no clear effect on AA6061. Thermodynamic analysis gave that the effect of the field on AA6022 and AA6111 was to reduce both the enthalpy ?H, and entropy ?H, of solution. Considering the chemical composition of the three alloys it appears that the influence of the field may depend on the amount of Cu plus excess Si present in the alloy.IntroductionKlypin and Soloviev [1, 2] were the first to report that the application of an external electric field during solution heat treatment (SHT) of Al alloys gave an increase in the as-quenched resistivity and hardness. They attributed these effects of the field to an increase in solubility of the alloying constituents during the SHT. More recently Liu and coworkers [3, 4] also reported an increase in the as-quenched resistivity of Al-Li alloys with application of an electric field during SHT. Further, the present authors [5] found that the application of an electric field during the SHT of the commercial Al-Mg-Si alloys AA6022 and AA61i1 increased their as-quenched resistivity and hardness. Their thermodynamic analysis of the results indicated that the field decreased both the enthalpy ?H, and entropy ?S, of solution."

Jan 1, 2004

By P. Ret, E. Üstiindag, R. Dieckmann, R. Subramanian, S. L. Sass

"Partial reduction reactions in the Ni-AI-O system, starting with the spinel compound NiAI20 4, are used to form metal-ceramic microstructures. By suitable choice of processing parameters, such as reduction temperature, oxygen partial pressure and time, two different morphologies of nearly pure Ni particles, equiaxed and rod-like, form within a ceramic matrix, which is either a-A12O3 or a metastable ""defect spinel"". Electron microscopy studies were performed for microstructural characterization, phase identification and chemical analysis. The fracture toughness of the Ni-AI2O 3 mixture was significantly improved with respect to that of the original spinel phase. The important issues that must be addressed to form useful metal-ceramic microstructures by partial reduction reactions rue discussed. It is shown that cracking at the original spinel grain boundaries, likely due to the large volume changes associated with the reduction reaction, can be avoided by the addition of small amounts of ZrO2• Initial results illustrating effect of ZrO2 on the microsuuctures are presented.IntroductionEngineering materials used in load bearing circumstances, particularly under extreme conditions (e.g. high temperatures or stresses), generally are formulated with complex microsuuctures. Such composite-like materials can possess properties unobtainable by either of the individual constituents. With metal-ceramic composites, for example, a material can be obtained with an optimum combination of the low density and high strength of the ceramic, and the toughness of the metal. For high temperature service, where demanding conditions are often present, for example, inside jet turbine engines, a successful new material must have low density, high Young's modulus as well as good oxidation resistance, strength, fracture toughness, creep and fatigue resistance. The candidates include intermetallic compounds, and metal-ceramic, intermetallic-ceramic and ceramic-ceramic composites."

Jan 1, 1994

By Dengfu Chen, Mujun Long, Youguang Ma, Xin Xie, Xing Zhang, Leilei Zhang

"Processing parameters of a submerged entry nozzle (SEN) affect significantly on the patterns of fluid flow and temperature distribution in beam blank continuous casting mold with double SEN s. Effect of the geometry structure and immersion depth of double SEN s on the fluid flow in beam blank continuous casting mold was studied by water modeling. Results showed that, the optimal nozzle inner diameter was 40mm, and immersion depth was 70-90mm. The mold surface fluctuation, slag distribution, impact depth and removing rate of inclusion particles were discussed under different processing parameters of double SENs. As the results indicated, slag distribution was more non-homogeneous with a higher casting speed. The results provided basic data for the design and optimization of SENs used in beam blank continuous casting mold.IntroductionNear-net-shape casting has the distinct advantages of less rolling procedures, higher metal recovery and lower energy cost. Therefore, in the recent decades, one of the recent trends in the steel making process is moving toward near net shape casting. in which beam blank casting is a typical technology. The schematic section of beam blank is shown in Fig 1."

Jan 1, 2014

By L. J. Davies

Refractories usage in furnaces for the extraction of nickel from both sulphides and lateritic ores is reviewed. Recent changes in raw materials and basic brick qualities developed to meet the increasing demands of existing and new processes are outlined. Examples of used brick examinations to establish mechanisms of wear are given. The importance of physical and chemical properties are discussed. The use of simulative laboratory testing to aid in refractories development and selection is described.

Jan 1, 1988

By Do-Hyeong Kim, Jong-Jin Pak, Jung-Mock Jang, Min-Kyu Paek

"Thermodynamic relations among Mn, Al and N in liquid iron were studied by measuring the effect of Mn on the solubility product of AlN in liquid Fe-Mn-Al-N alloys in the temperature range from 1773 to 1873 K. The critical Al and N contents for AlN formation were determined by the metal-nitride-gas equilibration technique over wide ranges of melt composition and temperature. The effects of Mn on N solubility in Fe-Mn and Fe-Mn-Al melts containing Mn up to 26 mass% were separately determined in the same temperature range. The experimental results were thermodynamically analyzed using the Wagner's formalism to estimate the critical Al and N contents for the onset of A1N formation. The validity was checked by the observation of inclusion evolution in Fe-20%Mn-1.5%Al-0.6%C-0.3%Si-0.012%N melt during cooling and solidification.IntroductionRecently, high manganese steels such as Twinning Induced Plasticity (TWIP) steels have been developed as next generation steels because of their high formability as well as excellent strength and ductility.[1•2l In these steel grades, a large amount of Mn (15-20 mass%) and Al (1-2 mass%) are added to liquid steels, and such high Mn and Al concentration bring the great challenges to the steelmaking and casting processes. Mn significantly increases the N solubility in liquid iron and the AlN inclusions can be easily formed at such high Al concentrations due to high affinity of Al and Mn with N in liquid steels. Although the AlN inclusion is known to be a dominating and considered as a detrimental phase for the hot ductility of steels,l3l thermodynamics of AlN formation in high Mn-Al alloyed liquid steels was not well known.Moreover, the melting point of these steels decreases down to near 1623 K as increasing Mn content up to 20 mass%. However, most of thermodynamic data has been measured at the steelmaking temperature around 1873 K. Even at steelmaking temperature, there are huge scatters in thermodynamic interactions of Mn and Al on N in liquid iron. The nitrogen solubility in Fe-Mn alloy melts has been measured using the Sieverts' method[4l and the samplinij method[5-7J in the temperature range of 1813 to 1973 K. In the authors' recent study,[8•9 the N solubility in Fe-Al alloy melts was measured using the sampling method in the temperature range of 1823 to 1973 K. However, the simultaneous effect of Mn and Al at high concentrations on Nin liquid Fe-Mn-Al-N alloys is still not known. Also, there remains uncertainty about the temperature dependence of the interaction parameter of Mn on N in liquid Fe-Mn alloys. Therefore, it is worthwhile to check the temperature dependence of this parameter at a low temperature near the melting point of Fe-Mn alloys. There have been few studies on the characterization of non-metallic"

Jan 1, 2014

By V. I. Lakshmanan

Crown ethers are gaining importance in separation technology specifically for rare earth elements (REE, La to Lu plus Y) and precious metals (Au, Ag, Pt, Pd, Rh and Ir) due to their specific binding ability, metal complex stability and high extraction efficiency. The selectivity of crown ethers in extraction of these metals depends on different factors, including the cavity diameter and nature of a donor atom of the crown ether, size and charge of the metal ion, diluents and counter ion. Demand for strategic REE and precious metals are consistently increasing in the world while the separation of these metals is most challenging tasks. In this paper, the use of crown ethers in separation of REE and precious metals, reaction mechanisms and simplified process flowsheets will be elucidated. New reagents with high selectivity for the separation of these metals are further expected to produce high purity metals.

By Saeid Pournaderi, Ahmet Geveci, Ender Keskinkilic, Yavuz A. Topkaya

"This study investigated calcination behavior of one of the Turkish laterite deposits, which was recently found in Sivrihisar region. Representative limonitic laterite samples (1.26% Ni) taken from Yunusemre Karasivritepe and Kucuksivritepe location were first subjected to drying. Removal of chemically bound water and other volatiles were then studied, in detail. In the calcination experiments, temperature and time were the main experimental variables. Thermal treatment was conducted at the specific temperatures in 250 °C - 800 °C range. The weight losses due to elimination of chemically bound water and other volatiles were reported to be approximately 10 per cent of the weight of the ore. For the particle size used in the current work, 700 °C and 40 minutes were determined to be the optimum calcination temperature and time, respectively.IntroductionThe nickel ores that are economically valuable can be grouped into two categories: sulphide type nickel ores and oxide type nickel ores, namely laterites. Over all reserves in the world, 40% are sulphide nickel ores and the remaining 60% are laterites [1]. Pyrometallurgical nickel extraction from sulphide type nickel ores is conducted via matte smelting. More recently, laterite ore bodies have been subjected to nickel extraction. Depending mainly on the chemical composition of the laterite and the process economics, various extraction techniques have been implemented: pyrometallurgical route involves ferronickel smelting. High pressure acid leaching (HPAL) is the commercial method for hydrometallurgical nickel extraction, while ammonia leaching (CARON Process) is a combination of pyrometallurgical and hydrometallurgical processes [2]. With the improvements in these processes, it is predicted that laterite’s share in the world nickel production will rise to 50% in 2012, while it was reported to be 42% in 1,200,000 tons of annual production in 2003 [3]."

Jan 1, 2011

By Harsh Deep Chopra, Jason N. Armstrong, Susan Z. Hua

"Existence of anisotropic Curie temperature materials [E. R. Callen, Phys. Rev. 124, 1373 (1961); J. Appl. Phys. 32 S221 (1961)] is a longstanding prediction - materials that become paramagnetic at a lower temperature along certain crystal directions while remaining magnetically ordered in other directions up to a higher temperature. Validating Callen's theory, we show that all directions within the basal plane of monoclinic F e1Ss (pyrrhotite) single crystal remain ordered up to 603 K while the c-axis becomes paramagnetic at 225 K. Results prompt a re-evaluation of existing magnetic materials with a focus on magnetic characteristics along different crystal orientations above instead of below the ordering temperatures. Theoretical guidelines for identifying new materials with large anisotropy of Curie temperature are also given, and analysis protocol to characterize them in a self-consistent manner is discussed. Materials with such a large directional dependence of Curie temperature open the possibility for uniquely new devices and phenomena, including energy storage and spintronics devices.IntroductionThis paper is an overview of our recently published work on anisotropic Curie temperature materials [l]. As a background, ferromagnetic and ferrimagnetic materials are characterized by a critical temperature below which magnetic interactions prevail over thermal agitation, leading to the appearance of a spontaneous magnetization. Above this critical point, called the Curie temperature, thermal energy eventually overcomes magnetic interactions and the material becomes paramagnetic.It is less well known that the Curie temperature varies with the orientation of the crystal. In ordinary ferromagnets this orientation dependence of Curie temperature is negligible because of the vanishingly small ratio of anisotropy to exchange energy, i.e., the spherical or isotropic exchange term dominates. Thus Curie temperature in ordinary ferromagnets appears to be an isotropic property, and assigning it a single characteristic ordering temperature suffices. However, a 'small' difference is not equivalent to being the 'same', and under appropriate set of conditions the anisotropy of Curie temperature is predicted to become appreciable, as discussed in the following.In formulating the theory of 'anisotropic magnetization' [2, 3] E. R. Callen and H. B. Callen first discussed the ""interesting possibility"" of anisotropic Curie temperature [2] or ACT; Callen and Callen noted that it was W. J. Carr, Jr. who initially raised this question, and they discussed it in detail at the Conference on Magnetism and Magnetic Materials (NY, November 1960), see footnote on page 320 of Ref. [2]. Soon thereafter, E. R. Callen developed the theory underlying the anisotropy of Curie temperature and conditions conducive to its observation [4, 5]."

Jan 1, 2013